Perylene-based Semiconducting Materials

Information

  • Patent Application
  • 20120226042
  • Publication Number
    20120226042
  • Date Filed
    March 05, 2012
    12 years ago
  • Date Published
    September 06, 2012
    12 years ago
Abstract
The present invention provides a compound of formula
Description
DESCRIPTION

Organic semiconducting materials can be used in electronic devices such as organic photovoltaic (OPV) cells, organic field-effect transistors (OFETs) and organic light emitting diodes (OLEDs).


For efficient and long lasting performance, it is desirable that the organic semiconducting material-based devices show high charge carrier mobility and high stability, in particular towards oxidation, under ambient conditions.


Furthermore, it is desirable that the organic semiconducting materials are compatible with liquid processing techniques as liquid processing techniques are convenient from the point of processability, and thus allow the production of low cost organic semiconducting material-based electronic devices. In addition, liquid processing techniques are also compatible with plastic substrates, and thus allow the production of light weight and flexible organic semiconducting material-based electronic devices.


The use of perylene-based organic semiconducting materials in electronic devices is known in the art.


U.S. Pat. No. 7,282,275 B2 describes a composition that includes

    • a first compound of formula [EC-]n-Ar1 (I), wherein
      • A1 is a first aromatic core and is a divalent, trivalent or tetravalent radical of a long list of formulae, including




embedded image






      • that is unsubstituted or substituted with a long list of substituents, including fluoro and cyano,

      • EC is a first end capping group and is a monovalent radical of a long list of formulae,

      • n is an integer of 2 to 4

      • Z is NH or CH2, and



    • a second compound having an aromatic radical that comprises the first aromatic core of the first compound, a second end capping group that comprises the first end capping group of the first compound, a divalent radical that comprises a divalent radical of the first end capping group, or a combination thereof,


      wherein the composition is amorphous and solution processible.





Also provided is an electronic device including the composition.


U.S. Pat. No. 7,355,198 B2 describes am organic thin film transistor (OFET), which interposes an organic acceptor film between source and drain electrodes and an organic semiconductor film. The organic semiconductor film is formed of pentacene. In particular, the organic acceptor film is formed of at least one electron withdrawing material selected from a long list of compounds, including N,N′-bis(di-tert-butyphenyl)-3,4,9,10-perylenedicarboxylmide.


U.S. Pat. No. 7,326,956 B2 describes a thin film transitor comprising a layer of organic semiconductor material comprising tetracarboxylic diimide 3,4,9,10-perylene-based compound having attached to each of the imide nitrogen atoms a carbocyclic or heterocyclic aromatic ring system substituted with one or more fluorine containing groups. In one embodiment the fluorine-containing N,N′-diaryl perylene-based tetracarboxylic diimide compound is represented by the following structure:




embedded image


wherein A1 and A2 are independently carbocyclic and/or heterocyclic aromatic ring systems comprising at least one aromatic ring in which one or more hydrogen atoms are substituted with at least one fluorine-containing group. The perylene nucleus can be optionally substituted with up to eight independently selected X groups, wherein n is an integer from 0 to 8. The X substituent groups on the perylene can include a long list of substituents, including halogens such as fluorine or chlorine, and cyano.


U.S. Pat. No. 7,671,202 B2 describes n-type semiconductor compounds of formula




embedded image


wherein each R1 to R8, R11 and R12 can be independently selected from H, an electron-withdrawing substituent and a moiety comprising such substituent. Electron-withdrawing substitutents include a long list of substituents, including cyano. R9 and R10 are independently selected from H, alkyl, substituted alkyl, cycloalkyl, substituted cycloalkyl, aryl, substituted aryl, polycyclic aryl and/or substituted polycyclic aryl moieties. At least one of R1, R4, R5, R8, R11 and R12 can be a cyano substituent. Such cyanated compounds can be di- or tetra-substituted as shown by the following structures:




embedded image


WO 2005/124453 describes perylenetetracarboxylic diimide charge-transfer materials, for example a perylenetetracarboxylic diimide charge-transfer material having formula




embedded image


wherein Y in each instance can be independently selected from H, CN, acceptors, donors and a polymerizable group; and X in each instance can be independently selected from a large group of listed compounds.


