Piezoelectric ceramic composition and piezoelectric ceramic device using the same

Information

  • Patent Grant
  • 6258291
  • Patent Number
    6,258,291
  • Date Filed
    Monday, February 7, 2000
    24 years ago
  • Date Issued
    Tuesday, July 10, 2001
    23 years ago
Abstract
A lead-free piezoelectric ceramic composition is composed of a main component represented by the general formula (Sr1−xM1x)Bi2(Nb1−yWy)2O9, wherein M1 is one of divalent metals other than Sr and trivalent metals other than Bi, 0
Description




BACKGROUND OF THE INVENTION




1. Field of the Invention




The present invention relates to piezoelectric ceramic compositions and piezoelectric ceramic devices using the same. In particular, the present invention relates to piezoelectric ceramic compositions, which are useful as materials for piezoelectric ceramic filters, piezoclectric ceramic oscillators and piezoelectric ceramic vibrators, and relates to piezoelectric ceramic devices using the same.




2. Description of the Related Art




Piezoelectric ceramic compositions comprising lead titanate zirconate (Pb(Ti


x


Zr


1−x


)O


3


) or lead titanate (PbTiO


3


) as main components are extensively used in piezoclectric ceramic filters, piezoelectric ceramic oscillators, and piezoelectric ceramic vibrators. In piezoelectric ceramic compositions comprising lead titanate zirconate or lead titanate as the main components, lead oxide is generally used. Lead oxide, however, requires facilities such as filters for removing powdered lead oxide, which is scattered by vaporization during the production steps. Such facilities incur increased production costs. In addition, the vaporization of the lead oxide causes deterioration of the uniformity of product quality.




On the other hand, piezoelectric ceramic compositions comprising bismuth layered compounds such as (Sr


1−x


M


x


)Bi


2


Nb


2


O


9


as main components and Mn as an optional component do not contain lead oxide and do not cause the above problems. These piezoelectric ceramic compositions, however, must be sintered at high temperatures of at least 1,250° C. in order to obtain piezoelectric ceramics having electromechanical coupling coefficients kt of at least 10%, which are at practical levels. Thus, these piezoelectric ceramic compositions require sintering furnaces which withstand such high-temperature sintering. Moreover, setters and the like for containing the piezoelectric ceramic compositions during sintering have short service lives in high-temperature operation, resulting in increased production costs.




SUMMARY OF THE INVENTION




Accordingly, it is an object of the present invention to provide a piezoelectric ceramic composition which can be sintered at a temperature of 1,100° C. or less, does not contains lead or lead compounds, and exhibits a practical level of electromechanical coupling coefficient kt at such a low sintering temperature. The piezoelectric ceramic composition is useful as materials for piezoelectric ceramic filters, piezoelectric ceramic oscillators and piezoelectric ceramic vibrators.




It is another object of the present invention to provide a piezoelectric ceramic device using the piezoelectric ceramic composition.




According to a first aspect of the present invention, a piezoelectric ceramic composition comprises a main component represented by the general formula SrBi


2


(Nb


1−x


W


y


)


2


O


9


, wherein 0<y≦0.3.




According to second aspect of the present invention, a piezoelectric ceramic composition comprises a main component represented by the general formula (Sr


1−x


M1


x


)Bi


2


)Nb


1−y


W


y


)


2


O


9


, wherein M1 is one of divalent metals other than Sr and trivalent metals other than Bi, 0<x ≦0.3, and 0<y ≦0.3. The M1 in the general formula may be at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.




According to a third aspect of the present invention, a piezoelectric ceramic composition comprises a main component represented by the general formula (Sr


1−x


M2


2x/3


)Bi


2


(Nb


1−y


W


y


)


2


O


9


, wherein M2 is a trivalent metal other than Bi, 0<x ≦0.45, and 0<y ≦0.3. The M2 in the general formula may be at least one element selected from the group consisting of La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.




