TREA

Phosphate phosphor and UV light-emitting device utilizing the same

Follow

Information

  • Patent Grant
  • 8636921
  • Patent Number
    8,636,921
  • Date Filed
    Thursday, February 7, 2013
    11 years ago
  • Date Issued
    Tuesday, January 28, 2014
    10 years ago
Information
Abstract
Disclosed is a phosphor having a formula of M3-2xM′x(M″1-y-zPryGdz)(PO4)2. M is Li, Na, K, or combinations thereof. M′ is Ca, Sr, Ba, Mg, Zn, or combinations thereof. M″ is Sc, Y, La, Lu, Al, Ga, In, or combinations thereof. 0≦x≦1, 0
Description
CROSS REFERENCE TO RELATED APPLICATIONS

The present application is based on, and claims priority from, Taiwan Application Serial Number 101139017, filed on Oct. 23, 2012, the disclosure of which is hereby incorporated by reference herein in its entirety


TECHNICAL FIELD

The disclosure relates to a phosphor, and in particular to a UV light-emitting device utilizing the same.


BACKGROUND

Excitation and emission properties of inorganic phosphors are mainly determined by host materials, activators, and other dopants. Phosphors composed of different host materials, activators or other dopants may have different luminescent properties, such that the composition is the most important factor in tuning the optoelectronic properties of the phosphors. Mainstream host materials of inorganic phosphors are sulfides, oxides, oxysulfides, or other complex oxides such as silicates, aluminates, phosphates, and the likes. Recently, phosphor development of host materials has partly moved in the direction of nitrides and oxynitrides. The major activators being used are ions of transition-metal elements or rare-earth elements.


Future, light sources should meet the environmental protection requirement of being mercury-less or mercury-free, such that a high-efficiency Xe2* excimer lamp will possibly become a mainstream light source in the future. The Xe2* excimer lamp should probably collocate with a phosphor to convert light from short-wavelength to long-wavelength. For example, the Xe2* excimer lamp emits a vacuum ultraviolet (VUV) light having a wavelength of 172 nm, which can be converted by an appropriate phosphor to emit a UV-B light having a wavelength of 280 to 320 nm or a UV-C light having a wavelength of 200 nm to 280 nm. The UV-B light can be applied in phototherapy such as treating skin diseases such as psoriasis, vitiligo, atopic dermatitis, and the likes. The UV-C light may be applied in disinfection, purification, TOC (total organic compounds) reduction, and the likes. Conventional phosphors excitable by the VUV light from the Xe2* excimer lamp are rare, such that developments of novel phosphors are still called for.


SUMMARY

One embodiment of the disclosure provides a phosphor, having the chemical formula: M3-2xM′x(M″1-y-zGdz)(PO4)2, wherein M is Li, Na, K, or combinations thereof; M′ is Ca, Sr, Ba, Mg, Zn, or combinations thereof; M″ is Sc, Y, La, Lu, Al, Ga, In, or combinations thereof; 0≦x≦1; 0<y≦0.15; and 0<z≦0.7.


One embodiment of the disclosure provides an ultraviolet light-emitting device, comprising: an excitation light source; and the described phosphor, wherein the excitation light source emits light having a wavelength of 140 nm to 240 nm.


A detailed description is given in the following embodiments with reference to the accompanying drawings.





BRIEF DESCRIPTION OF THE DRAWINGS

The disclosure can be more fully understood by reading the subsequent detailed description and examples with references made to the accompanying drawings, wherein:



FIG. 1 shows the ultraviolet light-emitting device in one embodiment of the disclosure;



FIG. 2 shows the emission spectra of the phosphors K3(Y1-yPry)(PO4)2 having different doping ratios of the activator Pr3+, wherein y was 0.02, 0.04, 0.06, 0.08, 0.1, 0.12, and 0.14, respectively, in one embodiment of the disclosure;



FIG. 3 shows the excitation spectrum of the phosphor K3(Y0.92Pr0.08)(PO4)2 in one embodiment of the disclosure;



