1. Field of the Invention
The present invention relates to a perpendicular magnetic recording medium which comprises a substrate and a multi-layered magnetic film composed of ferromagnetic metal layers and non-magnetic metal layers which are laminated alternately on top of the other.
2. Description of Related Arts
The recent advance in information society demands data recording apparatus, such as hard disk drive (“HDD” hereinafter) , with higher performance. Improving the performance of HDD is synonymous with increasing the recording density. One promising technology to meet this demand is the perpendicular magnetic recording system which magnetizes the medium perpendicularly to the film plane, rather than in the plane. There are several candidates as the magnetic material for the recording layer of the perpendicular magnetic recording medium. Among them are CoCr-based alloys incorporated with Pt, Ta, B, etc. as additives, which have been investigated most closely.
A recording medium of CoCr-based alloy is superior in recording characteristics, but CoCr-based alloy itself has insufficient perpendicular magnetic anisotropy energy (Ku) which holds the magnetization in its orientation. For this reason, CoCr-based alloy gives an M-H curve with a squareness ratio much smaller than 1 and permits small reversed magnetic domains to appear in magnetic recording domains, thereby reducing the strength of reproduced signals. Even though its M-H curve has a squareness ratio close to 1, CoCr-based alloy is still susceptible to “thermal signal loss” which is a phenomenon that the state of magnetization changes after recording due to thermal disturbance.
To cope with this situation, there has been proposed a recording medium in which the recording layer is a multi-layered film composed of thin films (with a thickness of an atomic order) laminated alternately on top of the other. This recording layer can be designed such that the magnetic structure formed by the magnetic head remains unchanged with time owing to its sufficiently large value of Ku.
The structure of the multi-layered film mentioned above is generally referred to as superlattice structure. It takes on a variety of physical properties owing to the state peculiar to the interface between atomic layers. It is known that the magnetic thin film of multi-layered structure has a large perpendicular magnetic anisotropy energy if it is formed from ferromagnetic metal (such as Co and Fe) and noble metal (such as Pd, Pt, and Au) laminated alternately. This multi-layered structure of ferromagnetic metal and noble metal is used in the perpendicular magnetic recording medium disclosed in U.S. Pat. Nos. 4,587,176, 4,678,721, and 5,106,703.
Unfortunately, the magnetic recording medium with the magnetic thin film mentioned above has a larger recording noise than the perpendicular recording medium of CoCr-based alloy. In other words, it is not necessarily superior in recording properties. The cause of recording noise arises from the reversal mechanism of the multi-layered magnetic film as has been pointed out in many studies.
The fact that CoCr-based alloy thin film is capable of low-noise recording is because there exist ferromagnetic fine particles in the film, with each particle being magnetically isolated by a phase with rich Cr which has spread out on its periphery. By contrast, the multi-layered magnetic film, which takes no special effort to form the fine structure in the magnetic film, permits magnetization reversal to take place in a large area as a unit. Therefore, the magnetic domain for recording has a zigzag contour regardless of the distribution of the magnetic field applied by the recording head. This zigzag contour reflects the random distribution of the magnetic properties of the magnetic film, and hence it brings about recording noise. To address the problem involved with the multi-layered magnetic film,. comprehensive studies have been made on a variety of additives and underlying materials.
Attempts have been made to use a multi-layered magnetic film of Co and Pd or Pt as a magnetic recording medium. Its composition, structure, and manufacturing method intended for better recording characteristics are disclosed in Toku-Hyo-Hei 11-501755 (Japanese translation of PCT international publication WO96/24927). According to this disclosure, each magnetic metal layer is made of Co or Co alloy with a thickness of 0.15-1.0 nm and a noble metal layer with a thickness of 0.5-1.5 nm. The number of the magnetic metal layers, each including one noble metal layers, is 10-30. The magnetic recording medium of this structure has a coercive force larger than 2.5 kOe. In addition, according to the disclosure, the multi-layered magnetic film and its nuclei-forming layer (such as Pd) should have a total thickness smaller than 150 nm so as to avoid an unnecessarily large space between the recording head and the backing soft magnetic layer (NiFe).
Moreover, an effective way of reducing the noise of recording medium is also disclosed in the patent publication just mentioned above. The disclosure mentions that the recording film should be made by sputtering with an oxygen-containing sputtering gas at a reduced degree of vacuum and at a high sputtering gas pressure, and annealing should be performed before and after the film forming step. The disclosure further mentions that it is possible to reduce the recording noise if the Co alloy layer is formed from CoCr or CoCrTa.
Another perpendicular magnetic recording medium with a multi-layered magnetic film of Pd/CoCr is disclosed in Appl. Phys. Lett. 64(21) pp. 2891-2893 by B. M Lairson et. al. This thesis deals with how the recording characteristics vary depending on the thickness of the CoCr layer and the amount of Cr added. With the thickness of the Pd layer fixed at 0.4 nm, it concludes that the recording characteristics are satisfactory if the content of Cr is about 15 at %.
The present inventors repeated the procedure mentioned in the foregoing patent publication (11-501755) to reproduce the sample No. 12 given in page 22. This sample is a multi-layered magnetic recording film composed of ferromagnetic layers of CoCr-based alloy and noble metal layers which are laminated alternately on top of the other. The recording film is of superlattice structure consisting of CoCr layers (0.35 nm) and Pd layers (1.0 nm), with a Pd underlying layer (20 nm). The CoCr-based alloy contains 12 at % Cr. The reproduced sample was actually tested for recording and reproducing performance. The test results indicate that the sample is stable to thermal disturbance but is not particularly superior to the conventional CoCrPt recording medium (proposed by Takano et al., Digest of Intermag 2000, AD-06).
