Permanent antistatic acid copolymer/quaternary amine polymeric films

This invention relates to an acid copolymer/quaternary amine mixture. The new, acid copolymer/quaternary amine mixtures of the invention are useful, for instance, in making film for packaging for electronic devices that are sensitive to static electricity. The film has permanent, non-bleeding antistatic characteristics. By "permanent, non-bleeding" antistatic characteristics is meant the film exhibits a static decay time (hereinafter abbreviated as SDT) under about 3000 milliseconds (hereinafter abbreviated as ms) when the static decay test using 5000 volts direct current (hereinafter abbreviated as Vdc) is conducted as per Federal Test Method 101c, Method 4046.1, after a 24-hour water shower, i.e. the antistat property is not washed out by the shower. In the preferred embodiments, the film will also still have this SDT of about 3000 ms or less even after 12 days in a hot (approximately 70.degree. C.) oven.
BACKGROUND OF THE INVENTION
When two surfaces are brought in contact with each other, a transfer of electrons may occur resulting in a residual static electrical charge when the surfaces are separated. This phenomena is known as triboelectricity. If the surface is composed of a material that is a conductor, the electrons will dissipate quickly thereby eliminating the excess charge. On the other hand, if the surface is composed of a material that is an insulator (a dielectric), the surface charge takes much longer to dissipate. Thermoplastic polymers are typically excellent insulators and thus are unsatisfactory for uses requiring a nature that will dissipate charges. As the polymers accumulate high charges promoting an attraction for dust and dirt, they can discharge to any lower potential body with which they come in contact. To modify a polymer to have antistatic characteristics and dissipate charges, the conductivity might be increased which in turn causes an increase in the rate of static dissipation. This has been accomplished in the past by the use of antistatic agents to promote static-charge decay of surfaces thereby reducing clinging effect, eliminating spark discharge, and preventing accumulation of dust.
It is well known that static charge can be reduced by increasing the moisture content of the atmosphere, and thus the approach in the past has been to use an antistatic agent which will modify the inherently dielectric polymer to impart hydrophilic properties to it by providing functional groups that attract moisture to it. For instance, it is well known to apply external antistatic agents onto polymers by conventional coating or painting methods. Also, it is well known to employ internal antistatic agents which are volume dispersed by admixing in the polymer; i.e. incorporated into the polymer by compounding or extrusion prior to or during molding or film-forming operations, and which work by migrating to the polymer surface. This migration is colloquially referred to in the art of antistatic polymer technology as a "blooming" or "bleeding" effect. When the antistatic agent has not remained volume dispersed but instead has bloomed or bled to the surface, the mechanism for moisture attraction is the same as with the painted on external antistatic agents. The atmospheric moisture is attracted causing decay or dissipation of static charges, i.e. such films depend on ambient humidity. Accordingly a high rate of blooming is required. Such films can overbloom and lose their antistatic character if subjected to a 24 hour water shower or a prolonged heat exposure.
Many patents show quaternary amines (also referred to as quaternary ammonium compounds or salts) as antistatic agents. Examples are U.S. Pat. No. 3,324,091 to Sauides, U.S. Pat. Nos. 3,445,440, and 3,517,045 both to Susi and Arthen, U.S. Pat. No. 3,894,077 to Horikawa et al, U.S. Pat. No. 4,104,175 to Martinsson et al, U.S. Pat. No. 4,268,583 and T961009 both to Hendy, and U.S. Pat. No. 4,605,684 to Pcolinsky.
Also of interest is Japanese Published Patent Application Kokai No. 59-47243, Ito et al, assignors to Mitsui (published Mar. 16, 1984) which shows an electrically conductive resin composition comprising ethylene/alpha,beta unsaturated carboxylic acid copolymer and a tertiary alkanolamine.
More particularly, U.S. Pat. No. 3,933,779 issued Jan. 20, 1976 to Baron et al assignors to Fine Organics discloses an antistatic polymer blend comprising a synthetic polymer and an antistatically effective amount of a compound of the formula: ##STR1## wherein R is alkyl of 4 to 18 carbon atoms unsubstituted or substituted by halo or aryl.
At pages 18 and 19 of published European Patent Application 0219315 Mott assignor to Dow, date of publication Apr. 22, 1987, is a passage stating that their preferred antistatic material is an acrylate monomer-oligomer mixture containing an alkylether triethyl ammonium sulfate available from Metallized Products under the trade-name Staticure, which material is curable by exposure to an electron beam to a permanent, non-bleeding coating which is not dependent on humidity for its antistatic effect. The passage in EP 0219315 goes on to say that further details concerning this material appear in British Patent Application No. 2,156,362 published Oct. 9, 1985.
British Patent Application No. 2,156,362 is the counterpart of U.S. Pat. No. 4,623,594 issued Nov. 18, 1986 to Keough assignor to Metallized Products. U.S. Pat. No. 4,623,594 claims:
1. An antistatic laminate, both sides of which have antistatic characteristics, comprising:
(A) a substrate sheet;
(B) a continuous coating on one side of said substrate sheet, said continuous coating comprising the electron radiation cured product of:
(1) an electron beam curable prepolymer; and
(2) an effective amount of a saturated quaternary ammonium compound antistatic agent soluble in said prepolymer the product being a reaction product of the prepolymer and the ammonium compound converted into a substantially solid product.
2. the antistatic laminate of claim 1 wherein said quaternary ammonium compound is a trialkylalkyle-therammonium salt. [Emphasis supplied.]
The laboratory examples of U.S. Pat. No. 4,623,594 show that the particular trialkyl alkylether ammonium salt employed was Emerstat 6660 from Emery Industries. Page 52 of a catalog entitled "Miscellaneous Surfactants" describes Emerstat 6660 as a 100% active liquid cationic compound which offers high performance antistatic capacity, but page 52 does not give any generic chemical formula. It is believed that Emerstat 6660 is a diethoxylated alkyl ammonium salt of the formula (A)(A')N[(CH.sub.2 CH.sub.2 O).sub.n H].sub.2.sup.+ A'0SO.sub.3.sup.- which is further described below.
Of general interest is U.S. Pat. No. 4,678,836 (Jul. 7, 1987) McKinney et al assignors to Dow Chemical. It shows blends of linear low density polyethylene (LLDPE) and ethylene-acrylic acid (EAA).
SUMMARY OF THE INVENTION
The present acid copolymer/quaternary amine mixture may be made into a single ply and/or multiple ply film, and additional advantageous features such as tougher films, further described below, may be obtained when such films are irradiated by electron beam. The films of the invention will dissipate an applied charge of .+-.5000 volts direct current (Vdc) in about 3000 milliseconds (ms) or less, more preferably about 2000 ms or less. The films of the invention still will exhibit this static decay time behavior after a 24 hour water shower. In the preferred embodiments, the films also will still exhibit this static decay time behavior after 12 days in a hot (approximately 70.degree. C.) oven. This is true even if the films were not previously irradiated by electron beam. Thus, the antistatic effect is permanent and non-bleeding, without any requirement for electron beam "curing". Accordingly, very satisfactory films may be obtained absent any electron beam irradiation. Thus the irradiation does not have to be employed but may be employed if desired to achieve enhanced toughness and the like as further described below. The new, acid copolymer/quaternary amine mixture may be molded or extruded alone or together with polymers known for their strength such as ethylene vinyl acetate (EVA), polypropylene (PP) or linear low density polyethylene (LLDPE). The resultant film is useful for making packaging, such as a bag or over-wrap, for electronic devices that are sensitive to static electricity. If desired, the packaging could be a heat-shrinkable or vacuum skin packaging. Such a film may also be fashioned to have cushioning characteristics by using bubble cap (also known as air cushioning) machinery such as that described in U.S. Pat. Nos. 4,576,669 and 4,579,516 both to Caputo, or that described in U.S. Pat. Nos. 3,416,984, 3,405,020, 3,586,565, and 3,785,899, all assigned to Sealed Air, the disclosures of which are incorporated herein by reference, to make a bubble cap package which provides cushioning and then bagging or wrapping an electronic device therewith. Such a cushioning bubble cap material (also known as cellular material or air cushioning material) is also useful in lining a portable work station used for storage and transportation of static electricity sensitive devices such as the work stations disclosed in U.S. Pat. No. 4,494,651 issued in 1985 to Malcolm. Also such a film, which may or may not be in a cushion form, is useful to make a package for devices in a medical operating room where explosive oxygen and/or ether are present and thus protection from static electricity must be provided. Also such films may be advantageously employed for any use requiring a plastic with a decreased tendency to accumulate dust.
Therefore, it is an object of the present invention to provide a novel, antistatic acid copolymer/quaternary amine mixture useful in making a film useful for wrapping static sensitive devices. It is also an object to provide such films having an increased tendency to dissipate electrostatic charges. It is also an object that the films are substantially independent of ambient humidity, i.e. the films are still able to decay an applied .+-.5000 VDC in less than about 3000 ms, more preferably less than about 2000 ms, when conditioned at less than about 15% relative humidity.
A feature of the films is that they also have excellent see-through properties which is advantageous for reading code numbers preprinted on a product wrapped with the film.
The present invention provides an acid copolymer/quaternary amine mixture comprising (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N].sup.+ [X].sup.-
wherein
R.sup.1 is selected from H, aryl, C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4, is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, trifluoroacetate, citrate, propionate, tartrate or carbonate. The present invention also provides for a film comprising this mixture.
Preferably, the C.sub.1 to C.sub.8 alkyl phosphate is methyl phosphate or ethyl phosphate, the C.sub.1 to C.sub.8 alkyl sulfate is methyl sulfate or ethyl sulfate, and the C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate is methanesulfonate, butanesulfonate, benzenesulfonate, or C.sub.1 to C.sub.18 alkyl benzenesulfonate.
The present invention also provides a method for making an acid copolymer/quaternary amine antistatic mixture comprising mixing with heat (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.3 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N]'[X].sup.-
wherein
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3 and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, trifluoroacetate, propionate, tartrate or carbonate.
The present invention also provides a method for making an antistatic film comprising
(1) mixing with heat (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N]'[X].sup.-
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, trifluoroacetate, propionate, tartrate or carbonate; and
(2) forming the resultant into a film having one or more layers.
The present invention also provides a permanently antistatic film resultant from mixing with heat and forming into a film having one or more layers (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N].sup.+ [X].sup.-
wherein
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, trifluoroacetate, propionate, tartrate, or carbonate.
