Patent Application
20080000520
The present invention relates to a photovoltaic device, a manufacturing method of a titanium dioxide particle used for making the photovoltaic device, and a dye-sensitized solar cell using the photovoltaic device. In this photovoltaic device, the titanium dioxide particle is dispersed in an electrically-conductive film.
In recent years, the dye-sensitized solar cell is noticed as a solar cell having a low cost. This dye-sensitized solar cell has an electrochemical cell structure passing through an iodine solution without using a silicon semiconductor. As a material suitable for a porous film of an electrode of the solar cell, the titanium dioxide particle is used. Now, as the electrode of the dye-sensitized solar cell, a porous electrode comprising a sintered body of an anatase type TiO2 is widely used.
On the other hand, the other type dye-sensitized solar cell is developed, where a second metal oxide thin film such as SiO2, Al2O3, ZrO2 or the like is coated on a TiO2 film. (for example, referring to Journal of American Chemical Society, 2, 125, 2003, P475-482) In this dye-sensitized solar cell, a cell performance can be improved rather than a solar cell using only the TiO2 film. In addition, the second metal oxide thin film is formed by dipping the TiO2 film in a precursor solution of the metal oxide and sintering it.
However, in the conventional dye-sensitized solar cell indicated in the above non-patent reference, there is a problem that the thickness of the whole of the cell is increased since the second metal oxide thin film is formed on the TiO2 film.
Further, in the conventional dye-sensitized solar cell indicated in the above non-patent reference, there is another problem that a number of the production process is increased since the TiO2 film must be dipped in the precursor solution of the metal oxide to form the second metal oxide thin film.
The object of the present invention is to provide a photovoltaic device capable of improving short circuit current density and photon-to-electron conversion efficiency without increasing the thickness of the whole of the cell and the number of the production process. Further, the object of the present invention is also to provide a manufacturing method of a titanium dioxide particle used for making the photovoltaic device, and a dye-sensitized solar cell using this photovoltaic device.
The invention according to claim 1 is the improved photovoltaic device comprising a light-transmittable base material 31, and a porous film 41b formed on the base material and adsorbing a dye 41d, as shown in
The characteristic of this invention is that the porous film 41b adsorbing the dye 41d contains a titanium dioxide particle 41c containing aluminum oxide.
In the photovoltaic device described in claim 1, since the titanium dioxide particle 41c contains aluminum oxide, it is prevented to backwardly flow an electron (e−) generated at the dye 41d to an electrolyte solution 33, so that the photon-to-electron conversion efficiency of the photovoltaic device 30 is improved.
The invention according to claim 2 is the invention according to claim 1, and further has the characteristic that the titanium dioxide particle is a titanium dioxide particle doped with aluminum oxide.
In the photovoltaic device described in claim 2, since the titanium dioxide particle is doped with aluminum oxide, it is prevented to backwardly flow an electron (e−) generated at the dye to the electrolyte solution, so that the photon-to-electron conversion efficiency of the photovoltaic device is improved.
The invention according to claim 3 is the invention according to claim 1, and further has the characteristic that the titanium dioxide particle 41c is a mixed particle of a first titanium dioxide particle and a second titanium dioxide particle, as shown in
In the photovoltaic device described in claim 3, since the titanium dioxide particle 41c contains the first titanium dioxide particle doped with aluminum oxide, it is prevented to backwardly flow the electron generated at the dye 41d to the electrolyte solution 33, so that the photon-to-electron conversion efficiency of the photovoltaic device 30 is improved. Further, since the titanium dioxide particle 41c contains the second titanium dioxide particle not doped with aluminum oxide, a specific surface area per unit volume of the porous film 41b is increased, the amount of the adsorbed dye is increased, and short circuit current density becomes high. Thus, the photon-to-electron conversion efficiency is improved. Further, when the mixing ratio of one kind of the first titanium dioxide particle and one kind of the second titanium dioxide particle is changed, the content of aluminum oxide in the titanium dioxide particle 41c can be easily adjusted, where the first titanium dioxide particle is doped with the predetermined amount of aluminum oxide, and the second titanium dioxide particle is not doped with aluminum oxide.
