Patent Application
20240216901
The present disclosure relates generally to reactor systems having at least one light source and reactor cells, each including an optically transparent enclosure and one or more plasmonic photocatalysts on a catalyst support disposed within the enclosure.
Industrial processes depend extensively on heterogeneous catalysts for chemical production and mitigation of environmental pollutants. These processes often rely on metal nanoparticles dispersed into high surface area support materials to both maximize catalytically active surface area and for the most cost-effective use of the catalysts (such as palladium, platinum, ruthenium, or rhodium). The catalytic processes utilizing transition metal nanoparticles are often energy intensive, relying on high temperatures and pressures to maximize catalytic activity. Thus, there remains a need for an efficient and cost-effective catalytic system.
The inventors have found efficient reactor systems that utilize an artificial or natural light source. The reactor systems of the disclosure can be designed to maximize absorption of one or more target wavelengths and/or catalyze a desired chemical reaction. As a result, the reactor systems disclosed herein may be cost effective and environmentally sustainable solutions for many current industrial processes.
Thus, in one aspect, the present disclosure provides a reactor system that includes a housing and at least one reactor cell disposed within an interior of the housing. The at least one reactor cell comprising an enclosure and a plasmonic photocatalyst on a catalyst support disposed within the at least one enclosure, wherein the enclosure is optically transparent and comprises at least one input for a reactant to enter the at least one cell and at least one output for a reformate to exit the at least one cell. When at least one light source is applied, the reactor cell is configured to transform the reactant into the reformate.
In another aspect, the present disclosure provides a solar concentrator and a photocatalytic reactor cell positioned relative to the solar concentrator to increase an incidence of electromagnetic radiation on the photocatalytic reactor cell.
In yet another aspect, the present disclosure provides a method for transforming at least one reactant into at least one reformate. The method includes (a) distributing at least one reactant into a plurality of reactor cells disposed within a housing, where each reactor cell comprises an optically transparent enclosure and a plasmonic photocatalyst on a catalyst support disposed within the optically transparent enclosure, (b) illuminating, via at least one light source, an interior of the housing to cause the plurality of reactor cells to transform at least one reactant into at least one reformate, and (c) accumulating the at least one reformate from the plurality of reactor cells.
The accompanying drawings are included to provide a further understanding of the methods and devices of the disclosure, and are incorporated in and constitute a part of this specification. The drawings are not necessarily to scale, and sizes of various elements may be distorted for clarity and/or illustrated as simplistic representations in order to promote comprehension. The drawings illustrate one or more embodiment(s) of the disclosure, and together with the description, serve to explain the principles and operation of the disclosure.
Before the disclosed systems and methods are described, it is to be understood that the aspects described herein are not limited to specific embodiments, apparatus, or configurations, and as such can, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular aspects only and, unless specifically defined herein, is not intended to be limiting.
Throughout this specification, unless the context requires otherwise, the word “comprise” and “include” and variations (e.g., “comprises,” “comprising,” “includes,” “including”) will be understood to imply the inclusion of a stated component, feature, element, or step or group of components, features, elements or steps but not the exclusion of any other component, feature, element, or step or group of components, features, elements or steps.
As used in the specification and the appended claims, the singular forms “a,” “an” and “the” include plural referents unless the context clearly dictates otherwise.
As used herein, the term “coupling” includes physical, electronic, thermal, or optical coupling of one element to another element.
Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another aspect includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint.
All percentages, ratios and proportions herein are by weight, unless otherwise specified. A weight percent (weight %, also as wt %) of a component, unless specifically stated to the contrary, is based on the total weight of the composition in which the component is included (e.g., on the total amount of the catalyst material).
In view of the present disclosure, the processes and active materials described herein can be configured by the person of ordinary skill in the art to meet the desired need. In general, the disclosed systems, methods, and apparatus provide improvements in photocatalysis processes and materials. In general, the present disclosure provides a reactor system that includes a housing having an interior surface that may be at least partially reflective. The reactor system also includes at least one reactor cell disposed within an interior of the housing. The at least one reactor cell includes an enclosure and a plasmonic photocatalyst on a catalyst support disposed within the at least one enclosure. The enclosure of the cell is optically transparent and includes at least one input for a reactant to enter the at least one cell and at least one output for a reformate to exit the at least one cell. The reactor system further includes at least one light source, which may be disposed within the interior of the housing and/or external to the housing.