According to a fourth aspect of the present invention, a piezoelectric ceramic composition comprises a main component represented by the general formula SrBi


2


Nb


2


O


9


and more than 0 to about 0.3 mole of W with respect to 1 mole of Bi in the main component. This piezoelectric ceramic composition may further comprise one of divalent metals other than Sr and trivalent metals other than Bi in an amount of more than 0 to about 0.15 mole with respect to 1 mole of Bi in the main component. The divalent metal or the trivalent metal may be at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.




The piezoelectric ceramic compositions according to the first to fourth aspects may further comprise manganese as an auxiliary component in an amount of more than 0 to about 1.0 percent by weight calculated as MnCO


3


.




According to a fifth aspect of the present invention, a piezoelectric ceramic device comprises a piezoelectric ceramic comprising the piezoelectric ceramic composition according to one of the first to fourth aspects, and electrodes.




The above objects, other objects, features and advantages of the present invention will be further apparent from the following preferred embodiments.











BRIEF DESCRIPTION OF THE DRAWINGS





FIG. 1

is an isometric view of an exemplary piezoelectric ceramic vibrator in accordance with the present invention; and





FIG. 2

is a schematic cross-sectional view of the piezoelectric ceramic vibrator shown in FIG.


1


.











DESCRIPTION OF THE PREFERRED EMBODIMENTS




The piezoelectric ceramic composition in accordance with the present invention is composed of a main component represented by the general formula (Sr


1−x


M


x


)Bi


2


Nb


2


O


9


wherein M is a divalent metal element other than Sr or a trivalent metal element other than Bi, and 0<x ≦0.3. Alternatively, the piezoelectric ceramic composition in accordance with the present invention is composed of a main component represented by the formula SrBi


2


Nb


2


O


9


.




In the piezoelectric ceramic composition comprising a main component represented by the general formula (Sr


1−x


M1


x


)Bi


2


(Nb


1−y


W


y


)


2


O


9


, the subscript x indicating the M1 content lies in a range of 0<x ≦0.3. At an M1 content outside this range, the electromechanical coupling coefficient kt does not reach a practical level.




In the piezoelectric ceramic composition comprising a main component represented by the general formula (Sr


1−x


M2


2x/3


)Bi


2


(Nb


1−y


)


2


O


9


, the subscript x indicating the M2 content lies in a range of 0<x≦0.45. At an M2 content outside this range, the electromechanical coupling coefficient kt does not reach a practical level.




In the piezoelectric ceramic compositions in accordance with the present invention, the subscript y indicating the W content lies in a range of 0 <y <0.3. When the piezoelectric ceramic composition does not contain W (y=0), this piezoelectric ceramic composition is not sufficiently sintered at a temperature of 1,100° C. or less and is not polarized. When the subscript y exceeds 0.3, the electromechanical coupling coefficient kt does not reach a practical level.




In the piezoelectric ceramic composition comprising a main component represented by the general formula SrBi


2


Nb


2


O


9


and W as an additional component, the W content lies in a range of more than 0 to about 0.3 mole respect to 1 mole of Bi in the main component. When the W content is 0, the piezoelectric ceramic composition is not sufficiently sintered at a temperature of 1,100° C. or less and is not polarized. When the W content exceeds about 0.3 mole, the electromechanical coupling coefficient kt does not reach a practical level.




This piezoelectric ceramic composition may further comprises one of divalent metals other than Sr and trivalent metals other than Bi in an amount of more than 0 to about 0.15 mole with respect to 1 mole of Bi in the main component. When the content of the divalent or trivalent metal exceeds about 0.15 mole, the electromechanical coupling coefficient kt does not reach a practical level.




The piezoelectric ceramic composition in accordance with the present invention preferably further comprises manganese as an auxiliary component in an amount of more than 0 to about 1.0 percent by weight as MnCO


3


. The addition of manganese contributes to improved sintering characteristics. When the manganese content exceeds about 1.0 percent by weight as MnCO


3


, the piezoelectric ceramic composition is not polarized.




