Patent Grant
9165689
The present invention relates to a plant operation method and a plant operation system which are suitable for the corrosion suppression of a structural material such as a feed water pipe.
In various plants, each of which is provided with a boiler, a steam generator and the like and uses high-temperature water, including a thermal power plant and a nuclear power plant, there may cause a case where a metal of a structural material is subjected to an aged deterioration phenomenon such as ionic elution and the formation of a corrosion product. Deposition of the corrosion product disturbs a flow channel in a pipe, resulting in a cause of vibration.
Furthermore, the vibration under a high flow-velocity condition may cause a crack or damage in the structural material, and in addition, when the corrosion product deposits on a heat transfer surface in the steam generator of a pressurized-water nuclear power plant, a feed water heater or the like of a boiling-water reactor power plant or a thermal power plant, the corrosion product may cause the decrease of the heat transfer coefficient.
In such steam generator and feed water heater, an impurity concentration in feed water is kept at low concentration by continuous blow water in the apparatus, but in a narrow portion such as a crevice portion between a heat transfer pipe and a support plate, water quality occasionally differs from a controlled value, which may result in that the impurities are concentrated in the narrow portion, a corrosive environment is created in the portion, and it may also be assumed that a scale (oxide) or the like deposits therein. In addition, even in the piping in a pipeline having an orifice, a valve or the like, a liquid passes through the inner space at a high speed, and accordingly, in such case, it is necessary to take measures against erosion, corrosion, flow-accelerated-type corrosion and the like.
These are representative phenomena occurring in high-temperature water environment, and exert various influences such as a problem on an operation caused by corrosion and increase of maintenance frequency on the piping and other members including the structural material. In addition, in recent years, such a phenomenon occurs in a carbon steel pipe that the thickness of the pipe decreases due to a wall-thinning phenomenon. Thus, the elution, the corrosion phenomenon and the like of metal are gradually accumulated during a plant operation in a long period of time, and potentially show a possibility of suddenly erupting into a disaster at some point.
In any power plant, in a pipeline on a downstream side of a condenser, iron and the like elute, and in a pipe disposed downstream side of a deaerator, the temperature rises and a condition of causing the flow-accelerated-type corrosion is formed. Because of this reason, the suppression of these phenomena leads to the enhancement of the soundness and the operation period of equipment. The method of suppressing the above descried phenomenon includes injecting a chemical agent having a corrosion-suppressing effect into the system to impart a quality of causing little corrosion to the water, for example, in the thermal power plant, the PWR power plant and the like.
For example, in a secondary system of the thermal power plant or the pressurized-water-type nuclear power plant, pH control or water quality control has been performed by injecting ammonia for reducing the elution of iron from the inside of the system and preventing the inflow of the iron to the steam generator. Furthermore, in order to eliminate the alkali concentration of the crevice portion in the steam generator, various water quality controls are implemented in an actual plant, such as an Na/Cl ratio control and a chloride ion concentration control for reducing an influence of a chlorine ion on corrosion. In recent years, the water-quality control method has been adopted by using improved chemicals such as ethanolamine and morpholine.
As for the improvement of chemicals to be injected, there is provided a method of utilizing an organic acid such as tannic acid and ascorbic acid as an oxygen scavenger (for example, as disclosed in Japanese Patent Laid-Open Publication No. 4-26784: Patent Document 1). In addition, as for the water-quality control method, there are proposed an operation method of controlling a molar ratio of all cations/SO4, a method of introducing at least one of a calcium compound and a magnesium compound into feed water to a steam generator for a nuclear reactor so that the ion concentration becomes 0.4 to 0.8 ppb (for example, as disclosed in Japanese Patent Laid-Open Publication No. 2004-12162: Patent Document 2), and the like. In addition, a technology for injecting a precious metal for protecting a material and injecting oxygen is also proposed (for example, as disclosed in Japanese Patent Laid-Open Publication No. 10-339793: Patent Document 3).
