Claims
- 1. A dispersant compatible with a variety of resin-containing coating compositions and especially adapted for dispersing pigments therein, said dispersant being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 20 percent to about 85 percent of an alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 5 percent to about 60 percent of a hardening monomer selected from the group consisting of a styrene, methyl methacrylate, ethyl methacrylate and mixtures thereof;
- (iii) from about 1 percent to about 25 percent of an ethylenically unsaturated carboxylic acid selected from the group consisting of acrylic acid, methacrylic acid, itaconic acid, crotonic acid, maleic acid, fumaric acid and mixtures thereof; and
- (iv) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group and at least one hydroxyl group selected from the group consisting of a monohydroxy alkyl acrylate, monohydroxy alkyl methacrylate, monohydroxy alkyl crotonate, monohydroxy alkyl fumarate, dihydroxy alkyl fumarate, monohydroxy alkyl itaconate, dihydroxy alkyl itaconate, monohydroxy alkyl maleate, dihydroxy alkyl maleate and mixtures thereof; and
- (v), wherein (v) is a compound which provides an amine or amine salt functional moiety on the polymerization product at a level of from about 0.1 percent to about 15 percent is provided by (1) a nitrogen-containing ring opening compound having the formula ##STR6## where R.sub.1, R.sub.2, R.sub.4, R.sub.5, and R.sub.6 are each selected from the group consisting of hydrogen, alkyl, aryl, alkaryl and aralkyl, R.sub.3 is selected from the group consisting of hydrogen and lower alkyl and n is 0 or 1, which can be either reacted with the polymerization product of monomers (i) through (iv) or polymerized with monomer (i) through (iv) or (2) an aliphatic or alicyclic amine compound which forms a salt with carboxyl moieties of the polymerization product of monomers (i) through (iv) and further wherein said dispersant has a weight average molecular weight, determined by gel permeation chromotography, using a polystyrene standard, of from about 1,000 to about 10,000.
- 2. A dispersant compatible with a variety of resin-containing coating compositions and especially adapted for dispersing pigments therein, said dispersant being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 20 percent to about 85 percent of an alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 5 percent to about 60 percent of a hardening monomer selected from the group consisting of a styrene, methyl methacrylate, ethyl methacrylate and mixtures thereof;
- (iii) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group, said compound being an alkyl acrylate; and
- (iv) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group and at least one hydroxyl group selected from the group consisting of a monohydroxy alkyl acrylate, monohydroxy alkyl methacrylate, monohydroxy alkyl crotonate, monohydroxy alkyl fumarate, dihydroxy alkyl fumarate, monohydroxy alkyl itaconate, dihydroxy alkyl itaconate, monohydroxy alkyl maleate, dihydroxy alkyl maleate and mixtures thereof;
- wherein the polymerization product of monomers (i) through (iv) is further reacted with water to provide carboxyl functionality from the units provided by the alkyl acrylate monomer and (v), wherein (v) is a compound which provides an amine or amine salt functional moiety on the polymerization product at a level of from about 0.1 percent to about 15 percent is provided by (1) a nitrogen-containing ring opening compound having the formula ##STR7## wherein R.sub.1, R.sub.2, R.sub.4, R.sub.5, and R.sub.6 are each selected from the group consisting of hydrogen, alkyl, aryl, alkaryl and aralkyl, R.sub.3 is selected from the group consisting of hydrogen and lower alkyl and n is 0 or 1, which is reacted with the polymerization product of monomers (i) through (iv) after said product has been reacted with the water or (2) an aliphatic or alicyclic amine compound which forms a salt with the carboxyl moieties of the polymerization product of monomers (i) through (iv) after said product has been reacted with the water and further wherein said dispersant has a weight average molecular weight, determined by gel permeation chromotography, using a polystyrene standard, of from about 1,000 to about 10,000.
