Patent Application
20090108236
1. Field of the Invention
Embodiments relate to a paste composition for a plasma display device and associated methods, and more particularly, to a paste composition that may provide excellent dispersion properties.
2. Description of the Related Art
A plasma display device includes a plasma display panel (PDP) that forms an image by exciting phosphor with vacuum ultraviolet (VUV) light generated by gas discharge in discharge cells. The PDP enables a wide screen with a high resolution, and has been spotlighted as a next-generation flat panel display.
In the PDP, inorganic material layers, e.g., phosphor layers, electrode layers, etc., may be formed using a paste composition. The paste composition may include inorganic particles, a binder, and a solvent. However, obtaining a desired degree of dispersion of the inorganic particles during fabrication of the plasma display panel may be difficult. Accordingly, there is a need for advances in the development of suitable paste compositions.
Embodiments are therefore directed to a paste composition for a plasma display device and associated methods, which substantially overcome one or more of the problems due to the limitations and disadvantages of the related art.
It is therefore a feature of an embodiment to provide a paste composition for a plasma display device and associated methods, in which a composite dispersant is used.
At least one of the above and other features and advantages may be realized by providing a composition for a plasma display device, including inorganic material particles, a composite of an acidic dispersant and a basic dispersant, a binder, and a solvent.
The acidic dispersant and basic dispersant may be present in an acidic dispersant:basic dispersant weight ratio of about 25:75 to about 75:25. The acidic dispersant and basic dispersant may be present in an acidic dispersant:basic dispersant weight ratio of about 60:40 to about 40:60. The composite dispersant may be present in an amount of about 1 part by weight to about 10 parts by weight, based on the total 100 parts by weight of the inorganic material particles in the composition. The composite dispersant may be present in an amount of about 2 parts by weight to about 5 parts by weight, based on the total 100 parts by weight of the inorganic material particles in the composition.
The acidic dispersant may include one or more of a carboxylic acid group, a phosphoric acid group, or a sulfonic acid group as an acidic group. The basic dispersant may have an amine group as a basic group. The acidic dispersant may be an oligomer or a polymer having a number average molecular weight of about 300 to about 10,000 g/mol. The basic dispersant may be an oligomer or a polymer having a number average molecular weight of about 300 to about 10,000 g/mol.
The inorganic material particles may include one or more of a phosphor, a dielectric material, or a conductor. The inorganic material particles may include a phosphor.
At least one of the above and other features and advantages may also be realized by providing a method of fabricating a plasma display device, including forming a plasma display panel including a patterned inorganic material layer, and coupling at least one driver to the plasma display panel. Forming the patterned inorganic material layer may include forming a material layer using a paste composition that includes inorganic material particles, a composite of an acidic dispersant and a basic dispersant, a binder, and a solvent, drying the material layer, and patterning the material layer.
The above and other features and advantages will become more apparent to those of ordinary skill in the art by describing in detail example embodiments with reference to the attached drawings, in which:
Korean Patent Application No. 10-2007-0109507, filed on Oct. 30, 2007, in the Korean Intellectual Property Office, and entitled: “Paste Composition for Plasma Display Panel,” is incorporated by reference herein in its entirety.
Example embodiments will now be described more fully hereinafter with reference to the accompanying drawings; however, they may be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art. Like reference numerals refer to like elements throughout.
As used herein, the expressions “at least one,” “one or more,” and “and/or” are open-ended expressions that are both conjunctive and disjunctive in operation. For example, each of the expressions “at least one of A, B, and C,” “at least one of A, B, or C,” “one or more of A, B, and C,” “one or more of A, B, or C” and “A, B, and/or C” includes the following meanings: A alone; B alone; C alone; both A and B together; both A and C together; both B and C together; and all three of A, B, and C together. Further, these expressions are open-ended, unless expressly designated to the contrary by their combination with the term “consisting of.” For example, the expression “at least one of A, B, and C” may also include an nth member, where n is greater than 3, whereas the expression “at least one selected from the group consisting of A, B, and C” does not.
As used herein, the expression “or” is not an “exclusive or” unless it is used in conjunction with the term “either.” For example, the expression “A, B, or C” includes A alone; B alone; C alone; both A and B together; both A and C together; both B and C together; and all three of A, B and, C together, whereas the expression “either A, B, or C” means one of A alone, B alone, and C alone, and does not mean any of both A and B together; both A and C together; both B and C together; and all three of A, B and C together.
