Piezoelectric ceramic composition

Abstract

Improved are the piezoelectric characteristics of conventional ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 where 0.ltoreq.x.ltoreq.1, and provided is a novel piezoelectric ceramic composition which does not contain lead and which can be practiced industrially as a material for piezoelectric ceramic devices such as piezoelectric ceramic filters, etc. The piezoelectric ceramic composition comprises, as the essential component, a ceramic component of the general formula, (1-y)(Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --yNaNbO.sub.3 where 0.ltoreq.x.ltoreq.1 and 0.15.ltoreq.y<1/3. Preferably, the composition contains, as the side component, at least one oxides of Mn, Cr, W, Si, Mo, Ni, Co, Sn, Mg, Sb, Ti, Zr and Fe, in a total amount of not larger than about 5% by weight in terms of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3, respectively.

Description

FIELD OF THE INVENTION

The present invention relates to a piezoelectric ceramic composition, particularly to a piezoelectric ceramic composition which is usable in the field of electronic parts as a material for piezoelectric ceramic devices such as piezoelectric ceramic filters, piezoelectric ceramic oscillators, etc.

BACKGROUND OF THE INVENTION

Piezoelectric ceramic compositions consisting essentially of lead titanate zirconate or lead titanate are widely used in piezoelectric ceramic devices such as piezoelectric ceramic filters, etc.

Known as piezoelectric materials are compounds containing Ba, Sr, Na, Nb, O and the like. For example, Ba.sub.2 NaNb.sub.5 O.sub.15, Sr.sub.2 NaNb.sub.5 O.sub.15 and the like are known as materials having piezoelectric characteristics and electro-optical effects, and single crystals of those compounds have been being widely studied. However, few studies have been made on the use of those compounds. In 1989, J. R. Oliver et al. (J. Am. Ceram. Soc., 72 �2! 202-11 (1989)) reported the ferroelectricity of ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 (0.ltoreq.x.ltoreq.1) , but they did not refer in detail to the piezoelectric characteristics of those ceramics.

Conventional piezoelectric ceramic compositions consisting essentially of lead titanate zirconate or lead titanate, which have heretofore been used widely, contain lead, and are therefore not so favorable from the viewpoint of environmental protection. To produce the conventional compositions, generally used are lead oxides. The lead oxides used easily vaporize, resulting in that it is relatively difficult to control the quality of the products produced.

On the other hand, ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 (0.ltoreq.x.ltoreq.1) do not contain lead and are therefore free from the problems mentioned above. However, those ceramics are inferior to the piezoelectric ceramic compositions consisting essentially of lead titanate zirconate or lead titanate in point of their piezoelectric characteristics as indicated by, for example, the electromechanical coupling factor and the piezoelectric constant, and therefore they have not been practiced industrially as materials for piezoelectric ceramic devices such as piezoelectric ceramic filters, piezoelectric ceramic oscillators, etc.

Given that situation, the object of the present invention is to improve the piezoelectric characteristics of those (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 (0.ltoreq.x.ltoreq.1) ceramics and to provide a novel piezoelectric ceramic composition which does not contain lead and which can be used industrially as a material for piezoelectric ceramic devices such as piezoelectric ceramic filters, piezoelectric ceramic oscillators, etc.

SUMMARY OF THE INVENTION

In order to solve the technical problems mentioned hereinabove, the present invention provides a piezoelectric ceramic composition comprising, as the essential component, a ceramic component represented by a general formula (1-y) (Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --yNaNbO.sub.3 where 0.ltoreq.x.ltoreq.1 and 0.15.ltoreq.y&lt;1/3. Preferably, x is about 0.25-0.75 and y is about 0.2-0.3.

In the formula, 0.15.ltoreq.y&lt;1/3. This is because when y&lt;0.15, polarizable piezoelectric ceramics could not be obtained. If y.gtoreq.1/3, the composition does not have satisfactory piezoelectric characteristics.

Preferably, the piezoelectric ceramic composition contains, as a side component, at least one oxide of Mn, Cr, W, Si, Mo, Ni, Co, Sn, Mg, Sb, Ti, Zr and Fe, in a total amount of not larger than about 5% by weight in terms of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3, respectively.

The side component, if added to the composition, is effective in further improving the piezoelectric characteristics of the composition. The total amount of the side component in the composition is defined to be not larger than about 5% by weight. This is because if it is larger than about 5% by weight, polarizable piezoelectric ceramics are difficult to obtain.