The advantages in the present invention are particularly noticeable when the MI is at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.




Also, the advantages in the present invention are particularly noticeable when the M2 is at least one element selected from the group consisting of La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.




Moreover, the advantages in the present invention are particularly noticeable when the divalent metal other than Sr or trivalent metal other than Bi is at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.





FIG. 1

is an isometric view of an exemplary piezoelectric ceramic vibrator in accordance with the present invention, and

FIG. 2

is a schematic cross-sectional view of the piezoelectric ceramic vibrator. A piezoelectric ceramic vibrator


10


includes, for example, a rectangular piezoelectric ceramic


12


. The piezoelectric ceramic


12


has two piezoelectric ceramic layers


12




a


and


12




b


. These piezoelectric ceramic layers


12




a


and


12




b


are composed of the piezoelectric ceramic composition of the present invention, and are laminated.




Moreover, the piezoelectric ceramic layers


12




a


and


12




b


are polarized in the same thickness direction, as shown by the arrows in FIG.


2


.




A circular vibrating electrode


14




a


is formed between the piezoelectric ceramic layers


12




a


and


12




b


, and an extraction electrode


16




a


having a T-shape extends from the vibrating electrode


14




a


to one end face of the piezoelectric ceramic


12


. Another circular vibrating electrode


14




b


is formed on the piezoelectric ceramic layer


12




a


, and another extraction electrode


16




b


having a T-shape extends from the vibrating electrode


14




b


to the other end face of the piezoelectric ceramic


12


. In addition, a third circular vibrating electrode


14




c


is formed on the piezoelectric ceramic layer


12




b


, and an extraction electrode


16




c


having a T-shape extends from the vibrating electrode


14




c


to the other end face of the piezoelectric ceramic


12


.




The extraction electrode


16




a


is connected to an external terminal


20




a


via a lead line


18




a


, whereas the extraction electrodes


16




b


and


16




c


are connected to another external terminal


20




b


via another lead line


18




b


.




The present invention is not limited to the device configuration shown by the piezoelectric ceramic vibrator


10


, and is applicable to other device configurations and other piezoelectric ceramic devices, such as piezoelectric ceramic vibrators using vibrational modes (for example, thickness shear vibration or thickness third harmonic waves), piezoelectric filters and piezoelectric ceramic oscillators.




EXAMPLES




As starting materials, SrCO


3


, Bi


2


O


3


, Nb


2


O


5


, CaCO


3


, BaCO


3


, La


2


O


3


, Nd


2


O


3


, Sm


2


O


3


, Y


2


O


3


, WO


3


and MnCO


3


were prepared. These materials were weighed and mixed by a wet process in a ball mill for approximately 4 hours so as to have a composition (Sr


1−x


M1


x


)Bi


2


(Nb


1−y


W


y


)


2


O


9


+z percent by weight of MnCO


3


, wherein M1 is one of divalent metals other than Sr and trivalent metals other than Bi0≦x≦0.35, 0≦y≦0.35, and 0≦z≦1.1, or to have a composition (Sr


1−x


M2


2x/3


)Bi


2


(Nb


1−y


W


y


)


2


O


9


+z percent by weight of MnCO


3


, wherein M2 is a trivalent metal other than Bi, 0≦x≦0.5, 0≦y≦0.35, and 0≦z≦1.1. The mixture was dried and calcined at 700 to 900° C. The calcined mixture was roughly pulverized and finely pulverized together with a proper amount of organic binder by a wet process for 4 hours. The pulverized powder was screened using a 40-mesh sieve to adjust the particle size. The powder was pressed under a pressure of 1.000 kg/cm


2


to form a disk with a diameter of 12.5 mm and a thickness of1 mm. The disk was sintered at 900 to 1,250° C. in the air to form a disk ceramic. A silver paste was applied onto both main faces of the disk ceramic to form silver electrodes. A DC voltage of 5 to 10 kV/mm was applied between the silver electrodes for 10 to 30 minutes in an insulating oil at 150 to 200° C. for polarization. A piezoelectric ceramic sample was thereby prepared. Similarly, piezoelectric ceramic samples were prepared in which the types of the M1 or M2, the M1, the M2 contents (x or k) and the W contents (y) were different.




