Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly

Description

BACKGROUND

Embodiments relate to subterranean operations and, in some embodiments, to introduction of fluids comprising kiln dust into a wellbore through a bottom hole assembly.

Wells are generally drilled into the ground to recover natural deposits of hydrocarbons and other desirable materials trapped in geological formations in the Earth's crust. Wells may be drilled by rotating a drill bit which is located on a bottom hole assembly at a distal end of a drill string. In conventional drilling, a wellbore is drilled to a desired depth and then the wellbore is lined with a larger-diameter pipe, typically referred to as a casing. Prior to inserting the casing and cementing it in place, the drill string and drill bit are removed from the wellbore. After the casing has been cemented in place, drilling is continued. In some instances, a technique referred to as “casing drilling” is used in which a casing is used in place of a drilling string. Similar to a drill string, the drill bit is connected to a distal end of the casing, and the casing is used to transmit rotational and axial forces to the drill bit. When the wellbore has been drilled to a desired depth, the casing may be cemented in place. In some instances, cement compositions and associated spacer fluids used in the cementing operation are placed into the wellbore through the bottom hole assembly. Casing drilling enables the well to be drilled and cased without the delays associated with removal of the drill bit and drill string from the wellbore.

A number of different fluids may be used in drilling and casing the wellbore. For instance, a drilling fluid may be pumped down through the drill string (or casing), out through the drill bit, and returned to the surface in the annulus between the drill string and the wellbore wall. The drilling fluid can act to lubricate and cool the drill bit as well as carry drill cuttings back to the surface. Spacer fluids can also be used in these operations. For instance, a spacer fluid may be used to displace drilling fluids from the wellbore before introduction of another fluid, such as a cement composition. Cement compositions may be used to cement the casing in the wellbore. The cement composition may be allowed to set in the annulus between the casing and the wellbore wall, thereby forming an annular sheath of hardened cement (e.g., a cement sheath) that should support and position the pipe string in the wellbore and bond the exterior surface of the pipe string to the walls of the wellbore. While a variety of different fluids have been used with some success in drilling and casing wellbore, improved fluids and techniques for their placement are needed in subterranean operations.

BRIEF DESCRIPTION OF THE DRAWINGS

These drawings illustrate certain aspects of some of the embodiments and should not be used to limit or define the invention.

FIG. 1 is a schematic view of an example system that may be used for casing while drilling in accordance with various embodiments.

FIG. 2 is a schematic view of an example system that may be used for casing while directional drilling in accordance with various embodiments.

FIGS. 3 and 4 are schematic views showing displacement of the drilling fluid with placement of the spacer fluid and cement composition through a bottom hole assembly in accordance with various embodiments.

FIG. 5 is a schematic view showing equipment for placement of a cement composition into a wellbore in accordance with various embodiments.

FIG. 6 is a graph showing measured static gel strength values at various temperature and pressure readings as a factor of time for an example treatment fluid.

FIG. 7 is a graph showing measured static gel strength values at various temperature and pressure readings as a factor of time for an example treatment fluid.

DESCRIPTION OF PREFERRED EMBODIMENTS

Embodiments relate to subterranean operations and, in some embodiments, to introduction of a treatment fluid comprising kiln dust into a wellbore through a bottom hole assembly. In particular embodiments, the bottom hole assembly may be attached to a tubular, such as a drill pipe and/or a casing. By way of example, the treatment fluid may be used in a casing drilling operation, wherein the treatment fluid may be introduced into a wellbore through a bottom hole assembly that is attached to a distal end of a casing. In some embodiments, the treatment fluid may be introduced through a drill bit at a distal end of the bottom hole assembly. The term “treatment fluid” does not imply any particular action by the fluid or any component thereof. Treatment fluids may be used, for example, for drilling, completion, production, work over, or in any way to prepare a wellbore and/or well equipment for recovery of materials residing in a subterranean formation penetrated by the wellbore.

Referring now to FIG. 1, a casing drilling system 100 is shown in accordance with various embodiments. As illustrated, the casing drilling system 100 may include a drilling platform 102 that supports a derrick 104 having a traveling block 106 for raising and lowering a casing 108. The casing 108 may be generally tubular and comprise a string of tubulars, which may include conductor casing, surface casing, intermediate casing, production casing, or a production liner. Casing collars or other suitable connectors may be used to couple joints of tubulars to form the casing 108. In some embodiments, completion equipment may be attached to the casing 108. The individual components of the casing 108 are not shown on FIG. 1. In the casing drilling operation, the casing 108 is generally a larger diameter tubular than would typically be used for drilling. A kelly 110 may support the casing 108 as it is lowered through a rotary table 112. A bottom hole assembly 114 may be coupled to the distal end of the casing 108. The bottom hole assembly 114 may be a retrievable or non-retrievable bottom hole assembly. The bottom hole assembly 114 may include a drill bit 116 on its distal end and may be driven either by a downhole motor and/or via rotation of the casing 108 from the well surface. As the drill bit 116 rotates, it creates a wellbore 118 that penetrates various subterranean formations 120. In the illustrated embodiment, the bottom hole assembly 114 further includes an underreamer 122, which may be used to enlarge the wellbore 118 beyond the diameter of the drill bit 116, for example. In some embodiments, the underreamer 122 may be incorporated into the drill bit 116, incorporated with a lower end of the casing 108, or be a separate component attached to the drill bit 116. It should be noted that while FIG. 1 generally depicts a casing drilling system 100 being land based, those skilled in the art will readily recognize that the principles described herein are equally applicable to subsea drilling operations that employ floating or sea-based platforms and rigs, without departing from the scope of the disclosure.

A pump 124 (e.g., a mud pump) may circulate the drilling fluid 126 through a feed pipe 128 and to the kelly 110, which conveys the drilling fluid 126 downhole through the interior of the casing 108 and through one or more orifices in the drill bit 116. The drilling fluid 126 may then be circulated back to the surface via an annulus 130 defined between the casing 108 and the walls of the wellbore 118. At the surface, the recirculated or spent drilling fluid 126 exits the annulus 130 and may be conveyed to one or more fluid processing unit(s) 132 via an interconnecting flow line 134. After passing through the fluid processing unit(s) 132, a “cleaned” drilling fluid 126 may be deposited into a nearby retention pit 136 (e.g., a mud pit). While illustrated as being arranged at the outlet of the wellbore 118 via the annulus 130, those skilled in the art will readily appreciate that the fluid processing unit(s) 132 may be arranged at any other location in the casing drilling system 100 to facilitate its proper function, without departing from the scope of the scope of the disclosure.

Referring now to FIG. 2, embodiments may include directional casing drilling. Directional drilling generally refers to the intentional deviation of the wellbore 118. Directional drilling may enable horizontal drilling through one or more subterranean formations 120. As illustrated by FIG. 2, directional casing drilling may be used to create wellbore 118 having a vertical upper section 136 and a slanted lower section 138. Any suitable technique may be used for creation of the slanted lower section 138 that is non-vertical. In some embodiments, the bottom hole assembly 114 used in directional casing drilling may be a rotatory steerable system that allows directional control while rotating.

With reference now to FIG. 3, the drilling fluid 126 may be displaced from the wellbore 118 by a spacer fluid 140 in accordance with certain embodiments. In some embodiments, the spacer fluid 140 may be a treatment fluid comprising kiln dust and water. The spacer fluid 140 may also remove the drilling fluid, dehydrated/gelled drilling fluid, and/or filter cake solids from the wellbore 118 in advance of the cement composition 142. Embodiments of the spacer fluid 140 may improve the efficiency of the removal of these and other compositions from the wellbore 118. Removal of these compositions from the wellbore 118 may enhance bonding of the cement composition 142 to surfaces in the wellbore 118. In particular embodiments, the spacer fluid 140 comprising kiln dust and water may be characterized by having a higher yield point than the drilling fluid 126 at 80° F. In further embodiments, the spacer fluid 140 comprising kiln dust and water may be characterized by having a higher yield point than the drilling fluid 126 at 130° F. In yet further embodiments, the spacer fluid 140 comprising kiln dust and water may be characterized by having a higher yield point than the drilling fluid 126 at 180° F.

The spacer fluid 140 may be pumped down through the casing 108, out through the bottom hole assembly 114, and into the annulus 130. In some embodiments, the spacer fluid 140 may be introduced into the annulus 130 through the drill bit 116 on the bottom hole assembly 114. As illustrated, the spacer fluid 140 may also separate the drilling fluid 126 from a cement composition 142. The cement composition 142 may be introduced into the wellbore 118 behind the spacer fluid 140 to cement the casing 108 into the wellbore 118. The cement composition 142 may also be pumped down through the casing 108, out through the bottom hole assembly 114, and into the annulus 130. In some embodiments, the cement composition 142 may be a treatment fluid that comprises kiln dust and water. In some embodiments, both the spacer fluid 140 and the cement composition 142 may comprise kiln dust. In alternative embodiments, either the spacer fluid 140 or cement composition 142 may comprise kiln dust. In an additional embodiment, at least a portion of used and/or unused kiln dust containing spacer fluid 140 may be included in the cement composition 142 that is placed into the wellbore 118 and allowed to set. As will be described in more detail below the spacer fluid 140 and/or cement composition 142 comprising kiln dust may also comprise one or more additional additives in various concentrations and combinations.

Referring now to FIG. 4, the wellbore 118 is shown after displacement of the drilling fluid 126 in accordance with various embodiments. As illustrated, the spacer fluid 140 and cement composition 142 may be disposed in the annulus 130 between the casing 108 and walls of the wellbore 118. The cement composition 142 may be allowed to consolidate in the annulus 130. More particularly, the cement composition may be allowed to set in the annulus 130 to form an annular sheath of hardened cement. The annular sheath may form a barrier that prevents the migration of fluids in the wellbore 118. The annular sheath may also, for example, support the casing 108 in the wellbore 118. In some embodiments, at least a portion of the spacer fluid 142 may also remain in the annulus 130. The remaining portion of the spacer fluid 142 may consolidate in the annulus 130. For example, the spacer fluid may set and harden to gain compressive strength by reaction of the kiln dust in the water. The spacer fluid 142 after consolidation may prevent the migration of fluids in the wellbore 118 and also support the casing 108 in the wellbore 118.

Referring now to FIG. 5, a cementing unit 144 is shown that may be used in the placement of the cement composition 142 into the wellbore 118 in accordance with certain embodiments. While not shown, the cementing unit 144 may also be used in placement of the spacer fluid 140 into the wellbore 118. As will be apparent to those of ordinary skill in the art, the cementing unit 144 may include mixing equipment, such jet mixers, re-circulating mixers, or batch mixers. In some embodiments, a jet mixer may be used, for example, to continuously mix the components of the spacer fluid 140 and/or the cement composition 142 as it is being pumped to the wellbore 118. In some embodiments, the cementing unit 144 may include one or more cement trucks, which include mixing and pumping equipment. As illustrated, the cementing unit 144 may pump the cement composition 142 through a feed pipe 146 and to a cementing head 148 which conveys the cement composition 142 into the wellbore 118. As further illustrated, fluids (e.g., the spacer fluid 140) returned to the surface in the annulus 130 may deposited, for example, in the spacer retention pit 150 via the flow line 134.

The exemplary treatment fluids disclosed herein may directly or indirectly affect one or more components or pieces of equipment associated with the preparation, delivery, recapture, recycling, reuse, and/or disposal of the disclosed treatment fluids. For example, the disclosed treatment fluids may directly or indirectly affect one or more mixers, related mixing equipment, mud pits (e.g., retention pit 136, spacer retention pit 150), storage facilities or units, composition separators, heat exchangers, sensors, gauges, pumps, compressors, and the like used generate, store, monitor, regulate, and/or recondition the exemplary treatment fluids. The disclosed treatment fluids may also directly or indirectly affect any transport or delivery equipment used to convey the treatment fluids to a well site or downhole such as, for example, any transport vessels, conduits, pipelines, trucks, tubulars, and/or pipes used to compositionally move the treatment fluids from one location to another, any pumps, compressors, or motors (e.g., topside or downhole) used to drive the treatment fluids into motion, any valves or related joints used to regulate the pressure or flow rate of the treatment fluids, and any sensors (i.e., pressure and temperature), gauges, and/or combinations thereof, and the like. The disclosed treatment fluids may also directly or indirectly affect the various downhole equipment and tools that may come into contact with the treatment fluids such as, but not limited to, wellbore casing (e.g., casing 108), wellbore liner, completion string, insert strings, drill string, coiled tubing, slickline, wireline, drill pipe, drill collars, mud motors, downhole motors and/or pumps, cement pumps, surface-mounted motors and/or pumps, centralizers, turbolizers, scratchers, floats (e.g., shoes, collars, valves, etc.), logging tools and related telemetry equipment, actuators (e.g., electromechanical devices, hydromechanical devices, etc.), sliding sleeves, production sleeves, plugs, screens, filters, flow control devices (e.g., inflow control devices, autonomous inflow control devices, outflow control devices, etc.), couplings (e.g., electro-hydraulic wet connect, dry connect, inductive coupler, etc.), control lines (e.g., electrical, fiber optic, hydraulic, etc.), surveillance lines, drill bits (e.g., drill bit 116) and reamers, sensors or distributed sensors, downhole heat exchangers, valves and corresponding actuation devices, tool seals, packers, cement plugs, bridge plugs, and other wellbore isolation devices, or components, and the like.

Embodiments of the treatment fluids (e.g., spacer fluid 140, cement composition 142) may comprise kiln dust and water. In some embodiments, the treatment fluids may consolidate when left in a wellbore. For example, the treatment fluids may set and harden to gain compressive strength by reaction of the kiln dust in the water. In some embodiments, the treatment fluids may be foamed. For example, the foamed treatment fluids may comprise water, kiln dust, a foaming agent, and a gas. A foamed treatment fluid may be used, for example, where it is desired for the fluid to be lightweight and not exert excessive force on subterranean formations 120 penetrated by the wellbore 118. Embodiments of the treatment fluids may further comprise fly ash, barite, pumicite, a free water control additive, or a combination thereof. In accordance with present embodiments, the treatment fluid may be a spacer fluid 140 that displaces a first fluid (e.g., a drilling fluid 126) from the wellbore 118. In some embodiments, the spacer fluid 140 may have a higher yield point than the first fluid. In further embodiments, the treatment fluid may be a cement composition 142 that is used in cementing the casing 108 in the wellbore 118. Embodiment may further comprise using a treatment fluid comprising the kiln dust in drilling the wellbore 118. For example, the treatment fluid may be circulated past the drill bit 116 to carry drill cuttings back to the surface.

