Phosphor

Abstract

A phosphor is disclosed. In an embodiment the phosphor includes an inorganic compound having at least one activator E and N and/or O in its empirical formula, wherein E is selected from the group consisting of Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof, and wherein the inorganic compound crystallizes in a crystal structure with the same atomic sequence as in K2Zn6O7.

Description

TECHNICAL FIELD

The invention relates to a phosphor, a method for producing a phosphor, use of a phosphor in a conversion element and use of a phosphor for the conversion of light.

BACKGROUND

For devices which are based on white light-emitting diodes (LEDs), particularly for backlighting, there are only a few solid phosphors which meet the requirements of an LED phosphor, in particular with emission in the dark red region of the electromagnetic spectrum. Hitherto, use has mainly been made of two orange to red-emitting phosphors of the formula (Sr, Ba)₂Si₅N₈:Eu²⁺ and (Sr,Ca)AlSiN₃:Eu²⁺. However, these have significant disadvantages with regard to emission, coverage of the color space, half-value width (FWHM=Full Width Half Maximum) and spectral filtering. In the case of the phosphor (Sr,Ba)₂Si₅N₈:Eu, the emission wavelength may be shifted from the orange into the red region of the spectrum by replacing barium with strontium. However, this replacement results in a reduction in the long-term stability of the phosphor. (Sr,Ba)₂Si₅N₈:Eu²⁺ phosphors additionally exhibit large half-value widths and do not exhibit any emission in the dark red region of the spectrum, i.e., no emission at a dominant wavelength of over 620 nm. Although the phosphor (Sr,Ca)AlSiN₃:Eu²⁺ already exhibits emission in the dark red region of the spectrum, it exhibits very broad emission, which extends into the non-visible region of the electromagnetic spectrum, whereby the luminescence efficiency of this phosphor is reduced. There is therefore considerable demand for a phosphor which exhibits emission in the dark red region of the electromagnetic spectrum and a small half-value width and thereby little emission outside the visible region of the electromagnetic spectrum.

WO 2013/175336 A1 and Nature Materials 2014, P. Pust et al., “Narrow-band red emitting Sr[LiAl₃N₄]:Eu²⁺ as a next-generation LED-phosphor material” disclose a phosphor of the formula SrLiAl₃N₄:Eu²⁺ which already has an emission in the dark red region of the electromagnetic spectrum and a small half-value width, said phosphor additionally exhibiting little emission outside the visible region of the electromagnetic spectrum. However, the phosphor has a lower quantum efficiency, i.e., a poor ratio between the number of emitted and absorbed photons, compared with (Sr,Ba)₂Si₅N₈:Eu²⁺ and (Sr,Ca)AlSiN₃:Eu^2+.

SUMMARY OF THE INVENTION

Embodiments provide a phosphor which has less emission outside the visible region of the electromagnetic spectrum, exhibits a small half-value width and additionally has high quantum efficiency. Further embodiments provide an efficient method for producing a phosphor, use of a phosphor in a conversion element and use of a phosphor for the conversion of light.

A phosphor is provided.

According to at least one embodiment, the phosphor comprises an inorganic compound, which comprises at least one activator E and N and/or O in its empirical formula. The activator E is here from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof. In particular, the activator E is responsible for the wavelength of the emitted radiation of the phosphor. Preferably, E is equal to Eu in combination with one, two or more further elements E, preferably selected from Mn or Li. Very particularly preferably, E=Eu, preferably Eu²+.

According to at least one embodiment, the phosphor consists of the inorganic compound. The phosphor then comprises at least one activator E and N and/or O in its empirical formula, wherein E is selected from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof.

According to one embodiment, the phosphor may comprise different phases, inter alia the inorganic compound, or it may consist of one or more further phases and the inorganic compound.

According to at least one embodiment, the inorganic compound crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇. The fact that the inorganic compound crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇ means here and hereinafter that the sequence of atoms of the inorganic compound follows the same pattern as the sequence of atoms in K₂Zn₆O₇. In other words, the crystal structure has the same structural motifs as K₂Zn₆O₇. If, for example, the inorganic compound or the phosphor follows the empirical formula (Sr,Eu)₂(Li_0.5Al_5.5)N₇, Sr and Eu occupy the sites of K, Li and Al occupy the sites of Zn and N occupies the sites of O in K₂Zn₆O₇.

According to at least one embodiment, the inorganic compound or the phosphor is described in the orthorhombic space group space group Pnnm. In the orthorhombic description with the space group Pnnm, lattice parameter c is in particular in the range from 3.21-3.29 Å, lattice parameter a in the range from 10.24-10.43 Å and lattice parameter b in the range from 10.29-10.43 Å. Particularly preferably, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(₇) Å and c=_3.2349(2) and α=β=γ=90°. Alternatively, the crystal structure may also be described in a tetragonal crystal system due to twinning and pseudosymmetry. Descriptions in other space groups are also possible.

According to at least one embodiment, the inorganic compound comprises one of the following general empirical formulae: (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y):E or (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y), wherein AX is selected from a group of monovalent metals, AY is selected from a group of divalent metals, AZ is selected from a group of trivalent metals, BV is selected from a group of monovalent metals, BW is selected from a group of divalent metals, BX is selected from a group of trivalent elements, BY is selected from a group of tetravalent elements, BZ is selected from a group of pentavalent elements, CX is selected from a group which comprises O, S, C, F, Cl, Br, I and combinations thereof, CY=N, E is selected from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof, wherein: 1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, 3<a+b+c<5, 10<d+e+f+g+h<14, 12<n+y<16 and −0.5≤z≤0.5.

Providing the conditions 1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, 3<a+b+c<5, 10<d+e+f+g+h<14, 12<n+y<16 and −0.5≤z≤0.5 are met, it is possible for individual parameters a, b, c, d, e, f, g, h, n or y to assume the value zero. In other words, not all the elements AX, AY, AZ, BV, BW, BX, BY, BZ, CX and CY are necessarily contained in the inorganic compound.

According to at least one embodiment, the inorganic compound comprises one of the following general empirical formulae: (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y):E or (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y), wherein AX is selected from a group comprising Li, Na, K, Rb, Cs and combinations thereof, AY is selected from a group comprising Mg, Ca, Sr, Ba, Eu, Yb, Mn, Ni and combinations thereof, AZ is selected from a group comprising Sc, Y, La, Pr, Ce, Yb, Cr and combinations thereof, BV=Li, BW is selected from a group comprising Mg, Zn, Mn, Ni and combinations thereof, BX is selected from a group comprising B, Al, Ga, Ce, Cr and combinations thereof, BY is selected from a group comprising Si, Ge, Mn and combinations thereof, BZ=P, CX is selected from a group comprising O, S, C, F, Cl, Br, I and combinations thereof, CX preferably being selected from a group comprising O, S and combinations thereof, CY=N and E is selected from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof. In this case the following apply:

1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, 3<a+b+c<5, 10<d+e+f+g+h<14, 12<n+y<16

and

−0.5≤z≤0.5.

According to at least one embodiment, the inorganic compound comprises the following general empirical formulae: (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y):E, wherein AX is selected from a group comprising Li, Na, K and combinations thereof, AY is selected from a group comprising Mg, Ca, Sr and Ba, AZ is selected from a group comprising Sc, Y, La, Pr, Ce, Yb and combinations thereof, BV=Li, BW is selected from a group comprising Mg, Zn and combinations thereof, BX is selected from a group comprising B, Al, Ga and combinations thereof, BY is selected from a group comprising Si, Ge, Mn and combinations thereof, CX is selected from a group comprising O, S and combinations thereof, CY=N and E is selected from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof, and wherein h=0.

According to a preferred embodiment, the following applies:

1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, a+b+c=4, d+e+f+g+h=12, n+y=14,

and

−0.1≤z≤0.1.

According to at least one embodiment, z=0. This embodiment thus relates to an electroneutral inorganic compound or an electroneutral phosphor. The phosphor is thus very stable and may be used for the most varied of applications. The phosphor is in particular suitable for application in a light-emitting diode, since it exhibits stable and uniform emission over the service life of the light-emitting diode.

According to at least one embodiment, the inorganic compound or the phosphor comprises one of the following empirical formulae: M₄Li_1+y′/2Al_11−y′/2N_14−y′O_y′:E, M₄Li_1−z′Al_11−z′Zn_2z′N₁₄:E, M₄Li₁Al_11−y″Mg_y″N_14−y″O_y″:E, M₄Li_1+Z″Al_11−3z″Si_2z″N₁₄:E or M₄Li₁Al_11−2x″Si_x″Mg_x″N₁₄:E.

In this case the following apply: M=Ca, Sr and/or Ba, 0≤y′≤14, 0≤z′≤1, 0≤x′≤11, 0≤y″≤11, 0≤z″≤3 and 0≤x″≤5. E in particular replaces M in the empirical formula and occupies the lattice sites of M.

According to at least one embodiment, M contains at least Sr, for example, Sr and Ba or Sr and Ca. Very particularly preferably, M=Sr.