A half of the subscript x in the above formula (Sr


1−x


M1


x


)Bi


2


(Nb


1−y


W


y


)


2


O


9


correspond to the content of the divalent or trivalent metal with respect to 1 mole of Bi in the above formula fourth aspect. Similarly, one-third of the subscript x in the above formula (Sr


1−x


M1


x


)Bi


2


(Nb


1−y


W


y


)


2


O


9


corresponds to the content of the divalent or trivalent metal with respect to 1 mole of Bi in the main component in the fourth aspect.




The density, resistivity and electromechanical coupling coefficient kt of each sample were measured. Table 1 to 3 show these results, in addition to the type of the M1 or M2, x or k, y, the MnCO


3


content and the sintering temperature. In Tables 1 to 3, a Sample No. with an asterisk indicates a sample outside the ranges of the present invention.




















TABLE 1














Sintering









Sample







MnCO


3






Temp.




Density




Resistivity




kt






No.




M1




x




y




(wt %)




(° C.)




(g/cm


3


)




(Ω · cm)




(%)































 1*









0




0




0




1,100




5.70




5.0 × 10


8 






Unpolarized






2









0




0.1




0




1,100




6.85




3.0 × 10


12






13.1






3









0




0.3




0




1,100




6.96




4.0 × 10


12






11.8






 4*









0




0.35




0




1,100




6.80




3.0 × 10


12






 8.8






 5*









0




0




0.5




1,250




6.96




6.0 × 10


12






17.6






 6*









0




0




0.5




1,100




6.05




2.0 × 10


9 






Unpolarized






7









0




0.05




0.5




1,100




6.98




8.0 × 10


12






17.9






8









0




0.1




0.5




1,100




7.01




6.0 × 10


12






17.3






9









0




0.1




0.5




1,000




6.99




8.0 × 10


11






16.0






10 









0




0.3




0.5




1,100




7.02




5.0 × 10


12






15.7






11*









0




0.35




0.5




1,100




6.98




2.0 × 10


12






 8.1






12*









0




0.35




0.5




1,000




6.65




2.0 × 10


10






 6.5






13*









0




0.35




0.5




  900




5.65




5.0 × 10


8 






Unpolarized






14*









0




0




1.0




1,100




5.98




1.0 × 10


9 






Unpolarized






15 









0




0.3




1.0




1,100




6.97




4.0 × 10


12






14.6






16*









0




0.35




1.0




1,100




6.84




2.0 × 10


12






 8.0






17 









0




0.1




1.1




1,100




6.96




7.0 × 10


9 






11.8






18 









0




0.3




1.1




1,100




6.95




5.0 × 10


9 






10.8






19*




Ca




0.1




0




0.5




1,100




6.07




4.0 × 10


9 






Unpolarized






20 




Ca




0.1




0.1




0.5




1,100




7.05




6.0 × 10


12






18.3






21 




Ca




0.1




0.3




0.5




1,100




7.07




6.0 × 10


12






16.6






22*




Ca




0.1




0.35




0.5




1,100




6.98




2.0 × 10


12






 9.1






23*




Ca




0.3




0




0.5




1,100




6.07




2.0 × 10


13






Unpolarized






24 




Ca




0.3




0.1




0.5




1,100




7.07




2.0 × 10


13






20.9






25 




Ca




0.3




0.3




0.5




1,100




7.07




1.0 × 10


13






19.1






























TABLE 1














Sintering









Sample







MnCO


3






Temp.




Density




Resistivity




kt






No.




M1




x




y




(wt %)




(° C.)




