PISTON RING

TECHNICAL FIELD

The present invention relates to a piston ring used for an internal combustion engine and especially, relates to a piston ring which can effectively prevent adhesion (deposition) phenomenon of aluminum to a piston ring.

TECHNICAL BACKGROUND

Generally, a compression ring and an oil ring are attached as a set of a piston ring to a piston that performs reciprocating motion. The compression ring possesses a function to prevent a phenomenon that high-pressure combustion gas flows into a crank room side from a combustion room side (blow-by). On the other hand, the oil ring mainly possesses a function to suppress a phenomenon that excess lubricant on the inner wall of a cylinder enters into the combustion room side from the crank room side to be consumed (oil-up). Moreover, as a combination of a conventional standard piston ring, a combination of three rings having two compression rings, which include a top ring and a second ring, and one oil ring has been known.

Recently, along with the weight saving and high power output of an internal combustion engine, quality required to a piston ring has been becoming higher. Conventionally, as a method to improve durability of a piston ring for an internal combustion engine, wear resistance surface treatment such as nitriding treatment, ion-plating treatment, or hard chrome plating treatment has been performed on a sliding surface.

Among these surface treatments, because nitriding treatment shows especially excellent wear resistance properties, is has attracted attention as a surface treatment for a piston ring used under harsh operating conditions and has been widely used.

However, though a piston ring on which a nitriding treatment layer has been formed has good wear resistance properties, when mounted on an aluminum alloy piston, it has a tendency to increase wear of ring groove of the piston. Moreover, due to the wear of ring groove of the piston, as shown in FIGS. 1 (a) to (c), aluminum adhesion in which aluminum of lower surface of groove 11 of an aluminum alloy piston 10 adheres on a lower surface 3 of a piston ring 1 (FIG. 1(c)) occurs.

FIGS. 2(
a) to (c) are charts showing the changes of surface roughness of an upper surface 2 and the lower surface 3 of a ring groove of a piston which were detected by a tracer type surface roughness test machine. As shown in FIG. 2, surface condition of the upper surface 2 and the lower surface 3 of the ring groove of the piston changes from normal condition (FIG. 2 (a)) to a roughened piston groove condition (FIG. 2 (b)) to aluminum adhesion condition (FIG. 2 (c)).

Note that in any of FIGS. 2 (a) to (c), horizontal axis show position of a piston and vertical axis show swell of the piston groove. (F) in the figures stands for front direction, while (AT) is for anti-thrust direction, (R) is for rear direction, and (T) is for thrust direction.

Moreover, FIGS. 3 (a) to (c) show aluminum adhesion mechanism. The lower surface 3 of the piston ring 1 and the lower surface of groove 11 of the aluminum alloy piston 10 comes into contact with each other via oxide films 8 (0.2 μm or below) formed on the surfaces respectively (FIG. 3 (a)), then stress of the oxide films 8 on contacting portions becomes high locally to break the oxide films 8, thus uniting Fe of the lower surface 3 of the piston ring 1 and Al of the lower surface of groove 11 of the aluminum alloy piston 10 (FIG. 3 (b)), and aluminum alloy 20 is deposited on the lower surface 3 of the piston ring 1. Note that enlarged view of the aluminum adhesion portion is shown in FIG. 4. In FIG. 4, reference numeral 20 is aluminum that is adhered and reference numeral 21 is joint part of Al and Fe.

As described above, when partial wear (also known as roughened piston groove) due to the adhesion phenomenon on a certain part of a groove of a piston occurs along with the up and down movement of a piston ring, sealing property of an internal combustion engine is deteriorated by blow-by of blow-by gas, leading to lowered output power. This phenomenon occurs within a short period of time in the lower side of a ring groove of a piston and influences durability of the internal combustion engine much. Therefore, many countermeasures against wear of piston groove have been conventionally proposed.

For example, to prevent direct contact between a piston and a piston ring, as a countermeasure against wear of piston groove, anodic oxide coating treatment, coating treatment, or matrix toughening treatment (inside of a piston) has been performed for a piston, while phosphate coating treatment or coating treatment has been performed on a piston ring. Or, as shown in FIGS. 5 (a) and (b), resin coating treatment 8 has been performed on the surface of a piston 10 and a piston ring 1 (for example, Defric (manufactured by Kawamura Research Laboratories).

Moreover, to solve the above-mentioned problem, a piston ring on which upper and lower surfaces or on lower surface, wear resistance treatment layer of nitrided layer or chrome plating layer is formed and upon that wear resistance treatment layer, polybenzimidazole resin film which includes solid lubricant has been developed (refer to Patent Reference 1).