In general, the reactor system is designed to allow for illumination of the reactor cells with a light source, which itself may be comprised of one or more individual light sources. One embodiment of the reactor system of the disclosure is shown in cross-sectional view in
In one embodiment, the reactor fittings 240 may comprise a reactor fluid distributor (for input) and a reactor fluid accumulator (for output). Any reactor fluid distributor or accumulator known in the art might be used. For example, the reactor fluid distributor or accumulator may be similar to those disclosed in U.S. Pat. No. 4,788,040 (incorporated by reference herein), where the orifices of the reactor fluid distributor and accumulator will match to the arrangement of the reactor cells. In some embodiments, the interior surfaces (i.e. facing the reactor cells) of the reactor fluid distributor and/or accumulator may be reflective.
In one embodiment, the at least one light source may be elongated and arranged coaxially along a central long axis of the housing. In further embodiments, the at least one light source may include at least one LED, metal halide bulb, high pressure sodium bulb, xenon lamp, incandescent bulb, fluorescent bulb, halogen bulb, HID, laser or combination thereof. In a further embodiment, the at least one light source may include at least one corn cob LED bulb having a plurality of LEDs arranged along its length.
In another embodiment, the at least one reactor cell may be elongated and may have a circular cross-section. In this embodiment, the at least one reactor cell may be arranged parallel to or even coaxial with the at least one light source. For example, in a further embodiment, the at least one light source may be arranged coaxially in the housing and the at least one reactor cell includes a plurality of reactor cells arranged surrounding the at least one light source.
In one embodiment, the housing has a circular or a polygonal cross-section. In one embodiment, the housing may have an inner diameter ranging from about 12 cm to about 128 cm. The housing may further have an inner diameter ranging from about 24 cm to about 72 cm. Each of the plurality of reactor cells has a diameter ranging from about 2 cm to about 4 cm, according to one embodiment. The plurality of reactor cells ranges in number from 12 cells to 24 cells, for example.
In another embodiment, the housing may have an inner diameter ranging from about 12 cm to about 18 cm. As shown in
In one embodiment, shown in
In another embodiment, the reactor system has a housing with an interior surface coupled to at least one light source. The reactor system further has at least one reactor cell disposed within an interior of the housing. The at least one reactor cell includes an enclosure and a plasmonic photocatalyst on a catalyst support disposed within the at least one enclosure. The enclosure is optically transparent and includes at least one input for a reactant to enter the at least one reactor cell and at least one output for a reformate to exit the at least one reactor cell. The reactor system may include at least one shaft having a reflective exterior surface that is disposed within the housing. In one embodiment, the at least one shaft is arranged coaxially within the housing.
In some embodiments, the light source is a solar light source. For example, the light source may include electromagnetic radiation from the sun, another star, or any other light-emitting celestial body. In such a case, the reactor system may comprise a solar concentrator to provide light energy to a photocatalytic reactor cell, which may be part of a reactor system comprising many such photocatalytic reactor cells.
A reactor system utilizing a solar light source may comprise a solar concentrator, such as a reflector or refractor, and a photocatalytic reactor cell positioned relative to the solar concentrator to increase an incidence of electromagnetic radiation on the photocatalytic reactor cell. According to one example, the solar concentrator comprises a reflector, such as a parabolic mirror trough, a parabolic dish, a Fresnel reflector, a Compact Linear Fresnel Reflector (CLFR), a solar power tower, a flat plate collector, an evacuated tube collector, or another type of reflector. According to another example, the solar concentrator comprises a refractor, such as a lens (e.g. a Fresnel lens).
While
As an alternative to the parabolic mirror trough 800 illustrated in
As another alternative, the solar concentrator may comprise a Fresnel reflector, where the photocatalytic reactor cell is positioned to be substantially aligned along its central axis to a focal line of the Fresnel reflector. The Fresnel reflector may comprise a Compact Linear Fresnel Reflector (CLFR), for example.
As yet another example, the solar concentrator may comprise a solar power tower configured to receive focused electromagnetic radiation from an array of movable reflectors. In such a configuration, the photocatalytic reactor cell is positioned in the solar power tower at a focal point of the array of movable reflectors, according to one embodiment.
