Patent Application
20120115711
The present teachings relate to photocatalysts suitable for the adsorption and decomposition of organic molecules and environmental pollutants.
Photocatalysis relates to the phenomenon of transforming light energy into chemical energy. There are many materials, such as, SrTiO3, ZnO, ZnS, CdS, and TiO2, for example, that are considered to be efficient photocatalysts. TiO2 is characterized by having an energy band gap in the range between 3 and 3.2 eV. Light energy and the electron band gap energy of TiO2 are compatible or equivalent to ensure effective interaction of TiO2 material with UV light. TiO2, as a photo-active material, can therefore, efficiently utilize energy from sunlight and transcend in photocatalyzing chemical reactions. For instance, absorption of a photon by a TiO2 crystal enables excitation of an electron (e−) from the valence band to the conduction band if the photon energy, hv, equals or exceeds the band gap energy of TiO2. Simultaneously, an electron vacancy or a positively charged hole (h+) is generated in the valence band:
hv+TiO2→e−+h+
The electron-hole pair (e−+h+) that is created migrates to the TiO2 photocatalyst surface triggering redox reactions to take place with compounds adsorbed to the surface of the photo-catalyst and/or in the surrounding medium. For TiO2, photo-generated positive holes have redox potential of ca. 2.5 eV against normal hydrogen electrode (NHE), this potential allows production of hydroxyl radicals from water. Whereas, the redox potential of photo-generated electrons (−0.52 eV) is capable of reducing oxygen O2 to superoxide (O2−) or hydrogen peroxide (H2O2). Hence, there are sufficient redox potentials to initiate a chain of redox reactions that can lead to decomposition of most organic molecules.
Thus, because of its inherent photoactivity, TiO2 can be an efficient photocatalyst. A need exists, however, for a photocatalyst that can adsorb and decompose organic molecules and/or environmental pollutants. In particular, a need exists for a substrate that can be used with TiO2 to provide a photocatalyst that can efficiently adsorb and decompose organic molecules and/or environmental pollutants. Furthermore, a need exists for an economical and environmentally friendly technique for producing such a substrate.
Features and advantages of the present teachings will become apparent from the following description. This description, which includes drawings and examples of specific embodiments, provides a broad representation of the present teachings. Various changes and modifications to the teachings will become apparent to those skilled in the art from this description and by practice of the teachings.
The present teachings relate to a photocatalyst comprising TiO2 and activated carbon. The activated carbon can be produced from date pits. The activated carbon can have a porous surface that is particularly useful for attracting and holding pollutants flowing in air or water. TiO2 can be photoactive and can have the ability to trigger redox reactions. The photoactivity of TiO2 and its ability to trigger redox reactions and the adsorption ability of the activated carbon make the photocatalyst particularly suitable for adsorption and decomposition of organic molecules and/or environmental pollutants.
According to some embodiments, the activity and adsorption of activated carbon produced from date pits can be comparable to that of activated carbon produced from conventional precursor materials, such as wood, coal, or coconut shells. Date pits can provide a particularly ideal precursor for manufacturing activated carbon because of the high content of carbonaceous material in date pits. Date pits are generally removed during industrial processing of dates. Thus, date pits can be obtained in copious amounts with little cost, especially in parts of the world where dates are widely grown. According to some embodiments, date pits can provide an environmentally safe and economical carbonaceous precursor for manufacturing activated carbon.
The present teachings further relate to a method comprising contacting date pits with an acidic aqueous solution, to form treated date pits, and calcining the treated date pits under conditions to cause the treated date pits to thermally decompose and form activated carbon. According to one or more embodiments, an acidic aqueous solution can comprise a phosphoric acid solution. In some embodiments, the phosphoric acid solution can comprise a concentration of from about 1% to about 30% phosphoric acid. The treated date pits can be treated at a temperature of from about 80° C. to about 150° C., for a period of from about one hour to about twelve hours, to dry the treated date pits, prior to the calcining. The calcining can occur at a temperature of from about 300° C. to about 900° C. The calcining can be conducted under a nitrogen blanket to form a calcined product. The calcined product can be treated with carbon dioxide gas. In some embodiments, the activated carbon can be impregnated with titanium dioxide, to form an impregnated product. A precursor compound can be contacted with the impregnated compound to photocatalyze a chemical reaction.
