Patent Application
20200119346
The present disclosure relates to a perovskite material, a method of preparing the perovskite material, and a secondary battery including the perovskite material.
A metal-air battery such as, may include a cathode at which oxygen present in the air is reduced, an anode at which lithium is oxidized, and an electrolyte interposed between the cathode and the anode. The metal-air battery may be a lithium-air battery including a lithium thin film as the anode. The lithium-air battery may serve as a high-capacity battery without the need to store oxygen in the battery.
A cathode of a lithium-air battery may include a carbonaceous material and an organic electrolyte. However, the carbonaceous material and the organic electrolyte may be decomposed by lithium oxide (Li2O2), which is a reaction product produced during discharge of the lithium-air battery, thereby producing carbon dioxide, which may cause deterioration of the cathode. The carbon dioxide may also be transferred to the anode through the organic electrolyte and subsequently react with the lithium in the anode, thereby causing deterioration of the anode and the charge and discharge characteristics of the lithium-air battery. Therefore, there is a need for improvement of a lithium-air battery in these aspects.
Provided is a perovskite material and a method of preparing the same.
Provided is a secondary battery including the perovskite material.
Additional aspects will be set forth in part in the description which follows and, in part, will be apparent from the description, or may be learned by practice of the presented embodiments.
According to an aspect of an embodiment, a perovskite material is represented by Formula 1:
LixAyMzO3-δ Formula 1
wherein, in Formula 1, 0<x≤1, 0<y≤1, 0<x+y<1, 0<z≤1.5, and 0≤δ≤1,
A is hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), or a combination thereof, and
M is nickel (Ni), palladium (Pd), lead (Pb), iron (Fe), iridium (Ir), cobalt (Co), rhodium (Rh), manganese (Mn), chromium (Cr), ruthenium (Ru), rhenium (Re), tin(Sn), vanadium (V), germanium (Ge), tungsten (W), zirconium (Zr), molybdenum (Mo), hafnium (Hf), uranium (U), niobium (Nb), thorium (Th), tantalum (Ta), bismuth (Bi), lithium (Li), hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), magnesium (Mg), aluminum (Al), silicon (Si), scandium (Sc), zinc (Zn), gallium (Ga), silver (Ag), cadmium (Cd), indium (In), antimony (Sb), platinum (Pt), gold (Au), or a combination thereof.
According to an aspect of another embodiment, a perovskite material is a composite represented by Formula 3, and has a ratio of a peak intensity at a diffraction angle 2θ of 46.5°±2.5° to a peak intensity at a diffraction angle 2θ of 32.5°±2.5° of less than 1:
LixAyMzO3-δ Formula 3
wherein, in Formula 3, 0<x≤1, 0<y≤1, 0<x+y<1, 0<z≤1.5, and 0≤δ≤1,
A is hydrogen (H) or at least one of a Group 2 to Group 16 element, and
M is at least one of a Group 2 to Group 16 element.
The perovskite material may have a ratio of a peak intensity at a diffraction angle 2θ of 57.5°±2.5° to a peak intensity at a diffraction angle 2θ of 32.5°±2.5° of less than 1.
According to an aspect of an embodiment, a method of preparing a perovskite material includes: providing a mixture comprising a lithium compound, an A element-containing compound, an M element-containing compound, and a solvent; first thermally treating the mixture to form a first thermally treated mixture; pulverizing the first thermally treated mixture to obtain a formed product; and second thermally treating the formed product to form the perovskite material,
wherein a temperature of the second thermally treating is greater than a temperature of the first thermally treating,
wherein A of the A element-containing compound is H, Na, K, Rb, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, or a combination thereof, and
M of the M element-containing compound is Ni, Pd, Pb, Fe, Ir, Co, Rh, Mn, Cr, Ru, Re, Sn, V, Ge, W, Zr, Mo, Hf, U, Nb, Th, Ta, Bi, Li, H, Na, K, Rb, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, Mg, Al, Si, Sc, Zn, Ga, Ag, Cd, In, Sb, Pt, Au, or a combination thereof.
According to an aspect of an embodiment, a secondary battery includes the perovskite material.
Also disclosed is a secondary battery including a cathode; an anode; and a gas-blocking layer interposed between the cathode and the anode, wherein the cathode or each of the cathode and the gas-blocking layer comprise the perovskite material.
Also disclosed is a secondary battery including a cathode, an anode, and an electrolyte interposed between the cathode and the anode, wherein the cathode or each of the cathode and the electrolyte include the perovskite material.
These and/or other aspects will become apparent and more readily appreciated from the following description of the embodiments, taken in conjunction with the accompanying drawings in which:
Reference will now be made in detail to embodiments, examples of which are illustrated in the accompanying drawings, wherein like reference numerals refer to like elements throughout. In this regard, the present embodiments may have different forms and should not be construed as being limited to the descriptions set forth herein. Accordingly, the embodiments are merely described below, by referring to the figures, to explain aspects.
The terminology used herein is for the purpose of describing particular embodiments only and is not intended to be limiting. As used herein, the singular forms “a,” “an,” and “the” are intended to include the plural forms, including “at least one,” unless the content clearly indicates otherwise. “At least one” is not to be construed as limiting “a” or “an.” “Or” means “and/or.” As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. It will be further understood that the terms “comprises” and/or “comprising,” or “includes” and/or “including” when used in this specification, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, regions, integers, steps, operations, elements, components, and/or groups thereof. As used herein, the term “and/or” includes any and all combinations of one or more of the associated listed items. Expressions such as “at least one of,” when preceding a list of elements, modify the entire list of elements and do not modify the individual elements of the list.
“About” or “approximately” as used herein is inclusive of the stated value and means within an acceptable range of deviation for the particular value as determined by one of ordinary skill in the art, considering the measurement in question and the error associated with measurement of the particular quantity (i.e., the limitations of the measurement system). For example, “about” can mean within one or more standard deviations, or within ±30%, 20%, 10% or 5% of the stated value.
Unless otherwise defined, all terms (including technical and scientific terms) used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this disclosure belongs. It will be further understood that terms, such as those defined in commonly used dictionaries, should be interpreted as having a meaning that is consistent with their meaning in the context of the relevant art and the present disclosure, and will not be interpreted in an idealized or overly formal sense unless expressly so defined herein.
Exemplary embodiments are described herein with reference to cross section illustrations that are schematic illustrations of idealized embodiments. As such, variations from the shapes of the illustrations as a result, for example, of manufacturing techniques and/or tolerances, are to be expected. Thus, embodiments described herein should not be construed as limited to the particular shapes of regions as illustrated herein but are to include deviations in shapes that result, for example, from manufacturing. For example, a region illustrated or described as flat may have rough and/or nonlinear features. Moreover, sharp angles that are illustrated may be rounded. Thus, the regions illustrated in the figures are schematic in nature and their shapes are not intended to illustrate the precise shape of a region and are not intended to limit the scope of the present claims.
Hereinafter, a perovskite material, a method of preparing the same, and a secondary battery including the perovskite material will be described in greater detail.
According to an aspect, there is provided a perovskite material represented by Formula 1.
LixAyMzO3-δ Formula 1
In Formula 1, 0<x≤1, 0<y≤1, 0<x+y<1, 0<z≤1.5, 0≤δ≤1, A may be hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), or a combination thereof.
In an embodiment in which A comprises a combination, A may be represented by A1aA2(a-1) wherein 0<a<1, and A1 and A2 are each independently hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), or erbium (Er).
M may be nickel (Ni), palladium (Pd), lead (Pb), iron (Fe), iridium (Ir), cobalt (Co), rhodium (Rh), manganese (Mn), chromium (Cr), ruthenium (Ru), rhenium (Re), tin(Sn), vanadium (V), germanium (Ge), tungsten (W), zirconium (Zr), molybdenum (Mo), hafnium (Hf), uranium (U), niobium (Nb), thorium (Th), tantalum (Ta), bismuth (Bi), lithium (Li), hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), magnesium (Mg), aluminum (Al), silicon (Si), scandium (Sc), zinc (Zn), gallium (Ga), silver (Ag), cadmium (Cd), indium (In), antimony (Sb), platinum (Pt), gold (Au), or a combination thereof.
In an embodiment in which M comprises a combination, M may be represented by M1mM2(m-1) wherein 0<m<1, and M1 and M2 are each independently nickel (Ni), palladium (Pd), lead (Pb), iron (Fe), iridium (Ir), cobalt (Co), rhodium (Rh), manganese (Mn), chromium (Cr), ruthenium (Ru), rhenium (Re), tin(Sn), vanadium (V), germanium (Ge), tungsten (W), zirconium (Zr), molybdenum (Mo), hafnium (Hf), uranium (U), niobium (Nb), thorium (Th), tantalum (Ta), bismuth (Bi), lithium (Li), hydrogen (H), sodium (Na), potassium (K), rubidium (Rb), cesium (Cs), calcium (Ca), strontium (Sr), barium (Ba), yttrium (Y), lanthanum (La), cerium (Ce), praseodymium (Pr), neodymium (Nd), promethium (Pm), samarium (Sm), gadolinium (Gd), terbium (Tb), dysprosium (Dy), holmium (Ho), erbium (Er), magnesium (Mg), aluminum (Al), silicon (Si), scandium (Sc), zinc (Zn), gallium (Ga), silver (Ag), cadmium (Cd), indium (In), antimony (Sb), platinum (Pt), or gold (Au).
In Formula 1, A and M may be to the same as or different from each other. For example, A may be La, Ce, Pr, Gd, Ca, Sr, Ba, or a combination thereof, and M may be, for example, Mn, Ni, Ru, Cr, Co, Ru, Ir, Fe, Pd, Pb, Rh, Sn, V, Re, Ge, W, Zr, Mo, Nb, Ta, Hf, Bi, or a combination thereof.
In Formula 1, x may satisfy the range of 0.1<x≤0.5, for example, 0.1<x≤0.45, 0.2<x≤0.5, or 0.3<x≤0.4; y may satisfy the range of 0.2<y≤0.7, for example, 0.4<y≤0.7, or 0.52<y≤0.67; and z may satisfy the range of 0.8<z≤1.2, for example, 0.9<z≤1.1. A sum of x and y may be 0.3 to 0.99, for example, 0.4 to 0.98, for example, 0.6 to 0.97, for example, 0.7 to 0.93, for example, 0.75 to 0.89. In Formula 1, 0.2<x≤0.5, 0.2<y≤0.7, and 0.8<z≤1.2, for example, 0.3<x≤1.4, 0.4<y≤0.7, and 0.9<z≤1.1.
