Phosphor particle with antireflection coating

Information

  • Patent Grant
  • 5792509
  • Patent Number
    5,792,509
  • Date Filed
    Friday, February 7, 1997
    27 years ago
  • Date Issued
    Tuesday, August 11, 1998
    26 years ago
Abstract
Improved luminous efficiency in plasma displays has been achieved by coating phosphor particles with a dielectric layer having a refractive index, for the ultraviolet light emitted by the plasma, that is intermediate between that of the phosphor and vacuum. When deposited in a thickness range between 0.5 and 5 microns, the layer causes the particle's reflectivity to be reduced because of reduced reflection at the vacuum-coating interface as well as internal reflection at the coating-vacuum interface. For coating thicknesses in the range of 0.1 to 0.5 microns, reflectivity is reduced because of interference between rays reflected at the vacuum-coating interface and the coating-phosphor interface. Several methods for forming these antireflection coatings are described. These include CVD, PVD, and suspension in molten dielectric followed by decanting onto either sticky or non-stick surfaces.
Description

BACKGROUND OF THE INVENTION
1. Field of the Invention
The invention relates to the general field of photoluminescent coatings, particularly as used in plasma displays.
2. Description of the Prior Art
In plasma displays, most of the light that is generated by the gas discharge of the display is in the ultraviolet (UV) region. Some of this is converted to visible light through use of a photoluminiscent coating on the inside surface of the viewing screen. In the conventional arrangements associated with the prior art, much of the ultraviolet radiation that strikes the photoluminescent phosphor particles is reflected from their surfaces and is then lost to the display. Thus, the luminous efficiency of current plasma displays is typically between about 0.3 and 3.5%.
FIG. 1 illustrates this problem of undesired UV reflection. Phosphor particles, such as 1, form a layer on the inside surface of viewing screen 2. A ray of UV light 4 from gas plasma 3 strikes phosphor particle 5. Some of the UV is reflected as ray 6 while the rest penetrates the phosphor where photoluminescence occurs and visible light rays 7 are emitted. Clearly, if ways can be found to reduce the reflectivity of the phosphor particles �at the wavelengths concerned, greater luminous efficiency of the display will result.
The present invention teaches use of a suitable dielectric coating on each of the phosphor particles as a way to reduce phosphor reflectivity in the UV. Although we have not found any prior art that describes this approach to the problem, there is mention in the prior art of coating phosphor particles:
Budd (U.S. Pat. No. 5,418,062 May 1995) coats electroluminescent phosphor particles with a view to protecting them against moisture during subsequent use. Possible effects on the reflectivity of the particles are not discussed since reflectivity of the particles is unimportant in electroluminescence. Budd uses Chemical Vapor Deposition (in a temperature range between 25.degree. and 170.degree. C.) as the preferred method for coating the particles with an oxide layer between about 0.1 and 3 microns thick. There is no attempt made to control the thickness of the coating. In an attempt to coat the particles uniformly, particles are subjected to continuous agitation, using a fluidized bed, during CVD.
Okada et al. (U.S. Pat. No. 5,433,888 Jul 1995) coat phosphor particles primarily for adhesive purposes. As an additional benefit, the adhesive layer is a water soluble rare earth compound that leads to improved luminous flux conditions. Their coatings are formed by suspending their phosphor particles in an aqueous solution, applying this solution to a surface, and then baking to dryness.
Dutta et al. (U.S. Pat. No. 5,441,774 Aug 1995) use a liquid polymer as a vehicle for conveying phosphor particles onto a surface. The polymer is subsequently removed by heating it above its decomposition temperature. No coating remains on the phosphor particles but they end up with good adhesion to the surface.
SUMMARY OF THE INVENTION
It has been an object of the present invention to provide a plasma display and fluorescent lamp that have improved luminous efficiency over the current art.
Another object has been to reduce the amount of ultraviolet light, generated within a plasma display, that is lost through reflection at the surfaces of the phosphor particles.
A still further object of the invention has been to provide methods for coating phosphor particles with an effective antireflective coating.