In another aspect of the invention, there is provided a piezoelectric ceramic composition comprising, as the essential component, a ceramic component represented by a general formula (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 where 0.ltoreq.x.ltoreq.1, and containing, as a side component, an oxide of Mn in an amount of not larger than about 5% by weight in terms of MnO.sub.2.

The amount of the Mn oxide is defined to be not larger than about 5% by weight for the same reason as above, that is, if the amount of the Mn oxide in the composition is larger than about 5% by weight, polarizable piezoelectric ceramics are difficult to obtain.

DESCRIPTION OF PREFERRED EMBODIMENTS OF THE INVENTION

Now, some preferred embodiments of the invention are described below, which, however, are not intended to restrict the scope of the invention.

EXAMPLE 1

First prepared were starting materials of BaCO.sub.3, SrCO.sub.3, Na.sub.2 CO.sub.3, Nb.sub.2 O.sub.5 and MnCO.sub.3.

Next, these materials were weighed to give a component of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 where x is as in Table 1 below. For some samples, the materials were weighed to have the MnO.sub.2 content as in Table 1. The thus-weighed materials were wet-milled in a ball mill for about 4 hours, and the resulting mixture was dried and then calcined at 700 to 900.degree. C.

Each of the thus-dried mixture was roughly ground and a suitable amount of an organic binder added. Then, this was ground still wet for about 4 hours, using a ball mill, and thereafter sieved through a 40-mesh sieve.

Next, each of the thus-sieved samples was press-shaped under a pressure of 1000 kg/cm.sup.2 to obtain circular discs each having a diameter of 12 mm and a thickness of 1.2 mm. These discs were baked at a temperature falling between 1150 and 1350.degree. C. in the usual manner to obtain sintered ceramic discs.

A silver paste was applied onto the both surfaces of those sintered ceramic discs and baked to form silver electrodes thereon in a conventional manner. Then, a direct-current voltage of from 5 to 15 kV/mm was applied to those discs for 30 to 120 minutes in an insulating oil at 100 to 200.degree. C. thereby polarizing the discs. Thus were finally obtained piezoelectric ceramic disc samples.

These samples were tested to obtain their relative dielectric constant (e), electromechanical coupling factor (Kt) of the vibration in the direction of the thickness, and piezoelectric constant (d.sub.33). The data obtained are shown in Table 1.

TABLE 1______________________________________ Amount of MnO.sub.2 Relative Coupling PiezoelectricSample Added Dielectric Factor, Kt Constant, d.sub.33No. x (wt. %) Constant, e (%) (pC/N)______________________________________1 0.0 0 174 10.2 132 0.25 0 394 10.7 173 0.5 0 779 11.4 334 0.75 0 1113 10.8 365 1.0 0 933 9.9 416 0.0 0.5 198 11.9 187 0.25 0.5 413 12.5 228 0.5 0.5 822 14.1 399 0.75 0.5 1177 13.2 4210 1.0 0.5 1163 12.8 4911 0.5 0.1 800 15.1 5112 0.5 2.0 968 12.8 3613 0.5 5.0 1052 12.3 2214 0.5 6.0 Non-polarized______________________________________

In Table 1, sample No. 6 to sample No. 13 are within the scope of the invention.

As seen in Table 1, sample Nos. 6 to 13 are all superior to sample Nos. 1 to 5 which are conventional ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 (0.ltoreq.x.ltoreq.1) in point of the electromechanical coupling factor (Kt) of the vibration in the direction of the thickness.

Sample No. 14 contained 6.0% by weight of MnO.sub.2, which does not satisfy the requirement for the MnO.sub.2 content of not larger than about 5% by weight. Sample No. 14 could not be polarized.

EXAMPLE 2

First prepared were starting materials of BaCO.sub.3, SrCO.sub.3, Na.sub.2 CO.sub.3, Nb.sub.2 O.sub.5, MnCO.sub.3, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3.

Next, these materials were weighed to give a component of (1-y) (Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --yNaNbO.sub.3 where x and y are as in Table 2 below. To specific samples, the side component shown in Table 2 was added. Next, these materials were processed in the same manner as in Example 1 to finally obtain piezoelectric ceramic disc samples.

These samples were tested to obtain their relative dielectric constant (e), electromechanical coupling factor (Kt) of the vibration in the direction of the thickness, and piezoelectric constant (d.sub.33). The data obtained are shown in Table 2.

