The present invention relates to a pile fabric whose pile fibers are inhibited from falling off, and a method of producing the same.
Conventionally, pile fabrics have been known under the names of imitation furs or fake furs, boas, etc., as fabrics designed to resemble appearances of furs. These are produced from pile knits and pile weaves. In the case of knitted piles, a seal-fraise knitting machine or a sliver knitting machine (circular knitting machine) is used mainly for knitting, and piles are cut in both cases. When a double Russell machine (warp knitting machine) is used for knitting, piles are knitted by forming a double ground structure while intertwining the double ground structure with a binder yarn, and cutting the middle of the binder yarn. In a weaving method, a velvet loom or a moquette loom is used to intertwine an upper and a lower ground structure and the middle of the ground structures with a binder yarn, and cut the middle of an upper and a lower base fabrics using a knife, whereby two weaves are obtained simultaneously (Non-Patent Document 1). However, these weaves and knits have the same problem, which is a large amount of pile fiber loss. As many pile fibers fall off, they attach to an inner wear or are dropped on the floor, resulting in a poor appearance and poor hygienic conditions.
In order to prevent such pile fiber loss, there has been a proposal of mixing low-melting fibers into pile fibers (Patent Document 1), and a proposal of mixing low-melting fibers into ground yarns constituting a ground structure (Patent Documents 2-3), etc. However, in these proposals, because the whole fabric is heated at a temperature equal to or higher than a melting point of the low-melting fibers, the entire ground structure or the pile fibers are also fused, resulting in a coarse texture.
Patent Document 1: JP 06(1994)-081248 A
Patent Document 2: JP 2000-314048 A
Patent Document 3: JP 07(1995)-048765 A
Non-Patent Document 1: “Fiber Handbook third edition”, page 341-342, edited by The Society of Fiber Science and Technology, Japan, published by Maruzen, issued on Dec. 15, 2004
In order to solve the above conventional problem, the present invention provides a pile fabric whose pile fibers are inhibited from falling off without impairing the texture by fusing only a specific area of the pile fabric, and a method of producing the same.
A pile fabric of the present invention is a pile fabric that includes: a ground structure; and pile fibers that are intertwined with ground yarns constituting the ground structure and napped on a front surface of the ground structure, wherein the pile fibers include at least one selected from the group consisting of acrylic fibers and acrylic-based fibers and have a softening point lower than a softening point of fibers constituting the ground structure, and wherein among the pile fibers intertwined with the ground yarns constituting the ground structure, at least part of the pile fibers located outside of the ground yarns constituting the ground structure are fused but the pile fibers napped on the front surface of the ground structure are not fused.
A method of producing a pile fabric of the present invention is a method of producing a pile fabric, the pile fabric including: a ground structure; and pile fibers that are intertwined with ground yarns constituting the ground structure and napped on a front surface of the ground structure, wherein the pile fibers include at least one selected from the group consisting of acrylic fibers and acrylic-based fibers and have a softening point lower than a softening point of fibers constituting the ground structure, and a contact heating/pressurization is performed at a temperature equal to or higher than the softening point of the pile fibers and lower than the softening point of the fibers constituting the ground structure from a back surface side of the ground structure, whereby among the pile fibers intertwined with the ground yarns constituting the ground structure, at least part of the pile fibers located outside of the ground yarns constituting the ground structure are fused but the pile fibers napped on the front surface of the ground structure are not fused.
In the pile fabric of the present invention, the pile fibers include at least one selected from the group consisting of acrylic fibers and acrylic-based fibers, and at least part of the pile fibers located outside of the ground yarns constituting the ground structure are fused but the pile fibers napped on the front surface of the ground structure are not fused. Thereby, the pile fibers can be prevented from falling off without impairing the texture. Further, in the method of producing a pile fabric of the present invention, a contact heating/pressurization is performed at a temperature equal to or higher than the softening point of the pile fibers but lower than the softening point of the fibers constituting the ground structure from a back surface side of the ground structure, whereby only a limited area of the pile fibers located outside of the ground yarns constituting the ground structure is fused but the pile fibers napped on the front surface of the ground structure are not fused. Thereby, the pile fibers can be prevented from falling off without impairing the texture.