These objects have been achieved by coating phosphor particles with a dielectric layer having a refractive index, at the wavelength concerned, that is intermediate between that of the phosphor and vacuum. When deposited in a thickness range between 0.5 and 5 microns, the layer causes the particle's reflectivity to be reduced because of reduced reflection at the vacuum-coating interface as well as internal reflection at the coating-vacuum interface. For coating thicknesses in the range of 0.1 to 0.5 microns, reflectivity is reduced because of interference between rays reflected at the vacuum-coating interface and the coating-phosphor interface. Several methods for forming these antireflection coatings are described. These include CVD, PVD, and suspension in molten dielectric followed by decanting onto either sticky or non-stick surfaces.





BRIEF DESCRIPTION OF THE DRAWINGS
FIG. 1 shows how ultraviolet light from a plasma can be reflected off the surface of phosphor particles so that only a fraction of it is available for photoluminescence.
FIGS. 2a and 2b illustrate how a relatively thick or a relatively thin coating of a dielectric on a phosphor particle can reduce its reflectivity.
FIG. 3 is a curve of refractive index vs. wavelength including regions of anomalous dispersion in both the UV and IR.
FIGS. 4 through 6 are steps in a method for coating phosphor particles with a layer of dielectric.





DESCRIPTION OF THE PREFERRED EMBODIMENTS
When light emerging from air or vacuum strikes the surface of a material at normal incidence and said material has a refractive index of n, the reflectivity R.sub.u (the u denoting that the surface is uncoated) is given by: ##EQU1##
If the wavelength of the light is close to an absorption edge, the refractive index can be very high. This is illustrated in FIG. 3 below. Curve 32 shows how refractive index gradually increases with decreasing wavelength (normal dispersion). Curve 31 illustrates the abrupt rise and subsequent abrupt fall of the refractive index in the vicinity of an absorption edge (anomalous dispersion). Thus, for example, for UV having a wavelength of about 2,000 Angstroms the refractive index of europium doped yttrium oxide is greater than 5, leading to a value of R.sub.u greater than 0.5. As already discussed relative to FIG. 1, such a high reflectivity can lead to a substantial reduction in luminous efficiency.
Consider now FIG. 2a which shows phosphor particle 21, having refractive index n.sub.p, coated with relatively thick dielectric layer 20 having refractive index n.sub.c. Arriving UV ray 24 strikes the outer surface of coating 20 and is partially reflected as ray 26, the remaining light going on to the coating-phosphor interface where it is once again partially reflected as ray 22, the unreflected component entering the phosphor where photoluminescence occurs. Ray 22 is itself partially internally reflected at the coating-vacuum interface emerging as attenuated ray 27. By definition, layer 20 is thick enough so that any coherence between rays 26 and 27 has been lost and interference between them is not a factor in determining the reflectivity.
Thus, the reflectivity R.sub.c of coated particle 21 is the sum of the reflectivities at the vacuum-coating and the coating-phosphor interfaces less the amount returned to the interior by internal reflection at the coating-vacuum interface: ##EQU2##
For example, for a UV wavelength of 1,470 Angstroms, for n.sub.c =2.75 and n.sub.p =6.75, we would reduce the reflectivity from 0.55 to 0.35 (at normal incidence).
In FIG. 2b we consider the case of a relatively thin antireflective coating. Phosphor particle 11 has been coated with dielectric layer 10. UV ray 14 striking the particle is reflected at both the vacuum-coating and coating-phosphor interfaces. By definition, layer 10 is thin enough so these two reflected rays are coherent and interference between them will occur. If the interference is fully destructive all of ray 14 enters the particle as ray 15 and the reflected ray 17 is eliminated.
The conditions for complete interference (zero reflectance) at normal incidence are:
(n.sub.c).sup.2 =n.sub.p and T.sub.c =w/4n.sub.c
where T.sub.c is coating thickness and w is wavelength.
Thus, unlike the thick coating case illustrated in FIG. 2a, control of coating thickness is important for the thin coating case. For example, for a UV wavelength of 1,470 Angstroms, n.sub.c =2.75 and n.sub.p =6.75, a thickness of 1336 Angstroms would be needed to achieve zero reflectivity (at normal incidence).
In the following examples we will discuss several different methods to effectively coat the phosphor particles, including comments on the degree of thickness control associated with each method.
Embodiment No. 1
Referring now to FIG. 4, the method of this embodiment begins with forming a suspension the phosphor particles, such as 41, in molten dielectric 43, contained in crucible 44. The level of liquid is chosen so that a small number of the particles, such as 42, lie above liquid surface 45. For phosphors such as europium doped yttrium oxide or manganese doped zinc silicate or europium doped barium magnesium aluminum oxide, suitable dielectrics would include silicon oxide, indium phosphide, lead fluoride, sodium fluoride, potassium chloride, indium arsenide, indium antimonide, gallium phosphide, calcium fluoride, barium fluoride, and glass and the temperature of the molten dielectric would be in the range of from about 600.degree. to 1,500.degree. C.