The recording medium reproduced by the present inventors has a higher level of recording noise than the CoCrPt medium (just mentioned above) despite incorporation with Cr. A probable reason for this is that magnetic exchange interaction between particles is not sufficiently reduced. On the other hand, the magnetic film has a greatly decreased level of saturation magnetization (˜100 kA/m) because the CoCr-based alloy contains 12 at % Cr. This results in a significant decrease in reproduced signal intensity. It was found that the S/N ratio of the reproduced recording medium is lower by 10 dB or less than that of the conventional CoCrPt recording medium, when measured with the same recording/reproducing head due to the increased noise (N) and the decreased signal (S).
The reason why the reproduced recording signal shows the sufficiently low recording noise is that Cr in the ferromagnetic layer of CoCr-based alloy does not fully block magnetic exchange interaction between magnetic fine particles. The laminate structure disclosed in the above-mentioned patent publication (11-501755) is characterized in that the ferromagnetic layer of CoCr-based alloy (of 0.35 nm thick) is relatively thinner than the noble metal (Pd) layer (of 1.0 nm thick). This thickness ratio is inadequate to reduce the magnetic exchange interaction between magnetic particles to such an extent as to suppress recording noise because there exists the magnetic exchange interaction between particles also in the Pd alloy layer due to magnetization induced in the Pd alloy layer by the ferromagnetic layer of CoCr-based alloy. In addition, the small saturation magnetization is apparently due to the excessively thin ferromagnetic layer of CoCr-based alloy.
However, the above-mentioned report by Lairson et al. shows (in
The foregoing suggests that the magnetic layer for recording cannot be applied in the practical perpendicular magnetic recording system simply because its axis of magnetization is perpendicular to the magnetic recording medium. Tackling this problem motivated the present invention. Accordingly, it is an object of the present invention to provide a perpendicular magnetic recording medium characterized by reduced recording noise such that the magnetic particles become less susceptible thermal disturbance.
In order to achieve the above-mentioned object, the present inventors studied the magnetic recording medium having a multi-layered magnetic film composed of ferromagnetic metal layers containing Co and non-magnetic metal layers containing Pd which are laminated alternately on top of the other. The result suggests that it is possible to obtain a perpendicular magnetic recording medium exhibiting sufficient perpendicular magnetic anisotropy energy with the recording noise reduced below a certain level, if the multi-layered magnetic film has a specific composition and layer structure and is produced under specific conditions.
The present invention is based on this finding. Thus, the gist of the present invention resides in a perpendicular magnetic recording medium having a substrate and a multi-layered magnetic film formed thereon with or without an underlying layer interposed between them. The multi-layered magnetic film is composed of ferromagnetic metal layers containing Co and non-magnetic metal layers containing Pd which are laminated alternately on top of the other, characterized in that the ratio of film thickness defined by d1/d2 ranges from 1.5 to 4.0, where d1 denotes the thickness of each of said ferromagnetic metal layers and d2 denotes the thickness of each of said non-magnetic metal layers which is between 0.6 nm and 2.0 nm (0.6nm≦d2≦2.0 nm).
The perpendicular magnetic recording medium constructed as mentioned above may be modified such that the ferromagnetic metal layers are formed from CoCr-based alloy. The resulting multi-layered magnetic film has a low level of recording noise due to the reduction in magnetic exchange interaction between magnetic particles and also has good resistance to thermal disturbance due to the sufficient perpendicular magnetic anisotropy energy to resist the demagnetizing field energy induced by magnetization of the magnetic film.
The gist of the present invention resides also in a process for producing the perpendicular magnetic recording medium, which comprises a step of forming a first underlying layer on a substrate which may contains, ex. Pd, a step of forming a second underlying layer which may contains, ex. CoCr40, then a multi-layered magnetic film composed of alternately laminated ferromagnetic metal layers containing Co and non-magnetic metal layers containing Pd.
The above-mentioned process is preferably modified such that an initial layer containing a paramagnetic Co alloy interposed between the underlying layer and the multi-layered magnetic film. In addition, the step of forming the multi-layered magnetic film is preferably followed by heat treatment in a vacuum at a temperature higher than 350° C.
A preferred embodiment of the present invention is illustrated in the accompanying drawings in which:
As shown in
The multi-layered magnetic film 14 shown in
To incorporate with Cr to reduce magnetic exchange interaction between particles, the ferromagnetic metal layers of CoCr-based alloy (“CoCr-based alloy layers” hereinafter) should be thicker than the non-magnetic metal layers of Pd alloy (“Pd alloy layers” hereinafter), so that the grain boundary with a high Cr concentration produces a strong effect. Specifically, the ratio of d1/d2 should range from 1.5 to 4.0, where d1 denotes the thickness of each of the ferromagnetic metal layers and d2 denotes the thickness of each of the non-magnetic metal layers.
The multi-layered film structure in the perpendicular magnetic recording medium 10 exhibits the interface magnetic anisotropy Ks and increases the perpendicular magnetic anisotropy energy Ku only when the thickness d2 of the Pd alloy layer is 0.6 nm or larger. If the Pd alloy layer is excessively thin, the surface magnetic anisotropy becomes small despite the multi-layered film structure. If the Pd alloy layer is excessively thick, magnetic exchange interaction between CoCr-based alloy layers may be insufficient and individual layers may have different coercive force. Therefore, the thickness of the Pd alloy layer should be 2.0 nm or less. Thus the thickness of the Pd alloy layer should be in the range of 0.6 nm to 2.0 nm, preferably 0.8 nm to 1.2 nm.