TABLE 2______________________________________ Amount of Side Relative Component Dielectric Coupling PiezoelectricSample Added Constant, Factor, Kt Constant, d.sub.33No. x y (wt. %) e (%) (pC/N)______________________________________15 0.0 1/3 Not added 174 10.2 1316 0.5 1/3 Not added 779 11.4 3317 1.0 1/3 Not added 1103 9.9 3618 0.0 0.3 Not added 166 13.7 2219 0.5 0.3 Not added 533 15.6 4320 1.0 0.3 Not added 998 12.3 4121 0.0 0.2 Not added 154 14.4 2522 0.3 0.2 Not added 316 17.7 3123 0.5 0.2 Not added 502 21.0 4524 0.7 0.2 Not added 991 18.1 4625 1.0 0.2 Not added 964 16.7 4626 0.0 0.2 MnO.sub.2 /1.0 182 15.7 2727 0.5 0.2 MnO.sub.2 /1.0 763 25.1 5128 0.5 0.2 MnO.sub.2 /5.0 1063 23.0 4729 0.5 0.2 MnO.sub.2 /6.0 Non-polarized30 1.0 0.2 MnO.sub.2 /1.0 1091 19.7 4931 0.0 0.2 Cr.sub.2 O.sub.3 /1.0 177 15.4 2532 0.5 0.2 Cr.sub.2 O.sub.3 /1.0 781 21.3 4633 1.0 0.2 Cr.sub.2 O.sub.3 /1.0 1211 18.3 4934 0.0 0.2 WO.sub.3 /1.0 169 20.4 3035 0.5 0.2 WO.sub.3 /1.0 721 24.4 5336 1.0 0.2 WO.sub.3 /1.0 960 20.0 5037 0.5 0.2 SiO.sub.2 /1.0 692 19.8 4938 0.5 0.2 MoO.sub.3 /1.0 777 21.8 5239 0.5 0.2 NiO/1.0 602 18.8 3740 0.5 0.2 Co.sub.2 O.sub.3 /1.0 732 20.8 4741 0.5 0.2 SnO.sub.2 /1.0 741 24.8 5142 0.5 0.2 MgO/1.0 722 22.3 4643 0.5 0.2 Sb.sub.2 O.sub.3 /1.0 792 21.9 4944 0.5 0.2 TiO.sub.2 /1.0 724 21.1 4845 0.5 0.2 ZrO.sub.2 /1.0 836 20.2 5046 0.5 0.2 Fe.sub.2 O.sub.3 /1.0 803 21.8 5047 0.0 0.15 Not added 116 13.3 1748 0.5 0.15 Not added 524 14.2 3749 1.0 0.15 Not added 1020 12.1 3850 0.0 0.1 Not added Non-polarized51 0.5 0.1 Not added Non-polarized52 1.0 0.1 Not added Non-polarized______________________________________

In Table 2, sample No. 18 to sample No. 29 and sample No. 30 to sample No. 49 are within the scope of the invention.

As shown in Table 2, sample Nos. 18 to 28 and Nos. 30 to 49 are all superior to sample Nos. 1 to 5 in Table 1, which are conventional ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 (0.ltoreq.x.ltoreq.1), in point of the electromechanical coupling factor (Kt) of the vibration in the direction of the thickness.

In particular, sample Nos. 26 to 28 and Nos. 30 to 46, which contain, as the side component, any of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3 in an amount not larger than about 5% by weight, are especially good in point of the electromechanical coupling factor (Kt).

It has been confirmed that the side component may be comprised of two or more of those oxides so far as its total amount is defined to be not larger than about 5% by weight. Preferably the amount is less that 2%.

Sample No. 29 contains, as the side component, MnO.sub.2 in an amount of 6.0% by weight. Sample No. 29 could not be polarized under the condition employed herein. From this, it is understood that the amount of the side component, if added, is desirably not larger than about 5% by weight for attaining easy polarization of the piezoelectric ceramic composition.

Sample Nos. 15 to 17 and Nos. 50 to 52 in Table 2 are outside the scope of the invention. In sample Nos. 15 to 17, y=1/3. In other words, these samples do not satisfy the requirement for y&lt;1/3. These sample Nos. 15 to 17 do not have a satisfactory electromechanical coupling factor (Kt). In sample Nos. 50 to 52, y=0.1. In other words, these samples do not satisfy the requirement for y.gtoreq.0.15. These sample Nos. 50 to 52 could not be polarized.