(g/cm


3


)




(Ω · cm)




(%)































 1*









0




0




0




1,100




5.70




5.0 × 10


8 






Unpolarized






2









0




0.1




0




1,100




6.85




3.0 × 10


12






13.1






3









0




0.3




0




1,100




6.96




4.0 × 10


12






11.8






 4*









0




0.35




0




1,100




6.80




3.0 × 10


12






 8.8






 5*









0




0




0.5




1,250




6.96




6.0 × 10


12






17.6






 6*









0




0




0.5




1,100




6.05




2.0 × 10


9 






Unpolarized






7









0




0.05




0.5




1,100




6.98




8.0 × 10


12






17.9






8









0




0.1




0.5




1,100




7.01




6.0 × 10


12






17.3






9









0




0.1




0.5




1,000




6.99




8.0 × 10


11






16.0






10 









0




0.3




0.5




1,100




7.02




5.0 × 10


12






15.7






11*









0




0.35




0.5




1,100




6.98




2.0 × 10


12






 8.1






12*









0




0.35




0.5




1,000




6.65




2.0 × 10


10






 6.5






13*









0




0.35




0.5




  900




5.65




5.0 × 10


8 






Unpolarized






14*









0




0




1.0




1,100




5.98




1.0 × 10


9 






Unpolarized






15 









0




0.3




1.0




1,100




6.97




4.0 × 10


12






14.6






16*









0




0.35




1.0




1,100




6.84




2.0 × 10


12






 8.0






17 









0




0.1




1.1




1,100




6.96




7.0 × 10


9 






11.8






18 









0




0.3




1.1




1,100




6.95




5.0 × 10


9 






10.8






19*




Ca




0.1




0




0.5




1,100




6.07




4.0 × 10


9 






Unpolarized






20 




Ca




0.1




0.1




0.5




1,100




7.05




6.0 × 10


12






18.3






21 




Ca




0.1




0.3




0.5




1,100




7.07




6.0 × 10


12






16.6






22*




Ca




0.1




0.35




0.5




1,100




6.98




2.0 × 10


12






 9.1






23*




Ca




0.3




0




0.5




1,100




6.07




2.0 × 10


13






Unpolarized






24 




Ca




0.3




0.1




0.5




1,100




7.07




2.0 × 10


13






20.9






25 




Ca




0.3




0.3




0.5




1,100




7.07




1.0 × 10


13






19.1






























TABLE 3














Sintering









Sample







MnCO


3






Temp.




Density




Resistivity




kt






No.




M


2






x′




y




(wt %)




(° C.)




(g/cm


3


)




(Ω · cm)




(%)































49*




La




0.15




0




0.5




1,100




6.01




2.0 × 10


9 






Unpolarized






50 




La




0.15




0.1




0.5




1,100




6.87




4.0 × 10


12






15.8






51 




La




0.15




0.3




0.5




1,100




6.75




4.0 × 10


12






14.3






52*




La




0.15




0.35




0.5




1,100




6.52




5.0 × 10


11






 7.2






53*




La




0.45




0




0.5




1,100




5.99




1.0 × 10


9 






Unpolarized






54 




La




0.45




0.1




0.5




1,100




6.75




4.0 × 10


12






14.7






55 




La




0.45




0.3




0.5




1,100




6.76




4.0 × 10


12






13.9






56*




La




0.45




0.35




0.5




1,100




6.29




4.0 × 10


11






 6.6






57 




La




0.5




0.1




0.5




1,100




6.50




4.0 × 10


9 






10.4






58*




Nd




0.15




0




0.5




1,100




5.98




2.0 × 10


9 






Unpolarized






59 




Nd




0.15




0.1




0.5




1,100




6.90




4.0 × 10


12






15.9






60 




Nd




0.15




0.3




0.5




1,100




6.86




4.0 × 10


12






14.7






61*




Nd




0.15




0.35




0.5




1,100




6.59




5.0 × 10


11






 7.9














As shown in Tables 1 to 3, the samples in accordance with the present invention have electromechanical coupling coefficients kt which are at practical levels when the samples are sintered at a temperature of 1,100° C. or less.