FIG. 4 shows the emission spectra of the phosphors K3(Y1-zGdz)(PO4)2 having different doping ratios of the activator Gd3+, wherein z was 0.3, 0.4, 0.5, 0.6, and 0.7, respectively, in one embodiment of the disclosure;



FIG. 5 shows the emission spectra of the phosphors K3(Y0.92-zPr0.08Gdz)(PO4)2 having different doping ratios of the activator Gd3+, wherein z was 0.3, 0.4, 0.5, 0.6, and 0.7, respectively, in one embodiment of the disclosure;



FIG. 6 shows the excitation spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2 and K3(Y0.5Gd0.5)(PO4)2 in one embodiment of the disclosure;



FIG. 7 shows the emission spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2 and K3(Y0.5Gd0.5)(PO4)2 in one embodiment of the disclosure;



FIG. 8 shows the emission spectra comparison of the phosphors Li3(Y0.42Pr0.08Gd0.5)(PO4)2, Na3(Y0.42Pr0.08Gd0.5)(PO4)2, and K3(Y0.42Pro0.08Gd0.5)(PO4)2 in one embodiment of the disclosure;



FIG. 9 shows the emission spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2, K3(Ga0.42Pr0.08Gd0.5)(PO4)2, and K3(In0.42Pr0.08Gd0.5)(PO4)2 in one embodiment of the disclosure;



FIG. 10 shows the emission spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2, K3(La0.42Pr0.08Gd0.5)(PO4)2, K3(Lu0.42Pr0.08Gd0.5)(PO4)2, and K3(Sc0.42Pr0.08Gd0.5)(PO4)2 in one embodiment of the disclosure;



FIG. 11 shows the emission spectra of the phosphors KCa(Y1-yPry)(PO4)2 having different doping ratios of the activator Pr3+, wherein y was 0.01, 0.02, 0.05, 0.1, and 0.15, respectively, in one embodiment of the disclosure;



FIG. 12 shows the emission spectra of the phosphors KCa(Y1-zGdz)(PO4)2 having different doping ratios of the activator Gd3+, wherein z was 0.1, 0.2, 0.3, 0.4, and 0.5, respectively, in one embodiment of the disclosure;



FIG. 13 shows the emission spectra of the phosphors KCa(Y0.7-yPryGd0.3)(PO4)2 having different doping ratios of the activator Pr3+, wherein y was 0, 0.001, 0.003, 0.005, 0.007, and 0.01, respectively, in one embodiment of the disclosure; and



FIG. 14 shows the emission spectra comparison of the phosphors KCa(Y0.699Pr0.001Gd0.3)(PO4)2, KSr(Y0.699Pr0.001Gd0.3)(PO4)2, KBa(Y0.699Pr0.001Gd0.3)(PO4)2, KMg(Y0.699Pr0.001Gd0.3)(PO4)2, and KZn(Y0.699Pr0.001Gd0.3)(PO4)2 in one embodiment of the disclosure.





DETAILED DESCRIPTION

In the following detailed description, for purposes of explanation, numerous specific details are set forth in order to provide a thorough understanding of the disclosed embodiments. It will be apparent, however, that one or more embodiments may be practiced without these specific details. In other instances, well-known structures and devices are schematically shown in order to simplify the drawing.


In general, phosphors with a phosphate host material have a wide band gap, and can be doped with different activators to exhibit different excitation and emission characteristics. In short, the phosphate is a multi-purpose host material system. In embodiments of the disclosure, the phosphate MM′M″(PO4)2 or M3M″(PO4)2 is selected as a host material doped with the activators Pr3+ and/or and Gd3+. M is a monovalent metal element selected from Li, Na, K, or combinations thereof. M′ is a divalent metal element selected from Ca, Sr, Ba, Mg, Zn, or combinations thereof. M″ is a trivalent metal element selected from Sc, Y, La, Lu, Al, Ga, In, or combinations thereof. Because Pr3+ ion and Gd3+ ion have a suitable energy level to emit UV-B light or UV-C light, they can be doped into the phosphate host materials MM′M″(PO4)2 or M3M″(PO4)2 to be applied as a UV light-emitting phosphor. As such, the phosphate doped with Pr3+ and Gd3+ can be collocated with a Xe2* excimer lamp to complete a UV-B or UV-C light source free of mercury.