As used herein, the terms “a” and “an” are open terms that may be used in conjunction with singular items or with plural items. For example, the term “a solvent” may represent a single compound, e.g., ethanol, or multiple compounds in combination, e.g., ethanol mixed with texanol.
As used herein, molecular weights of oligomeric and polymeric materials are number average molecular weights, and weight percentage (wt %) is relative to the amount of inorganic material particles, are unless otherwise indicated.
An embodiment provides a paste composition for fabricating a PDP of a plasma display device. The paste composition may include inorganic material particles, as well as a composite dispersant including an acidic dispersant and a basic dispersant. The paste composition may also include a binder and a solvent.
The composite of acidic and basic dispersants may provide an excellent synergic dispersion of the inorganic material particles as compared to an acidic or basic dispersant alone. The excellent dispersion may allow the paste composition according to an embodiment to include a higher solid content of phosphor, which may result in improved luminous efficiency of the PDP. The composite of the acidic and basic dispersants may be employed to increase a solid content in various compositions, e.g., a paste composition for a dielectric layer, a paste composition for a barrier rib, or a paste composition for an electrode.
The composite of acidic and basic dispersants in the paste composition may function together as a dispersant that may be strongly adsorbed on the surface of the inorganic material particles, regardless of whether the inorganic material particles exhibit acidic or basic characteristics. Accordingly, the paste composition according to an embodiment may provide high dispersion of a variety of inorganic material particles.
In general, a dispersant may be adsorbed on the surface of a dispersed material and thereby stabilize the material, e.g., inorganic material particles, when suspended in a solvent. The degree of adsorption of the dispersant on the material surface may depend on the acidity or basicity of the dispersant, and may depend on the acidity or basicity of the surface of the material that is to be dispersed. For example, when a dispersed material is basic on its surface, an acidic dispersant may exhibit a strong affinity for the dispersed material. However, a basic dispersant may exhibit a strong repulsion for the dispersed material that is basic on its surface, in which case the material may not be well dispersed. Thus, there can be significantly different dispersion results when using either an acidic or a basic dispersant, depending on the property of the surface of the material being dispersed.
According to this embodiment, both acidic and basic dispersants are present in order to have high affinity between the composite dispersant and the material to be dispersed. Thus, dispersion of inorganic material particles may be improved regardless of whether the dispersed material is acidic or basic. In addition, the acidic and basic dispersants form a composite that is physically combined through mutual interaction. Thus, the composite may exhibit synergistic effects that provide advantages superior to those afforded by the individual acidic and basic dispersants. For example, the composite may exhibit a reduced viscosity, which may further improve dispersion efficiency.
In an implementation, the composite of the acidic dispersant and the basic dispersant may include one or more oligomeric or polymer materials as acidic and basic dispersants. For the acidic dispersant and/or the basic dispersant, the oligomer or polymer may have a number average molecular weight of about 300 to about 20,000 g/mol. In a particular implementation, the acidic dispersant and/or the basic dispersant may be an oligomer or polymer having a number average molecular weight of about 500 to about 5,000 g/mol.
Using an oligomer or polymer having a number average molecular weight of about 300 g/mol or more may help ensure good particle stabilization and dispersion efficiency. Using an oligomer or polymer having a number average molecular weight of about 20,000 g/mol or less may help ensure that little or no carbon remains after a firing process that converts the dried and patterned paste composition into an inorganic material layer, and the elimination of carbon may improve the properties of the PDP.
The oligomer or polymer may include, e.g., an alkyl-based copolymer having an alkyl backbone, an ester-based copolymer, an acrylate-based copolymer, a polyurethane-based copolymer, an alkylol ammonium salt copolymer, an amide-based copolymer, an acryl block copolymer, etc.
The acidic dispersant may include an acidic functional group in its oligomer or polymer backbone. The acidic functional group may be, e.g., one or more of a carboxylic acid group, a phosphoric acid group, or a sulfonic acid group. Similarly, the basic dispersant may include a basic functional group, e.g., an amine group or amide group, in its oligomer or polymer backbone.
The composite dispersant including the acidic dispersant and the basic dispersant may be present in the paste composition in an amount of about 1 part by weight to about 10 parts by weight, based on 100 parts by weight of the inorganic material particles in the paste composition. In an implementation, the composite dispersant may be present in the paste composition in an amount of about 2 to about 5 parts by weight, based on 100 parts by weight of the inorganic material particles in the paste composition.