In addition, a piston ring of which surface is coated by heat-resistant resin which includes solid lubricant has been developed by someone other than the applicant of the present application (for example, refer to Patent References 2 and 3).

Patent Reference 1: Japanese Published Unexamined Patent Application No. 07-063266
Patent Reference 2: Japanese Published Unexamined Patent Application No. 10-246149
Patent Reference 3: Japanese Published Unexamined Patent Application No. 11-246823
DISCLOSURE OF THE INVENTION
Problems to Be Solved by the Invention

However, though the above-described conventional countermeasures against wear of piston groove have an effect to prevent adhesion of aluminum in the early stage of piston use, their mid and long term life is not well considered. Therefore, more improvement on durability is desired.

More specifically, for example, in the Patent Reference 1, surface coating by use of polybenzimidazole resin and solid lubricant (C or MOS₂) has been disclosed. However, polybenzimidazole resin is easily oxidized when it is in liquid resin state used to form a film and also deteriorates as time elapses. Therefore, it must be carefully used. Moreover, in some cases, it is difficult to stabilize the quality for a long period of time.

Furthermore, in the Patent Reference 2, surface coating by polyamide-imide resin or polyimide resin and solid lubricant (graphite, MoS₂, WS₂, or polytetrafluoroethylene) has been disclosed. However, such surface coating cannot sufficiently prevent aluminum adhesion and also high cost for coating becomes a problem.

In addition, in the Patent Reference 3, surface coating by polyamide-imide resin or polyimide resin and MOS₂as a solid lubricant and antimony oxide has been disclosed. However, surface coating by this combination also cannot sufficiently prevent aluminum adhesion. Moreover, since antimony oxide is harmful to environment, it is not preferable to use it.

The present invention has been made in consideration of such a condition and is aimed at providing a piston ring which can effectively prevent aluminum adhesion to the piston ring.

Means for Solving Problem

The present invention to solve the above-mentioned problems is a piston ring which includes a piston ring main body and a surface coating film on either upper or lower surface of the piston ring main body, or both the upper and lower surfaces the piston ring wherein the surface coating film comprises heat-resistant resin and copper based powder contained therein and rate of content of the copper based powder in the whole of the surface coating film is between 20 and 80% by mass.

Moreover, in the piston ring, the copper based powder may by any of pure copper, copper oxide, or copper alloy.

In addition, in the piston ring, the copper based powder has a scale-like shape in powder and an average particle diameter thereof may be between 8 and 12 μm.

Furthermore, in the piston ring, specific surface area of the copper based powder may be between 0.6 and 0.9 mm²/g.

Furthermore, in the piston ring, rate of area on the surface of the surface coating film occupied by the copper based powder may be between 6 and 74%.

Furthermore, in the piston ring, the heat-resistant resin may be polyamide-imide resin.

Furthermore, for the piston ring, on the surface of the piston ring main body where the surface coating film is formed, chemical conversion treatment may be performed.

Furthermore, in the piston ring, the heat-resistant resin may include a solid lubricant comprising one selected from molybdenum disulfide, tungsten disulfide, and graphite, and rate of content of the lubricant in the whole of the surface coating film may be between 1 and 10% by mass.

EFFECT OF THE INVENTION

According to the present invention, because on either of an upper surface or lower surface of a piston ring, or both of the surfaces, a surface coating film comprising heat-resistant resin and copper based powder has been formed, it is possible to prevent a part of ring groove of aluminum alloy piston from separation to be adhered to the piston ring.

In the above-mentioned wear resistance measures for piston ring groove, in other words, prevention of aluminum adhesion (refer to Description of the Related Art), surface coating film which includes solid lubricant is formed on the surface of the piston ring main body for the purpose of providing lubricity thereto. However, the present invention has a characteristic that a surface coating film containing copper based powder, instead of solid lubricant, is formed.

Conventionally, as a method to reduce wear of piston ring groove as much as possible, improvement of lubricity on the surface of the piston ring has been targeted. This is because when lubricity on the surface of the piston ring is improved, aggressiveness of the piston ring toward piston ring groove can be reduced by that much and as a result, wear of the piston ring groove can be prevented.

However, although this method has no problems in its early stage when the surface coating film which contributes to lubricity sufficiently exists, after a long period of time passes, the surface coating film itself has a high possibility of being separated and after wear or separation, there remains no more lubricity, leading wear of a piston ring groove by the exposed piston ring itself.

The applicant of the present application focused on this point and to solve this problem, the applicant reached a conclusion to ensure lubricity by heat-resistant resin that constitutes a surface coating film and, at the same time, for the purpose of retaining lubricity for a longer period of time, to mix copper based powder dispersively in the surface coating film so that wear resistance property is added to the surface coating film by the copper based powder. In other words, the idea of the present invention is different from that of the conventional ones. Major role of copper based powder in the present invention is to add heat-resistant and wear resistance properties to protect the surface coating film.