- 3. A dispersant compatible with a variety or resin-containing coating compositions and especially adapted for dispersing pigments therein, said dispersant being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 20 percent to about 85 percent of an alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 5 percent to about 60 percent of a hardening monomer selected from the group consisting of a styrene, methyl methacrylate, ethyl methacrylate and mixtures thereof;
- (iii) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group, said monomer being an unsaturated carboxylic anhydride; and
- (iv) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group and at least one hydroxyl group selected from the group consisting of a monohydroxy alkyl acrylate, monohydroxy alkyl methacrylate, monohydroxy alkyl crotonate, monohydroxy alky fumarate, dihydroxy alkyl fumarate, monohydroxy alkyl itaconate, dihydroxy alkyl itaconate, monohydroxy alkyl maleate, dihydroxy alkyl maleate and mixtures thereof;
- wherein the polymerization product of monomers (i) through (iv) is further reacted with water, alcohol or amine to provide carboxyl functionality from the units provided by the unsaturated carboxylic anhydride monomer and (v), wherein (v) is a compound which provides an amine or amine salt functional moiety on the polymerization product at a level of from about 0.1 percent to about 15 percent is provided by (1) a nitrogen-containing ring opening compound having the formula ##STR8## where R.sub.1, R.sub.2, R.sub.4, R.sub.5, and R.sub.6 are each selected from the group consisting of hydrogen, alkyl, aryl, alkaryl and aralkyl, R.sub.3 is selected from the group consisting of hydrogen and lower alkyl and n is 0 or 1, which is reacted with the polymerization product of monomers (i) through (iv) after said product has been reacted with the water, alcohol or amine or (2) an aliphatic or alicyclic amine compound which forms a salt with the carboxyl moieties of the polymerization product of monomers (i) through (iv) after said product has been reacted with the water, alcohol or amine and further wherein said dispersant has a weight average molecular weight, determined by gel permeation chromotography, using a polystyrene standard of from about 1,000 to about 10,000.
- 4. A dispersant compatible with a variety of resin-containing coating compositions and especially adapted for dispersing pigments therein, said dispersant being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 20 percent to about 85 percent of an alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 5 percent to about 60 percent of a hardening monomer selected from the group consisting of a styrene, methyl methacrylate, ethyl methacrylate and mixtures thereof;
- (iii) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group, said monomer being a hydroxy-containing monomer; and
- (iv) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group and at least one hydroxyl group selected from the group consisting of a monohydroxy alkyl acrylate, monohydroxy alkyl methacrylate, monohydroxy alkyl crotonate, monohydroxy alkyl fumarate, dihydroxy alkyl fumarate, monohydroxy alkyl itaconate, dihydroxy alkyl itaconate, monohydroxy alkyl maleate, dihydroxy alkyl maleate and mixtures thereof;
- wherein the polymerization product of monomers (i) through (iv) is further reacted with anhydride to provide carboxyl functionality from the units provided by the hydroxy-containing monomer (iii) and (v), wherein (v) is a compound which provides an amine or amine salt functional moiety on the polymerization product at a level of from about 0.1 percent to about 15 percent is provided by (1) a nitrogen-containing ring opening compound having the formula ##STR9## where R.sub.1, R.sub.2, R.sub.4, R.sub.5, and R.sub.6 are each selected from the group consisting of hydrogen, alkyl, aryl, alkaryl and aralkyl, R.sub.3 is selected from the group consisting of hydrogen and lower alkyl and n is 0 or 1, which is reacted with the polymerization product of monomers (i) through (iv) after said product has been reacted with the anhydride or (2) an aliphatic or alicyclic amine compound which forms a salt with the carboxyl moieties of the polymerization product of monomers (i) through (iv) after said product has been reacted with the anhydride and further wherein said dispersant has a weight average molecular weight, determined by gel permeation chromotography, using a polystyrene standard, of from about 1,000 to about 10,000.
- 5. A dispersant compatible with a variety of resin-containing coating compositions and especially adapted for dispersing pigments therein, said dispersant being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 20 percent to about 85 percent of an alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group:
- (ii) from about 5 percent to about 60 percent of a hardening monomer selected from the group consisting of a styrene, methyl methacrylate, ethyl methacrylate and mixtures thereof;
- (iii) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group, said monomer being an amine containing monomer; and
- (iv) from about 1 percent to about 25 percent of a monomer having a double bond alpha-beta to a carbonyl group and at least one hydroxyl group selected from the group consisting of a monohydroxy alkyl acrylate, monohydroxy alkyl methacrylate, monohydroxy alkyl crotonate, monohydroxy alkyl fumarate, dihydroxy alkyl fumarate, monohydroxy alkyl itaconate, dihydroxy alkyl itaconate, monohydroxy alkyl maleate, dihydroxy alkyl maleate and mixtures thereof;
- wherein the polymerization product of monomers (i) through (iv) is further reacted with anhydride to provide carboxyl functionality from the units provided by the amine containing monomer (iii) and (v), wherein (v) is a compound which provides an amine or amine salt functional moiety on the polymerization product at a level of from about 0.1 percent to about 15 percent is provided by (1) a nitrogen-containing ring opening compound having the formula ##STR10## wherein R.sub.1, R.sub.2, R.sub.4, R.sub.5, and R.sub.6 are each selected from the group consisting of hydrogen, alkyl, aryl, alkaryl and aralkyl, R.sub.3 is selected from the group consisting of hydrogen and lower alkyl and n is 0 or 1, which is reacted with the polymerization product of monomers (i) through (iv) after said product has been reacted with the anhydride or (2) an aliphatic or alicylic amine compound which forms a salt with the carboxyl moieties of the polymerization product of monomers (i) through (iv) after said product has been reacted with the anhydride and further wherein said dispersant has a weight average molecular weight, determined by gel permeation chromotography, using a polystyrene standard, of from about 1,000 to about 10,000.
