Phosphorylation of epoxides

Abstract

A process for the phosphorylation of epoxides, in particular of epoxidised fatty acid esters, and the use of the phosphorylation products for the production of lubricants.

Description

Phosphoric acid and its mono- and diesters react with epoxides to form phosphoric acid hydroxy esters. The following reactions are possible:

According to equation 1, phosphoric acid and its esters 1 react with the epoxide 2 to form a phosphoric acid hydroxy ester derivative 3. ##STR1##

Scheme 1 describes the addition of phosphoric acid and of its esters to epoxidized fatty acid glycerides. As the reaction scheme shows, the phosphorylation reaction may also give rise to oligomerised triglycerides. ##STR2##

Tertiary esters of ortho-phosphoric acid with alcohols or phenols are used as plasticizers, fire-resistant hydrolic liquids and compressor oils and oil and fuel additives. They are classified as triaryl, trialkyl or alkylaryl phosphates according to the nature of their alcoholic radicals. The reaction of alcohols with the acid chlorides of phosphoric acid is of technical importance.

It has now been found that the reaction products of phosphoric acid and their mono- and diesters with epoxides, in particular with epoxidized fatty acids and fatty acid derivatives, may be used as lubricant additives.

The invention relates to a process for the phosphorylation of epoxidized fatty acids, e.g. oleic acids, linoleic acids, erucic acids and fatty acid derivatives such as fatty acid esters, e.g. colza oil, soya bean oil or oleic acid methyl ester, characterised in that an epoxidized fatty acid or a derivative thereof having an epoxide content of from 1.5-15% by weight, preferably from 4-8% by weight, is reacted with the phosphoric acid or its ester at 0.degree.-120.degree. C., preferably at 20.degree.-80.degree. C., most preferably at about 40.degree. C. The quantity of phosphoric acid or its ester is calculated to provide about one equivalent of phosphoric acid for each epoxide group.

The invention also relates to the phosphorylated epoxylated fatty acids and fatty acid derivatives obtained as indicated above.

Epoxidized fatty acids and fatty acid derivatives, e.g. fatty acid esters, are in particular epoxidation products of fatty acid glycerides or of their alkyl esters (in particular methyl ester), e.g. of colza oil, soya bean oil, lard oil, etc. having an epoxide content of from 3-10% by weight. They may be used singly or as mixtures. Examples of such mixtures are epoxidized colza oil/epoxidized colza oleic acid methyl ester and epoxidized soya bean oil/epoxidized colza oleic acid methyl ester.

Epoxidized fatty acid esters may also be phosphorylated together with epoxidized hydrocarbons (straight chain or branched) or with epoxidized ether compounds preferably having 6-10 carbon atoms. An example of such compounds is 1-(2-ethyl-hexyloxy)-2,3-epoxypropane/epoxidized soya bean oil.

Phosphoric acid or mono- and diesters of phosphoric acid may be used for phosphorylation. Mono- and dialkylesters having straight chain or branched alkyl groups with a chain length of preferably 4-10 carbon atoms and mono- and diarylesters are particularly suitable.

The phosphorylated fatty acid esters according to the invention act as high pressure additives (EP additives) and wear-resistant additives (AW additives), e.g. in mineral oils, synthetic oils, lubricating fats and naturally occurring oils. Such additives may form iron-phosphorus compounds with the iron from the lubricated machine parts, and these iron-phosphorus compounds substantially reduce the wear on these parts (e.g. roller bearings, gear wheels, tools), thereby increasing their useful life. These compounds also prevent the seizing up of machine parts, especially of rotating machine parts. Further, phosphorylated fatty acid esters also act as corrosion inhibitors and as antioxidants. Better results may also be achieved, for example, in the chip cutting working of metals.