According to at least one embodiment, the inorganic compound or the phosphor comprises one of the following empirical formulae: M_4−xEu_xLi_1+y′/2Al_11−y′/2N_14−y′O_y′, M_4−xEu_xLi_1−z′Al_11−z′Zn_2z′N₁₄, M_4−x Eu_xLi₁Al_11−x′Zn_x′N_14−x′O_x′, M_4−xEu_xLi₁Al_11−y″Mg_y″N_14−y″O_y″, M_4−xEu_xLi_1+z″Al_11−3z″Si_2z″N₁₄ or M_4+xEu_xLi₁Al_11−2x″Si_x″Mg_x″N₁₄.

In this case the following apply: M=Ca, Sr and/or Ba, and 0≤y′≤14, 0≤z′≤1, 0≤x′≤11, 0≤y″≤11, 0≤z″≤3, 0≤x″≤5 and 0<x≤2.

The following preferably applies: 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2. Eu or Eu²⁺ ions in this case in particular replace M and occupy the lattice sites of M.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi_1+y′/2Al_11−y′/2N_14−y′O_y′, preferably Sr_4−xEu_xLi_1+y′/2Al_11−y′/2N_14−y′O_y′, wherein y′=0, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10, 11, 12, 13 or 14 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁N₁₄, in this embodiment AlN₂ may be replaced in part by LiO₂. Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor shifts. In particular, the peak wavelength is shifted to shorter wavelengths. The result is the following empirical formulae: M_4−xEu_xLiAl₁₁N₁₄, (M_4−xEu_x)₂Li₃Al₂₁n₂₆O₂, (M_4−xEu_x)_0.5LiAl₅N₆O, (M_4−xEu_x)₂Li₅Al₁₉N₂₂O₆, M_4−xEu_xLi₃Al₉N₁₀O₄, (M_4−xEu_x)₂Li₇Al₁₇N₁₈O₁₀, (M_4−xEu_x)_0.5Li₂Al₄N₄O₃, (M_4−xEu_x)₂Li₉Al₁₅N₁₄O₁₄, M_4−xEu_xLi₅Al₇N₆O₈, (M_4−xEu_x)₂Li₁₁Al₁₃N₁₀O₁₈, (M_4−xEu_x)_0.5Li₃Al₃N₂O₅, (M_4−xEu_x)₂Li₁₃Al₁₁N₆O₂₂, M_4−xEu_xLi₇Al₅N₂O₁₂, (M_4−xEu_x)₂Li₁₅Al₉N₂O₂₆, or (M_4−xEu_x)_0.5Li₄Al₂O₇, and/or Sr_4−xEu_xLiAl₁₁N₁₄, (Sr_4−xEu_x)₂Li₃Al₂₁N₂₆O₂, (Sr_4−xEu_x)_0.5LiAl₅N₆O, (Sr_4−xEu_x)₂Li₅Al₁₉N₂₂O₆, Sr_4−xEu_xLi₃Al₉N₁₀O₄, (Sr_4−xEu_x)₂Li₇Al₁₇N₁₈O₁₀, (Sr_4−xEu_x)_0.5Li₂Al₄N₄O₃, (Sr_4−xEu_x)₂Li₉Al₁₅N₁₄O₁₄, Sr_4−xEu_xLi₅Al₇N₆O₈, (Sr_4−xEu_x)₂Li₁₁Al₁₃N₁₀O₁₈, (Sr_4−xEu_x)_0.5Li₃Al₃N₂O₅, (Sr_4−xEu_x)₂Li₁₃Al₁₁N₆O₂₂, Sr_4−xEu_xLi₇Al₅N₂O₁₂, (Sr_4−xEu_x)₂Li₁₅Al₉N₂O₂₆ or (Sr_4−xEu_x)_0.5Li₄Al₂O₇.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi_1−z′Al_11−z′Zn_2z′N₁₄, preferably Sr_4−xEu_xLi_1−z′Al_11−z′Zn_2z′N₁₄, wherein z′=0 or 1 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁N₁₄, in this embodiment LiAl may be replaced in part by Zn₂. Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor may shift. The result is the following empirical formulae: M_4−xEu_xLiAl₁₁N₁₄ or M_4−xEu_xAl₁₀Zn₂N₁₄ and/or Sr_4−xEu_xLi₁₁N₁₄ or Sr_4−xEu_xAl₁₀Zn₂N₁₄.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi₁Al_11−x′Zn_x′N_14−x′O_x′, preferably Sr_4−xEu_xLi₁Al_11−x′Zn_x′N_14−x′O_x′, wherein x′=0, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁N₁₄, in this embodiment AIN may be replaced in part by ZnO.

Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor shifts. In particular, the peak wavelength is shifted to shorter wavelengths. The result is the following empirical formulae: M_4−xEu_xLiAl₁₁N₁₄, M_4−xEu_xLiAl₁₀Zn₁N₁₃O, M_4−xEu_xLiAl₉Zn₂N₁₂O₂, M_4−xEu_xLiAl₈Zn₃N₁₁O₃, M_4−xEu_xLiAl₇Zn₄N₁₀O₄, M_4−xEu_xLiAl₆Zn₅N₉O₅, M_4−xEu_xLiAl₅Zn₆N₈O₆, M_4−xEu_xLiAl₄Zn₇N₇O₇, M_4−xEu_xLiAl₃Zn₈N₆O₈, M_4−xEu_xLiAl₂Zn₉N₅O₉, M_4−xEu_xLiAlZn₁₀₂N₄O₁₀, M_4−xEu_xLiZn₁₁N₃O₁₁ or rather Sr_4−xEu_xLiAl₁₁N₁₄, Sr_4−xEu_xLiAl₁₀Zn₁N₁₃, Sr_4−xEu_xLiAl₉Zn₂N₁₂O₂, Sr_4−xEu_xLiAl₈Zn₃N₁₁O₃, Sr_4−xEu_xLiAl₇Zn₄N₁₀O₄ , Sr_4−xEu_xLiAl₆Zn₅N₉O₅, Sr_4−xEu_xLiAl₅Zn₆N₈O₆, Sr_4−xEu_xLiAl₄Zn₇N₇O₇, Sr_4−xEu_xLiAl₃Zn₈N₆O₈, Sr_4−xEu_xLiAl₂Zn₉N₅O₉, Sr_4−xEu_xLiAlZn₁₀N₄O₁₀, Sr_4−xEu_xLiZn₁₁₅N₃O₁₁.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi₁Al_11−y″Mg_y″N_14−y″O_y″, preferably Sr_4−xEu_xLi₁Al_11−y″Mg_y″N_14−y″O_y″, wherein y″=0, 1, 2, 3, 4, 5, 6, 7, 8, 9, 10 or 11 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁N₁₄, in this embodiment AIN may be replaced in part by MgO. Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor shifts. In particular, the peak wavelength is shifted to shorter wavelengths. The result is the following empirical formulae: M_4−xEu_xLiAl₁₁N₁₄, M_4−xEu_xLiAl₁₀Mg₁N₁₃O, M_4−xEu_xLiAl₉Mg₂N₁₂O₂, M_4−xEu_xLiAl₈Mg₃N₁₁O₃, M_4−xEu_xLiAl₇Mg₄N₁₀O₄, M_4−xEu_xLiAl₆Mg₅N₉O₅, M_4−xEu_xLiAl₅Mg₆N₈O₆, M_4−xEu_xLiAl₄Mg₇N₇O₇, M_4−xEu_xLiAl₃Mg₈N₆O₈, M_4−xEu_xLiAl₂Mg₉N₅O₉, M_4−xEu_xLiAlMg₁₀N₄O₁₀, M_4−xEu_xLiMg₁₁N₃O₁₁ or rather Sr_4−xEu_xLiAl₁₁N₁₄, Sr_4−xEu_xLiAl₁₀Mg₁N₁₃O, Sr_4−xEu_xLiAl₉Mg₂N₁₂O₂, Sr_4−xEu_xLiAl₈Mg₃N₁₁O₃, Sr_4−xEu_xLiAl₇Mg₄N₁₀O₄, Sr_4−xEu_xLiAl₆Mg₅N₉O₅, Sr_4−xEu_xLiAl₅Mg₆N₈O₆, Sr_4−xEu_xLiAl₄Mg₇N₇O₇, Sr_4−xEu_xLiAl₃Mg₈N₆O₈, Sr_4−xEu_xLiAl₂Mg₉N₅O, Sr_4−xEu_xLiAlMg₁₀N₄O₁₀, Sr_4−xEu_xLiMg₁₁N₃O₁₁.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi_1+z″Al_11−3z″Si_2z″N₁₄, preferably Sr_4−xEu_xLi_1+z″Al_11−3z″Si_2z″N₁₄, wherein z″=0, 1, 2 or 3 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁Mg₁N₁₄, in this embodiment Al₃ may be replaced in part by Si₂Li. Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor may shift. The result is the following empirical formulae M_4−xEu_xLiAl₁₁N₁₄, M_4−xEu_xLi₂Al₈Si₂N₁₄, M_4−xEu_xLi₃Al₅Si₄N₁₄, M_4−xEu_xLi₄Al₂Si₆N₁₄ beziehungsweise Sr_4−xEu_xLiAl₁₁N₁₄, Sr_4−xEu_xLi₂Al₈Si₁N₁₄, Sr_4−xEu_xLi₃Al₅Si₄N₁₄, Sr_4−xEu_xLi₄Al₂Si₆N₁₄.