A pile fabric of the present invention is a pile fabric that includes: a ground structure; and pile fibers that are intertwined with ground yarns constituting the ground structure (hereinafter, also referred to as “ground yarn” simply) and napped on a front surface of the ground structure. The pile fabric can be manufactured using a seal-fraise knitting machine, a sliver knitting machine (circular knitting machine), a boa machine (circular knitting machine), a double Russell machine, a velvet loom, a moquette loom, etc. Although the pile fabric of the present invention is not limited particularly, it may be a high pile fabric, a boa pile fabric, a tufted carpet, etc. The pile fabric is preferably a high pile fabric or a boa pile fabric, and more preferably a high pile fabric.
The pile fibers have a softening point lower than a softening point of fibers constituting the ground structure (hereinafter, also referred to as “ground structure constituent fibers”, simply). Among the pile fibers intertwined with the ground yarns, at least part of the pile fibers located outside of the ground yarns are fused but the pile fibers napped on the front surface of the ground structure are not fused. Although the means for the fusion is not limited as long as at least part of the pile fibers located outside of the ground yarns can be fused, it is preferable to perform a contact heating/pressurization at a temperature equal to or higher than the softening point of the pile fibers and lower than the softening point of the ground structure constituent fibers from a back surface side of the ground structure, i.e., a back surface side of the pile fabric.
In the present invention, “outside of the ground yarns constituting the ground structure” refers to the back surface side of the pile fabric when a surface thereof with napped pile fibers is defined as a front surface, and an outer side of the ground yarns. Further, there is a case where part of the pile fibers intertwined with the ground yarns are stitched into ground yarns. If the remaining parts of such fibers are present outside of ground yarns, they are considered as being located outside of the ground yarns.
The pile fibers are at least one selected from the group consisting of acrylic fibers and acrylic-based fibers. Thereby, it is possible to obtain a pile fabric with an excellent texture. If thermoplastic fibers are used as the pile fibers and a polishing process is performed at a temperature equal to or higher than a melting point of the thermoplastic fibers, generally the pile fibers on the front surface of the pile fabric melt, such that a pile fabric with a favorable appearance and texture is not obtained. Further, when the polishing process is performed at a temperature equal to or lower than the melting point of the thermoplastic fibers, crimps of the pile fibers on the front surface of the pile fabric are not straightened, such that a pile fabric with a favorable appearance and texture is not obtained. On the other hand, crimps of acrylic fibers and acrylic-based fibers can be straightened at temperatures equal to or lower than their softening points. Because of this, when at least one fiber selected from the group consisting of acrylic fibers and acrylic-based fibers is used as the pile fibers, the polishing process can be performed at a temperature equal to or lower than its softening point, (i.e., 150-160° C.). Therefore, when at least one fiber selected from the group consisting of acrylic fibers and acrylic-based fibers is used as the pile fibers, the pile fibers on the front surface of the pile fabric are not fused in the polishing process, such that a pile fabric with a favorable appearance and texture is obtained. Moreover, if the pile fibers contain fibers other than acrylic fibers and acrylic-based fibers, such as thermoplastic fibers having a softening point of 160° C. or lower (i.e., low-melting polyester fibers having a softening point of 160° C. or lower, etc.), these low-melting polyester fibers on the front surface of the pile fabric melt in the polishing process at 150-160° C., which makes it difficult to obtain a pile fabric with a favorable appearance and texture.
The pile fibers are not limited particularly as long as the softening point is lower than the softening point of the fibers constituting the ground structure. A difference between the softening point of the ground structure constituent fibers and the softening point of the pile fibers is preferably 10° C. or more, more preferably 20° C. or more, and particularly preferably 30° C. or more. The difference of 10° C. or more makes it easier to cause only at least part of the fibers located outside of the ground yarns constituting the ground structure to be fused and not to cause the pile fibers napped on the front surface of the ground structure to be fused.
The pile fibers may be fibers that are softened altogether at a predetermined temperature, or mixed fibers composed of fibers that are softened in different temperatures. When the pile fibers are mixed fibers composed of fibers softened at different temperatures, it is preferable that fibers to be softened at a relatively lower temperature are mixed at a ratio of 20% by weight (wt %) or more so that the fibers to be softened at a relatively lower temperature are fused.