The invention according to claim 7 is a manufacturing method of the titanium dioxide particle used for making the photovoltaic device described in any one of claim 1 to claim 6. This method comprises a process for preparing a first mixed gas by uniformly mixing a titanium tetrachloride gas, an aluminum chloride gas, oxygen and hydrogen; a process for making the first titanium dioxide particle doped with 0.01 to 1 wt. % aluminum oxide by flame-hydrolyzing the first mixed gas; a process for preparing the second mixed gas by uniformly mixing a titanium tetrachloride gas, oxygen and hydrogen; a process for making the second titanium dioxide particle by flame-hydrolyzing the second mixed gas; and a process for preparing the titanium dioxide particle by mixing the first titanium dioxide particle and the second titanium dioxide particle with a predetermined ratio.
In the manufacturing method of the titanium dioxide particle described claim 7, there are no agglomerations, and it is possible to make the titanium dioxide particle having excellent dispersibility to an acid solution.
The invention according to claim 8 is a dye-sensitized solar cell using the photovoltaic device 30 described in any one of claim 1 to claim 7, as shown in
In the dye-sensitized solar cell described in claim 8, since the titanium dioxide particle 41c contains aluminum oxide, it is prevented to backwardly flow the electron (e−) generated at the dye 41d to the electrolyte solution 33, so that the photon-to-electron conversion efficiency of the photovoltaic device 30 is improved. More particularly, since the titanium dioxide particle 41c contains the first titanium dioxide particle doped with aluminum oxide, it is prevented to backwardly flow the electron (e−) generated at the dye 41d to the electrolyte solution 33, so that the photon-to-electron conversion efficiency of the photovoltaic device 30 is improved. Further, since the titanium dioxide particle 41c contains the second titanium dioxide particle which is not doped with aluminum oxide, the specific surface area per unit volume of the porous film 41b is increased, the amount of the adsorbed dye is increased, and the short circuit current density becomes high. Thus, the photon-to-electron conversion efficiency is improved.
As mentioned above, according to the present invention, since the porous film of the photovoltaic device contains the titanium dioxide particle containing aluminum oxide, it is prevented to backwardly flow the electron generated at the dye to the electrolyte solution. As a result, the photon-to-electron conversion efficiency of the photovoltaic device can be improved.
Further, when the titanium dioxide particle is the mixed particle of the first titanium dioxide particle and the second titanium dioxide particle, where the first titanium dioxide is doped with aluminum oxide and the second titanium dioxide is not doped with aluminum oxide, since the titanium dioxide particle contains the first titanium dioxide particle doped with aluminum oxide, it is prevented to backwardly flow the electron generated at the dye to the electrolyte solution, so that the photon-to-electron conversion efficiency of the photovoltaic device is improved. Further, since the titanium dioxide particle contains the second titanium dioxide particle not doped with aluminum oxide, the specific surface area per unit volume of the porous film is increased, the amount of the adsorbed dye is increased, and the short circuit current density becomes high. Thus, the photon-to-electron conversion efficiency is improved. Further, when the mixing ratio of one kind of the first titanium dioxide particle and one kind of the second titanium dioxide particle is changed, the content of aluminum oxide in the titanium dioxide particle can be easily adjusted, where the first titanium dioxide particle is doped with the predetermined amount of aluminum oxide, and the second titanium dioxide particle is not doped with aluminum oxide. Thereby, it is possible to easily make the titanium dioxide containing the desired amount of aluminum oxide.
Further, it is possible to make the titanium dioxide particle having the excellent dispersibility to an acidic aqueous solution and a purity of 99.0% or more, where the agglomeration is not generated and chlorine with which it is difficult to treat is not generated. The manufacturing method of this titanium dioxide particle comprises, preparing the first mixed gas by uniformly mixing the titanium tetrachloride gas, the aluminum chloride gas, oxygen and hydrogen, making the first titanium dioxide particle doped with 0.01 to 1 wt. % aluminum oxide by flame-hydrolyzing the first mixed gas, preparing the second mixed gas by uniformly mixing the titanium tetrachloride gas, oxygen and hydrogen, making the second titanium dioxide particle by flame-hydrolyzing the second mixed gas, and preparing the titanium dioxide particle by mixing the first titanium dioxide particle and the second titanium dioxide particle with the predetermined ratio.
