Patent Application
20150174569
The subject of the invention are photocatalytic titanium oxide(IV) coatings on the polymer surfaces activated with visible light, method for their preparation and their use. The polymer surfaces are selected from the group of polymers used in medical and food packaging, in particular polyurethane (PU), polycarbonate (PC), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE).
There has been a significant increase in the use of plastics in almost every field of human activity in recent years. The low price and simplicity of adaptation of materials to the requirements of a developing society is contributed to this particularly. Polymeric materials also play an increasingly important role in medicine, since the disposable medical equipment is made of these materials. The surface of the plastics is exposed to the formation of biofilm what is dangerous to health and what is one of the most important etiological contribution to the nosocomial infections. According to World Health Organization, the minimization of the nosocomial infections positively impacts on the patients' health as well as on the economic condition of medical facilities. The answer to the problem of nosocomial infections is to design new materials with potential antibacterial effect. The increase in resistance of pathogens to conventionally available antimicrobial agents requires exploration of other innovative solutions.
The answer to the problem is utilization of photocatalytic materials, particularly semiconductors, for example titanium oxide(IV), in photoinactivation of the bacteria. The present state of art discloses such applications, however, titanium oxide(IV) usually occurs in the form of powders, solutions or colloidal layers at mineral surfaces such as glass or metal (Chen, X., Mao, S. S, 2007, Chemical Reviews, 107, 2891-2959), what significantly reduces the possibility of its application.
The activation process of the polymer surfaces by low-temperature plasma technique is well known and described in the literature by Hegemann (D. Hegemann et al., Nuclear Instruments and Methods in Physics Research B 2003, 208, 281-286), Kasanen (J. Kasanen et al., 2009, J. Appl. Polym. Sci., 111, 2597-2606) and Vandencasteele (N. Vandencasteele et al., 2010, Journal of Electron Spectroscopy and Related Phenomena, 178-179, 394-408). The activation of the polymer surfaces changes their physical and chemical properties. As a result of the activation process, many oxygen-containing functional groups are generated at the surface of polymeric material in the presence of oxygen, such as hydroxyl group (—OH), carboxyl group (—COOH), carbonyl group (—C═O).
The methods of modifying of the material properties without the changes in volume by applying plasma treatment are also known. For instance the plasma treatment used for modifying the optical fiber cable is disclosed in patent application GB 2481891 A. The entire length of optical fiber is subjected to plasma treatment by moving it through the plasma furnace, thereupon the surface of plasma-treated optical fiber is modified becoming more susceptible to combining it with the target substance. The method allows for creation a layer of target substance adhering to the surface of optical fiber cable. The materials used in abovementioned example for the adhering layer formation are epoxy resins, polyamide and polyurethane. Inconvenience observed in the prior art relates to the difficulty in obtaining sustained coatings of titanium oxide(IV) on the polymer surfaces and their sensitization to the visible light range. Permanent immobilization of titanium oxide(IV) on the polymer surfaces provides new opportunities for the application of photocatalytic processes at TiO2, for example to photosterilize of various medical materials made of plastics.
The aim of the present invention is to provide sustained photocatalytic coatings of titanium oxide(IV) on the polymer surfaces, activated with visible or ultraviolet light, exhibiting high photocatalytic and photosterilizing activity and the method of their preparation. The present invention provides also new opportunities for the application of coatings according to the invention, a certain set of characteristics to the sterilization of various materials, such as medical catheters or food packaging.
The invention relates to the photocatalytic coatings of titanium oxide(IV) on the polymer surfaces activated with visible light, characterized by:
a) their application on organic substrate which is a polymeric material used in medicine, food and pharmaceuticals packaging, in particular selected from the group of: polyurethane (PU), polycarbonate (PC), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE).
b) coating of nanocrystalline titanium oxide(IV) or nanocrystalline titanium oxide(IV) surface-modified with organic compounds.
Preferably, nanocrystalline titanium oxide(IV) is surface-modified with organic compound selected from the group consisting of:
a) compound with Formula 1:
Preferably, organic compound is selected from the group consisting of: phthalic acid, 4-sulfophthalic acid, 4-amino-2-hydroxybenzoic acid, 3-hydroxy-2-naphthyl acid, salicylic acid, 6-hydroxysalicylic acid, 5-hydroxysalicylic acid, 5-sulfosalicylic acid, 3,5-dinitrosalicylic acid, 1,4-dihydroxy-1,3-benzenedisulfonic disodium salt, gallic acid, pyrogallol, 2,3-naphthalenediol, 4-methylcatechol, 3,5-di-tert-butylcatechol, p-nitrocatechol, 3,4-dihydroxy-L-phenylalanine (DOPA), catechol, rutoside and ascorbic acid.