According to the present invention as described above, because it becomes possible to add lubricity on the surface of a piston ring by heat-resistant resin that constitutes a surface coating film while adding wear resistance property by copper based powder to the surface coating film formed on the surface of the piston ring, it is possible to keep lubricity given by the heat-resistant resin for a long period of time.

BRIEF DESCRIPTION OF THE DRAWINGS

[FIG. 1] These are explanatory views of aluminum adhesion phenomenon and (a) is a perspective view of a piston, (b) is an enlarged perspective view of a ring groove of a piston and a piston ring, and (c) is an enlarged perspective view showing aluminum adhesion to a piston ring.

[FIG. 2] (a) to (c) show changing state of upper and lower surfaces of a ring groove of a piston.

[FIG. 3] (a) to (c) are cross-sectional views showing mechanism of aluminum adhesion.

[FIG. 4] This is an enlarged view of a portion where aluminum adhesion occurs.

[FIG. 5] This is a cross-sectional view showing conventional resin coating treatment.

[FIG. 6] This is a cross-sectional view of a piston ring of the present invention.

[FIG. 7] (a) is an enlarged cross-sectional view of the vicinity of an upper surface of the piston ring shown in FIG. 6 and (b) is an enlarged elevation view of the piston ring shown in FIG. 6.

[FIG. 8] This is an enlarged photo of a cross section of a piston ring of an embodiment example 24.

[FIG. 9] This is an enlarged photo of a surface of the piston ring of an embodiment example 6.

[FIG. 10] This is a view showing a high temperature valve seat wear test device.

DESCRIPTION OF REFERENCE NUMERALS

- 1, 60—piston ring
- 2—upper surface of a piston groove
- 3—lower surface of a piston groove
- 10—piston
- 61—piston ring main body
- 62—surface coating film
- 63—heat-resistant resin
- 64—copper based powder

THE BEST MODE FOR CARRYING OUT THE CLAIMED INVENTION

Hereafter, descriptions will be given in detail regarding a piston ring of the present invention with reference to drawings.

FIG. 6 is a cross-sectional view of a piston ring of the present invention.

FIG. 7 (a) is an enlarged cross-sectional view of the vicinity of an upper surface of the piston ring shown in FIG. 6 and (b) is an enlarged elevation view of the piston ring shown in FIG. 6.

As shown in FIG. 6, a piston ring 60 of the present invention includes a piston ring main body 61 and a surface coating film 62 which is formed on either upper or lower surface, or both of the surfaces (in FIG. 6, on both surfaces) of the piston ring main body 61.

As material for the piston ring main body 61 of the present invention, any material can be used without limitation. For example, as material thereof, steel can be mainly used and among stainless steels, SUS 440, SUS 410, SUS 304 or the like, or 8Cr steel, 10Cr steel, SWOSC-V, SWRH or the like can be used. Moreover, as for the types of a piston ring, the piston ring main body 61 can be applied for a top ring which functions as a so-called compression ring and as a second ring, which is also a compression ring, and furthermore, can be applied for an oil ring.

As shown in FIGS. 6 and 7, on the surface of the piston ring 61 of the present invention, a surface coating film that includes a heat-resistant resin 63 and copper based powder 64 contained in the heat-resistant resin 63 is formed.

The heat-resistant resin 63 mainly aims at providing lubricity to the surface of the piston ring, while the copper based powder 64 provides wear resistance property to the surface coating film 62 in which the copper based powder 64 is included, aiming at retaining lubricity provided by the heat-resistant resin for a long period of time.

As the heat-resistant resin 63 that constitutes the surface coating film 62 of the present invention, any resin that can endure the environment (temperature) in which the piston ring is used, has lubricity, and can retain and fix later-described copper based powder can be used. Specifically, polyamide-imide (PAI) resin or polyimide (PI) resin can be listed.

Meanwhile, as the copper based powder 64 which constitutes the surface coating film 62 of the present invention, other than pure copper powder, various types of copper based powder such as powder of copper oxide or copper alloy (for example, brass alloy) can be used. However, in the present invention, hardness of the copper based powder should not be too high because the copper based powder has a role to prevent wear of the heat-resistant resin while it should avoid attacking a piston ring groove which is a counterpart material. From such a viewpoint, as material of the copper based powder, pure copper or copper oxide is preferable.