The treatment fluids generally should have a density suitable for a particular application as desired by those of ordinary skill in the art, with the benefit of this disclosure. In some embodiments, the treatment fluids may have a density in the range of from about 4 pounds per gallon (“ppg”) to about 24 ppg. In other embodiments, the treatment fluids may have a density in the range of about 4 ppg to about 17 ppg. In yet other embodiments, the treatment fluids may have a density in the range of about 8 ppg to about 13 ppg. Embodiments of the treatment fluids may be foamed or unfoamed or comprise other means to reduce their densities known in the art, such as lightweight additives. Those of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate density for a particular application.

Kiln dust, as that term is used herein, refers to a solid material generated as a by-product of the heating of certain materials in kilns. The term “kiln dust” as used herein is intended to include kiln dust made as described herein and equivalent forms of kiln dust. Kiln dust typically exhibits cementitious properties in that it can set and harden in the presence of water. Examples of suitable kiln dusts include cement kiln dust, lime kiln dust, and combinations thereof. Cement kiln dust may be generated as a by-product of cement production that is removed from the gas stream and collected, for example, in a dust collector. Usually, large quantities of cement kiln dust are collected in the production of cement that are commonly disposed of as waste. Disposal of the cement kiln dust can add undesirable costs to the manufacture of the cement, as well as the environmental concerns associated with its disposal. The chemical analysis of the cement kiln dust from various cement manufactures varies depending on a number of factors, including the particular kiln feed, the efficiencies of the cement production operation, and the associated dust collection systems. Cement kin dust generally may comprise a variety of oxides, such as SiO₂, Al₂O₃, Fe₂O₃, CaO, MgO, SO₃, Na₂O, and K₂O. Problems may also be associated with the disposal of lime kiln dust, which may be generated as a by-product of the calcination of lime. The chemical analysis of lime kiln dust from various lime manufacturers varies depending on a number of factors, including the particular limestone or dolomitic limestone feed, the type of kiln, the mode of operation of the kiln, the efficiencies of the lime production operation, and the associated dust collection systems. Lime kiln dust generally may comprise varying amounts of free lime and free magnesium, lime stone, and/or dolomitic limestone and a variety of oxides, such as SiO₂, Al₂O₃, Fe₂O₃, CaO, MgO, SO₃, Na₂O, and K₂O, and other components, such as chlorides.

The kiln dust may be included in embodiments of the treatment fluids as a rheology modifier. Among other things, using the kiln dust in various embodiments can provide treatment fluids having rheology suitable for a particular application. Desirable rheology may be advantageous to provide a treatment fluid that is effective for drilling fluid displacement, for example, in spacer fluid embodiments. In some instances, the kiln dust can be used to provide a treatment fluid with a low degree of thermal thinning. For example, the treatment fluid may even have a yield point that increases at elevated temperatures, such as those encountered downhole.

The kiln dust may be included in the spacer fluids in an amount sufficient to provide, for example, the desired rheological properties. The concentration of kiln dust may also be selected to provide a low cost replacement for higher cost additives, such as Portland cement, that may typically be included in a particular treatment fluid. In some embodiments, the kiln dust may be present in a treatment fluid in an amount in the range of from about 1% to about 65% by weight of the treatment fluid (e.g., about 1%, about 5%, about 10%, about 15%, about 20%, about 25%, about 30%, about 35%, about 40%, about 45%, about 50%, about 55%, about 60%, about 65%, etc.). In some embodiments, the kiln dust may be present in the treatment fluid in an amount in the range of from about 5% to about 60% by weight of the treatment fluid. In some embodiments, the kiln dust may be present in an amount in the range of from about 20% to about 35% by weight of the treatment fluid. Alternatively, the amount of kiln dust may be expressed by weight of cementitious components (“bwocc”). As used herein, the term “by weight of cementitious components” or “bwocc” refers to the amount of a component, such as kiln dust, relative to the overall amount of cementitious components used in preparation of the treatment fluid. Cementitious components include those components or combinations of components of the treatment fluid that set, or otherwise harden, to develop compressive strength, including, for example, kiln dust, hydraulic cement, fly ash, hydrated lime, and the like. For example, the kiln dust may be present in an amount in a range of from about 1% to 100% bwocc. (e.g., about 1%, about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, about 90%, 100%, etc.). In some embodiments, the kiln dust may be present in an amount in the range of from about 50% to 100% and, alternatively, from about 80% to 100% bwocc. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate amount of kiln dust to include for a chosen application.

The water used in an embodiment of the treatment fluids may include, for example, freshwater, saltwater (e.g., water containing one or more salts dissolved therein), brine (e.g., saturated saltwater produced from a subterranean formations), seawater, or any combination thereof. Generally, the water may be from any source, provided that the water does not contain an excess of compounds that may undesirably affect other components in the treatment fluid. The water may be included in an amount sufficient to form a pumpable fluid. In some embodiments, the water may be included in the treatment fluids in an amount in a range of from about 40% to about 200% bwocc. In some embodiments, the water may be included in an amount in a range of from about 40% to about 150% bwocc.

Optionally, embodiments of the treatment fluids may further comprise fly ash. A variety of fly ashes may be suitable, including fly ash classified as Class C or Class F fly ash according to American Petroleum Institute, API Specification for Materials and Testing for Well Cements, API Specification 10, Fifth Ed., Jul. 1, 1990. Suitable examples of fly ash include, but are not limited to, POZMIX® A cement additive, commercially available from Halliburton Energy Services, Inc., Duncan, Okla. Where used, the fly ash generally may be included in the treatment fluids in an amount desired for a particular application. In some embodiments, the fly ash may be present in an amount in a range of from about 1% to about 99% bwocc (e.g., about 1%, about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, about 90%, about 99%, etc.). In some embodiments, the fly ash may be present in an amount in the range of from about 1% to about 20% and, alternatively, from about 1% to about 10% bwocc. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate amount of the fly ash to include for a chosen application.

Optionally, embodiments of the treatment fluids may further comprise barite. In some embodiments, the barite may be sized barite. Sized barite generally refers to barite that has been separated, sieved, ground, or otherwise sized to produce barite having a desired particle size. For example, the barite may be sized to produce barite having a particle size less than about 200 microns in size. Where used, the barite generally may be included in the treatment fluids in an amount desired for a particular application. For example, the barite may be present in an amount in a range of from about 1% to about 99% bwocc (e.g., about 1%, about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, about 90%, about 99%, etc.). In some embodiments, the barite may be present in an amount in the range of from about 1% to about 20% and, alternatively, from about 1% to about 10% bwocc. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate amount of the barite to include for a chosen application.

Optionally, embodiments of the treatment fluids may further comprise pumicite. Generally, pumicite is a volcanic rock that may exhibits cementitious properties, in that it may set and harden in the presence of hydrated lime and water. Hydrated lime may be used in combination with the pumicite, in some embodiments. Where used, the pumicite generally may be included in the treatment fluids in an amount desired for a particular application. For example, the pumicite may be present in an amount in a range of from about 1% to about 99% bwocc (e.g., about 1%, about 5%, about 10%, about 20%, about 30%, about 40%, about 50%, about 60%, about 70%, about 80%, about 90%, about 99%, etc.). In some embodiments, the pumicite may be present in an amount in the range of from about 1% to about 20% and, alternatively, from about 1% to about 10% bwocc. One of ordinary skill in the art, with the benefit of this disclosure, should recognize the appropriate amount of the pumicite to include for a chosen application.

Optionally, embodiments of the treatment fluids may further comprise a free water control additive. As used herein, the term “free water control additive” refers to an additive included in a liquid for, among other things, reducing (or preventing) the presence of free water in the liquid. Free water control additives may also reduce (or prevent) the settling of solids. Examples of suitable free water control additives include, but are not limited to, bentonite, amorphous silica, hydroxyethyl cellulose, and combinations thereof. An example of a suitable free water control additive is SA-1015™ suspending agent, available from Halliburton Energy Services, Inc. Another example of a suitable free water control additive is WG-17™ solid additive, available from Halliburton Energy Services, Inc. The free water control additive may be provided as a dry solid in some embodiments. Where used, the free water control additive may be present in an amount in the range of from about 0.1% to about 16% bwocc, for example. In alternative embodiments, the free water control additive may be present in an amount in the range of from about 0.1% to about 2% bwocc.

In some embodiments, the treatment fluids may further comprise a lightweight additive. The lightweight additive may be included to reduce the density of embodiments of the treatment fluids. For example, the lightweight additive may be used to foam a treatment fluid, for example, having a density of less than about 13 ppg. The lightweight additive typically may have a specific gravity of less than about 2.0. Examples of suitable lightweight additives may include sodium silicate, hollow microspheres, gilsonite, perlite, and combinations thereof. An example of a suitable sodium silicate is ECONOLITE™ additive, available from Halliburton Energy Services, Inc. Where used, the lightweight additive may be present in an amount in the range of from about 0.1% to about 20% bwocc, for example. In alternative embodiments, the lightweight additive may be present in an amount in the range of from about 1% to about 10% bwocc.

As previously mentioned, embodiments of the treatment fluids may be foamed with a gas, for example, to provide a treatment fluid with a reduced density. It should be understood that reduced densities may be needed in displacement embodiments to more approximately match the density of a particular drilling fluid, for example, where lightweight drilling fluids are being used. The drilling fluid 126 may be considered lightweight if it has a density of less than about 13 ppg, alternatively, less than about 10 ppg, and alternatively less than about 9 ppg. In some embodiments, the treatment fluids may be foamed to have a density within about 10% of the density of the drilling fluid 126 and, alternatively, within about 5% of the density of the drilling fluid 126. While techniques, such as lightweight additives, may be used to reduce the density of the treatment fluids comprising kiln dust without foaming, these techniques may have drawbacks. For example, reduction of the treatment fluid's density to below about 13 ppg using lightweight additives may produce unstable slurries, which can have problems with settling of solids, floating of lightweight additives, and free water, among others. Accordingly, the treatment fluid may be foamed to provide a treatment fluid having a reduced density that is more stable.

Therefore, in some embodiments, the treatment fluids may be foamed and comprise water, kiln dust, a foaming agent, and a gas. Optionally, to provide a treatment fluid with a lower density and more stable foam, the treatment fluid may further comprise a lightweight additive, for example. With the lightweight additive, a base slurry may be prepared that may then be foamed to provide an even lower density. In some embodiments, the foamed treatment fluid may have a density in the range of from about 4 ppg to about 13 ppg and, alternatively, about 7 ppg to about 9 ppg. In one particular embodiment, a base slurry may be foamed from a density of in the range of from about 9 ppg to about 13 ppg to a lower density, for example, in a range of from about 7 ppg to about 9 ppg.

The gas used in embodiments of the foamed treatment fluids may be any suitable gas for foaming the treatment fluid, including, but not limited to air, nitrogen, and combinations thereof. Generally, the gas should be present in embodiments of the foamed treatment fluids in an amount sufficient to form the desired foam. In certain embodiments, the gas may be present in an amount in the range of from about 5% to about 80% by volume of the foamed treatment fluid at atmospheric pressure, alternatively, about 5% to about 55% by volume, and, alternatively, about 15% to about 30% by volume.

Where foamed, embodiments of the treatment fluids may comprise a foaming agent for providing a suitable foam. As used herein, the term “foaming agent” refers to a material (e.g., surfactant) or combination of materials that facilitate the formation of a foam in a liquid, for example, by reduction of surface tension. Any suitable foaming agent for forming a foam in an aqueous liquid may be used in embodiments of the treatment fluids. Examples of suitable foaming agents may include, but are not limited to: mixtures of an ammonium salt of an alkyl ether sulfate, a cocoamidopropyl betaine surfactant, a cocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; mixtures of an ammonium salt of an alkyl ether sulfate surfactant, a cocoamidopropyl hydroxysultaine surfactant, a cocoamidopropyl dimethylamine oxide surfactant, sodium chloride, and water; hydrolyzed keratin; mixtures of an ethoxylated alcohol ether sulfate surfactant, an alkyl or alkene amidopropyl betaine surfactant, and an alkyl or alkene dimethylamine oxide surfactant; aqueous solutions of an alpha-olefinic sulfonate surfactant and a betaine surfactant; and combinations thereof. An example of a suitable foaming agent is FOAMER™ 760 foamer/stabilizer, available from Halliburton Energy Services, Inc. Generally, the foaming agent may be present in embodiments of the foamed treatment fluids in an amount sufficient to provide a suitable foam. In some embodiments, the foaming agent may be present in an amount in the range of from about 0.8% to about 5% by volume of the water (“bvow”).

A wide variety of additional additives may be included in the treatment fluids as deemed appropriate by one skilled in the art, with the benefit of this disclosure. Examples of such additives include, but are not limited to: supplementary cementitious materials, weighting agents, viscosifying agents (e.g., clays, hydratable polymers, guar gum), fluid loss control additives, lost circulation materials, filtration control additives, dispersants, defoamers, corrosion inhibitors, scale inhibitors, formation conditioning agents, and water-wetting surfactant. Water-wetting surfactants may be used to aid in removal of oil from surfaces in the wellbore (e.g., the casing) to enhance cement and consolidating spacer fluid bonding. Examples of suitable weighting agents include, for example, materials having a specific gravity of 3 or greater, such as barite. Specific examples of these, and other, additives include: organic polymers, biopolymers, latex, ground rubber, surfactants, crystalline silica, amorphous silica, silica flour, fumed silica, nano-clays (e.g., clays having at least one dimension less than 100 nm), salts, fibers, hydratable clays, microspheres, rice husk ash, micro-fine cement (e.g., cement having an average particle size of from about 5 microns to about 10 microns), metakaolin, zeolite, shale, Portland cement, Portland cement interground with pumice, perlite, barite, slag, lime (e.g., hydrated lime), gypsum, and any combinations thereof, and the like. In some embodiments, a supplementary cementitious material may be included in the treatment fluid in addition to or in place of all or a portion of the kiln dust. Examples of suitable supplementary cementitious materials include, without limitation, Portland cement, Portland cement interground with pumice, micro-fine cement, fly ash, slag, pumicite, gypsum and any combination thereof. A person having ordinary skill in the art, with the benefit of this disclosure, will readily be able to detelinine the type and amount of additive useful for a particular application and desired result. It should be understood that, while the present disclosure describes a number of optional additives that may be included in the treatment fluids, it is intended to cover all combinations of the disclosed additives.