In one embodiment, the phosphor has the chemical formula in Formula 1.

M3-2xM′x(M″1-y-zPryGdz)(PO4)2  (Formula 1)


In Formula 1, M is Li, Na, K, or combinations thereof. M′ is Ca, Sr, Ba, Mg, Zn, or combinations thereof. M″ is Sc, Y, La, Lu, Al, Ga, In, or combinations thereof. 0≦x≦1, 0<y≦0.15, and 0<z≦0.7.


If x in Formula 1 is equal to 0 (x=0), the phosphor will have a formula of M3(M″1-y-zPryGdz)(PO4)2, such as Li3(Y1-y-zPryGdz)(PO4)2, Na3(Y1-y-zPryGdz)(PO4)2, K3(Y1-y-zPryGdz)(PO4)2, K3(Ga1-y-zPryGdz)(PO4)2, K3(In1-y-zPryGdz)(PO4)2, K3(La1-y-zPryGdz)(PO4)2, K3(Lu1-y-zPryGdz)(PO4)2, or K3(Sc1-y-zPryGdz)(PO4)2. If x in Formula 1 is equal to 1 (x=1), the phosphor will have a formula of MM′(M″1-y-zPryGdz)(PO4)2, such as KCa(Y1-y-zPryGdz)(PO4)2, KSr(Y1-y-zPryGdz)(PO4)2, KBa(Y1-y-zPryGdz)(PO4)2, KMg(Y1-y-zPryGdz)(PO4)2, or KZn(Y1-y-zPryGdz)(PO4)2. The phosphor can be excited by light having a wavelength of 140 nm to 240 nm to emit an ultraviolet light having a major emission peak of 240 nm to 400 nm. The phosphor M3-2xM′x(M″1-y-zPryGdz)(PO4)2 can be applied in an ultraviolet light-emitting device. In one embodiment, the ultraviolet light-emitting device 10 includes a lamp 12 filled with xenon 11, an outer electrode 13 on an outer surface of the lamp 12, an inner electrode 15 inside the lamp 12, and phosphor 14 (M3-2xM′x(M″1-y-zPryGdz)(PO4)2) coated on an inner surface of the lamp 12, as shown in FIG. 1. The inner electrode 15 and the outer electrode 13 are connected to a positive electrode and a negative electrode of a high voltage power supply 17, respectively, thereby exciting the xenon to emit light having a wavelength of 140 nm to 240 nm.


In addition, the disclosure also provides a method for manufacturing the described phosphate phosphors. First, (1) a compound containing M and oxygen, (2) a compound containing M′ and oxygen, (3) a compound containing M″ and oxygen, (4) (NH4)2HPO4 or (NH4)H2PO4, and (5) a compound containing Pr and oxygen and a compound containing Gd and oxygen were mixed to obtain a mixture. The mixture is then sintered at a temperature of 900° C. to 1300° C. After the mixture is heated to the sintering temperature, the mixture is sintered at the sintering temperature for eight hours to thirty-two hours. According to the embodiments, the compounds containing M and oxygen can be metal oxides, metal carbonates, or metal nitrates of Li, Na, K, or combinations thereof. The compounds containing M′ and oxygen can be metal oxides, metal carbonates, or metal nitrates of Ca, Sr, Ba, Mg, Zn, or combinations thereof. The compounds containing M″ and oxygen can be metal oxides, metal carbonates, or metal nitrates of Sc, Y, La, Lu, Al, Ga, In, or combinations thereof. The compound containing Pr and oxygen and the compound containing Gd and oxygen can be metal oxides or metal nitrites.