In Formula 1, δ denotes an oxygen vacancy, and the value of δ is selected to make the perovskite material electrically neutral.
In Formula 1, a ratio of x to y may be, for example, about 1:0.5 to about 1:7, or about 1:1 to about 1:6, or about 1:2 to about 1:5.
The perovskite material may be electrically neutral. The perovskite material may have an oxygen vacancy formation energy of 0 to less than about 4 electron volts, for example, about 3.5 electron volts (eV) or less, or about 3 eV or less, or about 2.5 eV or less, for example, 0 eV to about 3.5 eV, or 0 eV to 3 eV, or about 0.1 eV to about 3 eV, or about 0.5 eV to about 2.5 eV. For reference, Li0.34la0.55TiO3, as a perovskite material including titanium, may have an oxygen vacancy formation energy of about 3.59 eV, accordingly, the perovskite material may have an oxygen vacancy formation energy less than the oxygen vacancy formation energy of Li0.34La0.55TiO3, for example, an oxygen vacancy formation energy less than about 3.59 eV, for example, 0 eV to less than about 3.59 eV. As used herein, the “oxygen vacancy formation energy” may be defined by using a quantum computational method. Without being limited by theory, it is understood that the smaller the oxygen vacancy formation energy of the perovskite material, it the easier it may be to form a surplus of electrons due to oxygen vacancies, thereby increasing the electrical conductivity of the perovskite material.
The quantum computational method used to define the oxygen vacancy formation energy, may be a method which is the same as, or substantially similar to the method disclosed by Emery et al (Antoine A. Emery, Chris Wolverton, “High-throughput DFT calculations of formation energy, stability and oxygen vacancy formation energy of ABO3 perovskites,” Scientific Data 4, Article number 170153 (2017), hereinafter “Emery”), the content of which is incorporated herein by reference in its entirety. The oxygen vacancy formation energy is a value equal to the difference between the total energy of oxygen and a composition of the formula A2B2O5 existing separately and the energy of two ABO3 molecules resulting from the presence of oxygen and A2B2O5 together, as illustrated in Equation 1 below.
EvO=E(A2B2O5)+μO−2E(ABO3) Equation 1
In Equation 1, EvO is the oxygen vacancy formation energy, E(A2B2O5) is the energy of A2B2O5, μO is the chemical potential of oxygen, and E(ABO3) is the energy of ABO3. In Equation 1, A2B2O5 is a structure in which an oxygen atom has been removed from A2B2O6, and the A and B sites are the same as defined in by Emery et al.
The perovskite material represented by Formula 1 may be a compound represented by Formula 2.
LixA1yM1zO3-δ Formula 2
In Formula 2, 0.3<x≤1, 0<y≤0.7, 0<z≤1, 0<x+y<1, 0≤δ≤1, A1 may be La, Ce, Pr, Gd, Ca, Sr, Ba, or a combination thereof, and M1 may be Mn, Ni, Ru, Cr, Co, Ru, Ir, Fe, Pd, Pb, Rh, Sn, V, Re, Ge, W, Zr, Mo, Nb, Ta, Hf, Bi, or a combination thereof.
In Formula 2, A1 may be, for example, La, Ca, or a combination thereof, and M1 may be, for example, Ru, Mn, Ni, Cr, Ir, Co, Mn1-aWa, wherein 0<a<1, or a combination thereof.
A lithium-air battery includes a positive electrode (cathode) including a carbonaceous material and an organic electrolyte. In such a lithium-air battery, lithium oxide (Li2O2) is generated during discharge when lithium originating from an anode reacts with oxygen introduced to the cathode, and the Li2O2 is then deposited in pores of the cathode while the oxygen is reduced. During discharge, due to the deposition of the lithium oxide in the pores of the cathode, the carbonaceous material and the organic electrolyte may be decomposed, and the resulting decomposition product may deteriorate the lifetime characteristics of the lithium-air battery.
To address these drawbacks, a perovskite material has been advantageously discovered, which is capable of ensuring simultaneous conduction of lithium ions and electrons and which is not susceptible to decomposition by the lithium oxide discharge product.
The perovskite material may have an ABO3 phase including a vacancy at the oxygen site and in which lithium occupies a portion of the A sites. The perovskite material may also have an orthorhombic, cubic, monoclinic, or triclinic crystalline phase, having an oxygen defect. The perovskite material may have improved lithium ion conductivity due to an optimized lithium concentration at the A site, and an increased electronic conductivity due to the introduction of a metal M having a low oxygen vacancy formation energy into the B site.
The perovskite material may have an electronic conductivity of about 1×10−6 Siemens per centimeter (S/cm) or greater, or about 1×10−5 S/cm or greater, or about 1×10−3 S/cm or greater, for example, about 1×10−5 S/cm to about 1×10−1 S/cm, or about 1×10−4 S/cm to about 1×10−2 S/cm, or more specifically, about 2.6×10−4 S/cm to about 5.6×10−2 S/cm, and an ionic conductivity of about 1×10−7 S/cm or greater, or about 2×10−6 S/cm or greater, or about 1×10−6 S/cm or greater, for example, about 1×10−7 S/cm to about 1×10−6 S/cm, or about 5×10−6 S/cm to about 5×10−5 S/cm, or more specifically, about 2.0×10−6 S/cm to about 8.8×10−5 S/cm.
The perovskite material may have a structure including corner-sharing MO6 octahedra, as shown in
As measured by X-ray diffraction, the perovskite material may have a main peak at a diffraction angle 2θ of 32.5°±2.5°, and a minor peak at a diffraction angle 2θ of 46.5°±2.5° and/or a diffraction angle 2θ of 57.5°±2.5°. The main peak refers to the highest peak, e.g., having the greatest intensity, and the minor peak refers to a peak having an intensity lower than the intensity of the main peak.
The perovskite material may have a ratio (Ib/Ia) of a peak intensity (I*(46.5°±2.5°): Ib) at a diffraction angle 2θ of 46.5°±2.5° to a peak intensity (I(32.5°2.5°): Ia) at a diffraction angle 2θ of 32.5°±2.5° may be less than 1, for example, less than 0.9, for example, less than 0.8, for example, about 0.1 to about 0.8, for example, about 0.2 to about 0.8, for example, about 0.2 to about 0.6. In one or more embodiments, the perovskite material may have a ratio (Ic/Ia) of a peak intensity (I(57.5°±2.5°): Ic) at a diffraction angle 2θ of 57.5°±2.5° to a peak intensity (I(32.5°±2.5°): Ia) at a diffraction angle 2θ of 32.5°±2.5° of less than 1, for example, less than 0.9, for example, less than 0.8, for example, about 0.1 to about 0.8, for example, about 0.2 to about 0.8, for example, about 0.2 to about 0.4.
According to another aspect, a perovskite material may be a composite represented by Formula 3, having a ratio (Ib/Ia) of a peak intensity (I(46.5°±2.5°): Ib) at a diffraction angle 2θ of 46.5°±2.5° to a peak intensity (I(32.5°±2.5°): Ia) at a diffraction angle 2θ of 32.5°±2.5° of less than 1.
LixAyMzO3-δ Formula 3
In Formula 3, 0<x≤1, 0<y≤1, 0<x+y<1, 0<z≤1.5, 0≤δ≤1,
A may be hydrogen (H) or at least one element of a Group 2 to Group 16 element of the periodic table of elements, and
M may be at least one of a Group 2 to Group16 element of the periodic table of elements.
The perovskite material may have a ratio (Ic/Ia) of a peak intensity (I(57.5°≡2.5°): Ic) at a diffraction angle 2θ of 57.5°±2.5° to a peak intensity (I(32.5°±2.5°) Ia) at a diffraction angle 2θ of 32.5°±2.5° of less than 1.
In Formula 3, A may be, for example, H, Na, K, Rb, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, or a combination thereof, and M may be, for example, Ni, Pd, Pb, Fe, Ir, Co, Rh, Mn, Cr, Ru, Re, Sn, V, Ge, W, Zr, Mo, Hf, U, Nb, Th, Ta, Bi, Li, H, Na, K, Rb, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, Mg, Al, Si, Sc, Zn, Ga, Ag, Cd, In, Sb, Pt, Au, or a combination thereof.
For example, the above-described X-ray diffraction angle characteristics may be attributed to, for example, the perovskite material represented by Formula 3 in which A is La, and M in the crystal structure is as illustrated in
The perovskite material may have an average particle diameter of about 5 nm to about 500 micrometers (μm), for example, about 100 nm to about 15 (μm), for example, about 300 nm to about 10 μm. In one or more embodiments, the perovskite material may have a specific surface area of about 0.01 square meters per gram (m2/g) to about 1000 m2/g, for example, about 0.5 m2/g to about 100 m2/g, or about 5 m2/g to about 75 m2/g.