Other solar concentrator embodiments utilizing reflectors may also be used. A flat plate collector and/or an evacuated tube collector may possibly be used in some implementations.
As an alternative to a reflector implementation for the solar concentrator, a refractor may be used. For example, the solar concentrator may comprise a refractive lens, with the photocatalytic reactor cell positioned at a focal point of the refractive lens. For example, the solar concentrator may comprise a Fresnel lens, where the photocatalytic reactor cell is positioned at a focal point of the Fresnel lens.
In the above-described embodiments, the particular solar concentrating and/or focusing elements, such as the parabolic mirror trough 800 and others, may constitute a housing or at least a portion of the housing, as otherwise described herein. As an alternative, such solar concentrating and/or focusing elements may reside within a separate housing, such as one that is at least partially optically transparent.
For each of the solar light source embodiments described above, the solar concentrator may be advantageously oriented to substantially maximize an intensity of electromagnetic radiation incident normal to the solar concentrator. In one embodiment, the length of the solar concentrator is aligned along a north-south orientation, and the reactor system may further comprise a computer-controlled solar tracking system to orient the solar concentrator to maintain an optimized angle of incidence of the electromagnetic radiation to the solar concentrator. In general, any of the solar concentrator alternatives described above may be controlled to track motion of the sun (or other light source) to substantially maximize an intensity of electromagnetic radiation incident normal to the solar concentrator.
For at least some of the solar light source embodiments described above, the photocatalytic reactor cell may advantageously have at least a portion of an interior surface of the enclosure be reflective (e.g. mirrored) in order to reflect received light back into the catalyst support 120 (see, e.g.,
While several solar light source implementations for a reactor have been described, others are possible and are intended to be within the scope of the appended claims. Moreover, the embodiments described above may have applications with light sources other than the sun, including both natural and artificial (i.e. electric) light sources.
As noted above, the reactor system comprises one or more reactor cells. The reactor cells of the disclosure comprise an optically transparent enclosure comprising at least one input and at least one output; and one or more plasmonic photocatalysts on a catalyst support disposed within the enclosure. Typically, the plasmonic photocatalyst comprises a catalyst coupled to a plasmonic material, such as through a physical, electronic, thermal, or optical coupling. The reactor cells of the disclosure are configured, upon application of a light source, to transform at least one reactant into at least one reformate.
In traditional fixed bed reactors, the catalyst beds are not optically transparent (i.e., the light does not penetrate the catalyst bed). In contrast, according to some embodiments of the disclosure, at least the support is optically transparent. In other embodiments, the reactor cells of the disclosure additionally or alternatively comprise an enclosure that is optically transparent. In some embodiments, the optically transparent enclosure has at least 50% transmittance for a predetermined light wavelength. For example, in some embodiments, the optically transparent enclosure has between about 50% to about 100% transmittance for a predetermined light wavelength; or at least 55%, or at least 60%, or at least 70%, or at least 80%, or at least 90%, or at least 95%, or even at least 98% transmittance for a predetermined light wavelength.
Advantageously, the optically transparent enclosure according to some embodiments of the disclosure may have low thermal expansion. Thus, in one embodiment, the optically transparent enclosure comprises a material having less than about 1×10−4/° K linear coefficient of thermal expansion (CTE). In another embodiment, the optically transparent enclosure comprises a material having less than about 1×10−5/° K CTE; or less than about 5×10−6/° K CTE; or less than about 3×10−6/° K CTE; or even less than about 1×10−6/° K CTE. For example, some exemplary materials with suitable CTE values include, but are not limited to, borosilicate glass at 3.2×10−6/° K, PYREX® glass at 3.2×10−6/° K, quartz at about 0.59×10−6/° K to about 9×10−6/° K, sapphire at 5.3×10−6/° K, and fused silica at 0.55×10−6/° K.
One of skill in the art will recognize than any material having the desired transmittance for a predetermined light wavelength (or range of wavelengths) and/or coefficient of thermal expansion (CTE) may be used. In some embodiments, the optically transparent enclosure comprises glass, borosilicate glass, quartz, fused quartz, aluminosilicate glass, lithium-aluminosilicate glass, sapphire, or combinations thereof.