As previously mentioned, embodiments of the treatment fluids (e.g., cement composition 142, spacer fluid 140, etc.) may be consolidating in that the treatment fluids may develop gel strength and/or compressive strength in the wellbore 118. Consolidation is defined herein as one of three types of material behavior: Type 1 consolidation is identifiable as a gelled fluid that can be moved and/or pumped when the hydraulic shear stress exceeds the yield point (YP) of the gel. Type 2 consolidation is identifiable as a plastic semi-solid that can experience “plastic deformation” if the shear stress, compressive stress, or tensile stress exceeds the “plastic yield limit.” Type 3 consolidation is identifiable as a rigid solid similar to regular set cement. During a steady progressive strain rate during conventional compressive testing, both confined and unconfined, a Type 3 consolidated material would exhibit linear elastic Hookean stress-strain behavior, followed by some plastic yield and/or mechanical failure. The treatment fluid may transform from the pumpable fluid that was placed during the normal displacement operation to Type 1 and/or further progress to Type 2 and/or further progress to Type 3. It should be understood that the consolidation of the treatment fluid is at wellbore conditions and, as will be appreciated by those of ordinary skill in the art, wellbore conditions may vary. However, embodiments of the treatment fluids may be characterized by exhibiting Type 1, Type 2, or Type 3 consolidation under specific wellbore conditions.

Specific examples of how to characterize a Type 1 consolidation include measuring the yield stress. Type 1 consolidation exhibits a YP from about 25 Pascals to about 250 Pascals, where YP is measured by one of the methods described in U.S. Pat. No. 6,874,353, namely: using a series of parallel vertical blades on a rotor shaft, referred to by those skilled in the art as the “Vane Method”; or using the new device and method also described in U.S. Pat. No. 6,874,353. Another method used to define the YP of Type 1 consolidation is defined in Morgan, R. G., Suter, D. A., and Sweat, V. A., Mathematical Analysis of a Simple Back Extrusion Rheometer, ASAE Paper No. 79-6001. Additionally, other methods commonly known to those skilled in the art may be used to define the YP of Type 1 consolidated treatment fluid. Alternatively, another method of characterizing a Type 1 consolidation includes measuring the gelled strength of the material, which may be defined as “Static Gel Strength” (SGS) as is defined and measured in accordance with the API Recommended Practice on Determining the Static Gel Strength of Cement Formations, ANSI/API Recommended Practice 10B-6. A Type 1 consolidation may exhibit SGS values from about 70 lbf/100 ft²up to about 500 lbf/100 ft².

Specific examples of how to characterize a Type 2 consolidation include measuring the yield limit in compression (YL-C). The YL-C refers to the uniaxial compressive stress at which the material experiences a permanent deformation. Permanent deformation refers to a measurable deformation strain that does not return to zero over a period of time that is on the same order of magnitude as the total time required to conduct the measurement. YL-C may range from 1 psi (lbf/in²) to 2,000 psi, with the most common values ranging from 5 psi to 500 psi.

Specific examples of how to characterize a Type 3 consolidation include measuring the compressive strength. Type 3 consolidation will exhibit unconfined uniaxial compressive strengths ranging from about 5 psi to about 10,000 psi, while the most common values will range from about 10 psi to about 2,500 psi. These values are achieved in 7 days or less. Some formulations may be designed so as to provide significant compressive strengths within 24 hours to 48 hours. Typical sample geometry and sizes for measurement are similar to, but not limited to, those used for characterizing oil well cements: 2 inch cubes; or 2 inch diameter cylinders that are 4 inches in length; or 1 inch diameter cylinders that are 2 inches in length; and other methods known to those skilled in the art of measuring “mechanical properties” of oil well cements. For example, the compressive strength may be determined by crushing the samples in a compression-testing machine. The compressive strength is calculated from the failure load divided by the cross-sectional area resisting the load and is reported in units of pound-force per square inch (psi). Compressive strengths may be determined in accordance with API RP 10B-2, Recommended Practice for Testing Well Cements, First Edition, July 2005.

As a specific example of consolidation, when left in an annulus 130 (e.g., between walls of the wellbore 118 and the casing 108 or between the casing 108 and a larger conduit disposed in the wellbore 118), the treatment fluid may consolidate to develop static gel strength and/or compressive strength. The consolidated mass formed in the annulus 130 may act to support and position the casing 108 in the wellbore 118 and bond the exterior surface of the casing 108 to the walls of the wellbore 118 or to the larger conduit. The consolidated mass formed in the annulus 130 may also provide a substantially impermeable barrier to seal off formation fluids and gases and consequently also serve to mitigate potential fluid migration. The consolidated mass formed in the annulus 130 may also protect the casing 108 or other conduit from corrosion.

In some embodiments, consolidation of the treatment fluid (e.g., spacer fluid 140 or cement composition 142) in the wellbore 118 may be measured. The consolidation measurement may also include a measurement of the integrity of the bond formed between the consolidated treatment fluid and the exterior wall of the casing 108 and/or between the consolidated fluid and the walls of the wellbore 118 or larger conduit disposed in the wellbore 118. In some embodiments, data may be collected corresponding to the integrity of this bond, and the data may be recorded on a log, commonly referred to as a “bond long.” The bond log may be used to, for example, analyze the consolidation properties of the treatment fluid in the wellbore 118. Accordingly, embodiments may include running a cement bond log on at least the portion of the wellbore 118 containing the consolidated treatment fluid. The cement bond log for the consolidated treatment fluid may be obtained by any method used to measure cement integrity without limitation. In some embodiments, a tool may be run into the wellbore 118 on a wireline that can detect the bond of the consolidated treatment fluid to the casing 108 and/or the walls of the wellbore 118 (or larger conduit). An example of a suitable tool includes a sonic tool.

Embodiments of the treatments fluids (e.g., spacer fluid 140) may have a transition time that is shorter than the transition time of another fluid (e.g., cement composition 142) subsequently introduced into the wellbore 118. The term “transition time,” as used herein, refers to the time for a fluid to progress from a static gel strength of about 100 lbf/100 ft²to about 500 lbf/100 ft². By having a shorter transition time, the treatment fluid can reduce or even prevent migration of gas in the wellbore 118, even if gas migrates through a subsequently introduced cement composition 124 before it has developed sufficient gel strength to prevent such migration. Gas and liquid migration can typically be prevented at a static gel strength of 500 lbf/100 ft². By reducing the amount of gas that can migrate through the wellbore 118, the subsequently added cement composition 142 can progress through its slower transition period without gas migration being as significant factor as the cement develops static gel strength. Some embodiments of the treatment fluids may have a transition time (i.e., the time to progress from a static gel strength of about 100 lbf/100 ft²to about 500 lbf/100 ft²) at wellbore conditions of about 45 minutes or less, about 30 minutes or less, about 20 minutes or less, or about 10 minutes or less. Embodiments of the treatment fluids also quickly develop static gel strengths of about 100 lbf/100 ft²and about 500 lbf/100 ft², respectively, at wellbore conditions. The time for a fluid to a develop a static gel strength of about 100 lbf/100 ft²is also referred to as the “zero gel time.” For example, the treatment fluids may have a zero gel time at wellbore condition of about 8 hours or less, and, alternatively, about 4 hours or less. In some embodiments, the treatment fluids may have a zero gel time in a range of from about 0 minutes to about 4 hours or longer. By way of further example, the treatment fluids may develop static gel strengths of about 500 lbf/100 ft²or more at wellbore conditions in a time of from about 10 minutes to about 8 hours or longer. The preceding time for development of static gel strengths are listed as being at wellbore conditions. Those of ordinary skill in the art will understand that particular wellbore conditions (e.g., temperature, pressure, depth, etc.) will vary; however, embodiments of the treatment fluids should meet these specific requirements at the wellbore conditions. Static gel strength may be measured in accordance with API Recommended Practice on Determining the Static Gel Strength of Cement Formations, ANSI/API Recommended Practice 10B-6.

Embodiments of the treatment fluids may be prepared in accordance with any suitable technique. In some embodiments, the desired quantity of water may be introduced into a mixer (e.g., a cement blender) followed by the dry blend. The dry blend may comprise the kiln dust and additional solid additives, for example. Additional liquid additives, if any, may be added to the water as desired prior to, or after, combination with the dry blend. This mixture may be agitated for a sufficient period of time to form a base slurry. This base slurry may then be introduced into the wellbore 118 via pumps (e.g., cementing unit 144), for example. In the foamed embodiments, the base slurry may be pumped into the wellbore 118, and a foaming agent may be metered into the base slurry followed by injection of a gas, e.g., at a foam mixing “T,” in an amount sufficient to foam the base slurry thereby forming a foamed treatment fluid, in accordance with certain embodiments. After foaming, the foamed treatment fluid may be introduced into the wellbore 118. As will be appreciated by those of ordinary skill in the art, with the benefit of this disclosure, other suitable techniques for preparing treatment fluids may be used in accordance with the present disclosure.

In some embodiments, methods may include enhancing rheological properties of a treatment fluid (e.g., spacer fluid 140, cement composition 142, etc.). The method may comprise including kiln dust in a treatment fluid. Optional additives as described previously may also be included in the treatment fluid. The kiln dust may be included in the treatment fluid in an amount sufficient to provide a higher yield point than a first fluid. The higher yield point may be desirable, for example, to effectively displace the first fluid from the wellbore. As used herein, the term “yield point” refers to the resistance of a fluid to initial flow, or representing the stress required to start fluid movement. In an embodiment, the yield point of the treatment fluid at a temperature of up to about 180° F. is greater than about 5 lb/100 ft². In an embodiment, the yield point of the treatment fluid at a temperature of up to about 180° F. is greater than about 10 lb/100 ft². In an embodiment, the yield point of the treatment fluid at a temperature of up to about 180° F. is greater than about 20 lb/100 ft². It may be desirable for the treatment fluid to not thermally thin to a yield point below the first fluid at elevated temperatures. Accordingly, the treatment fluid may have a higher yield point than the first fluid at elevated temperatures, such as 180° F. or bottom hole static temperature (“BHST”). In one embodiment, the treatment fluid may have a yield point that increases at elevated temperatures. For example, the treatment fluid may have a yield point that is higher at 180° F. than at 80° F. By way of further example. The treatment fluid may have a yield point that is higher at BHST than at 80° F.

In some embodiments, the treatment fluids may be used in the displacement of a drilling fluid 126 from a wellbore 118. The drilling fluid 126 may include, for example, any number of fluids, such as solid suspensions, mixtures, and emulsions. In some embodiments, the drilling fluid 126 may comprise an oil-based drilling fluid. An example of a suitable oil-based drilling fluid comprises an invert emulsion. In some embodiments, the oil-based drilling fluid may comprise an oleaginous fluid. Examples of suitable oleaginous fluids that may be included in the oil-based drilling fluids include, but are not limited to, α-olefins, internal olefins, alkanes, aromatic solvents, cycloalkanes, liquefied petroleum gas, kerosene, diesel oils, crude oils, gas oils, fuel oils, paraffin oils, mineral oils, low-toxicity mineral oils, olefins, esters, amides, synthetic oils (e.g., polyolefins), polydiorganosiloxanes, siloxanes, organosiloxanes, ethers, acetals, dialkylcarbonates, hydrocarbons, and combinations thereof.

To facilitate a better understanding of the present invention, the following examples of certain aspects of some embodiments are given. In no way should the following examples be read to limit, or define, the scope of the invention. In the following examples, concentrations are given in weight percent of the overall composition.

Example 1

Sample treatment fluids were prepared to evaluate the rheological properties of spacer fluids containing kiln dust. In this example, cement kiln dust was used. The sample treatment fluids were prepared as follows. First, all dry components (e.g., cement kiln dust, fly ash, bentonite, free water control additive, etc.) were weighed into a glass container having a clean lid and agitated by hand until blended. Tap water was then weighed into a Waring blender jar. The dry components were then mixed into the water with 4,000 rpm stirring. The blender speed was then increased to 12,000 rpm for about 35 seconds.

Sample Spacer Fluid No. 1 was an 11 pound per gallon slurry that comprised 60.62% water, 34.17% cement kiln dust, 4.63% fly ash, and 0.58% free water control additive (WG-17™ solid additive).

Sample Spacer Fluid No. 2 was an 11 pound per gallon slurry that comprised 60.79% water, 30.42% cement kiln dust, 4.13% fly ash, 0.17% free water control additive (WG-17™ solid additive), 3.45% bentonite, and 1.04% Econolite™ additive.

Rheological values were then determined using a Fann Model 35 Viscometer. Dial readings were recorded at speeds of 3, 6, 100, 200, and 300 with a B1 bob, an R1 rotor, and a 1.0 spring. The dial readings, plastic viscosity, and yield points for the spacer fluids were measured in accordance with API Recommended Practices 10B, Bingham plastic model and are set forth in the table below. The abbreviation “PV” refers to plastic viscosity, while the abbreviation “YP” refers to yield point.

TABLE 1

YP

(lb/

Sample
Temp.
Viscometer RPM
PV
100

Fluid
(° F.)
300
200
100
6
3
(cP)
ft²)

1
80
145
127
90
24
14
113.3
27.4

180
168
143
105
26
15
154.5
30.3

2
80
65
53
43
27
22
41.1
26.9

180
70
61
55
22
18
51.6
25.8

The thickening time of the Sample Fluid No. 1 was also determined in accordance with API Recommended Practice 10B at 205° F. Sample Fluid No. 1 had a thickening time of more than 6:00+ hours.