The perovskite material may be, for example, Li0.34La0.55MnO3, Li0.34La0.55NiO3, Li0.34La0.55CrO3, Li0.34La0.55CoO3, Li0.34La0.55RuO3, Li0.34La0.55RuO3, Li0.34La0.55TiO3, Li0.34La0.55FeO3, Li0.34La0.55PdO3, Li0.34La0.55PbO3, Li0.34La0.55RhO3, Li0.34La0.55SnO3, Li0.34La0.55VO3, Li0.34La0.55ReO3, Li0.34La0.55GeO3, Li0.34La0.55WO3, Li0.34La0.55ZrO3, Li0.34La0.55MoO3, Li0.34La0.55NbO3, Li0.34La0.55TaO3, Li0.34La0.55HfO3, Li0.34La0.55BiO3; Li0.10La0.63MnO3, Li0.10La0.63NiO3, Li0.10La0.63CrO3, Li0.10La0.63CoO3, Li0.10La0.63IrO3, Li0.10La0.63RuO3, Li0.10La0.63TiO3, Li0.10La0.63FeO3, Li0.10La0.63PdO3, Li0.10La0.63PbO3, Li0.10La0.63RhO3, Li0.10La0.63SnO3, Li0.10La0.63VO3, Li0.10La0.63ReO3, Li0.10La0.63GeO3, Li0.10La0.63WO3, Li0.10La0.63ZrO3, Li0.10La0.63MoO3, Li0.10La0.63NbO3, Li0.10La0.63TaO3, Li0.10La0.63HfO3, Li0.10La0.63BiO3; Li0.20La0.60MnO3, Li0.20La0.60NiO3, Li0.20La0.60CrO3, Li0.20La0.60CoO3, Li0.10La0.60IrO3, Li0.20La0.60RuO3, Li0.20La0.60TiO3, Li0.20La0.60FeO3, Li0.20La0.60PdO3, Li0.20La0.60PbO3, Li0.20La0.60RhO3, Li0.20La0.60SnO3, Li0.20La0.60VO3, Li0.20La0.60ReO3, Li0.20La0.60GeO3, Li0.20La0.60WO3, Li0.20La0.60ZrO3, Li0.20La0.60MoO3, Li0.20La0.60NbO3, Li0.20La0.60TaO3, Li0.20La0.60HfO3, Li0.20La0.60BiO3; Li0.30La0.57MnO3, Li0.30La0.57NiO3, Li0.30La0.57CrO3, Li0.30La0.57CoO3, Li0.30La0.571rO3, Li0.30La0.57RuO3, Li0.30La0.57TiO3, Li0.30La0.57FeO3, Li0.30La0.57PdO3, Li0.30La0.57PbO3, Li0.30La0.57RhO3, Li0.30La0.57SnO3, Li0.30La0.57VO3, Li0.30La0.57ReO3, Li0.30La0.57GeO3, Li0.30La0.57WO3, Li0.30La0.57ZrO3, Li0.30La0.57MoO3, Li0.30La0.57NbO3, Li0.30La0.57TaO3, Li0.30La0.57HfO3, Li0.30La0.57BiO3, Li0.40La0.53MnO3, Li0.40La0.53NiO3, Li0.40La0.53CrO3, Li0.40La0.53CoO3, Li0.40La0.53IrO3, Li0.40La0.53RuO3, Li0.40La0.53TiO3, Li0.40La0.53FeO3, Li0.40La0.53PdO3, Li0.40La0.53PbO3, Li0.40La0.53RhO3, Li0.40La0.53SnO3, Li0.40La0.53VO3, Li0.40La0.53ReO3, Li0.40La0.53GeO3, Li0.40La0.53WO3, Li0.40La0.53ZrO3, Li0.40La0.53MoO3, Li0.40La0.53NbO3, Li0.40La0.53TaO3, Li0.40La0.53HfO3, Li0.40La0.53BiO3, Li0.45La0.52MnO3, Li0.45La0.52NiO3, Li0.45La0.52CrO3, Li0.45La0.52CoO3, Li0.45La0.52IrO3, Li0.45La0.52RuO3, Li0.45La0.52TiO3, Li0.45La0.52FeO3, Li0.45La0.52PdO3, Li0.45La0.52PbO3, Li0.45La0.52RhO3, Li0.45La0.52SnO3, Li0.45La0.52VO3, Li0.45La0.52ReO3, Li0.45La0.52GeO3, Li0.45La0.52WO3, Li0.45La0.52ZrO3, Li0.45La0.52MoO3, Li0.45La0.52NbO3, Li0.45La0.52TaO3, Li0.45La0.52HfO3, Li0.45La0.52BiO3, Li0.34Ce0.55MnO3, Li0.34Ce0.55NiO3, Li0.34Ce0.55CrO3, Li0.34Ce0.55CoO3, Li0.34Ce0.55IrO3, Li0.34Ce0.55RuO3, Li0.34Ce0.55TiO3, Li0.34Ce0.55FeO3, Li0.34Ce0.55PdO3, Li0.34Ce0.55PbO3, Li0.34Ce0.55RhO3, Li0.34Ce0.55SnO3, Li0.34Ce0.55VO3, Li0.34Ce0.55ReO3, Li0.34Ce0.55GeO3, Li0.34Ce0.55WO3, Li0.34Ce0.55ZrO3, Li0.34Ce0.55MoO3, Li0.34Ce0.55NbO3, Li0.34Ce0.55TaO3, Li0.34Ce0.55HfO3, Li0.34Ce0.55BiO3, Li0.10Ce0.63MnO3, Li0.10Ce0.63NiO3, Li0.10Ce0.63CrO3, Li0.10Ce0.63CoO3, Li0.10Ce0.63IrO3, Li0.10Ce0.63RuO3, Li0.10Ce0.63TiO3, Li0.10Ce0.63FeO3, Li0.10Ce0.63PdO3, Li0.10Ce0.63PbO3, Li0.10Ce0.63RhO3, Li0.10Ce0.63SnO3, Li0.10Ce0.63VO3, Li0.10Ce0.63ReO3, Li0.10Ce0.63GeO3, Li0.10Ce0.63WO3, Li0.10Ce0.63ZrO3, Li0.10Ce0.63MoO3, Li0.10Ce0.63NbO3, Li0.10Ce0.63TaO3, Li0.10Ce0.63HfO3, Li0.10Ce0.63BiO3, Li0.20Ce0.60MnO3, Li0.20Ce0.60NiO3, Li0.20Ce0.60CrO3, Li0.20Ce0.60CoO3, Li0.20Ce0.60IrO3, Li0.20Ce0.60RuO3, Li0.20Ce0.60TiO3, Li0.20Ce0.60FeO3, Li0.20Ce0.60PdO3, Li0.20Ce0.60PbO3, Li0.20Ce0.60RhO3, Li0.20Ce0.60SnO3, Li0.20Ce0.60VO3, Li0.20Ce0.60ReO3, Li0.20Ce0.60GeO3, Li0.20Ce0.60WO3, Li0.20Ce0.60ZrO3, Li0.20Ce0.60MoO3, Li0.20Ce0.60NbO3, Li0.20Ce0.60TaO3, Li0.20Ce0.60HfO3, Li0.20Ce0.60BiO3, Li0.30Ce0.57MnO3, Li0.30Ce0.57NiO3, Li0.30Ce0.57CrO3, Li0.30Ce0.57CoO3, Li0.30Ce0.57IrO3, Li0.30Ce0.57RuO3, Li0.30Ce0.57TiO3, Li0.30Ce0.57FeO3, Li0.30Ce0.57PdO3, Li0.30Ce0.57PbO3, Li0.30Ce0.57RhO3, Li0.30Ce0.57SnO3, Li0.30Ce0.57VO3, Li0.30Ce0.57ReO3, Li0.30Ce0.57GeO3, Li0.30Ce0.57WO3, Li0.30Ce0.57ZrO3, Li0.30Ce0.57MoO3, Li0.30Ce0.57NbO3, Li0.30Ce0.57TaO3, Li0.30Ce0.57HfO3, Li0.30Ce0.57BiO3, Li0.40Ce0.53MnO3, Li0.40Ce0.53NiO3, Li0.40Ce0.53CrO3, Li0.40Ce0.53CoO3, Li0.40Ce0.53IrO3, Li0.40Ce0.53RuO3, Li0.40Ce0.53TiO3, Li0.40Ce0.53FeO3, Li0.40Ce0.53PdO3, Li0.40Ce0.53PbO3, Li0.40Ce0.53RhO3, Li0.40Ce0.53SnO3, Li0.40Ce0.53VO3, Li0.40Ce0.53ReO3, Li0.40Ce0.53GeO3, Li0.40Ce0.53WO3, Li0.40Ce0.53ZrO3, Li0.40Ce0.53MoO3, Li0.40Ce0.53NbO3, Li0.40Ce0.53TaO3, Li0.40Ce0.53HfO3, Li0.40Ce0.53BiO3, Li0.45Ce0.52MnO3, Li0.45Ce0.52NiO3, Li0.45Ce0.52CrO3, Li0.45Ce0.52CoO3, Li0.45Ce0.52IrO3, Li0.45Ce0.52RuO3, Li0.45Ce0.52TiO3, Li0.45Ce0.52FeO3, Li0.45Ce0.52PdO3, Li0.45Ce0.52PbO3, Li0.45Ce0.52RhO3, Li0.45Ce0.52SnO3, Li0.45Ce0.52VO3, Li0.45Ce0.52ReO3, Li0.45Ce0.52GeO3, Li0.45Ce0.52WO3, Li0.45Ce0.52ZrO3, Li0.45Ce0.52MoO3, Li0.45Ce0.52NbO3, Li0.45Ce0.52TaO3, Li0.45Ce0.52HfO3, Li0.45Ce0.52BiO3, Li0.34Pr0.55MnO3, Li0.34Pr0.55NiO3, Li0.34Pr0.55CrO3, Li0.34Pr0.55CoO3, Li0.34Pr0.55IrO3, Li0.34Pr0.55RuO3, Li0.34Pr0.55TiO3, Li0.34Pr0.55FeO3, Li0.34Pr0.55PdO3, Li0.34Pr0.55PbO3, Li0.34Pr0.55RhO3, Li0.34Pr0.55SnO3, Li0.34Pr0.55VO3, Li0.34Pr0.55ReO3, Li0.34Pr0.55GeO3, Li0.34Pr0.55WO3, Li0.34Pr0.55ZrO3, Li0.34Pr0.55MoO3, Li0.34Pr0.55NbO3, Li0.34Pr0.55TaO3, Li0.34Pr0.55HfO3, Li0.34Pr0.55BiO3, Li0.10Pr0.63MnO3, Li0.10Pr0.63NiO3, Li0.10Pr0.63CrO3, Li0