However, the methods of controlling the water quality proposed in the Patent Documents 1 and 2 inject the chemical agent into the feed water of the pressurized-water-type nuclear power plant, and accordingly, this technology may apply an influence upon the purity of the feed water, the environment and the like.
Furthermore, although the method of controlling the water quality disclosed in the Patent Document 3 shows clear criteria for the injection of the precious metal such as platinum (Pt) and ruthenium (Ru), there is no disclosure concerning a necessary injection amount and an injection method for a metal compound such as titanium oxide (TiO2).
The present invention was conceived in consideration of the above circumstances, and an object of the present invention is to provide a plant operation method and a plant operation system, which can surely suppress the corrosion of a structural material such as a pipe or piping without injecting such a chemical agent as to exert an influence upon an environment therearound.
The above object of the present invention can be achieved by providing an operation method of any one of plants including: a secondary system of a pressurized-water-type nuclear power plant, which has at least a low-pressure feed water heater and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a steam generator from a condenser or further has a deaerator arranged between the low-pressure feed water heater and the high-pressure feed water heater, and leads high-temperature feed water to the steam generator; a primary system of a boiling-water-type nuclear power plant, which has a low-pressure feed water heater and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a pressure vessel from a condenser, and leads high-temperature feed water to the pressure vessel; and a feed water system of a thermal power plant which has at least a low-pressure feed water heater and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a boiler from a condenser, or further has a deaerator arranged between the low-pressure feed water heater and the high-pressure feed water heater, and leads high-temperature feed water to the pressure reaction vessel, wherein a film, for suppressing an elution of an element constituting a structural material such as the feed water pipe, the low-pressure feed water heater, the deaerator and the high-pressure feed water heater which come in contact with the high-temperature feed water, is formed on a surface of the structural material; and a corrosion suppression substance is deposited on the surface of the structural material in which the corrosion accelerated by a flow of the feed water occurs.
In addition, the above described object of the present invention is attained by providing, a secondary operation system of a pressurized-water type nuclear power plant which has a low-pressure feed water heater, a deaerator and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a steam generator from a condenser, and leads high-temperature feed water to the steam generator, wherein the plant operation system comprises: an oxidant injection unit which is provided in a downstream side of the condenser and in an upstream side of the low-pressure feed water heater in the feed water pipe, and injects an oxidant for forming a film that suppresses an elution of an element constituting a structural material such as the feed water pipe, the low-pressure feed water heater, the deaerator and the high-pressure feed water heater, which come in contact with the high-temperature feed water, onto a surface of the structural material; and a corrosion suppression substance introduction unit which is provided in a downstream side of the deaerator and in an upstream side of the high-pressure feed water heater in the feed water pipe, and introduces a corrosion suppression substance so as to deposit the corrosion suppression substance on the surface of the structural material in which corrosion accelerated by a flow of the feed water occurs.
Furthermore, the above described object of the present invention is attained by providing an operation system of a boiling-water-type nuclear power plant which has a low-pressure feed water heater and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a pressure reaction vessel from a condenser, and leads high-temperature feed water to the steam generator, or a thermal power plant which has a low-pressure feed water heater and a high-pressure feed water heater sequentially arranged in a feed water pipe reaching a boiler from a condenser, and leads high-temperature feed water to the boiler, wherein the operation system of the plant includes an injection unit which is provided in a downstream side of the condenser and in an upstream side of the low-pressure feed water heater in the feed water pipe, and injects an oxidant for forming a film which suppresses an elution of an element constituting a structural material such as the feed water pipe, the low-pressure feed water heater and the high-pressure feed water heater, which come in contact with high-temperature feed water, onto a surface of the structural material, or injects a corrosion suppression substance for depositing the corrosion suppression substance onto the surface of the structural material.
According to the plant operation method and the plant operation system of the present invention, a film for suppressing the elution of the element constituting the structural material is formed and the corrosion suppression substance is deposited on the surface of the structural material in which a flow-accelerated-type corrosion occurs, and the corrosion of the structural material such as the pipe can be thereby surely suppressed without injecting such a chemical agent as to exert an influence upon the environment and the like.
