The present invention relates to a pharmaceutical composition in a solid extruded form wherein extrusion may be at a lower temperature and the resulting extrudate has a higher compressibility.
Many pharmaceuticals and nutraceuticals are provided in a solid form using melt extrusion process. Generally, an extruder comprises a barrel with screws that force the materials including a polymeric material and the active pharmaceutical ingredient (API) through a shaping die. The extruder is typically heated to soften the polymeric material and to lower its melt viscosity. Such a melt extrusion process is often used to formulate poorly soluble APIs as solid dispersions. In the process, the non-active polymer is often in the amorphous state or semi-crystalline state and the API is converted to its amorphous state from its initial crystalline state to enhance its solubility. Once extruded the solid form is typically milled and then compressed into a tablet, pellet or granule.
Viscosity is an important aspect of melt extrusion and is often reduced by increasing heat. Many APIs, however, are heat sensitive, thus excessive heat must be avoided to prevent adversely affecting the activity of the API. After extrusion, compressibility is an important aspect, and the solid form must be sufficiently hard to be able to compress the extrudate into its desired form.
Thus, the present invention provides a pharmaceutical composition exhibiting a lower melt viscosity and a solid extruded from (extrudate) exhibiting a higher compressibility.
A pharmaceutical composition is provided and includes an extrudable solid and one or more pharmaceuticals or nutraceuticals. The extrudable solid comprises hydroxypropylmethylcellulose acetate succinate and isomalt.
The foregoing and other aspects of the present invention will now be described in more detail with respect to the description and methodologies provided herein. It should be appreciated that the invention can be embodied in different forms and should not be construed as limited to the embodiments set forth herein. Rather, these embodiments are provided so that this disclosure will be thorough and complete, and will fully convey the scope of the invention to those skilled in the art.
The terminology used in the description of the invention herein is for the purpose of describing particular embodiments only and is not intended to be limiting of the invention. As used in the description of the embodiments of the invention and the appended claims, the singular forms “a”, “an” and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise. Also, as used herein, “and/or” refers to and encompasses any and all possible combinations of one or more of the associated listed items. Furthermore, the term “about,” as used herein when referring to a measurable value such as an amount of a compound, dose, time, temperature, and the like, is meant to encompass variations of 20%, 10%, 5%, 1%, 0.5%, or even 0.1% of the specified amount.
It will be further understood that the terms “comprises” and/or “comprising,” when used in this specification, specify the presence of stated features, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of one or more other features, integers, steps, operations, elements, components, and/or groups thereof. Unless otherwise defined, all terms, including technical and scientific terms used in the description, have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs.
The term “consists essentially of” (and grammatical variants), as applied to in this invention, means the methods or compositions can contain additional steps or components as long as the additional steps or components do not materially alter the basic and novel characteristic(s) of the present invention.
The term “consisting of” excludes any additional step or component that is not specified in the claim.
Unless the context indicates otherwise, it is specifically intended that the various features of the invention described herein can be used in any combination.
Moreover, the present invention also contemplates that in some embodiments of the invention, any feature or combination of features set forth herein can be excluded or omitted.
All patents, patent applications and publications referred to herein are incorporated by reference in their entirety. In case of a conflict in terminology, the present specification is controlling.
As one of ordinary skill in the art may appreciate, the parameters described herein may vary greatly depending on the process, and/or formulation as well as the desired properties of the final product.
The present invention is directed to a novel pharmaceutical composition comprising an extrudable solid (i.e., an extrudate) and a pharmaceutical or nutraceutical mixed with the extrudable solid. The extrudable solid comprises hydroxypropylmethylcellulose acetate succinate (HPMCAS) and isomalt.
In one embodiment, the HPMCAS is commercially available such as Shin-Etsu AQOAT® from Shin-Etsu Chemical Co., Ltd. (Japan), AffiniSol® from Dow Chemical (USA), and AquaSolve™ from Ashland (USA). In one embodiment, the isomalt is galenIQ™ available from BENEO GmbH (Germany). Isomalt is a sugar alcohol comprising an equal mixture of two stereoisomers, α-glucopyranosyl-1-1-D-mannitol (GPM) and α-D-glucopyranosyl-1, 6-D-sorbitol (GPS).