WO 2008/063609 describes diimide-based semiconductor compounds. In a particular embodiment the compound can have formula




embedded image


wherein R1 at each occurrence is independently selected from a long list of groups, including branched C3-20-alkyl and branched C3-20-alkenyl.


WO 2009/098252 describes semiconducting compounds having formula




embedded image


wherein R1 and R2 at each occurrence independently are selected from a large list of groups, including H, C1-30-alkyl and C2-30-alkenyl; and R3, R4, R5 and R6 are independently H or an electron-withdrawing group. In certain embodiments, at least one of R3, R4, R5 and R6 can be Br or cyano. For example, the semiconducting compound can include




embedded image


WO 2009/144205 describes bispolycyclic rylene-based semiconducting materials, for example




embedded image


S. Nakanzono, S. Easwaramoorthi, D. Kim, H. Shinokubo, A. Osuka Org. Lett. 2009, 11, 5426 to 5429 describes the preparation of 2,5,8,11 tetraarylated perylene tetracaroxylic acid bisimides from perylene tetracarboxylic acid bisimides




embedded image


It was the object of the present invention to provide new perylene-based semiconducting materials.


The object is solved by the compound of claim 1, the process of claim 2, the compound of claim 6, and the electronic device of claim 7.


The perylene-based semiconducting compound of the present invention is of formula




embedded image


wherein

  • R1 and R2 are independently selected from the group consisting of H, C1-30-alkyl, C2-30-alkenyl, C2-30-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl,
    • wherein
    • if R1 or R2 are C1-30-alkyl, C2-30-alkenyl or C2-30-alkynyl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C3-10-cycloalkyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl;
    • if R1 or R2 are C3-10-cycloalkyl, C5-10-cycloalkenyl or 3-14 membered cycloheteroalkyl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C6-14-aryl and 5-14 membered heteroaryl;
    • if R1 or R2 are C6-14-aryl or 5-14 membered heteroaryl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl and 3-14 membered cycloheteroalkyl,
      • wherein R3 and R4 are at each occurrence are independently from each other selected from the group consisting of C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl. C1-10-alkyl and C1-30-alkyl can be branched or unbranched. Examples of C1-10-alkyl are methyl, ethyl, n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, neopentyl, isopentyl, n-(1-ethyl)propyl, n-hexyl, n-heptyl, n-octyl, n-(2-ethyl)hexyl, n-nonyl and n-decyl. Examples of C3-8-alkyl are n-propyl, isopropyl, n-butyl, sec-butyl, isobutyl, tert-butyl, n-pentyl, neopentyl, isopentyl, n-(1-ethyl)propyl, n-hexyl, n-heptyl, n-octyl and n-(2-ethyl)hexyl. Examples of C1-30-alkyl are C1-10-alkyl, and n-undecyl, n-dodecyl, n-undecyl, n-dodecyl, n-tridecyl, n-tetradecyl, n -pentadecyl, n-hexadecyl, n-heptadecyl, n-octadecyl, n-nonadecyl and n-icosyl (C20), n-docosyl (C22), n-tetracosyl (C24), n-hexacosyl (C26), n-octacosyl (C28) and n-triacontyl (C30).


C2-10-alkenyl and C2-30-alkenyl can be branched or unbranched. Examples of C2-10-alkenyl are vinyl, propenyl, cis-2-butenyl, trans-2-butenyl, 3-butenyl, cis-2-pentenyl, trans-2-pentenyl, cis-3-pentenyl, trans-3-pentenyl, 4-pentenyl, 2-methyl-3-butenyl, hexenyl, heptenyl, octenyl, nonenyl and docenyl. Examples of C2-30-alkenyl are C2-10-alkenyl, and linoleyl (C18), linolenyl (C18), oleyl (C18), arachidonyl (C20), and erucyl (C22).