According to at least one embodiment, the inorganic compound or the phosphor has the empirical formula M_4−xEu_xLi₁Al_11−2x″Si_x″Mg_x″N₁₄, preferably Sr_4−xEu_xLi₁Al_11−2x″Si_X″Mg_xN₁₄, wherein x″=0,1, 2, 3, 4 or 5 and 0<x≤2. On the basis of the empirical formula M_4−xEu_xLiAl₁₁Mg₁N₁₄, in this embodiment Al₂ may be replaced in part by MgSi. Surprisingly, the crystal structure is retained, while the spectral position and thus the peak wavelength of the phosphor may shift. The result is the following empirical formulae: M_4−xEu_xLiAl₁₁N₁₄, M_4−xEu_xLiAl₉SiMgN₁₄, M_4−xEu_xLiAl₇Si₂Mg₂N₁₄, M_4−xEu_xLiAl₅Si₃Mg₃N₁₄, M_4−xEu_xLiAl₃Si₄Mg₄N₁₄, M_4−xEu_xLiAlSi₅Mg₅N₁₄ or rather Sr_4−xEu_xLiAl₁₁N₁₄, Sr_4−xEu_xLiAl₉SiMgN₁₄, Sr_4−xEu_xLiAl₇Si₂Mg₂N₁₄, Sr_4−xEu_xLiAl₅Si₃Mg₃N₁₄, Sr_4−xEu_xLiAl₃Si₄Mg₄N₁₄, Sr_4−xEu_xLiAlSi₅Mg₅N₁₄.

Interestingly, monocrystals from substitution experiments based on a phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄, in which, for example, AlN₂ is replaced in part by LiO₂, LiAl in part by Zn₂, AlN in part by ZnO, AlN in part by MgO, Al_a in part by Si₂Li or Al₂ in part by MgSi, display significant variations with regard to the lattice parameters in comparison with unsubstituted Sr_4−xEu_xLiAl₁₁N₁₄, wherein the crystal structure is retained. Lattice parameter c is here in the range from _3.21-3.29 Å, lattice parameter a in the range from 10.24-10.42 Å and lattice parameter b in the range from 10.29-10.43 Å. As a result of the substitutions, variation may also be observed with regard to emission wavelength. The maximum intensity of the emission, i.e., the peak wavelength, in this case varies between 594 nm and 670 nm for Sr₄LiAl₁₁N₁₄:Eu²⁺.

According to at least one embodiment, the inorganic compound or the phosphor has the following empirical formula: M_4−xEu_xLiAl₁₁N₁₄wherein M=Ca, Sr and/or Ba, and 0<x≤2. Preferably M=Sr or Sr and Ba or Sr and Ca. This embodiment relates to a nitridoaluminate phosphor.

In one embodiment, in the X-ray powder diffractogram using Cu—K_α1 radiation, the inorganic compound or the phosphor has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. The X-ray diffraction data were recorded by means of flat sample holders on a powder diffractometer (PANalytical Empyrean) with X-Celerator CCD detector in Bragg-Brentano geometry.

According to at least one embodiment, the phosphor has an emission maximum in the range from 500 to 680 nm, preferably between 594 nm and 680 nm. The emission maximum may also be known as peak wavelength.

In the present case, “peak wavelength” here means the wavelength of a peak at which the maximum intensity of the peak is located.

According to at least one embodiment, the phosphor has a dominant wavelength of λ>500 nm, preferably λ>600 nm, particularly preferably λ>620 nm. Dominant wavelength is one possible way of describing non-spectral (polychromatic) light mixtures in terms of spectral (monochromatic) light that evokes a similar perception of hue. In the CIE color space, the line which connects a point for a specific color and the points x=0.333, y=0.333 may be extrapolated in such a way that it meets the outline of the space at two points. The point of intersection lying closer to said color represents the dominant wavelength of the color as wavelength of the pure spectral color at this point of intersection. The dominant wavelength is thus the wavelength which is perceived by the human eye.

According to one embodiment, the phosphor comprises a red-emitting phosphor. The phosphor thus exhibits emission in the red region of the electromagnetic spectrum.

According to one embodiment, the red-emitting phosphor comprises a nitridoaluminate phosphor. In other words, the inorganic compound may be a nitridoaluminate phosphor. In particular, the nitridoaluminate phosphor is doped with Eu^2+.

“Red-emitting” is understood here and hereinafter to mean that the phosphor inter alia exhibits emission in the red region of the spectrum. For example, the peak wavelength or the dominant wavelength may lie in the green region of the spectrum, but the phosphor may also exhibit emission in the red region of the spectrum.

According to one embodiment, the phosphor or the red-emitting phosphor may comprise different phases, inter alia the Eu²⁺-doped nitridoaluminate phosphor, or it may consist of one or more further phases and the Eu²⁺-doped nitridoaluminate phosphor.

In one embodiment, the phosphor or the red-emitting phosphor consists of the Eu²⁺-doped nitridoaluminate phosphor. This means that the red-emitting phosphor consists of just one phase, namely the Eu²⁺-doped nitridoaluminate phosphor. The red-emitting phosphor may consist of the Eu²⁺-doped nitridoaluminate phosphor, which is present in just one crystal structure.

According to one embodiment, the Eu²⁺-doped nitridoaluminate phosphor crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇.

The crystal structure may in particular be described in the orthorhombic space group Pnnm. In the orthorhombic description with the space group Pnnm, lattice parameter c is in particular in the range from _3.21-3.29 Å, lattice parameter a in the range from 10.24-10.43 Å and lattice parameter b in the range from 10.29-10.43 Å. In particular, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(7) Å and c=_3.2349(2) and α=β=γ=90°. Alternatively, the crystal structure may also be described in a tetragonal crystal system due to twinning and pseudosymmetry. Descriptions in other space groups are also possible.

According to one embodiment, the Eu²⁺-doped nitridoaluminate phosphor or the inorganic compound has the empirical formula M_4−xEu_xLiAl₁₁N₁₄, wherein M=Ca, Sr and/or Ba, and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies. Eu²⁺ ions in this case in particular replace M and occupy the lattice sites of M. The Eu²⁺-doped nitridoaluminate phosphor with the empirical formula M_4−xEu_xLiAl₁₁N₁₄ preferably crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇.

It is possible for the phosphor or the inorganic compound to comprise further elements, for instance in the form of impurities, wherein these impurities taken together should preferably at most constitute a proportion by weight of the phosphor of at most 1 per mil or 100 ppm or 10 ppm (parts per million).

According to at least one embodiment, the Eu²⁺-doped nitridoaluminate phosphor or the inorganic compound has the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies.

According to at least one embodiment, the phosphor or the red-emitting phosphor consists of an Eu²⁺-doped nitridoaluminate phosphor of the empirical formula M_4−xEu_xLiAl₁₁N₁₄. The red-emitting phosphor thus comprises just one phase. It is, however, also possible for a further phase consisting of AlN to be present.

According to at least one embodiment, the phosphor or the red-emitting phosphor comprises different phases, in particular one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu²⁺ or the red-emitting phosphor consists of these phases and/or phosphors.

In one embodiment, in the X-ray powder diffractogram using Cu—K_α1 radiation, the phosphor or the red-emitting phosphor, in particular the Eu²⁺-doped nitridoaluminate phosphor, comprises two characteristic reflections in an angular range of 11.5-12.5° 2θ and an angular range of 18.5-19.5° 20. The X-ray diffraction data were recorded by means of flat sample holders on a powder diffractometer (PANalytical Empyrean) with X-Celerator CCD detector in Bragg-Brentano geometry. The known phosphor SrLiAl₃N₄:Eu²⁺ (WO 2013/175336 A1 and Nature Materials 2014, P. Pust et al., “Narrow-band red emitting Sr[LiAl₃N₄]:Eu²⁺ as a next-generation LED-phosphor material”) does not have these reflections.

Compared with the known phosphor of formula SrLiAl₃N₄:Eu²⁺, the red-emitting phosphor, in particular the Eu²⁺-doped nitridoaluminate phosphor, has a higher quantum efficiency. To measure quantum efficiency, i.e., the ratio between the number of emitted and absorbed photons, the red-emitting phosphor according to the invention and the known phosphor of formula SrLiAl₃N₄:Eu²⁺ were each pressed into powder tablets and the relative quantum efficiency compared with the standard phosphor YAG:Ce³⁺ (yttrium aluminum garnet doped with cerium) was determined under identical conditions on a Fluoromax spectrometer. The known phosphor was in this case produced under comparable conditions to the method indicated in Nature Materials 2014, P. Pust et al. The phosphors were characterized by a Rietveld analysis based on X-ray powder diffractograms. When measured relative to a standard phosphor YAG:Ce³⁺, the red-emitting phosphor according to the invention surprisingly has a 15% higher relative quantum efficiency compared with the known phosphor SrLiAl₃N₄:Eu^2+.