Optionally, other materials typically used as additives or excipients in pharmaceutical or nutraceutical compositions may be included. Exemplary other components include control release agents such as hypromellose, hydroxypropyl cellulose, ethylcellulose, hydroxypropylmethylcellulose phthalate, cellulose acetate phthalate, carboxymethylethylcellulose, methyl methacrylate-methacrylate copolymer, methacrylate-ethyl acrylate copolymer, methacrylate-methyl acrylate-methyl methacrylate copolymer, polyvinyl acetate phthalate and shellac. These other components may be included in amounts of about 1 to about 50 percent by weight of the composition.
The extrudable solid composition to be extruded comprises about 10 to about 80 percent HPMCAS, about 3 to 50 percent isomalt and about 10 to about 80 percent API. The extrudate (tablet) comprises about 10 to about 100 percent of the extrudable solid composition for extrusion, about 0 to about 20 percent of a disintegrant, about 0 to about 80 percent filler, about 0 to about 80 percent binder and about 0 to about 1 percent lubricant/glidant.
Suitable disintegrants include hydroxypropylcellulose (HPC), low-substituted HPC (L-HPC), carboxymethylcellulose (CMC), sodium CMC, calcium CMC, crospovidone, croscarmellose sodium; starches (e.g., carboxymethyl starch, hydroxylpropyl starch, modified starch); crystalline cellulose, sodium starch glycolate; alginic acid or a salt thereof, such as sodium alginate or their equivalents and mixtures thereof.
Suitable fillers include lactose, lactose monohydrate, lactitol, saccharose, sorbitol, mannitol, dextrates, dextrins, dextrose, maltodextrin, croscarmellose sodium, silicified microcrystalline cellulose, microcrystalline cellulose, hydroxypropylcellulose, low-substituted hydroxypropylcellulose, hydroxypropylmethylcellulose polymers, hydroxyethylcellulose, sodium carboxymethylcellulose, carboxymethylene, carboxymethyl hydroxyethylcellulose and other cellulose derivatives, starches or modified starches (including potato starch, corn starch, maize starch and rice starch) and mixtures thereof.
Suitable binders include polyvinyl pyrrolidone (also known as povidone), polyethylene glycol(s), acacia, alginic acid, agar, calcium carrageenan, cellulose derivatives such as ethyl cellulose, methyl cellulose, hydroxypropyl cellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, dextrin, gelatin, gum arabic, guar gum, tragacanth, sodium alginate, or mixtures thereof or any other suitable binder.
Suitable lubricants/glidants include stearic acid and pharmaceutically acceptable salts or esters thereof (for example, magnesium stearate, calcium stearate, sodium stearyl fumarate or other metallic stearates), talc, microcrystalline waxes, glycerides, light mineral oil, polyethylene glycol, silica acid and pharmaceutically acceptable salts or esters thereof (for example, silicates, silicon dioxide, colloidal silicon dioxide, sucrose esters of fatty acids, hydrogenated vegetable oils (for example, hydrogenated castor oil), or mixtures thereof.
The overall composition may include about 65 to about 95 percent by water weight as the dispersing agent to provide the composition in aqueous form.
Other additives may include absorption enhancers, dissolution modifying agents, coloring aids, flavoring agents, and stabilizing agents (e.g., dibasic sodium phosphate).
The extruded form may be formed into tablets, pellets and granules.
In operation, the API may be blended with the hydropropylmethylcellulose acetate succinate and isomalt in a high-speed blender for 0 to 60 minutes. The blend may be extruded in one embodiment through a twin-screw extruder at a temperature of 100° to 200° C. and a screw speed of 100 to 1000 rpm. Specific shaping of the extrudate may occur as will be known to one skilled in the art. The extrudate may then be compressed into a tablet, pellet or granule using conventional tableting machines. The resulting tablet, pellet or granule may optionally then be coated using conventional coating equipment to improve the appearance or taste or film-coated with an aqueous or organic polymer composition.
The active pharmaceutical ingredient (API) may be a pharmaceutical or a nutraceutical. As used herein “pharmaceutical” is defined as any chemical substance intended for use in the medical diagnosis, cure, treatment, or prevention of disease, for example over-the-counter drugs (OTC) and prescription only medicine (POM). Exemplary active pharmaceutical components are listed in U.S. Pat. No. 6,723,358, column 9, line 25 to column 13, line 25, the disclosure of which is incorporated herein by reference in its entirety.
As used herein “nutraceutical” supplement include any nutrients that may provide health and medical benefits, including the prevention and treatment of disease. Examples include, but are not limited to, vitamins, minerals, probiotics, enzymes, herb and other botanical extracts, amino acid, concentrates, metabolites, constituents, etc.