In some embodiments, the present teachings provide a method for adsorbing organic molecules, pollutants, or both, by contacting the organic molecules, pollutants, or both, with a photocatalyst comprising the impregnated product.
In some embodiments, the present teachings provide a photocatalyst comprising the impregnated product.
In some embodiments, the present teachings provide activated carbon made from the method comprising contacting date pits with an acidic aqueous solution, to form treated date pits, and calcining the treated date pits under conditions to cause the treated date pits to thermally decompose and form activated carbon.
The accompanying drawings, which are incorporated into and constitute a part of the specification, illustrate specific embodiments of the invention, and taken in conjunction with the detailed description of the specific embodiments, serve to explain the principles of the invention.
The following detailed description serves to explain the principles of the present teachings. The present teachings are susceptible to modifications and alternative forms and are not limited to the particular forms disclosed herein. The present teachings cover modifications, equivalents, and alternatives.
According to various embodiments of the present teachings, a method is provided that comprises contacting date pits with an acidic aqueous solution, to form treated date pits, and calcining the treated date pits under conditions to thermally decompose the pits and form activated carbon. The acidic aqueous solution can comprise, for example, a phosphoric acid solution. The concentration of the acidic aqueous solution can comprise an acidic component present in an amount of from about 1% by weight to about 40% by weight, for example, from about 1% by weight to about 30% by weight, about 3% by weight to about 25% by weight, or from about 5% by weight to about 20% by weight. In an exemplary embodiment, the acidic aqueous solution comprises phosphoric acid present in an amount of from about 1% to about 30%, for example, from about 5% by weight to about 20% by weight.
According to one or more embodiments, the acidic aqueous solution can comprise a phosphoric acid (H3PO4) solution. In some embodiments, the phosphoric acid solution can comprise a concentration of from about 1% to about 30% phosphoric acid, for example, from about 5% to about 30%, from about 10% to about 20%, or from about 15% to about 25% phosphoric acid. In some embodiments, the phosphoric acid solution can comprise a concentration of about 5%, 10%, 15%, 20%, or 25% phosphoric acid. In some embodiments, other acids such as sulfuric acid, hydrochloric acid, and the like, can be used.
In some embodiments, the treated date pits are heated to a temperature of from about 80° C. to about 150° C., for a period of from about 1 hour to about 12 hours, to dry the treated date pits, prior to the calcining. The calcining can occur at a temperature of from about 200° C. to about 1,000° C., for example, from about 300° C. to about 900° C., from about 400° C. to about 800° C., or from about 500° C. to about 700° C. The calcining can be conducted under a nitrogen blanket. In some embodiments, the calcining is conducted under a nitrogen blanket to form a calcined product, and the method further can further comprise treating the calcined product with carbon dioxide gas.
For drying, the treated date pits can be treated at a temperature of from about 80° C. to about 150° C., for example, at a temperature of from about 85° C. to about 120° C., or from about 90° C. to about 100° C. The treated date pits can be dried for a period of from about one hour to about twelve hours, for example, from about two hours to about eight hours, from about three hours to about seven hours, or from about four hours to about six hours. In some embodiments, the treated date pits can be dried for about six hours at a temperature of about 120° C. Drying can take place at ambient pressure or at an elevated or reduced pressure.
