Abstract
The present disclosure is drawn to a photo active agent which includes a diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine.
Description
BACKGROUND

Recently, curing of ink by radiation, and in particular ultraviolet (UV) curing, has become popular. UV curable ink can be cured after printing by application of UV light. Typically, UV curable inks include monomers that form polymers by free radical polymerization. The growing end of each polymer chain is a radical that reacts with additional monomers, transferring the radical to the end of the chain as each monomer is added. A photo initiator can be used to form the first radicals to begin the polymerization process. The photo initiator can be capable of absorbing UV light to generate radicals to react with the monomers.


Two types of photo initiators can be used in UV curable compositions. Type I photo initiators are unimolecular photo initiators that undergo a hemolytic bond cleavage upon absorption of UV light, forming radicals. Type II photo initiators are bimolecular photo initiators. These are used as a system of a photo initiator with a synergist, which can together form radicals upon exposure to UV light. Some type II photo initiators react by hydrogen abstraction from the synergist to the photo initiator.





BRIEF DESCRIPTION OF THE DRAWINGS


FIG. 1 is example general scheme of forming a water soluble TPO compound in accordance with the present disclosure; and



FIG. 2 depicts an example method of preparing a photo curable ink in accordance with the present disclosure.





DETAILED DESCRIPTION

The inkjet printing industry uses various types of inks, such as oil-based inks, solvent-based (non-aqueous) inks, water-based (aqueous) inks, and solid inks which are melted in preparation for dispensing. Solvent-based inks are fast drying, and as a result, are widely used for industrial printing. When solvent-based inks containing binders and other ingredients are jetted onto a substrate, the solvent(s) partially or fully evaporate from the ink, leaving the binder and other ingredients such as pigment particles on the printed substrate in the form of a dry film. During the drying process, the solvents, which are often volatile organic compounds (VOC), emit vapors, and therefore, can pollute the environment. The amount of pollution produced can increase greatly with higher printing speeds or for wide format images, where large amounts of ink are deposited onto a substrate.


As a result of this and other concerns, efforts related to preparing inks that are environmentally friendly have moved some research in the direction of water-based inks. However, radiation-curable (or photo-curable) water-based ink compositions are noticeably limited among available options due to their specific formulation properties. For example, even though one can use dispersions of photo initiators along with a dispersant, there are still crystallization issues that can get introduced at high concentrations in the ink. Thus, it would be desirable to develop water soluble and UV reactive photo initiators, including those that may also be stable in photo curable ink formulations, have relatively high water solubility, and/or are chemical stable. In some specific examples, photo initiators (with or without the presence of sensitizers) may also be desirable that have high reactivity to commercially available UV-LED lights, such as 395 nm and other UV-LED lights.


Accordingly, the present disclosure is drawn to water soluble photo active agents that can be used as photo initiators, sensitizers, or both. More specifically, the present disclosure provides photo active agents including a tertiary amine modified diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide, wherein the tertiary amine is further modified by a C1 to C5 water solubilizing group, such as hydroxyl, sulfonic acid, sulfonates, carboxylate, carbyxylic acid, or polyethylene glycol having from 2 to 20 ether groups. Thus, the photo active agents can be water soluble and stable in aqueous inks, such as aqueous thermal inkjet inks, for example.


In one example, a photo active agent can include diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine.


In another example, a photo curable ink can include a photo reactive binder; a photo active agent including diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine; a co-photo initiator, a synergist, or combination thereof; a colorant; and a liquid vehicle including co-solvent and water. In this example, the photo curable ink can have a pH of 7 to 12, and the photo active agent is stable in the photo curable ink. In another example, the photo curable ink can be photo curable using UV-LED electromagnetic radiation. In some examples, the photo active agent can act as a sensitizer, and the photo curable ink can provide the co-photo initiator. In other examples, the photo active agent can be a photo initiator, and the photo curable ink can provide a synergist.


In another example, a method of making a photo curable ink can include mixing a photo reactive binder; a co-photo initiator, a synergist, or combination thereof; a colorant; and a liquid vehicle including co-solvent and water with a photo active agent. The photo active agent can include a diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine.


As mentioned, these examples include a diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide (TPO) modified with a tertiary amine group that includes a water solubilizing group. For reference, TPO is shown as follows:




embedded image


As shown, in the TPO structure, there are two available positions for modification of the 2,4,6-trimethylbenzoyl group (with the 1 position already occupied by the C═O group and diphenyl phosphine oxide group), namely the 3 position and the 5 position. Thus, water solubilized TPO (modified with the tertiary amine and water soluble groups) in accordance with examples of the present disclosure can be prepared, and shown in FIG. 1, and more specifically below as “General Formula:”




embedded image



where A includes a C1 to C5 water solubilizing group, and R includes an organic side group. The organic side group may include a C1 to C5 water solubilizing group or some other organic structure. Examples of other organic structures include an additional TPO structure, an alkyl group, an alicyclic group, another tertiary amine group, or combination thereof. Further, in this General formula, n can be 1 or 2. For clarity, as mentioned, there are two available positions (position 3 and position 5) structure, and the water solubilized tertiary amine group can be at one or both available positions. Furthermore, the A group and the R group can be different from one another if n is 2. In other words, when n is 2, the A water solubilizing groups do not need to be the same at the 3 position and the 5 position (likewise for the R group). However, in some examples, they can be the same.