In one embodiment, the red-emitting phosphor has an emission maximum, i.e., a peak wavelength, in the range from 620 to 680 nm, preferably in the range from 640 and 680 nm, particularly preferably in the range from 660 to 680 nm. The emission thus lies in the dark red region of the spectrum of the electromagnetic spectrum. In particular, the phosphor according to this embodiment has the empirical formula M_4−xEu_xLiAl₁₁N₁₄, wherein M=Ca, Sr and/or Ba, and 0<x≤2 or comprises this compound as inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor.

In one embodiment, the red-emitting phosphor with a peak wavelength in the range from 620 to 680 nm has a half-value width (FWHM) of less than 90 nm, preferably less than 70 nm, particularly preferably less than 65 nm and particularly preferably less than 60 nm. Such a small half-value width enables the phosphor according to the invention to emit only or almost only radiation in the visible region of the electromagnetic spectrum, so meaning that no or only slight losses in efficiency arise through emission in the non-visible region of the electromagnetic spectrum. In comparison, the known phosphors (Sr,Ba)₂Si₅N₈:Eu²⁺ have a half-value width of greater than 90 nm, (Sr,Ca)AlSiN₃:Eu²⁺ a half-value width of greater than 70 nm and SrLiAl₃N₄:Eu²⁺ a half-value width of greater than or equal to 48 nm. Relative to the phosphor SrLiAl₃N₄:Eu²⁺, however, the phosphor according to the invention has a detectably higher quantum efficiency.

In one embodiment, the phosphor or the red-emitting phosphor emits no or only little radiation outside the visible region of the spectrum. Thus, all or virtually all the emitted photons lie within the sensitivity range of the human eye, which eliminates or minimizes the losses in efficiency through emission in the non-visible region of the electromagnetic spectrum. In this way, high luminescence efficiency is achieved.

In one embodiment, the phosphor or the red-emitting phosphor is produced from starting materials which comprise Li₃N, LiAlH₄, AlN, Sr₃N₂ and EuF₃ or Li₃N, LiAlH₄, AlN, Sr₃N₂, SrH₂ and EuF₃. The phosphor may also be produced to consist of these starting materials. It has surprisingly been found that the phosphor or red-emitting phosphor according to the invention may be produced with a high quantum efficiency from these starting materials. Experiments have shown that the presence of the starting materials Li₃N and LiAlH₄ are essential to the production of the phosphor according to the invention. If just one of these starting materials is used, the X-ray powder diffractogram does not exhibit the characteristic reflections in the angular range of 11.5-12.5° 2θ and in the angular range of 18.5-19.5° 2θ. In particular, the phosphor or the inorganic compound then does not have a crystal structure with the same atomic sequence as in K₂Zn₆O₇.

In one embodiment, the red-emitting phosphor has a dominant wavelength of λ>620 nm.

In one embodiment, the phosphor or the red-emitting phosphor is excitable by radiation in the UV region to the blue region of the electromagnetic spectrum. For example, the phosphor or the red-emitting phosphor is excitable by radiation with a wavelength of 240 nm to 500 nm, preferably 400 nm to 500 nm, for example, of 460 nm. Compared to the known phosphor SrLiAl₃N₄:Eu²⁺, the phosphor according to the invention or the red-emitting phosphor has a higher absorption in the range from 450 nm to 500 nm.

The stated embodiments of the phosphor or of the red-emitting phosphor may be produced according to the method stated below. All the features described for the phosphor thus also apply to the method for the production thereof and vice versa.

A method is provided for producing a phosphor.

According to at least one embodiment, the phosphor comprises an inorganic compound, which comprises at least one activator E and N and/or O in its empirical formula. The activator E is here from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof.

According to at least one embodiment, the phosphor is a red-emitting phosphor comprising an Eu²⁺-doped nitridoaluminate phosphor or consisting of an Eu²⁺-doped nitridoaluminate phosphor.

According to one embodiment, in the X-ray powder diffractogram using Cu—K_α1 radiation, the phosphor or the red-emitting phosphor has two characteristic reflections in the angular range from 11.5-12.5° 2θ and in the range from 18.5-19.5° 2θ.

According to one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇. The crystal structure may in particular be described in the orthorhombic space group Pnnm. In particular, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(7) Å and c=3.2349(2) and α=β=γ=90°. Alternatively, the crystal structure may be described in a tetragonal crystal system due to twinning and pseudosymmetry. Descriptions in other space groups are also possible.

According to one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula M_4−xEu_xLiAl₁₁N₁₄, wherein M=Ca, Sr and/or Ba, and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies. Eu²⁺ ions in this case in particular replace M and occupy the lattice sites of M. The Eu²⁺-doped nitridoaluminate phosphor with the empirical formula M_4−xEu_xLiAl₁₁N₁₄ preferably crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇.

According to at least one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and 0<x≤0.4, preferably 0.01≤x≤2, particularly preferably 0.01≤x≤0.2 applies.

According to at least one embodiment, the phosphor or the red-emitting phosphor consists of an Eu²⁺-doped nitridoaluminate phosphor of the empirical formula M_4−xEu_xLiAl₁₁N₁₄. The phosphor or the red-emitting phosphor thus comprises just one phase. It is, however, also possible for a further phase consisting of AlN to be present.

According to at least one embodiment, the phosphor or the red-emitting phosphor comprises different phases, in particular one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu²⁺ or the phosphor or the red-emitting phosphor consists of these phases and/or phosphors.

The method comprises the following method steps: A) mixing the starting materials comprising or consisting of Li₃N, LiAlH₄, M₃N₂, AlN and EuF₃ or comprising or consisting of Li₃N, LiAlH₄, M₃N₂, MH₂, AlN and EuF₃, wherein M=Sr, Ca and/or Ba, B) heating the mixture obtained in A) to a temperature T1 of between 900 and 1400° C., and C) annealing the mixture at a temperature T1 of 900 to 1400° C. for five minutes to six hours.

According to one embodiment, the method comprises the following method steps: A) mixing the starting materials comprising or consisting of Li₃N, LiAlH₄, Sr₃N₂, AlN and EuF₃ or comprising or consisting of Li₃N, LiAlH₄, Sr₃N₂, SrH₂, AlN and EuF₃, B) heating the mixture obtained in A) to a temperature T1 of between 900 and 1400° C., and C) annealing the mixture at a temperature T1 of 900 to 1400° C. for five minutes to six hours.

It has surprisingly been found that the phosphor or the red-emitting phosphor according to the invention may be produced from the starting materials Li₃N, LiAlH₄, Sr₃N₂, AlN and EuF₃ or Li₃N, LiAlH₄, Sr₃N₂, SrH₂, AlN and EuF₃. Experiments have shown that the presence of the starting materials Li₃N and LiAlH₄ is essential to the production of the phosphor or the red-emitting phosphor according to the invention. If just one of these starting materials is used, the X-ray powder diffractogram does not exhibit the characteristic reflections in the angular range of 11.5-12.5° 2θ and in the angular range of 18.5-19.5° 2θ. In other words, the phosphor according to the invention or the red-emitting phosphor according to the invention does not form if Li₃N and LiAlH₄ are not used as starting materials. The phosphor produced in this way surprisingly has a high quantum efficiency.

According to at least one embodiment, Li₂O, SiO₂, ZnO, MgO, Li₂CO₃, Si₃N₄ and/or Zn₃N₂ may be used as additional starting materials.

In one embodiment, the starting materials are present as a powder.

According to at least one embodiment, the method comprises the following method steps: A) mixing the starting materials comprising or consisting of Li₃N, LiAlH₄, M₃N₂, AlN and EuF₃ or comprising or consisting of Li₃N, LiAlH₄, M₃N₂, MH₂, AlN and EuF₃, wherein M=Sr, Ca and/or Ba, B) heating the mixture obtained in A) to a temperature T1 of between 1000 and 1400° C., and C) annealing the mixture at a temperature T1 of 1000° C. to 1400° C., preferably of 1300° C. to 1400° C., for example, at 1400° C. for five minutes to one hour, for example, 15 minutes. If, in particular, the starting materials consisting of Li₃N, LiAlH₄, M₃N₂, MH₂, AlN and EuF₃ are used, the inventors have surprisingly established that the phosphor or red-emitting phosphor formed predominantly comprises the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula M_4−xEu_xLiAl₁₁N₁₄ or consists of this phosphor. M=Sr is preferred.