Further, as for the dye-sensitized solar cell using the photovoltaic device, since the titanium dioxide particle contains aluminum oxide, that is, the titanium dioxide particle contains the first titanium dioxide particle doped with aluminum oxide, it can be prevented to backwardly flow the electron generated at the dye to the electrolyte solution. Furthermore, since the titanium dioxide particle contains the second titanium dioxide particle not doped with aluminum oxide, the specific surface area per unit volume of the porous film is increased and the amount of the adsorbed dye is increased. As a result, the short circuit current density becomes high, so that the photon-to-electron conversion efficiency becomes high.
Then, the detailed description of the preferred embodiment of the present invention is explained based on drawings.
The titanium dioxide particle of the preferred embodiment (a titania (TiO2) particle) is the mixed particle of the first titanium dioxide particle doped with aluminum oxide and the second titanium dioxide particle not doped with aluminum oxide. The aluminum oxide doped to the first titanium dioxide is Al2O3. The content of aluminum oxide in the titanium dioxide particle is 0.0005 to 0.01 wt. %, and preferably 0.0007 to 0.005 wt. %. The content of aluminum oxide in the titanium dioxide particle is adjusted, for example, by changing the mixing ratio of the first titanium dioxide particle doped with the 0.1 wt. % aluminum oxide and the second titanium dioxide particle not doped with aluminum oxide. The advantage of this method is as follows, that is, the content of aluminum oxide in the titanium dioxide particle can be adjusted by only using two kinds of titanium dioxide particles, and the titanium dioxide particle containing aluminum oxide with the predetermined amount can be easily made, wherein the two kinds of titanium dioxide particles is the first titanium dioxide particle doped with the 0.1 wt. % aluminum oxide and the second titanium dioxide particle not doped with aluminum oxide. In addition, in the present preferred embodiment, although the doping amount of aluminum oxide in the first titanium dioxide particle is set to 0.1 wt. %, it is not limited by this amount. However, it is preferable that the doping amount of aluminum oxide to the first titanium dioxide particle is within the range of 0.01 to 1 wt. %, from the point of the easy manufacturing and operating, or the like.
On the other hand, the reason why the content of aluminum oxide in the titanium dioxide particle is limited within the range of 0.0005 to 0.01 wt. % is as follows, that is, the efficiency of the photovoltaic device containing the above titanium dioxide particle becomes to be low if the content is outside the above-mentioned range. Further, the first titanium dioxide particle has a crystalline anatase being 70 to 95 wt %, preferably 75 to 90 wt %, a specific surface area by the BET method being 35 to 65 m2/g, preferably 45 to 55 m2/g, and an oil absorption being 55 to 75 ml/100 g measured by the method according to JIS K5101, preferably 60 to 70 ml/100 g. At this time, the reason why the specific surface area by the BET method of the first titanium dioxide particle is limited within the range from 35 to 65 m2/g is as follows, that is, the particle size of the first titanium dioxide particle is increased too much if the specific surface area is less than 35 m2/g, and the productivity of the first titanium dioxide is remarkably decreased if the specific surface area is more than 65 m2/g. Furthermore, the reason why the oil absorption of the first titanium dioxide particle is limited within the range from 55 to 75 ml/100 g is, as follows, that is, a viscosity of a paste prepared using the acidic aqueous solution (hereinafter, this paste is said to as an acidic aqueous paste), in which the first titanium dioxide particle is dispersed, becomes too low if the oil absorption is less than 55 ml/100 g, and the viscosity of the acidic aqueous paste becomes too high if the oil absorption is more than 75 ml/100 g.
The manufacturing methods of the first and second titanium dioxide particles constituted in this way are explained.
(a) Manufacturing Method of the First Titanium Dioxide Particle
The manufacturing equipment 10 of the first titanium dioxide particle comprises a burner 11 for making an oxide by a thermal decomposition method, as shown in
On the other hand, an axial flow tube 19 is inserted into the central tube 13. A base end of the axial flow tube 19 is connected with an aerosol generator 23, and a top end of the axial flow tube 19 is opened in the central tube 13. The first mixed gas is made by making an aerosol comprising aluminum trichloride and water, feeding to the central tube 13 through the axial flow tube 19, and uniformly mixing with the above-mentioned mixed raw material gas before reacting. The aerosol is made by an ultrasonic spraying or the like of an aqueous solution or dispersion liquid of aluminum trichloride (aluminum chloride) in the aerosol generator 23. When this first mixed gas is combusted in the combustion chamber 14 and the flame tube 16, the first titanium dioxide particle doped with aluminum oxide is generated. The obtained first titanium dioxide particle doped with aluminum oxide is separated and recovered from an outflow gas by a commonly known method.