The phosphorylated fatty acid esters may be used e.g. as 0.1 to 1.5% by weight solutions, preferably 0.2 to 1% by weight solutions, in basic oils. With 0.3 to 1% by weight solutions in basic oils it is possible to obtain spherical cup diameters of from 0.3 to 0.4 mm in the four ball tester* or a damaging force stage of 12 in the gear wheel tension testing machine. The four ball apparatus test (VKA) according to ASTM-D-2266 serves to determine characteristic values which should permit high surface pressures in the region of mixed friction between surfaces moving in relation to one another. The testing of lubricants in the FZG gear wheel tension testing machine according to DIN 51354 T.1 is used for determining the maximum stress tolerated by the lubricants (occurrence of furrows and scoring at the flanks of the teeth).

*(test conditions: 1 h /300 N)

BRIEF DESCRIPTION OF THE TEST PROCESS

VKA test DIN 51350 - ASTM D 2783 and D 2266

The lubricant is tested in a four ball tester consisting of a rotating ball (running ball) sliding on three balls (standing balls) identical to the running ball. The testing forces may either be increased stepwise until the four ball tester fails or the diameters of the spherical indentations of the three standing balls may be measured after a predetermined testing time during which a constant testing force is applied.

FZG Test DIN 51354 - ASTM D 1947

Specified gear wheels rotate with the lubricant to be tested at a constant speed and a predetermined initial lubricant temperature. The stress on the flanks of the teeth may be increased stepwise. After termination of the test run or after each force stage in the stepwise test, the changes on the flanks of the teeth (flank damages) are recorded by description, photographs, measurements of roughness or contrast impression.

The weight changes in the test wheels may be determined in addition (gravimetric method).

EXAMPLE 1

AW Additive for mineral oils.

210.5 g of mono/dihexylphosphoric acid ester (molar ratio 1:1) are added to 339 g (1.82 mol) of 1-(2-ethylhexyloxy)-2,3-epoxipropane with stirring at 40.degree. C. within 15 minutes. The reaction is highly exothermic. After a reaction time of 30 minutes, the reaction product obtained may be used as AW additive.

______________________________________Test results:______________________________________Appearance: clear, oily liquidP content: 5.6% by weight 0.5% by weight of the additive in refined solvent ISO VG 46VKA (1500 rpm)(DIN 51 350 T.2)Product load 1200 NScuffing load 1300 N 0.4% by weight of the additive in refined solvent ISO VG 46VKA endurance run(DIN 51 350 T.3)1 h/300 NDiameter of indentation 0.45 mmFZG test, A8.3/90 12(DIN 51354) visualdamaging force stageCopper activity 1 a(ASTM-D-130) 3 h/100.degree. C. Refined solvent ISO VG 46 + 3% by weight additiveHumidity chamber after 200 h degree ofSteel quality QQS698 corrosion 0 (no corrosion)polished with abrasive Refined solvent ISO VG 46 +(DIN 51359) 0.8% by weight additiveProtection against Degree of corrosion 0corrosion in steel (no corrosion)(DIN 51585 B)______________________________________

EXAMPLE 2

AW Additive for vegetable oils, polyglycols and synthetic esters

500 g of epoxidized colza oleic acid methyl ester having an epoxide content of 4.9% by weight and 204 g of colza oil are introduced into the reaction vessel with stirring. 150 g of mono-di-2-ethyl hexyl phosphoric acid ester (ratio 1:1) are then added within 5 minutes. The reaction is slightly exothermic. The mixture is left to react for a further 5 minutes. The reaction product obtained may be used without further working up, inter alia as AW additive.

______________________________________Test results______________________________________Appearance: pale yellow, highly viscous liquidP content: 2.34% 1% by weight additive in synthetic estersVKA endurance run (DIN 51350, T.3) 0.3 mm1 h/300 NDiameter of spherical indentationFZG test A8, 3/90 (DIN 51354) 12visualDamaging force stageCopper activity (ASTM-D-130) 1 a3 h/100.degree. C.______________________________________

Claims

1. A lubricating oil or fat containing 0.1 to 1.5% by weight of a phosphorylated epoxidized fatty acid triglyceride which is produced by reacting an epoxidized fatty acid glyceride with a mixture of mono- and diester of phosphoric acid at 0.degree. to 120.degree. C.