In the present invention, a softening point is a softening temperature before fusion or decomposition. For example, a softening point of acrylic fibers is 190-232° C., and a softening point of acrylic-based fibers is 150-220° C. (“Encyclopaedia Chimica”, page 727-729, published by Kyoritsu Shuppan Co., Ltd., on Jun. 1, 1993; hereinafter, referred to as “literature value”). An acrylic fiber refers to a fiber containing 85 wt % or more of acrylonitrile. Further, an acrylic-based fiber refers to a fiber composed of a polymer containing 35 wt % or more and less than 85 wt % of acrylonitrile and 15 wt % or more and 65 wt % or less of other copolymerizable monomers. Here, examples of other copolymerizable monomers include: vinyl halides and vinylidene halides represented by vinyl chloride, vinylidene chloride, vinyl bromide, and vinylidene bromide; sulfonic acid-containing monomers represented by allylsulfonic acid, methallylsulfonic acid, styrenesulfonic acid, isoprenesulfonic acid, 2-acrylamido-2-methylpropanesulfonic acid, and their metal salts and amine salts; acrylic acid and methacrylic acid, and their lower alkyl esters, N- or N,N-alkyl substituted aminoalkyl esters and glycidyl esters; acrylamide and methacrylamide, and their N- or N,N-alkyl substituted products; anionic vinyl monomers such as carboxyl group-containing vinyl monomers represented by acrylic acid, methacrylic acid and itaconic acid and their sodium, potassium or ammonium salts; cationic vinyl monomers represented by quaternary aminoalkyl esters of acrylic acid and methacrylic acid; vinyl group-containing lower alkyl ethers; vinyl group-containing lower carboxylic acid esters represented by vinyl acetate; and styrene. These monomers may be used alone or as a mixture of two or more kinds. Among these, it is preferable to use one or more kinds of monomers selected from the group consisting of vinyl halides, vinylidene halides, and metal salts of sulfonic acid-containing monomers, and more preferable to use one or more kinds of monomers selected from the group consisting of vinyl chloride, vinylidene chloride, and sodium styrenesulfonate. Preferably, modacrylic fibers are used as the acrylic-based fibers. A modacrylic fiber refers to a fiber composed of a polymer containing 35 wt % or more and less than 85 wt % of acrylonitrile, and 15 wt % or more and 65 wt % or less, in total, of one or more kinds of monomers selected from the group consisting of vinyl chloride and vinylidene chloride as well as other copolymerizable monomers.
In the pile fabric of the present invention, at least part of the pile fibers located outside of the ground yarns are fused and pressure-bonded. Here, “pressure-bonded” refers to, for example, a state in which respective pile fibers are fused and bonded, or a state in which respective pile fibers are gathered into a mass and flattened, as shown in SEM photographs (
The thickness of the fused and pressure-bonded pile fibers located outside of the ground yarns is preferably 300 μm or less, more preferably 250 μm or less, and particularly preferably 200 μm or less. If the thickness of the pile fibers located outside of the ground yarns is 300 μm or less, the pile fibers are fused and fixed to each other with sufficient strength. In the present invention, the thickness of the pile fibers located outside of the ground yarns is measured in the following manner, for example. First, in order to maintain the shape of piles at the time of cutting a pile fabric, only front portions of the piles are fixed using an adhesive, and then the pile fabric is cut vertically to a knitting direction of the ground yarns. The cutting line is set so as to traverse loops of the ground yarns, and indicated by a line I-I in
If during the measurement of the thickness it is difficult to distinguish between the ground yarns and the pile fibers using a scanning electron microscope (SEM), an optical microscope, a laser microscope or the like that allows observation at 50× or more magnification may be used for distinguishing between the ground yarns and the pile fibers.
In the present invention, it is preferable that a back surface of the pile fabric is impregnated with a backing resin. If the back surface is impregnated with a backing resin, the napped pile fibers can be aligned before the process of performing a contact heating/pressurization from the back surface side of the ground structure, i.e., the back surface side of the pile fabric.