Referring to FIG. 5, the molten dielectric 53 is poured onto substrate 51, chosen so that it is wetted by 53. Examples of suitable substrate materials include silica and alumina. Thus a layer, between about 1 and 5 microns thick, of dielectric in which phosphor particles, such as 41, are trapped in suspension is formed on substrate 51. This layer is allowed to cool in place and can then be used directly as a photoluminescent layer for the plasma display.
For this embodiment, the effective thickness of the dielectric coating around each phosphor particle will vary over a wide range (between about 1 and 5 microns) and no attempt is made to control it precisely. However, by keeping the liquid level slightly below the minimum needed to cover all the particles, some particles, such as 42, remain behind in crucible 44. This eliminates the possibility of a non-functional layer of clear dielectric being formed above the phosphor particles.
Embodiment No. 2
As with embodiment no. 1, the method of this embodiment begins with forming a suspension of the phosphor particles, such as 41, in molten dielectric 43, contained in crucible 44 (as seen in FIG. 4) except that the level of liquid is such that all the particles will now be covered. For phosphors such as europium doped yttrium oxide or manganese doped zinc silicate or europium doped barium magnesium aluminum oxide, suitable dielectrics would include silicon oxide, indium phosphide, lead fluoride, sodium fluoride, potassium chloride, indium arsenide, indium antimonide, gallium phosphide, calcium fluoride, barium fluoride, and glass and the temperature of the molten dielectric would be in the range of from about 600.degree. to 1,500.degree. C.
Referring to FIG. 6, the molten dielectric 63 is poured onto substrate 61, chosen so that it is not wetted by 63. Examples of suitable substrate materials include silica and alumina. Since wetting does not occur, most of liquid 63 runs off, leaving behind the phosphor particles, such as 41, each with layer 60 of the dielectric on its surface. The final step in the method of this embodiment is allowing the substrate and coated particles to cool to room temperature.
For this embodiment, the effective thickness of the dielectric coating around each phosphor particle will vary to some extent, typically in the range of from about 1 to about 5 microns, and no attempt is made to control it precisely.
Embodiment No. 3
In this embodiment, the phosphor particles are coated by means of Chemical Vapor Deposition (CVD). Conventional means for performing CVD are provided, including a reaction chamber and the appropriate reactant materials that, when combined and heated, will deposit a layer of the desired dielectric material (such as barium fluoride or magnesium fluoride etc.) on all exposed surfaces, including phosphor particles such as europium doped yttrium oxide, manganese doped zinc silicate, or europium doped barium magnesium aluminum oxide. Once the particles have been placed inside the reaction chamber the deposition process is initiated. Throughout deposition the phosphor particles are continuously tumbled to ensure that the coating that each particle receives is uniform and of a controllable thickness. Once a layer of dielectric of the desired thickness has been deposited on the particles, the reaction is terminated.
Thickness control when using embodiment 3 can be quite precise and coatings of thickness ranging from about 0.1 to 1 micron can be formed.
Embodiment No. 4
In this embodiment, the phosphor particles are coated by means of vacuum evaporation, which is one form of Physical Vapor Deposition (PVD). Conventional means for performing vacuum evaporation are provided, including a vacuum chamber and a source in which the desired dielectric material (such as magnesium oxide or magnesium fluoride etc.) gets heated and from which it evaporates onto all surfaces in the line of sight, including phosphor particles such as europium doped yttrium oxide, manganese doped zinc silicate, or europium doped barium magnesium aluminum oxide. After the particles have been placed inside the vacuum chamber the deposition process is initiated. Throughout deposition the phosphor particles are continuously tumbled to ensure that the coating that each particle receives is uniform and of a controllable thickness. Once a layer of dielectric of the desired thickness has been deposited on the particles, the process is terminated.
Thickness control when using embodiment 4 can be very precise and coatings of thickness ranging from about 0.1 to 1 micron can be formed.