Best modes or embodiments for carrying out the present invention will be described hereunder with reference to the drawings. It is however to be noted that the present invention is not limited to these modes or embodiments.
As is illustrated in this
The temperature of the feed water flowing in the inside of the feed water pipe 18 reaching the steam generator 13 from the condenser 17 is 15° C. or higher and 350° C. or lower. For example, the temperature of the feed water passing to the low-pressure feed water heater 20 from the condenser 17 is approximately 40° C. to 180° C., and the temperature of the feed water passing to the high-pressure feed water heater 22 from the deaerator 21 is approximately 180° C. to 230° C. The flow velocity of the feed water flowing in the inside of the feed water pipe 18 which reaches the steam generator 13 from the condenser 17 is in the range of 1 m/sec. or more and 20 m/sec. or less.
A structural material of various equipments and pipes constituting this secondary system 12, particularly, the feed water pipe 18, the condensate pump 19, the low-pressure feed water heater 20, the deaerator 21 and the high-pressure feed water heater 22, which come in contact with high-temperature feed water are formed of a material of steel such as stainless steel, a non-ferrous material such as a nickel-based alloy or a non-ferrous metal such as copper and aluminum.
In the secondary system 12, an oxidant injection line 23 working as an oxidant injection unit is installed at a position in a downstream side of the condenser 17 and in an upstream side of the low-pressure feed water heater 20 in the feed water pipe 18, for example, in the vicinity of a downstream side of the condensate pump 19. Oxygen (gaseous state), hydrogen peroxide (liquid state) and ozone (gaseous state) are injected singularly or in a mixed state as an oxidant from the oxidant injection line 23. In the present embodiment, oxygen in a gaseous state is injected into the feed water in the feed water pipe 18 from the oxidant injection line 23. In order to facilitate the oxygen to be dissolved into the feed water, the bubble of the oxygen is fined to thereby enable the amount of dissolved oxygen to increase. For example, a nano-bubble is preferable.
By the injection of this oxidant (oxygen, for example), the dissolved oxygen concentration of water qualities of the feed water rises, and an oxide film, which suppresses the elution of elements constituting the structural material, for example, iron, chromium and the like, is formed on the surface to come in contact with feed water of the structural material such as the feed water pipe 18.
Herein, a result of a test on the effect of suppressing an elution of an element (iron, for example) constituting the structural material due to the oxide film will be described below with reference to
In this test, in order to produce the oxide film on the surface of the carbon steel, a test piece was produced by exposing a carbon steel in high-temperature (40 to 180° C., for example) water having a dissolved oxygen concentration of 200 ppb for 500 hours. The test of iron elution was conducted by using the produced test piece and a test piece of only the carbon steel. The test was conducted on a test condition of immersing both of the test pieces in an aqueous solution in which the dissolved oxygen concentration was adjusted to less than 5 ppb and the pH was adjusted to 9 to 10 by ammonia.
As for the test piece of only the carbon steel having no oxide film thereon, iron eluted and the color of the solution changed. On the other hand, as for the test piece of the carbon steel provided with the oxide film thereon, the color hardly changed, and the surface state also did not show a change. Thus, the elution of the iron is suppressed and the amount of the iron to be introduced into the steam generator 13 is reduced, by the existence of the stable oxide film.
Furthermore, in a secondary system 12 of this pressurized-water-type nuclear power plant, a corrosion suppression substance introduction line 24 working as a corrosion suppression substance introduction unit is installed at a position in a downstream side of the deaerator 21 and in an upstream side of the high-pressure feed water heater 22 in the feed water pipe 18. The corrosion suppression substance is, for example, an oxide or a hydroxide containing one or more elements selected from titanium (Ti), zirconium (Zr), cerium (Ce), niobium (Nb), lanthanum (La), neodymium (Nd) and yttrium (Y). The corrosion suppression substance is specifically titanium oxide (TiO2), zirconium oxide (ZrO2), cerium oxide (CeO2), niobium oxide (Nb2O5), lanthanum trioxide (La2O3), oxidization neodymium (Nd2O3), yttrium oxide (Y2O3), hydroxylation cerium (Ce(OH)4), lanthanum hydroxide (La(OH)3), hydroxylation yttrium (Y(OH)3) or the like. Among these corrosion suppression substances, the titanium oxide may be more preferable.