The ratio of d1/d2 should be in the range of 1.5 to 4.0. If the ratio of d1/d2 is smaller than 1.5, there is large magnetic exchange interaction between particles and large domain wall displacement at the time of recording, which lead to large recording noise. If the ratio of d1/d2 is larger than 4.0, the thickness of each of the ferromagnetic metal layers is large and the effect of increasing perpendicular magnetic anisotropy energy by Ks become negligible. Thus, the multi-layered film structure will not improve thermal stability.
In the case of magnetic recording medium with a multi-layered film composed of CoCr-based alloy layers and noble metal layers which are laminated alternately, it has been common practice to reduce the laminating period (λ) so as to increase the surface magnetic anisotropy energy Ks induced by the layer interfaces.
Under the condition specified by the thickness ratio of d1/d2, the value of λ is inevitably large and hence the crystal magnetic anisotropy energy Kv of each CoCr-based alloy layer accounts for a larger portion in the total perpendicular magnetic anisotropy energy Ku of the multi-layered magnetic films. Therefore, Ks merely enhances Ku, and it is essential that each CoCr-based alloy layer has a large value of Kv. Therefore, it is necessary to produce the multi-layered structure to obtain a high value of Kv.
One way to increase the value of Kv is to keep as low as possible the Cr concentration in the CoCr-based alloy layer. Unfortunately, reducing the Cr concentration in CoCr-based alloy generally tends to weaken the effect of reducing the magnetic exchange interaction between particles at the Cr grain boundary. (This is also applicable to monolayer CoCr-based alloys.) Up to now, a Cr concentration of 20% is the minimum amount to reduce the magnetic exchange interaction between particles and to suppress the recording noise.
However, the present inventors found that it is possible to sufficiently reduce the magnetic exchange interaction between particles in the multi-layered magnetic film 14 even though the Cr concentration is reduced below 20% in the CoCr-based alloy layer, if the following production process is adopted.
It was found that if the initial layer contains more than 30 at % of Cr or Cu, the magnetic exchange interaction between particles in the multi-layered magnetic film 14 greatly decreases, and consequently recording noise decreases. A probable reason for this phenomenon is that the reheating process causes Cr or Cu atoms in the initial layer to diffuse through grain boundary (with high Cr concentration) in the direction perpendicular to the multi-layered magnetic film 14, and this diffusion enhances the effect of decreasing the magnetic exchange interaction between particles at clear grain boundaries.
A single-layered recording film of CoCr-based alloy has a large value of Kv, but because of low Cr content, it also-has a high value of Ms (saturation magnetization) and hence a high value of demagnetizing energy. This large demagnetic-energy makes saturation recording difficult, and hence it is not suitable for use as the perpendicular magnetic recording medium.
On the other hand, the multi-layered magnetic film 14 which applies the above high-Kr CoCr (-based) alloy decreases in Ms due to the lamination with the Pd alloy layer and hence the demagnetizing field energy decreases to a proper value. Therefore, the CoCr-based alloy thin film, which has a high value of Kv (crystal magnetic anisotropy energy) and a high value of Ms (saturation magnetization), is provided for use as the CoCr-based alloy layer in the multi-layered magnetic film 14 according to the present invention.
Moreover, the magnetic recording medium 10 of the present invention is preferably modified such that the ferromagnetic metal layer in the multi-layered magnetic film 14 contains Pt in addition to Co and Cr. (The Pt-containing metal layer will be simply referred to as a “CoCrPt alloy layer”.)
The incorporation of Pt causes the conventional CoCr-based alloy medium to increase in perpendicular magnetic anisotropy energy has been reported many times. The present inventors found that the same phenomenon is also applicable to the multi-layered magnetic film according to the present invention.
In other words, the CoCrPt alloy layer used as the ferromagnetic metal layer in the multi-layered magnetic film 14 has a larger value of Ku than the CoCr-based alloy layer. This suggests that Pt added to the CoCr-based alloy layer increases the value of Kv (crystal magnetic anisotropy energy). Thus, the incorporation of Pt into the CoCr-based alloy layer is preferred.
It appears that the perpendicular magnetic recording medium exhibits better magnetic characteristics if it has the multi-layered magnetic film 14 composed of CoCrPt alloy layers (with a low Cr concentration) and Pd alloy layers (non-magnetic metal layers) which are laminated alternately, and if heat treatment is performed after the multi-layered magnetic film 14 has been formed.
A detailed description is given below of the kind and amount of elements to be added to the multi-layered magnetic film 14. The Cr concentration in the ferromagnetic metal layer should be in the range of 12 at % to 21 at %. As mentioned above, the lower the Cr concentration in the ferromagnetic metal layer, the greater the value of Kv. However, if the Cr concentration is lower than 12 at %, the resulting magnetic recording medium has a high level of recording noise due to magnetic exchange interaction between particles which cannot be reduced even by heat treatment. By contrast, if the Cr concentration is 21 at %, the resulting magnetic recording medium has an adequate level of magnetic exchange interaction between particles even though no heat treatment is performed.
Also, the Pt concentration in the ferromagnetic metal layer should be in the range of 10 at % to 16 at %. The Pt added to the ferromagnetic metal layer increases the value of Kv. The effect of Pt becomes maximum when the Pt concentration is higher than 10 at %. However, if the Pt concentration exceeds 16 at %, the magnetic exchange interaction between particles increases, and the recording noise increases accordingly. A probable reason for this is that Pt atoms prevent Cr atoms from displacement toward the grain boundaries.
In addition, it is desirable to add a small amount of B or Ta to the multi-layered film. In general, B or Ta added to the multi-layered film promotes displacement of Cr atoms toward the grain boundaries. However, an excess amount of B or Ta greatly lowers the perpendicular magnetic anisotropy; therefore, their amount is preferably several at %, at most.