C2-10-alkynyl and C2-30-alkynyl can be branched or unbranched. Examples of C2-10-alkynyl are ethynyl, 2-propynyl, 2-butynyl, 3-butynyl, pentynyl, hexynyl, heptynyl, octynyl, nonynyl and decynyl. Examples of C2-30-alkynyl are C2-10-alkynyl, and undecynyl, dodecynyl, undecynyl, dodecynyl, tridecynyl, tetradecynyl, pentadecynyl, hexadecynyl, heptadecynyl, octadecynyl, non-adecynyl and icosynyl (C20).


Examples of C3-10-cycloalkyl are preferably monocyclic C3-10-cycloalkyls such as cyclopropyl, cyclobutyl, cyclopentyl, cyclohexyl, cycloheptyl and cyclooctyl, but include also polycyclic C3-10-cycloalkyls such as decalinyl, norbornyl and adamantyl.


Examples of C5-10-cycloalkenyl are preferably monocyclic C5-10-cycloalkenyls such as cyclopentenyl, cyclohexenyl, cyclohexadienyl and cycloheptatrienyl, but include also polycyclic C5-10-cycloalkenyls.


Examples of 3-14 membered cycloheteroalkyl are monocyclic 3-8 membered cycloheteroalkyl and polycyclic, for example bicyclic 7-12 membered cycloheteroalkyl.


Examples of monocyclic 3-8 membered cycloheteroalkyl are monocyclic 5 membered cycloheteroalkyl containing one heteroatom such as pyrrolidinyl, 1-pyrrolinyl, 2-pyrrolinyl, 3-pyrrolinyl, tetrahydrofuryl, 2,3-dihydrofuryl, tetrahydrothiophenyl and 2,3-dihydrothiophenyl, monocyclic 5 membered cycloheteroalkyl containing two heteroatoms such as imidazolidinyl, imidazolinyl, pyrazolidinyl, pyrazolinyl, oxazolidinyl, oxazolinyl, isoxazolidinyl, isoxazolinyl, thiazolidinyl, thiazolinyl, isothiazolidinyl and isothiazolinyl, monocyclic 5 membered cycloheteroalkyl containing three heteroatoms such as 1,2,3-triazolyl, 1,2,4-triazolyl and 1,4,2-dithiazolyl, monocyclic 6 membered cycloheteroalkyl containing one heteroatom such as piperidyl, piperidino, tetrahydropyranyl, pyranyl, thianyl and thiopyranyl, monocyclic 6 membered cycloheteroalkyl containing two heteroatoms such as piperazinyl, morpholinyl and morpholino and thiazinyl, monocyclic 7 membered cycloheteroalkyl containing one hereoatom such as azepanyl, azepinyl, oxepanyl, thiepanyl, thiapanyl, thiepinyl, and monocyclic 7 membered cycloheteroalkyl containing two hereoatom such as 1,2-diazepinyl and 1,3-thiazepinyl.


An example of a bicyclic 7-12 membered cycloheteroalkyl is decahydronaphthyl.


C6-14-aryl can be monocyclic or polycyclic. Examples of C6-14-aryl are monocyclic C6-aryl such as phenyl, bicyclic C6-10-aryl such as 1-naphthyl, 2-naphthyl, indenyl, indanyl and tetrahydronaphthyl, and tricyclic C12-14-aryl such as anthryl, phenanthryl, fluorenyl and s-indacenyl.


5-14 membered heteroaryl can be monocyclic 5-8 membered heteroaryl, or polycyclic 7-14 membered heteroaryl, for example bicyclic 7-12 membered or tricyclic 9-14 membered heteroaryl.