Below, exemplary embodiments will be described in detail with reference to accompanying drawings so as to be easily realized by a person having ordinary knowledge in the art. The inventive concept may be embodied in various forms without being limited to the exemplary embodiments set forth herein. Descriptions of well-known parts are omitted for clarity, and like reference numerals refer to like elements throughout.


EXAMPLES
Example 1

According to the molar ratios of K3(Y1-yPry)(PO4)2, wherein y was 0.02, 0.04, 0.06, 0.08, 0.1, 0.12, and 0.14, respectively, appropriate stoichiometry of K2CO3, Y2O3, Pr2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 900° C.-1100° C. in air, the phosphors K3(Y1-yPry)(PO4)2 having different Y/Pr ratios were prepared. FIG. 2 shows the emission spectra of the phosphors K3(Y1-yPry)(PO4)2 with different Y/Pr molar ratios, which emit UV light of 230 nm to 300 nm. As shown in FIG. 2, the phosphor doped with 8 mol % of Pr3+ had excellent emission intensity. FIG. 3 shows the excitation spectrum of the phosphor K3(Y0. 92Pr0.08)(PO4)2, which has an excitation band of 140 nm to 240 nm.


According to the molar ratios of K3(Y1-zGdz)(PO4)2, wherein z was 0.3, 0.4, 0.5, 0.6, and 0.7, respectively, appropriate stoichiometry of K2CO3, Y2O3, Gd2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 900° C.-1100° C. in air, the phosphors K3(Y1-zGdz)(PO4)2 having different Y/Gd ratios were prepared. FIG. 4 shows the emission spectra of the phosphors K3(Y1-zGdz)(PO4)2 with different Y/Gd molar ratios, which emit UV light of 300 nm to 330 nm. As shown in FIG. 4, the phosphor doped with 50 mol % of Gd3+ had excellent emission intensity.


According to the molar ratios of K3(Y0.92-zPr0.08Gdz)(PO4)2, wherein the doping ratio of Pr3+ was a constant of 8 mol % and the doping ratio of Gd3+ (z) was changeable, appropriate stoichiometry of K2CO3, Y2O3, Pr2O3, Gd2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 900° C.-1100° C. in air, the phosphors K3(Y0.92-zPr0.008Gdz)(PO4)2 having different Y/Gd ratios were prepared. FIG. 5 shows the emission spectra of the phosphors K3(Y0.92-zPr0.08Gdz)(PO4)2 with different Y/Gd molar ratios, which emit UV light of 300 nm to 330 nm. As shown in FIG. 5, the phosphor doped with 8 mol % of Pr3+ and 50 mol % of Gd3+ had excellent emission intensity. FIGS. 6 and 7 show the comparison between the luminescence spectra of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2, and K3(Y0.5Gd0. 5)(PO4)2, respectively. As shown in FIG. 7, the phosphor doped with Pr3+ and Gd3+ has an emission intensity largely greater than that of the phosphor doped with only Gd3+. In addition, the phosphor doped with Pr3+ and Gd3+ has an excitation band wider than that of the phosphor doped with only Gd3+.


UV light-emitting phosphors including other monovalent cations (e.g. Li+ or Na+) could be synthesized by the described steps and suitable starting materials of appropriate molar ratios. FIG. 8 shows the emission spectra comparison of the phosphors Li3(Y0.42Pr0.08Gd0.5)(PO4)2, Na3(Y0.42Pr0.08Gd0.5)(PO4)2, and K3(Y0.42Pr0.08Gd0.5)(PO4)2.