Exemplary vitamins and minerals include, but are not limited to, vitamins A (in the form of, for example, palmitate or beta carotene), B-complex (such as B-1, B-2, B-6 and B-12), C, D, E and K; niacin; acid vitamins such as pantothenic acid and folic acid; biotin; minerals such as iron, calcium, magnesium, iodine, copper, phosphorus, zinc, manganese, potassium, chromium, cobalt, molybdenum, selenium, nickel, tin, silicon, vanadium and boron; nutraceutical supplements such as fluorine and chlorine; and the like. Various herbs and herbal remedies may be utilized as the nutraceutical supplements. The herbs are generally selected from those that have various medicinal or dietary supplement properties. Herbs are generally aromatic plants or plant parts that can be used medicinally or for flavoring. Examples include Gingko biloba, gotu kola, echinacea, St. John's wort, ginseng, valerian and the like. Suitable herbs may be used alone or in various mixtures in the filling described herein.
The present invention will be further illustrated by the following non-limiting examples.
The extrudate was prepared by blending HPMCAS (Shin-Etsu AQOAT® AS-MMP), isomalt and the API (nifedipine) for 20 minutes. Isomalt 720 and Isomalt 721 available GalenIQ™ from Beneo, Germany was added at 5, 10 and 20 percent levels. Mannitol (Pearlitol®), hydropropylcellulose (grade: HPC-L) and copovidone (Kollidon®) were used as comparative additives to isomalt. A control without isomalt or the other additives was also prepared.
Each was tested for percentage of maximum torque during an extrusion process. The extruder was a Pharma-11 twin-screw extruder (Thermo Scientific, Germany), at the main barrel temperature of 175° C. The results are provided in Table 1.
The extrudable composition including 20 percent added were compressed at 15, 20 or 25 KN using a Handtab-200 single station table press (Ichihashiseki, Japan). Tablet hardness was recorded using a TBH 125 (Erweka, Germany) hardness tester. The results are provided in
Using a Pharma-11 twin-screw extruder (Thermo Scientific, Germany), a mixture of API (nifedipine) (20%) HPMCAS (AS-MMP, 75 or 60%) and Isomalt 720 (5 or 20%) was extruded. The main barrel temperature was set at 155° C. or 175° C., and screw speed was set at 100 or 400 rpm. The parameters were set according to 23 factorial Plackett-Burman design to carry out 12 experiments. The extrudate was milled and compressed into a tablet using a single-punch tablet press (Handtab-200, Ichihashiseki, Japan) at 25 kN, and hardness was measured using a TBH 125 hardness tester (Erweka, Germany). The results are summarized in Table 2.
The results clearly indicate that higher content of isomalt provides higher tensile strength.
Using a Pharma-11 twin-screw extruder (Thermo Scientific, Germany), a mixture of API (itraconazole (20%)) and HPMCAS (AS-MMP, 80%) was extruded at the main barrel temperature of 175° C. (Example 3A). The extrudate was milled and compressed into tablets (diameter: 1 cm, weight: 400 mg) using a single-punch tablet press (Handtab-200, Ichihashiseki, Japan) at a compression force of 8 kN. The tablet hardness measured using a TBH 125 hardness tester (Erweka, Germany), was 90N. In the same way, a mixture of API (itraconazole (20%)), HPMCAS (AS-MMP, 65%), and Isomalt 721 (15%) was extruded (Example 3B). The main barrel temperature of 155° C. was necessary to achieve the same extruding torque as the extrusion without isomalt. The tablet hardness was 230N, which was significantly higher than the formulation without isomalt. Dissolution test for both tablets of Examples 3A and 3B was carried out using a dissolution tester (Model 2500, Distek, USA). The analysis of itraconazole was done using an Agilent 1100 HPLC (USA). The dissolution results are shown in
Having thus described certain embodiments of the present invention, it is to be understood that the invention defined by the appended claims is not to be limited by particular details set forth in the above description as many apparent variations thereof are possible without departing from the spirit or scope thereof as hereinafter claimed.
The present application claims priority from U.S. Provisional Application No. 62/541,928 filed Aug. 7, 2017, the disclosure of which is incorporation herein by reference in its entirety.
| Number | Date | Country | |
|---|---|---|---|
| 62541928 | Aug 2017 | US |