The structural material including the feed water pipe 18 and the high-pressure feed water heater 22 in a downstream side of the deaerator 21 comes in contact with the feed water of high temperature and is in a region in which the corrosion (flow-accelerated-type corrosion) accelerated by a flow of the feed water occurs. It becomes possible to deposit the corrosion suppression substance including the titanium oxide on the surface of the structural material, in which the flow-accelerated-type corrosion occurs, by introducing the corrosion suppression substance including the titanium oxide from the corrosion suppression substance introduction line 24.
Further, in a case where no deaerator 21 is disposed, the corrosion suppression substance introduction line 24 can be installed at a position in a downstream side of the condenser 17 and in an upstream side of the low-pressure feed water heater 20, and accordingly, can be united with the oxidant injection line 23 to form the same line.
This corrosion suppression substance is in a colloidal state or slurry state of a solution containing fine particles, and the fine particles are deposited on the surface of the structural material such as the feed water pipe 18 by injecting this solution into the feed water or are deposited on the surface of the structural material by a spraying or thermal spraying technique. In the present embodiment, particularly, the titanium oxide solution is injected into the feed water. It is preferable to deposit 5 μg/cm2 or more of the corrosion suppression substance including the titanium oxide on the surface of the structural material.
When the corrosion suppression substance including the titanium oxide is injected into the feed water, the amount of the corrosion suppression substance to be deposited on the structural material is controlled by selecting the concentration of the solution containing the corrosion suppression substance, adjusting the amount of the solution to be injected, and further considering the water quality (dissolved oxygen concentration, for example) of the feed water into which the solution has been injected.
When the corrosion suppression substance including the titanium oxide is deposited on the surface of the structural material under high temperature and high pressure, the corrosion suppression substance shows a catalytic action of promoting the oxidation reaction of water in place of the elution (specifically, oxidation reaction of iron, chromium and the like) of elements (iron, chromium and the like, for example) constituting the structural material, thereby suppresses the elution of the elements constituting the structural material including the iron, the chromium and the like, and also prevents the exfoliation of the above described oxide film which has been deposited on the surface of the structural material.
Although this corrosion suppression substance including the titanium oxide preferably should cover the whole surface which comes in contact with the feed water in the structural material including the feed water pipe 18, it is not necessarily need to cover the above described whole surface because the corrosion suppression substance has a function as a catalyst.
Herein, the test result (
On the other hand, as for the test piece of the carbon steel having the titanium oxide deposited thereon, the corrosion rate is reduced, and the dependency with respect to the temperature becomes small. The test piece of the carbon steel having the titanium oxide deposited thereon shows the effect of suppressing the corrosion in a low-temperature region and in a high-temperature region, and shows the effect for a pipe having a temperature gradient, for example. From the above results, it is found that at least the titanium oxide can provide the effect of suppressing the corrosion for the whole of the secondary system 12 of the pressurized-water type nuclear power plant.
Furthermore, a result of a corrosion suppression test about a corrosion suppression substance other than the titanium oxide is shown in
On the other hand, in the secondary system 12 of the pressurized-water-type nuclear power plant, each of the above described substances (particularly, yttrium, cerium and lanthanum) is injected in a state of hydroxide and is deposited on the carbon steel, and an oxidant such as oxygen is injected from the oxidant injection line 23 while this secondary system 12 is operated. According to such injection, the deposited hydroxide is oxidized by the oxidant and is formed as an oxide. Further, the corrosion suppression effect becomes higher by depositing the corrosion suppression substance on the surface of the structural material such as the feed water pipe 18 in a state having a high adhesive property such as hydroxide and by oxidizing the corrosion suppression substance.
