Patent Application
20180258265
The present invention relates to a pipe for the transport of water produced with a polymer composition comprising a polyolefin. The pipe has an improved resistance to chlorinated disinfectants.
Pipes for the transport of gas, for sanitation and for water supply may be produced with for example bimodal polyethylene compositions. Pipes have a very good resistance to water however their lifetime is shortened when the pipes come into contact with disinfectants which are often added to water for hygienic reasons. The chlorine dioxide used as disinfectant in water degrades most materials including polyethylene (Colin, Aging of polyethylene pipes transporting drinking water disinfected by chlorine dioxide, part I, Chemical aspects; Polymer engineering and Science 49(7); 1429-1437; July 2009). Other chlorinated solvents are for example chloramine and chlorine. It is known in the art to apply additives for example antioxidants and stabilizers to prevent said degradation. Several types of additives are proposed to protect polymers during processing and to achieve the desired end-use properties. However, appropriate combinations of stabilizers have to be carefully selected, depending on the desired final properties the polymeric article should have.
It is the object of the present invention to provide pipe applications with improved service lifetime for the transportation of water containing chlorinated disinfectants, for example chlorine dioxide, chloramine and chlorine.
The pipe for the transport of water according to the invention is produced with a polymer composition comprising a polyolefin and styrene isoprene blockcopolymer wherein the amount of styrene isoprene blockcopolymer in the composition is lower than 2.0 wt % relative to the total weight amount of the composition.
Suitable styrene isoprene blockcopolymers include for example styrene-isoprene diblock copolymers, styrene-isoprene-styrene triblock copolymers and mixtures.
The styrene isoprene blockcopolymer is a non-hydrogenated styrene isoprene blockcopolymer.
The drinking water pipe, preferably a pressure pipe, based on this polyolefin grade has an improved protection against for example chlorine dioxide containing cold or hot water and consequently a longer life time. It is also possible to transport waste water or water for cooling.
The polyolefin may be selected from polyethylene such as a multimodal polyethylene for example a bimodal or trimodal polyethylene or polypropylene.
Preferably, the polyolefin is multimodal polyethylene.
More preferably, the polyolefin is bimodal polyethylene.
According to a further preferred embodiment of the invention the pipe is produced with a composition comprising
(a) polyolefin
(b) styrene isoprene blockcopolymer
(c) polyphenolic compound and/or
(d) organic phosphite and/or phosphonite.
Preferably the weight ratio (b):(c+d) ranges between 7:1 and 1:7.
Suitable polyphenolic compounds include for example tetrakis[methylene-3-(3′,5′-di-t-butyl-4-hydroxyphenyl)propionate] methane; 1,1,3-tris(2-methyl-4-hydroxy-5-t-butylphenyl)butane; 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene, bis(3,3-bis(4′-hydroxy-3′-t-butylphenyl)butanoic acid]-glycol ester; tris(3,5-di-t-butyl-4-hydroxy benzyl)isocyanurate; 1,3,5-tris(4-t-butyl-2,6-dimethyl-3-hydroxy-benzyl)isocyanurate; 5-di-t-butyl-4-hydroxy-hydrocinnamic acid triester with 1,3,5-tris(2-hydroxyethyl)-s-triazine-2,4,6(1H, 3H, 5H)-trione; p-cresol/dicyclopentadiene butylated reaction product; 2,6-bis(2′-bis-hydroxy-3′-t-butyl-5′-methyl-phenyl-4-methyl-phenol).
A preferred polyphenolic compound is 1,3,5-trimethyl-2,4,6-tris(3,5-di-t-butyl-4-hydroxybenzyl)benzene (Irganox 1330 supplied by BASF).
Suitable organic phosphites and phosphonites include for example triphenyl phosphite, diphenyl alkyl phosphites, phenyl dialkyl phosphites, tris(nonylphenyl) phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl) phosphite, diisodecyl pentaerythritol diphosphite, bis(2,4-di-tert-butylphenyl) pentaerythritol diphosphate, bis(2,6-di-tert-butyl-4-methylphenyl) pentaerythritol diphosphate, bisisodecyloxy-pentaerythritol diphosphite, bis(2,4-di-tert-butyl-6-methylphenyl) pentaerythritol diphosphite, bis(2,4,6-tri-tert-butylphenyl) pentaerythritol diphosphite, tristearyl sorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl) 4,4′-biphenylenediphosphonite, 6-isooctyloxy-2,4,8,10-tetra-tert-butyl-12H-dibenzo[d,g]-1,3,2-dioxaphosphocin, 6-fluoro-2,4,8,10-tetra-tert-butyl-12-methyldibenzo[d,g]-1,3,2-dioxaphosphocin, bis(2,4-di-tert-butyl-6-methylphenyl) methyl phosphite, bis(2,4-di-tert-butyl-6-methylphenyl) ethyl phosphite.
A preferred phosphite is tris(2,4-di-tert-butylphenyl) phosphite (Irgafos 168 supplied by BASF).
According to another preferred embodiment of the invention the pipe is produced with a polyethylene composition comprising
Preferably (b, (c) and (d) are added during the granulation step of the multimodal, for example bimodal, high density polyethylene powder.
According to a preferred embodiment of the invention the components are added to the polyethylene resin while the polyethylene is in a molten state during extrusion.
The components may be added together and may be added separately.
Preferably the components are added in one step.
Preferably the amount of polyolefin in the composition is higher than 95.0 wt %.
Preferably the amount of styrene isoprene blockcopolymer in the composition is lower than 1.0 wt %.
More preferably this amount ranges between 0.05 and 0.9 wt %. These amounts protect the pipe against chlorine dioxide during a long period.