In one embodiment, the molar ratio of LiAlH₄:Li₃N is between 5:1 and 1:1, preferably between 4:1 and 1:1, for example, is 1:1 or 3:1. In particular, this molar ratio is present if the red-emitting phosphor is produced from the starting material consisting of Li₃N, LiAlH₄, Sr₃N₂, AlN and EuF₃. In this case in particular, the phosphor or the red-emitting phosphor may form comprising one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu²⁺.

In one embodiment, T1 is between 1100 and 1300° C., for example, at 1250° C., and the annealing in method step C) proceeds for one hour to five hours.

In one embodiment, method step C) is followed by a further method step: D) cooling the mixture to a temperature T2, wherein room temperature<T2<T1 applies. Room temperature is understood to mean 20° C.

In one embodiment, method step D) is followed by a further method step: E) annealing the mixture at a temperature T2 of 800 to 1300° C. for five minutes to two hours. Annealing preferably proceeds for five minutes to 60 minutes, particularly preferably for 10 minutes to 30 minutes. In particular if the method steps D) and E) take place, the annealing in method step C) may proceed for five minutes to two hours, preferably for five minutes to 60 minutes, particularly preferably for 10 minutes to 30 minutes.

In one embodiment, T2 is between 800° C. and 1300° C., preferably between 900° C. and 1200° C., particularly preferably between 950° C. and 1100° C., for example, at 1000° C.

In one embodiment, T1=1250° C. and T2=1000° C. In this embodiment the annealing in method steps C) and E) may proceed in each case for 10 minutes to 30 minutes, for example, in each case for 15 minutes.

In one embodiment, method step C) or E) is followed by a further method step: F) cooling mixture to room temperature.

In one embodiment, cooling of the mixture to room temperature in method step F) proceeds at a cooling rate of 100 to 400° C. per hour, preferably 150 to 300° C. per hour, particularly preferably 220 to 270° C. per hour, for example, at a cooling rate of 250° C. per hour.

In one embodiment, cooling of the mixture to T2 in method step D) proceeds at a cooling rate of 100 to 400° C. per hour, preferably 100 to 300° C. per hour, particularly preferably 150 to 200° C. per hour, for example, at a cooling rate of 170° C. per hour.

In one embodiment, method steps B), C), D), E) and/or F) proceed under a forming gas atmosphere. The forming gas preferably has a nitrogen:hydrogen ratio of 92.5:7.5.

In one embodiment, method steps B), C), D), E) and/or F) take place in a tube furnace.

In one embodiment, the heating in method step B) proceeds at a heating rate of 100 to 400° C. per hour, particularly preferably of 150 to 300° C. per hour, particularly preferably of 200 to 250° C. per hour, for example, at a heating rate of 250° C. per hour.

In one embodiment, the starting materials are used in a molar ratio of AlN:Sr₃N₂:Li₃N:LiAlH₄:EuF₃=1:0.05-0.3:0.05-0.2:0.05-0.4:0.0001-0.009. The starting materials are preferably used in a molar ratio of AlN:Sr₃N₂:Li₃N:LiAlH₄:EuF₃=1:0.1-0.2:0.05-0.1:0.05-0.3:0.001-0.003, particularly preferably in a molar ratio of AlN: Sr₃N₂:Li₃N:LiAlH₄:EuF₃=1:0.1-0.15:0.06-0.1:0.08-0.2:0.001-0.002. Under these molar ratios in particular, the phosphor or the red-emitting phosphor may form comprising one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu^2+.

It has been found that by varying the temperature Ti, the temperature T2, the duration of method step C), the duration of method step E) and/or the molar ratios of the starting materials, it is possible to control the half-value width of the red-emitting phosphor; if in particular Li₃N, LiAlH₄, Sr₃N₂, AlN and EuF₃ are used as starting materials, the composition of the red-emitting phosphor may be varied by selecting the temperature and the duration of method step C).

It has furthermore been found that it is possible to influence the composition of the red-emitting phosphor by varying the temperature Ti, the duration of method step C), and/or the molar ratios of the starting materials or by selecting the starting materials. In particular, if the starting materials consisting of Li₃N, LiAlH₄, M₃N₂, MH₂, AlN and EuF₃ are used and in method step C) annealing of the mixture proceeds at a temperature T1 of 1000° C. to 1400° C., preferably of 1300° C. to 1400° C., for example, of 1400° C. for five minutes to one hour, the phosphor formed or the red-emitting phosphor predominantly comprises the Eu²⁺-doped nitridoaluminate phosphor of empirical formula M_4−xEu_xLiAl₁₁N₁₄ or consists of this phosphor.

The stated embodiments of the phosphor or the red-emitting phosphor may be used for the following stated uses. The features of the phosphor are also disclosed for the use thereof and vice versa.

Use of a phosphor for the conversion of light into longer-wave light is provided. This may be understood to mean that light is absorbed by the phosphor and emitted as light with a longer wavelength.

Use of a red-emitting phosphor for the conversion of light into longer-wave, red light is further provided. This may be understood to mean that light is absorbed by the red-emitting phosphor and emitted as light with a longer wavelength located in the red region of the spectrum.

According to one embodiment, use of a phosphor or of a red-emitting phosphor in a conversion element is provided.

According to at least one embodiment, the phosphor comprises an inorganic compound, which comprises at least one activator E and N and/or O in its empirical formula. The activator E is here from a group comprising Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof.

According to at least one embodiment, the phosphor is a red-emitting phosphor comprising an Eu²⁺-doped nitridoaluminate phosphor or consisting of an Eu²⁺-doped nitridoaluminate phosphor.

According to one embodiment, in the X-ray powder diffractogram using Cu—K_α1 radiation, the phosphor has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ.

According to one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇. The crystal structure may in particular be described in the orthorhombic space group Pnnm. In particular, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(7) Å and c=_3.2349(2) and α=β=γ=90°. Alternatively, the crystal structure may be described in a tetragonal crystal system due to twinning and pseudosymmetry. Descriptions in other space groups are also possible.

According to one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula M_4−xEu_xLiAl₁₁N₁₄, wherein M=Ca, Sr and/or Ba, and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies. Eu²⁺ ions in this case in particular replace M and occupy the lattice sites of M. The Eu²⁺-doped nitridoaluminate phosphor with the empirical formula M_4−xEu_xLiAl₁₁N₁₄ preferably crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇.

According to at least one embodiment, the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies.

According to at least one embodiment, the phosphor or the red-emitting phosphor consists of an Eu²⁺-doped nitridoaluminate phosphor of the empirical formula M_4−xEu_xLiAl₁₁N₁₄. The phosphor or the red-emitting phosphor thus comprises just one phase. It is, however, also possible for a further phase consisting of AlN to be present.

According to at least one embodiment, the phosphor or the red-emitting phosphor comprises different phases, in particular one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu²⁺ or the red-emitting phosphor consists of these phases and/or phosphors.

In one embodiment of the use, the phosphor or the red-emitting phosphor is used for the conversion of blue light into longer-wave, red light. For example, the blue light has a wavelength of 400 nm to 500 nm.

In one embodiment of the use, the conversion element is comprised by a light-emitting diode (LED).

In one embodiment of the use, the LED comprises a semiconductor chip which, when in operation, emits blue radiation in a wavelength range from 400 nm to 500 nm, for example, at 460 nm. A semiconductor chip which is suitable for emitting blue radiation when in operation is based, for example, on gallium nitride or indium gallium nitride.

The LED preferably emits white light. In this embodiment, the conversion element may additionally comprise a phosphor which emits radiation in the green region of the electromagnetic spectrum.

The stated embodiments of the phosphor or of the red-emitting phosphor may be used in a conversion element of a light-emitting diode.

A light-emitting diode is provided. This comprises a semiconductor chip which, when the device is in operation, emits blue radiation in a wavelength range from 400 nm to 500 nm and a conversion element comprising a red-emitting phosphor, which comprises an Eu²⁺-doped nitridoaluminate phosphor.

According to one embodiment, in the X-ray powder diffractogram using Cu—K_α1 radiation, the phosphor or the red-emitting phosphor has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. The red-emitting phosphor is configured to convert the radiation emitted by the semiconductor chip into secondary radiation of a wavelength of between 620 nm and 680 nm when the light-emitting diode is in operation.

According to one embodiment, the inorganic compound or the Eu²⁺-doped nitridoaluminate phosphor crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇. The crystal structure may in particular be described in the orthorhombic space group Pnnm. In particular, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(7) Å and c=_3.2349(2) and α=β=γ=90°. Alternatively, the crystal structure may be described in a tetragonal crystal system due to twinning and pseudosymmetry. Descriptions in other space groups are also possible.

According to one embodiment, the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula M_4−xEu_xLiAl₁₁N₁₄, wherein M=Ca, Sr and/or Ba, and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies. Eu²⁺ ions in this case in particular replace M and occupy the lattice sites of M. The Eu²⁺-doped nitridoaluminate phosphor with the empirical formula M_4−xEu_xLiAl₁₁N₁₄ preferably crystallizes in a crystal structure with a comparable atomic sequence as in K₂Zn₆O₇.