Accordingly, the above example illustrates that the addition of cement kiln dust to a treatment fluid may provide suitable properties for use in subterranean applications. In particular, the above example illustrates, inter alia, that the cement kiln dust may be used to provide a treatment fluid that may not exhibit thermal thinning with the treatment fluid potentially even having a yield point that increases with temperature. For example, Sample Fluid No. 2 had a higher yield point at 180° F. than at 80° F. In addition, the yield point of Sample Fluid No. 1 had only a slight decrease at 180° F. as compared to 80° F. Even further, the example illustrates that addition of the cement kiln dust to a treatment fluid may provide a plastic viscosity that increases with temperature.

Example 2

Additional sample treatment fluids were prepared to further evaluate the rheological properties of spacer fluids containing kiln dust. Cement kiln dust was used in this example, The sample treatment fluids were prepared as follows. First, all dry components (e.g., cement kiln dust, fly ash) were weighed into a glass container having a clean lid and agitated by hand until blended. Tap water was then weighed into a Waring blender jar. The dry components were then mixed into the water with 4,000 rpm stirring. The blender speed was then increased to 12,000 rpm for about 35 seconds.

Sample Fluid No. 3 was a 12.5 pound per gallon fluid that comprised 47.29% water and 52.71% cement kiln dust.

Sample Fluid No. 4 was a 12.5 pound per gallon fluid that comprised 46.47% water, 40.15% cement kiln dust, and 13.38% fly ash.

Sample Fluid No. 5 was a 12.5 pound per gallon fluid that comprised 45.62% water, 27.19% cement kiln dust, and 27.19% fly ash.

Sample Fluid No. 6 was a 12.5 pound per gallon fluid that comprised 44.75% water, 13.81% cement kiln dust, and 41.44% fly ash.

Sample Fluid No. 7 (comparative) was a 12.5 pound per gallon fluid that comprised 43.85% water, and 56.15% fly ash.

Rheological values were then determined using a Fann Model 35 Viscometer. Dial readings were recorded at speeds of 3, 6, 30, 60, 100, 200, 300, and 600 with a B1 bob, an R1 rotor, and a 1.0 spring. The dial readings, plastic viscosity, and yield points for the spacer fluids were measured in accordance with API Recommended Practices 10B, Bingham plastic model and are set forth in the table below. The abbreviation “PV” refers to plastic viscosity, while the abbreviation “YP” refers to yield point.

TABLE 2

Cement

Kiln

YP

Dust-

(lb/

Sample
Fly Ash
Temp.
Viscometer RPM
PV
100

Fluid
Ratio
(° F.)
600
300
200
100
60
30
6
3
(cP)
ft²)

3
100:0
80
33
23
20
15
13
12
8
6
12
11

130
39
31
27
23
22
19
16
11
12
19

180
66
58
51
47
40
38
21
18
16.5
41.5

4
75:25
80
28
22
19
15
14
11
8
6
10.5
11.5

130
39
28
25
21
19
16
14
11
10.5
17.5

180
51
39
36
35
31
26
16
11
6
33

5
50:50
80
20
11
8
6
5
4
4
3
7.5
3.5

130
21
15
13
10
9
8
6
5
7.5
7.5

180
25
20
17
14
13
12
7
5
9
11

6
25:75
80
16
8
6
3
2
1
0
0
7.5
0.5

130
15
8
6
4
3
2
1
1
6
2

180
15
9
7
5
4
4
2
2
6
3

7
0:100
80
16
7
5
3
1
0
0
0
6
1

(Comp.)

130
11
4
3
1
0
0
0
0
4.5
−0.5

180
8
3
2
0
0
0
0
0
4.5
−1.5

Accordingly, the above example illustrates that the addition of the cement kiln dust to a treatment fluid may provide suitable properties for use in subterranean applications. In particular, the above example illustrates, inter alia, that the cement kiln dust may be used to provide a treatment fluid that may not exhibit thermal thinning with the treatment fluid potentially even having a yield point that increases with temperature. In addition, as illustrated in Table 2 above, higher yield points were observed for treatment fluids with higher concentrations of the cement kiln dust.

Example 3

A sample treatment fluid containing kiln dust was prepared to compare the rheological properties of a treatment fluid containing kiln dust with an oil-based drilling fluid. In this example, cement kiln dust was used. The sample fluid was prepared as follows. First, all dry components (e.g., cement kiln dust, fly ash, bentonite, etc.) were weighed into a glass container having a clean lid and agitated by hand until blended. Tap water was then weighed into a Waring blender jar. The dry components were then mixed into the water with 4,000 rpm stirring. The blender speed was then increased to 12,000 rpm for about 35 seconds.

Sample Fluid No. 8 was an 11 pound per gallon slurry that comprised 60.79% water, 30.42% cement kiln dust, 4.13% fly ash, 0.17% free water control additive (WG-17™ solid additive), 3.45% bentonite, and 1.04% Econolite™ additive.

The oil-based drilling fluid was a 9.1 pound per gallon oil-based mud.

Rheological values were then determined using a Fann Model 35 Viscometer. Dial readings were recorded at speeds of 3, 6, 100, 200, and 300 with a B1 bob, an R1 rotor, and a 1.0 spring. The dial readings, plastic viscosity, and yield points for the spacer fluid and drilling fluid were measured in accordance with API Recommended Practices 10B, Bingham plastic model and are set forth in the table below. The abbreviation “PV” refers to plastic viscosity, while the abbreviation “YP” refers to yield point. The abbreviation “OBM” refers to oil-based mud.

TABLE 3

YP

(lb/

Sample
Temp.
Viscometer RPM
PV
100

Fluid
(° F.)
300
200
100
6
3
(cP)
ft²)

8
80
59
50
39
22
15
42
21.2

180
82
54
48
16
13
65.3
17

OBM
80
83
64
41
11
10
74.6
12.1

180
46
35
23
10
10
36.7
10.5

Example 4

A foamed treatment fluid (Sample Fluid 9) was prepared that comprised cement kiln dust. First, a base slurry was prepared that had a density of 10 ppg and comprised cement kiln dust, a free water control additive (0.7% by weight of cement kiln dust), a lightweight additive (4% by weight of cement kiln dust), and fresh water (32.16 gallons per 94-pound sack of cement kiln dust). The free water control additive was SA-1015™ suspending aid. The lightweight additive was ECONOLITE™ additive. Next, a foaming agent (FOAMER™ 760 foamer/stabilizer) in an amount of 2% bvow was added, and the base slurry was then mixed in a foam blending jar for 4 seconds at 12,000 rpm. The resulting foamed treatment fluid had a density of 8.4 ppg. The “sink” of the resultant foamed treatment fluid was then measured using a free fluid test procedure as specified in API Recommended Practice 10B. However, rather than measuring the free fluid, the amount of “sink” was measured after the foamed treatment fluid remained static for a period of 2 hours. The foamed treatment fluid was initially at 200° and cooled to ambient temperature over the 2-hour period. The measured sink for this foamed treatment fluid was 5 millimeters.

Example 5

Another foamed treatment fluid (Sample Fluid 10) was prepared that comprised cement kiln dust. First, a base slurry was prepared that had a density of 10.5 ppg and comprised cement kiln dust, a free water control additive (0.6% by weight of cement kiln dust), a lightweight additive (4% by weight of cement kiln dust), and fresh water (23.7 gallons per 94-pound sack of cement kiln dust). The free water control additive was SA-1015™ suspending aid. The lightweight additive was ECONOLITE™ additive. Next, a foaming agent (a hexylene glycol/cocobetaine blended surfactant) in an amount of 2% bvow was added, and the base slurry was then mixed in a foam blending jar for 6 seconds at 12,000 rpm. The resulting foamed treatment fluid had a density of 8.304 ppg. The resultant foamed treatment fluid had a sink of 0 millimeters, measured as described above for Example 4.

Example 6

The following series of tests were performed to determine the compressive strength of sample treatment fluids after consolidation. Twenty-two samples, labeled sample fluids 11-32 in the table below, were prepared having a density of 12.5 ppg using various concentrations of additives. The amount of these additives in each sample fluid are indicated in the table below with “% by weight” indicating the amount of the particular component by weight of Additive 1+Additive 2. The abbreviation “gal/sk” in the table below indicates gallons of the particular component per 94-pound sack of Additive 1 and Additive 2.

The cement kiln dust used was supplied by Holcim (US) Inc., from Ada, Okla. The shale used was supplied by Texas Industries, Inc., from Midlothian, Tex. The pumice used was either DS-200 or DS-300 lightweight aggregate available from Hess Pumice Products, Inc. The silica flour used was SSA-1™ cement additive, from Halliburton Energy Services, Inc. The course silica flour used was SSA-2™ course silica flour, from Halliburton Energy Services, Inc. The metakaolin used was MetaMax® metakaolin, from BASF. The amorphous silica used was SILICALITE™ cement additive, from Halliburton Energy Services, Inc. The perlite used was supplied by Hess Pumice Products, Inc. The slag used was supplied by LaFarge North America. The Portland cement Interground with pumice was FineCem™ cement, from Halliburton Energy Services, Inc. The fly ash used was POZMIX® cement additive, from Halliburton Energy Services, Inc. The micro-fine cement used was MICRO MATRIX® cement having an average particle size of 7.5 microns, from Halliburton Energy Services, Inc. The rice husk ash used was supplied by Rice Hull Specialty Products, Stuttgart, Ark. The biopolymer used was supplied by CP Kelco, San Diego, Calif. The barite used was supplied by Baroid Industrial Drilling Products. The latex used was Latex 3000™ cement additive from Halliburton Energy Services, Inc. The ground rubber used was LIFECEM™ 100 cement additive from Halliburton Energy Services, Inc. The nano-clay used was supplied by Nanocor Inc. The set retarder used was SCR-100™ cement retarder, from Halliburton Energy Services, Inc. SCR-100™ cement retarder is a copolymer of acrylic acid and 2-acrylamido-2-methylpropane sulfonic acid.

After preparation, the sample fluids were allowed to cure for seven days in a 2″ by 4″ metal cylinder that was placed in a water bath at 180° F. to form set cylinders. Immediately after removal from the water bath, destructive compressive strengths were determined using a mechanical press in accordance with API RP 10B-2. The results of these tests are set forth below. The term “cement kiln dust” is abbreviated “CKD” in the table below.

TABLE 4

Additive

#1
Additive #2
Additive #3
Cement
7-Day

Sam-

%

%

%
Set
Comp.

ple
Water

by

by

by
Retarder
Strength

Fluid
gal/sk
Type
wt
Type
wt
Type
wt
% by wt
PSI

11
5.72
CKD
50
Shale
50
—
—
0
510

12
4.91
Pumice
50
Lime
50
—
—
1
646

DS-

200

13
5.88
CKD
50
Silica Flour
50
—
—
0
288

14
6.05
CKD
50
Metakaolin
50
—
—
0
104

15
5.71
CKD
50
Amorphous
50
—
—
1
251

Silica

16
5.13
CKD
50
Perlite
50
—
—
0
1031

17
5.4
CKD
50
Lime
50
—
—
0
58

18
5.49
CKD
50
Pumice DS-
50
—
—
0
624

200

19
6.23
CKD
50
Slag
50
—
—
0
587

20
5.88
CKD
50
Course
50
—
—
0
1018

Silica Flour

21
6.04
CKD
50
Portland
50
—
—
1
1655

Cement

Interground

with Pumice

22
5.63
CKD
50
Fly Ash
50
—
—
0
870

23
5.49
CKD
50
Pumice DS-
50
—
—
0
680

325

24
5.03
Fly
50
Lime
50
—
—
170

Ash

25
5.65
Slag
50
Lime
50
—
—
1
395

26
6.36
CKD
50
Micro-fine
50
—
—
2
788

cement

27
6.08
CKD
80
Rice Husk
20
—
—
1
203

Ash

28
5.42
CKD
50
Biopolymer
50
—
—
1
265

29
7.34
CKD
50
Barite
50
—
—
0
21

30
4.02
CKD
100
—
—
Latex
2
1
164.6

31
2.71
CKD
100
—
—
Ground
10
1
167.6

Rubber

32
6.15
CKD
100
—
—
Nano-
2
0
102.5

Clay

Accordingly, the above example illustrates that a treatment fluid comprising kiln dust may be capable of consolidation. For example, 7-day compressive strengths of 1000 psi or even higher were observed for certain sample slurries.

Example 7

The following series of tests were performed to evaluate the thickening times of sample treatment fluids. For this example, the thickening times for Sample Fluids 11-32 from Example 6 were determined. As indicated below, the compositions for Samples Fluids 11-32 were the same as from Example 6 except the concentration of the cement set retarder was adjusted for certain samples. The thickening time, which is the time required for the compositions to reach 70 Bearden units of consistency, was determined for each fluid at 230° F. in accordance with API RP 10B-2. The results of these tests are set forth below. The term “cement kiln dust” is abbreviated “CKD” in the table below.

TABLE 5

Additive

#1
Additive #2
Additive #3
Cement

%

%

%
Set
Thickening

Sample
Water

by

by

by
Retarder
Time

Fluid
gal/sk
Type
wt
Type
wt
Type
Wt
% by wt
hr:min

11
5.72
CKD
50
Shale
50
—
—
1
11:04

12
4.91
Pumice
50
Lime
50
—
—
1
0:30

DS-

200

13
5.88
CKD
50
Silica Flour
50
—
—
1
3:31

14
6.05
CKD
50
Metakaolin
50
—
—
1
3:13

15
5.71
CKD
50
Amorphous
50
—
—
1
2:15

Silica

16
5.13
CKD
50
Perlite
50
—
—
1
7:30

17
5.4
CKD
50
Lime
50
—
—
1
2:42

18
5.49
CKD
50
PumiceDS-
50
—
—
1
10:00

200

19
6.23
CKD
50
Slag
50
—
—
1
8:08

20
5.88
CKD
50
Course
50
—
—
1
20 hr+

Silica Flour

21
6.04
CKD
50
Portland
50
—
—
1
5:58

Cement

Interground

with Pumice

22
5.63
CKD
50
Fly Ash
50
—
—
1
12 hr+

23
5.49
CKD
50
Pumice DS-
50
—
—
1
7:30

325

24
5.03
Fly
50
Lime
50
—
—
1
3:32

Ash

25
5.65
Slag
50
Lime
50
—
—
1
4:05

26
6.36
CKD
50
Micro-fine
50
—
—
2
1:30

cement

27
6.08
CKD
80
Rice Husk
20
—
—
1
30 hr+

Ash

28
5.42
CKD
50
Biopolymer
50
—
—
1
1:35

29
7.34
CKD
50
Barite
50
—
—
1
18 hr+

30
4.02
CKD
100
—
—
Latex
2
1
1:10

31
2.71
CKD
100
—
—
Ground
10
1
20 hr+

Rubber

32
6.15
CKD
100
—
—
Nano-
2
0
54:00

Clay

Accordingly, the above example illustrates that a settable spacer fluid may have acceptable thickening times for certain applications.