Using about 1 part by weight or more of the composite dispersant may improve the viscosity of the paste composition as compared to the viscosity provided by a singular acidic dispersant or basic dispersant. Thus, the stability of the particle dispersion may be improved. Using about 10 parts by weight or less of the composite dispersant may provide significant reductions in viscosity of the paste composition. Using more than about 10 parts by weight may not provide further decreases, i.e., the viscosity may not decrease further even with additional composite dispersant, and carbon residue may remain after a subsequent firing process, which may negatively impact the properties of the final PDP.
The acidic dispersant and basic dispersant may be present in the composite dispersant in an acidic dispersant:basic dispersant weight ratio of about 25:75 to about 75:25. In an implementation, the acidic dispersant:basic dispersant weight ratio may be about 60:40 to about 40:60.
The binder may include a cellulose-based binder, an acryl-based, a butyral-based, an alcohol-based binder, or mixtures thereof. The cellulose-based binder may include, e.g., methyl cellulose, ethyl cellulose, propyl cellulose, hydroxymethyl cellulose, hydroxyethyl cellulose, hydroxypropyl cellulose, hydroxyethylpropyl cellulose, or mixtures thereof. The acryl-based binder may include, e.g., polymethyl methacrylate, polyisopropyl methacrylate, polyisobutyl methacrylate, copolymers of acryl-based monomers, etc. The copolymers may be copolymers of, e.g., methyl methacrylate, ethyl methacrylate, propyl methacrylate, butyl methacrylate, hexyl methacrylate, 2-ethyl hexyl methacrylate, benzyl methacrylate, dimethyl amino ethyl methacrylate, hydroxy ethyl methacrylate, hydroxy propyl methacrylate, hydroxy butyl methacrylate, phenoxy 2-hydroxy propyl methacrylate, glycidyl methacrylate, methyl acrylate, ethyl acrylate, propyl acrylate, butyl acrylate, hexyl acrylate, 2-ethyl hexyl acrylate, benzyl acrylate, dimethyl amino ethyl acrylate, hydroxy ethyl acrylate, hydroxy propyl acrylate, hydroxy butyl acrylate, phenoxy 2-hydroxy propyl acrylate, glycidyl acrylate, etc.
The butyral-based binder may include, e.g., polyvinyl butyral. The alcohol-based binder may include, e.g., polyvinyl alcohol.
The amount of binder included in the paste composition may vary depending on the kind of inorganic material particles included therein and the particular process used to coat the paste composition. For example, the amount of binder may be determined so that the paste composition has a good viscosity for coating.
In an implementation, when the paste composition is a phosphor paste composition having phosphor particles as the inorganic material particles, the binder may be included in an amount of about 5 wt % to about 12 wt %. Using about 5 wt % or more of the binder may provide the paste composition with a viscosity high enough to simplify preparation. Using about 12 wt % or less may help ensure that the viscosity does not increase so high as to deteriorate the working processes.
The solvent employed in the paste composition may include an alcohol-based solvent, an ether-based solvent, an ester-based solvent, mixtures thereof, etc. The alcohol-based solvent may include, e.g., ethanol, butyl carbitol, texanol, dihydroterpineol, terpineol, mixtures thereof, etc. The ester-based solvent may include, e.g., butyl carbitol acetate (BCA), etc. In an implementation, the solvent may be butyl carbitol (BC), butyl carbitol acetate (BCA), terpineol, or mixtures thereof.
The amount of solvent included in the paste composition may vary, and may be determined so that the paste composition has a viscosity appropriate for coating. The solvent may be included as the remaining amount of the paste composition, i.e., it may be added based on the amount of inorganic material particles, the composite dispersant, and the binder.
In an implementation, the paste composition may be used to form a phosphor layer. In other implementations, the paste composition may be used to form barrier ribs, dielectric layers, or electrode electrodes for a PDP. Accordingly, the inorganic material particles employed in the paste composition may vary depending on the applied fields. Thus, the inorganic material particles may be particles of, e.g., a phosphor, a dielectric material, or a conductor.
The amount of inorganic material particles included in the paste composition may be about 5 volume % to about 50 volume %. Providing about 5 volume % or more may help ensure that the desired effects are achieved. For example, when the inorganic material particles are a phosphor, it may help ensure a high luminous efficiency. Providing about 50 volume % or less may help avoid excessive increases in viscosity.