In the secondary system 12 of the pressurized-water-type nuclear power plant, a downstream side of the deaerator 21 is in a state of a higher temperature than that in an upstream side thereof, is in a region in which the flow-accelerated-type corrosion occurs as described above, and is in the environment in which the oxide film resists being formed.
Then, an oxidant such as oxygen is injected into the feed water in a structural material including the feed water pipe 18 in a downstream side of this deaerator 21 from the oxidant injection line 23 so that the dissolved oxygen concentration in the feed water becomes 5 ppb or more. According to such injection of the oxidant, it becomes possible to surely form an oxide film on the surface which comes in contact with the feed water of the structural material in a downstream side of the deaerator 21 and to deposit a corrosion suppression substance (titanium oxide, for example) injected from the corrosion suppression substance introduction line 24 on this oxide film. Thus, the corrosion suppression effect for the structural material increases, and accordingly, the amount of the corrosion suppression substance depositing on the surface of the structural material does not necessarily need to be 5 μg/cm2 or more.
Accordingly, the present embodiment attains the following effects. Specifically, the present embodiment can surely suppress corrosion phenomena such as the flow-accelerated-type corrosion, corrosion caused by the difference of partial environments and uniform corrosion which are a concern in the secondary system 12 of the pressurized-water-type nuclear power plant, by forming an oxide film for suppressing an elution of an element constituting the structural material such as the feed water pipe 18, and depositing a corrosion suppression substance (titanium oxide, for example) on the surface of the structural material in which the flow-accelerated-type corrosion occurs. On this occasion, it is not necessary to inject a chemical agent like amines such as ammonia and hydrazine that is a powerful drug, which exerts an influence on the environment into the feed water.
As a result of thus suppressing the corrosion of the structural material such as the feed water pipe 18, the present embodiment can reduce the amount of elements which have eluted from the structural material and flow into the steam generator 13 to thereby suppress the deposition of scale and crud onto the steam generator 13. Accordingly, the present embodiment can reduce the necessary number of works for removing the scale and the crud in the steam generator 13, and can reduce costs for operation, maintenance and the like.
A point in the present embodiment different from the first embodiment resides in injection of hydrogen into feed water, in addition to the injection of an oxidant such as oxygen from the oxidant injection line 23 into the feed water flowing through the structural material such as the feed water pipe 18, and deposition of a corrosion suppression substance such as titanium oxide injected from the corrosion suppression substance introducing line 24 on the surface to come in contact with the feed water of the structural material.
The hydrogen may be injected into the same position as the oxidant injection line 23 or the corrosion suppression substance introducing line 24 in the feed water pipe 18, or may also be injected into another position than the oxidant injection line 23 and the corrosion suppression substance introducing line 24. The hydrogen is preferably injected into the same position as the corrosion suppression substance introducing line 24 or into the vicinity thereof.
The hydrogen which has been dissolved in the feed water is oxidized by a catalytic action of the corrosion suppression substance such as titanium oxide, and suppresses the elution (in other words, oxidation reaction) of elements (iron, chromium and the like) constituting the structural material such as the feed water pipe 18. This oxidation reaction of hydrogen can suppress the elution of the element constituting the structural material by a smaller deposition amount of the corrosion suppression substance than that in the case of the above described reaction of oxidizing water in the first embodiment.
As is shown in
Thus, even when the deposition amount of the corrosion suppression substance such as titanium oxide is reduced, the effect of suppressing the corrosion of the structural material is developed by the injection of hydrogen. For example, by injecting hydrogen into the feed water so that the dissolved hydrogen concentration of the feed water is 1 ppb or more (approximately 10 ppb, for example), the corrosion suppression effect can be sufficiently developed, even when the deposition amount of the corrosion suppression substance such as titanium oxide is controlled to 5 μg/cm2 or less.