UV light-emitting phosphors including other trivalent cations (e.g. Ga3+, In3+, La3+, Lu3+, or Sc3+) could be synthesized by the described steps and suitable starting materials of appropriate molar ratios. FIG. 9 shows the emission spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2, K3(Ga0.42Pr0.08Gd0.5)(PO4)2, and K3(In0.42Pr0.08Gd0.5)(PO4)2. FIG. 10 shows an emission spectra comparison of the phosphors K3(Y0.42Pr0.08Gd0.5)(PO4)2, K3(La0.42Pr0.08Gd0.5)(PO4)2, K3(Lu0.42Pr0.08Gd0.5)(PO4)2, and K3(Sc0.42Pr0.08Gd0.5)(PO4)2.


Example 2

According to molar ratios of KCa(Y1-yPry)(PO4)2, wherein y was 0.01, 0.02, 0.05, 0.1, and 0.15, respectively, appropriate stoichiometry of K2CO3, CaCO3, Y2O3, Pr2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 950° C.-1250° C. in air, the phosphors KCa(Y1-yPry)(PO4)2 having different Y/Pr ratios were prepared. FIG. 11 shows emission spectra of the phosphors KCa(Y1-yPry)(PO4)2 with different Y/Pr molar ratios, which emit UV light of 230 nm to 330 nm. As shown in FIG. 11, the phosphor doped with 10 mol % of Pr3+ had excellent emission intensity.


According to molar ratios of KCa(Y1-zGdz)(PO4)2, wherein z was 0.1, 0.2, 0.3, 0.4, and 0.5, respectively, appropriate stoichiometry of K2CO3, CaCO3, Y2O3, Gd2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 950° C.-1250° C. in air, the phosphors KCa(Y1-zGdz)(PO4)2 having different Y/Gd ratios were prepared. FIG. 12 shows the emission spectra of the phosphors KCa(Y1-zGdz)(PO4)2 with different Y/Gd molar ratios, which emit UV light of 300 nm to 330 nm. As shown in FIG. 12, the phosphor doped with 30 mol % of Gd3+ had excellent emission intensity.


According to molar ratios of KCa(Y0.7-yPryGd0.3)(PO4)2, wherein the doping ratio of Pr3+ (y) was changeable and the doping ratio of Gd3+ was a constant of 30 mol %, appropriate stoichiometry of K2CO3, CaCO3, Y2O3, Pr2O3, Gd2O3, and (NH4)2HPO4 were evenly mixed and then charged into a crucible. The crucible was then heated in a high-temperature furnace. After sintering at 950° C.-1250° C. in air, the phosphors KCa(Y0.7-yPryGd0.3)(PO4)2 having different Y/Pr ratios were prepared. FIG. 13 shows the emission spectra of the phosphors KCa(Y0.7-yPryGd0.3)(PO4)2 with different Y/Pr molar ratios, which emit UV light of 305 nm to 315 nm. As shown in FIG. 13, the phosphor doped with 0.1 mol % of Pr3+ and 30 mol % of Gd3+ had excellent emission intensity.


UV light-emitting phosphors including other divalent cations (e.g. Sr2+, Ba2+, Mg2+, or Zn2+) could be synthesized by the described steps and suitable starting materials of appropriate molar ratios. FIG. 14 shows the emission spectra comparison of the phosphors KCa(Y0.699Pr0.001Gd0.3)(PO4)2, KSr(Y0.699Pr0.001Gd0.3)(PO4)2, KBa(Y0.699Pr0.001Gd0.3)(PO4)2, KMg(Y0.699Pr0.001Gd0.3)(PO4)2, and KZn(Y0.699Pr0.001Gd0.3)(PO4)2.


It will be apparent to those skilled in the art that various modifications and variations can be made to the disclosed methods and materials. It is intended that the specification and examples be considered as exemplary only, with a true scope of the disclosure being indicated by the following claims and their equivalents.