There are several examples of specific structures provided herein by way of example. These specific structures can be prepared in accordance with the General Formula provided above. Formulas I-XII are exemplary, and other similar structures can be prepared in accordance with examples of the present disclosure. In Formulas I-XII below, M can be hydrogen or a monovalent cation, such as an alkali metal (sodium, potassium, etc.) or ammonium.




embedded image


embedded image


embedded image


embedded image


There are various synthetic methods of preparing these and other water solubilized, TPO based, photo initiators shown above. For example, as shown in Scheme 1 below, reaction of commercially available TPO (1) with 3 equivalents of paraformaldehyde in the presence of AlCl3 in chloroform at 0° C., followed by heating at 60° C., gives a corresponding TPO chloride 2. Reaction of TPO chloride (2) with N-methyl-D-glucamine (3) in the presence of K2CO3 in acetonitrile under reflux gives the water soluble photo initiator I.




embedded image


As shown in Scheme 2, reaction of commercially available TPO (1) with 6 equivalents of paraformaldehyde in the presence of AlCl3 in chloroform at 0° C., followed by heating at 60° C., gives a corresponding TPO di-chloride 4. Reaction of TPO di-chloride (4) with 2 equivalents of N-methyl-D-glucamine (3) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator II.




embedded image


Similarly as shown in Scheme 3, reaction of TPO chloride (2) with 3-(Cyclohexylamino)-1-propanesulfonic acid (5) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator III.




embedded image


As shown in Scheme 4, reaction of TPO chloride (2) with 2-(Cyclohexylamino)ethanesulfonic acid (6) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator IV.




embedded image


As shown in Scheme 5, reaction of 2 equivalents of TPO chloride (2) with taurine (7) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator V.




embedded image


As shown in Scheme 6, reaction of TPO di-chloride (4) with 2 equivalents of 3-(Cyclohexylamino)-1-propanesulfonic acid (5) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator VI.




embedded image


As shown in Scheme 7, reaction of TPO di-chloride (4) with 2 equivalents of 2-(Cyclohexylamino)ethanesulfonic acid (6) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator VII.




embedded image


As shown in Scheme 8, reaction of 2 equivalents of TPO chloride (2) with Bis-tris propane (8) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator VIII.




embedded image


As shown in Scheme 9, reaction of TPO chloride (2) with N-[Tris(hydroxymethyl)methyl]-2-aminoethanesulfonic acid (9) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator IX.




embedded image


As shown in Scheme 10, reaction of TPO di-chloride (4) with 2 equivalents of N-[Tris(hydroxymethyl)methyl]-2-aminoethanesulfonic acid (9) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator X.




embedded image


As shown in Scheme 11, reaction of TPO chloride (2) with iminodiacetic acid (10) in the presence of K2CO3 in acetonitrile under reflux gives water soluble photo initiator XI.




embedded image


As shown in Scheme 12, reaction of TPO di-chloride (4) with iminodiacetic acid (10) in the presence of K2CO3 in acetonitrile under reflux gives soluble photo initiator XII.




embedded image


The present disclosure also extends to photo curable inks, such as UV curable inks including UV-LED curable inks. In some examples, a photo curable ink can include a photo reactive binder (such as a UV curable or UV-LED curable binder), a photo active agent, a co-photo initiator and/or a synergist, a colorant, a co-solvent, and water. The photo active agent can include the diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine. In various aspects, the photo active agent can act as a photo initiator with the synergist, or it can act as a sensitizer for a co-photo initiator, for example.


In some cases, the photo reactive binder can include a UV or UV-LED curable polyurethane and hydrophobic radiation-curable monomers. In one example, the UV reactive binder can include a water dispersible (meth)acrylated polyurethane, such as NeoRad® R-441 by NeoResins (Avecia). Other examples of UV reactive binders can include Ucecoat® 7710, Ucecoat® 7655 (available from Cytec), Neorad® R-440, Neorad® R-441, Neorad® R-447, Neorad® R-448 (available from DSM NeoResins), Bayhydrol® UV 2317, Bayhydrol® UV VP LS 2348 (available from Bayer), Lux 430, Lux 399, Lux 484 (available from Alberdingk Boley), Laromer® LR 8949, Laromer® LR 8983, Laromer® PE 22WN, Laromer® PE 55WN, Laromer® UA 9060 (available from BASF), or combinations thereof.


The photo active agents of the present disclosure can act as Type I or Type II photo initiators. Thus, in one example, the photo curable ink can include a synergist so that the photo initiator and synergist together can generate radicals during photo curing, such as with UV curing or even UV-LED curing processes. In some examples, the synergist can be an amine synergist. The amine synergist can be a tertiary amine compound. In one example, the amine synergist can be a polymeric amine synergist such as a derivative of aniline and a polyether amine such as Jeffamine® 900. In other examples, the amine synergist can be trimethylamine, triethanolamine, methyldiethanolamine, phenyldiethanolamine, N,N,N′,N′-tetra(hydroxylethyl)ethylenediamine, dimethylaminoethyl acrylate, dimethylaminoethyl methacrylate, ethyl dimethylaminobenzoate, or combinations thereof.