Examples of monocyclic 5-8 membered heteroaryl are monocyclic 5 membered heteroaryl containing one heteroatom such as pyrrolyl, furyl and thiophenyl, monocyclic 5 membered heteroaryl containing two heteroatoms such as imidazolyl, pyrazolyl, oxazolyl, isoxazolyl, thiazolyl, isothiazolyl, monocyclic 5 membered heteroaryl containing three heteroatoms such as 1,2,3-triazolyl, 1,2,4-triazolyl and oxadiazolyl, monocyclic 5 membered heteroaryl containing four heteroatoms such as tetrazolyl, monocyclic 6 membered heteroaryl containing one heteroatom such as pyridyl, monocyclic 6 membered heteroaryl containing two heteroatoms such as pyrazinyl, pyrimidinyl and pyridazinyl, monocyclic 6 membered heteroaryl containing three heteroatoms such as 1,2,3-triazinyl, 1,2,4-triazinyl and 1,3,5-triazinyl, monocyclic 7 membered heteroaryl containing one heteroatom such as azepinyl, and monocyclic 7 membered heteroaryl containing two heteroatoms such as 1,2-diazepinyl.


Examples of bicyclic 7-12 membered heteroaryl are bicyclic 9 membered heteroaryl containing one heteroatom such as indolyl, isoindolyl, indolizinyl, indolinyl, benzofuryl, isobenzofuryl, benzothiophenyl and isobenzothiophenyl, bicyclic 9 membered heteroaryl containing two heteroatoms such as indazolyl, benzimidazolyl, benzimidazolinyl, benzoxazolyl, benzisooxazolyl, benzthiazolyl, benzisothiazolyl, furopyridyl and thienopyridyl, bicyclic 9 membered heteroaryl containing three heteroatoms such as benzotriazolyl, benzoxadiazolyl, oxazolopyridyl, isooxazolopyridyl, thiazolopyridyl, isothiazolopyridyl and imidazopyridyl, bicyclic 9 membered heteroaryl containing four heteroatoms such as purinyl, bicyclic 10 membered heteroaryl containing one heteroatom such as quinolyl, isoquinolyl, chromenyl and chromanyl, bicyclic 10 membered heteroaryl containing two heteroatoms such as quinoxalinyl, quinazolinyl, cinnolinyl, phthalazinyl, 1,5-naphthyridinyl and 1,8-naphthyridinyl, bicyclic 10 membered heteroaryl containing three heteroatoms such as pyridopyrazinyl, pyridopyrimidinyl and pyridopyridazinyl, and bicyclic 10 membered heteroaryl containing four heteroatoms such as pteridinyl.


Examples of tricyclic 9-14 membered heteroaryls are dibenzofuryl, acridinyl, phenoxazinyl, 7H-cyclopenta[1,2-b:3,4-b′]dithiophenyl and 4H-cyclopenta[2,1-b:3,4-b′]dithiophenyl.


Examples of halogen are —F, —Cl, —Br and —I.


Examples of C1-10-alkoxy are methoxy, ethoxy, n-propoxy, isopropoxy, n-butoxy, sec-butoxy, isobutoxy, tert-butoxy, n-pentoxy, neopentoxy, isopentoxy, hexoxy, n-heptoxy, n-octoxy, n-nonoxy and n-decoxy.


Examples of C2-5-alkylene are ethylene, propylene, butylene and pentylene.


Preferably, R1 and R2 are independently selected from the group consisting of H, C1-30-alkyl, C2-30-alkenyl, C2-30-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl,

    • wherein
    • if R1 or R2 are C1-30-alkyl, C2-30-alkenyl or C2-30-alkynyl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C3-10-cycloalkyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl;
    • if R1 or R2 are C3-10-cycloalkyl, C5-10-cycloalkenyl or 3-14 membered cycloheteroalkyl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C6-14-aryl and 5-14 membered heteroaryl;
      • wherein R3 and R4 are at each occurrence are independently from each other selected from the group consisting of C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl.


More preferably, R1 and R2 are independently selected from the group consisting of H, C1-30-alkyl, C2-30-alkenyl,

    • wherein
    • if R1 or R2 are C1-30-alkyl or C2-30-alkenyl, this R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C3-10-cycloalkyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl;
      • wherein R3 and R4 are at each occurrence are independently from each other selected from the group consisting of C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl.