Accordingly, the present embodiment attains the following effects in addition to the same effect as that attained by the first embodiment. Specifically, the deposition amount of the corrosion suppression substance such as titanium oxide necessary for suppressing the corrosion of the structural material such as the feed water pipe 18 can be decreased by injecting hydrogen into the feed water.
The third embodiment differs from the first embodiment in a point of monitoring the corrosion potential of the surface to come in contact with the feed water of the structural material, for example, of the feed water pipe 18, to thereby control the amount of an oxidant such as oxygen to be injected into the feed water from the oxidant injection line 23.
In the secondary system 12 of the pressurized-water-type nuclear power plant illustrated in
Accordingly, the present embodiment attains the following effects, in addition to an effect similar to that in the first embodiment. Specifically, by monitoring the corrosion potential of the surface of the structural material such as the feed water pipe 18 and controlling the amount of the oxidant to be injected into the feed water, the amount of the oxidant to be used can be reduced and the operation cost can be reduced.
As is illustrated in this
The condensed water discharged from the condenser 31 becomes feed water, is heated by the low-pressure feed water heater 34 and the high-pressure feed water heater 35 to become a high-temperature state, and is introduced into the pressure vessel 27.
The temperature of the feed water flowing in the inside of the feed water pipe 32 which reaches the pressure vessel 27 from the condenser 31 is 15° C. or higher and 320° C. or lower. Furthermore, the flow velocity of the feed water flowing in the inside of the feed water pipe 32 which reaches the pressure vessel 27 from the condenser 31 is in the range of 1 m/sec or more and 20 m/sec or less.
A structural material composing various equipments and pipes constituting this boiling-water-type nuclear power plant 26, particularly, the feed water pipe 32, the condensate pump 33, the low-pressure feed water heater 34, and the high-pressure feed water heater 35, which come in contact with high-temperature feed water, are composed from a material of steel such as stainless steel, a non-ferrous material such as a nickel-based alloy or a non-ferrous metal such as copper and aluminum.
As was described above, the boiling-water-type nuclear power plant satisfies a condition that the present invention can be applied thereto, similarly to the secondary system of the pressurized-water-type nuclear power plant. Accordingly, by installing an oxidant injection line 36 working as an oxidant injection unit at a position in a downstream side of the condenser 31 and in an upstream side of the low-pressure feed water heater 34 in the feed water pipe 32, for example, in the vicinity of a downstream side of the condensate pump 33, and injecting an oxidant (oxygen, for example) into the feed water from the oxidant injection line 36, similarly to that in the operation method of the secondary system of the pressurized-water-type nuclear power plant shown in the first embodiment, the dissolved oxygen concentration among the water qualities of the feed water rises, and the oxide film which suppresses the elution of an element constituting this structural material, for example, iron, chromium or the like, is formed on the surface to come in contact with the feed water of the structural material such as the feed water pipe 32.
At the same time, in this boiling-water type nuclear power plant 26, a corrosion suppression substance introduction line 37 working as a corrosion suppression substance introduction unit is installed at a position in a downstream side of the condenser 31 and in an upstream side of the low-pressure feed water heater 34 in the feed water pipe 32, for example, in the vicinity of a downstream side of the condensate pump 33. Further, although the above described oxidant injection line 36 and the corrosion suppression substance introduction line 37 do not need to be individually installed, the oxidant injection line 36 may also be composed of the same injection line.
The structural material including the feed water pipe 32 in a downstream side of the low-pressure feed water heater 34, the low-pressure feed water heater 34 and the high-pressure feed water heater 35 is a region in which the corrosion (flow-accelerated-type corrosion) accelerated by a flow of the feed water occurs.
It becomes possible to deposit the corrosion suppression substance including the titanium oxide on the surface of the structural material in which the flow-accelerated-type corrosion occurs, by introducing the corrosion suppression substance including the titanium oxide into the feed water from the corrosion suppression substance introduction line 37.