The photo active agents of the present disclosure can likewise act as the primary photo initiator in the photo curable ink, or they can act as a sensitizer for another photo initiator. Therefore, the photo curable ink can in some cases include a second photo initiator in addition to the photo active agents disclosed herein. Examples of radical photo initiators include, by way of illustration and not limitation, 1-hydroxy-cyclohexylphenylketone, benzophenone, 2,4,6-trimethylbenzo-phenone, 4-methylbenzophenone, diphenyl-(2,4,6-trimethylbenzoyl)phosphine oxide, phenyl bis(2,4,6trimethylbenzoyl)phosphine oxide, 2-hydroxy-2-methyl-1-phenyl-1-propanone, benzyl-dimethyl ketal, 2-methyl-l-[4-(methylthio)phenyl]-2-morpholinopropan-l-one, or combinations thereof. Non-limiting examples of additional photo initiators include alpha amino ketone UV photo initiators such as Ciba® Irgacure® 907, Ciba® Irgacure® 369, and Ciba® Irgacure® 379; bis acylphosphine oxide (BAPO) UV photo initiators such as Irgacure® 819, Darocur® 4265, and Darocur® TPO; alpha hydroxy ketone UV photo initiators such as Irgacure® 184 and Darocur® 1173; including photo initiators with or without sensitizers such as Darocur® ITX (2-isopropyl thioxanthone).


The colorant in the photo curable ink can be a pigment, a dye, or a combination thereof. In some examples, the colorant can be present in an amount from 0.5 wt % to 10 wt % in the photo curable ink. In one example, the colorant can be present in an amount from 1 wt % to 5 wt %. In another example, the colorant can be present in an amount from 5 wt % to 10 wt %.


In some examples, the colorant can be a dye. The dye can be nonionic, cationic, anionic, or a mixture of nonionic, cationic, and/or anionic dyes. Specific examples of dyes that can be used include, but are not limited to, Sulforhodamine B, Acid Blue 113, Acid Blue 29, Acid Red 4, Rose Bengal, Acid Yellow 17, Acid Yellow 29, Acid Yellow 42, Acridine Yellow G, Acid Yellow 23, Acid Blue 9, Nitro Blue Tetrazolium Chloride Monohydrate or Nitro BT, Rhodamine 6G, Rhodamine 123, Rhodamine B, Rhodamine B Isocyanate, Safranine O, Azure B, and Azure B Eosinate, which are available from Sigma-Aldrich Chemical Company (St. Louis, Mo.). Examples of anionic, water-soluble dyes include, but are not limited to, Direct Yellow 132, Direct Blue 199, Magenta 377 (available from Ilford AG, Switzerland), alone or together with Acid Red 52. Examples of water-insoluble dyes include azo, xanthene, methine, polymethine, and anthraquinone dyes. Specific examples of water-insoluble dyes include Orasol® Blue GN, Orasol® Pink, and Orasol® Yellow dyes available from Ciba-Geigy Corp. Black dyes may include, but are not limited to, Direct Black 154, Direct Black 168, Fast Black 2, Direct Black 171, Direct Black 19, Acid Black 1, Acid Black 191, Mobay Black SP, and Acid Black 2.


In other examples, the colorant can be a pigment. The pigment can be self-dispersed with a polymer, oligomer, or small molecule; or can be dispersed with a separate dispersant. Suitable pigments include, but are not limited to, the following pigments available from BASF: Paliogen® Orange, Heliogen® Blue L 6901F, Heliogen® Blue NBD 7010, Heliogen® Blue K 7090, Heliogen® Blue L 7101 F, Paliogen® Blue L 6470, Heliogen® Green K 8683, and Heliogen® Green L 9140. The following black pigments are available from Cabot: Monarch® 1400, Monarch® 1300, Monarch® 1100, Monarch® 1000, Monarch® 900, Monarch® 880, Monarch® 800, and Monarch® 700. The following pigments are available from CIBA: Chromophtal® Yellow 3G, Chromophtal® Yellow GR, Chromophtal® Yellow 8G, Igrazin® Yellow 5GT, Igralite® Rubine 4BL, Monastral® Magenta, Monastral® Scarlet, Monastral® Violet R, Monastral® Red B, and Monastral® Violet Maroon B. The following pigments are available from Degussa: Printex® U, Printex® V, Printex® 140U, Printex® 140V, Color Black FW 200, Color Black FW 2, Color Black FW 2V, Color Black FW 1, Color Black FW 18, Color Black S 160, Color Black S 170, Special Black 6, Special Black 5, Special Black 4A, and Special Black 4. The following pigment is available from DuPont: Tipure® R-101. The following pigments are available from Heubach: Dalamar® Yellow YT-858-D and Heucophthal Blue G XBT-583D. The following pigments are available from Clariant: Permanent Yellow GR, Permanent Yellow G, Permanent Yellow DHG, Permanent Yellow NCG-71, Permanent Yellow GG, Hansa Yellow RA, Hansa Brilliant Yellow 5GX-02, Hansa Yellow-X, Novoperm® Yellow HR, Novoperm® Yellow FGL, Hansa Brilliant Yellow 10GX, Permanent Yellow G3R-01, Hostaperm® Yellow H4G, Hostaperm® Yellow H3G, Hostaperm® Orange GR, Hostaperm® Scarlet GO, and Permanent Rubine F6B. The following pigments are available from Mobay: Quindo® Magenta, Indofast® Brilliant Scarlet, Quindo® Red R6700, Quindo® Red R6713, and Indofast® Violet. The following pigments are available from Sun Chemical: L74-1357 Yellow, L75-1331 Yellow, and L75-2577 Yellow. The following pigments are available from Columbian: Raven® 7000, Raven® 5750, Raven® 5250, Raven® 5000, and Raven® 3500. The following pigment is available from Sun Chemical: LHD9303 Black. Any other pigment and/or dye can be used that is useful in modifying the color of the UV curable ink. Additionally, the colorant can include a white pigment such as titanium dioxide, or other inorganic pigments such as zinc oxide and iron oxide.