The piezoelectric ceramic composition in accordance with the present invention is not limited to the above EXAMPLES and may have other formulations within the scope of the present invention.




While preferred embodiments of the invention have been disclosed, various modes of carrying out the principles disclosed herein are contemplated as being within the scope of the following claims. Therefore, it is understood that the scope of the invention is not to be limited except as otherwise set forth in the claims.



Claims
  • 1. A piezoelectric ceramic composition comprising a main component represented by the general formula (Sr1−xM1x)Bi2(Nb1−yWy)2O9, wherein M1 is at least one element selected from the group consisting of divalent metals other than Sr and trivalent metals other than Bi, 0≦x≦0.3, and 0<y≦0.3.
  • 2. A piezoelectric ceramic composition according to claim 1, further comprising manganese as an auxiliary component in an amount of more than 0 to about 1.0 percent by weight calculated as MnCO3.
  • 3. A piezoelectric ceramic composition according to claim 1 wherein x is 0 and the main component is represented by the general formula SrBi2(Nb1−yWy)2O9.
  • 4. A piezoelectric ceramic composition according to claim 1, wherein said M1 is at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.
  • 5. A piezoelectric ceramic composition according to claim 1, wherein said M1 is selected from the group consisting of Ca, Ba, La, Nd, Sm and Y.
  • 6. A piezoelectric ceramic composition according to claim 1 comprising a main component represented by the general formula (Sr1−xM12x/3)Bi2(Nb1−yWy)2O9, wherein M1 is a trivalent metal other than Bi, and 0<x≦0.45.
  • 7. A piezoelectric ceramic composition according to claim 6, wherein M1 is at least one element selected from the group consisting of La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.
  • 8. A piezoelectric ceramic composition according to claim 6, wherein M1 is La or Nd.
  • 9. A piezoelectric ceramic composition comprising a main component represented by the general formula SrBi2Nb2O9 and containing more than 0 to about 0.3 mole of W with respect to 1 mole of Bi in the main component.
  • 10. A piezoelectric ceramic composition according to claim 9, further comprising a divalent metal other than Sr or trivalent metal other than Bi in an amount of more than 0 to about 0.15 mole with respect to 1 mole of Bi in the main component.
  • 11. A piezoelectric ceramic composition according to claim 10, wherein said divalent metal other than Sr or trivalent metal other than Bi is at least one element selected from the group consisting of Ca, Ba, Mg, La, Ce, Pr, Nd, Sm, Gd, Dy, Er, Yb, Sc and Y.
  • 12. A piezoelectric ceramic composition according to claim 9, further comprising manganese as an auxiliary component in an amount of more than 0 to about 1.0 percent by weight calculated as MnCO3.
  • 13. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 12; and a pair of electrodes thereon.
  • 14. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 9; and a pair of electrodes thereon.
  • 15. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 6; and a pair of electrodes thereon.
  • 16. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 3; and a pair of electrodes thereon.
  • 17. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 2; and a pair of electrodes thereon.
  • 18. A piezoelectric ceramic device comprising:a piezoelectric ceramic comprising a piezoelectric ceramic composition according to claim 1; and a pair of electrodes thereon.
Priority Claims (4)
Number Date Country Kind
11-030323 Feb 1999 JP
11-138164 May 1999 JP
11-291255 Oct 1999 JP
2000-007999 Jan 2000 JP
US Referenced Citations (2)
Number Name Date Kind
4978646 Bardhan et al. Dec 1990
6117354 Kimura et al. Sep 2000
Non-Patent Literature Citations (1)
Entry
Database WPI, Section Ch, Week 199703; Derwent Publications, Ltd., London GB; Class L03, An 1997-029376; XP002143528 & JP 08 290964 A (Sumitomo Chem. Co., Ltd.) Nov. 5, 1996; Abstract.