Where the inorganic material particles are a phosphor, the phosphor may be, e.g. a red phosphor, a green phosphor, or a blue phosphor. The red phosphor may include, e.g., (Y,Gd)BO3:Eu, Y(P,V)O4:Eu, (Y,Gd)2O3:Eu, Y2O3:Eu, or mixtures thereof. The green phosphor may include, e.g., Zn2SiO4:Mn, YBO3:Tb, (Zn,A)2SiO4:Mn (wherein A is an alkali metal), or mixtures thereof. The green phosphor may be mixed with one or more other phosphors, e.g., BaAl12O19:Mn, (Ba,Sr,Mg)O.αAl2O3:Mn (wherein α is 1 to 23), MgAlxOy:Mn (wherein x is 1 to 10 and y is 1 to 30), LaMgAlxOy:Tb,Mn (wherein x is 1 to 14 and y is 8 to 47), and ReBO3:Tb (wherein Re is at least one rare earth element selected from the group consisting of Sc, Y, La, Ce, and Gd). In the mixed phosphor, the green phosphor may be Zn2SiO4:Mn, YBO3:Tb, (Zn,A)2SiO4:Mn (A is an alkali metal). The phosphor may be used in an amount of about 10 wt % to about 70 wt %, based on the total weight of the composition. The blue phosphor may include, e.g., BaMgAl10O17:Eu, CaMgSi2O6:Eu, CaWO4:Pb, Y2SiO5:Eu, or mixtures thereof.
Where the inorganic material particles are a dielectric material, the dielectric material may be a material that is generally used in a dielectric layer of a PDP. Examples of the dielectric material include lead oxide and non-lead oxide low-melting amorphous glass.
The lead oxide or non-lead oxide low-melting amorphous glass may include, e.g., PbO, ZnO, B2O3, Al2O3, SiO2, SnO, P2O5, Sb2O5, BaO, TiO2, and Bi2O5. In an implementation, lead oxide or non-lead oxide low-melting amorphous glass may include lead oxide-boron oxide-silicon oxide (PbO—B2O3—SiO2), lead oxide-boron oxide-silicon oxide-aluminum oxide (PbO—B2O3—SiO2—Al2O3), zinc oxide-boron oxide-silicon oxide (ZnO—B2O3—SiO2), zinc oxide-boron oxide-silicon oxide-aluminum oxide (ZnO—B2O3—SiO2—Al2O3), lead oxide-zinc oxide-boron oxide-silicon oxide (PbO—ZnO—B2O3—SiO2), lead oxide-zinc oxide-boron oxide-silicon oxide-aluminum oxide (PbO—ZnO—B2O3—SiO2—Al2O3), bismuth oxide-boron oxide-silicon oxide (Bi2O3—B2O3—SiO2), bismuth oxide-boron oxide-silicon oxide-aluminum oxide (Bi2O3—B2O3—SiO2-Al2O3), bismuth oxide-zinc oxide-boron oxide-silicon oxide (Bi2O3—ZnO—B2O3—SiO2), bismuth oxide-zinc oxide-boron oxide-silicon oxide-aluminum oxide (Bi2O3—ZnO—B2O3—SiO2—Al2O3), zinc oxide-silicon oxide (ZnO—SiO2), and/or bismuth oxide-silicon oxide (Bi2O3—SiO2).
The paste composition may further include an additive in order to improve flow and process characteristics. The additive may include a photosensitizer such as benzophenone and the like, a silicon-based antifoaming agent, a rheology modifier, a plasticizer, and an antioxidant, which are all commercially available and the selection of which may be readily determined by one of skill in the art. They may be used singularly or in combination.
In an embodiment, the paste composition described above may be employed in the fabrication of a plasma display device. Referring to
The following Examples and Comparative Examples are provided in order to set forth particular details of one or more embodiments. However, it will be understood that the embodiments are not limited to the particular details described.
BaMgAl10O17:Eu as a blue phosphor, a composite dispersant including a carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant and an amine-containing acryl block copolymer having a number average molecular weight of 8,500 g/mol as a basic dispersant, and ethyl cellulose as a binder were mixed in a mixed solvent of terpineol/butyl carbitol acetate (3:7 volume ratio) to prepare a blue phosphor paste composition.
The blue phosphor, the composite dispersant, and the binder were respectively used in amounts of 40 wt %, 0.8 wt %, and 6 wt %, based on the weight of the entire paste composition, and the solvent was used for the balance. As a result, the composite dispersant was used in an amount of 2 parts by weight based on 100 parts by weight of the blue phosphor. In the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 50:50.