- 6. The dispersant of claims 1, 2, 3, 4 or 5 being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 40 percent to about 80 percent of the alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 15 percent to about 40 percent of the hardening monomer;
- (iii) from about 1 percent to about 20 percent of the ethylenically unsaturated carboxylic acid or the monomer which provides the carboxyl functionality when further reacted;
- (iv) from about 1 percent to about 15 percent of the monomer having a double bond alpha-beta to the carbonyl group and at least one hydroxyl group; and
- (v) from about 0.5 percent to about 3 percent of the compound providing an amine or amine salt functional moiety.
- 7. The dispersant of claim 6 wherein monomer (iv) is a hydroxyl-containing alkyl acrylate or alkyl methacrylate wherein the alkyl group contains from 2 to 20 carbon atoms.
- 8. The dispersant of claim 7 wherein monomer (iii) is the ethylenically unsaturated carboxylic acid.
- 9. The dispersant of claim 8 wherein the alkyl methacrylate is a branched chain methacrylate.
- 10. The dispersant of claim 9 wherein the alkyl methacrylate is isobutyl methacrylate.
- 11. The dispersant of claim 9 wherein the hardening monomer is styrene or methyl methacrylate.
- 12. The dispersant of claim 11 wherein the ethylenically unsaturated carboxylic acid is acrylic acid or methacrylic acid.
- 13. The dispersant of claim 7 wherein the hydroxyl-containing alkyl acrylate or alkyl methacrylate contains from 2 to 6 carbon atoms in the alkyl group.
- 14. The dispersant of claim 13 wherein the hydroxyl-containing alkyl acrylate or alkyl methacrylate is hydroxyethyl acrylate.
- 15. The dispersant of claim 6 wherein the component providing an amine or amine salt functional moiety is an aliphatic or alicyclic amine compound which forms a salt with the carboxyl moiety of the interpolymer.
- 16. The dispersant of claim 6 wherein the amine or amine salt functional moiety is provided by a nitrogen-containing ring opening compound.
- 17. The dispersant of claim 6 additionally consisting essentially of from about 1 percent to about 30 percent of a monomer selected from the group consisting of alkyl esters of acrylic acid wherein the alkyl group contains from 3 to 20 carbon atoms, alkyl esters of methacrylic acid wherein the alkyl group contains from 9 to 20 carbon atoms and mixtures thereof.
- 18. The dispersant of claim 12 being the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 60 percent to about 80 percent of the alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 20 percent to about 35 percent of the hardening monomer;
- (iii) from about 1 percent to about 15 percent of the ethylenically unsaturated carboxylic acid or the monomer which provides the carboxyl functionality when further reacted;
- (iv) from about 1 percent to about 10 percent of the monomer having a double bond alpha-beta to the carbonyl group and at least one hydroxyl group; and (v) from about 0.5 percent to about 3 percent of the compound providing an amine or amine salt functional moiety.
- 19. The dispersant of claim 18 wherein the alkyl methacrylate is isobutyl methacrylate, the hardening monomer is styrene or methyl methacrylate, the ethylenically unsaturated carboxylic acid is acrylic acid or methacrylic acid and the monomer having the carbonyl group and the alpha-beta unsaturation to the carbonyl group is hydroxyethyl acrylate.
- 20. The dispersant of claim 19 wherein the dispersant has a weight average molecular weight of from about 2,000 to about 6,000.
- 21. A pigment dispersion composition adapted for dispersing pigments in a film-forming resin-containing coating composition wherein said pigment dispersion composition consists essentially of:
- (a) from about 1 percent to about 50 percent of the dispersant of claims 1, 2, 3, 4 or 5;
- (b) from about 10 percent to about 90 percent of a pigment; and
- (c) the balance a liquid carrier.