In addition, it is supposed that when the aerosol comprising aluminum trichloride and water, which is generated in the aerosol generator 23, is fed to a heat zone 24 through the axial flow tube 19 with a mild career gas flow, the entrained water in the aerosol is evaporated in the heat zone 24, and then, the aerosol becomes the condition in which a fine salt crystal is finely dispersed in a gas phase. The aerosol having the condition, in which the fine salt crystal is finely dispersed in the gas phase, is uniformly mixed with the above-mentioned mixed raw material gas in the central tube 13 through the axial flow tube 19 to become the first mixed gas. When the first mixed gas is reacted in a flame, it is possible to make the first titanium dioxide particle which is doped with aluminum oxide and has the specific surface area by the BET method being 35 to 65 m2/g. Therefore, as for the first titanium dioxide particle doped with aluminum oxide being made in this way, the existing state of aluminum oxide is clearly different from that of the mixed oxide by the thermal decomposition method, which is commonly known, that is, a co-fumed method. In this co-fumed method, TiCl4 gas and AlCl3 gas are only premixed and combusted together in a flame reactor.
(b) Manufacturing Method of the Second Titanium Dioxide Particle
In order to make the second titanium dioxide particle not doped with aluminum oxide, the second mixed gas (the mixed raw material gas) is prepared by heating a high purity titanium tetrachloride liquid to be vaporized at first, and mixing the vaporized titanium tetrachloride gas with hydrogen and air. Then, the second titanium dioxide particle having the specific surface area by the BET method being 65 to 120 m2/g is made by flame-hydrolyzing the second mixed gas in the flame in which hydrogen and oxygen are combusted. In addition, a theoretical combustion temperature of the flame is set to as 400 to 700° C., and preferably 450 to 600° C. At this time, the reason why the theoretical combustion temperature of the flame is set within the range of 400 to 700° C. is as follows, that is, the productivity of the second titanium dioxide particle is remarkably decreased if it is less than 400° C., and the particle size of the made second titanium dioxide particle is increased if it is more than 700° C.
The manufacturing method of the second titanium dioxide particle by the flame hydrolysis method is explained concretely.
As shown in
The manufacturing method of the photovoltaic device using the titanium dioxide particle, in which the first titanium dioxide particle and the second titanium dioxide particle are mixed, is explained.
A first conductive film 41a is formed on a first base material 31 at first (
Then, a titanium dioxide paste containing the titanium dioxide particle 41c is coated on the first conductive film 41a, and heated and calcined. This titanium dioxide paste is prepared by uniformly mixing the made titanium dioxide particle 41c using the above equipment, an acidic aqueous solution, a thickening agent and a dispersing agent. As the acidic aqueous solution, nitric acid, hydrochloric acid, sulfuric acid or the like can be used, and it is preferable that pH of the acidic aqueous solution is 3 or less. The reason why the pH of the acidic aqueous solution is 3 or less is that an interfacial potential of the titanium dioxide particle 41c is controlled to increase the dispersibility of the titanium dioxide particle 41c. Further, as the thickening agent, glycols such as polyethylene glycol or the like is used. As the dispersing agent, acetylacetone and Triton-X100 (an alkylphenoxypolyethylene glycol type nonionic surfactant) are used. The reason why polyethylene glycol is added as the thickening agent is as follows, that is, the viscosity of the titanium dioxide paste can be increased to form the thick film, and when the polyethylene glycol is evaporated during heating the titanium dioxide paste, a penetration hole can be formed, where the hole is penetrated from the front surface to back surface of the porous film 41b containing the titanium dioxide particle 41c. Further, a bonding strength between the porous film 41b and the first conductive film 41a can be increased. When the Triton-X100 is used as the dispersing agent, there is an advantage that a residual component is not remained after heating.
