Patent Application
20190292314
The present invention belongs to the field of modification of macromolecular materials, and specifically relates to a PBS resin composition with good hydrolysis property.
PBS (poly(1,4-butylene succinate)) resin, being a biodegradable resin, can be completely degraded to water and carbon dioxide, thereby reducing plastic garbage, and it possesses an extensive application prospect in fields such as supermarket shopping bag, domestic garbage bag, agricultural plastic mulching film and packaging film. Although commercially available PBS resin satisfies the requirements of environment protection and biodegradation, the speed of hydrolysis of the PBS resin is too fast for long-term storage. Generally, the PBS resin has already started to be hydrolyzed before fully used, and thus severely influencing the application of PBS in various fields. Therefore, how to provide a PBS resin with good hydrolysis property has become a problem demanding prompt solution.
The objective of the present invention is to provide a PBS resin composition with good hydrolysis property.
Another objective of the present invention is to provide a preparation method of the above-described PBS resin composition.
In order to achieve the above objectives, following technical solutions are used.
A PBS resin composition, comprising following components:
(a) PBS resin
(b) element titanium
(c) element phosphorus,
wherein a range of a weight ratio of the element titanium to the element phosphorus is 0.6-10:1, the element titanium is from a titanium-containing compound and the element phosphorus is from a phosphorus-containing compound.
Particularly, the range of the weight ratio of the element titanium to the element phosphorus in the PBS resin composition is preferably 0.7-4:1, and more preferably 1.25-1.5:1. In the PBS resin composition, a weight content of the element titanium is preferably 20-200 ppm, and a weight content of the element phosphorus is 15-70 ppm.
The element titanium exhibits a catalysis effect on the proceeding of a reaction. A too low addition amount of the element titanium leads to low proceeding of a polymerization reaction, and a too high addition amount of the element titanium leads to easy degradation of the PBS resin. The element phosphorus can improve the color of a product, but there's a certain complexation between the element phosphorus and the titanium-containing compound. A too high addition amount of the element phosphorus leads to a reducing activity of a catalyst, slowing down a polymerization speed and increasing the possibility of thermal degradation of the resin during the polymerization; while a too low addition amount of the element phosphorus cannot effectively improve the color of the product. It is found by a great deal of experiments that when the weight ratio of the element phosphorus to the element titanium in the PBS resin composition is 0.6-10:1, the hydrolysis property of the PBS resin can be improved, and meanwhile the color of the PBS resin product also meets the requirement.
In the present invention, by controlling the addition amounts of the titanium-containing compound and the phosphorus-containing compound during the synthetic process of the PBSA resin composition, the weight ratio of the element titanium to the element phosphorus in the PBSA resin composition is adjusted.
With reference to the US EPA method 3052:1996 by using ICP-OES for analysis, the weight contents of the element titanium and the element phosphorus in the PBS resin composition of the present invention are determined according to the following procedure: weighing 0.1 g of the PBS resin composition and crushing, then dropping 5 mL of nitric acid to fully immerse the PBS resin composition; then dropping 1.0 mL of hydrogen peroxide to react for 2 minutes, sealing into a microwave digestion tank to digest at 210° C. for 3 hours; and after cooling to room temperature, filtering with a 0.45 μm filter membrane followed by diluting with distilled water to a volume of 50 mL for an ICP-OES test.
The PBS resin composition of the present invention has a melt flow index of 3.0-10.0 g/10 min when tested at 190° C. under a condition of 2.16 kg weight.
Said element phosphorus of the present invention is selected from one of or a mixture of more of triethyl phosphate, trimethyl phosphate, tributyl phosphate and triphenyl phosphate.
Said element titanium of the present invention is selected from one of or a mixture of N-butyl titanate and isopropyl titanate.
After treating in a 95° C.-distilled water bath for 12 hours and drying at 90° C. for 3 hours, a change of the melt flow index of the PBS resin composition in the present invention is less than 50.0 g/10 min.
A preparation method of the PBS resin composition comprises the following steps:
(1) mixing succinic acid, 1,4-butanediol and a titanium-containing compound, and maintaining at a temperature of 180-250° C. under a pressure of 50-100 kPa for 1-5 hours;
(2) after aerating CO2, adding a phosphorus-containing compound and maintaining for 10-30 minutes; and
(3) reducing the pressure to less than 100 Pa, heating a mixture obtained in step (2) to 230-250° C., maintaining for 3-6 hours, aerating nitrogen and pelletizing.