- 22. The composition of claim 21 wherein the dispersant is the polymerization product of a mixture of monomers consisting essentially of:
- (i) from about 40 percent to about 80 percent of the alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 15 percent to about 40 percent of the hardening monomer;
- (iii) from about 1 percent to about 20 percent of the ethylenically unsaturated carboxylic acid or the monomer which provides the carboxyl functionality when further reacted;
- (iv) from about 1 percent to about 15 percent of the monomer having a double bond alpha-beta to the carbonyl group and at least one hydroxyl group; and
- (v) from about 0.5 percent to about 3 percent of the compound providing an amine or amine salt functional moiety.
- 23. The composition of claim 22 wherein monomer (iv) is a hydroxyl-containing alkyl acrylate or alkyl methacrylate wherein the alkyl group contains from 2 to 20 carbon atoms.
- 24. The composition of claim 22 monomer (iii) is the ethylenically unsaturated carboxylic acid.
- 25. The composition of claim 24 wherein the alkyl methacrylate is a branched chain methacrylate.
- 26. The composition of claim 25 wherein the alkyl methacrylate is isobutyl methacrylate.
- 27. The composition of claim 25 wherein the hardening monomer is styrene or methyl methacrylate.
- 28. The composition of claim 27 wherein the ethylenically unsaturated carboxylic acid is acrylic acid or methacrylic acid.
- 29. The composition of claim 23 wherein the hydroxyl-containing alkyl acrylate or alkyl methacrylate contains from 2 to 6 carbon atoms in the alkyl group.
- 30. The composition of claim 29 wherein the hydroxyl-containing alkyl acrylate or alkyl methacrylate is hydroxyethyl acrylate.
- 31. The composition of claim 21 wherein the component providing an amine or amine salt functional moiety is an aliphatic or alicyclic amine compound which forms a salt with the carboxyl moiety of the interpolymer.
- 32. The composition of claim 22 wherein the amine or amine salt functional moiety is provided by a nitrogen-containing ring opening compound.
- 33. The composition of claim 22 wherein the dispersant additionally consists essentially of from about 1 percent to about 30 percent of a monomer selected from the group consisting of alkyl esters of acrylic acid wherein the alkyl group contains from 3 to 20 carbon atoms, alkyl esters of methacrylic acid wherein the alkyl group contains from 9 to 20 carbon atoms and mixtures thereof.
- 34. The composition of claim 28 wherein the dispersant is the polymerization product of:
- (i) from about 60 percent to about 80 percent of the alkyl methacrylate having from 3 to 8 carbon atoms in the alkyl group;
- (ii) from about 20 percent to about 35 percent of the hardening monomer;
- (iii) from about 1 percent to about 15 percent of the ethylenically unsaturated carboxylic acid or the monomer which provides the carboxyl functionality when further reacted;
- (iv) from about 1 percent to about 10 percent of the monomer having a double bond alpha-beta to the carbonyl group and at least one hydroxyl group; and
- (v) from about 0.5 percent to about 3 percent of the compound providing an amine or amine salt functional moiety.
- 35. The composition of claim 34 wherein the alkyl methacrylate is isobutyl methacrylate, the hardening monomer is styrene or methyl methacrylate, the ethylenically unsaturated carboxylic acid is acrylic acid or methacrylic acid and the monomer having the alpha-beta unsaturation to the carbonyl group is hydroxyethyl acrylate.
- 36. The composition of claim 35 wherein the dispersant has a molecular weight of from about 2,000 to about 6,000.
- 37. The composition of claim 22 consisting essentially of:
- (a) from about 3 percent to about 30 percent of the dispersant;
- (b) from about 15 percent to about 80 percent of the pigment; and
- (c) the balance a liquid carrier.
- 38. The composition of claim 37 wherein the carrier is an organic solvent.
- 39. The composition of claim 21 wherein the pigment is ground into the dispersant.
Parent Case Info
This is a division of application Ser. No. 166,643, filed July 7, 1980, now abandoned which is a continuation of application Ser. No. 938,746, filed Aug. 31, 1978, now abandoned.
US Referenced Citations (9)
Foreign Referenced Citations (1)
Number |
Date |
Country |
1393243 |
May 1975 |
GBX |
Divisions (1)
|
Number |
Date |
Country |
Parent |
166643 |
Jul 1980 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
938746 |
Aug 1978 |
|