Embodiment No. 5
In this embodiment, the phosphor particles are coated by means of sputtering which is another form of PVD. Conventional means for performing the sputtering, which may be reactive sputtering or RF sputtering (or even a combination), are provided, including a vacuum chamber, a controlled source of low pressure gas, such as argon, and a suitable target from which the desired dielectric material (such as magnesium oxide or magnesium fluoride etc.) can be sputtered. Sputtered material deposits onto all surfaces in the approximate line of sight of the target, including phosphor particles such as europium doped yttrium oxide, manganese doped zinc silicate, or europium doped barium magnesium aluminum oxide. After the particles have been placed inside the vacuum chamber the deposition process is initiated. Throughout deposition the phosphor particles are continuously tumbled to ensure that the coating that each particle receives is uniform and of a controllable thickness. Once a layer of dielectric of the desired thickness has been deposited on the particles, the process is terminated.
Thickness control when using embodiment 5 can be very precise and coatings of thickness ranging from about 0.1 to 1 micron can be formed.
While the invention has been particularly shown and described with reference to the preferred embodiments thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of the invention.
Claims
  • 1. A method for improving the luminous efficiency of a plasma display comprising:
  • providing a viewing screen that has an inside and an outside surface;
  • providing phosphor particles that photoluminesce in ultraviolet light;
  • covering each of said phosphor particles with an antireflective coating having a thickness between about 0.1 and 5 microns and a refractive index between ahout 2 and 4; and
  • depositing said coated particles on said inside surface to form a photoluminescent screen.
  • 2. The method of claim 1 wherein the phosphor particles are taken from the group consisting of europium doped yttrium oxide, manganese doped zinc silicate, and europium doped barium magnesium aluminum oxide.
  • 3. The method of claim 1 wherein the antireflective coating is taken from the group consisting of indium phosphide, lead fluoride, sodium fluoride, potassium chloride, indium arsenide, indium antimonide, gallium phosphide, calcium fluoride, barium fluoride, and glass.
  • 4. A method for coating phosphor particles, comprising:
  • suspending the particles in a molten dielectric;
  • pouring the molten dielectric and particles onto a substrate that is wetted by the molten dielectric, thereby forming, on the substrate, a layer, having a thickness, of phosphor particles suspended in dielectric; and
  • allowing the layer to cool to room temperature.
  • 5. The method of claim 4 wherein the substrate is taken from the group consisting of silica and alumina.
  • 6. The method of claim 4 wherein the phosphor particles are taken from the group consisting of europium doped yttrium oxide, manganese doped zinc silicate, and europium doped barium magnesium aluminum oxide.
  • 7. The method of claim 4 wherein the dielectric is taken from the group consisting of silicon oxide, indium phosphide, lead fluoride, sodium fluoride, potassium chloride, indium arsenide, indium antimonide, gallium phosphide, calcium fluoride, barium fluoride, and glass.
  • 8. The method of claim 4 wherein the temperature of the molten dielectric is between about 600.degree. and 1,500.degree. C.
  • 9. The method of claim 4 wherein the thickness of the layer of phosphor particles suspended in dielectric is between about 1 and 5 microns.
  • 10. A method for coating phosphor particles, comprising:
  • suspending the particles in a molten dielectric;
  • pouring the molten dielectric and particles onto a substrate that is not wetted by the molten dielectric;
  • allowing the molten dielectric to run off the substrate, while leaving behind phosphor particles coated, to some thickness, with a layer of the dielectric; and
  • allowing the coated particles to cool to room temperature.
  • 11. The method of claim 10 wherein the substrate is taken from the group consisting of silica and alumina.
  • 12. The method of claim 10 wherein the phosphor particles are taken from the group consisting of europium doped yttrium oxide, manganese doped zinc silicate, and europium doped barium magnesium aluminum oxide.
  • 13. The method of claim 10 wherein the dielectric is taken from the group consisting of silicon oxide, indium phosphide, lead fluoride, sodium fluoride, potassium chloride, indium arsenide, indium antimonide, gallium phosphide, calcium fluoride, barium fluoride, and glass.
  • 14. The method of claim 10 wherein the temperature of the molten dielectric is between about 600.degree. and 1,500.degree. C.
US Referenced Citations (6)
Number Name Date Kind
3926763 Reisman Dec 1975
5051277 Sigai Sep 1991
5418062 Budd May 1995
5433888 Okada et al. Jul 1995
5441774 Dutta et al. Aug 1995
5624705 Stutzmann et al. Apr 1997