.10Pr0.63CoO3, Li0.10Pr0.63IrO3, Li0.10Pr0.63RuO3, Li0.10Pr0.63TiO3, L0.10Pr0.63FeO3, Li0.10Pr0.63PdO3, Li0.10Pr0.63PbO3, Li0.10Pr0.63RhO3, Li0.10Pr0.63SnO3, Li0.10Pr0.63VO3, Li0.10Pr0.63ReO3, Li0.10Pr0.63GeO3, Li0.10Pr0.63WO3, Li0.10Pr0.63ZrO3, Li0.10Pr0.63MoO3, Li0.10Pr0.63NbO3, Li0.10Pr0.63TaO3, Li0.10Pr0.63HfO3, Li0.10Pr0.63BiO3, Li0.20Pr0.60MnO3, Li0.20Pr0.60NiO3, Li0.20Pr0.60CrO3, Li0.20Pr0.60CoO3, Li0.20Pr0.60IrO3, Li0.20Pr0.60RuO3, Li0.20Pr0.60TiO3, Li0.20Pr0.60FeO3, Li0.20Pr0.60PdO3, Li0.20Pr0.60PbO3, Li0.20Pr0.60RhO3, Li0.20Pr0.60SnO3, Li0.20Pr0.60VO3, Li0.20Pr0.60ReO3, Li0.20Pr0.60GeO3, Li0.20Pr0.60WO3, Li0.20Pr0.60ZrO3, Li0.20Pr0.60MoO3, Li0.20Pr0.60NbO3, Li0.20Pr0.60TaO3, Li0.20Pr0.60HfO3, Li0.20Pr0.60BiO3, Li0.30Pr0.57MnO3, Li0.30Pr0.57NiO3, Li0.30Pr0.57CrO3, Li0.30Pr0.57CoO3, Li0.30Pr0.57IrO3, Li0.30Pr0.57RuO3, Li0.30Pr0.57TiO3, Li0.30Pr0.57FeO3, Li0.30Pr0.57PdO3, Li0.30Pr0.57PbO3, Li0.30Pr0.57RhO3, Li0.30Pr0.57SnO3, Li0.30Pr0.57VO3, Li0.30Pr0.57ReO3, Li0.30Pr0.57GeO3, Li0.30Pr0.57WO3, Li0.30Pr0.57ZrO3, Li0.30Pr0.57MoO3, Li0.30Pr0.57NbO3, Li0.30Pr0.57TaO3, Li0.30Pr0.57HfO3, Li0.30Pr0.57BiO3, Li0.40Pr0.53MnO3, Li0..40Pr0.53NiO3, Li0.40Pr0.53CrO3, Li0.40Pr0.53CoO3, Li0.40Pr0.53IrO3, Li0.40Pr0.53RuO3, Li0.40Pr0.53TiO3, Li0.40Pr0.53FeO3, Li0.40Pr0.53PdO3, Li0.40Pr0.53PbO3, Li0.40Pr0.53RhO3, Li0.40Pr0.53SnO3, Li0.40Pr0.53VO3, Li0.40Pr0.53ReO3, Li0.40Pr0.53GeO3, Li0.40Pr0.53WO3, Li0.40Pr0.53ZrO3, Li0.40Pr0.53MoO3, Li0.40Pr0.53NbO3, Li0.40Pr0.53TaO3, Li0.40Pr0.53HfO3, Li0.40Pr0.53BiO3, Li0.45Pr0.52MnO3, Li0.45Pr0.52NiO3, Li0.45Pr0.52CrO3, Li0.45Pr0.52CoO3, Li0.45Pr0.52IrO3, Li0.45Pr0.52RuO3, Li0.45Pr0.52TiO3, Li0.45Pr0.52FeO3, Li0.45Pr0.52PdO3, Li0.45Pr0.52PbO3, Li0.45Pr0.52RhO3, Li0.45Pr0.52SnO3, Li0.45Pr0.52VO3, Li0.45Pr0.52ReO3, Li0.45Pr0.52GeO3, Li0.45Pr0.52WO3, Li0.45Pr0.52ZrO3, Li0.45Pr0.52MoO3, Li0.45Pr0.52NbO3, Li0.45Pr0.52TaO3, Li0.45Pr0.52HfO3, Li0.45Pr0.52BiO3; Li0.10Ca0.80MnO3, Li0.10Ca0.80NiO3, Li0.10Ca0.80CrO3, Li0.10Ca0.80CoO3, Li0.10Ca0.80IrO3, Li0.10Ca0.80RuO3, Li0.10Ca0.80TiO3, Li0.10Ca0.80FeO3, Li0.10Ca0.80PdO3, Li0.10Ca0.80PbO3, Li0.10Ca0.80RhO3, Li0.10Ca0.80SnO3, Li0.10Ca0.80VO3, Li0.10Ca0.80ReO3, Li0.10Ca0.80GeO3, Li0.10Ca0.80WO3, Li0.10Ca0.80ZrO3, Li0.10Ca0.80MoO3, Li0.10Ca0.80NbO3, Li0.10Ca0.80TaO3, Li0.10Ca0.80HfO3, Li0.10Ca0.80BiO3; Li0.20Ca0.60MnO3, Li0.20Ca0.60NiO3, Li0.20Ca0.60CrO3, Li0.20Ca0.60CoO3, Li0.20Ca0.60IrO3, Li0.20Ca0.60RuO3, Li0.20Ca0.60TiO3, Li0.20Ca0.60FeO3, Li0.20Ca0.60PdO3, Li0.20Ca0.60PbO3, Li0.20Ca0.60RhO3, Li0.20Ca0.60SnO3, Li0.20Ca0.60VO3, Li0.20Ca0.60ReO3, Li0.20Ca0.60GeO3, Li0.20Ca0.60WO3, Li0.20Ca0.60ZrO3, Li0.20Ca0.60MoO3, Li0.20Ca0.60NbO3, Li0.20Ca0.60TaO3, Li0.20Ca0.60HfO3, Li0.20Ca0.60BiO3; Li0.25Ca0.50MnO3, Li0.25Ca0.50NiO3, Li0.25Ca0.50CrO3, Li0.25Ca0.50CoO3, Li0.25Ca0.50IrO3, Li0.25Ca0.50RuO3, Li0.25Ca0.50TiO3, Li0.25Ca0.50FeO3, Li0.25Ca0.50PdO3, Li0.25Ca0.50PbO3, Li0.25Ca0.50RhO3, Li0.25Ca0.50SnO3, Li0.25Ca0.50VO3, Li0.25Ca0.50ReO3, Li0.25Ca0.50GeO3, Li0.25Ca0.50WO3, Li0.25Ca0.50ZrO3, Li0.25Ca0.50MoO3, Li0.25Ca0.50NbO3, Li0.25Ca0.50TaO3, Li0.25Ca0.50HfO3, Li0.25Ca0.50BiO3; Li0.30Ca0.40MnO3, Li0.30Ca0.40NiO3, Li0.30Ca0.40CrO3, Li0.30Ca0.40CoO3, Li0.30Ca0.40IrO3, Li0.30Ca0.40RuO3, Li0.30Ca0.40TiO3, Li0.30Ca0.40FeO3, Li0.30Ca0.40PdO3, Li0.30Ca0.40PbO3, Li0.30Ca0.40RhO3, Li0.30Ca0.40SnO3, Li0.30Ca0.40VO3, Li0.30Ca0.40ReO3, Li0.30Ca0.40GeO3, Li0.30Ca0.40WO3, Li0.30Ca0.40ZrO3, Li0.30Ca0.40MoO3, Li0.30Ca0.40NbO3, Li0.30Ca0.40TaO3, Li0.30Ca0.40HfO3, Li0.30Ca0.40BiO3; Li0.40Ca0.20MnO3, Li0.40Ca0.20NiO3, Li0.40Ca0.20CrO3, Li0.40Ca0.20CoO3, Li0.40Ca0.20IrO3, Li0.40Ca0.20RuO3, Li0.40Ca0.20TiO3, Li0.40Ca0.20FeO3, Li0.40Ca0.20PdO3, Li0.40Ca0.20PbO3, Li0.40Ca0.20RhO3, Li0.40Ca0.20SnO3, Li0.40Ca0.20VO3, Li0.40Ca0.20ReO3, Li0.40Ca0.20GeO3, Li0.40Ca0.20WO3, Li0.40Ca0.20ZrO3, Li0.40Ca0.20MoO3, Li0.40Ca0.20NbO3, Li0.40Ca0.20TaO3, Li0.40Ca0.20HfO3, Li0.40Ca0.20BiO3; Li0.10Sr0.80mnO3, Li0.10Sr0.80NiO3, Li0.10Sr0.80CrO3, Li0.10Sr0.80CoO3, Li0.10Sr0.80IrO3, Li0.10Sr0.80RuO3, Li0.10Sr0.80TiO3, Li0.10Sr0.80FeO3, Li0.10Sr0.80PdO3, Li0.10Sr0.80PbO3, Li0.10Sr0.80RhO3, Li0.10Sr0.80SnO3, Li0.10Sr0.80VO3, Li0.10Sr0.80ReO3, Li0.10Sr0.80GeO3, Li0.10Sr0.80WO3, Li0.10Sr0.80ZrO3, Li0.10Sr0.80MoO3, Li0.10Sr0.80NbO3, Li0.10Sr0.80TaO3, Li0.10Sr0.80HfO3, Li0.10Sr0.80BiO3, Li0.20Sr0.60MnO3, Li0.20Sr0.60NiO3, Li0.20Sr0.60CrO3, Li0.20Sr0.60CoO3, Li0.20Sr0.60IrO3, Li0.20Sr0.60RuO3, Li0.20Sr0.60TiO3, Li0.20Sr0.60FeO3, Li0.20Sr0.60PdO3, Li0.20Sr0.60PbO3, Li0.20Sr0.60RhO3, Li0.20Sr0.60SnO3, Li0.20Sr0.60VO3, Li0.20Sr0.60ReO3, Li0.20Sr0.60GeO3, Li0.20Sr0.60WO3, Li0.20Sr0.60ZrO3, Li0.20Sr0.60MoO3, Li0.20Sr0.60NbO3, Li0.20Sr0.60TaO3, Li0.20Sr0.60HfO3, Li0.20Sr0.60BiO3, Li0.25Sr0.50MnO3, Li0.25Sr0.50NiO3, Li0.25Sr0.50CrO3, Li0.25Sr0.50CoO3, Li0.25Sr0.501rO3, Li0.25Sr0.50RuO3, Li0.25Sr0.50TiO3, Li0.25Sr0.50FeO3, Li0.25Sr0.50PdO3, Li0.25Sr0.50PbO3, Li0.25Sr0.50RhO3, Li0.25Sr0.50SnO3, Li0.25Sr0.50VO3, Li0.25Sr0.50ReO3, Li0.25Sr0.50GeO3, Li0.25Sr0.50WO3, Li0.25Sr0.50ZrO3, Li0.25Sr0.50MoO3, Li0.25Sr0.50NbO3, Li0.25Sr0.50TaO3, Li0.25Sr0.50HfO3, Li0.25Sr0.50BiO3, Li0.30Sr0.40MnO3, Li0.30Sr0.40NiO3, Li0.30Sr0.40CrO3, Li0.30Sr0.40CoO3, Li0.30Sr0.401rO3, Li0.30Sr0.40RuO3, Li0.30Sr0.40TiO3, Li0.30Sr0.40FeO3, Li0.30Sr0.40PdO3