Even more preferably, R1 and R2 are independently from each other C1-30-alkyl,

    • wherein
    • R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C3-10-cycloalkyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl;
      • wherein R3 and R4 are at each occurrence are independently from each other selected from the group consisting of C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl.


Most preferably, R1 and R2 are the same and are C1-30-alkyl, preferably Cm-alkyl,

    • wherein
    • R1 or R2 can be optionally substituted with 1 to 6 groups independently selected from the group consisting of halogen, —CN, —NO2, —OH, C1-10-alkoxy, —O—CH2CH2O—C1-10-alkyl, —O—COR3, —S—C1-10-alkyl, —NH2, —NHR3, —NR3R4, —NH—COR3, —COOH, —COORS, —CONH2, —CONHR3, —CONR3R4, —CO—H, —COR3, C3-10-cycloalkyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl;
      • wherein R3 and R4 are at each occurrence are independently from each other selected from the group consisting of C1-10-alkyl, C2-10-alkenyl, C2-10-alkynyl, C3-10-cycloalkyl, C5-10-cycloalkenyl, 3-14 membered cycloheteroalkyl, C6-14-aryl and 5-14 membered heteroaryl.


In particular, R1 and R2 are the same and are unsubstituted C1-30-alkyl, preferably unsubstituted C3-8-alkyl such as n-(1-ethyl)propyl.


Also part of the invention, is a process for the preparation of the compound of formula




embedded image


wherein R1 and R2 are as defined above,


which process comprises the steps of


(i) treating a compound of formula (2) with a boron-containing compound of formula (3) in the presence of a transition metal-containing catalyst to form a boron-containing compound of formula (4)




embedded image


wherein R1 and R2 are as defined above, and L is a linking group, and


(ii) treating the boron-containing compound of formula (4) with a cyanide source in order to form the compound of formula (1).


L is preferably C2-5-alkylene, which can be optionally substituted with 1 to 6 C1-10-alkyl groups. More preferably L is ethylene or propylene and is substituted with 2 to 4 methyl groups.


The transition metal-containing catalyst can be an iridium-containing catalyst such as [Ir(cod)OMe]2, or, preferably, a ruthenium-containing catalyst, such as RuH2(CO)(PPh3)3.


If the transition metal-containing catalyst is an iridium-containing catalyst, the first step can be performed in the presence of a base such as di-tert-butylbipyridine. If the transition metal-containing catalyst is an iridium-containing catalyst, the first step is usually performed in a suitable organic solvent such as tetrahydrofuran or 1,4-dioxane. If the transition metal-containing catalyst is an iridium-containing catalyst, the first step is usually performed at elevated temperatures, such as at temperatures from 60 to 110° C. In principal, if the transition metal-containing catalyst is an iridium-containing catalyst, the first step can be performed in analogy to the method described by C. W. Liskey; X. Liao; J. F. Hartwig in J. Am. Chem. Soc. 2010, 132, 11389-11391, and by I. A. I. Mkhalid, J. H. Barnard, T. B. Marder, J. M. Murphy and J. F. Hartwig in Chem. Rev. 2010, 110, 890-931.


If the transition metal-containing catalyst is a ruthenium-containing catalyst, the first step is usually performed in a suitable organic solvent such as toluene, pinacolone and mesitylene or mixtures thereof. If the transition metal-containing catalyst is ruthenium-containing catalyst, the first step is usually performed at elevated temperatures, such as at temperatures from 120 to 160° C.


In one embodiment, the cyanide source in step two can be tetra-C1-10-alkylammoniumcyanide, tetra-C1-10-alkylphosphoniumcyanide or hexa-C1-10-alkylguanidiniumcyanide.


In a second embodiment, the cyanide source in step two can be Zn(CN)2.


The second step is usually performed in the presence of a base such as CsF and a copper reagent such as Cu(NO3)2. The second step is usually performed in a suitable solvent such as water, methanol and dioxane, or mixtures thereof. The second step is usually performed at elevated temperatures, such as at temperatures from 80 to 120° C.