As the backing resin, it is possible to use a latex, an emulsion, a dispersion, etc., of acrylic ester-based resin, polyurethane-based resin, etc. For preventing pile fiber loss, the amount of the impregnation backing resin generally is, for example, about 50 g/m2 at the concentration of solid resin. However, since the present invention has an effect of preventing pile fiber loss by fusing a specific area of the pile fibers, the amount of the impregnation backing resin may be about ½ to ⅓ of the above-described general amount. In other words, the back surface may be impregnated with the backing resin at the concentration of solid resin of about 17-25 g/m2. Any polishing process of pile fibers is performed before fusing a specific area of the pile fibers, and the pile fibers can be fixed temporarily using a backing resin to prevent the fibers from falling off. For this process, the amount of the resin impregnation need not be high.
Next, a method of producing a pile fabric of the present invention will be described. The method of producing a pile fabric of the present invention includes performing a contact heating/pressurization at a temperature equal to or higher than a softening point of the pile fibers and lower than a softening point of the ground structure constituent fibers from the back surface side of the ground structure. Thereby, among the pile fibers intertwined with the ground yarns, at least part of the pile fibers located outside of the ground yarns are fused and pressure-bonded. Preferably, the contact heating/pressurization is performed using a heating roller or a hot plate. The use of a heating roller or a hot plate shortens the time of the contact heating treatment, and allows only at least part of the pile fibers located outside of the ground yarns to be fused and pressure-bonded. Further, since the temperature of the heating is not so high as to melt the pile fibers on the front surface of the pile fabric, the pile fibers napped on the front surface of the ground structure are not fused.
Further, when the pile fibers are mixed fibers composed of fibers that are softened in different temperatures, it is preferable to perform the contact heating/pressurization treatment at a temperature equal to or higher than a softening point of pile fibers to be softened at a relatively lower temperature and lower than a softening point of pile fibers to be softened at a relatively higher temperature, so that the pile fibers to be softened at a relatively lower temperature are fused. In this manner, pile fiber loss can be prevented and a pile fabric with an excellent texture can be easily obtained.
During and/or after performing the contact heating/pressurization step, it is preferable to cool the napped pile fiber side. Further, after performing the contact heating/pressurization step, it is preferable to perform cooling from the back surface side of the ground structure. In the above-described cooling step, it is preferable to cool the surface of the napped pile fibers using a cooling roller through which water of 30° C. or lower passes. By performing such cooling, dimensional stability is maintained, and damages to the pile fibers due to heat is reduced.
Although the ground structure constituent fibers are not particularly limited as long as the softening point is higher than the softening point of the pile fibers, the fibers may be synthetic fibers composed of polyester resin such as polyethylene terephthalate, cotton, etc.
In the present invention, if using polyethylene terephthalate (PET, softening point about 258° C.) fibers as the ground structure constituent fibers for example, it is possible to use one or more fibers selected from the group consisting of acrylic-based fibers and acrylic fibers as the pile fibers. Preferably, the pile fibers are acrylic-based fibers, or mixed fibers of acrylic-based fibers and acrylic fibers. The following fibers can be used as the acrylic-based fibers.
In the present invention, if using cotton (no softening point) fibers as the ground structure constituent fibers, for example, acrylic fibers (e.g., trade name “Exlan K691” manufactured by Exlan Co., Ltd., softening point 190-232° C., literature value) can be used as the pile fibers.
Hereinafter, a description will be made with reference to the drawings.
An amount of pile fiber loss of the pile fabric according to the present invention is preferably 0.6 g/m2 or less, and more preferably 0.3 g/m2 or less. In the present invention, the amount of pile fiber loss is measured by: rubbing a front surface of a pile fabric ten times in a forward direction and ten times in a reverse direction of piles with a stroke width of 30 cm while applying a constant load of 600 g (14.3 kg/cm2) using a rubber brush (trade name “prescale mat” 5 mm (particle diameter), length 4 cm, width 10.5 cm, manufactured by FUJIFILM Corporation); collecting fallen pile fibers by an adhesive tape; and converting the weight into per 1 m2.
Hereinafter, the present invention will be described more specifically by way of examples. Note that the present invention is not limited to the examples below.
<Measurement Method>
A rubber brush (trade name “prescale mat” 5 mm (particle diameter), length 4 cm, width 10.5 cm, manufactured by FUJIFILM Corporation) was used to rub a front surface of a pile fabric ten times in a forward direction and ten times in a reverse direction of piles with a stroke width of 30 cm while applying a constant load of 600 g (14.3 kg/cm2). Thereafter, fallen pile fibers were collected using an adhesive tape, and the weight was converted into per 1 m2, which was defined as the amount of pile fiber loss.
