The present invention is directed on a photovoltaic cell as well as on a method of manufacturing same.
Photovoltaic solar energy conversion offers the perspective to provide for an environmentally friendly means to generate electricity. However, at the present state, electric energy provided by photovoltaic energy conversion units is still significantly more expensive than electricity provided by conventional power stations. Therefore, the development of more cost-effective means of producing photovoltaic energy conversion units attracted attention in the recent years. Amongst different approaches of producing low-cost solar cells, thin-film silicon solar cells combine several advantageous aspects: firstly, thin-film silicon cells can be prepared by known thin-film deposition techniques such as plasma enhanced chemical vapor deposition (PEVCD) and thus offer the perspective of synergies to reduce manufacturing costs by using experiences achieved in the past for example in the field of other thin-film deposition technologies such as from display manufacturing technology. Secondly, thin-film silicon solar cells can achieve high energy conversion efficiencies striving for 10% and more. Thirdly, the main raw materials for the production of thin-film silicon-based solar cells are abundant and non-toxic.
A thin-film solar cell subject to further development by the present invention and as generically known to the skilled artisan comprises as schematically shown in
We understand under “type” of doping, positive -p- and negative -n- doping.
We further understand as a “silicon compound” a material which predominantly comprises silicon, but which additionally comprises one or more than one additional elements.
Subsequently to the addressed first active layer 2 there is provided a second active layer 3 which occupies the predominant part of the thickness of the thin-film junction structure and which is predominantly responsible for photovoltaic conversion. This layer 3 is of intrinsic type and of a silicon compound.
We understand by the term “intrinsic type” material a material which is either undoped or only doped to a neglectable amount or which is both type doped in such a manner that the respective doping types mutually compensate.
Subsequent to the second active layer 3 which is also called in the subsequent description “i-layer” is followed in the addressed direction L, by a third active layer 5 which is of a second type doped silicon compound.
In dependency from the fact where with respect to the solar cell structure as shown in
With an eye on the material structure of the addressed layers it is known to provide the second active layer 3, the i-layer, of amorphous or of microcrystalline (often also called nanocrystalline) structure.
We understand under a material of microcrystalline structure a material wherein 20% to 80% of the volume (both limits included) is crystalline. In opposition thereto we define a material as being of amorphous structure if less than 20% of its volume is crystalline.
Irrespective whether the second active layer 3, the i-layer, 3 is of amorphous or of microcrystalline structure, it is known to apply the first active layer 2 as an amorphous material layer.
The present invention is addressing solar cells at which the said first active layer of first-type doped silicon compound is of amorphous structure.
So as to avoid optical losses by respective absorption in the first active layer 2 facing the illumination side of the cell, typically a wide band gap material layer is applied. However, this increases electrical series resistance at the interface between the electrode layer 1, the TCO layer, and the addressed first-type doped first active layer 2. This is particularly true if ZnO is selected as material of the electrode layer 1. To remedy this effect it is known to apply a contact layer 11 between the first active layer 2 of the cell and the electrode layer 1. Thereby, the contact layer 11 is of microcrystalline silicon compound and is first-type doped.
Provision of such contact layer of microcrystalline first-type doped silicon compound may only be realized at a relatively low deposition rate and additionally requires more advanced equipment due to higher power density to be applied for such deposition. This results in increased equipment and thereby product costs. Furthermore, a deposition process for depositing a layer in microcrystalline structure is more difficult and critical to accurately control, especially if such layer is to be deposited over a large area. Apart from thickness uniformity and doping uniformity, additionally the distribution of crystallinity over the extent of such layer has to be reproducibly controlled. Low deposition rates limit a high manufacturing throughput. It must be kept in mind that for large volume industrial production in fact every second saved in deposition time directly adds to throughput and to the amount of power for manufacturing.
It is an object of the present invention to provide for a photovoltaic cell whereat, as was addressed, a contact layer 11 according to
Thus, a photovoltaic cell according to the present invention comprises:
The approach of providing the contact layer of amorphous material structure was discarded by the skilled artisan to now, because of the relatively high absorption of light by amorphous silicon compound material. According to the present invention this is taken into account by reducing such absorption losses to a minimum by applying the contact layer of a very small thickness, as addressed, of 10 nm at most.
Deposition of the contact layer according to the present invention may further be performed at a high deposition rate compared with deposition rates for microcrystalline silicon compound deposition. This lead to significantly improved throughput especially important in industrial manufacturing. Further, deposition of a contact layer according to the present invention can be executed at definitely lower power densities and thus with a substantially lower amount of power. Typically microcrystalline silicon layers are deposited at a power density of about 2 kW/m2, compared to approx. 300 W/m2 for amorphous layers. This not only leads to a substantial reduction in power consumption, but additionally to a more streamlined processing setup. As the first active layer of first-type silicon compound is of amorphous material structure, the processing equipment for depositing the contact layer according to the present invention and such first active layer may be tailored for application of power densities in the range of just hundreds of Watts per m2.