The present invention also provides a permanently antistatic film comprising a film obtained from mixing with heat and forming into a film (A) ethylene-acrylic acid or ethylene-methacrylic acid and (B) a quaternary amine of the formula [R.sup.1 R.sup.2 R.sup.3 R.sup.4 N].sup.+ [X].sup.- where R.sup.1 is a C.sub.4 to C.sub.30 straight or branched alkyl optionally including one or more ether linkages, each of R.sup.2 and R.sup.3 and R.sup.4 is the same or different and selected from methyl or ethyl, and X is chloride, methyl sulfate, or ethyl sulfate.
The present invention also provides a film comprising a 5-layer, permanently antistatic film having the layers in direct surface-to-surface contact with each other in the following order:
(1) a first layer, said layer being an outside layer comprising about 90% or more by weight of ethylene vinyl acetate copolymer and about 10% or less by weight of antiblock,
(2) a second layer, said layer being an interior layer comprising about 65% or more by weight ethylene vinyl acetate copolymer, and about 35% or less by weight of a mixture of (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N]'[X].sup.-
wherein
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, trifluoroacetate, propionate, tartrate, or carbonate,
(3) a third layer, said layer being a core layer comprising about 65% or more by weight of a mixture of linear low density polyethylene copolymer and ethylene vinyl acetate copolymer and about 35% or less by weight of a mixture of (A) a polymer containing carboxylic acid moieties and (B) an antistatically effective amount of a quaternary amine wherein:
(A) the polymer containing carboxylic acid moieties is a copolymer of (i) a major amount by mol % of an alpha-olefin of the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl, and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid, and
(B) the quaternary amine is of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N]'[X].sup.-
wherein
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contiguous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substituted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, fluoride, iodide, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, trifluoroacetate, propionate, tartrate, or carbonate.
(4) a fourth layer, comprising an interior layer the same as layer (2), and
(5) a fifth layer, comprising an outside layer the same as layer (1).
DETAILED DESCRIPTION OF THE INVENTION
The acid copolymer is a polymer containing carboxylic acid moieties. By "polymers containing carboxylic acid moieties" as that term is used herein it is intended to mean copolymers of (i) a major amount by mol % of an alpha-olefin having the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl and (ii) a minor amount by mol % of an alpha,beta-ethylenically unsaturated carboxylic acid. Preferably, the alpha,beta-ethylenically unsaturated carboxylic acid is present in an amount by mol % of about 40% or less, more preferably about 30% or less, most preferably about 20% or less. Also, by the term "polymers containing carboxylic acid moieties", it is intended to mean that the copolymer of an alpha-olefin having the formula RHC.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl and an alpha,beta-ethylenically unsaturated carboxylic acid may be wholly or partially neutralized with a suitable cation such as zinc cation or sodium cation. Thus, the polymer containing carboxylic acid moieties may be an ionomer.
The acid copolymer need not necessarily comprise a two component polymer. Thus, although the olefin content of the acid copolymer preferably is at least 50 mol percent, more than one olefin may be employed. Also, other copolymerizable monoethylenically unsaturated monomers may be employed in combination with the olefin and the carboxylic acid comonomer. It is intended also to include terpolymers. Accordingly, acid copolymers or terpolymers suitable for use in the present invention include, but are not limited to, ethylene/acrylic acid copolymers, ethylene/methacrylic acid copolymers, ethylene/itaconic acid copolymers, ethylene/methyl hydrogen maleate copolymers, ethylene/maleic acid copolymers, ethylene/methyl hydrogen maleate/ethyl acrylate terpolymers, ethylene/methacrylic acid/vinyl acetate terpolymers,. ethylene/acrylic acid/vinyl acetate terpolymers, ethylene/acrylic acid/vinyl alcohol terpolymers, ethylene/propylene/acrylic acid terpolymers, ethylene/styrene/acrylic acid terpolymers, ethylene/acrylic acid/methyl methacrylate terpolymers, ethylene/methacrylic acid/ethyl acrylate terpolymers, ethylene/itaconic acid/methyl methacrylate terpolymers, ethylene/methacrylic acid/acrylonitrile terpolymers, ethylene/fumaric acid/vinyl methyl ether terpolymers, ethylene/vinyl chloride/acrylic acid terpolymers, ethylene/vinylidene chloride/acrylic acid terpolymers, ethylene/vinyl flouride/methacrylic acid terpolymers, and ethylene/chlorotrifluroethylene/methacrylic acid terpolymers.
The copolymer of an alpha-olefin having the formula RCH.dbd.CH.sub.2 wherein R is H or C.sub.1 to C.sub.8 alkyl and an alpha,beta-ethylenically unsaturated carboxylic acid representatively may be produced by the free radical copolymerization of ethylene and a carboxylic acid comonomer therefor such as acrylic acid or methacrylic acid. Suitable such acid copolymers are the Primacor (TM) polymers, supplied by Dow Chemical Company, Midland, Mich. Primacor is produced by the copolymerization of ethylene and acrylic acid. Ethylene-acrylic acid copolymers are herein referred to as EAA copolymer. A very suitable Primacor polymer is Primacor 1410 or Primacor 5981. Other suitable such acid copolymers are sold under the trade-name Nucrel by du Pont; they are produced by the copolymerization of ethylene and methacrylic acid. Ethylene-methacrylic acid copolymers are herein referred to as EMAA copolymers. Ionomers are commercially available as Surlyn (R) from the E. I. du Pont de Nemours Company of Wilmington, Del., and are described in detail in U.S. Pat. Nos. 3,355,319 and 3,845,163.
The amine is a quaternary amine of the formula
[(R.sup.1)(R.sup.2)(R.sup.3)(R.sup.4)N].sup.+ [X].sup.-
wherein
R.sup.1 is selected from H, aryl, or C.sub.1 to C.sub.50 alkyl optionally having one or more non-contigous C.dbd.O or NHC.dbd.O or --S-- or --O-- in the carbon chain, or the same as R.sup.2 ;
each of R.sup.2, R.sup.3, and R.sup.4 is the same or different and selected from H, C.sub.1 to C.sub.18 alkyl optionally substiuted with one or more OH or from --(R.sup.5 --O).sub.a --H where a is an integer from 1 to 10 and R.sup.5 is ethylene or propylene; and
X is an anion selected from chloride, bromide, iodide, fluoride, nitrate, fluoborate, phosphate, C.sub.1 to C.sub.8 alkyl phosphate, sulfate, C.sub.1 to C.sub.8 alkyl sulfate, formate, C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate, acetate, citrate, propionate, tartrate or carbonate. Preferably, the C.sub.1 to C.sub.8 alkyl phosphate is methyl phosphate or ethyl phosphate, the C.sub.1 to C.sub.8 alkyl sulfate is methyl sulfate or ethyl sulfate, and the C.sub.1 to C.sub.8 alkyl or C.sub.6 to C.sub.24 alkaryl or aryl sulfonate is methanesulfonate, butanesulfonate, benzenesulfonate, or C.sub.1 to C.sub.18 alkyl benzenesulfonate.
By "quaternary amine" as that term is employed herein, it is intended to include quaternary ammonium compounds and/or quaternary ammonium salts.
Suitable quaternary amines (QA) may be chosen from, but are not limited to, the methyl chloride salts of ethoxylated fatty amines. Commercial ones are available from the Tomah Division (Milton, Wis.) of Exxon Chemical and are represented by the formula: ##STR2## where Z is an alkyl or alkoxy radical, and q+t is the total number of moles of ethylene oxide in the chains. Examples of commercially available ones are as follows:
COMMERCIAL QUATERNARY AMINES
______________________________________QA ProductIndentification Number Z q + t______________________________________Q-14-2 C.sub.10 OC.sub.3 2Q-14-5 C.sub.10 OC.sub.3 5Q-14-15 C.sub.10 OC.sub.3 15Q-17-2 C.sub.13 OC.sub.3 2Q-S-2 Soya 2Q-S-5 Soya 5Q-S-15 Soya 15Q-18-2 C.sub.18 2Q-18-5 C.sub.18 5Q-18-8 C.sub.18 8Q-18-10 C.sub.18 10Q-18-15 C.sub.18 15Q-T-2 Tallow 2Q-T-5 Tallow 5Q-T-15 Tallow 15Q-DT-3 "Tallow Diamine" 3______________________________________
Other very suitable quaternary amines are the ethyl sulfate salts or methyl sulfate salts of alkoxylated fatty amines. Commercial ones are available under the trade-name Emerstat 6660 from Emery Industries and it is believed from applicants' own chemical analysis that they are represented by the formula: (A)(A')N[(CH.sub.2 CH.sub.2 O).sub.n H].sub.2.sup.+ A'OSO.sub.3.sup.- where A is C.sub.8 to C.sub.20 alkyl, A' is ethyl and n is an integer from 1 to 4. Also suitable are methyl sulfate salts such as that sold under the trade-name Cyastat by Cyanamid; it has the formula C.sub.11 H.sub.23 CONHC.sub.3 H.sub.6 N(CH.sub.3).sub.3 .sup.+ CH.sub.3 OSO.sub.3.sup.-. Also suitable are ethosulfate salts such as that sold under the trade-name Larostat 264A Anhydrous, which is a modified soyadimethyl ethylammonium ethosulfate.
Additional QA's may be prepared by reacting a tertiary amine (TA) and an acid or alkylating agent, as further described in the Examples below.
The polymer containing carboxylic acid moieties and the quaternary amine are combined by mixing with heat. Optionally, a polymer compatible therewith, such as a polyolefin, may be blended in the mixture. Any suitable mixing means may be employed such as a blender or a twin screw extruder. The heat should be from about 50.degree. C. to 290.degree. C., more preferably about 100.degree. C. to 250.degree. C., even more preferably about 100.degree. C. to 200.degree. C. Then the resultant may be formed into a film such as by heat pressing on a platen or by any of the various methods further discussed below. The film is permanently antistatic. It will dissipate an applied charge of .+-.5000 Vdc in less than about 3000 ms, more preferably less than 2000 ms, using the method described in Federal Test Method Standard 101c, Method 4046.1, even after a 24 hour water shower. This is unlike prior polymeric films containing an antistatic agent to give them antistatic characteristics, which characteristics can be washed out after a 24 hour water shower because the agents operate by migrating to the surface and attracting moisture. Furthermore, in some embodiments, the films survive 1 day, more preferably 3 days, even more preferably 5 days, and most preferably 12 days in a hot oven at approximately 70.degree. C. and still exhibit this static decay time of less than about 3000 ms, more preferably less than about 2000 ms. Based on the % weight amount of polymer containing carboxylic acid moieties, it is preferred that the quaternary amine be present in a weight % amount up to about 50%, more preferably up to about 30%, even more preferably up to about 20%. Based on the total composition weight, which optionally may contain polyolefin, preferably the quaternary amine is present in a weight % amount of about 0.001% to about 30%, more preferably about 0.01% to about 20%, and even more preferably about 2% to about 10%.
It is also noted that in multi-layer film embodiments, the layer or layers comprising the composition of quaternary amine and acid copolymer should comprise about half the thickness or more of the multilayer film for the film to be permanently antistatic, i.e. exhibit an SDT under 3000 ms after a 24-hour water shower. Otherwise, the film as is, will exhibit an SDT under 3000 ms, but after the 24-hour water shower the film will not accept a charge. It is also further preferred that both skin layers of the multi-layer film comprise the composition of quaternary amine and acid copolymer, as compared to 1 skin layer or a core layer, for the film to have a permanent antistatic surface resistivity, i.e. a surface resistivity from 10.sup.5 to 10.sup.12 ohms/square after a 24-hour water shower. All of this is illustrated by Example XII below wherein the multilayer film had only 1/5 its thickness (i.e. 1 layer out of 5) be the composition of quaternary amine and acid copolymer. This film exhibited an antistatic SDT of 1824 ms and 1852 ms when tested as is, but would not accept a charge after a 24-hour water shower. Also this film exhibited an antistatic surface resistivity of 5.9.times.10.sup.11 ohms/square when tested as is, but showed an insulative surface resistivity of 1.9.times.10.sup.14 ohms/square after a 24-hour water shower.