2. Evaluation of Pile Fiber Loss
The pile fiber loss of a pile fabric was ranked on a scale of A to D as below:
3. Softening Point
1 g of each of fibers used in the following Production Examples was opened, placed on a hot plate heated to a predetermined temperature, and pressurized at 0.07 Kgf/cm2 for 3 seconds. The temperature at which surfaces of single fibers in contact with the hot plate softened, bonded to each other and formed into a plate shape was defined as the softening point of the fibers.
4. Thickness of Pile Fibers Located Outside of the Ground Yarns Constituting the Ground Structure
In order to maintain the shape of piles at the time of cutting a pile fabric, only front portions of the piles were fixed using an adhesive, and then the pile fabric was cut vertically to a knitting direction of the ground yarns. The cutting line was set so as to traverse loops of the ground yarns, and indicated by line I-I in
5. Texture
The texture was ranked on a scale of A to D as below:
1. Pile fibers
2. Ground Structure Constituent Fiber (Ground Yarn)
A multifilament with a total fineness of 334 dtex (a fiber yarn composed of two filaments, each filament having a fineness of 167 dtex and being composed of 50 polyester single fibers) was used The softening point is 258° C.
A cotton yarn composed of two spun yarns of cotton count 40 was used. Cotton does not have a softening point, and is decomposed at high temperature.
In Production Examples 1-30, Production Examples 1, 7, 13, 19, 23 and 27 are comparative examples, and the other Production Examples are examples. A sliver knitting machine (circular knitting machine) for manufacturing fake furs was used The above identified polyester fiber yarns were used as the ground yarns. Pile fabrics of Production Examples 1-30 were knitted by supplying pile fiber slivers (10-14 g/m) composed of acrylic-based fibers respectively shown in Table 1 below. The number of loops in the wales of the ground structure was 16-17/inch, and the number of loops in the course of the ground structure was 22-33/inch. The other conditions are shown in Table 1 below. Next, back surfaces of the pile fabrics were impregnated with a backing resin. As the backing resin, an emulsion copolymer latex composed mainly of acrylic ester was used. The backing resin was an aqueous solution (emulsified solution) with a latex concentration of 40 wt %. The pile fabrics of the examples and the pile fabrics of the comparative examples were impregnated and attached with the backing resin at a solid resin concentration of 25 g/m2 and 50 g/m2, respectively, and then dried. Next, pile fibers on front surfaces of the pile fabrics were aligned by polishing, brushing and shearing. Specifically, first, they were polished twice at 155° C., brushed twice, polished once at each of 150° C., 145° C., 130° C. and 120° C., then sheared twice, and last, polished twice at 100° C. Except for the pile fabrics of the comparative examples, the back surfaces of the pile fabrics were subjected to a contact heating/pressurization treatment using a hot plate. The conditions for the contact heating/pressurization treatment are shown in Table 1 below.
The same pile fibers and the same ground yarns were used in Production Examples 1-6. Production Example 1 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 2-6 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 7-12. Production Example 7 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 8-12 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 13-18. Production Example 13 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 14-18 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 19-22. Production Example 19 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 20-22 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 23-26. Production Example 23 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 24-26 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 27-30. Production Example 27 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 28-30 are examples in which the contact heating/pressurization treatment was performed differently from each other.
Pile fabrics of Production Examples 31-35 were obtained in the same manner as Production Examples 1-30, except that pile fiber slivers composed of acrylic fibers shown in Table 2 below were used, and the contact heating/pressurization treatment was performed under the conditions shown in Table 2 below. Further, pile fabrics of Production Examples 36-40 were obtained in the same manner as Production Examples 1-30, except that the above cotton yarns were used as the ground yarns, pile fiber slivers composed of acrylic fibers shown in Table 2 below were used, and the contact heating/pressurization treatment was performed under the conditions shown in Table 2 below. The same pile fibers and the same ground yarns were used in Production Examples 31-35. Production Example 31 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 32-34 are comparative examples in which the contact heating/pressurization treatment was performed at a predetermined temperature lower than a softening point of the pile fibers. Production Example 35 is an example in which the contact heating/pressurization treatment was performed at a predetermined temperature equal to or higher than a softening point of the pile fibers. Further, the same pile fibers and the same ground yarns were used in Production Examples 36-40. Production Example 36 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 37-40 are examples in which the contact heating/pressurization treatment was performed differently from each other.