Example 8

The following series of tests were performed to evaluate the rheological properties of sample fluids. For this example, the rheological properties of Sample Fluids 11-32 were determined. The rheological values were determined using a Fann Model 35 Viscometer. Dial readings were recorded at speeds of 3, 6, 30, 60, 100, 200, 300, and 600 with a B1 bob, an R1 rotor, and a 1.0 spring. An additional sample was used for this specific test. It is Sample Fluid 33 and comprised barite and 0.5% of a suspending agent by weight of the barite. The suspending agent was SA™-1015, available from Halliburton Energy Services, Inc. The water was included in an amount sufficient to provide a density of 12.5 ppg. Sample 33's rheological properties were measured twice at two different temperatures and the values per temperature were averaged to present the data shown below. Temperature is measured in degrees Fahrenheit. The results of these tests are set forth below.

TABLE 6

Additive

Additive

Sample
#1
% by
Additive #2
% by
#3
% by

Viscometer RPM

Fluid
Type
wt
Type
wt
Type
wt
Temp.
300
200
100
60
30
6
3
600

11
CKD
50
Shale
50
—
—
80
29
21
14
11
9
6
5
39

12
Pumice
50
Lime
50
—
—
80
24
17
9
6
5
2
1
48

DS-200

13
CKD
50
Silica Flour
50
—
—
80
16
12
8
6
5
4
3
24

14
CKD
50
Metakaolin
50
—
—
80
36
28
19
15
12
9
8
64

15
CKD
50
Amorphous
50
—
—
80
31
24
18
14
12
10
9
49

Silica

16
CKD
50
Perlite
50
—
—
80
40
34
27
23
20
15
9
61

17
CKD
50
Lime
50
—
—
80
46
41
34
30
27
16
11
65

18
CKD
50
Pumice DS-
50
—
—
80
23
19
14
11
9
7
6
40

200

19
CKD
50
Slag
50
—
—
80
23
20
14
11
9
6
5
41

20
CKD
50
Course
50
—
—
80
27
19
12
9
7
4
3
64

Silica Flour

21
CKD
50
Portland
50
—
—
80
15
10
7
5
3
2
1
18

Cement

Interground

with Pumice

22
CKD
50
Fly Ash
50
—
—
80
12
9
6
4
3
2
1
21

23
CKD
50
Pumice DS-
50
—
—
80
39
32
24
21
17
12
7
57

325

24
Fly Ash
50
Lime
50
—
—
80
12
9
6
4
3
2
2
24

25
Slag
50
Lime
50
—
—
80
15
10
5
3
2
1
1
23

26
CKD
50
Micro-fine
50
—
—
80
10
7
4
3
2
1
0
14

cement

27
CKD
80
Rice Husk
20
—
—
80
24
15
9
7
5
3
2
41

Ash

28
CKD
50
Biopolymer
50
—
—
80
175
111
53
31
15
4
3
220

29
CKD
50
Barite
50
—
—
80
48
40
30
26
22
15
13
2

30
CKD
100
—
—
Latex
2
80
48
39
28
23
19
17
15
82

31
CKD
100
—
—
Ground
10
80
65
56
42
40
39
30
22
105

Rubber

32
CKD
100
—
—
Nano-
2
80
22
18
12
10
8
6
5
37

Clay

33
Barite
100
—
—
SA™-
0.5
80
41
36.5
30.5
28
25.5
20.5
18.5
NA

1015

33
Barite
100
—
—
SA™-
0.5
180
38
35.5
32
30
28
23.5
22
NA

1015

Accordingly, the above example indicates that a treatment fluid may have acceptable rheological properties for a particular application.

Example 9

The following series of tests were performed to further evaluate the compressive strength of sample treatment fluids. Ten samples, labeled Sample Fluids 34-43 in the table below were prepared, having a density of 13 ppg using various concentrations of additives. The amount of these additives in each sample are indicated in the table below with “% by weight” indicating the amount of the particular component by weight of the dry solids, which is the kiln dust, the Portland cement, the cement accelerator, the fly ash, and/or the lime. The abbreviation “gal/sk” in the table below indicates gallons of the particular component per 94-pound sack of the dry solids. The term “cement kiln dust” is abbreviated “CKD” in the table below.

The cement kiln dust used was Mountain cement kiln dust from Laramie Wyo., except for Sample Fluid 43 which used cement kiln dust from Holcim (US) Inc., Ada, Okla. The Portland cement used in Sample Fluids 34 and 35 was CEMEX Type 3 Portland cement, from CEMEX USA. The cement accelerator used in Sample Fluid 34 was CAL-SEAL™ accelerator, from Halliburton Energy Services Inc. CAL-SEAL™ Accelerator is gypsum. The Class F fly ash used in Slurries 37-41 was from Coal Creek Station. The Class C fly ash used in Slurries 36 was from LaFarge North America.

After preparation, the samples were allowed to cure for twenty-four or forty-eight hours in a 2″ by 4″ metal cylinder that was placed in a water bath at 160° F. to form set cylinders. For certain samples, separate cylinders were cured for twenty-four hours and forty-eight hours. Immediately after removal from the water bath, destructive compressive strengths were determined using a mechanical press in accordance with API RP 10B-2. The results of these tests are set forth below.

TABLE 7

Class
Class

Portland
Cement
F Fly
C Fly

24-Hr
48-Hr

Cement
Accel.
Ash
Ash
Lime
Comp.
Comp.

Sample
Water
CKD %
% by
% by
% by
% by
% by
Strength
Strength

Fluid
gal/sk
by wt
wt
wt
wt
wt
wt
PSI
PSI

34
8.75
85
10
5
0
0
0
73.4
—

35
8.75
90
10
0
0
0
0
99.8
—

36
8.14
70
0
0
0
30
0
210
—

37
8.25
70
0
0
25
0
5
388
—

38
8.20
75
0
0
21
0
4
300
784

39
8.27
80
0
0
17.5
0
2.5
224
641

40
9.61
70
0
0
25
0
5
219
567

41
11.5
70
0
0
25
0
5
165
369

42
5.12
100
0
0
0
0
0
36.2
—

43
5.12
100
0
0
0
0
0
60.8
—

Accordingly, the above example illustrates that a treatment fluid may have acceptable compressive strengths for certain applications.

Example 10

The following series of tests were performed to evaluate the static gel strength development of sample treatment fluids. Two samples, labeled Sample Fluids 44 and 45 were prepared having a density of 11 and 13.5 ppg respectively using various concentrations of additives. The component concentrations of each sample are as follows:

For Sample Fluid 44, the sample comprised a blend of cement kiln dust (80% by weight), fly ash (16% by weight) and hydrated lime (4% by weight). The sample also comprised a suspending aid in an amount of 0.4% by weight of the blend. Sufficient water was included in the sample to provide a density of 11 ppg. The cement kiln dust used was from Holcim (US) Inc., Ada, Okla. The fly ash used was POZMIX® cement additive, from Halliburton Energy Services, Inc. The suspending agent was SA™-1015 suspending agent, available from Halliburton Energy Services, Inc.

For Sample Fluid 45, the sample comprised a mixture of cement kiln dust (80% by weight), fly ash (16% by weight), and hydrate lime (4% by weight). Sufficient water was included in the sample to provide a density of 13.5 ppg. The cement kiln dust used was from Holcim (US) Inc., Ada, Okla. The fly ash used was POZMIX® cement additive, from Halliburton Energy Services, Inc.

The static gel strength of the samples was measured in accordance with API Recommended Practice on Determining the Static Gel Strength of Cement Formations, ANSI/API Recommended Practice 10B-6. FIGS. 1 and 2 show the static gel strength measurements for Sample Fluids 44 and 45, respectively, as a function of time. As seen in the figures, the samples progress through the transition time, defined as the time between 100 SGS and 500 SGS, very quickly with a total transition time of 19 minutes for the sample 34 and 6 minutes for sample 35. These short transition times are faster than most cement compositions.

Example 11

The following tests were performed to further evaluate the static gel strength development of sample treatment fluids. Two samples, labeled Samples Fluids 46 and 47 were prepared having a density of 13.002 and 10.999 ppg respectively using various concentrations of additives. The component concentrations of each sample are as follows:

For Sample Fluid 46, the sample comprised a blend of cement kiln dust (100% by weight), POZMIX® cement additive (50% by weight of the cement kiln dust), He-601 cement retarder (1% by weight of the cement kiln dust), HR®-25 cement retarder (0.6% by weight of the cement kiln dust), and D-Air 5000™ defoamer (0.5% by weight of the cement kiln dust). Sufficient water was included in the sample to provide a density of 13.002 ppg. The cement kiln dust used was from Holcim (US) Inc., Ada, Okla. POZMIX® cement additive was from Halliburton Energy Services, Inc. HR®-601 cement retarder was from Halliburton Energy Services, Inc. HR®-25 cement retarder was from Halliburton Energy Services, Inc. D-Air 5000™ defoamer was from Halliburton Energy Services, Inc.

For Sample Fluid 47, the sample comprised a blend of cement kiln dust (100% by weight), SA-1015 (0.4% by weight of the cement kiln dust), and D-Air 5000™ defoamer (0.5% by weight of the cement kiln dust). Sufficient water was included in the sample to provide a density of 10.999 ppg. The cement kiln dust used was from Holcim (US) Inc., Ada, Okla. SA™-1015 suspending agent was from Halliburton Energy Services, Inc. D-Air 5000™ defoamer was from Halliburton Energy Services, Inc.

TABLE 8

Difference

between 100

Time to reach
Time to reach
lbf/100 ft^sand

Sample
Temp
100 lbf/100 ft^s
500 lbf/100 ft^s
500 lbf/100 ft^s

Fluid
(° F.)
(hr:min)
(hr:min)
(hr:min)

46
220
3:25
5:04
1:39

47
220
3:07
3:17
00:10

As seen in the table, Sample Fluid 47 progresses through the transition time, defined as the time between 100 SGS and 500 SGS, very quickly with a total transition time of 10 minutes. Sample Fluid 46 is much slower taking over an hour to progress through the transition time. The short transition time of Sample Fluid 47 is faster than most cement compositions.

It should be understood that the compositions and methods are described in terms of “comprising,” “containing,” or “including” various components or steps, the compositions and methods can also “consist essentially of” or “consist of” the various components and steps. Moreover, the indefinite articles “a” or “an,” as used in the claims, are defined herein to mean one or more than one of the element that it introduces.

For the sake of brevity, only certain ranges are explicitly disclosed herein. However, ranges from any lower limit may be combined with any upper limit to recite a range not explicitly recited, as well as, ranges from any lower limit may be combined with any other lower limit to recite a range not explicitly recited, in the same way, ranges from any upper limit may be combined with any other upper limit to recite a range not explicitly recited. Additionally, whenever a numerical range with a lower limit and an upper limit is disclosed, any number and any included range falling within the range are specifically disclosed. In particular, every range of values (of the form, “from about a to about b,” or, equivalently, “from approximately a to b,” or, equivalently, “from approximately a-b”) disclosed herein is to be understood to set forth every number and range encompassed within the broader range of values even if not explicitly recited. Thus, every point or individual value may serve as its own lower or upper limit combined with any other point or individual value or any other lower or upper limit, to recite a range not explicitly recited.

Therefore, the present invention is well adapted to attain the ends and advantages mentioned as well as those that are inherent therein. The particular embodiments disclosed above are illustrative only, as the present invention may be modified and practiced in different but equivalent manners apparent to those skilled in the art having the benefit of the teachings herein. Although individual embodiments are discussed, the invention covers all combinations of all those embodiments. Furthermore, no limitations are intended to the details of construction or design herein shown, other than as described in the claims below. Also, the terms in the claims have their plain, ordinary meaning unless otherwise explicitly and clearly defined by the patentee. It is therefore evident that the particular illustrative embodiments disclosed above may be altered or modified and all such variations are considered within the scope and spirit of the present invention. If there is any conflict in the usages of a word or term in this specification and one or more patent(s) or other documents that may be incorporated herein by reference, the definitions that are consistent with this specification should be adopted.