The treated date pits can be calcined under conditions to cause the treated date pits to thermally decompose and form activated carbon. The treated product can be calcined in a manner familiar to those of skill in the art. In some embodiments, both a drying step and a calcination step can be carried out at the same time, together. In some embodiments, calcining can be carried out after drying to form activated carbon. The calcining can occur at a temperature of from about 300° C. to about 900° C., for example, at a temperature of from about 400° C. to 800° C. or at a temperature of from about 500° C. to 750° C. The calcining can be carried out for a period of time of from one hour to four hours, for example, from one hour to three hours or from one hour to two hours. The calcining can be conducted under a nitrogen blanket.
After calcining to form a calcined product, the calcined product can be treated with a gas, for example, with carbon dioxide gas. The gas treatment can be carried out at an elevated pressure, at a reduced pressure, or at ambient pressure. In some embodiments, the calcined product can be pulverized, granulated, screened, and/or otherwise treated to form a desired particle size and/or uniformity.
According to various embodiments, a photocatalyst can be made by impregnating the activated carbon made as described herein, with titanium dioxide, to form an impregnated product. A method can be provided for photocatalyzing a chemical reaction by contacting a precursor compound with the impregnated product. In some embodiments, a method is provided that comprises adsorbing organic molecules, pollutants, or both, by contacting the organic molecules, pollutants, or both, with the photocatalyst.
In some embodiments, the photocatalyst can be made by first preparing activated carbon using date pits as a precursor material, and then impregnating the activated carbon with TiO2. The activated carbon can be prepared by contacting date pits with an acidic aqueous solution, to form treated date pits.
According to various embodiments, the photocatalyst can be prepared by mixing TiO2 with the activated carbon under conditions sufficient to impregnate the activated carbon with TiO2. According to some embodiments, the photocatalysts prepared by mixing TiO2 and the activated carbon can exhibit enhanced affinity to adsorption of organic molecules, such as alkanes and phenols. In some embodiments, TiO2 in a solution can be mixed with the activated carbon to form a mixture. According to some embodiments, the concentration of TiO2 in the mixture can be from about 10% by weight to about 50% by weight, for example, from about 15% to about 40%, or from about 20% to about 30%, by weight. The mixture can be heated for a period of from one to five hours, for example, from one to four hours, or from one to three hours, and then dried. The mixture can be heated at a temperature of from about 70° C. to about 200° C., for example, at a temperature of from about 80° C. to 100° C. or at a temperature of from about 90° C. to 150° C.
According to some embodiments, the photocatalyst can comprise TiO2 particles having one or more sizes, and/or one or more polymorph forms. Examples of TiO2 products that can be used include those available from National Titanium Dioxide Company, Ltd. (Yanbu Al-Sinaiyah, Saudi Arabia), for example, as described in U.S. patent application Ser. No. 12/584,699, filed Sep. 10, 2009, which is incorporated herein in its entirety by reference. The TiO2 can have an average particle size of from about 0.005 μm to 1 μm, for example, from 0.005 μm to 0.75 μm, from 0.01 μm to 0.6 μm, from 0.1 μm to 0.5 μm, from 0.2 μm to 0.4 μm, or about 0.3 μm. According to various embodiments, any suitable crystalline polymorph of TiO2 can be used. In some embodiments, TiO2 in rutile and/or anatase form can be used. According to some embodiments, the TiO2 particles can be doped with one or more cationic and/or anionic species. Exemplary dopants that can be used include, but are not limited to, Na+, Cl−, and Al3+. According to some embodiments, prior to mixing with the activated carbon, the TiO2 can have a surface acidity of from about pH 3.6 to about pH 12.8, for example, from about pH 3.8 to about pH 10.5, or from about pH 4.0 to about pH 7.7.
In addition to methods, the present teachings also provide impregnated products, for example, made by the methods described herein, activated carbon made from the methods described herein, and photocatalysts made by the methods described herein.
According to various embodiments, a photocatalyst can comprise titanium dioxide (TiO2) and activated carbon that is produced from date pits. Table 1 shows approximate values of date pit constituents. As shown in Table 1, date pits can comprise a high content of carbonaceous material.
The date pits can, for example, be immersed in the acidic aqueous solution for a period of about one hour to about twenty fours hours, for example, for about eight hours to about fifteen hours, or from about ten hours to about twenty hours.