The present inventors also studied the magnetic recording medium in which a Pt layer is used as the non-magnetic metal layer. However, it was found that the Pt layer did not contribute to good characteristics. If a Pt alloy layer is used as the non-magnetic metal layer, the interface between the Pt alloy layer and the CoCr-based alloy layer is mixed during sputtering at a low gas pressure. This leads to an insufficient level of Ks (surface magnetic anisotropy energy). In order to use Pt non-magnetic metal layer, the production of the multi-layered magnetic film needs a high sputtering gas pressure in order to achieve a large value of Ks. On the other hand, it is necessary to raise the degree of crystallization of CoCr-based alloy in order to increase the value of Kv. To this end, it is desirable to perform sputtering at a low gas pressure in order to prevent the sputtering gas from entering the alloy. These film-forming conditions are incompatible with one another for the Pt non-magnetic metal layer.
The results of the present inventors' investigation revealed that a large value of Ks can be obtained at a comparatively low gas pressure if the non-magnetic metal layer is composed mainly of Pd the multi-layered magnetic film 14 composed of ferromagnetic metal layers and non-magnetic metal layers each one layer of which is alternately laminated on top of one layer of the other kind. The magnetic recording film 14, in which Pd is a major component in the non-magnetic metal layer, has high surface magnetic anisotropy, with the CoCr-based alloy layer keeping high crystal magnetic anisotropy.
Incidentally, the multi-layered magnetic film 14 is not specifically restricted in thickness. However, it should have an adequate thickness corresponding to the perpendicular magnetic anisotropy of the multi-layered magnetic film 14, because it is vulnerable to thermal disturbance if it is excessively thin.
The perpendicular magnetic recording medium according to the present invention is described more in detail with reference to the following examples.
This example demonstrates the perpendicular magnetic recording medium according to the present invention, in which the substrate is a glass disk (76 mm in diameter) with a planarized surface suitable for HDD. This glass disk has a hole (an inside diameter of 15 mm) at its center through which it is placed on to a spindle.
This glass disk was mounted on a sputtering apparatus and then heated at about 100° C. to remove any adsorbed water. On the glass disk was formed an underlying layer (40 nm thick) from NiTa37Zr10 alloy. On the underlying layer was sequentially formed a Pd film (5 nm thick), a multi-layered magnetic film, a Pd film (1 nm thick), and a carbon protective film. The multi-layered magnetic film is composed of noble metal layers and ferromagnetic metal layers each one layer of which are laminated alternately on top of one layer of the other kind.
The multi-layered magnetic film is formed by using a rotary cathode device as shown in
If two target cathodes (A and B) are mounted on the rotary cathode device and they are subjected to discharging, it is possible to form a multi-layered film (composed of layers A and layers B which are laminated alternately) in a short time (hereinafter “simultaneous discharging method”).
This rotary cathode device gives rise to a multi-layered magnetic film 31 shown in
It is also possible to form the multi-layered structure as shown in
In general, the simultaneous discharging method is advantageous over the alternate discharging method in producing the multi-layered magnetic film of periodic structure in a short time. Therefore, the simultaneous discharging method was employed in this and following examples.
In this example, a recording medium of multi-layered structure having a multi-layered magnetic film composed of ferromagnetic metal layers of CoCr21 (referred to as CoCr21 alloy layers) and noble metal layers of Pd which are laminated alternately on top of the other was prepared. (“Pd/CoCr21 medium” hereinafter.)
In this example, a recording medium of multi-layered structure having a multi-layered magnetic film composed of ferromagnetic metal layers of CoCr21 (referred to as CoCr21 alloy layers) and noble metal layers of Pt which are laminated alternately on top of the other was also prepared for comparison. (“Pd/CoCr21 medium” hereinafter.)
The multi-layered magnetic film was formed such that each CoCr21 alloy layer is 2.0 nm thick and each noble metal layer is 0.2-1.4 nm thick, with the total thickness being 20 nm. The layer thickness d1 and d2, the thickness ratio d1/d2, and the laminating period were controlled by regulating the sputtering power onto the noble metal target and Co alloy target, as well as the speed of the rotary cathode device. The substrate was preheated so that its temperature was 250° C. when the multi-layered magnetic film was formed.
In a comparative example, a perpendicular magnetic recording medium which consists of a substrate, an underlying layer (40 nm thick) of NiTa37Zr10 alloy, a Pd film (5 nm thick), a single-layered magnetic film (20 nm thick) of CoCr21, a Pd film (1 nm thick), and a carbon protective film was prepared (“CoCr21 medium” hereinafter). The single-layered magnetic film is a CoCr21 film having the axis of magnetization in the perpendicular direction. The substrate was heated at 250° C. immediately before the magnetic film was formed as in the case of forming the Pd (Pt) /CoCr21 medium.
The sputtering gas pressure affects the surface magnetic anisotropy energy Ks of the multi-layered magnetic film and the crystal magnetic anisotropy energy Kv of the CoCr21 film (which is a single-layered magnetic film) as shown in
The perpendicular magnetic anisotropy energy Ku in the multi-layered magnetic film medium depends on Ks and Kv, as approximately represented by equation (1) below. (H. J. G. Draaisam et al., J. Magn. Magn. Mater. 66 (1987) 351-355)
Ku·λ=2·Ks+t·Kv (1)
In equation (1), Ku represents the perpendicular magnetic anisotropy energy of the multi-layered magnetic film as a whole, Ks represents the surface magnetic anisotropy energy (per unit area) in the interface between the CoCr21 alloy layer and the noble metal layer, and Kv represents the crystal magnetic anisotropy energy of the CoCr21 alloy layer. T denotes the thickness of each CoCr21 alloy layer, λ denotes the period of lamination, and 2·Ks denotes the surface magnetic anisotropy energy (for two interfaces) due to one period in the multi-layered film.