Then, a forming method of the porous film 41b is explained. When the glass plate is used as the first base material 31, the porous film 41b is formed by coating and drying the titanium dioxide paste on the first conductive film 41a using a doctor blade method, a squeegee method, a spin coat method, a screen printing method or the like, taking it into an electric furnace, and calcining it in an atmosphere while keeping 300 to 600° C. for 30 to 90 minutes. Thereby, the forming process for the porous film 41b on the first conductive film 41a is completed. At this time, the reason why the calcining temperature is limited within the range of 300 to 600° C. is as follows, that is, if this temperature is less than 300° C., there are problems that an organic additive which cannot be combusted is remained to prevent the adsorption of the dye, and the high photon-to-electron conversion ability cannot be obtained since the sintering of the titanium dioxide particle 41c itself is insufficient. Further, if this temperature is more than 600° C., there are problems that the base material 31 is softened to cause the trouble to make a working electrode 41. Furthermore, the reason why the calcining time is limited within the range of 30 to 90 minutes is as follows, that is, there is a problem of causing the insufficient sintering if it is less than 30 minutes, and the particle growth by calcining progresses is too much to decrease the specific surface area if it is more than 90 minutes. On the other hand, when the plastic film having the flexibility (for example, a polyethyleneterephthalate film) is used as the first base material, the porous film is formed by coating the titanium dioxide paste on the first conductive film of the first base material using a squeegee (applicator) method, a screen printing method, an electrodepositing method, a spray method, DJP (Direct jet printing) method or the like, carrying out a press forming if necessary, and then, irradiating a microwave. Thereby, the forming process for the porous film on the first conductive film is completed.
Then, the dye 41d is adsorbed to the porous film 41b to be fixed by dipping the first base material 31 in a dye solution, where the porous film 41b is formed on the first conductive film 41a. As the dye 41d, it is preferable to use an organic dye having a photoelectric effect in addition to a ruthenium complex. More particularly, a methine dye, a xanthene-based dye, a porphyrin dye, a phthalocyanine dye, an azo-based dye, a coumarin dye or the like is preferably used. Further, a mixed dye of one or more than two kinds selected from a group consisting of these dyes may be used as a photon-to-electron conversion material. When the ruthenium complex is used as the dye 41d, the ruthenium complex is dissolved with an independent solvent of acetonitrile, t-BuOH, ethanol or the like or a mixed solvent of these solvents to prepare the dye solution, and the concentration of the dye solution is adjusted to have 3×10−4 to 5×10−4 mol. At this time, the reason why the concentration of the dye solution is limited within the range of 3×10−4 to 5×10−4 mol is as follows, that is, if it is less than 3×10−4 mol, there is a problem that the amount of the adsorbed dye is insufficient and the photon-to-electron conversion efficiency decreases. If it is more than 5×10−4 mol, it is difficult to improve the characteristics of the photon-to-electron conversion material even when adding the dye more since the concentration reaches the saturated condition. Further, the dipping time of the first base material 31 to the dye solution is about 20 hours at a room temperature in general. Although the dipping time of the first base material 31 to the dye solution is about 20 hours, this time can be shortened to about 5 minutes at the shortest by heating and refluxing the dye solution to near the boiling point. It should be took care suitably so as to make the amount of the adsorbed dye into the maximum on balance with the operation time by considering the film thickness of the titanium dioxide particle 41c, a damaging risk of the electrode, or the like. Furthermore, the surface of the porous film 41b adsorbed with the dye is washed and dried. Thereby, the photovoltaic device 30 can be made.
In the conventional photovoltaic device comprising the titanium dioxide particle not containing aluminum oxide, although almost all electrons (e−) generated at the dye is transferred to the titanium dioxide particle quickly, a part of the electron (e−) is transferred to the electrolyte solution, so that the photon-to-electron conversion efficiency of the photovoltaic device is a little low.
However, in the photovoltaic device 30 of the present invention, since the titanium dioxide particle 41c contains aluminum oxide, that is, the titanium dioxide particle 41c contains the first titanium dioxide particle doped with aluminum oxide, it can be prevented to backwardly flow the electron (e−) generated at the dye 41d to the electrolyte 33. Further, since the titanium dioxide particle 41c contains the second titanium dioxide particle not doped with aluminum oxide, the specific surface area per unit volume of the porous film 41b is increased, and the amount of the adsorbed dye is increased. As a result, the short circuit current density becomes high, so that the photon-to-electron conversion efficiency becomes high.