Many polymer resins are suitable polymers for blending with the new, acid copolymer/quaternary amine. Unless specifically set forth and defined or otherwise limited, the terms "polymer" or "polymer resin" as used herein generally include, but are not limited to, homopolymers, copolymers, such as, for example block, graft, random and alternating copolymers, terpolymers etc. and blends and modifications thereof. Furthermore, unless otherwise specifically limited the terms "polymers" or "polymer resin" shall include all possible structures of the material. These structures include, but are not limited to, isotactic, syndiotactic and random symmetries. Particularly suitable for blending are the polyolefins. The term "polyolefin" as used herein generally includes, but is not limited to, materials such as polyethylene (PE), polypropylene (PP), ethylene-vinyl acetate (EVA) and the like, the homopolymers, copolymers, terpolymers etc. thereof, and blends and modifications thereof. The term "polyolefin" shall include all possible structures thereof, which includes, but is not limited to, isotactic, syndiotactic and random symmetries.
According to Modern Plastics Encyclopedia, 1985-86, polyethylenes having densities ranging from about 0.900 g/cc to about 0.935 g/cc are called low density polyethylenes (LDPE), while those having densities from about 0.936 g/cc to about 0.940 g/cc are called medium density polyethylenes (MDPE), and those having densities from about 0.941 g/cc to about 0.965 g/cc and over are called high density polyethylenes (HDPE). The older, classic low density types of polyethylenes are usually polymerized at high pressures and temperatures whereas, the older, classic high density types are usually polymerized at relatively low temperatures and pressures. The term "linear low density polyethylene" (LLDPE) as used herein, for a type of polyolefin, refers to the newer copolymers of a major amount of ethylene with a minor amount of one or more comonomers selected from C.sub.3 to C.sub.10 alpha olefins such as butene-1pentene-1hexene-1, 4-methyl-pentene-1, octene-1, etc. in which the molecules thereof comprise long chains with few side chains or branched structures achieved by low pressure polymerization. LLDPE has a density preferably in the range from about 0.911 g/cc to about 0.935 g/cc, and more preferably in the range of from about 0.912 g/cc to about 0.928 g/cc. Also, very low density linear low density polyethylenes (VLDPE) may be employed, and such have a density from about 0.910 g/cc to about 0.860 g/cc, or even lower.
The term "ethylene vinyl acetate copolymer" (EVA) as used herein, for a type of polyolefin refers to a copolymer formed from ethylene and vinyl acetate (VA) monomers. The ethylene derived units in the copolymer are present in major amounts by weight and the VA derived units in the copolymer are present in minor amounts by weight. For film making purposes, it is preferred that the VA content of the EVA be from about 3% to about 25%.
The term "polypropylene" (PP) as used herein for a type of polyolefin refers to polymers of propylene, and includes homopolymers, copolymers, such as for example block, graft, random, and alternating, copolymers, terpolymers etc. and blends and modifications thereof.
The term "ethylene/alkyl-acrylate copolymer" (EA1Acr) as used herein refers to a copolymer formed from ethylene and alkyl acrylate wherein the alkyl moiety has 1 to 8 carbon atoms and the ethylene derived units in the copolymer are present in major amounts by weight and the alkylacrylate derived units in the copolymer are present in minor amounts by weight. Thus, the term "ethylene/methyl acrylate copolymer" (EMA) as used herein refers to a copolymer formed from ethylene and methyl acrylate monomers. The term "ethylene/ethyl acrylate copolymer" (EEA) as used herein refers to a copolymer formed from ethylene and ethyl acrylate monomers. The term "ethylene/butyl acrylate copolymer" (EBA) as used herein refers to a copolymer formed from ethylene and butyl acrylate monomers. Many suitable EBA's are commercially available and these have a butyl acrylate content from about 3% up to about 18% by weight. USI is a commercial supplier of Resin No. 4895, which is an EBA having about 3% by weight butyl acrylate and a melt index of about 3 and a melting point of about 106.degree. to 110.degree. C.
Blends of all families of polyolefins, such as blends of EVA, EA1Acr, PP, LDPE, HDPE, VLDPE, and LLDPE, may also be advantageously employed.
Measuring the antistatic property: The antistatic property is exhibited by the ability of the polymer containing the agent to promote static charge decay, i.e. to dissipate a static charge. The polymer alone will not dissipate a static charge, but the polymer containing the agent is able to dissipate 99% of an applied static charge of .+-.5000 volts direct current (Vdc) in a short amount of time, i.e. less than 3 seconds, more preferably less than 2 seconds (2000 milliseconds). Federal Test Method Standard 101c, Method 4046.1, "Electrostatic Properties of Materials" states less than 2000 ms and thus it is preferred to have a material that complies with 101c. Decay meters for measuring the time for dissipation of the applied volts are commercially available, such as the 406c static decay meter supplied by Electrotech Systems, Inc. Unless otherwise indicated in the Examples below, the films, prior to testing, were equilibrated at less than about 15% relative humidity (RH) at about room temperature (RT) for about 24 hours.
Some films were tested for triboelectric charge generation. Two aluminum plates were used for this test. Plate 1 was a ground plane and was about 12 inches (30.5 cm).times.12 inches (30.5 cm).times.3/16 inch (0.5 cm) in size. Plate 2 was about 4 inches (10.2 cm).times.3 inches (7.6 cm).times.3/16 inch (0.5 cm) in size and had a non-contacting static voltmeter attached to it. Plate 2 also had an insulating rod or handle attached to it to allow the person performing the test to separate the plates without touching them and affecting the charge accumulation. The material under test was placed on Plate 1. Plate 2 was pushed against the material to make intimate contact with the sample. Plate 2 was then separated rapidly up against a stop, while the sample remained in contact with Plate 1. This stop limited the travel to approximately 1 inch (2.54 cm) of separation between the two plates. This procedure was repeated 4 times and the voltmeter readings averaged. The principle of this measurement is that when two materials are placed in contact and then separated they give up or take on electrons thus leaving both materials with a net charge. Since one of the materials in the test is a metal plate, the charge on it can be measured by a static voltmeter. The magnitude and polarity of the charge is then an indicator of the tribo-charging propensity of the material under test. A desirable reading is between about -200 volts and +200 volts.
Some of the films were tested for surface resistivity and volume resistivity according to ASTM D257. There is not necessarily a correlation between the surface or volume resistivity of a film and the ability of a film to decay or dissipate charges. Thus, the term "antistatic" as used herein describes a material which can dissipate 99% of an applied static charge of .+-.5000 Vdc in a short amount of time, preferably a static decay time less than about 3 seconds, more preferably less than about 2 seconds (Federal Test Method Standard 101c, Method 4046.1, "Electrostatic Properties of Materials"). If the material also happens to have an antistatic resistivity, i.e. a surface resistivity of about 10.sup.5 to 10.sup.12 ohms/square as further described below, then that material will be described using the term "antistatic surface resistivity."
The Department of Defense and the Electronics Industry Association have standards on surface resistivity of a material in ohms/square as follows:
______________________________________Surface Resistivity Ranges (ohms/square) Antistatic orInsulative Static Dissipative Conductive______________________________________greater than 10.sup.12 10.sup.12 to 10.sup.5 less than 10.sup.5______________________________________
It is noted that some of the 5-layer films of the invention, as illustrated by Examples XIII and XIV below, have both a preferred static decay time of about 3000 milliseconds or less and a static dissipative (as opposed to insulative) surface resistivity of 10.sup.12 to 10.sup.5 ohms/square, even after a 24-hour water shower or after 12 days in a hot oven. Thus these 5-layer films are permanently antistatic by the definition of static decay time and permanently antistatic by the definition of antistatic surface resistivity; neither the 24-hour water shower nor the 12-day hot oven takes out the "antistatic" characteristic.
Some of the films were tested for crazing, i.e. polycarbonate compatability, which was a test developed by General Electric Company, published as their "LEXAN (.RTM.) Resin Technifacts" T-47 test method. This test consists of bending or flexing test coupons or bars of LEXAN (.RTM.) about 1/8 inch (0.32 cm) thick on metal jigs to several known stress levels of about 500 to 3400 psi (35 to 239 kg/cm.sup.2) and the material being evaluated is then applied to the stressed coupons and the combination maintained at several temperatures for 5 days. The temperatures are about 73.degree. F. (22.8.degree. C.), 120.degree. F. (48.9.degree. C.), 158.degree. F. (70.degree. C.), and 185.degree. F. (85.degree. C.). A comparison of the strain independent of the material being evaluated, the radius of the curvature of the upper surface of the jig, and the stress level of the LEXAN (.RTM.) bars is as follows:
______________________________________STRESS LEVEL 1/8" RADIUS OF STRAIN INDE-THICK BARS UN- UPPER SUR- PENDENT OFFILLED LEXAN RESIN FACE OF JIG MATERIALPSI kg/cm.sup.2 Inches cm percent______________________________________ 500 35 42.437 107.8 0.15 750 53 28.270 71.8 0.221000 70 21.187 53.8 0.291250 88 17.063 43.3 0.371500 105 14.103 35.8 0.441750 123 12.080 30.7 0.512000 141 10.563 26.8 0.592250 158 9.381 23.8 0.662500 176 8.437 21.4 0.742750 193 7.664 19.5 0.813000 211 7.020 17.8 0.883400 239 6.187 15.7 1______________________________________
At the end of the exposure, the bars are visually checked for crazing. Results are reported as the maximum stress to which the bar can be subjected while in contact with the particular environment without the occurrence of crazing. It is desired that the film exhibit no crazing or only very slight crazing at a temperature 158.degree. F. (70.degree. C.) and stress of 1700 psi, more preferably a temperature of 185.degree. F. (85.degree. C.) and stress of 1700 psi.
Manufacture of Films: Typically, in the manufacture of films, a suitable polymer usually in the form of pellets or the like, is brought into a heated area where the polymer feed is melted and heated to its extrusion temperature and extruded as a tubular "blown bubble" through an annular die. Other methods, such as "slot die" extrusion wherein the resultant extrudate is in planar, as opposed to tubular, form are also well known. If heat shrinkable film is desired, then after extrusion, the film is typically cooled and then reheated and stretched, i.e. oriented by "tenter framing" or by inflating with a "trapped bubble", to impart the heat-shrinkable property to the film, as is further described below. If desired, high energy irradiation, typically via an electron beam, preferably takes place prior to the stretching for orienting the film. However, for the present invention, such irradiation is not necessary since a very suitable packaging film having permanent antistatic characteristics is obtained without irradiation. Below, first is described the general process for making and orienting film. Then irradiation is described.
