Patent Grant
8871111
1. Field of the Invention
The present invention relates to a piezoelectric/electrostrictive ceramic composition.
2. Description of the Background Art
Piezoelectric/electrostrictive devices used in diesel engine injectors and the like employ an Ag/Pd-based electrode as their inner electrode in view of costs. Since the Ag/Pd-based electrode has a low melting point, it is required to reduce the firing temperature of such piezoelectric/electrostrictive ceramics. To be more specific, piezoelectric/electrostrictive ceramic compositions that are densified at a firing temperature of less than 1000° C. are desired. To this end, using a sintering agent to reduce the firing temperature has been considered. The use of a sintering agent, however, has a drawback in that the original piezoelectric/electrostrictive properties may be reduced.
Japanese Patent Application Laid-open No. 2006-188414 discloses a substance represented by the general formula: xBiMeO3-yPbZrO3-(1-x-y)PbTiO3 (where Me is Sc and/or In.) In Japanese Patent Application Laid-open No. 2008-94707, an element is selected based on the ionic radius in a perovskite structure, Bi(Al, Fe, M)O3, with Bi at the A site (M is at least any one of Cr, Mn, Co, Ni, Ga, and Sc). These composition design may promote deformation due to the tolerance factor calculated from the ionic radius, but in practical cases, satisfactory piezoelectric characteristics can not be obtained because the perovskite structure is hard to be synthesized, or availability in practical application can not be realized because of low density or because of low insulating performance due to the volatilization of the element Bi at high temperatures.
The present invention has been made in view of these conventional problems and has an object to provide a piezoelectric/electrostrictive ceramic composition with high density and excellent crystallinity, even in the case of firing under lower temperature conditions than in conventional cases; and with excellent piezoelectric/electrostrictive properties.
According to an aspect of the present invention, a piezoelectric/electrostrictive ceramic composition contains: a first main component composed of an ABO3 compound with Bi at the A site that has a valence of three and with B1 and B2 elements at the B site that has a valence of three; and a second main component composed of an ABO3 compound with at least Pb at the A site. The B1 element consists of at least one kind of element having an ionic valence of two or less and selected from the group consisting of Mg, Cr, Mn, Fe, Co, Ni, Cu, Zn, and rare-earth elements. The B2 element consists of at least one kind of element having an ionic valence of four or more and selected from the group consisting of V, Nb, Ta, Sb, Mo, and W.
According to another aspect of the present invention, the piezoelectric/electrostrictive ceramic composition contains: a first main component composed of an ABO3 compound with Bi at the A site that has a valence of three and with B1 and B2 elements at the B site that has a valence of three; and a second main component composed of an ABO3 compound with at least Pb at the A site and with at least two kinds of elements selected from the group consisting of Mg, Al, Sc, Ga, Cr, Mn, Fe, Co, Ni, Cu, Zn, V, Nb, Ta, Sb, Mo, W, In, Ti, Zr, Hf, and rare-earth elements at the B site that has a valence of four. The B1 element consists of at least one kind of element having an ionic valence of two or less and selected from the group consisting of Mg, Cr, Mn, Fe, Co, Ni, Cu, Zn, and rare-earth elements. The B2 element consists of at least one kind of element having an ionic valence of four or more and selected from the group consisting of V, Nb, Ta, Sb, Mo, and W.
According to still another aspect of the present invention, the piezoelectric/electrostrictive ceramic composition contains: a first main component composed of an ABO3 compound with Bi at the A site that has a valence of three and with an element selected from the group consisting of Mg, Ni, Zn, and Mn and an element selected from the group consisting of Nb and Ta at the B site that has a valence of three; and a second main component composed of an ABO3 compound with at least Pb at the A site and with Ti and Zr at the B site that has a valence of four.
Even in firing under low-temperature conditions, the piezoelectric/electrostrictive ceramic composition provided exhibits high density and excellent crystallinity as well as excellent piezoelectric/electrostrictive properties.
It is, therefore, an object of the present invention to provide a piezoelectric/electrostrictive ceramic composition with high density and excellent crystallinity, even in the case of firing under lower-temperature conditions than in conventional cases; and with excellent piezoelectric/electrostrictive properties.