Then, a manufacturing method of a dye-sensitized solar cell 50 using the photovoltaic device 30 is explained.
A counter electrode 42 is formed by forming a second conductive film 42a on a second base material 32. The second conductive film 42a is formed on one surface, both surfaces, or a whole surface of the second base material 32 by the vapor deposition method, the sputtering method, the ion plating method, the hydrolyzing method or the like. As the second base material 32, it is preferable to use the glass plate or the plastic film having the flexibility. As the second conductive film 42a, it is preferable to use a film, in which one or more kinds selected from the following group are laminated, that is, the group consisting of a platinum foil, a FTO film in which tin oxide is doped with fluorine, or a ITO film in which indium oxide is mixed with a little amount of tin oxide.
The electrolyte solution 33 is stored between the working electrode 41 and the counter electrode 42, while having the predetermined space between the working electrode 41 of the first base material 31 and the counter electrode 42 of the second base material 42. The electrolyte solution 33 is prepared by mixing a supporting electrolyte, a redox pair and an alcohol-based or nitrile-based independent solvent or a mixed solvent of them. The supporting electrolyte comprises a positive ion, such as a lithium ion, a negative ion, such as a chlorine ion, or the like. The redox pair is an iodine-iodine compound, a bromine-bromine compound, which exist in the supporting electrolyte. The alcohol-based solvent is ethanol or t-butanol, and the nitrile-based solvent is acetonitrile, methoxyacetonitrile or 3-methoxypropionitrile. In addition, in order to keep the space with a predetermined value between the working electrode 41 of the first base material 31 and the counter electrode 42 of the second base material 32, a spacer (which is not shown in this drawing) made with a resin film having a thickness of 10 to 30 μm is interposed between the working electrode 41 and the counter electrode 42. Further, in order to prevent the leakage of the electrolyte solution 33, an electrically insulating adhesive, such as an epoxy resin or the like, is coated to the periphery of these electrodes at between the working electrode 41 and the counter electrode 42, and hardened. Thereby, the dye-sensitized solar cell 50 is made.
In the dye-sensitized solar cell made in this way, since the titanium dioxide particle 41c contains aluminum oxide, that is, the titanium dioxide particle 41c contains the first titanium dioxide particle doped with aluminum oxide, it can be prevented to backwardly flow the electron (e−) generated at the dye 41d to the electrolyte 33. Further, since the titanium dioxide particle 41c contains the second titanium dioxide particle not doped with aluminum oxide, the specific surface area per unit volume of the porous film 41b is increased, and the amount of the adsorbed dye is increased. As a result, the short circuit current density becomes high, so that the photon-to-electron conversion efficiency becomes high.
In addition, in this preferred embodiment, the titanium dioxide particle is the mixed particle of the first titanium dioxide particle doped with aluminum oxide and the second titanium dioxide not doped with aluminum dioxide. However, the titanium dioxide particle may comprises only a titanium dioxide particle doped with aluminum oxide of 0.0005 to 0.01 wt. %, preferably 0.007 to 0.005 wt. %. This titanium dioxide particle doped with aluminum oxide is made by the manufacturing equipment of the first titanium dioxide particle, which is shown in
Further, in this preferred embodiment, although the first titanium dioxide particle is made by the manufacturing equipment shown in
Then, examples of the present invention are explained concretely with comparison examples.