More particularly, manufacturing of films may be accomplished as follows. For instance, the manufacture of shrink films may be generally accomplished by extrusion (single layer films) or coextrusion (multilayer films) of thermoplastic resinous materials which have been heated to or above their flow or melting point from an extrusion or coextrusion die in, for example, either tubular or planar (sheet) form, followed by a post extrusion cooling. The stretching for orientation may be conducted at some point during the cool down and while the film is still hot and within its orientation temperature range followed by completing the cooling. Alternatively, after the post extrusion cooling, the relatively thick "tape" extrudate is then reheated to a temperature within its orientation temperature range and stretched to orient or align the crystallites and/or molecules of the material and then cooled. The orientation temperature range for a given material or materials will vary with the different resinous polymers and/or blends thereof which comprise the material. However, the orientation temperature range for a given thermoplastic material may generally be stated to be below the crystalline melting point of the material but above the second order transition temperature (sometimes referred to as the glass transition point) thereof. Within this temperature range, the material may be effectively oriented. The terms "orientation" or "oriented" are used herein to describe generally the process steps and resultant product characteristics obtained by stretching and immediately cooling a resinous thermoplastic polymeric material which has been heated to a temperature within its orientation temperature range so as to revise the intermolecular configuration of the material by physical alignment of the crystallites and/or molecules of the material to improve certain mechanical properties of the film such as, for example, shrink tension and orientation release stress. Both of these properties may be measured in accordance with ASTM D 2838-81. When the stretching force is applied in one direction monoaxial orientation results. When the stretching force is simultaneously applied in two directions biaxial orientation results. The term oriented is also herein used interchangeably with the term "heat-shrinkable" with these terms designating a material which has been stretched and set by cooling while substantially retaining its stretched dimensions. An oriented (i.e. heat-shrinkable) material will tend to return to its original unstretched (unextended) dimensions when heated to an appropriate elevated temperature.
An "oriented" or "heat-shrinkable" material is defined herein as a material which, when heated to an appropriate temperature above room temperature (for example 96.degree. C.), will have a free shrink of about 5% or greater in at least one linear direction.
Returning to the basic process for manufacturing the film as discussed above, it can be seen that the film, once extruded (or coextruded if it is a multi-layer film) and initially cooled, is then reheated to within its orientation temperature range and oriented by stretching. The stretching to orient may be accomplished in many ways such as, for example, by "trapped bubble" techniques or "tenter framing". These processes are well known to those in the art and refer to orientation procedures whereby the material is stretched in the cross or transverse direction (TD) and/or in the longitudinal or machine direction (LD or MD). After being stretched, the film is quickly cooled while substantially retaining its stretched dimensions to cool the film rapidly and thus set or lock-in the oriented molecular configuration.
Of course, if a film having little or no orientation is desired, e.g. non-oriented or non-heat shrinkable film, the film may be formed from a non-orientable material or, if formed from an orientable material may be formed from a tube by using a "trapped bubble" technique commonly known as the "hot blown" technique. In forming a hot blown film, the tube is not cooled initially after extrusion or coextrusion but rather is first stretched by a hot blown bubble essentially immediately after extrusion while the tube is still at an elevated temperature above the orientation temperature range of the material. Thereafter, the film is cooled, by well-known methods. Those of skill in the art are well familiar with this process and the fact that the resulting film has substantially unoriented characteristics. Other methods for forming unoriented films are well known. Exemplary, is the method of cast extrusion or cast coextrusion which, likewise, is well known to those in the art.
Whichever film has been made (the non-oriented molecular configuration or the stretch-oriented "heat-shrinkable" molecular configuration), it may then be stored in rolls and utilized to package a wide variety of items. If the material was manufactured by "trapped bubble" techniques the material may still be in tubular form or it may have been slit and opened up to form a sheet of film material. In this regard, the product to be packaged may first be enclosed in the material by heat sealing the film to itself where necessary and appropriate to form a pouch or bag and then inserting the product therein. Alternatively, a sheet of the material may be utilized to overwrap the product, or the product may be vacuum skin packaged with the material. These packaging methods are all well known to those of skill in the art.
If the material is of the heat-shrinkable, i.e. "oriented", type, then after wrapping, the enclosed product may be subjected to elevated temperatures, for example, by passing the enclosed product through a hot air tunnel. This causes the enclosing heat shrinkable film to shrink around the product to produce a tight wrapping that closely conforms to the contour of the product. As stated above, the film sheet or tube may be formed into bags or pouches and thereafter utilized to package a product. In this case, if the film has been formed as a tube it may be preferable first to slit the tubular film to form a film sheet and thereafter form the sheet into bags or pouches. Such bag or pouch forming methods, likewise, are well known to those of skill in the art.
Alternative methods of producing films of this type are known to those in the art. One well-known alternative is the method of forming a multi-layer film by an extrusion coating rather than by an extrusion or coextrusion process as was discussed above. In extrusion coating a first tubular layer is extruded and thereafter an additional layer or layers is simultaneously or sequentially coated onto the outer surface of the first tubular layer or a successive layer.
The above general outline for manufacturing of films is not meant to be all inclusive since such processes are well known to those in the art. For example, see U.S. Pat. Nos. 4,274,900; 4,229,241; 4,194,039; 4,188,443; 4,048,428; 3,555,604; 3,741,253; 3,821,182 and 3,022,543. The disclosures of these patents are generally representative of such processes and are hereby incorporated by reference.
Many other process variations for forming films are well known to those in the art. For, example, conventional pressing, thermoforming or laminating techniques (including corona laminating) may be employed. For instance, multiple layers may be first coextruded with additional layers thereafter being laminated thereon, or two multi-layer tubes may be coextruded with one of the tubes thereafter being laminated onto the other.
If a heat shrinkable, i.e. "oriented", film is desired, after extrusion and cooling, then after irradiation (or without irradiation), the tube may then be heated to soften it, and then the softened tube is passed through pinch rolls and stretch oriented by the trapped blown bubble technique discussed above.
Irradiation, if desired, may be accomplished by the use of high energy electrons, ultra violet radiation, X-rays, gamma rays, beta particles etc. Preferably, electrons are employed up to about 20 megarads (Mr) dosage level. The irradiation source can be any electron beam generator operating in a range of about 150 kilovolts to about 6 megavolts with a power output capable of supplying the desired dosage. The voltage can be adjusted to appropriate levels which may be for example 1,000,000 or 2,000,000 or 3,000,000 or 6,000,000 or higher or lower. Many apparatus for irradiating films are known to those of skill in the art. The irradiation is usually carried out at a dosage between about 1 Mr (10 kilogrey) and about 20 Mr (200 kilogrey), with a preferred dosage range of about 2 Mr (20 kilogrey) to about 12 Mr (120 kilogrey). Irradiation can be carried out conveniently at room temperature, although higher and lower temperatures, for example, 0.degree. C. to 60.degree. C. may be employed.
It is also generally well known in the art that irradiation, such as by electron beam irradiation, of certain polymeric film materials generally results in a material having improved heat shrink properties, abuse resistance, structural integrity, tensile strength, puncture resistance, and/or delamination resistance. Such physical toughness improvements from irradiation, are discussed in U.S. Pat. No. 3,022,543 (1962) to Baird et al, U.S. Pat. No. 4,178,401 (1979) to Weinberg and U.S. Pat. No. 3,741,253 to Brax et al.
Advantageously, an outside polymeric layer of a film may include a small amount of about 10% by weight or less, more desirably about 7% by weight or less of an antiblock, to help alleviate any tackiness. A suitable antiblock is EPE 8160 supplied by Teknor Apex.
The following Examples are intended to illustrate the preferred embodiments of the invention and comparisons thereto. It is not intended to limit the invention thereby.
Unless indicated otherwise in the Examples, the testing for static decay time (SDT) was done after equilibration for 24 hours, at about room temperature (RT), at less than about 15% relative humidity (RH). Also it is noted that sometimes SDT testing was done to samples that had been subjected to abuse such as 1 to 12 days in a hot, about 160.degree. F. (71.degree. C.), oven or a 24-hour water shower. Where the oven is designated as "humid", a beaker of water had been kept in the oven with the film sample during testing to maintain a "humid" atmosphere; otherwise the oven was simply a "dry" or "ambient" oven, without any water beaker.
__________________________________________________________________________MATERIALS EMPLOYED IN THE EXAMPLES__________________________________________________________________________ANTIBLOCK INGREDIENTS SUPPLIER__________________________________________________________________________EPE 8160 Polyethylene Containing Teknor Apex Micron Sized Silica__________________________________________________________________________LLDPE MI* DENSITY COMONOMER SUPPLIER__________________________________________________________________________DOWLEX 1.1 0.920 Octene Dow Chemical2045.03__________________________________________________________________________EVA MI % VA COMONOMER SUPPLIER__________________________________________________________________________LD318.92 2.0 9 Vinyl Acetate Exxon__________________________________________________________________________ % BY WEIGHT % BY WEIGHTEAA MI ACRYLIC ACID ETHYLENE SUPPLIER__________________________________________________________________________PRIMACOR 1.5 9 91 Dow Chemical1410PRIMACOR 300 20 80 Dow Chemical5981__________________________________________________________________________ZINC METHACRYLATEIONOMER OF EMAA FORMULA SUPPLIER__________________________________________________________________________Surlyn 1650 Partially zinc neutralized du Pont ethylene methacrylic acid copolymer__________________________________________________________________________QA FORMULA SUPPLIER__________________________________________________________________________Q-14-2 [C.sub.10 H.sub.21 OC.sub.3 H.sub.6 N(C.sub.2 H.sub.4 OH).sub.2 CH.sub.3 ]'Cl.sup.- Tomah Div. of ExxonEmerstat [H(CH.sub.2).sub.8-20 ](C.sub.2 H.sub.5)N[(C.sub.2 H.sub.4 O).sub.1-4 H].sub.2.sup.+ C.sub.2 H.sub.5 OSO.sub.3.sup.- Emery Industries6660Cyastat C.sub.11 H.sub.23 CONHC.sub.3 H.sub.6 N(CH.sub.3).sub.3.sup.+ CH.sub.3 OSO.sub.3.sup.- CyanamidLarostat Modified soyadimethyl Jordan/PPG/Mazer264A ethylammonium ethosulfateAnhydrous__________________________________________________________________________TA FORMULA SUPPLIER__________________________________________________________________________Empigen AB Lauryl dimethylamine Albright & WilsonEmpigen AY H(CH.sub.2).sub.10-18 (OC.sub.2 H.sub.4).sub.n N(CH.sub.3).s ub.2 Albright & WilsonE-14-2 C.sub.10 H.sub.21 OC.sub.3 H.sub.6 N(C.sub.2 H.sub.4 OH).sub.2 Tomah Div., ExxonDMCA N,N-dimethylcocoamine Akzo Chemie__________________________________________________________________________ACID ORALKYLATINGAGENT FORMULA SUPPLIER__________________________________________________________________________MSA Methanesulfonic Acid AldrichDBSA H(CH.sub.2).sub.12-18 C.sub.6 H.sub.4 SO.sub.3 H Alfa/Morton ThiokolDES Diethyl Sulfate Aldrich__________________________________________________________________________ *MI is melt index.