OTHER EXAMPLES

The piezoelectric ceramic composition of the invention is not limited to the embodiments of Examples 1 and 2, but can be variously modified without overstepping the scope of the invention.

As has been mentioned hereinabove and is obvious from the data in Examples 1 and 2, the invention has improved the piezoelectric characteristics of the conventional ceramics of (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 where 0.ltoreq.x.ltoreq.1, and has provided a novel piezoelectric ceramic composition which does not contain lead and which can be used practically as a material for piezoelectric ceramic devices such as piezoelectric ceramic filters, piezoelectric ceramic oscillators, etc.

In particular, where the piezoelectric ceramic composition of the invention which comprises, as the essential component, a ceramic component represented by the general formula, (a) (Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --(b)NaNbO.sub.3 (where 0.ltoreq.x.ltoreq.1) and contains, as the side component, at least one oxides of Mn, Cr, W, Si, Mo, Ni, Co, Sn, Mg, Sb, Ti, Zr and Fe, in a total amount of not larger than about 5% by weight in terms of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3, respectively, and either a=(1-y) and b=y where 0.15.ltoreq.y.ltoreq.1/3 or a=2 and b=1 and Mn oxide is present, the piezoelectric characteristics are improved.

While the invention has been described in detail and with reference to specific embodiments thereof, it will be apparent to one skilled in the art that various changes and modifications can be made therein without departing from the spirit and scope thereof.

Claims

1. A piezoelectric ceramic composition comprising a main component represented by the general formula, (a) (Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --(b)NaNbO.sub.3 where 0.ltoreq.x.ltoreq.1 and either (A) a is 1-y and b is y and 0.15.ltoreq.y&lt;1/3 or (B) a is 2 and b is 1 and present is an oxide of Mn in an amount of not larger than about 5% by weight in terms of MnO.sub.2.

2. A piezoelectric ceramic composition comprising a main component represented by the general formula, (1-y) (Ba.sub.1-x Sr.sub.x)Nb.sub.2 O.sub.6 --yNaNbO.sub.3 where 0.ltoreq.x.ltoreq.1 and 0.15.ltoreq.y&lt;1/3.

3. The piezoelectric ceramic composition according to claim 2, wherein x is about 0.25-0.75 and y is about 0.2-0.3.

4. The piezoelectric ceramic composition according to claim 3 further comprising at least one member selected from the group consisting of the oxides of Mn, Cr, W, Si, Mo, Ni, Co, Sn, Mg, Sb, Ti, Zr and Fe, in a total amount of not larger than about 5% by weight in terms of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, CO.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3, respectively.

5. The piezoelectric ceramic composition according to claim 4 in which the amount of said oxide is less than 2% by weight.

6. The piezoelectric ceramic composition according to claim 2 further comprising at least one member selected from the group consisting of the oxides of Mn, Cr, W, Si, Mo, Ni, Co, Sn, Mg, Sb, Ti, Zr and Fe, in a total amount of not larger than about 5% by weight in terms of MnO.sub.2, Cr.sub.2 O.sub.3, WO.sub.3, SiO.sub.2, MoO.sub.3, NiO, Co.sub.2 O.sub.3, SnO.sub.2, MgO, Sb.sub.2 O.sub.3, TiO.sub.2, ZrO.sub.2 and Fe.sub.2 O.sub.3, respectively.

7. Th e piezoelectric ceramic composition according to claim 6 in which the amount of said oxide is less than 2% by weight.

8. A piezoelectric ceramic composition comprising a ceramic component represented by the general formula (Ba.sub.1-x Sr.sub.x).sub.2 NaNb.sub.5 O.sub.15 where 0.ltoreq.x.ltoreq.1, and containing an oxide of Mn in an amount of not larger than about 5% by weight in terms of MnO.sub.2.

9. The piezoelectric ceramic composition according to claim 8 in which the amount of said oxide is less than 2% by weight.

10. The piezoelectric ceramic composition according to claim 6, wherein x is about 0.25-0.75.

11. The piezoelectric ceramic composition according to claim 10 in which the amount of said oxide is less than 2% by weight.

12. A polarized piezoelectric ceramic composition according to claim 10.

13. A polarized piezoelectric ceramic composition according to claim 8.

14. A polarized piezoelectric ceramic composition according to claim 6.

15. A polarized piezoelectric ceramic composition according to claim 4.

16. A polarized piezoelectric ceramic composition according to claim 3.

17. A polarized piezoelectric ceramic composition according to claim 2.

18. A polarized piezoelectric ceramic composition according to claim 1.