The value of Kv (crystal magnetic anisotropy energy) includes the shape anisotropy of the film (−2πMs2) which occurs when the recording film is magnetized in one direction. As equation (1) suggests, the ratio of Kv to Ku increases in proportion to the thickness (t) of the CoCr21 alloy layer.
In the present invention, the surface magnetic anisotropy energy was calculated according to equation (1) under on the assumption that Kv of the CoCr21 alloy layer in the multi-layered magnetic film is equal to Kv of the CoCr21 film (20 nm thick) as a single-layered magnetic film.
In order to achieve the object of the present invention, it is necessary to form the multi-layered magnetic film which has high surface anisotropy energy Ks such that the CoCr21 alloy layer keeps high crystal magnetic anisotropy.
The results shown in
As mentioned, it is desirable to increase the sputtering gas pressure in the production of superlattice. In fact, U.S. Pat. No. 5,106,703 (mentioned above) mentions that the coercive force increases if the sputtering gas pressure is increased, and Ar, as the sputtering gas, is replaced by Xe or Kr. Usually, the coercive force is proportional with the perpendicular magnetic anisotropy energy.
However,
Such a difference between Pd and Pt in the noble metal layer arises from the difference in their atomic weight (Pd=195.1, Pt=106.4). The multi-layered structure requires that the layer interface (as the source of surface magnetic anisotropy) be formed neatly. To this end, it is necessary to keep sufficiently low the kinetic energy of sputtering particles sticking to the film such that sputtering particles impinge upon the film without destroying the layer interface.
Sputtering particles are scattered by collision with sputtering gas at a high pressure in the chamber, so that they lose their kinetic energy. However, Pt particles do not readily lose their kinetic energy unless the sputtering gas pressure is considerably high, because Pt has a much larger atomic weight than Ar. (Ar=40) By contrast, Pd particles readily lose their kinetic energy at a comparatively low sputtering gas pressure although the difference between Pd and Ar in atomic weight is not so large.
The relation between sputtering gas pressure and sputtering rate was investigated by using the same chamber as mentioned. It was found that when the sputtering gas pressure was raised from 3 Pa to 10 Pa, the sputtering rate of Pt remained almost unchanged but the sputtering rate of Pd decreased by more than half. This result suggests that there are more Pd particles which do not reach the substrate due to scattering by the sputtering gas. This coincides with the above-mentioned prediction.
Sputtering at a low gas pressure is close to the condition under which the conventional single-layered CoCr-based alloy crystalline recording film is formed. In this case, a good layer interface is readily obtained because there is only a small amount of impurities in the multi-layered magnetic film. In the case where Pd is used to form the noble metal layer, the value of Ks is high when the gas pressure is low because the effect of making a good layer interface excels the effect of destroying the interface by the sputtering particles.
Incidentally, since Co has a smaller atomic weight (58.9) than noble metal, Co sputtering particles are less likely to damage the interface than the noble metal sputtering particles. Sputtering with Xe or Kr (with an atomic weight of 131.2 and 83.8, respectively) would be favorable to Pt; however, Ar is advantageous costwise.
An experiment was carried out to see how the surface magnetic anisotropy energy of the multi-layered magnetic film depends on the thickness of the noble metal layer in the case of CoCr21 alloy medium in which the thickness of the CoCr21 alloy layer is fixed at 2.0 nm. The result of the experiment is shown in
Why the surface perpendicular magnetic anisotropy energy is small when the thickness of the Pd layer is small may be explained as follows. (1) If the Pd layer is excessively thin, no good layer structure is formed. (2) There are no sufficient electrons to generate the magnetic anisotropy energy if the Pd layer is excessively thin. (Magnetic anisotropy is caused by electrons in the Pd layer.)
It was found that each of the CoCr21 alloy layers have individually different coercive force if the Pd noble metal layer is made thicker than 2.0 nm. This suggests that magnetic exchange interaction between CoCr21 alloy layers becomes so small that domains in each layer can reverse independently. Under this situation, the multi-layered magnetic films as a whole do not function as a single magnetic film. That is, it cannot be used as the recording magnetic film. The Pd noble metal layer in the multi-layered magnetic film should be thinner than 2.0 nm.
A probable reason why the surface magnetic anisotropy energy becomes saturated when the thickness of the Pd noble metal layer is approximately 1.0 nm is that magnetization induced by the Pd noble metal layer is limited to about 0.5 nm (about two-atom layer) from the interface between the CoCr21 alloy layer and the Pd noble metal layer caused by Co.
The present inventors measured the magnitude of magnetization induced in the Pd noble metal layer by the adjacent CoCr21 alloy layer. It was found that average magnetization remains nearly constant at about 100 kA/m when the Pd noble metal alloy is thinner than 1.0 nm but it decreases as the thickness of the Pd noble metal layer exceeds 1.0 nm. It is considered that magnetization induced in the Pd noble metal layer is responsible for at least part of surface magnetic anisotropy energy.
Then, the present inventors prepared several samples of multi-layered magnetic film medium (Pt/CoCr21 medium) which vary in the thicknesses of the Pd noble metal layer and the CoCr21 alloy layer. The multi-layered magnetic film was tested for perpendicular magnetic anisotropy energy and saturation magnetization. The results are shown in Tables 1 and 2.