The invention relates also to the method of preparation of titanium oxide(IV) photocatalytic coatings activated with visible light on the surfaces of the polymers used in medicine, food and pharmaceuticals packaging, in particular selected from the group of: polyurethane (PU), polycarbonate (PC), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE) and is characterized in that it comprises three stages:
a) surface activation of a polymer material with low temperature plasma technique,
b) synthesis of nanocrystalline coating of titanium oxide(IV) using a suspension of nanocrystalline titanium oxide(IV),
c) modification of the coating surface using organic compounds by means of application of the modifier in solution.
Preferably, the activation takes place under the influence of the oxygen or nitrogen plasma. Preferably, the activation takes place at a plasma pressure of 0.1-1 mbar with the time of plasma operation between 5-500 s. Also preferably, when polymeric materials activated with plasma are left in the air to form oxygen-containing functional groups.
Also preferably, if nanocrystalline titanium oxide(IV) with a grain size up to 100 nm in the form of an aqueous colloidal solution is used for the synthesis. Preferably, the synthesis process is carried out by the immersion techniques (for instance dip-coating technique), spraying or painting techniques. Preferably, the process takes place at room temperature.
Preferably, surface modification of coating with organic compounds takes place in aqueous or alcoholic solution of modifier with minimum concentration 10−4 mol/dm3 followed by drying.
Preferably, organic compound is selected from the group consisting of: phthalic acid, 4-sulfophthalic acid, 4-amino-2-hydroxybenzoic acid, 3-hydroxy-2-naphthyl acid, salicylic acid, 6-hydroxysalicylic acid, 5-hydroxysalicylic acid, 5-sulfosalicylic acid, 3,5-dinitrosalicylic acid (Table 1), 1,4-dihydroxy-1,3-benzenedisulfonic disodium salt, gallic acid, pyrogallol, 2,3-naphthalenediol, 4-methylcatechol, 3,5-di-tert-butylcatechol, p-nitrocatechol, 3,4-dihydroxy-L-phenylalanine (DOPA), catechol (Table 2), rutoside and ascorbic acid.
Particular steps of the method are also graphically illustrated in
Another subject of the invention is the use of the photocatalytic coatings of titanium oxide(IV), as defined above activated with visible light on the surfaces of polymers, and/or obtainable in the method according to the invention, for sterilization of plastic components used in medicine, food and pharmaceuticals packaging, in particular selected from the group of: polyurethane (PU), polycarbonate (PC), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE).
Particular subject of the invention is use of the coatings according to the invention and/or obtained by the process according to the invention for the production of selected products from the group consisting of: photosterilization materials, photobactericidal, photofungicidal, photocatalytic and other materials, especially transparent, for instance medical catheters, medical plastic tubes, foil and packaging for food and pharmaceuticals.
Particular subject of the invention is use of the coatings according to the invention and/or obtained by the process according to the invention, in medicine (for example in dermatology, ophthalmology, otolaryngology, urology, gynecology, rheumatology, oncology, surgery, hospitality, veterinary medicine and dentistry) and in cosmetology, preferably, for the sterilization of medical catheters, plastic tubes and other surfaces, sterilization which is advantageous and/or required.
The material according to the present invention exhibits photocatalytic activity when irradiated with visible light (l>400 nm; photocatalysis is a consequence of the absorption of visible light by surface complex of titanium, type charge-transfer) and ultraviolet light (l<400 nm; photocatalysis is a consequence of the absorption of ultraviolet light by surface complex of titanium, type charge-transfer or directly by titanium oxide(IV)). As a result of light exposure, Reactive Oxygen Species are formed (OH., O2−, H2O2, 1O2), which are responsible for oxidation of organic compounds and decay of microorganisms.
The present invention in embodiments not limiting the scope of its application is presented in
Starting substrates for the synthesis of described materials are:
a) commercially available plastic materials, particularly polyurethane (PU), polycarbonate (PC), polyvinyl chloride (PVC), polytetrafluoroethylene (PTFE),
b) unmodified, nanocrystalline titanium oxide(IV) in the form of a colloidal, aqueous solution having a particle size less than 100 nm and organic surface modifiers.
A square with a side length of 3 cm was cut from a commercially available film of polytetrafluoroethylene (PTFE) and purified with detergent. The surface was activated with oxygen plasma in conditions: p=0.3 mbar, t=120 s, v=2 cm3/min, power 100 W. After activation process, the polymer material was left in the air for 2 minutes. The synthesis of the coating was carried out using immersion technique (dip-coating) from colloidal solution of nanocrystalline titanium oxide(IV) (15% wt). The drawing speed of polymer material from the solution was established at 1 cm/min at room temperature. As a result, uniform, durable coating of TiO2 was created at the surface of foil. The resulting coatings were modified using impregnation by immersing the samples for 2 min in a solution of the modifier from the group S (S-2, S-3; Table 1) or group K (K-1, K-4, K-9; Table 2) or ascorbic acid or rutoside in the form of aqueous solution with concentration 10−4 mol/dm3 and then dried in the air.