These and other objects, features, aspects and advantages of the present invention will become more apparent from the following detailed description of the present invention when taken in conjunction with the accompanying drawings.
As a result of diligent study to solve the above problems, the inventors have accomplished the present invention, concluding that the above problems can be solved by the use of a Bi compound, the melting point of which can be low for low-temperature firing, and then by the dissolution of an ABO3 compound (first main component) with Bi at the A site and B1 and B2 elements at the B site in the form of a solid solution into another ABO3 compound (second main component) with at least Pb at the A site, in order to develop piezoelectric/electrostrictive properties such as excellent electric-field-induced strain properties (B1 consists of at least one kind of element having an ionic valence of two or less and selected from the group consisting of Mg, Cr, Mn, Fe, Co, Ni, Cu, Zn, and rare-earth elements; and B2 consists of at least one kind of element having an ionic valence of four or more and selected from the group consisting of V, Nb, Ta, Sb, Mo, and W.)
Bi compounds, typified by Bi2O3, are known as low-melting materials and used as raw materials for sintering agents, low-melting glass, and the like. Typical examples of Bi-based ABO3 structural materials that include Bi as a main constituent element include Bi1/2Na1/2TiO3, Bi/1/2K1/2TiO3, and BiFeO3 and are capable of being synthesized by atmospheric firing, but they are inferior in piezoelectric/electrostrictive properties because of their stable ABO3 structure.
On the other hand, composite ABO3 compounds except BiFeO3 with Bi at the A site and with the B site having a valence of three cannot maintain their ABO3 structure because they are unstable and thus difficult to be synthesized in a single phase by atmospheric firing. However, if they maintain their ABO3 structure, they may be able to attain excellent piezoelectric/electrostrictive properties derived from their instability.
It is thus considered that dissolving a Pb-based ABO3 compound as a skeleton into a solid solution may allow the ABO3 structure to be maintained.
More specifically, this is based on the idea that the combination of two different kinds of ABO3 compounds that are different in tolerance factor (cf. Equation 1) defined by the ionic radius of each ABO3 compound will easily cause the deformation of a perovskite structure.
where rA is the A-site ionic radius, rB is the B-site ionic radius, and rO is the oxide-ion radius.
Various compositions based on the above design have been examined, and it has been found that incorporating highly-valent ionic species, such as quadrivalent or higher-valent ions, on the B site is also effective in providing high insulating performance. As a result, the present invention has shown that, into the second main component that is a Pb-based piezoelectric/electrostrictive ceramic composition, the first main component composed of an ABO3 compound with Bi having a different tolerance factor from the second main component and at the A site and with B1 and B2 elements at the B site is dissolved, which brings about the effect of improving the electric-field-induced strain properties in addition to achieving low-temperature firing with the Bi compound (the B1 element consists of at least one kind of element having an ionic valence of two or less and selected from the group consisting of Mg, Cr, Mn, Fe, Co, Ni, Cu, Zn, and rare earth elements; and the B2 element consists of at least one kind of element having an ionic valence of four or more and selected from the group consisting of V, Nb, Ta, Sb, Mo, and W.).