The multimodal ethylene polymer may be an ethylene homo- or copolymer.
The multimodal ethylene grades to be applied in pipe applications may comprise additives such as for example carbon black, pigments, stearates, a UV stabilizer for example a sterically hindered amine, fillers, minerals, lubricants and/or other stabilisers.
The production processes for bimodal high density polyethylene (HDPE) are summarised at pages 16-20 of “PE 100 Pipe systems” (edited by Bromstrup; second edition, ISBN 3-8027-2728-2).
The production of bimodal high density polyethylene (HDPE) via a low pressure slurry process is described by Alt et al. in “Bimodal polyethylene-Interplay of catalyst and process” (Macromol. Symp. 2001, 163, 135-143). Bimodal high density polyethylene may be produced via a low pressure slurry process for the production of comprising a polymerisation stage, a powder drying stage, an extrusion and pellet handling stage, a recycling stage and a wax removal unit. In a two stage cascade process the reactors may be fed continuously with a mixture of monomers, hydrogen, catalyst/co-catalyst and diluent recycled from the process. In the reactors, polymerisation of ethylene occurs as an exothermic reaction at pressures in the range between for example 0.5 MPa (5 bar) and 1 MPa (10 bar) and at temperatures in the range between for example 75° C. and 88° C. The heat from the polymerisation reaction is removed by means of cooling water. The characteristics of the polyethylene are determined amongst others by the catalyst system and by the concentrations of catalyst, co monomer and hydrogen. The production of bimodal high density polyethylene (HDPE) via a low pressure slurry process may also be performed via a three stage process.
The concept of the two stage cascade process is elucidated at pages 137-138 by Alt et al. “Bimodal polyethylene-Interplay of catalyst and process” (Macromol. Symp. 2001, 163). The reactors are set up in cascade with different conditions in each reactor including low hydrogen content in the second reactor. This allows for the production of HDPE with a bimodal molecular mass distribution and defined co monomer content in the polyethylene chains.
Suitable catalysts for the production of multimodal polyethylene include Ziegler Natta catalysts, chromium based catalysts and single site metallocene catalysts. In all potential possible technologies the process and the catalyst have to form a well-balanced system. The catalyst is crucial for the polymerisation reaction of multimodal polyethylene. By cooperation of process and catalyst a definite polymer structure is produced.
EP2484723 discloses a thermoplastic elastomer composition comprising: 100 parts by mass of (a) a hydrogenated block copolymer that is a hydrogenated product of a block copolymer containing (A) a polymer block containing a structural unit derived from an aromatic vinyl compound and (B) a polymer block containing a structural unit derived from isoprene or a mixture of isoprene and butadiene, having a total content of a 3,4-bond unit and a 1,2-bond unit of 45% or more, has a peak top molecular weight (Mp) obtained by gel permeation chromatograph in terms of polystyrene standard of from 250,000 to 500,000, and is in a form of powder having a bulk density of from 0.10 to 0.40 g/mL; from 10 to 300 parts by mass of (b) a softening agent; and from 5 to 200 parts by mass of (c) a polyolefin resin. The styrene thermoplastic elastomer composition is excellent in flexibility, molding processability, visual transparency, damping property, retention of a softening agent and compression set at a high temperature. EP2484723 provides a sealing material for medical use that contains the styrene thermoplastic elastomer composition, and is excellent in oxygen gas barrier property, liquid leakage resistance (sealing property), coring resistance and liquid leakage resistance after needle stick.
U.S. Pat. No. 3,299,174 discloses a polymer composition comprising a hydrogenated block copolymer having the general configuration prior to hydrogenation polystyrene-polyisoprene-polystyrene.
US20120070597 is directed to a composition to be applied in the production of flexible medical tubing to be used in the human body during medical treatments. The composition comprises a mixture of a polyolefin and a styrenic based block copolymer.
EP2484723, US32999174 and US20120070597 do not disclose pipes for the transport of water having an improved resistance to chlorinated disinfectants.
EP2454076 discloses a pipe for transport of water comprising a layer comprising a crosslinked polyethylene.
The invention will be elucidated by means of the following non-limiting examples.
SABIC Vestolen A5924 (Resin A) used as base polymer in all examples was a bimodal high density polyethylene with MFR5 of 0.24 g/10 min and density 958 kg/m3.
The Examples I-II and Comparative Examples A-C use different additive packages in combination with Resin A to protect the polyethylene from attack by chlorine dioxide (see Table 1). The components as indicated in Table 1 were mixed at 245 degrees Celcius using a twin screw extruder.
wherein:
Compounds were compression molded using ISO1872-2 resulting in plaques, which were cut to ISO527-1A tensile bars (4 mm thick).
The tensile bars were aged in a continuous water flow at a temperature of 40° C. with a chlorine dioxide concentration maintained at 1 mg/L and a pH maintained at 7.2. Flow rate was regulated at 200 L/h. Water hardness was regulated to 20° F. A constant fresh water flow was added during testing allowing full renewal of the testing water each 4 hrs.
The compression molded samples were aged for 1000 hrs.
Tensile tests according to Plastics-Determination of tensile properties ISO527-1 at room temperature at a strain rate of 50 mm/min on aged and non-aged tensile bars were performed to determine the residual elongation at break for the aged samples and reported in Table 2.
From Table 2 it can be concluded that Examples I and II demonstrate significantly higher elongation at break after being exposed to water containing chlorine dioxide than Comparative Example A.
| Number | Date | Country | Kind |
|---|---|---|---|
| 15187971.5 | Oct 2015 | EP | regional |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/EP2016/072928 | 9/27/2016 | WO | 00 |