The invention relates to the modification of piezoelectric ceramic materials based on lead zirconate titanate (PZT).
The properties of piezoceramic multi-layer actuators based on lead zirconate titanate are determined to a great extent by the compatibility of low-sintering PZT-ceramic with the AgPd internal metalization during co-firing.
It should be noted here that Ag ions in PZT modifications have high diffusivity at high temperatures (>800° C.) and also act as an acceptor dopant when incorporated into the PZT system. A non-, or only partly, compensated acceptor substitution by donor ions such as Nb5+ can lead to drastic changes in the ferroelectric properties and thus also in the deformation behavior of actuator materials. This effect must be taken into account when selecting the AgPd alloy for the internal electrodes. There is a limit to how far the content of the noble metal palladium can be reduced, as an increase in the silver content of the internal electrodes leads to increased diffusion of the silver in the piezoceramic.
The use of the alloy AgPd 70/30 for the internal metalization fulfills the premises for compatibility with the piezoceramic in the cofiring process. A Pd content of ≧30% has the effect of preventing the diffusion of silver.
Ag-additives to originally valence-compensated PZT modifications act as acceptor dopants, which influence the polarity behavior. This also results in a reduction in deformation in the vicinity of an electric field.
Accordingly, the deformation characteristic is not stabilized by anticipating the introduction of Ag+ ions when sintering piezoceramic laminates with AgPd internal metalization by adding Ag when formulating the composition of conventionally modified PZT compositions.
The object of the invention is to prevent diffusion of Ag in the ceramic material as far as possible in spite of a reduced Pd content of the electrode material.
The object is achieved with the aid of the present invention.
The invention consists in that in the modifications of piezoelectric ceramic materials based on lead zirconate titanate as valence-compensated compositions with n complex compounds in the multi-component systems with the general formula PbTiO3—PbZrO3-ΣnAM′αM″βO3 with heterovalent ions, at least one ion M′ is represented by Ag+ and M″ are pentavalent cations of Sb, Ta, Nb, wherein n≦3, α=¼, β=¾, the content of the respective complex compounds being ≦20 mol % and A≡A2+, populated by ions of the elements Pb, Ba, Ca, or Sr.
The multi-component systems with the general formula PbTiO3—PbZrO3-ΣnA′αA″βBO3 with heterovalent ions are modified so that at least one ion A′ is represented by Ag+ and A″ are trivalent cations of Bi, La, Nd, wherein n≦3, α=β=½, the content of the respective complex compounds being ≦20 mol % and B≡B4+, populated by ions of the elements Ti or Zr.
In the modified system, the hypothetical complex Sr (Ag0.25Nb0.75)O3 in a PZT-SAN (1−y)Pb(ZrxTi1-x)O3-ySr(Ag0.25Nb0.75)O3 system, for example, may be considered as a coupled substitution of Ag+ acceptor ions and Nb5+ donor ions.
The composition 0.98Pb(Zr0.52Ti0.48)O3-0.02Sr(Ag0.25Nb0.75)O3 of the PZT-SAN system with an Ag content of 0.178 wt. % was compared with the model substance with the non-stoichiometric composition 0.98Pb(Zr0.52Ti0.48)O3-0.02Sr(Ag0.00Nb0.75)O3 without Ag+ ions for acceptor-donor valence compensation. The properties show that it is not possible to achieve valence compensation by removing the acceptor deficit via the diffusion of Ag from the internal electrodes. The deformation of the non-stoichiometric composition is substantially less than that of the stoichiometric composition.
The invention is explained in more detail with the aid of an embodiment. The polarization and deformation behavior of laminates with and without internal electrodes was investigated. The interaction of the modified PZT ceramics with different AgPd alloys (AgPd 70/30 and AgPd 85/15) during cofiring of the laminates is assessed and a solution for the reduction of the Pd content <30 is indicated.
Knowledge of effective x- and y-concentrations arises from the development of the PZT system: The properties relevant for the application of the modified PZT ceramics for sensors and actuators can be optimized in a narrow concentration range of x=0.46 to 0.49 for y=0.02. Accordingly, in an example, a PZT-SAN composition series 0.98 Pb(ZrxTi1-x)O3-0.02 Sr(Ag0.25Nb0.75)O3 for x=0.51 to 0.55 was formulated in steps from Δx=0.005 and synthesized by the mixed oxide method.
When synthesizing (sintering) the PZT-SAN ceramics, an increased action of Ag+ ions as acceptor dopants with coupled substitution of Nb5+ donor ions was already
The characteristic functional properties (piezoelectric and dielectric coefficients) of the compositions 0.98Pb(Zr0.52Ti0.48)O3-0.02Sr(Ag0.25Nb0.75)O3 and 0.98Pb(Zr0.53Ti0.47)O3-0.02Sr(Ag0.25Nb0.75)O3 from this series of compositions are given in the following table as examples.
Dielectric and electromechanical properties of PZT-SAN ceramics
When forming valence-compensated compositions of the PZT-SAN system, a high level of deformation is obtained upon polarization.
The influence of the diffusion of silver during cofiring of the laminates with internal electrodes of differing Pd contents is less pronounced. The values of the coercive field strength and deformation for the composition 0.98Pb(Zr0.52Ti0.48)O3-0.02Sr(Ag0.25Nb0.75)O3 of the PZT-SAN system for example are virtually the same for both internal metalizations, as can be seen from
Reducing the diffusion of silver during cofiring of laminates with internal electrodes makes it possible to use AgPd alloys with reduced Pd content. The values of coercive field strength and deformation for the composition of 0.98Pb(Zr0.52Ti0.48)O3-0.02Sr(Ag0.25Nb0.75)O3 of the PZT-SAN system for internal metalization with AgPd 70/30 and AgPd 85/15 are virtually the same. When using Ag+ ions to form valence-compensated compositions of the PZT system, a high level of deformation is still obtained, i.e. the acceptor-donor action of the system is very similar to that of the conventionally modified PZT system without internal electrodes, as can be seen from
Number | Date | Country | Kind |
---|---|---|---|
101 48 333 | Sep 2001 | DE | national |
102 31 471 | Jul 2002 | DE | national |
Filing Document | Filing Date | Country | Kind | 371c Date |
---|---|---|---|---|
PCT/DE02/03656 | 9/26/2002 | WO | 00 | 5/24/2004 |
Publishing Document | Publishing Date | Country | Kind |
---|---|---|---|
WO03/029164 | 4/10/2003 | WO | A |
Number | Name | Date | Kind |
---|---|---|---|
3518198 | Akashi et al. | Jun 1970 | A |
5164882 | Kanai et al. | Nov 1992 | A |
6230378 | Cramer et al. | May 2001 | B1 |
Number | Date | Country |
---|---|---|
WO 0193345 | Dec 2001 | WO |
Number | Date | Country | |
---|---|---|---|
20040238784 A1 | Dec 2004 | US |