In principal, if the metal cyanide is Zn(CN)2, step two can be performed in analogy to the method described by C. W. Liskey; X. Liao; J. F. Hartwig in J. Am. Chem. Soc. 2010, 132, 11389-11391.


The compounds of formulae (4) and (1) can be isolated by methods known in the art, such as column chromatography.


The compound of formula (2) can be obtained by methods known in the art, for example as described in the subsection titled “Synthesis” of F. Würthner, Chem. Commun., 2004, 1564-1579.


Also part of the invention are the compounds of formula




embedded image


wherein R1, R2 and L are as defined above.


Also part of the present invention is an electronic device comprising the compound of formula (1) as semiconducting material.


Also part of the invention is the use of the compound of formula (1) as semiconducting material.


In FIG. 1 the design of the bottom-gate organic field effect transistor of example 5 is shown.


In FIG. 2 the drain current ISD [A] in relation to the gate voltage VSG [V] (top transfer curve) and the drain current ISD0.5 [μA0.5] in relation to the gate voltage VSG [V] (bottom transfer curve) for the bottom-gate organic field effect transistor of example 5 comprising compound 1b as semiconducting material at a drain voltage VSD of 100 V is shown.


In FIG. 3 the charge carrier mobility μsat [cm2/Vs] in relation to the gate voltage VSG [V] for the bottom-gate organic field effect transistor of example 5 comprising compound 1b as semiconducting material is shown.


The compounds of formula (1) show a high charge carrier mobility and a high stability, in particular towards oxidation, under ambient conditions. Furthermore the compounds of formula (1) are compatible with liquid processing techniques.







EXAMPLES
Example 1
Preparation of N,N′-bis(1-ethylpropyl)-2,5,8,11-tetrakis[4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-y]perylene-3,4:9,10-tetracarboxylic acid bisimide (4a)



embedded image


N,N′-Bis(1-ethylpropyl) perylene-3,4:9,10-tetracarboxylic acid bisimide (2a) (100 mg, 0.189 mmol) and bispinacolondiboronate (3a) (0.383 g, 1.51 mmol) are mixed together and dissolved in 2 mL dry mesitylene and 0.15 mL dry pinacolone. Argon is bubbled trough the solution for 30 minutes. RuH2(CO)(PPh3)3 (0.082 mg, 0.09 mmol) is added to the reaction mixture and the vessel heated to 140° C. for 30 hours. After cooling the system to room temperature, the solvent is evaporated and the desired compound purified by column chromatography (silica, CH2Cl2/AcOEt 50/1). An orange bright solid is obtained with 60% yield (117 mg, 0.113 mmol).



1H NMR (250 MHz, CD2Cl2) δ 8.59 (s, J=7.3 Hz, 4H), 4.94 (tt, J=9.2, 6.0 Hz, 2H), 2.33-2.10 (m, 4H), 2.04-1.84 (m, 4H), 1.51 (s, J=7.2 Hz, 48H), 0.92 (t, J=7.4 Hz, 12H). FD Mass Spectrum (8 kV): m/z=1033.33 (100%) [M+]. Absorption: 537 nm (in toluene). Emission: 548 nm (in toluene, exc 537 nm). Extinction Coefficient: 7.30×104M−1 cm−1. Fluorescence Quantum Yield: 0.89. Elemental Analysis: theoretical: C, 67.34; H, 7.21; N, 2.71; experimental: C, 67.29; H, 7.40; N, 2.96.