Examples of the first main component according to the present invention include ABO3 compounds with Bi at the A site that has a valence of three and with the B site having a valence of three, and more specifically, Bi(Ni2/3Nb1/3)O3, Bi(Mg2/3Nb1/3)O3, Bi(Zn2/3Nb1/3)O3, Bi(Cu2/3Nb1/3)O3, Bi(Fe2/3Nb1/3)O3, Bi(Mn2/3Nb1/3)O3, Bi(Co2/3Nb1/3)O3, Bi(Cr2/3Nb1/3)O3, Bi(Ni2/3V1/3)O3, Bi(Mg2/3V1/3)O3, Bi(Zn2/3V1/3)O3, Bi(Cu2/3V1/3)O3, Bi(Fe2/3V1/3)O3, Bi(Mn2/3V1/3)O3, Bi(Co2/3V1/3)O3, Bi(Cr2/3V1/3)O3, Bi(Ni2/3Ta1/3)O3, Bi(Mg2/3Ta1/3)O3, Bi(Zn2/3Ta1/3)O3, Bi(Cu2/3Ta1/3)O3, Bi(Fe2/3Ta1/3)O3, Bi(Mn2/3Ta1/3)O3, Bi(Co2/3Ta1/3)O3, Bi(Cr2/3Ta1/3)O3, Bi(Mg3/4Mo1/4)O3, Bi(Ni3/4Mo1/4)O3, Bi(Zn3/4W1/4)O3, Bi(Cu3/4W1/4)O3, Bi(Fe3/4W1/4)O3, Bi(Mn3/4W1/4)O3, Bi(Mg3/4W1/4)O3, Bi(Ni3/4W1/4)O3, Bi(Zn3/4W1/4)O3, Bi(Cu3/4W1/4)O3, Bi(Fe3/4W1/4)O3, Bi(Mn3/4W1/4)O3, and Bi(Cu1/2Nb1/2)O3. While the first main component has A- and B-site valences of three in terms of stoichiometry, it may have a non-stoichiometric composition for fine property control.
Examples of the second main component include ABO3 compounds with at least Pb at the A site, and more specifically, PZT, Pb(Mg, Nb)O3-PT, Pb(Ni, Nb)O3-PT, Pb(Zn, Nb)O3-PT, Pb(Mg, Nb)O3-PZT, Pb(Ni, Nb)O3-PZT, Pb(Zn, Nb)O3-PT, Pb(Yb, Nb)O3-PZT, Pb(Co, Nb)O3-PZT, (Pb, Sr)ZT, and PLZT.
Alternatively, various secondary components may be used for substitution or addition in order to allow fine property control to such an extent as not to impair its basic properties.
Next, the present invention is described in more detail, referring to examples. The present invention is, however, not limited only thereto. The following describes how to measure various kinds of physical properties.
[Bulk Density Determination]
A sintered body (piezoelectric/electrostrictive body) is measured using Archimedes' law to calculate the relative density from the theoretical density measured by XRD (X-ray diffraction).
[Crystal Structure Analysis]
The crystal structure of the sintered body is analyzed by the 2θ/θ scan technique using an X-ray diffractometer. Also, the theoretical density is calculated from the crystal-structure information obtained.
[Microstructure Observation]
The surface microstructure of the sintered body and the internal microstructure thereof after polishing are observed under a scanning electron microscope to measure the grain size by the intercept method.
[Piezoelectric Constant Measurement]
The piezoelectric constant, d31, is measured with reference to JEITA EM-4501.
[Curie Point Determination]
The relative-permittivity temperature characteristics are measured by connecting an electric furnace to an LCR meter, and the temperature at which the relative permittivity peaks is defined as the Curie point.
[Electric-Field-Induced Strain]
A strain gauge is attached to the electrode to measure, as the electric-field-induced strain (ppm), the amount of strain in the direction perpendicular to the electric field under the application of a 4 kV/mm voltage.
Raw materials including PbO powder, Bi2O3 powder, NiO powder, Nb2O5 powder, TiO2 powder, and ZrO2 powder were weighed to attain the following composition (Equation 2) and were wet-mixed in a ball mill for 40 hours.
xBi(Ni2/3Nb/1/3)O3-(1-x)Pb(Zr1-yTiy)O3 (2)
The mixed powder was dried and calcined in air at 800° C. for two hours. The powder was then ground and dried in the wet ball mill until a given specific surface area was attained, and it was sifted through a sieve for granulation, formed into a disc shape with a uniaxial pressurizer and a hydrostatic pressurizer, and enclosed in a ceramic sheath to be fired at 950° C.
The density of the sintered body was measured and the microstructure and the crystal structure were evaluated. To evaluate the electrical characteristics, after the sintered body was cut into 1-mm thick strip slices, it was coated on both sides with an Ag paste and fired at 600° C. to form electrodes. After these electrodes were polarized at 75° C. for 15 minutes at 2 kV/mm, the piezoelectric constant was measured. The electric-field-induced strain properties were also measured as well.