The components of the photo curable ink can be selected to give the ink good ink jetting performance. Besides the photo curable binder, photo reactive photo active agents, and the colorant, the photo curable ink can also include a liquid vehicle. Liquid vehicle formulations that can be used in the photo curable ink can include water and one or more co-solvents present in total at from 1 wt % to 50 wt %, depending on the jetting architecture. Further, one or more non-ionic, cationic, and/or anionic surfactant can be present, ranging from 0.01 wt % to 20 wt %. In one example, the surfactant can be present in an amount from 5 wt % to 20 wt %. The liquid vehicle can also include dispersants in an amount from 5 wt % to 20 wt %. The balance of the formulation can be purified water, or other vehicle components such as biocides, viscosity modifiers, materials for pH adjustment, sequestering agents, preservatives, and the like. In one example, the liquid vehicle can be predominantly water.


Classes of co-solvents that can be used can include organic co-solvents including aliphatic alcohols, aromatic alcohols, diols, glycol ethers, polyglycol ethers, caprolactams, formamides, acetamides, and long chain alcohols. Examples of such compounds include primary aliphatic alcohols, secondary aliphatic alcohols, 1,2-alcohols, 1,3-alcohols, 1,5-alcohols, ethylene glycol alkyl ethers, propylene glycol alkyl ethers, higher homologs (C6-C12) of polyethylene glycol alkyl ethers, N-alkyl caprolactams, unsubstituted caprolactams, both substituted and unsubstituted formamides, both substituted and unsubstituted acetamides, and the like. Specific examples of solvents that can be used include, but are not limited to, 2-pyrrolidinone, N-methylpyrrolidone, 2-hydroxyethyl-2-pyrrolidone, 2-methyl-1,3-propanediol, tetraethylene glycol, 1,6-hexanediol, 1,5-hexanediol and 1,5-pentanediol.


One or more surfactants can also be used, such as alkyl polyethylene oxides, alkyl phenyl polyethylene oxides, polyethylene oxide block copolymers, acetylenic polyethylene oxides, polyethylene oxide (di)esters, polyethylene oxide amines, protonated polyethylene oxide amines, protonated polyethylene oxide amides, dimethicone copolyols, substituted amine oxides, and the like. The amount of surfactant added to the formulation of this disclosure may range from 0.01 wt % to 20 wt %. Suitable surfactants can include, but are not limited to, liponic esters such as Tergitol™ 15-S-12, Tergitol™ 15-S-7 available from Dow Chemical Company, LEG-1 and LEG-7; Triton™ X-100; Triton™ X-405 available from Dow Chemical Company; LEG-1, and sodium dodecylsulfate.


Consistent with the formulation of this disclosure, various other additives can be employed to optimize the properties of the ink composition for specific applications. Examples of these additives are those added to inhibit the growth of harmful microorganisms. These additives may be biocides, fungicides, and other microbial agents, which are routinely used in ink formulations. Examples of suitable microbial agents include, but are not limited to, NUOSEPT® (Nudex, Inc.), UCARCIDE™ (Union carbide Corp.), VANCIDE® (R.T. Vanderbilt Co.), PROXEL® (ICI America), and combinations thereof.


Sequestering agents, such as EDTA (ethylene diamine tetra acetic acid), may be included to eliminate the deleterious effects of heavy metal impurities, and buffer solutions may be used to control the pH of the ink. From 0.01 wt % to 2 wt %, for example, can be used. Viscosity modifiers and buffers may also be present, as well as other additives to modify properties of the ink as desired. Such additives can be present at from 0.01 wt % to 20 wt %.


Table A shows the composition of an example of a photo curable ink, e.g., UV LED curable ink, formulation in accordance with the present disclosure. The ink can be formulated by mixing these ingredients or by mixing other similar formulations. The pH of the ink can then be adjusted. In one example, the ingredients can be stirred for 30 minutes, and then aqueous potassium hydroxide can be added to adjust the pH to 7 to 12, or in one example, about 8.5. It is noted that though water concentrations are listed as “balance,” it is understood that the balance of components could included other liquid vehicle components or minor amounts of solids often present in inkjet ink compositions.












TABLE A







Component
Weight Percent









Photo reactive binder

1-20%




(UV reactive polymer)



Photo active agent
0.15-5%



(sensitizer or photo initiator)



Co-photo initiator
 *0-10%



Synergist

*0-5%




Surfactant

0-20%




Anti-kogation agent
  0-5%



Pigment
0.5-10%



Organic Co-solvent
0.1-50%



Water
balance







*As noted, when the photo active agent is included as a sensitizer, the co-photo initiator is at greater than 0%. When the photo active agent is included as a photo initiator, the synergist is at greater than 0%. All three components can likewise be present, namely the photo active agent, the co-photo initiator, and the synergist.