Pile fabrics of Production Examples 41-52 were obtained in the same manner as Production Examples 1-30, except that pile fiber slivers composed of mixed fibers of acrylic-based fibers and acrylic fibers shown in Table 3 below were used, and the contact heating/pressurization treatment was performed under the conditions shown in Table 3 below. The same pile fibers and the same ground yarns were used in Production Examples 41-44. Production Example 41 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 42-44 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 45-48. Production Example 45 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 46-48 are examples in which the contact heating/pressurization treatment was performed differently from each other. Further, the same pile fibers and the same ground yarns were used in Production Examples 49-52. Production Example 49 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Examples 50-52 are examples in which the contact heating/pressurization treatment was performed differently from each other. In all Examples, the contact heating/pressurization treatments were performed at a temperature equal to or higher than the softening point of acrylic-based fibers and lower than the softening point of acrylic fibers.
Results of the amount of pile fiber loss, the evaluation of pile fiber loss, the texture, and the thickness of the pile fibers located outside of the ground yarns (hereinafter, also referred to as “thickness” simply) of the pile fabrics of Production Examples 1-52 are shown in Tables 1-3 below. In Tables 1-3, a mark * indicates a comparative example (the same applies to Tables 4-6).
Further, as can be seen from the results in Tables 1-3, the pile fiber loss was low and the texture was favorable for those examples that underwent the contact heating/pressurization treatment. In these examples, at least part of the pile fibers located outside of the ground structure constituent fibers were fused and pressure-bonded by the contact heating/pressurization treatment at a temperature equal to or higher than the softening point of the pile fibers and lower than the softening point of the ground structure constituent fibers. Further, regarding the examples in which the thickness of the fused and pressure-bonded pile fibers located outside of the ground yarns was 300 μm or less, the pile fiber loss was low and the texture was favorable. Incidentally, it can be confirmed from SEM photographs (50× magnification) such as those shown in
Further, a relationship between the thickness of the pile fibers located outside of the ground yarns and the pile fiber loss is summarized from the results in Tables 1-3, and shown by a graph in
A pile fabric of Production Example 53 was obtained in the same manner as Production Example 26, except that the pile fabric was not impregnated with a backing resin. Results of the amount of pile fiber loss, the evaluation of pile fiber loss, the texture, the thickness, etc., of the pile fabric of Production Example 53 are shown in Table 4 below. The results of Production Example 23 (comparative example) also are shown in Table 4. A comparison between Production Example 23 (comparative example) and Production Example 53 (example) indicates that, even without impregnation with a backing resin, the amount of pile fiber loss was greatly reduced. In other words, only performing the contact heating/pressurization treatment on the back surface of the ground structure greatly reduced the amount of pile fiber loss.
Pile fabrics of Production Examples 54-55 were obtained in the same method as a general method of producing boa piles, using the above polyester fiber yarns as ground yarns and pile fibers composed of mixed fibers of acrylic-based fibers shown in Table 5 below. Conditions for the contact heating/pressurization treatment on the back surface of the ground structure of boa piles as well as results of the amount of pile fiber loss, the evaluation of pile fiber loss, the texture, the thickness, etc., are shown in Table 5 below. The same pile fibers and the same ground yarns were used in Production Examples 54-55. Production Example 54 is a comparative example in which the contact heating/pressurization treatment was not performed. Production Example 55 is an example in which the contact heating/pressurization treatment was performed.
As apparent from Table 5, since boa piles are knitted from worsted yarns, the thickness is thin by nature and the amount of pile fiber loss is low. By performing the contact heating/pressurization treatment, the thickness is further reduced and the amount of pile fiber loss tends to be further reduced. Incidentally, all of the Production Examples except Production Examples 54 and 55 are production examples of high piles.
Pile fabrics of Production Examples 56-59 were obtained in the same manner as Production Example 16, except that the above polyester fiber yarns were used as ground yarns, pile fibers shown in Table 6 below were used, and the contact heating/pressurization treatment was performed using the processing device shown in
As can be seen from the results in Table 6, as the pressure of the contact heating/pressurization treatment increases, an effect of preventing pile fiber loss tends to increase while the texture decreases. Both the effect of preventing pile fiber loss and the texture become excellent when the pressure of the contact heating/pressurization treatment ranges from 0.01 to 100 Kgf/cm2.