Example 2
Preparation of N,N′-bis(1-ethylpropyl)-2,5,8,11-tetracarbonitrile-perylene-3,4:9,10-tetracarboxylic acid bisimide (1a)



embedded image


N,N′-Bis(1-ethylpropyl)-2,5,8,11-tetrakis[4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-y]perylene-3,4:9,10-tetracarboxylic acid bisimide (4a) (50 mg, 0.048 mmol), zinc cyanide (68 mg, 0.58 mmol) caesium fluoride (29 mg, 0.19 mmol) and copper nitrate (90 mg, 0.38) are suspended in a mixture of water (1 mL), methanol (1 mL) and dioxane (1 mL). The reaction vessel is closed and heated in microwave for 1 hour at 100° C. The reaction mixture is then poured into a saturated solution of ammonium chloride and extracted with dichloromethane. The organic phase is dried over magnesium sulfate and the solvent evaporated. The product is purified via column chromatography (silica, dichloromethane/acetone 50/1) and obtained as a red-orange solid (yield 40%, 13 mg, 0.019 mmol).



1H NMR (250 MHz, CD2Cl2) δ 8.98 (s, 4H), 5.09 (m, 2H), 2.38-2.16 (m, 4H), 2.11-1.90 (m, 4H), 0.96 (t, J=7.5 Hz, 12H). FD Mass Spectrum (8 kV): m/z=630.9 (100%) [M+]. Absorption: 517 nm (in CH2Cl2). Emission: 525 nm (in CH2Cl2, exc 517 nm). Extinction Coefficient: 7.31×104 M−1 cm−1.


Example 3
Preparation of N,N′-bis(1-heptyloctyl)-2,5,8,11-tetrakis[4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-y]perylene-3,4:9,10-tetracarboxylic acid bisimide (4b)



embedded image


N,N′-Bis(1-heptyloctyl) perylene-3,4:9,10-tetracarboxylic acid bisimide (2b) (0.12 mmol) and bispinacolondiboronate (3a) (0.99 mmol) are mixed together and dissolved in 2 mL dry mesitylene and 0.15 mL dry pinacolone. Argon is bubbled trough the solution for 30 minutes. RuH2(CO)(PPh3)3 (0.06 mmol) is added to the reaction mixture and the vessel heated to 140° C. for 24 hours. After cooling the system to room temperature, the solvent is evaporated and the desired compound 4b is purified by column chromatography (silica, CH2Cl2/AcOEt 50/1).


Example 4
Preparation of N,N′-bis(1-heptyloctyl)-2,5,8,11-tetracyano-perylene-3,4:9,10-tetracarboxylic acid bisimide (1b)



embedded image


N,N′-Bis(1-heptyloctyl)-2,5,8,11-tetrakis[4,4,5,5-tetramethyl-1,3,2-dioxaborolan-2-y]perylene-3,4:9,10-tetracarboxylic acid bisimide (4b) (63 mg, 0.05 mmol), prepared as described in example 3, cesium fluoride (29 mg, 0.19 mmol), zinc cyanide (68 mg, 0.58 mmol) and copper(II) nitrate×2.5 H20 (89 mg, 0.38 mmol) are suspended in 3 mL of a 5/1 mixture of dioxane/methanol and heated in a microwave vessel at 80° C. for 5 minutes. The reaction mixture is then poured in a saturated solution of ammonium chloride and extracted with dichloromethane. The organic phase is dried over magnesium sulfate and the solvent evaporated. The desired compound is obtained as a brownish solid after column chromatography (silica, dichloromethane) in 40% yield (18 mg, 0.019 mmol). 1H NMR (500 MHz, CD2Cl2) δ 8.99 (s, 4H), 5.25-5.14 (m, 2H), 2.30-2.12 (m, 4H), 1.93 (m, 4H), 1.29 (m, 40H), 0.84 (t, J=5.7 Hz, 12H). 13C NMR (126 MHz, CD2Cl2) δ 161.33 (s), 133.20 (s), 131.01 (s), 129.89 (s), 128.74 (s), 127.35 (s), 117.63 (s), 117.26 (s), 57.17 (s), 32.61 (s), 32.32 (s), 29.97 (s), 29.74 (s), 27.51 (s), 23.16 (s), 14.38 (s). FD/MS (8 kV): m/z=909.9 (100%) [M+]. UV-Vis (in dichloromethane, λmax (∈[M−1 cm−1]: 518 nm (7.0×104 M−1 cm−1). Fluorescence (in dichloromethane, λex=528 nm. φex: 0.55. Elem. Anal.: theoretical: C, 76.46%, H, 7.30%; N, 9.22%; experimental: C, 76.80%; H, 6.98%; N, 9.50%.