As a reference, the present inventors also prepared a CoCr21 medium with a 20-nm thick single-layered magnetic film. It was found that the single-layered magnetic film has perpendicular anisotropy energy of about 0.8×105 J/m3 and saturation magnetization of 250 kA/m. This single-layered magnetic film gave an M-H curve with a squareness ratio of about 0.55.
It is noted that the multi-layered magnetic film has much larger perpendicular anisotropy energy than the single-layered magnetic film of CoCr21 medium. It is noted from Table 2 that the multi-layered magnetic film decreases in saturation magnetization due to the Pd layer.
For the perpendicular magnetic recording medium to have stable magnetization, it is necessary that its M-H curve has a squareness ratio close to 1. This can be checked in terms of a parameter of Ku/2πMs2 according to Shimazu et al. (Nippon Ouyou Jiki Gakkaishi, vol. 25, No. 4-2, pp. 539-542). The reference pointed out that this parameter should essentially be greater than 3 for a practical magnetic recording medium (with magnetic particles with an approximate diameter of 10 nm) in consideration of effect on it by thermal disturbance and demagnetizing field. Since Ku/2πMs2=Hk/4πMs, this parameter represents the magnitude ratio of the anisotropic magnetic field to the demagnetizing field (Hk is a value of the physical property which indicates how hard it is for magnetic particles to undergo magnetization reversal). In other words, it is an index indicating how stable the magnetization is in the medium against the demagnetization field induced when the recording bits are uniformly magnetized.
The CoCr21 alloy medium referenced in this example has a value of Ku/2πMs2=1.73. This value suggests that the squareness ratio apparently deviating from 1. This parameter was calculated also for the multi-layered magnetic film in this example. The results are shown in Table 3.
It is noted from Table 3 that the multi-layered magnetic film has a considerably large value of Ku/2πMs2 because the surface magnetic anisotropy enhances the perpendicular magnetic anisotropy energy and the Pd layer suppresses the average magnetization of the multi-layered film as a whole.
For the multi-layered magnetic film to be a suitable perpendicular magnetic recording medium, it should have perpendicular magnetic anisotropy energy, saturation magnetization, and Ku/2πms2 value as desired, as well as good recording characteristics.
Thus, the present inventors tested the perpendicular magnetic recording medium in this example so as to realize low recording noise for the structure of the multi-layered magnetic film.
The test procedure consists of recording a continuous pattern with a recording density of 300 kFCI on each sample of the perpendicular magnetic recording medium and reproducing the continuous pattern to measure the integral value of recording noise.
The perpendicular magnetic recording medium for recording and reproducing tests has an FeTaC soft magnetic layer (400 nm thick) on that side of the NiTaZr underlying layer which faces the substrate. Recording was accomplished by using a single pole type head, and reproducing was accomplished by using a GMR sensor mounted on the same head.
It was found that recording noise depends on the ratio of d1/d2 (where d1 denotes the thickness of the CoCr21 alloy layer and d2 denotes the thickness of the Pd noble metal layer) as shown in
It is noted that the relative noise strength decreases as the relative thickness of the CoCr21 alloy layer increases (or it is about 1 when d1/d2 is about 1.5). A probable reason why the recording noise is large when the d1/d2 is small is that there is large magnetic exchange interaction between particles and there is large domain wall displacement at the time of recording. This result suggests that the multi-layered magnetic recording medium has a low level of recording noise as in the CoCr21 medium with the single-layered magnetic film if it is constructed such that the CoCr21 alloy layer is more than 1.5 times thick than the Pd noble metal layer. It was necessary to keep the substrate at about 250° C. when layers are formed thereon.
The values of Ku/2πMs2 (smaller than 10) in Table 3 are plotted against the thickness of the Pd noble metal layer, with the thickness of the CoCr21 alloy layer varied, as shown in
In
The present inventors examined the relation between the Ku/2πMs2 value and the thermal demagnetizing factor S of the multi-layered magnetic film medium in this example by recording a continuous pattern (20 kFCI) on each sample of the medium and then measuring the amount of loss in the reproduced signal. The thermal demagnetizing factor S is the coefficient of magnetic viscosity which relates the rate of signal loss to log10 (time). It was determined by plotting the amount of signal loss (measured for a period of 1000 seconds) on a graph in which the abscissa represents log10 (time) and the ordinate represents the rate of signal loss. An example of measurements is shown in
In
It is noted from
The data in
This example demonstrates a magnetic recording medium in which the ferromagnetic metal layer is formed from a material having a large value of Kv in place of the CoCr-based alloy used in Example 1. In Example 1, the CoCr layer as the ferromagnetic metal layer is inherently limited in crystal perpendicular magnetic anisotropy energy Kv and hence the range of d1/d2 for keeping the Ku/2πMs2 value exceeding 6 (with the maximum being about 10) is rather narrow. The advantage of the recording medium in this example is that the problem with thermal demagnetization can be avoided even in the case where the diameter of magnetic particles is reduced further in order to decrease recording noise.
The multi-layered magnetic recording medium prepared in this example consists of a substrate, an underlying layer of NiTa37Zr10 alloy (40 nm thick), a Pd film (5 nm thick) a multi-layered magnetic film of Pd/CoCr21Pt14, a Pd film (1 nm thick), and a carbon protective film, which are sequentially placed on top of the other. The multi-layered magnetic film of Pd/CoCr21Pt14 is referred to as “Pd/CoCr21Pt14 film” hereinafter. The multi-layered magnetic recording medium is referred to as “Pd/CoCr21Pt14 medium” hereinafter. Incidentally, the total thickness of the multi-layered magnetic film is about 20 nm, and the substrate was heated to 250° C. immediately before film lamination.