EXAMPLE I
LLDPE and EAA (Primacor 5981) were premixed in parts by weight and then blended therein with heating was a QA in parts by weight. The resultant mix of LLDPE+EAA+QA was then further blended in an amount of 331/3% by wt. with EAA (Primacor 1410) in an amount of 662/3% by wt. and that was hot blown into an extruded, tubular film. Films were about 1.5 to 2 mils (0.04 to 0.05 mm) thick. What was made is listed in Table IA.
TABLE IA__________________________________________________________________________60 parts by wt LLDPE [Dowlex2045.03]15 parts by wt QA [Q-14-2] 331/3% by wt mix of LLDPE + EAA + QA30 parts by wt EAA [Primacor 5981] 662/3% by wt EAA [Primacor1410] 100% Resultant Film__________________________________________________________________________
Then, the following electrical measurements were taken on samples of film as reported in Table IB.
TABLE IB______________________________________SAMPLE______________________________________A Static Decay Time as is 180 msB Static Decay Time after 24 992 ms hours water showerC Static Decay Time after days 3 days 783 ms in hot oven at 71.degree. C. 5 days 1149 ms 9 days 7340 ms 12 days 14683 msD Surface resistivity as is 2 .times. 10.sup.10 ohms/squareE Volume resistivity as is 8.7 .times. 10.sup.10 ohm-cm after 24 hr. water shower 1.5 .times. 10.sup.12 ohm-cm after 12 day dry oven 1.8 .times. 10.sup.14 ohm-cm______________________________________
The results show the film performed well as an antistatic film both in terms of static decay time and resistivity, and was resistant to abusive aging, except that it did not survive 12 days in a hot oven with a desirable SDT of about 3000 ms or less.
EXAMPLE II
Films were made as in Example I except that this time the QA was Emerstat 6660 supplied by Emery Industries. The resultant film that was made is as listed in Table IIA below.
TABLE IIA__________________________________________________________________________60 parts by wt LLDPE [Dowlex 2045.03]15 parts by wt QA [Emerstat 6660] 331/3% by wt Mix of LLDPE + EAA + QA30 parts by wt EAA [Primacor 5981] 662/3% by wt EAA [Primacor1410] 100% Resultant Film__________________________________________________________________________
Then, the following electrical measurements were taken on samples of film as reported in Table IIB.
TABLE IIB______________________________________SAMPLE______________________________________A Static Decay Time as is 209 msB Static Decay Time after 24 539 ms hours water showerC Static Decay Time after days 3 days 78 ms in hot oven at 71.degree. C. 5 days 97 ms 9 days 361 ms 12 days 195 msD Surface resistivity as is 1.2 .times. 10.sup.11 ohms/ squareE Volume resistivity as is 2.8 .times. 10.sup.12 ohm-cm after 24 hr. water shower 2.2 .times. 10.sup.12 ohm-cm after 12 day hot dry oven 1.3 .times. 10.sup.12 ohm-cm______________________________________
The results show the film performed well as an antistatic film both in terms of decay time and resistivity, and was resistant to abusive aging.
EXAMPLE III
By blending with heat using a Berstorff twin screw extruder, a premix of pellets was made. First, 60 parts by weight EVA [LD318.92] and 30 parts by weight EAA [Primacor 5981] were mixed, and then added thereto was 15 parts by wt. QA [Emerstat 6660]. The resultant EVA+EAA+QA was then further blended with more polymer, and hot blown, 5-layer, extruded, tubular film having a thickness of about 4 mil (0.102 mm) was made. The ingredients of each layer were as recited in Table IIIA and are in % by weight.
TABLE IIIA__________________________________________________________________________OUTSIDE INTERIOR CORE INTERIOR OUTSIDELAYER 1 LAYER 2 LAYER 3 LAYER 4 LAYER 5__________________________________________________________________________95% EVA 662/3% EVA 90% LLDPE 662/3% EVA 95% EVA 5% Anti- 331/3% Mix of 10% Mix of 331/3% Mix of 5% Anti-block EVA + EAA + QA EVA + EAA + QA EVA + EAA + QA block__________________________________________________________________________
Then, the following electrical measurements were taken on samples of film as reported in Table IIIB.
TABLE IIIB__________________________________________________________________________Abuse Static Decay Time(ms)Treatment 1 Hr. 24 Hr.Noted Equilibration Equilibrationor Film Ohms/square Ohms-cm for the Film for the FilmTested Surface Volume as is or after as is or after TriboAs is Resistivity Resistivity abuse treatment abuse treatment Volts__________________________________________________________________________As is 1.8 .times. 10.sup.13 7.0 .times. 10.sup.13 111 222 -1.2 1 Hr. 1.4 .times. 10.sup.14 2.1 .times. 10.sup.14 7 177 181.9Shower 3 Hr. 5.7 .times. 10.sup.14 1.6 .times. 10.sup.14 Less Than 115 161.5Shower MMSDT*24 Hr. 6.4 .times. 10.sup.12 4.4 .times. 10.sup.14 Less Than 102 76.4Shower MMSDT24 Hr. 1.6 .times. 10.sup.13 2.5 .times. 10.sup.14 183 328 48.6Hot HumidOvenHotDry OvenDay 1 NT** NT 332 185 NTDay 2 NT NT 272 178 NTDay 3 NT NT 180 164 NTDay 4 NT NT 287 Won't Accept NT Full ChargeDay 5 NT NT 148 115 NTDay 6 NT NT 164 348 NTDay 7 NT NT 359 200 NTDay 8 NT NT NT 455 NTDay 9 NT NT 400 97 NTDay 10 NT NT 213 259 NTDay 11 NT NT 247 93 NTDay 12 4.2 .times. 10.sup.13 1.0 .times. 10.sup.16 299 164 19.3__________________________________________________________________________ *MMSDT = minimum measurable static decay time **NT = not tested
It is noted from Table IIIB that while the resistivity measurements bordered between antistatic and insulative (i.e. 10.sup.13 to 10.sup.16), the static decay times were excellent, well under the preferred 2000 ms or less, even after the hot oven abuse or the water shower abuse. As for the film sample that would not accept a full cahrge after day 4 of the hot dry oven, while it is not intended to be bound to any theory, it is believed this happened due to a mechanical difficulty in that the sample was placed in the test meter in a curved or bowed position instead of a flat, taut position, with respect to the sensing electrode. (It is also noted that 2 similar 5-layer films were made, the only difference being that core layer 3 contained only 5% of the premix of EVA+EAA+QA or contained no premix of EVA+EAA+QA. These similar films performed substantially the same, but for not accepting a full charge during the SDT test after 10 to 12 days in a hot dry oven. While it is not intended to be bound to any theory, it is believed this was also due to a mechanical difficulty in that samples were placed in the test meter in a bowed position.)
EXAMPLE IV
Six tubes of a 5-layer film were made as in Example III, but containing the following amounts of ingredients for each layer as recited in Table IVA below:
TABLE IVA__________________________________________________________________________Layer 1 Layer 2 Layer 3 Layer 4 Layer 5__________________________________________________________________________90% EVA 662/3% EVA 90% LLDPE 662/3% EVA 90% EVA10% Anti- 331/3% Mix of 10% Mix of 331/3% Mix of 10% Anti-block EVA + EAA + QA EVA + EAA + QA EVA + EAA + QA block__________________________________________________________________________
Samples of the 6 tubes of the 5-layer film were tested for static decay time after 1 hour of equilibration and the results were as reported in Table IVB below:
TABLE IVB______________________________________SAMPLE OF FILM SDT (ms)______________________________________Tube 1 14Tube 2 43Tube 3 9Tube 4 23Tube 5 31Tube 6 18______________________________________
As can be seen, excellent SDT's were obtained.
Next 3 sets of 4 samples each of the 6 tubes of 5-layer Film were subjected to a 24-hour water shower. Then, each set was equilibrated for 1 hour, 24 hours, and 48 hours, respectively and then checked for SDT. The results were as reported in Table IVC below:
TABLE IVC______________________________________ SDT (ms) After 1 Hour After 24 Hours After 48 HoursTube Sample Equilibration Equilibration Equilibration______________________________________1 1 Less Than 24 29 MMSDT*1 2 Less Than 23 41 MMSDT1 3 Less Than 15 23 MMSDT1 4 Less Than 16 24 MMSDT2 1 Less Than 60 54 MMSDT2 2 Less Than 54 50 MMSDT2 3 Less Tnan 71 66 MMSDT2 4 Less Than 70 71 MMSDT3 1 Less Than 18 16 MMSDT3 2 Less Than 17 20 MMSDT3 3 Less Than 13 20 MMSDT3 4 Less Than 11 18 MMSDT4 1 Less Than 76 78 MMSDT4 2 Less Than 38 32 MMSDT4 3 Less Than 53 60 MMSDT4 4 Less Than 84 85 MMSDT5 1 Less Than 69 65 MMSDT5 2 Less Than 84 76 MMSDT5 3 Less Than 32 30 MMSDT5 4 Less Than 33 34 MMSDT6 1 Less Than 106 108 MMSDT6 2 Less Than 114 136 MMSDT6 3 Less Than 64 92 MMSDT6 4 Less Than 152 161 MMSDT______________________________________ *MMSDT = Minimum measurable static decay time
As can be seen, when film was left to equilibrate for 24 hours, which is as per the specifications of Federal Test Method 101c, then excellent SDT's were obtained. Also, the film retained excellent SDT's even after further equilibration. Thus, these films indeed survived the vigorous abuse of a 24 hour water shower.
EXAMPLE V
For polycarbonate compatability, i.e. crazing tests, also a mono-layer film was extruded from the pellets of premix having the ingredients as recited in Table V-A below:
TABLE V-A______________________________________60 parts by wt LLDPE [Dowlex2045.03]15 parts by wt QA [Q-14-2]30 parts by wt EAA [Primacor 5981]______________________________________
and then both a sample from Tube 1 of the 5-layer film of Example IV and a sample from the mono-layer film were tested for crazing of polycarbonate. The results are summarized in Table V-B below:
TABLE V-B______________________________________Test Conditions Tube 1 of Pressure 5-layer Mono-layerTemperature PSI kg/cm.sup.2 Film Film______________________________________ 73.degree. F.(22.8.degree. C.) 1000 70 N N 1700 120 N N 2000 141 N N 2500 176 N N 3400 239 N N 120.degree. F.(48.9.degree. C.) 1000 70 N N 1700 120 N N 2000 141 N N 2500 176 N N 3400 239 VSLC N158.degree. F.(70.degree. C.) 1000 70 N N 1700 120 N N 2000 141 N VSLC 2500 176 N VSLC 3400 239 VSLC VSLC185.degree. F.(85.degree. C.) 1000 70 N N 1700 120 N N 2000 141 N VSLC 2500 176 VSLC VSLC 3400 239 VSLC SLC______________________________________ N = NO ATTACK VSLC = VERY SLIGHT CRAZE SLC = SLIGHTLY CRAZED
As can be seen the 5-layer film D performed excellently and did not exhibit very slight crazing till the most extreme condition of 3400 psi, whereas the mono-layer film only showed very slight crazing beginning at a less extreme condition of 2000 psi.
EXAMPLE VI
Quaternary amine additives QA1-QA5 (below) were prepared by mixing the following TA's (tertiary amines) and acids or alkylating agents without solvent for the indicated time/temp.
TABLE VIA__________________________________________________________________________ Acid or Alkylating Time/QA Formula TA (gms) Agent (gms) Temp.__________________________________________________________________________QA1 H(CH.sub.2).sub.12 N(CH.sub.3).sub.2 H.sup.+ Empigen MSA 10 min./ CH.sub.3 SO.sub.3.sup.- AB (3.2) 60.degree. C. (8.8)QA2 H(CH.sub.2).sub.12 N(CH.sub.3).sub.2 C.sub.2 H.sub.5.sup.+ Empigen DES 16 hr./ C.sub.2 H.sub.5 OSO.sub.3.sup.- AB (5.2) 60.degree. C. (8.8)QA3 H(CH.sub.2).sub.12-18 (OC.sub.2 H.sub.4).sub.n Empigen MSA 10 min./ N(CH.sub.3).sub.2 H.sup.+ CH.sub.3 SO.sub.3 AY (3.2) 60.degree. C. (14.4)QA4 C.sub.10 H.sub.21 OC.sub.3 H.sub.6 N(C.sub.2 H.sub.4 OH).sub.2 H.sup.+ E14-2 MSA 10 min./ CH.sub.3 SO.sub.3.sup.- (12.4) (3.2) 60.degree. C.QA5 C.sub.10 H.sub.21 OC.sub.3 H.sub.6 N(C.sub.2 H.sub.4 OH).sub.2 H.sup.+ E14-2 DBSA 10 min./ H(CH.sub.2).sub.12-18 C.sub.6 H.sub.4 SO.sub.3.sup. (12.4) (10.0) 60.degree. C.__________________________________________________________________________
Several quaternary amines (QA, 3.6 parts by weight) were blended with Primacor 5981 ethylene-acrylic acid copolymer (7.1 parts by weight) and LD318.92 ethylene-vinyl acetate copolymer (89.3 parts by weight). The blending was carried out by kneading at 130.degree.-150.degree. C. for approximately 20 minutes in a Brabender Plasticorder (.RTM.) mixer. Samples of the resultant materials were pressed at approximately 1,000 psi (70 kg/cm) between platens heated to 150.degree. C. Monolayer films of about 3 inches (7.6 cm) by 5 inches (12.7 cm) by 0.005 inch (0.013 cm) were thus obtained. The SDT of each film was determined before and after a 24-hour water shower. The results are summarized below:
TABLE VIB______________________________________ SDT Before SDT AfterSample QA Shower (ms) Shower (ms)______________________________________1 QA5 490 24502 QA4 40 10003 QA1 90 5104 QA2 100 880______________________________________
These results demonstrate that the performance of the films tested was slightly degraded by an extensive water shower, but still less than 3000 ms for Sample 1 and less than the preferred 2000 ms for Samples 2, 3, and 4.
Next, several quaternary amines (QA 5.0 parts by weight) were blended with Primacor 1410 ethylene-acrylic acid copolymer (71.3 parts by weight) and LD318.92 ethylene-vinyl acetate copolymer (23.7 parts by weight). The blending and subsequent film preparation and testing were carried out as described above for the samples reported in Table VIB. The results were as follows:
TABLE VIC______________________________________ SDT Before SDT AfterSample QA Shower (ms) Shower (ms)______________________________________5 Cyastat LS 420 5006 Larostat 264A 590 6307 QA3 110 6508 QA1 550 7209 QA2 70 180______________________________________
These results demonstrate that there was almost no loss of static decay performance after extensive water washing, and all SDT's were less than the preferred 2000 ms.
To demonstrate further permanence of these materials, the same samples 5 through 9 from after the water shower were further aged for 12 days in an oven at 70.degree. C. and ambient humidity, i.e. a "dry" oven as there was no water beaker. SDT, surface resistivity, and volume resistivity for the resulting films are given below:
TABLE VID______________________________________RESULTS AFTER WATER SHOWER AND 12-DAYAGING AT 70.degree. C. Surface Resistivity Volume ResistivitySample SDT (ms) (ohms/square) (ohm-cm)______________________________________5 1660 1.1 .times. 10.sup.13 4.4 .times. 10.sup.126 1790 4.0 .times. 10.sup.12 1.3 .times. 10.sup.127 330 3.8 .times. 10.sup.11 7.7 .times. 10.sup.118 790 4.7 .times. 10.sup.11 9.1 .times. 10.sup.119 120 3.8 .times. 10.sup.11 1.1 .times. 10.sup.11______________________________________
The results demonstrate that films produced with 5% of a QA additive in an EAA/EVA resin show excellent static decay times, surface resistivities, and volume resistivities, and are highly permanent, i.e., insensitive to water washout of additive and 12-day aging at elevated temperature.
COMPARATIVE EXAMPLE VII
A comparative sample was run for comparison with Sample 5 as reported in Tables VIC and VID above to show the result of omitting the ethylene-acrylic acid copolymer from the formulation. Thus, Cyastat LS (5.0 parts by weight) and LD318.92 ethylene-vinyl acetate copolymer (95.0 parts by weight) were kneaded at 130.degree.-150.degree. C. in a Brabender Plasticorder (.RTM.) mixer. Effective mixing of these ingredients was never obtained, even after 4 hours of kneading. Reduction of the additive content to 2.5 parts by weight did not solve the problem. This demonstrates that an acid copolymer containing carboxylic acid moieties (i.e. the ethylene-acrylic acid copolymer) plays a critical role in compatibilizing the polyolefin with the ionic additive.
Another comparative sample was run but this time for comparison with Sample 9 as reported in Tables VIC and VID above to show the result of omitting the ethylene-acrylic acid copolymer from the formulation. Thus, QA2 (1.5 parts by weight) and LD318.92 ethylene-vinyl acetate copolymer (98.5 parts by weight) were kneaded at 130.degree.-150.degree. C. in a Brabender Plasticorder (.RTM.) mixer. Effective mixing of these ingredients was obtained, finally after 4 hours of kneading. Some of the resultant material was pressed at approximately 1000 psi (70 kg/cm.sup.2) between platens heated to 150.degree. C. Mono-layer film of about 3.times.5.times.0.005 inches (7.6.times.12.7.times.0.013 cm) was thus obtained. The SDT of each film was determined before and after a 24-hour water shower. The results are summarized below:
TABLE VII______________________________________SDT Before SDT AfterShower (ms) Shower (ms)______________________________________580 over 30000______________________________________
Also, after the water shower, the film held a charge of 10 kilovolts, which indicates the antistatic property was lost. This demonstrates that an acid copolymer containing carboxylic acid moieties (i.e. the ethylene-acrylic acid copolymer) plays a critical role in providing permanent antistatic characteristics, i.e. enabling the film still to have a SDT less than about 3000 ms, more preferably less than about 2000 ms, after a 24-hour water shower.
EXAMPLE VIII
Quaternary amine QA2 (as defined in Table VIA, 6.0 parts) was blended with Surlyn 1650 partially zinc neutralized ethylene-methacrylic acid-zinc methacrylate ionomer (23.5 parts) and LD318.92 ethylene-vinyl acetate copolymer (70.5 parts). The blending and subsequent testing were carried out as described in Example VI. The results were as follows:
______________________________________Before Water Shower:SDT (ms) 470Surface Resistivity (ohms/square) 1.7 .times. 10.sup.12Volume Resistivity (ohm-cm) 2.5 .times. 10.sup.12After 24-Hour Water Shower:SDT (ms) 880Surface Resistivity (ohms/square) 7.6 .times. 10.sup.12Volume Resistivity (ohm-cm) 3.6 .times. 10.sup.10After 24-Hour Water Shower Followed by 12-Day/70.degree. C. Aging:SDT (ms) 460Surface Resistivity (ohms/square) 1.7 .times. 10.sup.12Volume Resistivity (ohm-cm) 2.5 .times. 10.sup.12______________________________________
These results demonstrate that the film showed excellent static decay time, surface and volume resistivity, and resistance to water washout of additive and aging at elevated temperature.
EXAMPLE IX
Quaternary amine QA1 (5.0 parts) was blended with Surlyn 1650 partially zinc neutralized ethylene-methacrylic acid-zinc methacrylate ionomer (23.7 parts) and LD318.92 ethylene-vinyl acetate copolymer (71.3 parts). The blending and subsequent testing were carried out as described in Example VI. The results were as follows:
______________________________________Before Water Shower:SDT (ms) 230Surface Resistivity (ohms/square) 5.2 .times. 10.sup.11Volume Resistivity (ohm-cm) 1.4 .times. 10.sup.12After 24-Hour Water Shower:SDT (ms) 150Surface Resistivity (ohms/square) 6.5 .times. 10.sup.11Volume Resistivity (ohm-cm) 1.1 .times. 10.sup.12After 24-Hour Water Shower Followed by 12-Day/70.degree. C. Aging:SDT (ms) 80Surface Resistivity (ohms/square) 5.9 .times. 10.sup.11Volume Resistivity (ohm-cm) 5.9 .times. 10.sup.12______________________________________
These results demonstrate that the film showed excellent static decay time, surface and volume resistivity, and resistance to water washout of additive and aging at elevated temperature.
EXAMPLE X