In one embodiment, the optically transparent enclosure of the reactor cell is optically transparent on all sides of the enclosure. But one of skill in the art would appreciate that, in one embodiment, the optically transparent enclosure may not be optically transparent on all sides of the enclosure. For example, the outer cavity of the optically transparent enclosure may comprise a reflective surface facing the central cavity (which may be optically transparent).
The reactor cells of the disclosure also require one or more plasmonic photocatalysts comprising a catalyst coupled to a plasmonic material, such as through a physical, electronic, thermal, or optical coupling. Without being bound by theory, the plasmonic material is believed to act as an optical antenna capable of absorbing light due to the unique interaction of light with plasmonic materials and, as a result, generates a strong electric field on and near the plasmonic material (i.e., as a result of collective oscillation of electrons within the plasmonic material). This strong electric field on or near the plasmonic material allows for coupling between the catalyst and the plasmonic material, even when the catalyst and the plasmonic material are separated by distances of up to about 20 nm or more.
In general, the plasmonic material may be any metal, metal alloy, metalloid element, or its alloy. In some embodiments, the plasmonic material of the disclosure is selected from gold, gold alloy, silver, silver alloy, copper, copper alloy, aluminum, or aluminum alloy. In the present disclosure the term “alloys” is intended to cover any possible combination of metals. For example, the alloys may be binary alloys such as AuAg, AuPd, AgPd, AuCu, AgCu, etc., or they may be ternary alloys, or even quaternary alloys.
In some embodiments, the plasmonic material of the disclosure comprises an oxide shell surrounding a non-oxidized core. In one or more embodiments, the oxide shell may be a natural/native oxide shell that forms upon a metal or alloy's exposure to air or water. For example, a copper plasmonic material may possess a copper oxide (e.g., CuO or Cu2O) shell surrounding a copper core, or an aluminum plasmonic material may possess an aluminum oxide shell surrounding an aluminum core. In some embodiments, the oxide shell may be at least partially artificially produced, such as by artificially increasing the thickness of a native/natural oxide shell by appropriate chemical methods, or by chemically synthesizing, or otherwise depositing, an oxide material around a pre-formed plasmonic material. In some embodiments, the oxide shell may have a thickness of up to about 30 nm, or up to about 25 nm, or up to about 15 nm. In some embodiments, the oxide shell may have a thickness of at least about 0.5 nm, or at least 1 nm, or at least 1.5 nm. In some embodiments, the oxide shell has a thickness ranging from about 0.1 nm to about 5 nm; or from about 0.1 nm to about 30 nm; or from about 1 nm to about 5 nm; or from about 1 nm to about 30 nm.
One of skill in the art will recognize that the size, shape, and chemical structure of the plasmonic material will affect the absorption of one or more target wavelengths. Thus, the plasmonic material or materials may be designed to maximize absorption of a target wavelength (or a set or range of target wavelengths, such as to recognize the target wavelength but have the material absorb relatively less of other, non-target wavelengths. In another example, the plasmonic material of the disclosure may be designed to catalyze a desired chemical reaction. Thus, in some embodiments, the plasmonic material may have a plasmon resonant frequency, or optical absorption maximum, in the ultraviolet to infrared region of the electromagnetic spectrum. In some embodiments, the plasmonic material has a plasmon resonant frequency in the visible light spectrum (such as at a wavelength ranging from about 380 nm to about 760 nm).
In general, the catalyst material coupled to the plasmonic material may be any compound capable of catalyzing a desired reaction (e.g., even if it were not coupled to a plasmonic material). For example, the catalyst may be capable of oxidation and reduction chemistry, water or air pollution remediation reactions, NOX and N2O decompositions, catalyzing hydrogenation reactions such as acetylene hydrogenation, carbon dioxide conversion to carbon monoxide via the reverse water-gas shift reaction (which can be coupled with a hydrogenation to create hydrocarbons using FisherTropsch synthesis), and nitrogen activation chemistry, including the synthesis of ammonia. In some embodiments, the catalyst of the disclosure may be any metal or metalloid element, and any alloy, oxide, phosphide, nitride, or combination thereof of said elements. For example, the catalyst of the disclosure may comprise catalytically active palladium, platinum, ruthenium, rhodium, nickel, iron, copper, cobalt, iridium, osmium, titanium, vanadium, indium, or any combination thereof. The catalyst of the disclosure may comprise any alloy, oxide, phosphide, or nitride of catalytically active palladium, platinum, ruthenium, rhodium, nickel, iron, copper, cobalt, iridium, osmium, titanium, vanadium, or indium. In some embodiments, the catalyst of the disclosure comprises catalytically active iron or copper. In some embodiments, the catalyst of the disclosure may be intermetallic nanoparticles, core-shell nanoparticles, or semiconductor nanoparticles (e.g., Cu2O).