Claims
  • 1. A phosphor, having the chemical formula: M3-2xM′x(M″1-y-zPryGdz)(PO4)2,wherein M is Li, Na, K, or combinations thereof;M′ is Ca, Sr, Ba, Mg, Zn, or combinations thereof;M″ is Sc, Y, La, Lu, Al, Ga, In, or combinations thereof;0≦x≦1;0<y≦0.15; and0<z≦0.7.
  • 2. The phosphor as claimed in claim 1, being excited by light having a wavelength of 140 nm to 240 nm to emit an ultraviolet light having a major emission peak of 240 nm to 400 nm.
  • 3. The phosphor as claimed in claim 1, having the chemical formula: M3(M″1-y-zPryGdz)(PO4)2.
  • 4. The phosphor as claimed in claim 3, having the chemical formula: Li3(Y1-y-zPryGdz)(PO4)2, Na3(Y1-y-zPryGdz)(PO4)2, or K3(Y1-y-zPryGdz)(PO4)2.
  • 5. The phosphor as claimed in claim 3, having the chemical formula: K3(Y1-y-zPryGdz)(PO4)2, K3(Ga1-y-zPryGdz)(PO4)2, K3(In1-y-zPryGdz)(PO4)2, K3(La1-y-zPryGdz)(PO4)2, K3(Lu1-y-zPryGdz)(PO4)2, or K3(Sc1-y-zPryGdz)(PO4)2.
  • 6. The phosphor as claimed in claim 1, having the chemical formula: MM′(M″1-y-zPryGdz)(PO4)2.
  • 7. The phosphor as claimed in claim 6, having the chemical formula: KCa(Y1-y-zPryGdz)(PO4)2, KSr(Y1-y-zPryGdz)(PO4)2, KBa(Y1-y-zPryGdz)(PO4)2, KMg(Y1-y-zPryGdz)(PO4)2, or KZn(Y1-y-zPryGdz)(PO4)2.
  • 8. An ultraviolet light-emitting device, comprising: an excitation light source; andthe phosphor as claimed in claim 1,wherein the excitation light source emits light having a wavelength of 140 nm to 240 nm.
  • 9. The ultraviolet light-emitting device as claimed in claim 8, wherein the excitation light source comprises a Xe2* excimer lamp.
Priority Claims (1)
Number Date Country Kind
101139017 A Oct 2012 TW national
US Referenced Citations (51)
Number Name Date Kind
3417027 Wanmaker et al. Dec 1968 A
3542690 Borchardt Nov 1970 A
4222890 Takahara et al. Sep 1980 A
4764301 Awazu et al. Aug 1988 A
4931652 Nakamura Jun 1990 A
5154852 Chau Oct 1992 A
5156764 Kaneda et al. Oct 1992 A
5422040 Maofu et al. Jun 1995 A
5592052 Maya et al. Jan 1997 A
5738985 Miles et al. Apr 1998 A
5952253 Dejneka et al. Sep 1999 A
6156496 Miles et al. Dec 2000 A
6190780 Shoji et al. Feb 2001 B1
6579674 Miles et al. Jun 2003 B2
6613248 Setlur et al. Sep 2003 B2
6623961 Miles et al. Sep 2003 B2
6667152 Miles et al. Dec 2003 B2
6777179 Miles et al. Aug 2004 B2
6824976 Miles et al. Nov 2004 B1
6953952 Asakawa Oct 2005 B2
7138757 Tóth et al. Nov 2006 B2
7255812 McSweeney et al. Aug 2007 B2
7396491 Marking et al. Jul 2008 B2
7497974 Fan et al. Mar 2009 B2
7723740 Takashima et al. May 2010 B2
7854859 Kameshima et al. Dec 2010 B2
8158027 Chiu et al. Apr 2012 B2
20020177551 Terman Nov 2002 A1
20040053245 Tang et al. Mar 2004 A1
20040214783 Terman Oct 2004 A1
20050156496 Takashima et al. Jul 2005 A1
20050168125 Srivastava et al. Aug 2005 A1
20050277216 Asakawa Dec 2005 A1
20060243987 Lai Nov 2006 A1