Shape of the copper based powder 64 is not limited specifically in the present invention and it may be fixed form-shaped, polygonal, or amorphous. However, as mentioned in the description of the material of the copper based powder, attack on the piston ring groove which is a counterpart material by the copper based powder 64 must be avoided and from such a viewpoint, polygonal shape is not preferable and as shown in FIG. 7, scale-like shape is preferable. By adopting scale-like shape for the copper based powder 64 and arranging it to be accumulated in the thickness direction of the surface coating film as shown in FIG. 7, it becomes possible to prevent a piston ring groove from being damaged.

When the shape of the copper based powder 64 is set to be scale-like one, the size thereof is not especially limited. However, it is preferable that an average diameter thereof is between 8 and 12 μm. When an average diameter is less than 8 μm, cost for miniaturizing copper based powder becomes high, while when it is larger than 12 μm, there is a possibility that a piston ring groove which is a counterpart material is attacked. Note that diameter of the scale-like shaped copper based powder is the length of reference coder in FIG. 7 (b) and means length of long axis of a scale.

Moreover, it is preferable that when the copper based powder 64 is set to be scale-like shape, specific surface area of the copper based powder is between 0.6 and 0.9 mm²/g. When the specific surface area is less than 0.6 mm²/g, adhesiveness between the heat-resistant resin 63 and the copper based powder 64 may become bad (in other words, there may be a case where the copper based powder is not fixed by the heat-resistant resin), while when the specific surface area is larger than 0.9 mm²/g, the copper based powder becomes too large and there is a possibility that a piston ring groove which is a counterpart material is attacked. Note that the specific surface area in the present invention means a surface area per 1 gram of copper based powder and is a value measured by air permeability method.

Although the rate of content of the copper based powder 64 in the heat-resistant resin 63 of the surface coating film 62 constituting a piston ring of the present invention can be appropriately set with a balanced ratio by which the heat-resistant resin 63 can sufficiently show lubricity thereof and the copper based powder 64 can sufficiently show wear resistance properties thereof, specifically, it is preferable to set the rate of content of the copper based powder 64 in the whole of the surface coating film 62 to be between 20 and 80% by mass and it is especially preferable to set it to be 50% by mass. When the rate of content of the copper based powder is less than 20% by mass, decrease and annihilation of the surface coating film by friction cannot be effectively prevent and also aluminum adhesion cannot be sufficiently prevented. On the other hand, when the rate of content of the copper based powder exceeds 80% by mass, flexibility of the surface coating film is lowered as a whole and at the same time, it become difficult to fix the copper based powder by heat-resistant resin and may result in elimination of the copper based powder.

It is preferable that a solid lubricant comprising one selected from molybdenum disulfide, tungsten disulfide, and graphite is included in the heat-resistant resin 63. Thus, by adding a small amount of solid lubricant, it becomes possible to fit the heat-resistant resin more to aluminum adhesion in an early stage of use. As a specific content, it is preferable to set the content of the solid lubricant in the whole of the surface coating film 62 to be between 1 and 10% by mass (in this case, if the content of the copper based powder 64 is between 20 and 80% by mass, the rest is for heat-resistant resin). By forming a surface coating film which includes solid lubricant as well as copper based powder on upper and lower surfaces of a piston ring, the surface coating film fits better with the material of the piston which is made of aluminum material in the early stage of use while improving wear resistance properties of the film and, as a result, aluminum adhesion is prevented and a piston ring having superior durability can be provided. Though not shown in FIG. 7, it is preferable that the solid lubricant is uniformly dispersed in the heat-resistant resin 63.

It is preferable that rate of area on the surface of the surface coating film 62 occupied by the copper based powder 64 which constitutes a piston ring of the present invention (refer to FIG. 7 (b)) is between 6 and 74%. By limiting the rate of area within this range, balance between the heat-resistant resin 63 and the copper based powder 64 becomes good and effects of both of them can be sufficiently realized.

Method for forming the surface coating film 62 of the present invention is not limited especially and for example, the copper based powder 64 may be included in polyamide-imide resin and the mixture may be applied on the surface of the piston ring main body 61 by spray coating, dip coating, electrostatic coating or the like. Moreover, depending on necessity, the surface coating film 62 may be performed after treatment such as heat baking.

It is preferable that the thickness of the surface coating film thus formed in the present invention is, for example, between about 3 and 20 μm.

Moreover, in a stage before forming the surface coating film 62, on a surface of the piston ring main body 61 where the surface coating film 62 is to be formed, chemical conversion treatment may be performed as a pretreatment. As chemical conversion treatment, for example, phosphatization, more specifically, manganese phosphate treatment can be listed. By performing phosphatization, it becomes possible to improve adhesiveness of surface of the piston ring main body 61 and the surface coating film 62.