Thus, at least for depositing these two layers the respective processing equipment may be tailored for relatively low power densities, avoiding equipment for applying power densities higher by about 1 decade as is necessary if, as customarily, the addressed contact layer is provided in microcrystalline structure.
Additionally, also gas flow is substantially reduced by applying the addressed contact layer in amorphous structure with respect to gas flowing time as well as to necessitated overall amount of gas. E.g. and if the silicon compound of the contact layer at least compensates hydrogenated silicon, the hydrogen flow amounts to about 10′000 sccm for first-type, as an example p-doped, microcrystalline hydrogenated silicon. For depositing such first-type doped contact layer as an amorphous material layer the gas flow necessitated is only about 500 sccm.
The fact that the contact layer as provided according to the present invention has a band gap which is smaller than the band gap of the first active, first-type doped layer implies that the top of the valance band in the contact layer material and thus at the interface to the material of the electrode layer is approached to the Fermi level in the material of the addressed electrode layer. Thereby, the energetic difference between electrons and holes at the interface between the addressed materials becomes smaller and which leads to an increase of recombination rate and thus to a reduction of the appearing electrical series resistance.
In one embodiment of the photovoltaic cell according to the present invention the second active layer, which is the i-layer, is of hydrogenated silicon material.
In a further embodiment the addressed second active layer is of amorphous silicon compound. In this embodiment not only the contact layer, the first active layer, but additionally the second active layer—the i-layer—is of amorphous material structure. Thereby, the advantages as addressed above with respect to reduced power density and reduced gas flow, especially if the second active layer is of hydrogenated silicon, may be further exploited. The processing equipment for depositing all the contact layer, the first and the second active layers, may be tailored for low-power densities and gas consumption for depositing the addressed three layers is significantly reduced as well.
In one embodiment of the photovoltaic cell according to the invention the electrode layer is of ZnO. On one hand this material has shown to be highly advantageous for the addressed electrode layer, but leads with respect to a contact layer of microcrystalline structure to a significant series resistance increase. By providing the contact layer according to the present invention it becomes possible on one hand to further exploit the advantages of ZnO electrode layer material and to nevertheless avoid a respectively high series resistance across the interface of the electrode layer material and the contact layer material.
In a further embodiment of the photovoltaic cell according to the invention the material of the first active layer comprises carbon with a first atomic percentage and the material of the contact layer comprises carbon with a second atomic percentage. The second percentage is thereby lower than the first percentage. Thereby, by respectively selecting the amount of carbon in the first active layer on one hand and in the contact layer on the other hand the band gaps of the materials of these two layers may be accurately staggered to fit with the material of the electrode layer as was addressed above.
In one embodiment of the photovoltaic cell according to the invention absorption losses in the contact layer are further minimized by selecting the thickness of the contact layer to be at most 3 nm. The present invention is further directed on a photovoltaic converter panel comprising at least one cell as was addressed.
The method of manufacturing the photovoltaic cell according to the present invention comprises depositing an electrode layer of a transparent electrically conductive oxide and in contact therewith
In one embodiment of the method according to the present invention the band gap in the contact layer material as well as in the first active layer are controlled by respectively selecting the amounts of carbon in the materials of these layers.
In one embodiment of the method according to the invention the electrode layer is deposited of ZnO.
In one embodiment of the method according to the invention the contact layer is deposited with a thickness of at most 3 nm.
In one embodiment of the method according to the invention the second active layer is deposited of hydrogenated silicon, and still in a further embodiment the material of the second active layer is deposited in amorphous material structure.
The invention shall now be further exemplified by an example and with the help of figures.
The figures show:
According to
Subsequently, the first active layer 2b was deposited of amorphous p-doped SiC. Subsequently, as a second active layer 3b, an amorphous layer of hydrogenated silicon was deposited, followed by the third active layer 5b of n-type doped amorphous hydrogenated silicon. Then second electrode layer 13 of n-doped ZnO and a wide-band metal reflector layer 15 was deposited. The contact layer was of 2 nm.
In
It may be seen that by applying the thin contact layer 7b of amorphous hydrogenated silicon, whereas the band gap was reduced with respect to the band gap in the first active layer of p-doped amorphous SiC by respectively selecting the C content in the material of the two layers, the efficiency (ETA) was risen from 8.54 to 9.4%, the open loop voltage Voc was risen from 0.8705 to 0.8878 V, the fill factor from 67.28 to 72.56, whereas the series resistance of the cell was reduced from 7.1966Ω to 5.2666Ω.
Thereby, it may be considered to reduce the thickness of the first active layer 2b when applying the contact layer 11b thereby maintaining the overall performance of the cell.
It must be emphasized that the photovoltaic cell as was exemplified and discussed may be one cell of a more than one cell structure wherein e.g. there is provided in direction of impinging light L, following a cell with an amorphous material structure a further cell with e.g. a microcrystalline material second active layer as i-layer.
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/EP2009/058695 | 7/8/2009 | WO | 00 | 4/6/2011 |
Number | Date | Country | |
---|---|---|---|
61089934 | Aug 2008 | US |