20080149957 Kameshima et al. Jun 2008 A1
20080233034 Liu et al. Sep 2008 A1
20090020897 Winkler et al. Jan 2009 A1
20090021144 Chen et al. Jan 2009 A1
20090242839 Winkler et al. Oct 2009 A1
20090243467 Shimizu et al. Oct 2009 A1
20100061077 Winkler et al. Mar 2010 A1
20100181580 Masuda Jul 2010 A1
20100187976 Winkler Jul 2010 A1
20110186887 Trottier et al. Aug 2011 A1
20110215348 Trottier et al. Sep 2011 A1
20110304261 Winkler et al. Dec 2011 A1
20120057098 Lin et al. Mar 2012 A1
20120089180 Fathi et al. Apr 2012 A1
20120121656 Watson et al. May 2012 A1
20120140438 Winkler et al. Jun 2012 A1
20120162575 Lin et al. Jun 2012 A1
Foreign Referenced Citations (22)
Number Date Country
473094 Apr 1951 CA
504902 Aug 1954 CA
517680 Oct 1955 CA
561514 Aug 1958 CA
780307 Mar 1968 CA
830387 Dec 1969 CA
101054519 Oct 2007 CN
1 572 221 Mar 1970 DE
2005-220353 Aug 2005 JP
7003248 Sep 1970 NL
483875 Apr 2002 TW
M279023 Oct 2005 TW
200615653 May 2006 TW
200825155 Jun 2008 TW
200912475 Mar 2009 TW
200930793 Jul 2009 TW
I326704 Jul 2010 TW
201032355 Sep 2010 TW
201211632 Mar 2012 TW
I366594 Jun 2012 TW
201227072 Jul 2012 TW
WO 0001784 Jan 2000 WO
Non-Patent Literature Citations (10)
Entry
Hong et al., “Crystal Structure and Fluorescence Lifetime of Potassium Neodymium Orthophosphate, K3Nd(PO4)2, A New Laser Material”, Mat. Res. Bull. vol. 11, 1976, pp. 421-428.
Ju et al., “A reddish orange-emitting stoichiometric phosphor K3Eu(PO4)2 for white light-emitting diodes”, Optics & Laser Technology, 44, 2012, pp. 39-42.
Kharsika et al., “Luminescence of Eu3+-Activated Potassium Scandium and Potassium Yttrium Phosphate Vanadates”, Inorganic Materials, vol. 37, No. 8, 2001, pp. 831-835.
Mikhailik et al., “Efficient VUV sensitization of Eu3+ emission by Tb3+ in potassium rare-earth double phosphate”, Phys. Status Solidi RRL 3, No. 1, 2009, pp. 13-15.
Tie et al., “Investigation on the Luminescence of Ln3+(Ln=Eu, Gd, and Dy) in Hexagonal KCaR(PO4)2 Phosphates (R=Gd, Y)”, Phys. Stat. Sol. (a) 147, 1995, pp. 267-275.
Tie et al., “Structure and site-symmetry investigation on the hexagonal KCaY(PO4)2”, Journal of Alloys and Compounds, 227, 1995, pp. 1-4.
Wang et al., “Spectroscope properties of KCaY(PO4)2: Eu3+ in vacuum ultraviolet region”, Materials Science and Engineering B, 133, 2006, pp. 218-221.
Zhang et al., “Investigation on the luminescence of Re3+(RE=Ce, Tb, Eu and Tm) in KMGd(PO4)2(M=Ca, Sr) phosphates”, Optical Materials, 30, 2008, pp. 1848-1853.
Zhang et al., “Vacuum ultraviolet spectroscopic properties of rare earth (RE=Ce, Tb, Eu, Tm, Sm)-doped hexagonal KCaGd(PO4)2 phosphate”, Journal of Appliesd Physics, 102, 2007, 8 pages.
Zhang et al., “VUV-UV spectroscopic properties of RE(RE3+=Ce, Eu and Tb)-doped KMLn(PO4)2(M2+=Ca, Sr; Ln3+=Y, La, Lu)”, Optical Materials, 32, 2009, pp. 99-103.