, Li0.30Sr0.40PbO3, Li0.30Sr0.40RhO3, Li0.30Sr0.40SnO3, Li0.30Sr0.40VO3, Li0.30Sr0.40ReO3, Li0.30Sr0.40GeO3, Li0.30Sr0.40WO3, Li0.30Sr0.40ZrO3, Li0.30Sr0.40MoO3, Li0.30Sr0.40NbO3, Li0.30Sr0.40TaO3, Li0.30Sr0.40HfO3, Li0.30Sr0.40BiO3, Li0.40Sr0.20MnO3, Li0.40Sr0.20NiO3, Li0.40Sr0.20CrO3, Li0.40Sr0.20CoO3, Li0.40Sr0.20IrO3, Li0.40Sr0.20RuO3, Li0.40Sr0.20TiO3, Li0.40Sr0.20FeO3, Li0.40Sr0.20PdO3, Li0.40Sr0.20PbO3, Li0.40Sr0.20RhO3, Li0.40Sr0.20SnO3, Li0.40Sr0.20VO3, Li0.40Sr0.20ReO3, Li0.40Sr0.20GeO3, Li0.40Sr0.20WO3, Li0.40Sr0.20ZrO3, Li0.40Sr0.20MoO3, Li0.40Sr0.20NbO3, Li0.40Sr0.20TaO3, Li0.40Sr0.20HfO3, Li0.40Sr0.20BiO3; Li0.10Ba0.80MnO3, Li0.10Ba0.80NiO3, Li0.10Ba0.80CrO3, Li0.10Ba0.80CoO3, Li0.10Ba0.80IrO3, Li0.10Ba0.80RuO3, Li0.10Ba0.80TiO3, L0.10Ba0.80FeO3, L0.10Ba0.80PdO3, Li0.10Ba0.80PbO3, Li0.10Ba0.80RhO3, Li0.10Ba0.80SnO3, Li0.10Ba0.80VO3, Li0.10Ba0.80ReO3, Li0.10Ba0.80GeO3, Li0.10Ba0.80WO3, Li0.10Ba0.80ZrO3, Li0.10Ba0.80MoO3, Li0.10Ba0.80NbO3, Li0.10Ba0.80TaO3, Li0.10Ba0.80HfO3, Li0.10Ba0.80BiO3; Li0.20Ba0.60MnO3, Li0.20Ba0.60NiO3, Li0.20Ba0.60CrO3, Li0.20Ba0.60CoO3, Li0.20Ba0.60IrO3, Li0.20Ba0.60RuO3, Li0.20Ba0.60TiO3, Li0.20Ba0.60FeO3, Li0.20Ba0.60PdO3, Li0.20Ba0.60PbO3, Li0.20Ba0.60RhO3, Li0.20Ba0.60SnO3, Li0.20Ba0.60VO3, Li0.20Ba0.60ReO3, Li0.20Ba0.60GeO3, Li0.20Ba0.60WO3, Li0.20Ba0.60ZrO3, Li0.20Ba0.60MoO3, Li0.20Ba0.60NbO3, Li0.20Ba0.60TaO3, Li0.20Ba0.60HfO3, Li0.20Ba0.60BiO3; Li0.25Ba0.50MnO3, Li0.25Ba0.50NiO3, Li0.25Ba0.50CrO3, Li0.25Ba0.50CoO3, Li0.25Ba0.50IrO3, Li0.25Ba0.50RuO3, Li0.25Ba0.50TiO3, Li0.25Ba0.50FeO3, Li0.25Ba0.50PdO3, Li0.25Ba0.50PbO3, Li0.25Ba0.50RhO3, Li0.25Ba0.50SnO3, Li0.25Ba0.50VO3, Li0.25Ba0.50ReO3, Li0.25Ba0.50GeO3, Li0.25Ba0.50WO3, Li0.25Ba0.50ZrO3, Li0.25Ba0.50NbO3, Li0.25Ba0.50NbO3, Li0.25Ba0.50TaO3, Li0.25Ba0.50HfO3, Li0.25Ba0.50BiO3; Li0.30Ba0.40MnO3, Li0.30Ba0.40NiO3, Li0.30Ba0.40CrO3, Li0.30Ba0.40CoO3, Li0.30Ba0.40IrO3, Li0.30Ba0.40RuO3, Li0.30Ba0.40TiO3, Li0.30Ba0.40FeO3, Li0.30Ba0.40PdO3, Li0.30Ba0.40PbO3, Li0.30Ba0.40RhO3, Li0.30Ba0.40SnO3, Li0.30Ba0.40VO3, Li0.30Ba0.40ReO3, Li0.30Ba0.40GeO3, Li0.30Ba0.40WO3, Li0.30Ba0.40ZrO3, Li0.30Ba0.40MoO3, Li0.30Ba0.40NbO3, Li0.30Ba0.40TaO3, Li0.30Ba0.40HfO3, Li0.30Ba0.40BiO3, Li0.40Ba0.20MnO3, Li0.40Ba0.20NiO3, Li0.40Ba0.20CrO3, Li0.40Ba0.20CoO3, Li0.40Ba0.20IrO3, Li0.40Ba0.20RuO3, Li0.40Ba0.20TiO3, Li0.40Ba0.20FeO3, Li0.40Ba0.20PdO3, Li0.40Ba0.20PbO3, Li0.40Ba0.20RhO3, Li0.40Ba0.20SnO3, Li0.40Ba0.20VO3, Li0.40Ba0.20ReO3, Li0.40Ba0.20GeO3, Li0.40Ba0.20WO3, Li0.40Ba0.20ZrO3, Li0.40Ba0.20MoO3, Li0.40Ba0.20NbO3, Li0.40Ba0.20TaO3, Li0.40Ba0.20HfO3, Li0.40Ba0.20BiO3, Li0.25La0.50MnO3, Li0.25La0.50NiO3, Li0.25La0.50CrO3, Li0.25La0.50CoO3, Li0.25La0.50IrO3, Li0.25La0.50RuO3, Li0.25La0.50TiO3, Li0.25La0.50FeO3, Li0.25La0.50PdO3, Li0.25La0.50PbO3, Li0.25La0.50RhO3, Li0.25La0.50SnO3, Li0.25La0.50VO3, Li0.25La0.50ReO3, Li0.25La0.50GeO3, Li0.25La0.50WO3, Li0.25La0.50ZrO3, Li0.25La0.50MoO3, Li0.25La0.50NbO3, Li0.25La0.50TaO3, Li0.25La0.50HfO3, Li0.25La0.50BiO3; Li0.05La0.82Mn0.70O3, Li0.10La0.80Mn0.70O3, Li0.20La0.77Mn0.70O3, Li0.05La0.82Nb0.70O3, Li0.10La0.80Nb0.70O3, Li0.20La0.77Nb0.70O3, Li0.05La0.82Ta0.70O3, Li0.10La0.80Ta0.70O3, Li0.20La0.77Ta0.70O3, Li0.05La0.82V0.70O3, Li0.10La0.80V0.70O3, Li0.20La0.77V0.70O3; Li0.05La0.82W0.70O3, Li0.10La0.80W0.70O3, Li0.20La0.77W0.70O3, Li0.05La0.82Mo0.70O3, Li0.10La0.80Mo0.70O3, Li0.20La0.77Mo0.70O3, Li0.05La0.82Bi0.70O3, Li0.10La0.80Bi0.70O3, Li0.20La0.77Bi0.70O3, Li0.05La0.82Cr0.70O3, Li0.10La0.80Cr0.70O3, Li0.20La0.77Cr0.70O3, or a combination thereof.
The perovskite material may be a material in which O3-δ (where 0<δ≤1) is substituted for O3 in any of the above-listed materials.
The perovskite material may be, for example, Li0.34La0.55RuO3-δ (wherein 0≤δ≤1), Li0.34La0.55MnO3-δ (wherein 0≤δ≤1), Li0.34La0.55NiO3-δ (wherein 0≤δ≤1), Li0.34La0.55CrO3-δ (wherein 0≤δ≤1), Li0.34La0.55IrO3-δ (wherein 0≤δ≤1), Li0.34La0.55CoO3-δ (wherein 0≤δ≤1), Li0.34Ca0.58(Mn0.5W0.5)O3-δ (wherein 0≤δ≤1), or a combination thereof. For example, the perovskite material may be any material in which δ is 0 in the above-listed formulae, for example, Li0.34La0.55RuO3, Li0.34La0.55MnO3, Li0.34La0.55NiO3, Li0.34La0.55CrO3, Li0.34La0.55RuO3, Li0.34La0.55CoO3, or a combination thereof.
Hereinafter, a method of preparing a perovskite material according to embodiments will be further described.
A mixture of a lithium compound, an A element-containing compound, an M element-containing compound, and a solvent may be provided. Next, a first thermal treatment may be performed on the mixture to provide a first thermally treated mixture. The solvent may be any suitable solvent in which the A element-containing compound and the M element-containing compound may be dissolved and/or dispersed. For example, the solvent may be at least one of ethanol, water, ethylene glycol, or isopropanol. The amount of the solvent may be about 3 parts by weight to about 1,000 parts by weight, or about 200 parts by weight to about 800 parts by weight, for example, about 300 parts by weight to about 600 parts by weight, with respect to 100 parts by weight of a total weight of the lithium compound, the A element-containing compound, and the M element-containing compound.