Claims

1. A drilling system comprising: a bottom hole assembly comprising a drill bit;a cement composition;a drilling fluid; anda consolidating spacer fluid for introduction into a wellbore through the drill bit between the drilling fluid and the cement composition, wherein the consolidating spacer fluid comprises a kiln dust and water.
2. The system of claim 1, further comprising a tubular, wherein the bottom hole assembly is attached to the tubular.
3. The system of claim 2, wherein the tubular is a drill pipe, a casing, or a combination thereof.
4. The system of claim 1, wherein the bottom hole assembly is retrievable.
5. The system of claim 1, wherein the bottom hole assembly is non-retrievable.
6. The system of claim 1, wherein at least a portion of the wellbore extends at a direction that is slanted from vertical.
7. The system of claim 1, wherein the consolidating fluid has a transition time of about 45 minutes or less.
8. The system of claim 1, wherein the consolidating spacer fluid has a density of about 4 pounds per gallon to about 13 pounds per gallon.
9. The system of claim 1, wherein the kiln dust is from the manufacture of cement.
10. The system of claim 1, wherein the kiln dust comprises SiO2, Al2O3, Fe2O3, CaO, MgO, SO3, Na2O, and K2O.
11. The system of claim 1, wherein the kiln dust may be present in the consolidating spacer fluid in an amount of about 1% to about 65% by weight of the consolidating spacer fluid.
12. The system of claim 1 wherein the consolidating spacer fluid is capable of displacing at least a portion of the drilling fluid from the wellbore.
13. A drilling system comprising: a bottom hole assembly comprising a drill bit;a drilling fluid;a cement composition; anda consolidated spacer fluid for introduction into a wellbore through the drill bit between the drilling fluid and the cement composition, wherein the consolidated spacer fluid comprises a kiln dust and water, wherein the consolidated spacer fluid has at least one property selected from the group consisting of: (i) a yield point of from about 25 Pascals to about 250 pascals; (ii) a static gel strength of from about 70 lbf/100 ft2 to about 500 lbf/100 ft2, (iii) a yield limit in compression from about 1 psi to about 2,000 psi, and (iv) an unconfined uniaxial compressive strength of from about 5 psi to about 10,000 psi.
14. The system of claim 13, wherein the consolidated spacer fluid further has at least one property selected from the group consisting of: (i) a zero gel time of about 8 hours or less, (ii) a transition time of about 45 minutes or less, and (iii) a static gel strength of about 500 lbf/100 ft2 in a time of from about 10 minutes to about 8 hours.
15. The system of claim 13, wherein the kiln dust is from the manufacture of cement.
16. The system of claim 13, further comprising a bond log capable for measuring the degree of bonding of the consolidated spacer fluid to a casing in the well bore.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a divisional application of U.S. patent application Ser. No. 14/091,332, filed Nov. 26, 2013, which is a continuation-in-part of U.S. patent application Ser. No. 13/851,925, filed Mar. 27, 2013, which is a divisional application of U.S. patent application Ser. No. 13/725,833, filed Dec. 21, 2012, issued as U.S. Pat. No. 8,505,630 on Aug. 13, 2013, which is a continuation-in-part of U.S. application Ser. No. 13/535,145, filed Jun. 27, 2012, issued as U.S. Pat. No. 8,505,629 on Aug. 13, 2013, which is a continuation-in-part of U.S. application Ser. No. 12/895,436, filed Sep. 30, 2010, issued as U.S. Pat. No. 8,522,872 on Sep. 3, 2013, which is a continuation-in-part of U.S. application Ser. No. 12/264,010, filed Nov. 3, 2008, issued as U.S. Pat. No. 8,333,240 on Dec. 18, 2012, which is a continuation-in-part of U.S. application Ser. No. 11/223,669, filed Sep. 9, 2005, issued as U.S. Pat. No. 7,445,669 on Nov. 4, 2008, the entire disclosures of which are incorporated herein by reference.

US Referenced Citations (412)

Number	Name	Date	Kind
1931921	Breerwood	Oct 1933	A
2021956	Gladney et al.	Nov 1935	A
2045899	Davis	Jun 1936	A
2094316	Cross et al.	Sep 1937	A
2133622	Larmour et al.	Oct 1938	A
2144254	Breerwood	Jan 1939	A
2193775	Stratford	Mar 1940	A
2193807	Dieterich	Mar 1940	A
2214715	Breerwood	Sep 1940	A
2329940	Ponzer	Sep 1943	A
2592468	Rex et al.	Apr 1952	A
2772739	Arie	Dec 1956	A
2842205	Allen et al.	Jul 1958	A
2844361	Dilcher et al.	Jul 1958	A
2848051	Willaims	Aug 1958	A
2871133	Palonen et al.	Jan 1959	A
2880096	Hurley	Mar 1959	A
2945769	Gama et al.	Jul 1960	A
3024125	Lee	Mar 1962	A
3066031	Schifferle	Nov 1962	A
3168139	Kennedy et al.	Feb 1965	A
3320077	Prior	May 1967	A
3411580	Roberts et al.	Nov 1968	A
3421703	Galer	Jan 1969	A
3454095	Messenger et al.	Jul 1969	A
3467193	Messenger	Sep 1969	A
3473939	Mayberry et al.	Oct 1969	A
3499491	Wyant et al.	Mar 1970	A
3557876	Tragesser	Jan 1971	A
3574113	Shannon	Apr 1971	A
3574816	Abbdellatif et al.	Apr 1971	A
3628973	Greening et al.	Dec 1971	A
3748159	George	Jul 1973	A
3749173	Hill et al.	Jul 1973	A
3863718	Bruist	Feb 1975	A
3876005	Fincher et al.	Apr 1975	A
3887009	Miller et al.	Jun 1975	A
3887385	Quist et al.	Jun 1975	A
3921717	Danjushevsky et al.	Nov 1975	A
3959007	Pitt	May 1976	A
4018617	Nicholson	Apr 1977	A
4018619	Webster et al.	Apr 1977	A
4031184	McCord	Jun 1977	A
4036301	Powers et al.	Jul 1977	A
4083407	Griffin et al.	Apr 1978	A
4101332	Nicholson	Jul 1978	A
4105459	Mehta	Aug 1978	A
4141843	Watson	Feb 1979	A
4160674	Sawyer	Jul 1979	A
4176720	Wilson	Dec 1979	A
4268316	Wills	May 1981	A
4274881	Langton	Jun 1981	A
4304300	Watson	Dec 1981	A
4333764	Richardson	Jun 1982	A
4341562	Ahlbeck	Jul 1982	A
RE31190	Detroit et al.	Mar 1983	E
4400474	Copperthwaite et al.	Aug 1983	A
4407677	Wills, Jr.	Oct 1983	A
4423781	Thomas	Jan 1984	A
4432800	Kneller et al.	Feb 1984	A
4435216	Diehl et al.	Mar 1984	A
4436850	Burdick et al.	Mar 1984	A
4440576	Flannery et al.	Apr 1984	A
4460292	Durham et al.	Jul 1984	A
4462835	Car	Jul 1984	A
4470463	Holland	Sep 1984	A
4494990	Harris	Jan 1985	A
4515635	Rao et al.	May 1985	A
4519452	Tsao et al.	May 1985	A
4555269	Rao et al.	Nov 1985	A
4614599	Walker	Sep 1986	A
4624711	Styron	Nov 1986	A
4633950	Delhommer et al.	Jan 1987	A
4676317	Fry et al.	Jun 1987	A
4676832	Childs et al.	Jun 1987	A
4741782	Styron	May 1988	A
4784223	Worrall et al.	Nov 1988	A
4829107	Kindt et al.	May 1989	A
4883125	Wilson et al.	Nov 1989	A
4941536	Brothers et al.	Jul 1990	A
4992102	Barbour	Feb 1991	A
5030366	Wilson et al.	Jul 1991	A
5049288	Brothers et al.	Sep 1991	A
5058679	Hale et al.	Oct 1991	A
RE33747	Hartley et al.	Nov 1991	E
5086850	Harris et al.	Feb 1992	A
5113943	Wilson et al.	May 1992	A
5121795	Ewert et al.	Jun 1992	A
5123487	Harris et al.	Jun 1992	A
5125455	Harris et al.	Jun 1992	A
5127473	Harris et al.	Jul 1992	A
5183505	Spinney	Feb 1993	A
5183506	Zhang	Feb 1993	A
5213160	Nahm et al.	May 1993	A
5215585	Luthra et al.	Jun 1993	A
5238064	Dahl et al.	Aug 1993	A
5252128	Gopalkrishnan	Oct 1993	A
5266111	Barbour	Nov 1993	A
5290355	Jakel et al.	Mar 1994	A
5295543	Terry et al.	Mar 1994	A
5305831	Nahm	Apr 1994	A
5314022	Cowan et al.	May 1994	A
5316083	Nahm et al.	May 1994	A
5327968	Onan et al.	Jul 1994	A
5337824	Cowan	Aug 1994	A
5339902	Harris	Aug 1994	A
5346548	Mehta	Sep 1994	A
5352288	Mallow	Oct 1994	A
5358044	Hale et al.	Oct 1994	A
5358049	Hale et al.	Oct 1994	A
5361841	Hale et al.	Nov 1994	A
5361842	Hale et al.	Nov 1994	A
5368103	Heathman et al.	Nov 1994	A
5370185	Cowan et al.	Dec 1994	A
5372641	Carpenter	Dec 1994	A
5382290	Nahm et al.	Jan 1995	A
5383521	Onan et al.	Jan 1995	A
5383967	Chase	Jan 1995	A
5398758	Onan et al.	Mar 1995	A
5417759	Huddleston	May 1995	A
5421409	Mueller et al.	Jun 1995	A
5423379	Hale et al.	Jun 1995	A
5430235	Hooykaas et al.	Jul 1995	A
5439056	Cowan	Aug 1995	A
5454867	Brothers et al.	Oct 1995	A
5456751	Zandi et al.	Oct 1995	A
5458195	Totten et al.	Oct 1995	A
5464060	Hale et al.	Nov 1995	A
5472051	Brothers	Dec 1995	A
5476144	Nahm et al.	Dec 1995	A
5478391	Babaev et al.	Dec 1995	A
5484019	Griffith	Jan 1996	A
5494513	Fu et al.	Feb 1996	A
5499677	Cowan	Mar 1996	A
5515921	Cowan et al.	May 1996	A
5518996	Maroy et al.	May 1996	A
5520730	Barbour	May 1996	A
5529123	Carpenter et al.	Jun 1996	A
5529624	Riegler	Jun 1996	A
5536311	Rodrigues	Jul 1996	A
5542782	Carter et al.	Aug 1996	A
5554352	Jaques et al.	Sep 1996	A
5569324	Totten et al.	Oct 1996	A
5571318	Griffith et al.	Nov 1996	A
5580379	Cowan	Dec 1996	A
5584926	Borgholm et al.	Dec 1996	A
5585333	Dahl et al.	Dec 1996	A
5588489	Chatterji et al.	Dec 1996	A
5641584	Andersen et al.	Jun 1997	A
5673753	Hale et al.	Oct 1997	A
5681384	Liskowitz et al.	Oct 1997	A
5688844	Chatterji et al.	Nov 1997	A
5711383	Terry et al.	Jan 1998	A
5716910	Totten et al.	Feb 1998	A
5728654	Dobson et al.	Mar 1998	A
5789352	Carpenter et al.	Aug 1998	A
5795924	Chatterji et al.	Aug 1998	A
5820670	Chatterji et al.	Oct 1998	A
5851960	Totten et al.	Dec 1998	A
5866516	Costin	Feb 1999	A
5866517	Carpenter et al.	Feb 1999	A
5874387	Carpenter et al.	Feb 1999	A
5897699	Chatterji et al.	Apr 1999	A
5900053	Brothers et al.	May 1999	A
5913364	Sweatman	Jun 1999	A
5968255	Mehta et al.	Oct 1999	A
5988279	Udarbe et al.	Nov 1999	A
6022408	Stokes et al.	Feb 2000	A
6060434	Sweatman et al.	May 2000	A
6060535	Villar et al.	May 2000	A
6063738	Chatterji et al.	May 2000	A
6098711	Chatterji et al.	Aug 2000	A
6138759	Chatterji et al.	Oct 2000	A
6143069	Brothers et al.	Nov 2000	A
6145591	Boncan et al.	Nov 2000	A
6153562	Villar et al.	Nov 2000	A
6167967	Sweatman	Jan 2001	B1
6170575	Reddy et al.	Jan 2001	B1
6230804	Mueller et al.	May 2001	B1
6244343	Brothers et al.	Jun 2001	B1
6245142	Reddy et al.	Jun 2001	B1
6258757	Sweatman et al.	Jul 2001	B1
6264738	Lorke et al.	Jul 2001	B1
6277189	Chugh	Aug 2001	B1
6312515	Barlet-Gouedard et al.	Nov 2001	B1
6315042	Griffith et al.	Nov 2001	B1
6328106	Griffith et al.	Dec 2001	B1
6332921	Brothers et al.	Dec 2001	B1
6367550	Chatterji et al.	Apr 2002	B1
6379456	Heathman et al.	Apr 2002	B1
6402833	O'Hearn et al.	Jun 2002	B1
6409819	Ko	Jun 2002	B1
6416574	Steelhammer et al.	Jul 2002	B1
6451104	Mehta	Sep 2002	B2
6457524	Roddy	Oct 2002	B1
6478869	Reddy et al.	Nov 2002	B2
6478870	Marko	Nov 2002	B2
6488763	Brothers et al.	Dec 2002	B2
6488764	Westerman	Dec 2002	B2
6494951	Reddy et al.	Dec 2002	B1
6500252	Chatterji et al.	Dec 2002	B1
6502634	Evans et al.	Jan 2003	B1
6508305	Brannon et al.	Jan 2003	B1
6516884	Chatterji et al.	Feb 2003	B1
6524384	Griffith et al.	Feb 2003	B2
6547871	Chatterji et al.	Apr 2003	B2
6547891	Linden et al.	Apr 2003	B2
6555307	Maruyama	Apr 2003	B2
6561273	Brothers et al.	May 2003	B2
6562122	Dao et al.	May 2003	B2
6565647	Day et al.	May 2003	B1
6572697	Gleeson et al.	Jun 2003	B2
6610139	Reddy et al.	Aug 2003	B2
6626243	Go Boncan	Sep 2003	B1
6641658	Dubey	Nov 2003	B1
6645289	Sobolev et al.	Nov 2003	B2
6645290	Barbour	Nov 2003	B1
6656265	Garnier et al.	Dec 2003	B1
6660080	Reddy et al.	Dec 2003	B2
6666268	Griffith et al.	Dec 2003	B2
6668927	Chatterji et al.	Dec 2003	B1
6668929	Griffith et al.	Dec 2003	B2
6689208	Brothers	Feb 2004	B1
6702044	Reddy et al.	Mar 2004	B2
6706108	Polston	Mar 2004	B2
6708760	Chatterji et al.	Mar 2004	B1
6715568	Bailey	Apr 2004	B1
6716282	Griffith et al.	Apr 2004	B2
6729405	DiLullo et al.	May 2004	B2
6749679	Shi	Jun 2004	B2
6755905	Oates	Jun 2004	B2
6767398	Trato	Jul 2004	B2
6776237	Dao et al.	Aug 2004	B2
6796378	Reddy et al.	Sep 2004	B2
6797054	Chatterji et al.	Sep 2004	B2
6823940	Reddy et al.	Nov 2004	B2
6832652	Dillenbeck et al.	Dec 2004	B1
6835243	Brothers et al.	Dec 2004	B2
6837316	Reddy et al.	Jan 2005	B2
6840318	Lee	Jan 2005	B2
6840996	Morioka et al.	Jan 2005	B2
6846357	Reddy et al.	Jan 2005	B2
6848519	Reddy et al.	Feb 2005	B2
6869474	Perez-Pena	Mar 2005	B2
6869475	Krowl	Mar 2005	B1
6874353	Johnson	Apr 2005	B2
6874578	Garnier	Apr 2005	B1
6883609	Drochon	Apr 2005	B2
6887833	Brothers et al.	May 2005	B2
6889767	Reddy et al.	May 2005	B2
6899177	Chatterj et al.	May 2005	B2
6904971	Brothers et al.	Jun 2005	B2
6908507	Lalande et al.	Jun 2005	B2
6908508	Brothers	Jun 2005	B2
6911078	Barlet-Gouedard et al.	Jun 2005	B2
6964302	Luke et al.	Nov 2005	B2
6989057	Getzlaf et al.	Jan 2006	B2
7004263	Moriarty et al.	Feb 2006	B2
7022755	Chatterji et al.	Apr 2006	B1
7048053	Santra et al.	May 2006	B2
7055603	Caveny et al.	Jun 2006	B2
7073584	Reddy et al.	Jul 2006	B2
7073585	Morgan et al.	Jul 2006	B2
7077203	Roddy et al.	Jul 2006	B1
7096944	Vargo et al.	Aug 2006	B2
7101829	Guichard et al.	Sep 2006	B2
7137446	Gagliano et al.	Nov 2006	B2
7140439	Luke et al.	Nov 2006	B2
7140440	Luke et al.	Nov 2006	B2
7143827	Chatterji et al.	Dec 2006	B2
7147055	Brothers et al.	Dec 2006	B2
7147067	Getzlaf et al.	Dec 2006	B2
7150321	Luke et al.	Dec 2006	B2
7174962	Roddy et al.	Feb 2007	B1
7182137	Fyten et al.	Feb 2007	B2
7198104	Griffith et al.	Apr 2007	B2
7199086	Roddy et al.	Apr 2007	B1
7204307	Roddy et al.	Apr 2007	B2
7204310	Roddy et al.	Apr 2007	B1
7213646	Roddy et al.	May 2007	B2
7217441	Bour et al.	May 2007	B2
7219733	Luke et al.	May 2007	B2
7255739	Brothers et al.	Aug 2007	B2
7284609	Roddy et al.	Oct 2007	B2
7284930	Shi et al.	Oct 2007	B2
7285164	Luke et al.	Oct 2007	B2
7285166	Luke et al.	Oct 2007	B2
7293609	Dealy et al.	Nov 2007	B2
7297664	Santra et al.	Nov 2007	B2
7303008	Badalamenti et al.	Dec 2007	B2
7316744	De La Roij et al.	Jan 2008	B2
7325611	Santra et al.	Feb 2008	B2
7335252	Roddy et al.	Feb 2008	B2
7337842	Roddy et al.	Mar 2008	B2
7338923	Roddy et al.	Mar 2008	B2
7341104	Roddy et al.	Mar 2008	B2
7341105	Bingamon et al.	Mar 2008	B2
7350573	Reddy	Apr 2008	B2
7353870	Roddy et al.	Apr 2008	B2
7381263	Roddy et al.	Jun 2008	B2
7387675	Roddy et al.	Jun 2008	B2
7395860	Roddy et al.	Jul 2008	B2
7404855	Chatterji et al.	Jul 2008	B2
7409990	Burts et al.	Aug 2008	B1
7413014	Chatterji et al.	Aug 2008	B2
7442249	Mueller	Oct 2008	B2
7445669	Roddy et al.	Nov 2008	B2
7478675	Roddy et al.	Jan 2009	B2
7527688	Bingamon et al.	May 2009	B2
7544640	Luke et al.	Jun 2009	B2
7607482	Roddy et al.	Oct 2009	B2
7607484	Roddy et al.	Oct 2009	B2
7627870	Michaeli et al.	Dec 2009	B1
7631692	Roddy et al.	Dec 2009	B2
7651563	Datta et al.	Jan 2010	B2
7655088	Bethani	Feb 2010	B2
7658796	Nordmeyer	Feb 2010	B2
7674332	Roddy et al.	Mar 2010	B2
7708071	Roddy et al.	May 2010	B2
7712527	Roddy	May 2010	B2
7740070	Santra et al.	Jun 2010	B2
7741841	Edwards et al.	Jun 2010	B2
7743828	Roddy et al.	Jun 2010	B2
7748454	Roddy et al.	Jul 2010	B2
7757766	Lewis et al.	Jul 2010	B2
7784542	Roddy et al.	Aug 2010	B2
7789150	Roddy et al.	Sep 2010	B2
7815880	Constantz et al.	Oct 2010	B2
7837412	O'Hearn	Nov 2010	B2
7867954	Warrender et al.	Jan 2011	B2
7887694	Constantz et al.	Feb 2011	B2
7919064	Kawatra et al.	Apr 2011	B2
7922809	Constantz et al.	Apr 2011	B1
7927419	Roddy	Apr 2011	B2
7938201	Giroux et al.	May 2011	B2
7939336	Constantz et al.	May 2011	B2
7963323	Bailey	Jun 2011	B2
7993451	Brouillette et al.	Aug 2011	B2
8006446	Constantz et al.	Aug 2011	B2
8029618	Al-Shafei	Oct 2011	B2
8030253	Roddy et al.	Oct 2011	B2
8039253	Asou et al.	Oct 2011	B2
8062999	Reddy et al.	Nov 2011	B2
8143198	Lewis et al.	Mar 2012	B2
8162055	Lewis et al.	Apr 2012	B2
8186457	Boyle	May 2012	B2
8261827	Roddy et al.	Sep 2012	B2
8281859	Roddy et al.	Oct 2012	B2
8297357	Brenneis et al.	Oct 2012	B2
8307899	Brenneis et al.	Nov 2012	B2
8318642	Roddy et al.	Nov 2012	B2
8324137	Roddy et al.	Dec 2012	B2
8327939	Roddy	Dec 2012	B2
8333240	Roddy et al.	Dec 2012	B2
8342242	Roddy et al.	Jan 2013	B2
8360160	Giroux et al.	Jan 2013	B2
8394744	Woytowich et al.	Mar 2013	B2
8399387	Roddy et al.	Mar 2013	B2
8403045	Brenneis	Mar 2013	B2
8434553	Brenneis et al.	May 2013	B2
8440596	Brenneis et al.	May 2013	B2
8470275	Constantz et al.	Jun 2013	B2
8486868	Brenneis et al.	Jul 2013	B2
8486869	Brenneis et al.	Jul 2013	B2
8505629	Benkley et al.	Aug 2013	B2
8505630	Chatterji et al.	Aug 2013	B2
8522873	Benkley	Sep 2013	B2
8540025	Reddy et al.	Sep 2013	B2
8544543	Chatterji et al.	Oct 2013	B2
8551923	Benkley et al.	Oct 2013	B1
8554543	Cherepanov et al.	Oct 2013	B2
8555967	Chatterji et al.	Oct 2013	B2
8586508	Reddy et al.	Nov 2013	B2
8586512	Roddy et al.	Nov 2013	B2
8598093	Roddy et al.	Dec 2013	B2
8603951	Perez	Dec 2013	B2
8609595	Morgan	Dec 2013	B2
8672028	Karcher et al.	Mar 2014	B2
8691737	Chatterji et al.	Apr 2014	B2
20020117090	Ku	Aug 2002	A1
20030116887	Scott	Jun 2003	A1
20040149431	Wylie et al.	Aug 2004	A1
20040187740	Timmons	Sep 2004	A1
20060166834	Roddy	Jul 2006	A1
20070056479	Gray	Mar 2007	A1
20070056732	Roddy et al.	Mar 2007	A1
20070137528	Le Roy-Delage et al.	Jun 2007	A1
20080169130	Norman	Jul 2008	A1
20080229979	Lewis	Sep 2008	A1
20090124522	Roddy et al.	May 2009	A1
20100044057	Dealy et al.	Feb 2010	A1
20100196104	Constantz et al.	Aug 2010	A1
20100258035	Constantz et al.	Oct 2010	A1
20100294496	Woytowich et al.	Nov 2010	A1
20110000400	Roddy	Jan 2011	A1
20120145387	Pyatina et al.	Jun 2012	A1
20120152539	Karcher	Jun 2012	A1
20120227631	Roddy	Sep 2012	A1
20120285682	Santra et al.	Nov 2012	A1
20120318506	Benkley et al.	Dec 2012	A1
20120325476	Brenneis et al.	Dec 2012	A1
20120328377	Brenneis et al.	Dec 2012	A1
20130008352	Roddy et al.	Jan 2013	A1
20130118752	Hannegan et al.	May 2013	A1
20130126159	Bryan et al.	May 2013	A1
20130153214	Roddy et al.	Jun 2013	A1
20130157903	Benkley et al.	Jun 2013	A1
20130210685	Chatterji et al.	Aug 2013	A1
20130213643	Chatterji et al.	Aug 2013	A1
20140048266	Morgan et al.	Feb 2014	A1
20140060389	Chatterji et al.	Mar 2014	A1
20140076204	Brenneis et al.	Mar 2014	A1