A comparative sample of perpendicular magnetic recording medium was also prepared, which consists of a substrate, an underlying layer of NiTa37Zr10 alloy (40 nm thick), a Pd film (5 nm thick), a single-layered magnetic film of CoCr21Pt14, a Pd film (1 nm thick), and a carbon protective film, which are sequentially placed on top of the other. The single-layered magnetic film of CoCr21Pt14 is referred to as “CoCr21Pt14 film” hereinafter. The single-layered magnetic recording medium is referred to as “CoCr21Pt14 medium” hereinafter. As in the Pd/CoCr21Pt14 medium, the substrate was heated to 250° C. immediately before film deposition.
The CoCr21Pt14 film was found to have perpendicular anisotropy energy of about 1.6×105 J/m3 and saturation magnetization of 250 kA/m. The CoCr21Pt14 film is quite similar in saturation magnetization to the CoCr21 alloy layer (in Example 1) which does not contain Pt. However, the CoCr21Pt14 single-layered magnetic film increases in crystal magnetic anisotropy.
As shown above, the incorporation of Pt into the ferromagnetic metal layer of CoCr-based alloy is an effective way for increasing the magnetic anisotropy of the magnetic film. The comparison of the Pd/CoCr21Pt14 medium with the Pd/CoCr21 medium revealed that the former has larger perpendicular magnetic anisotropy energy than the latter but there is no significant difference between them in the average saturation magnetization of the entire multi-layered film. The increment of perpendicular magnetic anisotropy is due mostly to crystal magnetic anisotropy energy but very little to surface magnetic anisotropy energy. The CoCr21Pt14 alloy is suitable for use as the ferromagnetic metal layer of the multi-layered magnetic film medium, because it increases in crystal magnetic anisotropy owing to the incorporation of Pt even if it is made into multi-layered thin film.
The multi-layered magnetic film medium (Pd/CoCr21Pt14 medium) in this example was examined for a relation between d1/d2 and recording noise. It was found that recording noise can be suppressed if d1/d2 is larger than 1.5 as in Example 1.
Samples of Pd/CoCr21Pt14 medium varying in their layer thickness were measured for Ku/2πMs2 values. The results are shown in
Samples of Pd/CoCr21Ptx medium were examined for perpendicular magnetic anisotropy, with the amount of Pt varying in the ferromagnetic metal layer of CoCr-based alloy. The CoCr21Ptx alloy layer is 1.6 nm thick, and the Pd noble metal layer is 0.8 nm thick.
It was found that the perpendicular magnetic anisotropy energy linearly increases in proportion to the amount of Pt added (up to 10 at %). However, the perpendicular magnetic anisotropy remained almost unchanged beyond 10 at %, and recording noise begins to increase beyond 16 at %. This indicates that incorporation with Pt increases magnetic exchange interaction between particles. It is concluded from the foregoing that the ferromagnetic metal layer of CoCr-based alloy should be incorporated with Pt in an amount from 10 at % to 16 at %.
This example demonstrates a multi-layered magnetic film recording medium (“Pd/CoCr15Pt14B2 medium” hereinafter) which was prepared in the following manner. First, a substrate was coated sequentially with an underlying layer (40 nm thick) of NiTa37Zr10 alloy and a Pd film (5 nm thick). With the substrate heated to 250° C., the Pd film was coated with an initial layer (3 nm thick) of CoCr40 alloy and subsequently with a multi-layered magnetic film of Pd/CoCr15Pt14B2 (“Pd/CoCr15Pt14B2 film” hereinafter) by using the rotary cathode device. After the multi-layered magnetic film had been formed, a heat treatment was performed at 350° C. or above for 10 seconds. After cooling, a Pd film (1 nm thick) and a carbon protective film were formed sequentially.
In general, the crystal magnetic anisotropy energy (Kv) increases but the effect of reducing the magnetic exchange interaction between particles at Cr grain boundaries is lost as the Cr concentration decreases in the CoCr-based alloy. According to the conventional technology, the minimum Cr concentration was 20% which decreases the magnetic exchange interaction between particles without increase in recording noise.
The present inventors found that the magnetic exchange interaction between particles decreases to a level suitable for magnetic recording if heat treatment is performed at 350° C. or above for 10 seconds or so after the multi-layered magnetic film has been formed.
The reason why the magnetic exchange interaction between particles decreases upon a heat treatment may be understood as follows. The CoCr40 initial layer just under the multi-layered magnetic film contains Cr atoms which, during reheating, diffuse through the grain boundaries of magnetic particles in the direction perpendicular to the film surface.
A comparative sample of single-layered magnetic film medium (“CoCr15Pt14B2 medium” hereinafter) was prepared in the following manner. A substrate was coated sequentially with an underlying layer (40 nm thick) of NiTa37Zr10 alloy and a Pd film (5 nm thick). With the substrate heated to 250° C., the Pd film was coated with an initial layer (3 nm thick) of CoCr40 alloy and subsequently with a single-layered magnetic film of CoCr15Pt14B2 (“CoCr15Pt14B2 film” hereinafter). After the CoCr15Pt14B2 film had been formed, a heat treatment was performed at 350° C. or above for 10 seconds. After sufficient cooling, a Pd film (1 nm thick) and a carbon protective film were formed sequentially.
The CoCr15Pt14B2 alloy film was found to have large perpendicular anisotropy energy of about 2.5×105 J/m3 and saturation magnetization of 320 kA/m (which is larger than that of the CoCr15 alloy film) due to the small Cr content (15%). Therefore, the recording medium has a large demagnetizing field, and the single-layered film of CoCr15Pt14B2 has a Ku/2πMs2 value of 3.9. In other words, the single-layered film of CoCr15Pt14B2 differs very little from the CoCr21Pt14 film with a large Cr content (without heat treatment, referred to Example 2) in terms of Ku/2πMs2 (thermal stability), because the increased perpendicular magnetic anisotropy is cancelled by the increased demagnetizing field.