Quaternary amine QA6, N,N-dimethyl-N-ethyl-N-cocoammonium ethosulfate, was prepared as follows: 9.36 g of N,N-dimethylcocoamine, was combined with 6.10 g of diethyl sulfate. After mixing at 80.degree. C. for 2-3 minutes, a clear liquid was formed in an exothermic process. On cooling, a waxy solid (m.p. 65.degree.-75.degree. C.) resulted (QA6).
Quaternary amine QA6 (4.44 g) was blended with 10 g Dow Primacor 1410 (ethylene-acrylic acid copolymer, 9% AA, 1.5 melt index) and 30 g Exxon LD318.92 (ethylene-vinyl acetate copolymer, 9% VA, 2.0 melt index). Blending was carried out in a Brabender Plasticorder mixer at 130.degree. C. for 30 minutes. A sample of the resultant material was pressed at approximately 1,000 psi (70 kg/cm.sup.2) between platens heated to 150.degree. C. A monolayer film of about 3 inches (7.6 cm) by 5 inches (12.7 cm) by 0.005 inch (0.013 cm) was thus obtained.
The surface resistivity of the sample was tested by two methods: First, the sample was equilibrated at 12.5.+-.0.5% RH for 48 hours and tested with a Keithley 6105 resistivity adapter (Keithley Instruments, Cleveland, Ohio) connected to a Keithley 247 high voltage supply and a Keithley 485 picoammeter. With an applied voltage of 100 volts, a surface resistivity of 9.96.times.10.sup.9 ohms/square was obtained. Second, the sample was equilibrated at 35 .+-.5% for >2 hours and tested with a TREK model 150 resistivity meter (TREK, Inc., Medina, N.Y.). A surface resistivity of 9.times.10.sup.7 ohms/square was obtained.
EXAMPLE XI
Quaternary amine QA6 (4.44 g) was blended with 10 g Surlyn 1650 partially zinc neutralized ethylene-methacrylic acid-zinc methacrylate terpolymer and 30 g Exxon LD318.92 as described in Example X.
When prepared and tested as described in Example X, a film sample of this material gave the following results:
Surface Resistivity after equilibration
at 12.5.+-.0.5% RH for 48 hrs.: 2.00.times.10.sup.10 ohms/square
Surface Resistivity after equilibration
at 35.+-.5% RH 1/4 2 hrs.: 2.times.10.sup.8 ohms/square
EXAMPLE XII
By blending with heat using a Berstorff twin screw extruder, a premix of pellets was made. First, 60 parts by weight EVA (LD318.92) and 30 parts by weight EAA (Primacor 5981) were mixed, and then added thereto was 20 parts by wt. QA [Emerstat 6660]. The resultant EVA+EAA+QA was then further blended with more polymer, and hot blown, 5-layer, extruded, tubular film having a thickness of about 4 mil (0.102 mm) was made. The ingredients of each layer were as recited in Table XIIA and are in % by weight.
TABLE XIIA__________________________________________________________________________OUTSIDE INTERIOR CORE INTERIOR OUTSIDELAYER 1 LAYER 2 LAYER 3 LAYER 4 LAYER 5__________________________________________________________________________100% EVA 100% EVA 100% LLDPE 100% EVA 662/3% EVA 331/3% Mix of EVA + EAA + QA__________________________________________________________________________
Then, the following electrical measurements were taken on samples of film as reported in Table XIIB. Resistivity was measured at about 12.5.+-.2.5% RH using a Keithley picoammeter with a separate 100 volt power source and an Electro Technical Services cell conforming to ASTM D257.
TABLE XIIB__________________________________________________________________________Abuse Static Decay Time (ms)Treatment or Ohms/square Ohms-cm 1 Hr. 24 Hr. 48 Hr.Film Tested Surface Volume Equilibration Equilibration Equilibration TriboAs is Resistivity Resistivity treatment treatment treatment Volts__________________________________________________________________________As is 5.9 .times. 10.sup.11 1.8 .times. 10.sup.16 1852 1824 NT* 8624 Hr. 1.9 .times. 10.sup.14 NT NT WON'T WON'T NTShower ACCEPT ACCEPT FULL FULL CHARGE CHARGEHot Dry OvenDay 1 NT NT 2190 1722 NT NTDay 2 NT NT 1492 3000 NT NTDay 3 NT NT 1471 1398 NT NTDay 4 NT NT 1326 1332 NT NTDay 5 NT NT 1501 1453 NT NTDay 6 NT NT NT NT NT NTDay 7 NT NT NT NT NT NTDay 8 NT NT NT NT NT NTDay 9 NT NT NT NT NT NTDay 10 NT NT NT 1845 NT NTDay 11 NT NT NT 1794 NT NTDay 12 2.0 .times. 10.sup.12 2.3 .times. 10.sup. 16 NT 15940 NT 537__________________________________________________________________________ *NT = not tested
These results illustrate that after 11 days in a hot oven, the film exhibited an excellent SDT less than 2000 ms.
EXAMPLE XIII
By blending with heat using a Berstorff twin screw extruder, a premix of pellets was made. First, 60 parts by weight EVA [LD318.92] and 30 parts by weight EAA [Primacor 5981] were mixed, and then added thereto was 20 parts by wt. QA [Emerstat 6660]. The resultant mix of EVA+EAA+QA was then further blended with more polymer, and hot blown, 5-layer extruded, tubular film having a thickness of about 4 mil (0.102 mm) was made. The ingredients of each layer were as recited in Table XIIIA and are in % by weight.
TABLE XIIIA__________________________________________________________________________OUTSIDE INTERIOR CORE INTERIOR OUTSIDELAYER 1 LAYER 2 LAYER 3 LAYER 4 LAYER 5__________________________________________________________________________662/3% 662/3% EVA 100% LLDPE 662/3% EVA 662/3%Primacor 1410 331/3% Mix 331/3% Mix Prmacor 1410331/3% Mix of EVA + EAA + QA of EVA + EAA + QA 331/3% Mixof EVA + EAA + QA of EVA + EAA__________________________________________________________________________ + QA
Then, the following electrical measurements were taken on samples of film as reported in Table XIIIB. Resistivity was measured at about 12.5.+-.2.5% RH using a Keithley picoammeter with a separate 100 volt power source and an Electro Technical Services cell conforming to ASTM D257.
TABLE XIIIB__________________________________________________________________________Abuse Static Decay Time (ms)Treatment or Ohms/square Ohms-cm 1 Hr. 24 Hr. 48 Hr.Film Tested Surface Volume Equilibration Equilibration Equilibration TriboAs is Resistivity Resistivity treatment treatment treatment Volts__________________________________________________________________________As is 1.3 .times. 10.sup.11 5.1 .times. 10.sup.13 40 80 NT* 4724 Hr. 7.9 .times. 10.sup.11 NT NT 109 108 NTShowerHot Dry OvenDay 1 NT NT 217 185 NT NTDay 2 NT NT 130 181 NT NTDay 3 NT NT 68 64 NT NTDay 4 NT NT 73 84 NT NTDay 5 NT NT 86 88 NT NTDay 6 NT NT 107 NT NT NTDay 7 NT NT NT NT NT NTDay 8 NT NT NT NT NT NTDay 9 NT NT NT NT NT NTDay 10 NT NT NT 84 NT NTDay 11 NT NT NT 94 NT NTDay 12 1.6 .times. 10.sup.11 2.1 .times. 10.sup.13 NT 51 NT 56__________________________________________________________________________ *NT = not tested
These results illustrate that after a 24-hour water shower and also after 12 days in a hot oven, the film exhibited both a permanent antistatic SDT less than 2000 ms and a permanent surface resistivity in the antistatic surface resistivity range of 10.sup.5 to 10.sup.12 ohms/square.
EXAMPLE XIV
By blending with heat using a Berstorff twin screw extruder, a premix of pellets was made. First, 60 parts by weight EVA [LD318.92] and 30 parts by weight EAA [Primacor 5981] were mixed, and then added thereto was 20 parts by wt. QA [Emerstat 6660]. The resultant mix of EVA+EAA+QA was then further blended with more polymer, and hot blown, 5-layer, extruded, tubular film having a thickness of about 4 mil (0.102 mm) was made. The ingredients of each layer were as recited in Table XIVA and are in % by weight.
TABLE XIVA__________________________________________________________________________OUTSIDE INTERIOR CORE INTERIOR OUTSIDELAYER 1 LAYER 2 LAYER 3 LAYER 4 LAYER 5__________________________________________________________________________562/3% 662/3% EVA 100% LLDPE 662/3% EVA 562/3%Primacor 1410 331/3% Mix 331/3% Mix Primacor 1410331/3% Mix of EVA + EAA + QA of EVA + EAA + QA 331/3% Mixof EVA + EAA + QA of EVA + EAA + QA10% Antiblock 10% Antiblock__________________________________________________________________________
Then, the following electrical measurements were taken on samples of film as reported in Table XIVB. Resistivity was measured at about 12.5.+-.2.5% RH using a Keithley picoammeter with a separate 100 volt power source and an Electro Technical Services cell conforming to ASTM D257.
TABLE XIVB__________________________________________________________________________AbuseTreatment Static Decay Time (ms)or Film Ohms/square Ohms-cm 1 Hr. 24 Hr. 48 Hr.Tested Surface Volume Equilibration Equilibration Equilibration TriboAs is Resistivity Resistivity treatment treatment treatment Volts__________________________________________________________________________As is 1.2 .times. 10.sup.11 5.8 .times. 10.sup.13 11 31 NT* 3524 Hr. 6.6 .times. 10.sup.11 NT NT 70 62 NTShowerHotDryOvenDay 1 NT NT 40 26 NT NTDay 2 NT NT 42 32 NT NTDay 3 NT NT 41 40 NT NTDay 4 NT NT 36 33 NT NTDay 5 NT NT 52 42 NT NTDay 6 NT NT 53 NT NT NTDay 7 NT NT NT NT NT NTDay 8 NT NT NT NT NT NTDay 9 NT NT NT NT NT NTDay 10 NT NT NT 45 NT NTDay 11 NT NT NT 44 NT NTDay 12 1.6 .times. 10.sup.11 2.4 .times. 10.sup.13 NT 65 NT 35__________________________________________________________________________ *NT = not tested
These results illustrate that after a 24-hour water shower and also after 12 days in a hot oven, the film exhibited both a permanent antistatic SDT less than 2000 ms and a permanent surface resistivity in the antistatic surface resistivity range of 10.sup.5 to 10.sup.12 ohms/square.
From the foregoing description, one skilled in the art can easily ascertain the essential characteristics of this invention, and without departing from the spirit and scope thereof, can make various changes and modifications of the invention to adapt it to various usages and conditions.