In the A element-containing compound, A may be hydrogen (H) or at least one element of a Group 1 to Group 16 element of the Periodic Table, and M may be at least one of a Group 1 to Group 16 element of the Periodic Table. For example, A of the A element-containing compound and M of the M element-containing compound may be the same as those defined for A and M in Formula 1 above. That is, A of the A element-containing compound may be H, Na, K, Rb, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, or a combination thereof, and M of the M element-containing compound may be Ni, Pd, Pb, Fe, Ir, Co, Rh, Mn, Cr, Ru, Re, Sn, V, Ge, W, Zr, Ti, Mo, Hf, U, Nb, Th, Ta, Bi, Li, H, Na, K, Cs, Ca, Sr, Ba, Y, La, Ce, Pr, Nd, Pm, Sm, Gd, Tb, Dy, Ho, Er, Mg, AI, Si, Sc, Zn, Ga, Ag, Cd, In, Sb, Pt, Au, or a combination thereof.
The provision of the mixture may include combining the lithium compound, the A element-containing compound, the M element-containing compound, and the solvent and mixing to form the mixture. The mixing may be performed by any suitable method, for example, milling, blending, stirring, or a combination thereof. The milling may be performed using, for example, a ball mill, an air-jet mill, a bead mill, a roll mill, or a combination thereof.
The first thermal treatment may be performed at a heating rate of about 1 degree Celsius per minute (° C./min) to about 10° C./min, and a temperature of the first thermal treatment may be in the range of about 600° C. to about 900° C., or about 650° C. to about 900° C. or about 650° C. to about 750° C. During the first thermal treatment, CO3 and OH may be removed. Following the first thermal treatment process, a perovskite material may be obtained by performing a second thermal treatment process that will be further described later. When the heating rate of the first thermal treatment is within the above-described range, the first thermal treatment may be sufficient to enable formation of a perovskite material having a selected crystal structure after the second thermal treatment process that is to be further described later.
The first thermal treatment may be performed in an oxidizing gas atmosphere.
The oxidizing gas atmosphere may be created using, for example, ambient air or pure oxygen. The time of the first thermal treatment may vary depending on the first thermal treatment temperature, and may be, for example, about 1 to 20 hours, for example, about 1 to 10 hours, for example, about 2 to 5 hours.
The lithium compound may be, for example, at least one of lithium oxide, lithium carbonate, lithium chloride, lithium sulfide, lithium nitrate, lithium phosphate, or lithium hydroxide.
The A element-containing compound may be, for example, at least one of lanthanum oxide, lanthanum carbonate, lanthanum chloride, lanthanum sulfide, lanthanum nitrate, lanthanum phosphate, lanthanum hydroxide, yttrium oxide, yttrium carbonate, yttrium chloride, yttrium sulfide, cerium oxide, cerium carbonate, cerium chloride, cerium sulfide, cerium nitrate, cerium phosphate, cerium hydroxide, calcium oxide, calcium carbonate, calcium chloride, calcium sulfide, calcium nitrate, calcium phosphate, calcium hydroxide, barium oxide, barium carbonate, barium chloride, barium sulfide, barium nitrate, barium phosphate, barium hydroxide, strontium oxide, strontium carbonate, strontium chloride, strontium sulfide, strontium nitrate, strontium phosphate, or strontium hydroxide.
The M element-containing compound may be, for example, at least one of nickel oxide, nickel hydroxide, cobalt oxide, cobalt hydroxide, ruthenium oxide, ruthenium hydroxide, chromium oxide, chromium hydroxide, iridium oxide, iridium hydroxide, manganese oxide, or manganese hydroxide.
The amount of the lithium compound, the A element-containing compound, and the M element-containing compound may be stoichiometrically controlled in order to obtain the perovskite material represented by Formula 1.
Next, the product from the first thermal treatment may be pulverized to obtain a formed product. The formed product may be, for example, a powder including a particle. The formed product (particle) may have a particle size of about 10 μm or less, for example, about 5 μm or less, or about 1 μm or less. When a particle size of the formed product is within this range, the particle size may be small enough to ensure sufficient pulverization and mixing, thereby facilitating formation of a crystalline phase in the perovskite material. The expression “particle size” used herein refers to an average particle diameter when the particle is spherical in shape, and refers to a length along the major axis (longest dimension) when the particle is non-spherical. The particle size may be measured using any suitable method, for example, a scanning electron microscope or a particle size analyzer.
The method according one or more embodiments may include heating the formed product using a second thermal treatment to form the perovskite material. A heating rate of the second thermal treatment may be at about 1° C./min to about 10° C./min. A temperature of the second thermal treatment may be, for example, greater than the temperature of the first thermal treatment.
Prior to the second thermal treatment, the formed product (particle) may be pressed into a pellet form. When the formed product is pressed into pellet form and then subsequently heated using the second thermal treatment, a heat diffusion distance in the heated formed product is decreased, and the formation of a perovskite material may be facilitated. On the other hand, when the particle of the formed product is in powder form, and not in pellet form, the heat diffusion distance may be greater than when the formed product is in the pellet form, and as a result, the time and temperature of the second thermal treatment may be increased to form a perovskite material, as compared to when the second thermal treatment is performed on the pellet form.
The conditions of the second thermal treatment may be adjusted according to a predetermined oxidation number of M in Formula 1. For example, the second thermal treatment may be performed in an oxidizing gas atmosphere, a reducing gas atmosphere, or an inert gas atmosphere. The oxidizing gas atmosphere may be created, for example, using ambient air or oxygen. The reducing gas atmosphere may be created using a reducing gas such as hydrogen, and the inert gas atmosphere may be created using a gas such as nitrogen, argon, and/or helium.
The second thermal treatment may be performed at a temperature of about 900° C. to about 1500° C., or about 1000° C. to about 1400° C., or about 1100° C. to about 1200° C. The second thermal treatment time may vary depending on the temperature of the second thermal treatment. The second thermal treatment time may be, for example, about 1 hour to about 50 hours, for example, about 6 hours to about 48 hours, or about 10 hours to about 36 hours.
Through the second thermal treatment a perovskite material may be formed. In the preparation method according to one or more embodiments, if the temperature of the second thermal treatment is less than the temperature of the first thermal treatment, it may be difficult to obtain a perovskite material having a crystalline phase. When a time and temperature of the second thermal treatment are within the above-described ranges, the second thermal treatment may be capable of forming the perovskite material having a crystalline structure, and the synthesis time of the perovskite material may be short enough to be economically and commercially beneficial.
According to another aspect, a secondary battery includes a perovskite material according to any of the above-described embodiments. The secondary battery may include a cathode, an anode, and an electrolyte interposed between the cathode and the anode. The cathode, or each of the cathode and the electrolyte may include the perovskite material according to any of the above-described embodiments.
The secondary battery may be, for example, a lithium-air battery, a lithium ion battery, or an all-solid-state lithium secondary battery. The shape of the secondary battery is not limited and may have any of a variety of shapes, for example, a shape like a coin, a button, a sheet, a stack, a cylinder, a plane, or a horn. The secondary battery may also be used as a large-scale battery for an electric vehicle.
The secondary battery may be, for example, a lithium-air battery. The lithium-air battery may include a cathode including the perovskite material according to any of the above-described embodiments, a gas blocking layer (for example, an oxygen blocking layer), and a lithium-containing anode. Since the cathode of the lithium-air battery includes the perovskite material according to any of the above-described embodiments, the lithium-air battery may have improved charge and discharge characteristics. The cathode may also serve as an electrolyte.
Referring to
The cathode 11 may be manufactured by thermal treatment (heating) of the perovskite material according to any of the above-described embodiments at a temperature of about 500° C. to about 1400° C., or about 600° C. to about 1300° C., or about 750° C. to about 1200° C. When the thermal treatment temperature is within this range, the manufactured cathode 11 may have excellent ionic conductivity and electronic conductivity.
The weight and thickness of the cathode 11 manufactured as described above, are not limited. For example, the cathode 11 may have a weight of about 0.1 milligrams (mg) to about 1000 mg, or about 1 mg to about 750 mg, or about 10 mg to about 500 mg, and a thickness of about 0.1 μm to about 1000 μm, or about 1 μm to about 800 μm, or about 100 μm to about 500 μm.
Next, after the cathode 11 is disposed on a surface of the gas blocking layer 12, the anode 13 may be disposed on a surface of the gas blocking layer 12 opposite the cathode 11.
After the cathode 11 and the anode 13 are disposed on the gas blocking layer 12, a thermal treatment may be performed. The thermal treatment temperature may be, for example, about 500° C. to about 1000° C., or about 600° C. to about 1300° C., or about 750° C. to about 1200° C.
The anode 13 may be a lithium-containing anode. For example, the anode 13 may be a lithium metal thin film and/or a lithium-based alloy thin film. The lithium metal-based alloy may be an alloy of lithium with at least one of, for example, aluminum, tin, magnesium, indium, calcium, titanium, or vanadium.
The gas blocking layer 12, acts as a lithium ion conductive solid electrolyte membrane, and may also function as a protective layer for preventing direct reaction between the lithium metal anode and impurities such as oxygen. For example, the lithium ion conductive solid electrolyte membrane may be a layer including an inorganic material, for example, a lithium ion conductive glass, a lithium ion conductive crystal (e.g., ceramic or glass-ceramic), or a combination thereof. However, embodiments are not limited thereto. For example, any solid electrolyte membrane having lithium ion conductivity, impervious to oxygen, and capable of protecting the anode, may be used. For example, in view of chemical stability, the lithium ion conductive solid electrolyte membrane may include a metal oxide.
When the lithium ion conductive solid electrolyte membrane contains a large percentage of lithium ion conductive crystals, high ionic conductivity may be obtained. For example, the lithium ion conductive solid electrolyte membrane may include about 50 wt % or greater, for example, about 55 wt % or greater, or about 60 wt % or greater of lithium ion conductive crystals, based on a total weight of the lithium ion conductive solid electrolyte membrane.
The lithium ion conductive crystals may include for example, Li3N, a lithium super ionic conductor (LISICON), or crystals having a perovskite structure and lithium ion conductivity, for example, La055Li0.35TiO3; LiTi2P3O12 having a NASICON type structure; Li1+x+y(Al, Ga)x(Ti, Ge)2-xSiyP3-yO12 (wherein 0≤x≤1 and 0≤y≤1, for example, 0≤x≤0.4 and 0≤y≤0.6, or 0.1≤x≤0.3 and 0.1<y≤0.4); a glass-ceramic able to precipitate these crystals; or a combination thereof.