EXAMPLES

A piston ring of the present invention will be more specifically described by using examples.

Examples 1 to 46
Comparative Examples 1 to 86

Members equivalent to a piston ring main body were prepared by use of following two types of material.

- 10Cr material—C: 0.5% by mass, Si: 0.2% by mass, Mn: 0.3% by mass, P: 0.02% by mass, S: 0.01% by mass, Cr: 10.2% by mass, the rest are Fe and unavoidable impurities (Examples 1 to 23, Comparative Examples 1 to 38).
- Material equivalent to JIS SWOSC-V—C: 0.55% by mass, Si: 1.4% by mass, Mn: 0.6% by mass, P: 0.02% by mass, S: 0.02% by mass, Cr: 0.65% by mass, Cu: 0.08% by mass, the rest are Fe and unavoidable impurities (Examples 24 to 46, Comparative Examples 39 to 86).

On both the upper and lower surfaces of the members made of the two materials, a surface coating film having a thickness of 10 μm has been formed by spraying method using polyamide-imide resin as heat-resistant resin and scale-like shape copper powder (purity 99.5%) as copper based powder. Note that an average particle diameter of the scale-like copper based powder used here is 9 μm and the additive amount of the copper based powder to the whole of the surface coating film is shown in Tables 1 and 2. Moreover, there are examples in which molybdenum disulfide, tungsten disulfide, or graphite has been added as solid lubricant and additive amount thereof are shown in Tables 1 and 2. In addition, in the case where material equivalent to JIS SWOSC-V was used as the member, chemical conversion treatment was performed on the surface where the surface coating film is to be formed by use of manganese phosphate (refer to Table 2). Each of the piston ring specimen formed as such are called Examples 1 to 46 and Comparative Examples 1 to 76 (refer to Tables 1 and 2). Furthermore, for Comparative Examples 77 to 86, material equivalent to JIS SWOSC-V was used as the member and on both the upper and lower surfaces thereof, a surface coating film including polyamide-imide resin that contains MoS₂, WS₂, or graphite, which has been conventionally used, was formed with a thickness of 5 μm. Here, an average particle diameter of solid lubricant added is between 1 and 7 μm.

Enlarged photos of a cross-section and surface of a specimen of a piston ring of Example 24 were taken. The results are shown in FIGS. 8 and 9.

In FIG. 8, compound resin layer is the surface coating film 62 shown in FIGS. 6 and 7. In FIG. 8, PAI indicates the heat-resistant resin layer 63 including polyamide-imide resin and in FIG. 8, Cu indicates the copper based powder 64.

Moreover, for Examples 1 to 46 and Comparative Examples 1 to 86, attack test with sliding was performed.

This test was performed by use of a high temperature valve seat wear test device 101 shown in FIG. 10. Test conditions were: stroke: 4 mm, repeating speed: 500 times/min, ring rotation number: 3 rpm, test time: 7 hrs, piston temperature: about 250° C., piston material: aluminum alloy (AC8A).

Note that the attack test with sliding is performed by fixing a piston material 103 so that it cannot move in the shaft direction toward a test device 101, concentrically mounting a piston ring specimen 102 on the piston material 103 and having a cast iron round bar 105 which is provided on the inner surface side of the piston ring specimen 102 reciprocated in a shaft direction and is a test method in which the piston ring specimen 102 is rotated while attacking the piston material 103. The test device 101 has a heater 104 for heating a test subject and can recreate high-temperature condition of combustion in an engine. Therefore, change of condition of the piston materials can be simulated.

By the test, amount of wear on piston side and piston ring side were evaluated. Note that the amount of wear was calculated by measuring unevenness by a surface roughness meter setting the amount of wear Comparative Example 5 as 100.

Evaluation results are shown in Tables 1 and 2.