The photo curable ink can be used to print on a broad selection of substrates including untreated plastics, flexible as well as rigid, porous substrates such as paper, cardboard, foam board, textile, and others. The ink has a good adhesion on a variety of substrates. The photo curable ink also has a good viscosity, enabling good printing performances and enables the ability to formulate inks suitable for inkjet application. In some examples, the ink can be formulated for thermal inkjet printing. The photo curable ink composition of the present disclosure enables high printing speed and is very well suited for use in digital inkjet printing.


The photo active agents of the present disclosure can be stable in aqueous environments at pH from 7 to 12 or higher. Thus, the photo curable ink can be formulated to have a pH from 7 to 12 or higher. In some examples, the photo curable ink can have a pH of 8 or higher. In one specific example, the photo curable ink can have a pH of 8.5.


The present disclosure also extends to a method of making a photo curable ink. The method is shown in FIG. 2 and can include mixing 210 a photo reactive binder; a co-photo initiator, a synergist, or combination thereof; a colorant; and a liquid vehicle including co-solvent and water with a photo active agent including diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine. The photo curable ink can be UV curable, and in one specific example, UV LED curable. In one example, the method can also include adjusting the pH of the ink to be from 7 to 12. In another example, the method can include adjusting the pH of the ink to be 8 or higher.


It is to be understood that this disclosure is not limited to the particular process steps and materials disclosed herein because such process steps and materials may vary somewhat. It is also to be understood that the terminology used herein is used for the purpose of describing particular examples only. The terms are not intended to be limiting because the scope of the present disclosure is intended to be limited only by the appended claims and equivalents thereof.


It is noted that, as used in this specification and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise.


As used herein, “photo active agent” refers to materials that participate in the initiation of photo polymerization, particularly materials that act as a photo initiator or a sensitizer for a photo initiator. The photo active agents disclosed herein can be used either as a photo initiator or as a sensitizer for another photo initiator. In some systems, the photo active agent can act as both a photo initiator and a sensitizer.


As used herein, “UV curable” refers to compositions that can be cured by exposure to ultraviolet light from any UV source such as a mercury vapor lamp, UV LED source, or the like. Mercury vapor lamps emit high intensity light at wavelengths from 240 nm to 270 nm and 350 nm to 380 nm. “LED curable” refers to compositions that can be cured either by ultraviolet light from an ultraviolet LED. Ultraviolet LEDs emit light at specific wavelengths. For example, ultraviolet LEDs are available at 365 nm and 395 nm wavelengths, among others. The term “photo curable” refers generally to compositions that can be cured by exposure to light from any wavelength suitable for the composition being cured. Typically, the photo curable composition will be UV curable, and in some cases UV LED curable.


As used herein, “liquid vehicle” or “ink vehicle” refers to a liquid fluid in which colorant is placed to form an ink. A wide variety of ink vehicles may be used with the systems and methods of the present disclosure. Such ink vehicles may include a mixture of a variety of different agents, including, surfactants, solvents, co-solvents, anti-kogation agents, buffers, biocides, sequestering agents, viscosity modifiers, surface-active agents, water, etc.


As used herein, “colorant” can include dyes and/or pigments.


As used herein, “dye” refers to compounds or molecules that absorb electromagnetic radiation or certain wavelengths thereof. Dyes can impart a visible color to an ink if the dyes absorb wavelengths in the visible spectrum.


As used herein, “pigment” generally includes pigment colorants, magnetic particles, aluminas, silicas, and/or other ceramics, organo-metallics or other opaque particles, whether or not such particulates impart color. Thus, though the present description primarily exemplifies the use of pigment colorants, the term “pigment” can be used more generally to describe not only pigment colorants, but other pigments such as organometallics, ferrites, ceramics, etc. In one specific example, however, the pigment is a pigment colorant.


As used herein, “ink-jetting” or “jetting” refers to compositions that are ejected from jetting architecture, such as ink-jet architecture. Ink-jet architecture can include thermal or piezo architecture. Additionally, such architecture can be configured to print varying drop sizes such as less than 10 picoliters, less than 20 picoliters, less than 30 picoliters, less than 40 picoliters, less than 50 picoliters, etc.


As used herein, the term “substantial” or “substantially” when used in reference to a quantity or amount of a material, or a specific characteristic thereof, refers to an amount that is sufficient to provide an effect that the material or characteristic was intended to provide. The exact degree of deviation allowable may in some cases depend on the specific context.


As used herein, the term “about” is used to provide flexibility to a numerical range endpoint by providing that a given value may be “a little above” or “a little below” the endpoint. The degree of flexibility of this term can be dictated by the particular variable and determined based on the associated description herein.


As used herein, a plurality of items, structural elements, compositional elements, and/or materials may be presented in a common list for convenience. However, these lists should be construed as though each member of the list is individually identified as a separate and unique member. Thus, no individual member of such list should be construed as a de facto equivalent of any other member of the same list solely based on their presentation in a common group without indications to the contrary.