According to at least one embodiment, the Eu²⁺-doped nitridoaluminate phosphor has the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄and 0<x≤2, preferably 0.001≤x≤0.4, particularly preferably 0.01≤x≤0.2 applies.

According to at least one embodiment, the phosphor or the red-emitting phosphor consists of an Eu²⁺-doped nitridoaluminate phosphor of the empirical formula M_4−xEu_xLiAl₁₁N₁₄. The red-emitting phosphor thus comprises just one phase. It is, however, also possible for a further phase consisting of AlN to be present.

According to at least one embodiment, the red-emitting phosphor comprises different phases, in particular one phase of the Eu²⁺-doped nitridoaluminate phosphor of the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ and one phase of the phosphor of the empirical formula SrLiAl₃N₄:Eu²⁺ or the red-emitting phosphor consists of these phases and/or phosphors.

One possible embodiment of the conversion element is an embodiment in the form of a potting compound, wherein the potting compound encloses the semiconductor chip in form-fitting manner. Furthermore, the potting compound enclosing the semiconductor chip in form-fitting manner may be stabilized at the side walls, for example, by a package and is located, for example, in a recess in such a package. Materials for the potting compound are known to a person skilled in the art.

The conversion element may moreover take the form of a conversion layer. In the case of the conversion layer, there is direct contact between conversion layer and semiconductor chip, wherein the thickness of the conversion layer may, for example, be less than the thickness of the semiconductor chip and may, for example, be constant at all radiation exit faces.

The conversion element may furthermore assume the shape of a plate or a film. The plate or the film is arranged over the semiconductor chip. In these further variant embodiments of the conversion element, there is not necessarily any direct and/or form-fitting contact between the conversion element and the semiconductor chip. That is to say, there may be a gap between the conversion element and the semiconductor chip. In other words, the conversion element is arranged downstream of the semiconductor chip and is irradiated by the emitted radiation of the semiconductor chip. A potting body or an air gap may then be formed between conversion element and semiconductor chip.

According to one embodiment, the light-emitting diode may be used for backlighting.

BRIEF DESCRIPTION OF THE DRAWINGS

Further advantageous embodiments and further developments of the invention are revealed by the exemplary embodiments described below in conjunction with the figures.

FIGS. 1, 4 and 7 show X-ray powder diffractograms using copper K_α1 radiation of three exemplary embodiments of a red-emitting phosphor;

FIGS. 2, 5 and 8 show emission spectra from three exemplary embodiments of a red-emitting phosphor;

FIGS. 3, 6 and 9 show reflectances from three exemplary embodiments of a red-emitting phosphor;

FIG. 10 shows an emission spectrum of an exemplary embodiment of a red-emitting phosphor;

FIG. 11 shows the reflectance of an exemplary embodiment of a red-emitting phosphor;

FIGS. 12A, 12B, 13A, 13B and 14 show an X-ray powder diffractogram using copper K_α1 radiation from an exemplary embodiment of a red-emitting phosphor;

FIG. 15 shows a portion of the crystal structure of a red-emitting phosphor;

FIGS. 16A, 16B and 16C show characteristic properties of a red-emitting phosphor;

FIG. 17 shows the emission spectra from three substitution variants based on Sr₄Eu_xLiAl₁₁N₁₄; and

FIGS. 18A and 18B show a selection of possible, electroneutral empirical formulae for substitution experiments.

DETAILED DESCRIPTION OF ILLUSTRATIVE EMBODIMENTS

FIG. 1 shows three X-ray powder diffractograms using copper K_α1 radiation. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The X-ray powder diffractogram provided with reference sign I shows that of a first exemplary embodiment of the red-emitting phosphor according to the invention. It has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. These characteristic reflections of the red-emitting phosphor according to the invention have a relative intensity compared to the strongest reflection in the X-ray powder diffractogram of over 2% (absolute intensity) or over 1% (integral intensity). The intensity of these reflections is at least three times as great as the average noise in the X-ray powder diffractogram and the reflections are thus significant reflections, which may be associated with the red-emitting phosphor. The X-ray powder diffractogram provided with reference sign II corresponds to that of the known phosphor of formula SrLiAl₃N₄:Eu²⁺. As is apparent, this known phosphor does not show the characteristic reflections of the red-emitting phosphor according to the invention in the angular range of 11.5-12.5° 2θ and in the angular range of 18.5-19.5° 2θ. The X-ray powder diffractogram provided with reference sign III is a simulated diffractogram of a compound of formula SrLiAl₃N₄. It is clear from the X-ray powder diffractograms shown that the red-emitting phosphor according to the invention is a phosphor which differs from the known phosphor of formula SrLiAl₃N₄:Eu²⁺. This is also proven by the additional reflections in an angular range of 11.5-12.5° 2θ and in the angular range of 18.5-19.5° 2θ of the red-emitting phosphor according to the invention compared with the known phosphor. The phosphor according to the invention comprises the known phosphor SrLiAl₃N₄:Eu²⁺ and additionally also one further phase of an Eu²⁺-doped nitridoaluminate phosphor of empirical formula Sr_4−xEu_xLiAl₁₁N₁₄.

The first exemplary embodiment of the phosphor according to the invention, which has the X-ray powder diffractogram with the reference sign I in FIG. 1, was produced as follows: 0.0591 mol Sr₃N₂, 0.0297 Li₃N, 0.089 mol LiAlH₄, 0.445 mol AlN and 0.0007 mol EuF₃ are mixed together homogeneously. The molar ratio AlN:Sr₃N₂:Li₃N:LiAlH₄:EuF₃ is 1:0.1328:0.0667:0.2:0.0016. The mixture is transferred into a tungsten crucible, which is transferred into a tube furnace. Under a forming gas atmosphere (N₂:H₂=92.5:7.5) the mixture is heated at a heating rate of 250° C. per hour to a temperature of 1250° C. The mixture is annealed for 15 minutes at a temperature of 1250° C., and then cooling to 1000° C. proceeds at a cooling rate of 170° C. per hour. The mixture is held for 15 minutes at 1000° and then cooled to room temperature at a cooling rate of 250° C. per hour.

FIG. 2 shows the emission spectrum of the first exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 1. The wavelength in nanometers is plotted on the x axis and the emission intensity in per cent is plotted on the y axis. To measure the emission spectrum, the phosphor according to the invention was excited with blue light of a wavelength of 460 nm. The phosphor has a half-value width of 59 nm and a dominant wavelength of 627 nm, the emission maximum being at about 654 nm. Compared with the known phosphors (Sr,Ba)₂Si₅N₈:Eu²⁺ with a half-value width of greater than 90 nm and (Sr,Ca)AlSiN₃:Eu²⁺ with a half-value width of greater than 70 nm, the phosphor according to the invention thus has a smaller half-value width. The phosphor according to the invention thus emits virtually only in the visible range of the electromagnetic spectrum, which leads to a reduction in losses in the IR region. The known phosphor SrLiAl₃N₄:Eu²⁺ has a half-value width of about 50 nm, but in comparison with the phosphor SrLiAl₃N₄:Eu²⁺ the quantum efficiency of the phosphor according to the invention is higher.

FIG. 3 shows the reflectance of the first exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 1, as a function of wavelength. The wavelength in nanometers is plotted on the x axis and the reflectance in per cent is plotted on the y axis. As is apparent, the phosphor according to the invention has a minimum reflectance between 450 and 500 nm and is thus best excited with a wavelength of between 450 and 500 nm, since absorption is particularly high at this wavelength. Compared to the known phosphor SrLiAl₃N₄:Eu²⁺, the phosphor according to the invention has a higher absorption in the range from 450 nm to 500 nm.

FIG. 4 shows three X-ray powder diffractograms using copper K_α1 radiation. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The X-ray powder diffractogram provided with reference sign I′ shows that of a second exemplary embodiment of the red-emitting phosphor according to the invention. Like the first exemplary embodiment, it has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. In comparison with the first exemplary embodiment, the intensity of the characteristic reflections is higher. The X-ray powder diffractogram provided with reference sign II shows that of the known phosphor of formula SrLiAl₃N₄:Eu²⁺. As in FIG. 1, it is here also apparent that the known phosphor does not have the characteristic reflections of the phosphor according to the invention in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. The X-ray powder diffractogram provided with reference sign III is a simulated diffractogram of a compound of formula SrLiAl₃N₄.