TABLE 1

additive

tack test

amount
rate of

with
result of attack test with sliding

material

of
area
additive
slidi

rate of

of

the Cu
occupied
amount of
piston

abrasion

piston
type
based
by
solid
tem-

alu-
rate
amount

ring
of pre-
powder
the Cu
lubricant
pera-
test
minum
of
of

main
treat-
(% by
based
(%
ture
time
adhe-
abra-
piston

al

body
ment
mass)
powder
MoS₂
WS₂

raphit
(° C.)
(h)
sion
sion
ring
evaluat
remark

example 1
LOCr
no
20
6
□
□
□
250
7
no
97
89
◯

example 2
material
no
40
30
□
□
□
250
7
no
93
87
◯

example 3

no
60
57
□
□
□
250
7
no
93
85
◯

example 4

no
70
65
□
□
□
250
7
no
92
82
◯

example 5

no
80
74
□
□
□
250
7
no
91
81
◯

comparative

no
15
4
□
□
□
250
7
found
91
89
X

example 1

comparative

no
90
80
□
□
□
250
7
no
100
73
Δ

example 2

example 6

no
20
6
1
□
□
250
7
no
97
77
⊚

example 7

no
50
44
1
□
□
250
7
no
95
75
⊚

example 8

no
80
74
1
□
□
250
7
no
91
72
⊚

example 9

no
20
6
10
□
□
250
7
no
96
79
⊚

example 10

no
50
44
10
□
□
250
7
no
94
76
⊚

example 11

no
80
74
10
□
□
250
7
no
92
73
⊚

comparative

no
20
6
0.5
□
□
250
7
no
97
88
◯

example 3

comparative

no
50
44
0.5
□
□
250
7
no
95
86
◯

example 4

comparative

no
80
74
0.5
□
□
250
7
no
91
83
◯

example 5

comparative

no
20
6
12
□
□
250
7
no
96
95
Δ

example 6

comparative

no
50
44
12
□
□
250
7
no
94
93
Δ

example 7

comparative

no
80
74
12
□
□
250
7
no
90
91
Δ

example 8

comparative

no
15
4
0.5
□
□
250
7
found
91
89
X

example 9

comparative

no
15
4
1
□
□
250
7
found
91
89
X

example 10

comparative

no
15
4
10
□
□
250
7
found
90
90
X

example 11

comparative

no
15
4
12
□
□
250
7
found
90
90
X

example 12

comparative

no
90
80
0.5
□
□
250
7
found
100
72
X

example 13

comparative

no
90
80
1
□
□
250
7
found
100
72
X

example 14

example 12

no
20
6
□
1
□
250
7
no
97
78
⊚

example 13

no
50
44
□
1
□
250
7
no
94
76
⊚

example 14

no
80
74
□
1
□
250
7
no
90
72
⊚

example 15

no
20
6
□
10
□
250
7
no
95
78
⊚

example 16

no
50
44
□
10
□
250
7
no
94
76
⊚

example 17

no
80
74
□
10
□
250
7
no
91
74
⊚

comparative

no
20
6
□
0.5
□
250
7
no
96
88
◯

example 15

comparative

no
50
44
□
0.5
□
250
7
no
95
87
◯

example 16

comparative

no
80
74
□
0.5
□
250
7
no
91
84
◯

example 17

comparative

no
20
6
□
12
□
250
7
no
97
93
Δ

example 18

comparative

no
50
44
□
12
□
250
7
no
95
94
Δ

example 19

example 18

comparative

no
80
74
□
12
□
250
7
no
92
92
Δ

example 20

comparative

no
15
4
□
0.5
□
250
7
found
92
89
X

example 21

comparative

no
15
4
□
1
□
250
7
found
92
90
X

example 22

comparative

no
15
4
□
10
□
250
7
found
91
90
X

example 23

comparative

no
15
4
□
12
□
250
7
found
90
91
X

example 24

comparative

no
90
80
□
0.5
□
250
7
found
100
75
X

example 25

comparative

no
90
80
□
1
□
250
7
found
99
74
X

example 26

example 18

no
20
6
□
□
1
250
7
no
95
77
⊚

example 19

no
50
44
□
□
1
250
7
no
94
76
⊚

example 20

no
80
74
□
□
1
250
7
no
92
73
⊚

example 21

no
20
6
□
□
10
250
7
no
95
78
⊚

example 22

no
50
44
□
□
10
250
7
no
93
76
⊚

example 23

no
80
74
□
□
10
250
7
no
91
73
⊚

comparative

no
20
6
□
□
0.5
250
7
no
97
89
◯

example 27

comparative

no
50
44
□
□
0.5
250
7
no
95
87
◯

example 28

comparative

no
80
74
□
□
0.5
250
7
no
92
85
◯

example 29

comparative

no
20
6
□
□
12
250
7
no
96
95
Δ

example 30

comparative

no
50
44
□
□
12
250
7
no
94
93
Δ

example 31

comparative

no
80
74
□
□
12
250
7
no
91
92
Δ

example 32

comparative

no
15
4
□
□
0.5
250
7
found
90
90
X

example 33

comparative

no
15
4
□
□
1
250
7
found
93
89
X

example 34

comparative

no
15
4
□
□
10
250
7
found
92
90
X

example 35

comparative

no
15
4
□
□
12
250
7
found
90
92
X

example 36

comparative

no
90
80
□
□
0.5
250
7
found
100
73
X

example 37

comparative

no
90
80
□
□
1
250
7
found
100
75
X

example 38

indicates data missing or illegible when filed

TABLE 2

rate of

additive
area
additive

amount of
occupied
amount of

material of
the Cu based
by the Cu
solid

piston ring
powder (% by
based
lubricant (%

main body
type of pretreatment
mass)
powder
MoS₂
WS₂

raphit

example 24
SWOSC-V
chemical conversion treatment
20
6