Concentrations, amounts, and other numerical data may be expressed or presented herein in a range format. It is to be understood that such a range format is used merely for convenience and brevity and thus should be interpreted flexibly to include not only the numerical values explicitly recited as the limits of the range, but also to include individual numerical values or sub-ranges encompassed within that range as if each numerical value and sub-range is explicitly recited. As an illustration, a numerical range of “about 1 wt % to about 5 wt %” should be interpreted to include not only the explicitly recited values of about 1 wt % to about 5 wt %, but also include individual values and sub-ranges within the indicated range. Thus, included in this numerical range are individual values such as 2, 3.5, and 4 and sub-ranges such as from 1-3, from 2-4, and from 3-5, etc. This same principle applies to ranges reciting only one numerical value. Furthermore, such an interpretation should apply regardless of the breadth of the range or the characteristics being described.


EXAMPLES

The following illustrates several examples of the present disclosure. However, it is to be understood that the following are only illustrative of the application of the principles of the present disclosure. Numerous modifications and alternative compositions, methods, and systems may be devised without departing from the spirit and scope of the present disclosure. The appended claims are intended to cover such modifications and arrangements.


Example 1—Synthesis of TPO Chloride (2)

A mixture of 5.0 grams (14.3 mmol) of commercially available TPO (1) in 100 mL of chloroform was cooled to 0° C. under N2 and mechanical stirring. AlCl3 (12.0 grams, 85.8 mmol) and paraformaldehyde (1.3 grams, 43 mmol) was added portion-wise. After the completion of the addition, the mixture was heated to 60° C. for 6 hours. Then, the reaction mixture was cooled to room temperature and poured into ice-water. The mixture was extracted with dichloromethane (3×100 mL). The combined organic layers were washed by water and brine and then dried over sodium sulfate. Evaporation of solvent gave a residue, which was further purified by flash chromatography using hexanes/ethyl acetate (100% hexanes to 50% hexanes in ethyl acetate) as eluents, giving rise to 3.7 grams (65 wt %) of the desired TPO chloride (2).


Example 2—Synthesis of TPO Di-Chloride (4)

A mixture of 5.0 grams (14.3 mmol) of commercially available TPO (1) in 100 mL of chloroform was cooled to 0° C. under N2 and mechanical stirring. AlCl3 (12.0 grams, 85.8 mmol) and paraformaldehyde (2.6 grams, 86 mmol) was added portion-wise. After the completion of the addition, the mixture was heated to 60° C. for 12 hours. Then, the reaction mixture was cooled to room temperature and poured into ice-water. The mixture was extracted with dichloromethane (3×100 mL). The combined organic layers were washed by water, brine, and then dried over sodium sulfate. Evaporation of solvent gave a residue, which was further purified by flash chromatography using hexanes/ethyl acetate (100% hexanes to 50% hexanes in ethyl acetate) as eluents, giving rise to 3.8 grams (60 wt %) of the desired TPO-dichloride (4).


Example 3—Synthesis of Water Soluble Photo Initiator I

To a solution of TPO chloride (2) (3.97 grams, 10 mmol) in 150 mL of acetonitrile was added potassium carbonate (1.55 grams, 11 mmol). To this mixture was added a solution of N-methyl-D-glucamine (3) (2.55 grams, 11 mmol) in 5 mL of DMF and 50 mL of ethanol. After the completion of the addition, the reaction mixture was stirred under reflux for 24 hours. Then, the reaction mixture was cooled to room temperature. The solid was filtered off by filtration and washed with ethyl acetate. The combined organic layers were washed by water, brine, and then dried over sodium sulfate. Evaporation of solvent gave a residue, which was further purified by flash chromatography using hexanes/ethyl acetate (100% CHCl3 to 10% methanol in CHCl3) as eluents, giving rise to 3.61 grams (65 wt %) of the desired water soluble photo initiator I.


Example 4—Synthesis of Water Soluble Photo Initiator II

To a solution of TPO di-chloride (4) (4.45 grams, 10 mmol) in 150 mL of acetonitrile was added potassium carbonate (3.10 grams, 22 mmol). To this mixture was added a solution of N-methyl-D-glucamine (3) (5.10 grams, 22 mmol) in 10 mL of DMF and 100 mL of ethanol. After the completion of the addition, the reaction mixture was stirred under reflux for 24 hours. Then, the reaction mixture was cooled to room temperature. The solid was filtered off by filtration and washed with ethyl acetate. The combined organic layers were washed by water, brine, and then dried over sodium sulfate. Evaporation of solvent gave a residue, which was further purified by flash chromatography using hexanes/ethyl acetate (100% CHCl3 to 10% methanol in CHCl3) as eluents, giving rise to 4.57 grams (60 wt %) of the desired water soluble photo initiator II.


Example 5—Photo Curable Ink 1

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 1.












TABLE 1







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819
0.3%



(co-photo initiator from BASF)



Thioxanthone derivative of PEG-600
0.5%



(sensitizer)



Water soluble TPO (photo initiator I)
0.5%



LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
69.2% 










Example 6—Photo Curable Ink 2

A photo curable inkjet ink is prepared by mixing the following components as shown in Table 2.