Example 5
Preparation of Bottom-Gate Organic Field Effect Transistors Containing Compound 1b as Semiconducting Material

Thermally grown silicon dioxide (thickness: 200 nm) is used as dielectric layer. The gate electrode is formed by depositing highly doped silicon on one side of the dielectric layer. The other side of the dielectric layer is treated with hexamethyldisilazane (HMDS) by vapour deposition of hexamethyldisilazane. The contact angle of the surface of the HMPS-treated side of the dielectric layer is 93.2±1.3°. Source/drain electrodes (Ta (thickness: 10 nm) covered by Au (thickness: 40 nm)) are deposited on the HMPS-treated side of the dielectric layer by vapour deposition. The channel length is 20 μm and the channel width is 1.4 mm, affording W/L=70. The source/drain electrodes are then covered with the semiconducting layer (thickness: ca. 100 nm) by drop-casting a solution of compound 1b in chloroform (concentration=10 mg/mL) in a nitrogen filled glove box (02 content: 0.1 ppm, H2O content: 0.0 ppm, pressure: 1120 Pa, temperature: 17° C.) using a Keithley 4200 machine.


The design of the bottom-gate organic field effect transistor of example 5 is shown in FIG. 1.


The drain current ISD [A] in relation to the gate voltage VSG [V] (top transfer curve) and the drain current ISD0.5 [μA0.5] in relation to the gate voltage VSG [V] (bottom transfer curve) for the bottom-gate organic field effect transistor of example 5 comprising compound 1b as semiconducting material at a drain voltage VSD of 100 V is determined in a nitrogen filled glove box (O2 content: 0.1 ppm, H2O content: 0.0 ppm, pressure: 1120 Pa, temperature: 17° C.) using a Keithley 4200 machine is shown. The results are shown in FIG. 2.


In FIG. 3 the charge carrier mobility μsat [cm2/Vs] in relation to the gate voltage VSG [V] for the bottom-gate organic field effect transistor of example 5 comprising compound 1b as semiconducting material is shown.


The average values and the 90% confidence interval (in parentheses) of the charge carrier mobility μsat [cm2/Vs], the ION/IOFF ratio and the switch-on voltage V50 [V] for the bottom-gate organic field effect transistor of example 5 comprising compound 1b as semiconducting material is given in table 1. The switch-on voltage V50 [V] is the gate voltage V50 [V] where the drain current ISD [A] starts to increase (out of the off-state).












TABLE 1






μsat

VSO


Compound
[cm2/Vs]
ION/IOFF
[V]







1b
1.5 (±1.2) × 10−6
1.6 (±0.4) × 102
61.3 (±2.0)








Claims
  • 1. A compound of formula
  • 2. A process for the preparation of the compound of formula (1) of claim 1, which process comprises the steps of
  • 3. The process of claim 2, wherein in the compound of formula (4) L is C2-5-alkylene, which can be optionally substituted with 1 to 6 C1-10-alkyl groups.
  • 4. The process of claim 2, wherein the cyanide source in step (ii) is selected from the group consisting of tetra-C1-10-alkylammoniumcyanide, tetra-C1-10-alkylphosphoniumcyanide and hexa-C1-10-alkylguanidiniumcyanide.
  • 5. The process of claim 2, wherein the cyanide source in step (ii) is Zn(CN)2.
  • 6. A compound of formula
  • 7. An electronic device comprising the compound of formula (1) of claim 1 as semiconducting material.
  • 8. A compound according to claim 6, wherein L is C2-5-alkylene, which can be optionally substituted with 1 to 6 C1-10-alkyl groups.
Parent Case Info

This application claims the benefit of U.S. Provisional Application No. 61/448,669 filed Mar. 3, 2011 herein incorporated entirely by reference.