In some embodiments, the catalyst may be physically attached to the plasmonic material, while in other embodiments the catalyst may be separated by a small distance from the plasmonic material (but still coupled thereto, such as through a physical, electronic, thermal, or optical coupling). The separation may be either by empty space (i.e., a distinct physical separation) or the separation may be by the thin oxide layer discussed above. For example, the plasmonic material and the catalyst may be separated by a small distance when they are prepared via lithographic methods to have a distinct physical separation. In one or more embodiments, the small separation may be a distance of up to about 30 nm, or up to about 25 nm, or up to about 15 nm. In some embodiments, the separation may be at least about 0.5 nm, or at least 2 nm, or at least 5 nm, or at least 10 nm. In some embodiments, one or more catalysts may be physically attached to the surface of a single plasmonic material, which can increase the surface area available for reactions. In some embodiments, the catalyst may form a shell that surrounds the plasmonic material.
The plasmonic photocatalysts may have a diameter ranging from about 5 nm to about 300 nm. In some embodiments, the plasmonic photocatalyst of the disclosure may have a diameter ranging from about 10 nm to about 300 nm; or about 50 nm to about 300 nm; or about 80 nm to about 300 nm; or about 100 nm to about 300 nm; or about 5 nm to about 250 nm; about 10 nm to about 250 nm; or about 50 nm to about 250 nm; or about 80 nm to about 250 nm; or about 100 nm to about 250 nm; or about 5 nm to about 200 nm; about 10 nm to about 200 nm; or about 50 nm to about 200 nm; or about 80 nm to about 200 nm; or about 100 nm to about 200 nm; or about 80 nm to about 200 nm.
The reactor cells according to at least some embodiments also include one or more plasmonic photocatalysts dispersed onto a catalyst support. As with the enclosure, in some embodiments, the catalyst support has a low absorbance, and in particular, a low enough absorbance (for the particular radiation wavelength or wavelength range) so that the reactants are exposed to a sufficient amount of radiation to result in the desired catalytic effect for the particular reactor cell geometry in use.
One of skill in the art will recognize that any material having the desired absorbance or transmittance for a predetermined light wavelength (or set or range of wavelengths) may be used for the catalyst support. In some embodiments, the catalyst support of the disclosure comprises silica, quartz, fused quartz, glass, borosilicate glass, aluminosilicate glass, lithium-aluminosilicate glass, sapphire, diamond, or combinations thereof. The catalyst support may be in any form known in the art, such as in the form of beads, microporous beads, fibers, spheres, pellets, cylinders (hollow or otherwise), honeycombs, or symmetrical or asymmetrical tri-quadrulobes (for example, using extrusion or tableting methods). For example,
The plasmonic photocatalyst may be present on the catalyst support in any amount suitable for the desired use. For example, the plasmonic photocatalyst may be present on the catalyst support in an amount between about 0.01 wt % and about 30 wt %; or about 0.01 wt % and about 80 wt %; or about 10 wt % and about 80 wt %; or about 0.01 wt % and about 70 wt %; or about 10 wt % and about 70 wt %. In some embodiments, the plasmonic photocatalyst may be present on the catalyst support in an amount between about 0.01 vol % and about 30 vol %; or about 0.01 vol % and about 20 vol %; or about 10 vol % and about 50 vol %; or about 0.01 vol % and about 70 vol %; or about 10 vol % and about 70 vol %.