A square with a side length of 3 cm was cut from a commercially available film of polyurethane (PU) and purified with detergent. The surface was activated with oxygen plasma in conditions: p=0.4 mbar, t=60 s, v=2 cm3/min, power 100 W. After activation process, the polymer material was left in the air for 2 minutes. The synthesis of the coating was carried out using immersion technique (dip-coating) from colloidal solution of nanocrystalline titanium oxide(IV) (4% wt). The drawing speed of polymer material from the solution was established at 1 cm/min at room temperature. As a result, uniform, durable coating of TiO2 was created at the surface of foil. The resulting coatings were modified using impregnation by immersing the samples for 2 min in a solution of the modifier from the group S (S-2, S-3; Table 1) or group K (K-1, K-4, K-9; Table 2) or ascorbic acid or rutoside in the form of aqueous solution with concentration 10−4 mol/dm3 and then dried in the air.
A square with a side length of 3 cm was cut from a commercially available film of polycarbonate (PC) and purified with detergent. The surface was activated with oxygen plasma in conditions: p=0.4 mbar, t=120 s, v=2 cm3/min, power 100 W. After activation process, the polymer material was left in the air for 2 minutes. The synthesis of the coating was carried out using immersion technique (dip-coating) from colloidal solution of nanocrystalline titanium oxide(IV) (15% wt). The drawing speed of polymer material from the solution was established at 1 cm/min at room temperature. As a result, uniform, durable coating of TiO2 was created at the surface of foil. Prepared coatings were modified using impregnation by immersing the samples for 2 min in a solution of the modifier from the group S (S-2, S-3; Table 1) or group K (K-1, K-4, K-9; Table 2) or ascorbic acid or rutoside in the form of aqueous solution with concentration 10−4 mol/dm3 and then dried in the air.
Coatings synthesized according to the Example 1 are permanently affixed to the substrate and indelible. UV-vis spectra of the coatings modified with compounds from the group K are presented in
The activity of obtained coatings was specified using “dry mode”. Aqueous solutions of azure B were used as model pollution for photocatalytic activity tests. A sample of plastic with the synthesized TiO2 coating was impregnated in a solution of pigment with a concentration 2.5·10−4 mol/dm3 for 1 h. Afterwards, the sample was irradiated for 3 h and the changes occurring during the experiment were monitored. The measuring system consisted of the xenon lamp XBO-150. Directly behind the lamp a water filter with copper sulfate(II) solution was placed (which cuts off radiation from the near infrared range, l>700 nm) and a high-pass filter which transmits radiation in the range l>320 nm. The sample was placed at a distance of 40 cm from the light source. Changes in the intensity of the dye colour were assessed during irradiation by spectrophotometry. The diffuse-reflectance spectrum and absorbance spectrum of azure B degradation during irradiation are shown in
Coatings synthesized according to the Example 1 were tested to determine the spectral range of their activity. For photoelectrochemical measurements the set which included: xenon lamp XBO-150 (Osram) with power 150 W and power supply adaptor LPS-250 (Photon Technology International), monochromator with the shutter and electrochemical analyzer BAS-50W (Bioanalytical systems), was used. The control system of shutter and monochromator allows automatic control of wavelength of the incident light and the time of exposure to radiation of the working electrode. Photoelectrochemical measurements were carried out in three-electrode cell, in quartz cuvette with volume 25 cm3 filled with electrolyte (KNO3 solution with concentration 0.1 mol dm−3). A platinum electrode was used as an auxiliary electrode and silver chloride electrode (Ag/AgCl)—as a reference electrode. Working electrode was the ITO film (transparent electrically conductive material, a mixture of indium-tin oxide) coated with a layer of nanocrystalline TiO2 modified with organic compounds according to the method described in Example 1. The idea of the photoelectrochemical experiment is to measure the intensity of generated photocurrent as a function of light wavelength (l=f(I)) incident at photoelectrode in the form of short flashes (10 s.), at constant potential applied to the working electrode. The coatings were irradiated with monochromatic light in the wavelength range of 330-700 nm, changing with each flash of fixed interval (9.5 nm). The change in wavelength occurred when the shutter was closed. The plots I=f(I) (share spectra without taking into account the absolute intensity of light) recorded in the potential range 600÷−200 mV were used to determine the photoreply profile as a function of wavelength and potential applied to the working electrode (so called photocurrent maps, l=f(E,l)). Surface modification with catechol derivatives and salicylic acid results in well-defined extension of the scope of activity to visible light (
| Number | Date | Country | Kind |
|---|---|---|---|
| PL400098 | Jul 2012 | PL | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2013/065400 | 7/22/2013 | WO | 00 |