Finely divided TiO2 can be used to impregnate the carbonaceous, soaked, dried, and calcined date pit material. Table 2 below shows exemplary TiO2 materials (Samples Nos. 1-15) that can be used to form the photocatalysts of the present teachings. Table 2 also shows corresponding properties of each of the exemplary TiO2 materials.
The present teachings are further illustrated with reference to the following examples which are intended to exemplify, not limit, the present teachings.
To examine the effectiveness of photocatalysts prepared in accordance with the present teachings, three experimental setups were used. The first setup was a fixed bed reactor 10 comprising an open flow system that operates as shown in the flowchart depicted in
The second setup, like the first setup, comprises a fixed bed reactor 20. Unlike the second setup, however, the second setup comprises a closed flow system. After the product stream is analyzed by GC-MS equipment 14, it is recirculated through photocatalysis reactor 12 (closed system), as shown in
Date pits were immersed overnight in an aqueous solution comprising 5% H3PO4, then removed, and dried for six hours at 120° C. The treated date pits were then calcined for three hours at 850° C. in the presence of nitrogen, producing a sample of activated carbon. The produced sample of activated carbon had a surface area of 665 m2/g. Two grams of the activated carbon sample were purged with 1% ethane/air gas at a flow rate of 0.1 ml/min to test its affinity as an efficient adsorbent. As shown in Table 3, ethane was not detected in the effluent stream for up to about 300 minutes. As such, it was determined that the activated carbon sample was an efficient adsorbent.
An activated carbon sample was prepared by a method similar to that described in Example 1, except that an aqueous solution comprising 10% H3PO4 was used, instead of a solution of 5% H3PO4. The activated carbon sample was tested for adsorption affinity to a phenol compound. A sample aqueous medium was prepared by mixing 40 ppm phenol aqueous solution with the activated carbon sample. A second aqueous medium containing a mixture of 40 ppm phenol aqueous solution and commercial activated carbon was also prepared, for comparison with the sample aqueous medium. The sample aqueous medium, the second aqueous medium, and a reference solution containing 40 ppm phenol solution were incubated in the dark (in the absence of UV light). Measurement readings using UV/VIS spectrophotometer were taken before and after incubation to monitor the presence of phenol in the aqueous medium, and the results are shown in Table 4.
As shown in Table 4, phenol adsorption of UV/VIS light between initial and final readings decreased. This can be explained by adsorption of phenol molecules by the activated carbon.
Activity of Catalysts when Tested in Closed Loop Photocatalysis System
Activated carbon samples were prepared by the method described in Example 1. Each of TiO2 Sample Nos. 3, 5, 6, and 10 were loaded into a respective activated carbon sample. A closed loop cycle reactor system, as shown in
Reaction of Methane with Light Using Open Reactor System
An activated carbon sample was prepared by the same method described in Example 3, except that calcination was conducted in the presence of CO2. Each of TiO2 Sample Nos. 3, 5, 12, and 14 were loaded into a respective activated carbon sample. This time the photocatalysis reaction of methane was carried out in an open reactor system, as shown
Activated carbon was prepared by the same method described in Example 4. Each of TiO2 Sample Nos. 3, 4, 6, and 10 were loaded into a respective activated carbon sample. Photocatalytic degradation of phenol under sunlight was observed, using the batch reactor system, shown in
Activated carbon was prepared by the same method described in Example 5. Each of TiO2 Sample Nos. 3, 4, 6, and 10 were loaded into a respective activated carbon sample. Photocatalytic degradation of phenol under sunlight was observed, using the batch reactor system, shown in
While the present teachings have been described in terms of exemplary embodiments, it is to be understood that changes and modifications can be made without departing from the true scope of the present teachings.
This application is a divisional of U.S. patent application Ser. No. 12/725,010, filed Mar. 16, 2010, which is incorporated herein in its entirety by reference.