The Pd/CoCr15Pt14B2 medium, which underwent heat treatment after the multi-layered magnetic film had been formed, was examined for perpendicular magnetic anisotropy energy (Ku) and saturation magnetization (Ms), with the thickness of the multi-layered magnetic film being adequately varied. The results are shown in Tables 4 and 5.
It is noted from that the multi-layered magnetic film has higher values of both Ku and Ks as compared with that in Example 2 for the same layer thickness. On the other hand, the multi-layered magnetic film has larger surface magnetic anisotropy energy (Ks) as compared with that of Pd/CoCr21 medium in Example 1 and that of Pd/CoCr21Pt14 medium in Example 2, both by more than 50%, for the same structure. This may be attributable to the increased Co concentration in the Co alloy layer and the increased area of Pd/Co interface.
As in Example 1 (
What Ku/2πMs2 values represent is thermal stability which manifests itself when magnetization in the medium is oriented in the same direction or when the recording density is low. With a low recording density, the Pd/CoCr15Pt14B2 medium in this example is almost identical in thermal stability to the medium in Example 2, due to the effect of the demagnetizing field. However, as the recording density increases, the medium in this example, which has a larger value of Ku, has the advantage in thermal stability. Another of the preferable properties is the high strength of reproduced signals. In other words, the Pd/CoCr15Pt14B2 medium in this example has larger magnetization than the medium in Example 2, which provides a larger output of reproduced signals.
The present inventors closely studied heat treatment performed after the CoCr15Pt14B2 film has been formed. It was found that reheating does not cut off the magnetic exchange interaction between particles in the multi-layered magnetic film if the Cr content is lower than 12 at %. This result suggests that it is necessary that the Cr content in the Co alloy should be higher than 12 at %.
It was found that Cu in place of Cr is also useful as the additive to the initial layer. The amount of Cu in the initial layer should be larger than that in the multi-layered magnetic film. An amount more than 30 at % is necessary for reheating to produce a remarkable effect.
In addition, this example is characterized by that the Co alloy is incorporated with a small amount (2 at %) of B. The incorporation of B reduces the size of magnetic particles by about 10%. It is known that, in general, such elements as B and Ta added in small quantities to the CoCr-based alloy promote segregation of Cr atoms on the grain boundary and reduce the size of crystal grains. It was confirmed that this is effective also in the multi-layered magnetic film medium. More details are discussed in Example 4.
This example demonstrates a multi-layered magnetic film recording medium of the same structure as in Example 1, except that the multi-layered film is incorporated with boron (B). This recording medium has a ferromagnetic metal layer of CoCr21Pt14Bx (1.8 nm thick) and a noble metal layer of PdBx (0.8 nm thick). The multi-layered magnetic film has a total thickness of 20 nm.
The amount of B added is expressed in terms of x at %. The layers containing B were prepared in the same way as in Example 1. The substrate was heated to 250° C. after the underlying layer had been formed. With x varied from 0 at % to 5 at %, the multi-layered magnetic film was examined for magnetic properties and crystal grain sizes. The results are shown in Table 6. Incidentally, the measurements of crystal grain size were carried out by using a scanning tunnel electron microscope (TEM) and crystal structure analysis.
It is noted from Table 6 that the incorporation of B into the non-magnetic metal layer (Pd) slightly decreases the crystal grain size as well as Ku and Hc. Because of the decrease in Ku and the grain size, the perpendicular magnetic recording medium is subject to thermal disturbance and hence is poor in thermal stability. Nevertheless, it has a low level of recording noise owing to the reduction in grain size.
In this example, the incorporation of 5 at % B did not cause appreciable thermal demagnetization. Rather, the incorporation of B reduces the grain size and adjust Ku and Ms to adequate values suitable for perpendicular magnetic recording. This in turn improves resistance to thermal disturbance and contributes to the multi-layered magnetic film suitable for the perpendicular magnetic recording medium.
The same effect as mentioned above was also obtained when B was replaced by tantalum (Ta).
As mentioned above, the perpendicular magnetic recording medium consists of a substrate and a multi-layered magnetic film, with or without an underlying layer interposed between them. The multi-layered magnetic film is composed of ferromagnetic metal layers containing Co and non-magnetic metal layers containing Pd, each one layer of which are laminated alternately on top of one layer of the other. The ferromagnetic metal layers and the non-magnetic metal layers have a thickness of d1 and d2, respectively, with the ratio of d1/d2 being in the range of 1.5 to 4.0. This specific layer structure reduces the magnetic exchange interaction between magnetic particles in the magnetic recording film and increases the perpendicular magnetic anisotropy energy (Ku) relative to the demagnetizing field of the recording medium. As a result, the perpendicular magnetic recording medium is stable against thermal disturbance and has a low level of recording noise.
The invention may be embodied in other specific forms without departing from the spirit or essential characteristics thereof. The present embodiment is therefore to be considered in all respects as illustrative and not restrictive, the scope of the invention being indicated by the appended claims rather than by the foregoing description and all changes which come within the meaning and range of equivalency of the claims are therefore intended to be embraced therein.
Number | Date | Country | Kind |
---|---|---|---|
P2002-048937 | Feb 2002 | JP | national |
Number | Date | Country | |
---|---|---|---|
Parent | 10217478 | Aug 2002 | US |
Child | 10952735 | Sep 2004 | US |