Pile fabrics of Production Examples 60-95 were obtained in the same manner as Production Examples 1-30, except that polyester fiber yarns were used as ground yarns, low-melting polyester fibers or mixed fibers of low-melting polyester fibers and acrylic fibers shown in Table 7 below were used as pile fibers, and the contact heating/pressurization treatment was performed under the conditions shown in Table 7 below. Conditions for the contact heating/pressurization treatment as well as results of the amount of pile fiber loss, the evaluation of pile fiber loss, the texture, the thickness, etc., are shown in Table 7 below. All of Production Examples 60-95 are comparative examples.
As can be seen from Table 7, when a content of low-melting polyester fibers “Tetoron SD” in the pile fibers is less than 25 wt %, the effect of preventing pile fiber loss cannot be obtained even if the contact heating/pressurization treatment is performed at a temperature equal to or higher than the softening point of the low-melting polyester fibers and lower than the softening point of the acrylic fibers. Further, when the content of the low-melting polyester fibers “Tetoron SD” in the pile fibers exceeds 25 wt %, the pile fiber loss tends to be suppressed as the temperature of the contact heating/pressurization treatment increases, but the texture is poor. Further, when the low-melting polyester fibers “Tetoron SD” are contained in the pile fibers, the low-melting polyester fibers melt during the polishing process at the time of producing the pile fabric, resulting in an unfavorable appearance.
Pile fabrics of Production Examples 96-107 were obtained in the same manner as Production Examples 1-30, except that polyester fiber yarns were used as ground yarns, low-melting polyester fibers or mixed fibers of low-melting polyester fibers and acrylic fibers shown in Table 8 below were used as pile fibers, and the contact heating/pressurization treatment was performed under the conditions shown in Table 8 below. Conditions for the contact heating/pressurization treatment as well as results of the amount of pile fiber loss, the evaluation of pile fiber loss, the texture, the thickness, etc., are shown in Table 8 below. All of Production Examples 96-107 are comparative examples.
As can be seen from Table 8, when a content of low-melting polyester fibers “UNITIKA 1680” in the pile fibers is 20 wt % or less, no remarkable effect of preventing pile fiber loss is obtained even though the contact heating/pressurization treatment is performed at a temperature equal to or higher than the softening point of the low-melting polyester fibers and lower than the softening point of the acrylic fibers.
Although a pile fabric of Production Example 108 was attempted to be produced using polyester fiber yarns as ground yarns and mixed fibers of low-melting polyester fibers “UNITIKA 1680” and acrylic fibers “K691” as pile fibers with the content of the low-melting polyester fibers “UNITIKA 1680” exceeding 20 wt %, they could not be processed into a pile fabric. The reason for this may be as follows. When compared to acrylic fibers and acrylic-based fibers, the low-melting polyester fibers “UNITIKA 1680” have a strong resilience (i.e., an elasticity of staple fibers is strong), have a strong crimp and are voluminous, and they are difficult to be processed into a pile fabric when the content of the low-melting polyester fibers “UNITIKA 1680” in the pile fibers exceeds 20 wt %. Further, since crimps of the low-melting polyester fibers “UNITIKA 1680” are not straightened in the polishing process, problems of high resistance, an occurrence of twines, etc., are caused in the next brushing process if the content of the low-melting polyester fibers “UNITIKA 1680” in the pile fibers exceeds 20 wt %, resulting in the poor processing into a pile fabric.
The present invention provides a pile fabric whose pile fibers are inhibited from falling off while having an excellent texture, and can be applied to general pile fabrics, such as fake furs, boa piles, car sheets and carpets.
1, 21, 31 ground yarn
2, 22, 32 pile fiber
3 napped pile
4 fused part
5, 25, 35 pile fabric
10 processing device
11 heating roller
12 cooling rubber roller
13,14 metal cooling roller
15 guide roller
16,17 container
18 raw pile fabric
18
a front surface of raw pile fabric
18
b back surface of raw pile fabric
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2009/069054 | 11/9/2009 | WO | 00 | 4/25/2012 |