When the corrosion suppression substance including the titanium oxide is deposited on the surface of the structural material under high temperature and high pressure, the corrosion suppression substance achieves a catalytic action of promoting the oxidation reaction of water in place of the elution (specifically, oxidation reaction of iron, chromium and the like) of elements (iron, chromium and the like, for example) constituting the structural material, thereby suppressing the elution of the elements constituting structural material including the iron and the chromium and preventing the exfoliation of the above described oxide film which has been deposited on the surface of the structural material.
Furthermore, similarly to the second embodiment to be conducted in the secondary system 12 of the pressurized-water-type nuclear power plant, it becomes possible to suppress the elution of the element constituting the structural material, by injecting hydrogen into the feed water from the corrosion suppression substance introduction line 37, in addition to the deposition of the corrosion suppression substance such as titanium oxide injected from the corrosion suppression substance introduction line 37 on the surface of the structural material.
Furthermore, similarly to the third embodiment to be conducted in the secondary system 12 of the pressurized-water-type nuclear power plant, it is possible to reduce the amount of a used oxidant and reduce the operation cost, in addition to depositing the corrosion suppression substance such as titanium oxide injected from the corrosion suppression substance introduction line 37 on the surface of the feed water pipe 32 and the like, by injecting the oxidant into the feed water from the oxidant injection line 36 to form the oxide film on the surface of the structural material to come in contact with the feed water and controlling the amount of the oxidant to be injected by using a corrosion potentiometer 38 which measures the change of the corrosion potential of the surface of the feed water pipe 32 and the like.
As is illustrated in this
The temperature of the feed water flowing in the inside of the feed water pipe 46 which reaches the boiler 40 from the condenser 45 is 15° C. or higher and 320° C. or lower. Furthermore, the flow velocity of the feed water flowing in the inside of the feed water pipe 46 which reaches the boiler 40 from the condenser 45 is in the range of 1 m/sec or more and 20 m/sec or less.
A structural material of various equipments and pipes constituting this thermal power plant 39, particularly, the feed water pipe 46, the condensate pump 47, the low-pressure feed water heater 48, the deaerator 49 and the high-pressure feed water heater 50, which come in contact with high-temperature feed water, are composed from a material of steel such as stainless steel, a non-ferrous material such as a nickel-based alloy or a non-ferrous metal such as copper and aluminum.
As described above, since the thermal power plant satisfies a condition for being applied to the present invention, similarly to the secondary system of the pressurized-water-type nuclear power plant. Accordingly, by installing an oxidant injection line 51 working as an oxidant injection unit at a position in a downstream side of the condenser 45 and in an upstream side of the low-pressure feed water heater 48 in the feed water pipe 46, for example, in the vicinity of a downstream side of the condensate pump 47, and injecting an oxidant (oxygen, for example) into the feed water from the oxidant injection line 51, similarly to that in the operation method of the secondary system of the pressurized-water-type nuclear power plant shown in the first embodiment, the dissolved oxygen concentration among the water qualities of the feed water rises, and the oxide film which suppresses the elution of an element constituting this structural material, for example, iron, chromium or the like is formed on the surface to come in contact with the feed water of the structural material such as the feed water pipe 46.
At the same time, in this thermal power plant 39, a corrosion suppression substance introduction line 52 working as a corrosion suppression substance introduction unit is installed at a position in a downstream side of the deaerator 49 and in an upstream side of the high-pressure feed water heater 50 in the feed water pipe 46.
The structural material including the feed water pipe 46 and the high-pressure feed water heater 50 in a downstream side of the deaerator 49 is in a region in which the corrosion (flow-accelerated-type corrosion) accelerated by a flow of the feed water occurs. It becomes possible to deposit the corrosion suppression substance including titanium oxide on the surface of the structural material in which the flow-accelerated-type corrosion occurs, by introducing the corrosion suppression substance including the titanium oxide into the feed water from the corrosion suppression substance introduction line 52. In an arrangement of including no deaerator 49, the corrosion suppression substance introduction line 52 can be installed at a position in a downstream side of the condenser 45 and in an upstream side of the low-pressure feed water heater 48, thus being united with the oxidant injection line 51 to form the same line.