Number	Name	Date
T961009	Hendy	Aug 1977
2236515	Cahn et al.	Apr 1941
3022543	Baird, Jr. et al.	Feb 1962
3236881	Distler et al.	Feb 1966
3324091	Savides	Jun 1967
3405020	Chavannes	Oct 1968
3416984	Chavannes et al.	Dec 1968
3445440	Susi et al.	May 1969
3517045	Susi et al.	Jun 1970
3555604	Pahlke	Jan 1971
3586565	Fielding	Jun 1971
3732196	Dieterich	May 1973
3741253	Brax et al.	Jun 1973
3785899	Fielding	Jan 1974
3821182	Baird, Jr. et al.	Jun 1974
3894077	Horikawa et al.	Jul 1975
3933779	Baron et al.	Jan 1976
4048428	Baird et al.	Sep 1977
4070531	Schwarze et al.	Jan 1978
4104175	Martinsson et al.	Aug 1978
4178401	Weinberg et al.	Dec 1979
4188443	Mueller et al.	Feb 1980
4194039	Mueller	Mar 1980
4229241	Mueller	Oct 1980
4268583	Hendy	May 1981
4274900	Mueller et al.	Jun 1981
4433113	Woodward	Feb 1984
4494651	Malcolm	Jan 1985
4576669	Caputo	Mar 1986
4579516	Caputo	Apr 1986
4605684	Pcolinsky, Jr.	Aug 1986
4623594	Keough	Nov 1986
4678836	McKinney et al.	Jul 1987

Number	Date	Country
0206446	Dec 1986	EPX
0219315	Apr 1987	EPX
1559322	Mar 1969	FRX
59-47243	Mar 1984	JPX
54093025	Oct 1987	JPX
1206273	Jan 1986	SUX
938729	Oct 1963	GBX
2010851	Jul 1979	GBX

Permanent antistatic acid copolymer/quaternary amine polymeric films

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract

Description

Claims

Parent Case Info

US Referenced Citations (33)

Foreign Referenced Citations (8)

Non-Patent Literature Citations (4)

Divisions (1)

Continuation in Parts (1)

Entry
"Antistatic Agents", Exxon Chemicals Americas, p A-6, Sept. 21, 1983.
"Polymer Preprints", vol. 29, No. 2, Sept. 1988.
Copolymers of Ethylene and Acryl Acids, pp. 21-23.
Permanent Antistatic Acid, vol. 1, pp. 196-197, 1972.