Foreign Referenced Citations (37)

Number	Date	Country
2064682	Apr 1992	CA
2336077	Jan 2000	CA
2153372	Jan 2006	CA
2736148	May 2012	CA
0752048	Jan 1997	EP
0814067	Dec 1997	EP
1092693	Apr 2001	EP
1236701	Sep 2002	EP
1394137	Jul 2003	EP
1348831	Oct 2003	EP
1900703	Mar 2008	EP
2075303	Jul 2009	EP
1853680	Apr 2010	EP
1769132	Apr 2011	EP
1469954	Apr 1997	GB
2455446	Jun 2009	GB
WO 8301443	Sep 1982	WO
WO 9321122	Oct 1993	WO
WO 9721637	Jun 1997	WO
WO 9854108	Dec 1998	WO
WO 0063134	Jan 2000	WO
WO 03031364	Apr 2003	WO
WO 2004101951	Nov 2004	WO
WO 2004101952	Nov 2004	WO
WO 2005047212	May 2005	WO
WO 2005061846	Jul 2005	WO
WO 2006032841	Mar 2006	WO
WO 2007028952	Mar 2007	WO
WO 2007041841	Apr 2007	WO
WO 2007048999	May 2007	WO
WO 2007128945	Nov 2007	WO
WO 2009071962	Dec 2007	WO
WO 2006074946	Jun 2009	WO
WO 2009138747	Nov 2009	WO
WO 2010086592	Aug 2010	WO
WO 2011051664	May 2011	WO
WO 2012001343	Jan 2012	WO

Non-Patent Literature Citations (184)