Non-limiting examples of a lithium ion conductive glass-ceramic may include lithium-aluminum-germanium-phosphate (LAGP), lithium-aluminum-titanium-phosphate (LATP), lithium-aluminum-titanium-silicon-phosphate (LATSP), or a combination thereof. For example, when a mother glass having a Li2O—Al2O3—TiO2—SiO2P2O5 composition is crystallized by a thermal treatment, the resulting primary crystal phase may be Li1+x+yAlxTi2-xSiyP3-yO12 (wherein 0≤x≤1 and 0≤y≤1). For example, in the formula of Li1+x+yAlxTi2-xSiyP3-yO12, x and y may satisfy, for example, 0≤x≤0.4 and 0<y≤0.6, for example, 0.1≤x≤0.3 and 0.1<y≤0.4.
The lithium ion conductive glass-ceramic of the gas blocking layer 12 may include Li1+x+yAlxTi2-xSiyP3-yO12 (wherein 0≤x≤1 and 0≤y≤1, for example, 0≤x≤0.4 and 0<y≤0.6, for example, 0.1≤x≤0.3 and 0.1<y≤0.4), or Li1+x+yAlx(Ti,Ge)2-xSiyP3-yO12 (wherein 0≤x≤2 and 0≤y≤3). For example, the gas blocking layer 12 may be a solid electrolyte membrane including LATP (Li1.4Ti1.6Al0.4P3O12).
In one or more embodiments, the lithium-air battery may further include a cathode intermediate layer (not shown) between the cathode 11 and the gas blocking layer 12. The lithium-air battery may further include an anode intermediate layer (not shown) between the gas blocking layer 12 and the anode 13. The cathode intermediate layer and the anode intermediate layer may suppress a side reaction that may take place between the cathode or the anode and the gas blocking layer 12. The cathode intermediate layer and the anode intermediate layer may each have a thickness of, for example, about 0.1 μm to about 10 μm, or about 1 μm to about 10 μm, or about 1 μm to about 7.5 μm.
The cathode intermediate layer and the anode intermediate layer may each include an electrolyte including at least one of a liquid electrolyte, a gel electrolyte, or a solid electrolyte.
The liquid electrolyte, the gel electrolyte, and the solid electrolyte are not particularly limited, and may be any electrolyte suitable for a lithium-air battery.
For example, the liquid electrolyte may include a solvent and a lithium salt. The solvent may include at least one of an organic solvent, an ionic liquid, or an oligomer. However, embodiments are not limited thereto. Any solvent in liquid form at room temperature (25° C.) may be used.
The organic solvent may include at least one of an ether-based solvent, a carbonate-based solvent, an ester-based solvent, or a ketone-based solvent. For example, the organic solvent may include at least one of propylene carbonate, ethylene carbonate, fluoroethylene carbonate, vinylethylene carbonate, butylene carbonate, dimethyl carbonate, diethyl carbonate, methylethyl carbonate, methylpropyl carbonate, ethylpropyl carbonate, methylisopropyl carbonate, dipropyl carbonate, dibutyl carbonate, benzonitrile, acetonitrile, tetrahydrofuran, 2-methyltetrahydrofuran, γ-butyrolactone, dioxolane, 4-methyldioxolane, dimethyl acetamide, dimethylsulfoxide, dioxane, 1,2-dimethoxyethane, sulfolane, dichloroethane, chlorobenzene, nitrobenzene, succinonitrile, diethylene glycol dimethyl ether (DEGDME), tetraethylene glycol dimethyl ether (TEGDME), polyethylene glycol dimethyl ether (PEGDME, Mn=˜500), dimethyl ether, diethyl ether, dibutyl ether, or dimethoxyethane. However, embodiments are not limited thereto. The organic solvent may be any organic solvent that is in liquid form at room temperature.
The lithium salt may include at least one of LiTFSI, LiPF6, LiBF4, LiAsF6, LiNO3, lithium bis(oxalato) borate (LiBOB), LiCF3SO3 (lithium trifluoromethanesulfonate, lithium triflate, LiTfO), LiN(SO2CF3)2, LiN(SO2C2F5)2, LiC(SO2CF3)3, LiN(SO3CF3)2, LiC4F9SO3, or LiAlCl4. However, embodiments are not limited thereto. Any materials suitable for use as a lithium salt may be used. A concentration of the lithium salt may be about 0.01 molar (M) to about 3.0 M. However, embodiments are not limited thereto. The concentration of the lithium salt may be appropriately adjusted as desired.
A non-limiting example of the solid electrolyte may include at least one of an ionically conducting polymer, a polymeric ionic liquid (PIL), an inorganic electrolyte, a polymer matrix, or an electronically conducting polymer. The polymer matrix may not have ionic conductivity or electronic conductivity.
The solid electrolyte may include at least one of polyethylene oxide (PEO), a solid graft copolymer including at least two polymer blocks having low glass transition temperatures (Tg), poly(diallyldimethylammonium)/bis(trifluoromethanesulfonyl) imide (poly(diallyldimethylammonium)TFSI), Cu3N, Li3N, lithium phosphorous oxynitride (LiPON), Li3PO4.Li2S.SiS2, Li2S.GeS2 Ga2S3, Li2O.11Al2O3, Na2O.11Al2O3, (Na,Li)1+xTi2-xAlx(PO4)3 (wherein 0.1≤x≤0.9), Li1+xHf2-xAlx(PO4)3 (wherein 0.1≤x≤0.9), Na3Zr2Si2PO12, Li3Zr2Si2PO12, Na5ZrP3O12, Na5TiP3O12, Na3Fe2P3O12, Na4NbP3O12, a Na-silicate, Li0.3a0.5TiO3, Na5MSi4O12 (wherein M may be a rare earth element, for example, Nd, Gd, or Dy), Li5ZrP3O12, Li5TiP3O12, Li3Fe2P3O12, Li4NbP3O12, Li1+x(M,Al,Ga)x(Ge1-yTiy)2-x(PO4)3 (wherein 0≤x≤0.8, 0≤y≤1.0, and M may be Nd, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, or Yb), Li1+x+yQxTi2-xSiyP3-yO12 (wherein 0≤x≤0.4, 0<y≤0.6, and Q may be Al or Ga), Li6BaLa2Ta2O12, Li7La3Zr2O12, Li5La3Nb2O12, Li5La3M2O12 (wherein M may be Nb or Ta), or Li7+xAxLa3-xZr2O12 (wherein 0<x≤3 and A may be Zn).
The solid electrolyte may include, as an ion conductive polymer, an ion conductive repeating unit which may be at least one of an ether-based monomer, an acryl-based monomer, a methacryl-based monomer, or a siloxane-based monomer.
The ion conductive polymer may be at least one of polyethylene oxide, polypropylene oxide, poly(methyl methacrylate), poly(ethyl methacrylate), polydimethylsiloxane, polyacrylate, polyethyl acrylate, poly(2-ethylhexyl acrylate), poly(butyl methacrylate), poly(2-ethylhexyl methacrylate), poly(decyl acrylate), or polyethylene vinyl acetate. The ion conductive polymer may be a copolymer including an ion conductive repeating unit and a structural repeating unit. The ion conductive repeating unit may be derived from at least one monomer of acrylic acid, methacrylic acid, methyl acrylate, methyl methacrylate, ethyl acrylate, ethyl methacrylate, 2-ethylhexyl acrylate, butyl methacrylate, 2-ethylhexyl methacrylate, decyl acrylate, ethylene vinyl acetate, ethylene oxide, or propylene oxide. For example, the structural repeating unit may be derived from at least one monomer of styrene, 4-bromo styrene, tert-butylstyrene, divinylbenzene, methyl methacrylate, isobutyl methacrylate, butadiene, ethylene, propylene, dimethyl siloxane, isobutylene, N-isopropyl acrylamide, vinyl fluoride, acrylonitrile, 4-methyl-1-pentene, butylene terephthalate, ethylene terephthalate, or vinyl pyridine. The ion conductive polymer may be a block copolymer including an ion conductive phase and a structural phase. Examples of the block copolymer including an ion conductive phase and a structural phase may include block copolymers disclosed in U.S. Pat. Nos. 8,269,197 and 8,563,168, and U.S. patent publication No. 2011/0206994, the contents of each of which are incorporated herein by reference in their entirety.
The anode intermediate layer may include a solid polymer electrolyte. For example, the solid polymer electrolyte may be polyethylene oxide (PEO) doped with a lithium salt, wherein non-limiting examples of the lithium salt may be at least one of LiN(SO2F)2, LiBF4, LiPF6, LiSbF6, LiAsF6, LiClO4, LiCF3SO3, LiN(SO2CF3)2, LiN(SO2C2F5)2, LiC(SO2CF3)3, LiN(SO3CF3)2, LiC4F9SO3, or LiAlCl4. The anode intermediate layer may be a polymer electrolyte prepared by mixing polyethylene oxide and a lithium salt.
The cathode intermediate layer may be, for example, a polymer electrolyte prepared by mixing poly(oxyethylene methacrylate) poly(dimethyl siloxane) and a lithium salt.
The lithium-air battery may further include an electrolyte. The electrolyte may have a structure including a separator impregnated with a solid polymer electrolyte. The structure having the separator impregnated with the solid polymer electrolyte may be prepared by disposing a solid polymer electrolyte film on one or both surfaces of the separator and roll-pressing the separator-film structure at the same time. In some embodiments, the structure may be prepared by injecting a liquid electrolyte including a lithium salt into the separator.
Next, after mounting the anode on an inner side of a case, the cathode with the gas blocking layer thereon may be disposed on the anode. The anode intermediate layer, when present, may be further disposed between the anode and the gas blocking layer. The cathode intermediate layer, when present, may be further disposed between the gas blocking layer and the cathode. The gas blocking layer may be oxygen blocking layer.
Next, a gas diffusion layer including metal or carbon may be disposed on the cathode, thereby completing the manufacture of the lithium-air battery.