□
□
□

example 25

chemical conversion treatment
40
29
□
□
□

example 26

chemical conversion treatment
60
58
□
□
□

example 27

chemical conversion treatment
70
66
□
□
□

example 28

chemical conversion treatment
80
74
□
□
□

comparative example 39

chemical conversion treatment
15
3.5
□
□
□

comparative example 40

chemical conversion treatment
90
79
□
□
□

example 29

chemical conversion treatment
20
6
1
□
□

example 30

chemical conversion treatment
50
44
1
□
□

example 31

chemical conversion treatment
80
74
1
□
□

example 32

chemical conversion treatment
20
6
10
□
□

example 33

chemical conversion treatment
50
44
10
□
□

example 34

chemical conversion treatment
80
74
10
□
□

comparative example 41

chemical conversion treatment
20
6
0.5
□
□

comparative example 42

chemical conversion treatment
50
44
0.5
□
□

comparative example 43

chemical conversion treatment
80
74
0.5
□
□

comparative example 44

chemical conversion treatment
20
6
12
□
□

comparative example 45

chemical conversion treatment
50
44
12
□
□

comparative example 46

chemical conversion treatment
80
74
12
□
□

comparative example 47

chemical conversion treatment
15
4
0.5
□
□

comparative example 48

chemical conversion treatment
15
4
1
□
□

comparative example 49

chemical conversion treatment
15
4
10
□
□

comparative example 50

chemical conversion treatment
15
4
12
□
□

comparative example 51

chemical conversion treatment
90
80
0.5
□
□

comparative example 52

chemical conversion treatment
90
80
1
□
□

example 35

chemical conversion treatment
20
6
□
1
□

example 36

chemical conversion treatment
50
44
□
1
□

example 37

chemical conversion treatment
80
74
□
1
□

example 38

chemical conversion treatment
20
6
□
10
□

example 39

chemical conversion treatment
50
44
□
10
□

example 40

chemical conversion treatment
80
74
□
10
□

comparative example 53

chemical conversion treatment
20
6
□
0.5
□

comparative example 54

chemical conversion treatment
50
44
□
0.5
□

comparvtive example 55

chemical conversion treatment
80
74
□
0.5
□

comparative example 56

chemical conversion treatment
20
6
□
12
□

comparative example 57

chemical conversion treatment
50
44
□
12
□

comparative example 58

chemical conversion treatment
80
74
□
12
□

comparative example 59

chemical conversion treatment
15
4
□
0.5
□

comparative example 60

chemical conversion treatment
15
4
□
1
□

comparative example 61

chemical conversion treatment
15
4
□
10
□

comparative example 62

chemical conversion treatment
15
4
□
12
□

comparative example 63

chemical conversion treatment
90
80
□
0.5
□

comparative example 64

chemical conversion treatment
90
80
□
1
□

example 41

chemical conversion treatment
20
6
□
□
1

example 42

chemical conversion treatment
50
44
□
□
1

example 43

chemical conversion treatment
80
74
□
□
1

example 44

chemical conversion treatment
20
6
□
□
10

example 45

chemical conversion treatment
50
44
□
□
10

example 46

chemical conversion treatment
80
74
□
□
10

comparative example 65

chemical conversion treatment
20
6
□
□
0.5

comparative example 66

chemical conversion treatment
50
44
□
□
0.5

comparative example 67

chemical conversion treatment
80
74
□
□
0.5

comparative example 68

chemical conversion treatment
20
6
□
□
12

comparative example 69

chemical conversion treatment
50
44
□
□
12

comparative example 70

chemical conversion treatment
80
74
□
□
12

comparative example 71

chemical conversion treatment
15
4
□
□
0.5

comparative example 72

chemical conversion treatment
15
4
□
□
1

comparative example 73

chemical conversion treatment
15
4
□
□
10

comparative example 74

chemical conversion treatment
15
4
□
□
12

comparative example 75

chemical conversion treatment
90
80
□
□
0.5

comparative example 76

chemical conversion treatment
90
80
□
□
1

comparative example 77
SWOSC-V
no
□
□
□
□
□

comparative example 78

no
□
□
1
□
□

comparative example 79

no
□
□
10
□
□

comparative example 80

no
□
□
□
1
□

comparative example 81

no
□
□
□
10
□

comparative example 82

no
□
□
□
□
1

comparative example 83

no
□
□
□
□
10

comparative example 84