TABLE 2







Component
Weight Percent









UV reactive binder

5%




Thioxanthone derivative of PEG-600
0.25% 



(Sensitizer)



Water soluble TPO (photo initiator II)
0.5%



LEG-1 (surfactant)

1%




CT-211 (surfactant)
0.5%



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments

3%




2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
79.15% 










Example 7—Photo Curable Ink 3

A photo curable inkjet ink is prepared by mixing the following components as shown in Table 3.












TABLE 3







Component
Weight Percent









UV reactive binder
 10%



Thioxanthone derivative of PEG-600
0.25% 



(Sensitizer)



Water soluble TPO (photo initiator III)
0.5%



LEG-1 (surfactant)

1%




CT-211 (surfactant)
0.5%



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments

3%




2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
74.15% 










Example 8—Photo Curable Ink 4

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 4.












TABLE 4







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator IV)

1%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
68.7% 










Example 9—Photo Curable Ink 5

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 5.












TABLE 5







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator V)

3%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
66.7% 










Example 10—Photo Curable Ink 6

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 6.












TABLE 6







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator VI)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 11—Photo Curable Ink 7

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 7.












TABLE 7







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator VII)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 12—Photo Curable Ink 8

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 8.












TABLE 8







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator VIII)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 13—Photo Curable Ink 9

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 9.












TABLE 9







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator IX)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 14—Photo Curable Ink 10

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 10.












TABLE 10







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator X)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 15—Photo Curable Ink 11

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 11.












TABLE 11







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator XI)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 16—Photo Curable Ink 12

A photo (UV LED) curable inkjet ink is prepared by mixing the following components as shown in Table 12.












TABLE 12







Component
Weight Percent









UV reactive binder
 15%



Irgacure ® 819 (co-photo initiator from
0.3%



BASF)



Thioxanthone derivative of PEG-600
0.5%



(Sensitizer)



Water soluble TPO (photo initiator XII)

5%




LEG-1 (surfactant)

1%




Surfynol ® CT-211

1%




(surfactant from Air Products)



Crodafos ® N3
0.5%



(anti-kogation agent from Croda Inc.)



Pigments
2.5%



2-hydroxyethyl-2-pyrrolidone (co-solvent)
 10%



Water
64.7% 










Example 17—Preparation of Photo Curable Ink 1

Photo Curable Ink 1 was prepared in accordance with the following steps. Notably, Photo Curable Inks 2-12 can be prepared using similar steps. As a first batch, a UV reactive binder was mixed with a minor portion of the total water (less than about 30 wt %) and the Irgacure 819 (co-photo initiator) at 60° C. for 5 minutes. As a second batch, 2-hydroxyethyl-2-pyrrolidone (co-solvent) was mixed with a larger portion of the total water content (less than about 70 wt %) and Crodafos® N3A, CT211, and LEG-1. The second batch was neutralized to a pH of 7.5 with KOH solution. The first batch and the second batch were then combined. Next, a thioxanthone derivative of PEG-600 (sensitizer) and the water soluble TPO (photo initiator I) were added and mixed well until they dissolved into mixture. The black pigment dispersion was then added to the admixture and the pH was adjusted to 8.5 using KOH solution. Notably, some additional water content is added during subsequent steps after combing the first and second batch, resulting in the water content listed in Table 1.


A print durability test was then conducted using Photo Curable Ink 1, as follows:


Sample Preparation

    • 1. The Photo Curable Ink was filled into a thermal inkjet pen.
    • 2. Fixer was printed from a different pen right before the ink was printed. The fixer formulation was a solution of calcium propionate, calcium nitrate tetrahydrate, Surfynol® SEF, tetraethylene glycol, and water.
    • 3. Two paper substrates were evaluated:
      • a. Offset coated paper—Sterling® Ultra Gloss (SUG), and
      • b. White Top coated Kraft Liner—RockTenn® 1 (RT1).
    • 4. The ink was immediately dried using a hot air blower for 5 seconds at 375° F.
    • 5. The dried ink was then immediately cured at a speed of 100 feet per minute using a 16 W/cm2 LED 395 nm wavelength (from Phoseon).


Durability Measurements


1. Wet Rub Test

    • 1. This test was performed after a pre-defined time period after printing and curing. For SUG it was performed 24 hours after printing, and for RT1 it was preformed 72 hours after printing.
    • 2. A taber test tool was used with Crockmeier cloth attached to the tip.
    • 3. The weight load was 350 gram.
    • 4. One (1) cycle was used for SUG, and two (2) cycles were used for RT1.
    • 5. The solution was Windex®;
    • 6. For the Wet Rub Test, the delta optical density (ΔOD) was measured before and after the rub; and
    • 7. In this test, the lower the ΔOD, the better the durability.
    • 8. A ΔOD<0.15 is considered to be a good score.


2. Immediate Rub Test

    • 1. Hand held rubbing tool was used to assess the smearing of dried and cured ink immediately after printing;
    • 2. The tool used was fit with a rubber tip that when pushed down to apply a constant pressure of 6 to 7 Ibs;
    • 3. For the Immediate Rub Test, the delta optical density (ΔOD) was measured before and after the rub.
    • 4. In this test, the lower the ΔOD, the better the durability.
    • 5. A ΔOD<0.15 is considered a good score.