The phosphor paste composition was applied on a discharge cell and was subjected to baking to form a blue phosphor layer, and then a PDP was fabricated using generally known operations.
A PDP was fabricated according to the same method as in Example 1, except that the composite dispersant was used in an amount of 1.2 wt % based on the total weight of the composition. The amount of the composite dispersant was 3 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that the composite dispersant was used in an amount of 2 wt % based on the total weight of the composition. The amount of the composite dispersant was 5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that the composite dispersant was used in an amount of 4.0 wt % based on the total weight of the composition. The amount of the composite dispersant was 10 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 75:25.
A PDP was fabricated according to the same method as in Example 1, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 60:40.
A PDP was fabricated according to the same method as in Example 1, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 40:60.
A PDP was fabricated according to the same method as in Example 1, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 25:75.
BaMgAl10O17:Eu as a blue phosphor, a composite dispersant including a carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant and an amide-containing acryl block copolymer having a number average molecular weight of 1,500 g/mol as a basic dispersant, and ethyl cellulose as a binder were mixed in a mixed solvent of terpineol/butyl carbitol acetate (3:7 volume ratio) to prepare a blue phosphor paste composition.
The blue phosphor, the composite dispersant, and the binder were respectively used in amounts of 40 wt %, 0.8 wt %, and 6 wt %, based on the weight of the entire paste composition, and the solvent was used for the balance. As a result, the composite dispersant was used in an amount of 2 parts by weight based on 100 parts by weight of the blue phosphor. In the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 25:75.
The phosphor paste composition was applied on a discharge cell and was subjected to baking to form a blue phosphor layer, and then a PDP was fabricated using generally known operations.
A PDP was fabricated according to the same method as in Example 9, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 50:50.
A PDP was fabricated according to the same method as in Example 9, except that, in the composite dispersant, the acidic dispersant and basic dispersant were used in a weight ratio of 25:75.
A PDP was fabricated according to the same method as in Example 9, except that, a composite dispersant including a carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant and an amine-containing acryl block copolymer having a number average molecular weight of 20,000 g/mol as a basic dispersant in a weight ratio of 50:50 was used.
A PDP was fabricated according to the same method as in Example 9, except that, a composite dispersant including a carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant and an amine-containing acryl block copolymer having a number average molecular weight of 7,000 g/mol as a basic dispersant in a weight ratio of 50:50 was used.
A PDP was fabricated according to the same method as in Example 9, except that, a composite dispersant including a carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant and an amine-containing acryl block copolymer having a number average molecular weight of 10,000 g/mol as a basic dispersant in a weight ratio of 50:50 was used.
A PDP was fabricated according to the same method as in Example 1, except that a (Y,Gd)BO3:Eu red phosphor was used instead of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that a Zn2SiO4:Mn green phosphor was used instead of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that a composite dispersant including a phosphoric acid-containing alkyl polymer having a number average molecular weight of 370 g/mol was used instead of the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol.
A PDP was fabricated according to the same method as in Example 1, except that a composite dispersant including a sulfonic acid-containing alkyl polymer having a number average molecular weight of 370 g/mol was used instead of the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol.
A PDP was fabricated according to the same method as in Example 1, except that the composite dispersant was used in an amount of 0.2 wt % based on the total weight of the composition. The amount of the composite dispersant was 0.5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that the composite dispersant was used in an amount of 0.4 wt % based on the total weight of the composition. The amount of the composite dispersant was 1 part by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that a dispersant was not used.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 0.5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 1 part by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 1.5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 2 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 2.5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 3 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 4 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the carboxyl-containing alkyl polymer having a number average molecular weight of 370 g/mol as an acidic dispersant was used, and the acidic dispersant was used in an amount of 5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the amine-containing acryl block copolymer having a number average molecular weight of 8,500 g/mol as a basic dispersant was used, and the basic dispersant was used in an amount of 0.5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the amine-containing acryl block copolymer having a number average molecular weight of 8,500 g/mol as a basic dispersant, and the basic dispersant was used in an amount of 2 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the amine-containing acryl block copolymer having a number average molecular weight of 8,500 g/mol as a basic dispersant, and the basic dispersant was used in an amount of 3 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 1, except that only the amine-containing acryl block copolymer having a number average molecular weight of 8,500 g/mol as a basic dispersant, and the basic dispersant was used in an amount of 5 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 9, except that only the amide-containing acryl block copolymer having a number average molecular weight of 1,500 g/mol as a basic dispersant, and the basic dispersant was used in an amount of 2 parts by weight based on 100 parts by weight of the blue phosphor.