The second exemplary embodiment of the phosphor according to the invention, the X-ray powder diffractogram of which is shown in Figure ₄ with reference sign I′, was produced as follows: 0.0509 mol Sr₃N₂, 0.0383 Li₃N, 0.0383 mol LiAlH₄, 0.4216 mol AlN and 0.0006 mol EuF₃ are processed into a homogeneous mixture. The molar ratio AlN:Sr₃N₂:Li₃N:LiAlH₄:EuF₃ is 1:0.1207:0.0908:0.0908:0.0014. The mixture is transferred into a tungsten crucible, which is transferred into a tube furnace. Under a forming gas atmosphere (N₂:H₂=92.5:7.5), the mixture is heated at a heating rate of 250° C. per hour to a temperature of 1250°, held for one hour at this temperature and then cooled to room temperature at a cooling rate of 250° C. per hour. The phosphor according to the invention of the second exemplary embodiment comprises the known phosphor SrLiAl₃N₄:Eu²⁺ and additionally also one further phase of an Eu²⁺-doped nitridoaluminate phosphor of empirical formula Sr_4−xEu_xLiAl₁₁N₁₄.

FIG. 5 shows the emission spectrum of the second exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 4. The wavelength in nanometers is plotted on the x axis and the emission intensity in per cent is plotted on the y axis. To measure the emission spectrum, the phosphor according to the invention was excited with blue light of a wavelength of 460 nm. The phosphor has a half-value width of 61 nm and a dominant wavelength of 627 nm, the emission maximum being at about 654 nm.

FIG. 6 shows the reflectance of the second exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 4, as a function of wavelength. The wavelength in nanometers is plotted on the x axis and the reflectance in per cent is plotted on the y axis. As is apparent, the phosphor according to the invention has a minimum reflectance between 450 and 500 nm and is thus best excited with a wavelength of between 450 and 500 nm, since absorption is particularly high at this wavelength. In comparison with the known phosphor SrLiAl₃N₄:Eu²⁺, the second exemplary embodiment of the phosphor according to the invention also has a higher absorption in the range from 450 nm to 500 nm.

FIG. 7 shows three X-ray powder diffractograms using copper K_α1 radiation. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The X-ray powder diffractogram provided with reference sign I″ shows that of a third exemplary embodiment of the red-emitting phosphor according to the invention. Like the first and second exemplary embodiments, it has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ. In comparison with the first and second exemplary embodiments, the intensity of the characteristic reflections is greater. The X-ray powder diffractogram provided with reference sign II shows that of a phosphor of formula SrLiAl₃N₄:Eu²⁺. As in FIGS. 1 and 4, it is here also apparent that the known phosphor does not have the characteristic reflections of the phosphor according to the invention in an angular range of 11.5-12.5° 2θ and in the range 18.5-19.5° 2θ. The X-ray powder diffractogram provided with reference sign III is a simulated diffractogram of a compound of formula SrLiAl₃N₄. The phosphor according to the invention of the third exemplary embodiment comprises the known phosphor SrLiAl₃N₄:Eu²⁺ and additionally also one further phase of an Eu²⁺-doped nitridoaluminate phosphor of empirical formula Sr_4−xEu_xLiAl₁₁N₁₄.

The third exemplary embodiment of the phosphor according to the invention, the X-ray powder diffractogram of which is shown in FIG. 7 with reference sign I″, was produced as follows: 0.0591 mol Sr₃N₂, 0.0297 Li₃N, 0.089 mol LiAlH₄, 0.445 mol AlN and 0.0007 mol EuF₃ were processed into a homogeneous mixture. The molar ratio AlN:Sr₃N₂:Li₃N:LiAlH₄:EuF₃ is 1:0.1328:0.0667:0.20:0.0016. The mixture is transferred into a tungsten crucible, which is transferred into a tube furnace. Under a forming gas atmosphere (N₂:H₂=92.5:7.5), the mixture is heated at a heating rate of 250° C. per hour to a temperature of 1250° , held for five hours at this temperature and then cooled to room temperature at a cooling rate of 250° C. per hour.

FIG. 8 shows the emission spectrum of the third exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 7. The wavelength in nanometers is plotted on the x axis and the emission intensity in per cent is plotted on the y axis. To measure the emission spectrum, the phosphor according to the invention was excited with blue light of a wavelength of 460 nm. The phosphor has a half-value width of 68 nm and a dominant wavelength of 625 nm, the emission maximum being at about 652 nm.

FIG. 9 shows the reflectance of the third exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 7, as a function of wavelength. The wavelength in nanometers is plotted on the x axis and the reflectance in per cent is plotted on the y axis. As is apparent, the phosphor according to the invention has a minimum reflectance between 450 and 500 nm and is thus best excited with a wavelength of between 450 and 500 nm, since absorption is particularly high at this wavelength. In comparison with the known phosphor SrLiAl₃N₄:Eu²⁺, a higher absorption in the range from 450 nm to 500 nm may also be shown for the third exemplary embodiment of the phosphor according to the invention.

Overall, it is clear from the three exemplary embodiments of the red-emitting phosphor according to the invention that by varying the temperature T1, the duration of method step C) and/or the molar ratios of the starting materials, the half-value width of the red-emitting phosphor or the composition of the red-emitting phosphor may be varied. In summary, the three exemplary embodiments have the following half-value widths and dominant wavelengths:

	FWHM/nm	λdom/nm
First exemplary embodiment	59	627
Second exemplary embodiment	61	627
Third exemplary embodiment	68	625

FIG. 10 shows the emission spectrum of a fourth exemplary embodiment of the red-emitting phosphor according to the invention. The wavelength in nanometers is plotted on the x axis and the emission intensity in per cent is plotted on the y axis. To measure the emission spectrum, the phosphor according to the invention in the form of a powder tablet was excited with blue light of a wavelength of 460 nm. The phosphor has a half-value width of 85 nm and a dominant wavelength of 623.5 nm, the emission maximum being at 670 nm.

The fourth exemplary embodiment of the phosphor according to the invention was produced as follows: 161.75 mmol Sr₃N₂, 485.26 mmol SrH₂, 828.27 mmol LiAlH₄ 48.72 mmol Li₃N, 1843.60 mmol AlN and 3.90 mmol EuF₃ were processed into a homogeneous mixture. The molar ratio AlN:Sr₃N₂:SrH₂:LiAlH₄:Li₃N:EuF₃ is 1:0.088:0.263:0.449:0.026:0.002. The mixture is transferred into a tungsten crucible, which is in turn transferred into a tube furnace. Under a forming gas atmosphere (N₂:H₂=92.5:7.5), the mixture is heated at a heating rate of 250° C. per hour to a temperature of 1400°, held for 15 minutes at this temperature and then cooled to room temperature at a cooling rate of 250° C. per hour. The phosphor has the empirical formula Sr₄LiAl₁₁N₁₄:Eu²⁺, wherein Eu²⁺ partly replaces Sr. This can alternatively be written Sr_4−xEu_xLiAl₁₁N₁₄. The red-emitting phosphor or the Eu²⁺-doped nitridoaluminate phosphor crystallizes in a crystal structure with the same atomic sequence as in K₂Zn₆O₇. The crystal structure may in particular be described in the orthorhombic space group Pnnm. In particular, the lattice parameters in the orthorhombic description with the space group Pnnm are a=10.4291(7) Å, b=10.4309(7) Å and c=3.2349(2) and α=β=γ=90°. Descriptions in other space groups are also possible.

FIG. 11 shows the reflectance of the fourth exemplary embodiment of the phosphor according to the invention, which was synthesized as described in relation to FIG. 10, as a function of wavelength. The wavelength in nanometers is plotted on the x axis and the reflectance in per cent is plotted on the y axis. As is apparent, the phosphor according to the invention has a minimum reflectance between 450 and 500 nm and is thus best excited with a wavelength of between 450 and 500 nm, since absorption is particularly high at this wavelength. In comparison with the known phosphor SrLiAl₃N₄:Eu²⁺, a higher absorption in the range from 450 nm to 500 nm may also be shown for the fourth exemplary embodiment of the phosphor according to the invention.

FIG. 12A shows the X-ray powder diffractogram using copper K_α1 radiation of the fourth exemplary embodiment, which was synthesized as described in relation to FIG. 10. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The fourth exemplary embodiment also has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ.

FIG. 12B shows a portion of the X-ray powder diffractogram from FIG. 12A. Here again, the two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ are clearly apparent.

FIG. 13A shows two X-ray powder diffractograms using copper Km radiation. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The X-ray powder diffractogram provided with reference sign I″′ shows that of the fourth exemplary embodiment of the red-emitting phosphor according to the invention. The X-ray powder diffractogram provided with reference sign II shows that of a phosphor of formula SrLiAl₃N₄:Eu²⁺. As in FIGS. 1 and 4 and 7, it is here also apparent that the known phosphor does not have the characteristic reflections of the phosphor according to the invention in an angular range of 11.5-12.5° 2θ and in the range 18.5-19.5° 2θ.

FIG. 13B shows a portion of the X-ray powder diffractogram of FIG. 13A.