The results were as follows. The sintered body had a relative density of 98% and its crystal structure was a single-phase tetragonal perovskite structure. The microstructure observation showed that the average grain size was 4.7 μm. The piezoelectric constant d31 was 195 pm/V, and the Curie temperature was 225° C. During the application of a 4 kV/mm electric field, the electric-field-induced strain was 1250 ppm.
The compositions given in Table 1 were prepared by a manufacturing method similar to the method in Example 1 and evaluated in the same manner as in Example 1. The result in each case was that densification was possible at 1000° C. or below and good piezoelectric characteristics were obtained.
The compositions given in Table 1 were prepared by a manufacturing method similar to the method in Example 1 and evaluated in the same manner as in Example 1. The results were either that a single-phase perovskite structure was not obtained because of unstable synthesis or that, even if the composition exhibited a perovskite structure, it was low in density and could not obtain good piezoelectric characteristics.
Changes in Relative Density and in 4 kV/mm Electric-Field-Induced Strain at Different Firing Temperatures
As shown in
While the invention has been shown and described in detail, the foregoing description is in all aspects illustrative and not restrictive. It is therefore understood that numerous modifications and variations can be devised without departing from the scope of the invention.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-024825 | Feb 2009 | JP | national |
| Number | Name | Date | Kind |
|---|---|---|---|
| 6118209 | Okuyama et al. | Sep 2000 | A |
| 6140746 | Miyashita et al. | Oct 2000 | A |
| 7965020 | Sakaki et al. | Jun 2011 | B2 |
| 20060043863 | Yamaguchi et al. | Mar 2006 | A1 |
| 20060044730 | Yamaguchi et al. | Mar 2006 | A1 |
| 20060279901 | Miyamoto et al. | Dec 2006 | A1 |
| 20070060467 | Matsuda et al. | Mar 2007 | A1 |
| 20080074004 | Yamamoto et al. | Mar 2008 | A1 |
| 20080074471 | Sakashita et al. | Mar 2008 | A1 |
| 20090069294 | Chen et al. | Mar 2009 | A1 |
| Number | Date | Country |
|---|---|---|
| 1742121 | Mar 2006 | CN |
| 1956234 | May 2007 | CN |
| 1637508 | Mar 2006 | EP |
| S45-030151 | Sep 1970 | JP |
| S47-021696 | Oct 1972 | JP |
| S48-012717 | Apr 1973 | JP |
| 48-014839 | May 1973 | JP |
| 49-085598 | Aug 1974 | JP |
| 49-085598 | Sep 1974 | JP |
| S60-215568 | Oct 1985 | JP |
| 62-089372 | Apr 1987 | JP |
| H09-223831 | Aug 1997 | JP |
| 2000-178068 | Jun 2000 | JP |
| 2001-328864 | Nov 2001 | JP |
| 2006-089366 | Apr 2006 | JP |
| 2006-188414 | Jul 2006 | JP |
| 2008-094707 | Apr 2008 | JP |
| 2006-129434 | Dec 2006 | WO |
| 2008-096761 | Aug 2008 | WO |
| WO2008096761 | Aug 2008 | WO |
| Entry |
|---|
| Kholkin. Fatigue of piezoelectric properties in Pb(Zr,Ti)O3 films. Appl. Phys. Lett. 68, 2577 (1996); doi: 10.1063/1.116189. |
| Zhang. Investigation of bismuth-based perovskite system: (1-x)Bi(Ni2/3Nb1/3)O3-xPbTiO3. Journal of Applied Physics vol. 98, Issue 3. Aug. 2005. |
| Remiens. Piezoelectric properties of sputtered PZT films: influence of structure, micro structure, film thickness (Zr,Ti) ratio and Nb substitution. Materials Science in Semiconductor Processing 5 (2003) 123-127. |
| Japanese Office Action (and translation provided by foreign counsel) from a corresponding Japanese patent application bearing a mailing date of Feb. 5, 2013, 7 pages. |
| Number | Date | Country | |
|---|---|---|---|
| 20090236557 A1 | Sep 2009 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61037372 | Mar 2008 | US |