The titanium dioxide paste was coated in a square shape on the first conductive film 41a of the first base material 31 having the first conductive film 41a (
On the other hand, the counter electrode 42 was made by forming the second conductive film 42a on one surface of the second base material 32 comprising the glass plate. The second conductive film was not shown in this drawing, but comprised a fluorine doped tin oxide layer and a platinum layer. The fluorine doped tin oxide layer was laminated on the second base material 32 by the vapor deposition method, and the platinum layer was laminated on the fluorine doped tin oxide layer by the sputtering method. As the spacer made by the resin film, a “Himilan” film produced by Dupont-Mitsui Polychemicals Corporation was used, and this film had a thickness being 25 μm. Further, the electrolyte solution 33 was prepared by dissolving the following electrolytes with 3-methoxypropionitril as a solvent. That is, the electrolytes were 0.05 mol of iodine a solute, 0.1 mol of lithium iodide, 0.6 mol of 1,2-dimethyl-3-n-propylimidazolium iodide and 0.5 mol of tert-butyl-pyridine. Then, the dye-sensitized solar cell 50 was made by interposing the resin film spacer between the working electrode 41 and the counter electrode 42, and enclosing the electrolyte solution 33 between the both electrodes 41 and 42, where the resin film spacer was not shown in this drawing and formed with the Himilan film having the thickness being 25 μm. This dye-sensitized solar cell 50 was named as Example 1. In addition, an effective area of the porous film 41b was 24.5 mm2, and a film thickness of the porous film 41b was 8.1 μm.
The dye-sensitized solar cell was made like Example 1 except the 1 wt. % first titanium dioxide particle and 100 wt. % second titanium dioxide particle were mixed to prepare the titanium dioxide particle in which the content of aluminum oxide was diluted to 0.001 wt. %. This cell was named as Example 2. In addition, the effective area of the porous film was 24.0 mm2, and the film thickness of the porous film was 7.8 μm.
The dye-sensitized solar cell was made like Example 1 except the 1 wt. % first titanium dioxide particle and 10 wt. % second titanium dioxide particle were mixed to prepare the titanium dioxide particle in which the content of aluminum oxide was diluted to 0.01 wt. %. This cell was named as Example 3. In addition, the effective area of the porous film was 24.0 mm2, and the film thickness of the porous film was 8.1 μm.
The first titanium dioxide particle doped with 0.0005 wt. % aluminum oxide and having the specific surface area by the BET method being 50 m2/g was made at first, using the manufacturing equipment 10 of the first titanium dioxide particle shown in
The first titanium dioxide particle doped with 0.01 wt. % aluminum oxide and having the specific surface area by the BET method being 50 m2/g was made at first, using the manufacturing equipment 10 of the first titanium dioxide particle shown in
The dye-sensitized solar cell was made like Example 1 except the second titanium dioxide particle not doped with aluminum oxide and having the specific surface area by the BET method being 90 m2/g was only used as the titanium dioxide particle. This dye-sensitized solar cell was named as Comparison example 1. In addition, the effective area of the porous film was 24.0 mm2, and the film thickness of the porous film was 6.4 μm.
The dye-sensitized solar cell was made like Example 1 except the 1 wt. % first titanium dioxide particle and the 1000 wt. % second titanium dioxide particle were mixed to prepare the titanium dioxide particle in which the content of aluminum oxide was diluted to 0.0001 wt. %. This cell was named as Comparison example 2. In addition, the effective area of the porous film was 24.3 mm2, and the film thickness of the porous film was 8.2 μm.
The dye-sensitized solar cell was made like Example 1 except the second titanium dioxide particle doped with 0.1 wt. % aluminum oxide was used as the titanium dioxide particle. This dye-sensitized solar cell was named as Comparison example 3. In addition, the effective area of the porous film was 24.0 mm2, and the film thickness of the porous film was 7.7 μm.
Each of photon-to-electron conversion efficiencies η (%) of the dye-sensitized solar cell of Examples 1 to 5 and Comparison examples 1 to 3 was measured respectively. This photon-to-electron conversion efficiency η (%) was calculated from the following formula (I), using Voc (an open voltage value: V) taken by measuring an I-V curve characteristic, Isc (a short-circuit current value: mA), ff (a file factor value), L (an irradiation light amount: mW/cm2), and S (an area of the porous film: cm2).
η=(Voc×Isc×ff×100)/(L×S) (1)
The results of these efficiencies were shown in Table 1 and
Clearly from Table 1, although the photon-to-electron conversion efficiencies of Comparison examples 1 to 3 were low values 4.94 to 5.35%, those of Examples 1 to 5 were high values 5.40 to 6.52%. Further, clearly from
The present invention does not increase the whole thickness of a photovoltaic device and the number of the production process, and can improve short circuit current efficiency. Therefore, the present invention can be applicable to a dye-sensitized solar cell.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2004-368989 | Dec 2004 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP05/16733 | 9/12/2005 | WO | 6/21/2007 |