A PDP was fabricated according to the same method as in Example 15, except that a dispersant was not used.
A PDP was fabricated according to the same method as in Example 15, except that only the acidic dispersant was used.
A PDP was fabricated according to the same method as in Example 16, except that a dispersant was not used.
A PDP was fabricated according to the same method as in Example 16, except that only the acidic dispersant was used.
A first test sample was prepared from the acidic dispersant used in Comparative Example 5 and a mixed solvent of terpineol/butyl carbitol acetate having a volume ratio of 3:7.
A second test sample was prepared from the basic dispersant used in Comparative Example 11 and a mixed solvent of terpineol/butyl carbitol acetate having a volume ratio of 3:7.
A third test sample was prepared from the composite dispersant used in Example 1 and a mixed solvent of terpineol/butyl carbitol acetate having a volume ratio of 3:7.
The hydrodynamic radius (a size of a material in a liquid) of the first, second and third test samples was measured in the mixed solvent. The results are provided in the following Table 1.
As shown in Table 1, Comparative Example 5 and Comparative Example 11, which included only an acidic or basic dispersant, respectively, had a hydrodynamic radius of around 10 nm. Example 1, which included a composite of an acidic dispersant and a basic dispersant, had a hydrodynamic radius of 52.5 nm. Without being bound by theory, it is believed that the hydrodynamic radius of 52.5 nm indicates that the acidic dispersant and the basic dispersant had an acid/base reaction in the paste composition of Example 1, and thereby formed a new composite.
The absorption amount of the dispersant against a blue phosphor for the paste compositions of Comparative Examples 2 though 6, 8, 10, 12, and 13 were measured using a nonaqueous titration method. The results are shown in
Referring to
Referring to
In the Reference Examples, when the acidic dispersant and the basic dispersant were simultaneously used, the phosphor was adsorbed on both the acidic dispersant and the basic dispersant, even though the amount of the composite dispersant was respectively 0.5 parts by weight (Reference Example 1) and 1 part by weight (Reference Example 2). However, the adsorbed amounts were significantly reduced (in Reference Example 1, the acidic dispersant was 0.53 mg/m2 and the basic dispersant was 0.19 mg/m2, and in Reference Example 2, the acidic dispersant was 0.65 mg/m2 and the basic dispersant was 0.27 mg/m2).
The viscosity as a function of shear rate was measured for the paste compositions of Example 1, and Comparative Examples 1, 5, and 11. The shear rates were varied from 0.01 s−1 to 100 s−1 to measure viscosity. The results are shown in
Referring to
Measurement of Viscosity with Respect to Dispersant Concentration
Measurement of Viscosity with Respect to Mixing Ratio of Acidic and Basic Dispersants
The viscosities of the paste compositions of Examples 1, 5 to 8, and Comparative Examples 5 and 11 were measured with respect to the mixing ratio of the acidic dispersant and the basic dispersant. The results are provided in
In
Referring to
Measurement of Viscosity with Respect to Type of Basic Dispersants
The viscosities of the paste compositions of Examples 12 to 14, and Comparative Examples 1 and 5 were measured. The results are provided in
Referring to
As described above, embodiments may provide a paste composition for a plasma display device and associated methods, in which the paste composition includes inorganic material particles, a composite dispersant including a composite of an acidic dispersant and a basic dispersant, and a binder and solvent. The composite of acidic and basic dispersants may provide excellent and synergistic dispersion as compared to a singular acidic or basic dispersant. The dispersion afforded by the paste composition according to an embodiment may allow the paste composition to include phosphor in a large amount, which may result in improved luminous efficiency of the PDP. The mixed acidic and basic dispersants may be used to form a paste composition for forming a phosphor layer, a dielectric layer, a barrier rib, or an electrode, each of which may exhibit an increased solid content. Therefore, desirable properties of a phosphor layer, a dielectric layer, a barrier rib, or an electrode may be realized.
Exemplary embodiments have been disclosed herein, and although specific terms are employed, they are used and are to be interpreted in a generic and descriptive sense only and not for purpose of limitation. Accordingly, it will be understood by those of ordinary skill in the art that various changes in form and details may be made without departing from the spirit and scope of the present invention as set forth in the following claims.