Compared with the prior art, the present invention has following advantages:
In the present invention, by controlling the range of the weight ratio of the element titanium to the element phosphorus in the PBS resin composition to be 0.6-10:1, and after treating in a 95° C.-distilled water bath for 12 hours and drying at 90° C. for 3 hours, a change of the melt flow index of the above-described PBS resin composition is less than 50.0 g/10 min. The PBS resin composition of the present invention has an apparently improved hydrolysis property.
The present invention is further described by specific implementations. The following embodiments are preferred implementations of the present invention, but the implementation of the present invention is not limited to the following embodiments.
Following raw materials are used in the present invention, but the present invention is not limited to these raw materials:
succinic acid: purity≥99.9, Shandong Jinyu Chemical Co., Ltd.
1,4-butanediol: purity≥99.5, Shanxi Sanwei Group
N-butyl titanate: purity≥99.0, Tianjin Kemiou Chemical Reagent Co., Ltd.
isopropyl titanate: purity≥95.0, Aladdin Reagent
triphenyl phosphate: purity≥98.0, Aladdin Reagent
trimethyl phosphate: purity≥99.0, Aladdin Reagent
triethyl phosphate: purity≥99.5, Aladdin Reagent.
Succinic acid, 1,4-butanediol and a titanium-containing compound were mixed according to the formulas in Table 1, and maintained at a temperature of 180-250° C. under a pressure of 50-100 kPa for 1-5 hours; after CO2 was aerated, a phosphorus-containing compound was added and maintained for 10-30 minutes; the pressure was reduced to less than 100 Pa, the mixture was heated to 230-250° C. and maintained for 3-6 hours, nitrogen was aerated, and the PBS resin composition was obtained by pelletizing. By controlling addition amounts of the titanium-containing compound and the phosphorus-containing compound, a weight ratio of element titanium to element phosphorus in the PBS resin composition can be adjusted.
Property Test Methods:
With reference to the US EPA method 3052:1996 by using ICP-OES for analysis, weight contents of the element titanium and the element phosphorus in the PBS resin composition of the present invention are determined according to the following procedure: 0.1 g of the PBS resin composition is weighed and crushed, then 5 mL of nitric acid is dropped to fully immerse the PBS resin composition; then 1.0 mL of hydrogen peroxide is dropped to react for 2 minutes, and the mixture is sealed into a microwave digestion tank to digest at 210° C. for 3 hours; and after cooling to room temperature, the mixture is filtered with a 0.45 μm filter membrane followed by diluting with distilled water to a volume of 50 mL for an ICP-OES test.
Melt flow index: testing at 190° C. under a condition of 2.16 kg weight. First, a melt flow index of a product of the embodiments or comparative embodiments is tested for the first time. The above-described product is treated in a 95° C.-distilled water bath for 12 hours and dried at 90° C. for 3 hours. Then, a melt flow index of the PBS resin composition is tested again. A change value of the melt flow index is obtained by subtracting the melt flow index which is after the PBS resin composition subjected to the water bath from the melt flow index which is before the PBS resin composition subjected to the water bath.
The PBS resin compositions of the present invention were treated in a 95° C.-distilled water bath for 12 hours and dried at 90° C. for 3 hours, and the melt flow index thereof changed. The smaller the change, the better the hydrolysis property of the PBS resin composition proved. It can be seen from Table 2 that the weight ratio of the element titanium to the element phosphorus in the PBS resin composition is 0.6-10:1, and a change of the melt flow index after the 95° C.-distilled water bath for 12 hours and drying at 90° C. for 3 hours is less than 50.0 g/10 min which indicates that the PBS resin composition has good hydrolysis property. While the weight ratio of the element titanium to the element phosphorus in Comparative Example 1 is less than 0.6 and the weight ratio of the element titanium to the element phosphorus in Comparative Example 2 is greater than 10, the change of the melt flow index is greater than 50.0 g/10 min which indicates a poor hydrolysis property of the composition.
| Number | Date | Country | Kind |
|---|---|---|---|
| 201611182854.1 | Dec 2016 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2017/113750 | 11/30/2017 | WO | 00 |