FIG. 14 shows two X-ray powder diffractograms using copper K_α1 radiation. The diffraction angles are plotted on the x axis in ° 2θ values and the intensity is plotted on the y axis. The X-ray powder diffractogram provided with reference sign I″′ shows that the measured X-ray powder diffractogram of the fourth exemplary embodiment of the red-emitting phosphor according to the invention. The diffractogram provided with reference sign IV corresponds to the X-ray powder diffractogram calculated from single crystal data for the phosphor according to the invention of formula Sr_4−xEu_xLiAl₁₁N₁₄. The reflections marked * should be assigned to a secondary phase of AlN. This may also result from the starting material or possibly also be attributable to partial decomposition of the phosphor. As is apparent, the match between the measured X-ray powder diffractogram with the reference sign I″′ and the calculated diagram with the reference sign VI is very high.

FIG. 15 shows the orthorhombic crystal structure of the phosphor Sr_4−xEu_xLiAl₁₁N₁₄ in a schematic diagram. The phosphor crystallizes orthorhombically in the space group Pnnm. The structure of the phosphor was determined on the basis of single crystal diffraction data. The structure has corner-linked and edge-linked (Al,Li)N-tetrahedra. Sr atoms are arranged amongst the network of tetrahedra. Descriptions in other space groups are also possible. The phosphor according to the invention thus has the same atomic sequence as K₂Zn₆O₇.

FIG. 16A shows crystallographic data of Sr_4−xEu_xLiAl₁₁N₁₄.

FIG. 16B shows atomic layers in the structure of Sr_4−xEu_xLiAl₁₁N₁₄.

FIG. 16C shows anisotropic displacement parameters for Sr_4−xEu_xLiAl₁₁N₁₄.

FIG. 17 shows the emission spectra of three substitution variants of the phosphor Sr_4−xEu_xLiAl₁₁N₁₄. Substitution variants should here be understood to mean that in these phosphors the elements Sr, Eu, Li, Al and/or N in the empirical formula Sr_4−xEu_xLiAl₁₁N₁₄ are in part replaced by other elements. The wavelength in nanometers is plotted on the x axis and the emission intensity E in per cent is plotted on the y axis. To measure the emission spectrum, the samples in the form of individual crystals were excited with blue light of a wavelength of 460 nm. By varying the composition, while preserving the half-value width, i.e., while preserving the atomic sequences, it is possible to achieve a significant shift in the emission bands towards shorter wavelengths, leading to a further increase in the overlap with the sensitivity of the eye and thus more efficient phosphors. The phosphor, which has the emission with reference sign A, shows in EDX measurements an Al:Si molar ratio of about 1:1 and has a peak wavelength of 636 nm and is thus markedly blueshifted compared with the unsubstituted phosphor Sr₄LiAl₁₁N₁₄:Eu²⁺, which has a peak wavelength at 670 nm.

FIGS. 18A and 18B show tables with possible, electroneutral compounds, which may be achieved by substitution experiments, as with general empirical formula (AX_aAY_bAZ_c)(BV_dBW_eBX_fBY_gBZ_h)(CX_nCY_y):E. The substitutions shown are merely exemplary, other substitutions are likewise possible while preserving the crystal structure.

The description made with reference to exemplary embodiments does not restrict the invention to these embodiments. Rather, the invention encompasses any novel feature and any combination of features, including in particular any combination of features in the claims, even if this feature or this combination is not itself explicitly indicated in the claims or exemplary embodiments.

Claims

1-19. (canceled)

20. A phosphor comprising: an inorganic compound having at least one activator E and N and/or O in its empirical formula,wherein E is selected from the group consisting of Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof, andwherein the inorganic compound crystallizes in a crystal structure with the same atomic sequence as in K2Zn6O7.

21. The phosphor according to claim 20, wherein the crystal structure is described in the orthorhombic space group Pnnm.

22. The phosphor according to claim 20, wherein the inorganic compound has one of the following general empirical formulae: (AXaAYbAZc)(BVdBWeBXfBYgBZh)(CXnCYy):E or(AXaAYbAZc)(BVdBWeBXfBYgBZh)(CXnCYy),wherein AX is selected from the group consisting of monovalent metals,wherein AY is selected from the group consisting of divalent metals,wherein AZ is selected from the group consisting of trivalent metals,wherein BV is selected from the group consisting of monovalent metals,wherein BW is selected from the group consisting of divalent metals,wherein BX is selected from the group consisting of trivalent elements,wherein BY is selected from the group consisting of tetravalent elements,wherein BZ is selected from the group consisting of pentavalent elements,wherein CX is selected from the group consisting of O, S, C, F, Cl, Br, I and combinations thereof,wherein CY=N,wherein E is selected from the group consisting of Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof, andwherein: 1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, 3<a+b+c<5,10<d+e+f+g+h<14,12<n+y<16 and−0.5≤z≤0.5.

23. The phosphor according to claim 22, wherein: 1a+2b+3c+1d+2e+3f+4g+5h−2n−3y=z, a+b+c=4,d+e+f+g+h=12,n+y=14, and−0.1≤z≤0.1.

24. The phosphor according to claim 22, wherein z=0.

25. The phosphor according to claim 24, wherein the inorganic compound has one of the following empirical formulae: M4Li1+y′/2Al11−y′/2N14−y′Oy′:E, M4Li1−z′Al11−z′Zn2z′N14:E, M4Li1Al11−x′Znx′N14−x′Ox′:E,M4Li1Al11−y″Mgy″N14−y″Oy″:E, M4Li1+z″Al11−3z″Si2z″N14:E or M4Li1Al11−2x″Six″Mgx″N14:E,wherein M=Ca, Sr and/or Ba, andwherein: 0≤y′≤14,0≤z′≤1,0≤x′≤11,0≤y″≤11,0≤z″≤3 and and0≤x′≤5.

26. The phosphor according to claim 25, wherein M=Sr.

27. The phosphor according to claim 20, wherein AX is selected from the group consisting of Li, Na, K, Rb, Cs and combinations thereof,wherein AY is selected from the group consisting of Mg, Ca, Sr, Ba, Eu, Yb, Mn, Ni and combinations thereof,wherein AZ is selected from the group consisting of Sc, Y, La, Pr, Ce, Yb, Cr and combinations thereof,wherein BV is selected from the group consisting of Li, Na and combinations thereof,wherein BW is selected from the group consisting of Mg, Zn, Mn, Ni and combinations thereof,wherein BX is selected from the group consisting of B, Al, Ga, Ce, Cr and combinations thereof,wherein BY is selected from the group consisting of Si, Ge, Mn and combinations thereof,wherein BZ=P,wherein CX is selected from the group consisting of O, S and combinations thereof,wherein CY=N, andwherein E is selected from the group consisting of Mn, Cr, Ni, Ce, Pr, Nd, Sm, Eu, Tb, Dy, Ho, Er, Yb, Tm, Li, Na, K, Rb, Cs and combinations thereof.

28. The phosphor according to claim 20, wherein the inorganic compound has one of the following empirical formulae: M4−xEuxLi1+y′/2Al11−y′/2N14−y′Oy′, M4−xEuxLi1−z′Al11−z′Zn2z′N14, M4−xEuxLi1Al11−x′Znx′N14−x′Ox′,M4−xEuxLi1Al11−y″Mgy″N14−y″Oy″, M4−xEuxLi1+z″Al11−3z″Si2z″N14 or M4−xEuxLi1Al11−2x″Six″Mgx″N14 wherein M=Ca, Sr and/or Ba, and 0≤y′≤14,0≤z′≤1,0≤x′≤11,0≤y″≤11,0≤z″≤3,0≤x″≤5 and0≤x≤2.

29. The phosphor according to claim 20, wherein the inorganic compound has the following empirical formula: M4−xEuxLiAl11N14, wherein M=Ca, Sr and/or Ba, and 0<x≤2.

30. The phosphor according to claim 20, wherein the phosphor has an emission maximum in a range from 500 to 680 nm.

31. The phosphor according to claim 20, wherein the phosphor has a dominant wavelength of λ>500 nm.

32. A method for producing the phosphor according to claim 20, the method comprising: mixing starting materials comprising Li3N, LiAlH4, Sr3N2, AlN and EuF3 or Li3N, LiAlH4, Sr3N2, AlN, SrH2 and EuF3; heating the mixture to a temperature of between 900 and 1400° C.;annealing the mixture at a temperature of 900 to 1400° C. for five minutes to six hours; andcooling the mixture to room temperature.

33. The method according to claim 32, wherein method comprises performing the method between heating the mixture and cooling the mixture under a gas atmosphere.

34. A conversion element comprising the phosphor according to claim 20.

35. The conversion element according to claim 34, wherein the conversion element is a conversion element for an LED.

36. A method for using the phosphor according to claim 20, the method comprising: converting incoming light, by the phosphor, into a longer-wave light.

37. A red-emitting phosphor comprising: an Eu2+-doped nitridoaluminate phosphor,wherein, in a X-ray powder diffractogram using Cu—Kα1 radiation, the red-emitting phosphor has two characteristic reflections in an angular range of 11.5-12.5° 2θ and in an angular range of 18.5-19.5° 2θ.

38. The red-emitting phosphor according to claim 37, wherein a crystal structure of the Eu2+-doped nitridoaluminate phosphor has the same atomic sequence as in K2Zn6O7.