In some embodiments, the plasmonic photocatalyst may be present on the catalyst support as a thin coating on the outer surface of the support (e.g., as one or a few layers). In one or more embodiments, the plasmonic photocatalyst layer that is coated onto the support may be up to about 30 nm, or up to about 25 nm, or up to about 15 nm; or at least about 0.5 nm, or at least 2 nm, or at least 5 nm, or at least 10 nm; or between about 5 nm to about 300 nm; or about 10 nm to about 300 nm; or about 50 nm to about 300 nm; or about 80 nm to about 300 nm; or about 100 nm to about 300 nm; or about 5 nm to about 200 nm; about 10 nm to about 200 nm; or about 50 nm to about 200 nm; or about 80 nm to about 200 nm; or about 100 nm to about 200 nm; or about 80 nm to about 200 nm; or about 5 nm to about 100 nm; about 10 nm to about 100 nm; or about 50 nm to about 100 nm; or about 10 nm to about 50 nm; or about 1 nm to about 50 nm.
In some embodiments, the reactor cell comprises one plasmonic photocatalyst on the catalyst support disposed within the enclosure (e.g., one type of supported plasmonic photocatalyst would be disposed within the enclosure). In some embodiments, the reactor cell comprises two or more plasmonic photocatalysts on the catalyst support disposed within the enclosure (e.g., two or more different supported plasmonic photocatalysts would be disposed within the enclosure). Two or more plasmonic photocatalysts on the catalyst support may be provided, either mixed or in distinct layers. For example, each layer would have one type of supported plasmonic photocatalyst having a desired plasmon resonant frequency and/or a desired diameter. In a non-limiting example, one layer would absorb one desired wavelength range relative to other wavelengths, the next layer would absorb another wavelength range, and the final layer (e.g., an intermediate layer) would absorb other wavelengths, such as wavelengths outside the first and second wavelength ranges.
In general, the reactor cell is designed to allow for illumination of the plasmonic photocatalysts with a light source. One embodiment of the reactor cell of the disclosure is shown in cross-sectional view in
The size and shape of the enclosure of the reactor cell may be adapted to meet the desired need. In some embodiments, the enclosure has an inner diameter ranging from about 0.2 cm to about 10 cm; or about 0.5 cm to about 3 cm. In some embodiments, the enclosure has a length ranging from about 10 cm to about 2 m; or about 50 cm to about 1 m. The enclosure of the reactor cell may have a circular cross-section or a polygonal cross-section, for example.
As noted above, the reactor cell may further comprise one or more fittings (such as fittings 160 in
The reactor cell may further comprise one or more packing support elements (such as packing support elements 150 in
In some embodiments, the optically transparent enclosure further comprises an outer cavity and a central cavity arranged coaxially with the outer cavity, wherein the outer cavity contains the plasmonic photocatalyst on the catalyst support and the central cavity is configured to receive a light source or a thermal management feature. In some embodiments, the light source is disposed within the central cavity of the optically transparent enclosure. In some embodiments, the light source extends along or through a length of the enclosure. Any suitable light source may be used such as, but not limited to, LED, metal halide bulb, high pressure sodium bulb, xenon lamp, incandescent bulb, fluorescent bulb, halogen bulb, HID, laser or combination thereof. Natural light, such as solar light, may also be directed into the central cavity to serve as the light source. In some embodiments, the thermal management feature is disposed within the central cavity of the optically transparent enclosure. Any thermal management feature known in the art might be used. For example, the thermal management feature may include a fluid input coupled to a first end of the central cavity and a fluid output coupled to a second end of the central cavity such that fluid may flow through the reactor cell to add or remove heat from the reactor cell; or the thermal management feature may comprise a metal rod or metal wires configured for heat conduction.
In one alternative embodiment, neither the housing of the reactor system nor the enclosure of each reactor cell need be optically transparent. In this alternative embodiment, the reactor system comprises a housing and a plurality of reactor cells each having its own light source. Since, in this embodiment, each reactor cell has its own light source, the enclosure of each reactor cell need not be optically transparent, and may instead be reflective, in order to reflect light from the light source back into the interior of the enclosure. Each reactor cell may also include an input and an output, and each reactor cell includes at least one plasmonic photocatalyst on a catalyst support disposed within the enclosure, where the plasmonic photocatalyst comprises a catalyst coupled to a plasmonic material. The reactor system may further include a distributor for distributing at least one reactant into the plurality of reactor cells via the input of each reactor cell, and an accumulator for accumulating at least one reformate from the plurality of reactor cells via the output of each reactor cell.