When the corrosion suppression substance including the titanium oxide is deposited on the surface of the structural material under high temperature and high pressure, and the corrosion suppression substance achieves a catalytic action of promoting the oxidation reaction of water in place of the elution (specifically, oxidation reaction of iron, chromium and the like) of elements (iron, chromium and the like, for example) constituting the structural material, the elution of the elements constituting the structural material including the iron, the chromium and the like can be suppressed and the exfoliation of the above described oxide film which has been deposited on the surface of the structural material can be prevented.
Furthermore, similarly to the second embodiment to be conducted in the secondary system 12 of the pressurized-water-type nuclear power plant, it becomes possible to suppress the elution of the element constituting the structural material, by injecting hydrogen into the feed water from the corrosion suppression substance introduction line 52, in addition to depositing the corrosion suppression substance such as titanium oxide injected from the corrosion suppression substance introduction line 52 on the surface of the structural material.
Moreover, similarly to the third embodiment to be conducted in the secondary system 12 of the pressurized-water type nuclear power plant, it is possible to reduce the amount of a used oxidant and reduce the operation cost, by injecting the oxidant into the feed water from the oxidant injection line 51 to form an oxide film on the surface of the structural material to come in contact with the feed water, and controlling the amount of an oxidant to be injected by using a corrosion potentiometer 53 which measures the change of the corrosion potential of the surface of the feed water pipe 46, in addition to depositing the corrosion suppression substance such as titanium oxide injected from the corrosion suppression substance introduction line 52 on the surface of the feed water pipe.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2009-027570 | Feb 2009 | JP | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/JP2010/051772 | 2/8/2010 | WO | 00 | 11/4/2011 |
| Publishing Document | Publishing Date | Country | Kind |
|---|---|---|---|
| WO2010/090307 | 8/12/2010 | WO | A |
| Number | Name | Date | Kind |
|---|---|---|---|
| 4842812 | Panson et al. | Jun 1989 | A |
| 5015436 | Nagase et al. | May 1991 | A |
| 7449101 | Okamura et al. | Nov 2008 | B2 |
| 8900670 | Singh et al. | Dec 2014 | B2 |
| 20020122526 | Hidaka et al. | Sep 2002 | A1 |
| 20030180180 | Okamura et al. | Sep 2003 | A1 |
| 20060050833 | Ichikawa et al. | Mar 2006 | A1 |
| 20060146975 | Okamura et al. | Jul 2006 | A1 |
| 20140242299 | Okamura et al. | Aug 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 54 101734 | Aug 1979 | JP |
| 10 339793 | Dec 1998 | JP |
| 2002 71883 | Mar 2002 | JP |
| 2003 232886 | Aug 2003 | JP |
| 2004 20411 | Jan 2004 | JP |
| 2005 195346 | Jul 2005 | JP |
| 2005-291815 | Oct 2005 | JP |
| 2006 38811 | Feb 2006 | JP |
| Entry |
|---|
| Christopher J. Wood, Recent Developments in LWR Radiation Field Control, Progress in Nuclear Energy, vol. 19, No. 3, pp. 241-266, 1987. |
| Machine Translation of JP2004-20411 A, Toshiba Corp., Jan. 22, 2004. |
| Machine Translation of JP10-339793A, Toshiba Corp., Dec. 22, 1998. |
| Korean Office Action issued Jan. 29, 2014 in Patent Application No. 10-2011-7018497. |
| International Search Report Issued Mar. 16, 2010 in PCT/JP10/051772 filed Feb. 8, 2010. |
| Supplementary European Search Report Issued Dec. 5, 2012 in Patent Application No. 10 73 8635.1. |
| International Preliminary Report on Patentability and Written Opinion issued Sep. 13, 2011 in patent application No. PCT/JP2010/051772 filed Feb. 8, 2010. |
| Number | Date | Country | |
|---|---|---|---|
| 20120039429 A1 | Feb 2012 | US |