The Results for the Wet Rub Test and the Immediate Rub Test are provided in Table 13. Notably, the black Photo Curable Ink was printed as described and tested both with and without curing on both papers (SUG and RT1).









TABLE 13







Results for Photo Curable Black Ink 1










With Curing
Without Curing












Wet Rub
Immediate Rub
Wet Rub
Immediate Rub


Paper
(ΔOD)
(ΔOD)
(ΔOD)
(ΔOD)





SUG
0.10
0.12
1.73
0.95


RTI
0.07
0.05
1.55
0.75









As can be seen in Table 13 above, the black Photo Curable Ink exhibited significantly better wet rub and immediate rub resistance after curing. The initial OD was 2.12 and 1.66 on SUG and RT1, respectively, and therefore a ΔOD of 0.10, for example, indicates that after rubbing the print, only 0.10 OD units were lost from the initial 2.12 OD measurement. Conversely, without curing, a ΔOD of 1.73 means that that the ink lost significant OD units from the initial 2.12 OD measurement. The durability improvement by curing is evident in both Wet Rub and Immediate Rub measurements, suggesting that the polymeric TPO based photo initiator package efficiently participated in the curing and crosslinking of the Photo Curable Ink.


While the present technology has been described with reference to certain examples, those skilled in the art will appreciate that various modifications, changes, omissions, and substitutions can be made without departing from the spirit of the disclosure. It is intended, therefore, that the disclosure be limited only by the scope of the following claims.

Claims
  • 1. A photo active agent, comprising diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine.
  • 2. The photo active agent of claim 1, having the structure:
  • 3. The photo active agent of claim 2, wherein the organic side group, R, includes an additional C1 to C5 water solubilizing group, a diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide group, an alkyl group, an alicyclic group, a tertiary amine group, or combination thereof.
  • 4. The photo active agent of claim 2, wherein the C1 to C5 water solubilizing group, A, includes hydroxyl, sulfonic acid, sulfonate, carboxylic acid, carboxylate, or polyethylene glycol having from 2 to 20 ether groups.
  • 5. The photo active agent of claim 1, having one of the following structures:
  • 6. A photo curable ink, comprising: a photo reactive binder;a photo active agent comprising diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine;a co-photo initiator, a synergist, or combination thereof;a colorant; anda liquid vehicle including co-solvent and water.
  • 7. The photo curable ink of claim 6, wherein the photo curable ink has a pH of 7 to 12, and the photo active agent is stable in the photo curable ink.
  • 8. The photo curable ink of claim 6, wherein the photo curable ink is photo curable using UV LED electromagnetic radiation.
  • 9. The photo curable ink of claim 6, wherein the photo active agent is a sensitizer, and the photo curable ink comprises the co-photo initiator.
  • 10. The photo curable ink of claim 6, wherein the photo active agent is a photo initiator, and the photo curable ink comprises the synergist.
  • 11. The photo curable ink of claim 6, wherein the photo active agent has the structure:
  • 12. The photo curable ink of claim 11, wherein the organic side group, R, includes a C1 to C5 water solubilizing group, a diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide group, an alkyl group, an alicyclic group, a tertiary amine group, or combination thereof.
  • 13. The photo curable ink of claim 11, wherein the C1 to C5 water solubilizing group, A, includes hydroxyl, sulfonic acid, sulfonate, carboxylic acid, carboxylate, or polyethylene glycol having from 2 to 20 ether groups.
  • 14. The photo curable ink of claim 6, wherein the photo active agent comprises one of the following structures:
  • 15. A method of making a photo curable ink comprising mixing a photo reactive binder; a co-photo initiator, a synergist, or combination thereof; a colorant; and a liquid vehicle including co-solvent and water with a photo active agent comprising diphenyl(2,4,6-trimethylbenzoyl)phosphine oxide modified with a tertiary amine having a water solubilizing group attached to the tertiary amine.
PCT Information
Filing Document Filing Date Country Kind
PCT/US2017/015789 1/31/2017 WO 00
Publishing Document Publishing Date Country Kind
WO2018/143928 8/9/2018 WO A
US Referenced Citations (3)
Number Name Date Kind
8119830 Schlueter Feb 2012 B2
20090169765 Nakamura et al. Jul 2009 A1
20160304734 Feng et al. Oct 2016 A1
Foreign Referenced Citations (5)
Number Date Country
107400144 Nov 2017 CN
0825201 Feb 1998 EP
2005307199 Nov 2005 JP
2015189639 Dec 2015 WO
2016122454 Aug 2016 WO
Non-Patent Literature Citations (4)
Entry
Wang et al, CN 107400144 Machine Translation, Nov. 28, 2017 (Year: 2017).
Benedikt et al., Highly efficient water-soluble visible light photoinitiators, Journal of Polymer Science Part A: Polymer Chemistry, vol. 54, Issue 4, pp. 473-479, 2016.
De Groot et al., Hydrophilic Polymeric Acylphospine Oxide Photoinitiators/Crosslinkers for in Vivo Blue-Light Photopolymerization, Bio Macromolecules, pp. 1271-1278, 2001.
International Search Report dated Oct. 19, 2017 for PCT/US2017/015789, Applicant Hewlett-Packard Development Company, L.P.
Related Publications (1)
Number Date Country
20190284417 A1 Sep 2019 US