Another aspect provides methods for using the reactor systems to transform reactants. Specifically, the disclosure provides methods for transforming at least one reactant into at least one reformate, the method comprising: adding at least one reactant into a reactor system of the disclosure; and illuminating, via the at least one light source, an interior of the reactor system and/or reactor cell(s).
In an alternative embodiment of the methods of the disclosure, the illuminating is from a light source external to the reactor system.
In some embodiments of the method, no external heating (e.g. from a dedicated heating source) is applied. In some embodiments, the methods further comprise externally heating the reactor cell. The external heating may be accomplished via the thermal management feature as described above, or via some other heating technique.
Representative methods of the disclosure include, but are not limited to, oxidation and reduction, water or air pollution remediation reactions, NOX and N2O decompositions, hydrogenation such as acetylene hydrogenation, carbon dioxide conversion, and nitrogen activation, including the synthesis of ammonia. Some of the representative chemical transformations include:
Thus, in some embodiments, the reactants are methane and water; or the reactants are methane and carbon dioxide; or the reactants are carbon monoxide and water; or the reactants are carbon dioxide and hydrogen gas; or the reactant is nitrous oxide; or the reactants are acetylene and hydrogen gas; or the reactants are hydrogen gas and nitrogen gas; or the reactants are carbon dioxide and hydrogen gas.
The methods of the disclosure may be performed at any suitable temperature. For example, in some embodiments, the methods of the disclosure are performed at a temperature ranging from about 100° ° C. to about 300° C.; or about 100° C. to about 250° C.; or about 100° C. to about 200° C.; or about 150° C. to about 300° C.; or about 150° ° C. to about 250° C.; or about 150° C. to about 200° C.; or about 200° C. to about 300° C.; or about 200° C. to about 250° C.; or about 180° ° C. to about 220° C.; or about 190° C. to about 210° C.; or about 20° C. to about 300° C.; or about 20° C. to about 250° C.; or about 20° C. to about 200° C.; or about 20° C. to about 150° C.; or about 20° C. to about 100° C.
The methods of the disclosure may be performed at any suitable pressure. For example, in some embodiments, the methods of the disclosure are performed at a pressure ranging from about 14 psi to about 300 psi, or about 14 psi to about 200 psi, or about 14 psi to about 100 psi, or about 14 psi to about 50 psi, or about 100 psi to about 300 psi, or about 100 psi to about 200 psi.
In the methods of the disclosure, the reactants might be introduced into the reactor system at any suitable temperature. In some embodiments, the reactant has temperature ranging from about 200° ° C. to about 300° C.; or about 200° C. to about 270° C.; or about 200° C. to about 250° C.; or about 230° C. to about 270° C., when introduced into the reactor cell.
It is understood that the examples and embodiments described herein are for illustrative purposes only and that various modifications or changes in light thereof will be suggested to persons skilled in the art and are to be incorporated within the spirit and purview of this application and scope of the appended claims. All publications, patents, and patent applications cited herein are hereby incorporated herein by reference for all purposes.
The present application is a continuation of and incorporates by reference U.S. patent application Ser. No. 16/625,527, filed on Dec. 20, 2019, which is a U.S. national phase application under 35 U.S.C. § 371 of International Application No. PCT/2018/039476, filed on Jun. 26, 2018, which claims priority to and incorporates by reference the entireties of the following U.S. patent applications: U.S. Provisional Patent Application No. 62/525,301, filed on Jun. 27, 2017, U.S. Provisional Patent Application No. 62/525,305, filed on Jun. 27, 2017, U.S. Provisional Patent Application No. 62/525,380, filed on Jun. 27, 2017, and U.S. Provisional Patent Application No. 62/586,675, filed on Nov. 15, 2017. In addition, the entireties of the following patent applications are incorporated by reference herein: International Patent Application No. PCT/US18/32375, filed on May 11, 2018, U.S. patent application Ser. No. 15/977,843, filed on May 11, 2018, and International Patent Application No. PCT/2018/039470, titled “Photocatalytic Reactor Cell,” filed on Jun. 26, 2018.
| Number | Date | Country | |
|---|---|---|---|
| 62586675 | Nov 2017 | US | |
| 62525301 | Jun 2017 | US | |
| 62525305 | Jun 2017 | US | |
| 62525380 | Jun 2017 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 16625527 | Dec 2019 | US |
| Child | 18432460 | US |