Claims
- 1. A two container pack for providing, on mixing of the two parts of the pack, a phenol-formaldehyde resin foam, which two part pack comprises:
- in a first part, in stable combination, a phenolic resin, a blowing agent which is an inert low boiling liquid, an effective amount of a nitrogenous modifier capable of permitting dispersion of the blowing agent in the resin, and a surfactant; and
- in a second container in stable combination an acid catalyst composition dispersed in a polyhydroxy compound, in a weight ratio of acid catalyst to polyhydroxy compound of at least 1:1.
- 2. A two part pack according to claim 1 which comprises:
- in a first part in stable combination,
- (a) a resole phenol-formaldehyde resin with a water content of up to 20%, which has been prepared under acid conditions, and has a pH of between 4.0 and 6.0;
- (b) an inert blowing agent chosen from a hydrocarbon or a chlorofluorohydrocarbon;
- (c) a surfactant; and
- (d) a nitrogeneous modifier chosen from an amine, a polymeric amine, or a natural vegetable oil containing amine or amino nitrogen; and in a second part in stable combination;
- (i) an acid catalyst composition containing sulphuric acid or an organic sulphonic acid together with phosphoric acid; and
- (ii) a polyhydroxy compound chosen from ethylene glycol, propylene glycol and glycerine in a weight ratio of acid catalyst (i) to polyhydroxy compound (ii) of at least 1:1. excluding the phosphoric acid, and into which polyhydroxy compound (ii) the acid catalyst (i) is dispersed.
- 3. A two part pack according to claim 1 wherein the phenol-formaldehyde resin used in the first part of the pack has a pH of from 4.5 to 6.0.
- 4. A two part pack according to claims 1 or 2 wherein the blowing agent used in the first part of the pack is dichlorodifluoromethane.
- 5. A two part pack according to claims 1 or 2 wherein the surfactant used in the first part of the pack is a silicone-based material.
- 6. A two part pack according to claims 1 or 2 wherein the organic sulphonic acid used in the second part of the pack is chosen from one or more of methane sulphonic acid, benzene sulphonic acid, and para-toluene sulphonic acid.
- 7. A two part pack according to claims 1 or 2 wherein the nitrogenous modifier used in the first part of the pack is chosen from at least one of diethanolamine, triethanolamine, diethanoltriamine, triethanoltetramine, piperazine, hexamethylene tetramine, tall oil, and amino group containing polymers of formaldehyde with urea, melamine, or guanidine.
- 8. A two part pack according to claims 1 or 2 wherein the acid catalyst system used in the second part of the pack contains 1 part by weight sulphuric acid or organic sulphonic acid, together with zero to 1 part by weight phosphoric acid, provided that the weight ratio of phosphoric acid to sulphuric acid or organic sulphonic acid does not exceed 1:1.
- 9. A two part pack according to claims 1 or 2 wherein the first part of the pack contains in parts by weight:
- ______________________________________phenol-formaldehyde resin: 100 parts;surfactant: 0.1 to 4.0 parts;nitrogenous modifier 1 to 20 parts;andblowing agent: 1 to 20 parts.______________________________________
- 10. A two part pack according to claims 1 or 2 wherein the second part of the pack contains in parts by weight:
- ______________________________________sulphuric acid 1 part85% phosphoric acid 1 partpropylene glycol at least 0.5 parts.______________________________________
- 11. A two part pack according to claims 1 or 2 wherein the first part of the pack contains a phenol-formaldehyde resin prepared from substantially pure phenol.
- 12. A two part pack according to claims 1 or 2 wherein the first part of the pack contains a phenol-formaldehyde resin prepared from technical grade phenol.
- 13. A two part pack according to claims 1 or 2 wherein the first part of the pack contains a phenol-formaldehyde resin prepared from a technical grade phenol having a boiling range of 180.degree. C. to 200.degree. C. and containing not more than 15% by weight ortho-cresol plus xylenols.
- 14. A two part pack according to claims 1 or 2 wherein the first part of the pack contains a polyhydroxy compound which may be the same as or different to the polyhydroxy-compound used in the second part of the pack.
CROSS-REFERENCE TO RELATED APPLICATION
This application is a continuation-in-part of our application Ser. No. 919,972, filed June 28, 1978 and now U.S. Pat. No. 4,219,623.
US Referenced Citations (19)
Continuation in Parts (1)
|
Number |
Date |
Country |
Parent |
919972 |
Jun 1978 |
|