Entry
Hall, “Bridging Effectiveness of Perlite for Light Weight Cements and Lost Circulation”, Petroleum Branch, AIME, Paper No. 141-G, Oct. 1951.
Saunders, “Trend in Use of Low-weight Cement Slurries”, Abstract, Mar. 1952.
Murphy,“A Critique of Filler Cements”, Journal of Petroleum Technology, Aug. 1967.
Sugama, “Carbonation of Hydrothermally Treated Phosphate-Bonded Calcium Aluminate Cements”, pp. 1-9, 1973.
Herndon, “Setting Downhole Plugs: A State-of-the-Art”, Petroleum Engineer International, Apr. 1978.
Morgan, R.G., Suter, D.A., and Sweat, V.A., “Mathematical Analysis of a Simple Back Extrusion Rheometer,” ASAE Paper No. 79/6001, Jun. 24, 1979.
“API Specification for Materials and Testing for Well Cements”, API Spec. 10, 5th ed., pp. 7, 19-21, Jul. 1, 1980.
The Professional Standard of the People's Republic of China, “Rotary Kiln Dust Added to Cement,” ZB Q 12001-84, issued by State Bureau of Building Material Industry, Oct. 25, 1984.
Sersale, “Portland-Zeolite-Cement for Minimizing Alkali-Aggregate Expansion”, 1987.
Smith, “Cementing” Society of Professional Engineers, pp. 14, 38, 1987.
Nelson, “Well Cementing”, 1990.
Smith, “Cementing” Society of Petroleum Engineers, p. 38, 1990.
“Appendix A”, API RP 13B-2, 2d ed.; pp. 6-8, Dec. 1, 1991.
Sugama, “Carbonation of Hydrothermally Treated Phosphate Bonded Calcium Aluminate Cements,” pp, 1-10, 1992.
Vinson, “Acid Removable Cement System Helps Lost Circulation in Productive Zones”, IADC/SPE 23929, Feb. 18, 1992.
Marfil, “Zeolite Crystallization in Portland Cement Concrete Due to Alkali-Aggregate Reaction”, 1993.
Atkins, “Zeolite P in Cements”, “Its Potential for Immobilizing Toxic and Radioactive Waste Species”, 1995.
Janotka, “The Properties of Mortar Using Blends With Portland Cement Clinker, Zeolite Tuff and Gypsum”, 1995.
“Manufacture of supplementary cementitious materials from cement kiln dust”, Mishulovich et al., World Cement Research and Development, p. 116-120, Mar. 1996.
Sugama, “Hot Alkali Carbonation of Sodium Metaphosphate Modified Fly Ash/Calcium Aluminate Blend Hydrothermal Cements”, pp. 1661-1672, Sep. 11, 1996.
Rogers, “Designing a Remedial Acid Treatment for Gulf of Mexico Deepwater Turbidite Sands Containing Zeolite Cement”, 1996.
Janotka, “Effect of Bentonite and Zeolite on Durability of Cement Suspension Under Sulfate Attack”, 1998.
Naiqian, “Study on the Suppression Effect of Natural Zeolite on Expansion of Concrete Due to Alkali-Aggregate Reaction”, 1998.
Chan, Comparative Study of the Initial Surface Absorption and Chloride Diffusion of High Performance Zeolite Silica Fume and PFA concretes, 1999.
Poon, “A Study of the Hydration of Natural Zeolite Blended Cement Pastes”, 1999.
Ding, “Extreme Vertices Design of Concrete With Combined Mineral Admixtures”, 1999.
Feng, “Zeolite Ceramiste Cellular Concrete”, 2000.
Bartlet-Gouedard, “A Non-Conventional Way of Developing Cement Slurry for Geothermal Wells”, 2001.
TXI Material Safety Data Sheet for Pressur-Seal, Oct. 2003.
“Kiln Dusts”, Apr. 14, 2005.
“Beneficial use of Solid Waste in Maine”, Apr. 14, 2005.
“Standards for the Management of Cement Kiln Dust Waste”, Apr. 14, 2005.
“Use of Cement Kiln Dust for the Stabilization of Soils”, R. L. Parsons, et al., Apr. 14, 2005.
“Alkali-activated binders by use of industrial by-products”, Buchwald et al., Cement and concrete Research 35, p. 968-973, 2005.
Answer 3 of 24 Chemical Abstracts on STN “Effect of cement kiln dust substitution on chemical and physical properties and compressive strength of Portland and slag cements”, Adb El-aleem et al. (abstract only), 2005.
Adaska and Taubert, “Beneficial Uses of Cement Kiln Dust”, 2008 IEEE/PCA 50th Cement Industry technical Conference, Miami, Fl, May 19-22, 2008, pp. 1-19, 2008.
“Fly Ash Resource Center-Pozzolan,” available at http://www.rmajko.com/pozzolan.htm, Apr. 20, 2009.
Suyan, “An innovative Material for Severe Lost Circulation Control in Depleted Formations” SPE/IADC 125693, Oct. 2009.
The Schundler Company, “Perlite as an Ultra Fine Filler”, Schundler Product Guide, http://www.schundler.com/filler.htm, 2010.
IP.com Electronic Publication, “Use of Cement Kiln Dust (CKD) in Low Temperature Cementing to Reduce Transition Times”, Sep. 25, 2013.
HES Brochure “SCR-100 Cement Retarder a Valuable Time Saver”, 1994.
HES Brochure “Halad-344 Fluid Loss Additive”, 1998.
HES Brochure “HR-5 Cement Additive”, 1998.
HES Brochure “AQF-2 Foaming Agent”, 1999.
HES Brochure “ThermaLock™ Cement for Corrosive CO2 Environments”, 1999.
HES Brochure “Halad-413 Fluid Loss Additive”, 1999.
HES Brochure “Howco Suds Surfactant”, 1999.
HES Brochure “HR-12 Cement Retarder”, 1999.
HES Brochure “HR-15 Cement Retarder”, 1999.
HES Brochure “HR-25 Cement Retarder”, 1999.
HES Brochure “HR-4 Cement Retarder”, 1999.
HES Brochure “HR-7 Cement Retarder”, 1999.
HES Brochure “Pozmix a Cement Additive”, 1999.
HES Brochure “Pozmix Cement and Pozmix 140”, 1999.
HES Brochure “SCR-100T™ Cement Retarder”, 1999.
HES Brochure “SCR-500L High Temp Retarder”, 2000.
HES Brochure “Halad-23 Fluid Loss Additive”, 2000.
HES Brochure “Thermatek Service”, May 2005.
HES Brochure “Tuned Spacer™ III”, Apr. 2007.
HES Brochure “Cal-Seal 60™ Cement Accelerator”, Aug. 2007.
HES Brochure “Cementing-Perlite Cement Additive”, Aug. 2007.
HES Brochure “Econolite™ Additive for cement Slurries”, Aug. 2007.
HES Brochure “Silicalite™”, Aug. 2007.
HES Brochure “SSA-1™ Strenght-Stabilizing Agent”, Aug. 2007.
HES Brochure “SSA-2™ Coarse Silica Flour”, Aug. 2007.
HES Brochure “WG-17 LXP™ Free-Water Control Agent”, Dec. 2007.
HES Brochure “HR®-601 Cement Retarder”, Jan. 2008.
HES Brochure “Thermatek® RSP Rapid Set Plug Service”, Mar. 2008.
HES Product Data Sheet “Baroid®”, Mar. 25, 2010.
HES Brochure “Enhancer 923™ Cement Agent”, Jun. 2010.
HES Brochure “Enhancer 923™ Agent-Successes from the Field”, Jun. 2010.
HES Brochure “Latex 3000™ Cement Additive”, Jun. 2010.
HES Brochure “Foamer 760™ foamer/Stabilizer”, Aug. 2010.
HES Brochure “Tuned® Spacer IV”, Aug. 2010.
HES Brochure “Tuned® Spacer V”, Dec. 2010.
HES Brochure “D-Air 5000™ Defoamer”, Aug. 2011.
HES Brochure “SA-1015™ Suspending Agent”, Mar. 2012.
HES Brochure “WellLife® III Cementing Service”, Jan. 2012.
HES Brochure “TergoVis1 efficiency fluid”, Apr. 2013.
“3M Scotchlite, Glass Bubbles Floated Product Series Product Information”, 1999.
BASF Technical Bulletin “MetaMax® PA”, Aug. 2007.
Hess Pumice Products Inc., Fact Sheet for “DS-200”, “DS-325”, and “Ultrafine Grout”, Aug. 2007.
LAFARGE MSDS “Cement Kiln Dust”, Mar. 3, 2005.
LAFARGE MSDS “LaFarge Blended Cement (cement)”, Mar. 3, 2005.
LAFARGE brochure “TerraCemTM™”, Aug. 2006.
Office Action from U.S. Appl. No. 11/223,671, Dec. 15, 2005.
Office Action from U.S. Appl. No. 11/271,431, Mar. 6, 2006.
Office Action from U.S. Appl. No. 11/223,671, Mar. 31, 2006.
Office Action from U.S. Appl. No. 11/271,431, May 17, 2006.
Office Action from U.S. Appl. No. 11/271,431 (Advisory Action), Jul. 11, 2006.
Office Action from U.S. Appl. No. 11/416,563, Jul. 21, 2006.
Office Action from U.S. Appl. No. 11/403,032, Jul. 24, 2006.
Office Action from U.S. Appl. No. 11/271,431, Aug. 15, 2006.
Office Action from U.S. Appl. No. 11/440,627, Aug. 21, 2006.
Office Action from U.S. Appl. No. 11/402,741, Oct. 19, 2006.
Office Action from U.S. Appl. No. 11/484,951, Oct. 26, 2006.
Office Action from U.S. Appl. No. 11/484,951, Dec. 21, 2006.
Office Action from U.S. Appl. No. 11/223,703, Jan. 17, 2007.
Office Action from U.S. Appl. No. 11/402,741, Feb. 2, 2007.
Office Action from U.S. Appl. No. 11/223,485, Feb. 28, 2007.
Office Action from U.S. Appl. No. 11/223,669, Feb. 28, 2007.
Office Action from U.S. Appl. No. 11/271,690, Mar. 13, 2007.
Office Action from U.S. Appl. No. 11/402,741, Mar. 22, 2007.
Office Action from U.S. Appl. No. 11/223,703, Apr. 25, 2007.
Office Action from U.S. Appl. No. 11/402,741, May 29, 2007.
Office Action from U.S. Appl. No. 11/223,669, Jun. 18, 2007.
Office Action from U.S. Appl. No. 11/257,261, Aug. 10, 2007.
Office Action from U.S. Appl. No. 11/402,741, Sep. 6, 2007.
Office Action from U.S. Appl. No. 11/223,669, Oct. 9, 2007.
Office Action from U.S. Appl. No. 11/223,750, Oct. 16, 2007.
Office Action from U.S. Appl. No. 11/402,741, Oct. 24, 2007.
Office Action from U.S. Appl. No. 11/223,669, Jan. 29, 2008.
Office Action from U.S. Appl. No. 11/223,669, Apr. 8, 2008.
Office Action from U.S. Appl. No. 12/263,800, May 1, 2009.
Office Action from U.S. Appl. No. 12/283,398, Jul. 15, 2009.
Office Action from U.S. Appl. No. 12/263,800, Jul. 28, 2009.
Office Action from U.S. Appl. No. 12/420,630, Aug. 3, 2009.
Office Action from U.S. Appl. No. 12/349,676, Nov. 4, 2009.
Office Action from U.S. Appl. No. 12/606,381, Mar. 23, 2010.
Office Action from U.S. Appl. No. 12/609,993, Apr. 9, 2010.
Office Action from U.S. Appl. No. 12/609,993, Jun. 15, 2010.
Office Action from U.S. Appl. No. 12/558,097, Jun. 30, 2010.
Notice of Allowance from U.S. Appl. No. 12/609,993, Jul. 26, 2010.
Office Action from U.S. Appl. No. 12/558,097, Sep. 3, 2010.
Office Action from U.S. Appl. No. 12/833,189, Oct. 1, 2010.
Office Action from U.S. Appl. No. 12/844,612, Oct. 1, 2010.
Office Action from U.S. Appl. No. 12/364,998, Jan. 14, 2011.
Office Action from U.S. Appl. No. 12/844,612, Jan. 28, 2011.
Notice of Allowance from U.S. Appl. No. 12/544,915, Aug. 1, 2011.
Office Action from U.S. Appl. No. 12/844,612, Sep. 6, 2011.
Office Action from U.S. Appl. No. 12/264,010, Oct. 31, 2011.
Final Office Action from U.S. Appl. No. 12/844,612, Dec. 23, 2011.
Final Office Action from U.S. Appl. No. 12/264,010, Apr. 10, 2012.
Office Action from U.S. Appl. No. 12/844,612, Apr. 11, 2012.
Office Action from U.S. Appl. No. 13/399,913, May 15, 2012.
Office Action from U.S. Appl. No. 13/447,560, May 31, 2012.
Office Action from U.S. Appl. No. 12/821,412, Jun. 5, 2012.
Office Action from U.S. Appl. No. 12/825,004, Jun. 14, 2012.
Notice of Allowance from U.S. Appl. No. 13/447,560, Jun. 21, 2012.
Office action from U.S. Appl. No. 13/479,476, Jul. 2, 2012.
Office action from U.S. Appl. No. 12/975,196, Jul. 3, 2012.
Final Office Action from U.S. Appl. No. 12/844,612, Jul. 30, 2012.
Notice of Allowance from U.S. Appl. No. 13/399,913, Aug. 23, 2012.
Notice of Allowance from U.S. Appl. No. 13/535,258, Sep. 7, 2012.
Notice of Allowance from U.S. Appl. No. 12/825,004, Sep. 20, 2012.
Office Action from U.S. Appl. No. 13/477,777, Oct. 15, 2012.
Office Action from U.S. Appl. No. 13/560,406, Oct. 17, 2012.
Notice of Allowance from U.S. Appl. No. 12/844,612, Oct. 18, 2012.
Office Action from U.S. Appl. No. 13/555,624, Oct. 19, 2012.
Final Office Action from U.S. Appl. No. 12/975,196, Oct. 23, 2012.
Office Action from U.S. Appl. No. 13/431,701, Nov. 9, 2012.
Office Action from U.S. Appl. No. 13/620,163, Nov. 9, 2012.
Office Action from U.S. Appl. No. 13/606,098, Dec. 13, 2012.
Office Action from U.S. Appl. No. 13/669,149, Dec. 19, 2012.
Office Action from U.S. Appl. No. 13/620,013, Feb. 26, 2013.
Office Action from U.S. Appl. No. 13/725,833, Apr. 10, 2013.
Notice of Allowance from U.S. Appl. No. 13/669,149, May. 13, 2013.
Notice of Allowance form U.S. Appl. No. 13/535,145, May 24, 2013.
Office Action from U.S. Appl. No. 13/620,013, May 28, 2013.
Notice of Allowance from U.S. Appl. No. 12/895,436, May 28, 2013.
Final Office Action from U.S. Appl. No. 13/477,777, May 29, 2013.
Notice of Allowance from U.S. Appl. No. 13/560,406, May 29, 2013.
Office Action from U.S. Appl. No. 13/851,925, Jun. 6, 2013.
Office Action from U.S. Appl. No. 13/889,398, Jun. 20, 2013.
Office Action from U.S. Appl. No. 13/851,391, Jul. 3, 2013.
Office Action from U.S. Appl. No. 13/872,063, Jul. 12, 2013.
Office Action from U.S. Appl. No. 13/767,710, Jul. 19, 2013.
Notice of Allowance from U.S. Appl. No. 13/851,391, Jul. 31, 2013.
Notice of Allowance from U.S. Appl. No. 13/889,398, Aug. 20, 2013.
Final Office Action from U.S. Appl. No. 13/477,777, Sep. 20, 2013.
Office Action from U.S. Appl. No. 13/767,710, Sep. 20, 2013.
Final Office Action from U.S. Appl. No. 13/851,925, Sep. 20, 2013.
Office Action from U.S. Appl. No. 13/180,238, Sep. 25, 2013.
Final Office Action from U.S. Appl. No. 13/620,013, Oct. 2, 2013.
Notice of Allowance from U.S. Appl. No. 13/662,111, Oct. 21, 2013.
Office Action form U.S. Appl. No. 13/955,516, Dec. 19, 2013.
Notice of Allowance from U.S. Appl. No. 13/180,238, Jan. 22, 2014.
Notice of Allowance from U.S. Appl. No. 13/851,925, Jan. 24, 2014.
Office Action from U.S. Appl. No. 13/851,475, Jan. 24, 2014.
Office Action from U.S. Appl. No. 13/620,013, Jan. 30, 2014.
Office Action from U.S. Appl. No. 14/079,421, Jan. 30, 2014.
Office Action from U.S. Appl. No. 14/091,332, Jun. 19, 2014.
U.S. Appl. No. 13/622,821, first named inventor Brenneis et. al., filed Sep. 19, 2012.
USPTO Office Action for U.S. Appl. No. 14/091,332 dated Oct. 27, 2014.

Related Publications (1)

	Number	Date	Country
	20140326446 A1	Nov 2014	US

Divisions (2)

	Number	Date	Country
Parent	14091332	Nov 2013	US
Child	14312253		US
Parent	13725833	Dec 2012	US
Child	13851925		US

Continuation in Parts (5)

	Number	Date	Country
Parent	13851925	Mar 2013	US
Child	14091332		US
Parent	13535145	Jun 2012	US
Child	13725833		US
Parent	12895436	Sep 2010	US
Child	13535145		US
Parent	12264010	Nov 2008	US
Child	12895436		US
Parent	11223669	Sep 2005	US
Child	12264010		US

Placing a fluid comprising kiln dust in a wellbore through a bottom hole assembly

Information

Patent Number

Date Filed

Date Issued

Inventors

Original Assignees

Examiners

Agents

CPC

US Classifications

Field of Search

US

International Classifications

Abstract