One or more embodiments of the inventive concept will now be described in detail with reference to the following examples. However, these examples are only for illustrative purposes and are not intended to limit the scope of the one or more embodiments of the inventive concept.
Li2CO3, La2O3, and RuO2 powders were added into ethanol in stoichiometric amounts to provide the composition of Li0.34La0.55RuO3-δ (wherein 0≤δ≤1), and then mixed. The resulting mixture was then put into a ball-mill mixer and pulverized and mixed for about 4 hours. The resulting mixture was dried and then heated to about 800° C. at a heating rate of about 5° C./min, followed by a continuous first thermal treatment at the same temperature for about 4 hours in an air atmosphere.
The resulting heated mixture obtained after the first thermal treatment was pulverized into a powder (primary particles) having a particle size of about 0.3 μm. This powder was then pressed to form cylindrical pellets having a diameter of about 1.3 centimeters (cm), a height of about 0.5 cm, and a weight of about 0.3 grams (g). The pellets were then subjected to a second thermal treatment in an air atmosphere at a temperature of about 1200° C. for about 24 hours to obtain a target product. For the second thermal treatment, the temperature was increased to 1200° C. at a heating rate of about 5° C./min. The target product was Li0.34La0.55RuO3-δ with 6=0 and/or 0<61.
A target product was obtained in the same manner as in Example 1, except that Ni(OH)2 was used instead of RuO2. The target product was Li0.34La0.55NiO3-δ with δ=0 and/or 0<δ≤1.
A target product was obtained in the same manner as in Example 1, except that MnO2 was used instead of RuO2. The target product was Li0.34La0.55MnO3-δ with δ=0 and/or 0<δ≤1.
A target product was obtained in the same manner as in Example 1, except that Cr2O3 was used instead of RuO2. The target product was Li0.34La0.55CrO3-δ with δ=0 and/or 0<δ≤1.
A target product was obtained in the same manner as in Example 1, except that Co2O3 was used instead of RuO2. The target product was Li0.34La0.55CoO3-δ with δ=0 and/or 0<δ≤1.
A target product was obtained in the same manner as in Example 1, except that IrO2 was used instead of RuO2. The target product was Li0.34La0.55CoO3-δ with δ=0 and/or 0<δ≤1.
A target product was obtained in the same manner as in Example 1, except that TiO2 was used instead of RuO2 and both the first thermal treatment and the second thermal treatment were performed at about 1000° C.
A cathode having a weight of about 5 milligrams per square centimeter (mg/cm2) per unit area and a thickness of about 10 μm was manufactured by heating the perovskite material Li0.34La0.55RuO3-δ (wherein 0≤δ≤1) prepared according to Example 1 at about 1000° C. under the air atmosphere for about 60 minutes.
A lithium-aluminum-titaniumphosphate (LATP) layer having a thickness of about 250 μm(available from Ohara Corp., Japan) was disposed as a gas blocking layer on a lower surface of the cathode, and the lower surface of the cathode with the gas blocking layer was heated at about 900° C. for about 60 minutes.
A polymer electrolyte as an anode intermediate layer was disposed under the gas blocking layer. The polymer electrolyte was prepared by mixing polyethylene oxide (Mn=100,000 Daltons) and lithium bis(trifluoromethylsulonly)imide (LiTFSI) as a lithium salt in an EO/Li molar ratio of 20:1.
A lithium metal foil was disposed under the polymer electrolyte, and a gas diffusion layer (GDL) (25BC, available from SGL) was attached to an upper surface of the cathode. A nickel mesh was disposed on the GDL, and then pressed with a pressing member capable of transferring air to the cathode to fix the cell, thereby manufacturing a lithium-air battery.
A lithium-air battery was manufactured in the same manner as in Example 7, except that the perovskite material Li0.34La0.55MnO3-δ (wherein 0≤δ≤1) prepared according to Example 3 was used instead of the perovskite material Li0.34La0.55RuO3-δ (wherein 0≤δ≤1) of Example 1.
A cathode having a weight of about 5 mg/cm2 per unit area and a thickness of about 10 μm was manufactured by heating the perovskite material Li0.34La0.55RuO3-δ (wherein 0≤δ≤1) prepared according to Example 1 at about 1000° C. under the air atmosphere for about 60 minutes.
A polymer electrolyte as a cathode intermediate layer was disposed on a surface of a lithium-aluminum-titaniumphosphate (LATP) layer having a thickness of about 250 μm(available from Ohara Corp., Japan) and serving as a gas blocking layer. This polymer electrolyte was prepared by mixing a copolymer of poly(oxyethylene methacrylate) and polydimethyl siloxane (Mn=100,000 Daltons)(a weight ratio of poly(oxyethylene) methacrylate and polydimethyl siloxane=7:3) and lithium bis(trifluoromethylsulonly)imide (LiTFSI) as a lithium salt in an EO/Li molar ratio of 20:1.
Subsequently, a polymer electrolyte as an anode intermediate layer was disposed on an opposite surface of the gas blocking layer. This polymer electrolyte was prepared by mixing polyethylene oxide (Mn=600,000 Daltons) and lithium bis(trifluoromethylsulonly)imide (LiTFSI) as a lithium salt in an EO/Li molar ratio of 20:1.
A lithium metal foil was disposed under the polymer electrolyte, and a gas diffusion layer (GDL) (25BC, available from SGL) was attached to an upper surface of the cathode. A nickel mesh was arranged on the GDL, and then pressed with a pressing member capable of transferring air to the cathode to fix the cell, thereby manufacturing a lithium-air battery.
Example 10
A lithium-air battery was manufactured in the same manner as in Example 9, except that the perovskite material Li0.34La0.55MnO3-δ (wherein 0≤δ≤1) prepared according to Example 3 was used instead of the perovskite material Li0.34La0.55RuO3-δ (wherein 0≤δ≤1) of Example 1.
Perovskite materials were prepared in the same manner as in Example 1, except that the amounts of Li2CO3, La2O3, and RuO2 were varied to provide the perovskite materials represented in Table 1.
Perovskite materials were prepared in the same manner as in Example 3, except that the amounts of Li2CO3, La2O3, and MnO2 were varied to provide the compositions of perovskite materials represented in Table 2.
A lithium-air battery was manufactured in the same manner as in Example 7, except that the perovskite material Li0.34La0.55TiO3-δ (wherein 0≤δ≤1) prepared according to Comparative Example 1 was used instead of the perovskite material Li0.34La0.55RuO3-δ (wherein 0≤δ≤1) of Example 1.
The perovskite materials of Examples 1 to 6 and Comparative Example 1 were analyzed by X-ray diffraction (XRD) analysis. The results of the X-ray diffraction analysis are shown in
The XRD spectrometry was performed using a Bruker D8 Advance diffractometer with Cu Ka radiation. Based on the results of the XRD spectrometry on each of the perovskite materials, a ratio (Ib/Ia) of a peak intensity (I(46.5°±2.5°): Ib) at a diffraction angle 2θ of 46.5°±2.5° to a peak intensity (I(32.5°±2.5°): Ia) at a diffraction angle 2θ of 32.5°±2.5°, and a ratio (Ic/Ia) of a peak intensity (I(57.5°±2.5°): Ic) at a diffraction angle 2θ of 57.5°±2.5° to a peak intensity (I(32.5°±2.5°): Ia) at a diffraction angle 2θ of 32.5°±2.5° were calculated. The results are represented in Table 3.
Referring to Table 3 and
Electronic conductivities and ionic conductivities of the perovskite materials of Examples 1 to 6 and Comparative Example 1 were measured. The results are represented in Table 4 and
Referring to Table 4 and
The lithium air batteries of Examples 7 and 8 and Comparative Example 2 were discharged with a constant current of 0.01 milliampere per square centimeter (mA/cm2) under the conditions of about 60° C. and 1 atmosphere (atm) oxygen pressure until a voltage of 2.0 volts (V) with respect to Li was reached. The lithium-air battery was then charged with the same current until a voltage of 4.3 V was reached (1st charge and discharge cycle). Results of the charge and discharge test at the 1st charge and discharge cycle are shown in
Referring to
Charge and discharge characteristics of the lithium air batteries of Example 9 and Example 10 were also evaluated in the same manner as applied to the lithium air batteries of Example 7 and Example 8. As a result of the charge and discharge characteristic evaluation, charge and discharge characteristics of the lithium air batteries of Examples 9 and 10 were found to be nearly similar to those of the lithium air batteries of Examples 7 and 8.
After separately pulverizing the perovskite materials of Examples 1 and 3, 85% by weight of a pulverized product, 10% by weight of carbon black as a conducting agent, and 5% by weight of polyvinylidene fluoride (PVDF) as a binder were mixed together in N-methyl-2-pyrrolidone (NMP) used as a solvent to prepare a slurry. The slurry was coated on an aluminum foil and then dried to manufacture a working electrode. The working electrode and a lithium metal foil as a counter electrode were assembled together with a separator disposed between the working electrode and the counter electrode, the separator impregnated with a liquid electrolyte (1M LiTFSI in propylene carbonate (PC)), thereby completing manufacture of a half-cell.
Electrochemical stability of each of the perovskite materials, each coated on the lithium metal, was evaluated by cyclic voltammetry (CV) in which a voltage in a range of about 2 V to about 4 V (with respect to Li) was applied to the half-cell at a scanning rate of about 0.1 millivolts per second (mV/sec). The results are shown in
As shown in
As described above, according to the one or more embodiments, a secondary battery including a cathode containing the perovskite material according to any of the above-described embodiments may have improved charge and discharge characteristics.
It should be understood that embodiments described herein should be considered in a descriptive sense only and not for purposes of limitation. Descriptions of features or aspects within each embodiment should be considered as available for other similar features or aspects in other embodiments.
While an embodiment has been described with reference to the figures, it will be understood by those of ordinary skill in the art that various changes in form and details may be made therein without departing from the spirit and scope as defined by the following claims.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10-2018-0122041 | Oct 2018 | KR | national |
This application claims priority to and the benefit of U.S. Provisional Application No. 62/744,614, filed on Oct. 11, 2018, and Korean Patent Application No. 10-2018-0122041, filed on Oct. 12, 2018, and all the benefits accruing therefrom under 35 U.S.C. § 119, the contents of which are incorporated herein by reference in their entirety.