no
□
□
5
5
□

comparative example 85

no
□
□
□
5
5

comparative example 86

no
□
□
5
□
5

tack test

with slidi
result of attack test with sliding

piston

rate
rate of

temperature
test
aluminum
of
abrasion amount

(° C.)
time (h)
adhesion
abrasion
of piston ring

al evaluat
remark

example 24
250
7
no
96
87
◯

example 25
250
7
no
94
86
◯

example 26
250
7
no
93
84
◯

example 27
250
7
no
92
82
◯

example 28
250
7
no
92
81
◯

comparative example 39
250
7
found
92
90
X

comparative example 40
250
7
no
100
81
Δ

example 29
250
7
no
96
76
⊚

example 30
250
7
no
93
73
⊚

example 31
250
7
no
90
72
⊚

example 32
250
7
no
95
75
⊚

example 33
250
7
no
93
76
⊚

example 34
250
7
no
92
74
⊚

comparative example 41
250
7
no
96
87
◯

comparative example 42
250
7
no
94
86
◯

comparative example 43
250
7
no
92
84
◯

comparative example 44
250
7
no
95
94
Δ

comparative example 45
250
7
no
93
93
Δ

comparative example 46
250
7
no
91
92
Δ

comparative example 47
250
7
found
92
88
X

comparative example 48
250
7
found
90
88
X

comparative example 49
250
7
found
91
90
X

comparative example 50
250
7
found
91
92
X

comparative example 51
250
7
found
99
74
X

comparative example 52
250
7
found
100
74
X

example 35
250
7
no
96
77
⊚

example 36
250
7
no
93
75
⊚

example 37
250
7
no
90
73
⊚

example 38
250
7
no
94
76
⊚

example 39
250
7
no
94
77
⊚

example 40
250
7
no
92
75
⊚

comparative example 53
250
7
no
95
88
◯

comparative example 54
250
7
no
94
86
◯

comparvtive example 55
250
7
no
90
83
◯

comparative example 56
250
7
no
96
92
Δ

comparative example 57
250
7
no
96
93
Δ

comparative example 58
250
7
no
93
92
Δ

comparative example 59
250
7
found
92
90
X

comparative example 60
250
7
found
93
89
X

comparative example 61
250
7
found
92
88
X

comparative example 62
250
7
found
90
90
X

comparative example 63
250
7
found
100
76
X

comparative example 64
250
7
found
98
73
X

example 41
250
7
no
94
76
⊚

example 42
250
7
no
94
75
⊚

example 43
250
7
no
93
72
⊚

example 44
250
7
no
95
77
⊚

example 45
250
7
no
92
77
⊚

example 46
250
7
no
92
74
⊚

comparative example 65
250
7
no
96
88
◯

comparative example 66
250
7
no
94
88
◯

comparative example 67
250
7
no
93
86
◯

comparative example 68
250
7
no
95
95
Δ

comparative example 69
250
7
no
95
94
Δ

comparative example 70
250
7
no
92
93
Δ

comparative example 71
250
7
found
91
89
X

comparative example 72
250
7
found
93
88
X

comparative example 73
250
7
found
93
88
X

comparative example 74
250
7
found
91
93
X

comparative example 75
250
7
found
100
75
X

comparative example 76
250
7
found
100
76
X

comparative example 77
250
7
found
100
100
X

comparative example 78
250
7
found
98
98
X

comparative example 79
250
7
found
97
96
X

comparative example 80
250
7
found
98
97
X

comparative example 81
250
7
found
96
95
X

comparative example 82
250
7
found
97
96
X

comparative example 83
250
7
found
95
94
X

comparative example 84
250
7
found
96
98
X

comparative example 85
250
7
found
98
96
X

comparative example 86
250
7
found
96
95
X

indicates data missing or illegible when filed

As apparent from comparison between the Examples 1 to 46 and the Comparative Examples 77 to 86, which are conventional ones, there is no aluminum adhesion found in piston ring specimens of the Examples of the present invention. Moreover, as apparent by comparison between the Examples 1 to 10 and the Comparative Examples 1 to 4, when additive amount of copper based powder was 15%, aluminum adhesion occurred. Furthermore, when the additive amount of copper based powder was 90%, there was no aluminum adhesion but since the effect of the copper based powder becomes large, amount of wear on piston is, when compared with the Comparative Example 5 as a conventional art, not preferable. From these results, it is understood that additive amount of 20 to 80% is preferable for copper based powder.

PISTON RING

Information

Publication Number

Date Filed

Date Published

Inventors

Original Assignees

CPC

US Classifications

International Classifications

Abstract

Description

Claims

Priority Claims (1)

PCT Information