Patent Application
20190126330
The present invention relates to a plasma melting method for melt-processing materials to be processed, such as general wastes, industrial wastes and incineration ashes produced during incineration of such wastes, as well as to a plasma melting furnace for use in such a method.
Incineration ashes produced when general wastes and industrial wastes are incinerated below 900° C. contain toxic substances such as PCB, dioxins, lead and cadmium. Among other means to process such toxic substances, incinerators that operate using common fuels are incapable of processing these toxic substances.
As a means to process incineration ashes, a technique using an electric resistance furnace for melt-processing has been proposed. In particular, JP 2002-254052A discloses one such technique for melt-processing incineration ash. In this technique, a gas drawn out from within a hermetic electric resistance melting furnace is subjected to a dust collection process. The processed gas is circulated back into the melting furnace. While the dust collection process of the furnace gas is repeated, incineration ashes are charged into the melting furnace where they are melted. The resulting exhaust gas discharged from the melting furnace is then introduced into an exhaust gas-processing unit.
Thermal plasma is used as a means to process general industrial wastes, such as melt-processing of incineration ashes. Use of thermal plasma can insolubilize incineration ashes discharged from garbage incinerators and heavy metals present in the incineration ashes and can decompose dioxins to make them harmless. In 1994, an experimental furnace was installed in Matsuyama in a plant for melt-processing incineration ashes using thermal plasma.
In the conventional technique for melt-processing incineration ashes using a conventional electric resistance furnace, however, the heat source is located at the bottom of the furnace, which leads to an increased amount of time required for heat transfer to the top of the incineration ashes that have a low bulk density and low heat conductance. This makes the melt-processing process time-consuming.
Also, the conventional thermal plasma technique for processing incineration ashes requires high voltage operation in order to generate plasma. During this process, the incinerator ash in the incinerator is agitated and emits undesired dust and gaseous components that can diffuse out from the furnace to contaminate work environments.
Accordingly, it is the objective of the present invention to provide a plasma melting method for processing materials to be processed and a plasma melting furnace for use in the method, that enables efficient melt-processing of the materials to be processed, such as general wastes, industrial wastes and incineration ashes, by generating plasma in the upper portion of the furnace at a low voltage. In this manner, the present invention addresses problems associated with the conventional techniques.
In order to address the above-described problems, one plasma melting method according to the present invention for processing a material to be processed is characterized by including providing a plasma electric melting furnace having a metal layer disposed at the bottom of the furnace and a plurality of electrodes vertically movable by an electrode elevator; initially placing coke at the bottom of the furnace; charging a part of a material to be processed that is at least one of a general waste, an industrial waste and an incinerating ash, over the coke; initiating power supply at a low voltage with lower ends of the electrodes positioned near the bottom of the furnace; lifting upwards the lower ends of the electrodes while the power is stabilized; charging an additional amount of the material to be processed; and applying an operational voltage higher than the low voltage applied during the stable power supply to cause plasma generation below the electrodes and to thereby melt-process the material to be processed.
In one embodiment, the plasma melting method according to the present invention for processing a material to be processed is characterized in that the low voltage applied during the stable power supply is 70 V and the operational voltage is in a range of 100 to 200 V.
In one embodiment, the plasma melting method according to the present invention for processing a material to be processed is characterized in that a manganese ion source is added to the material to be processed that is charged during application of the operational voltage.
In a further aspect, a plasma electric melting furnace according to the present invention for processing a material to be processed is characterized by including a metal layer disposed on the bottom of the furnace; a plurality of graphite electrodes vertically movable by an electrode elevator; a power source; and an electrode power controller in electrical communication with the power source to control the current and voltage of the power supplied to the plurality of the graphite electrodes.
According to the method of the present invention, which includes providing a plasma electric melting furnace having a metal layer disposed at the bottom of the furnace and a plurality of electrodes vertically movable by an electrode elevator; initially placing coke at the bottom of the furnace; charging a part of a material to be processed that is at least one of a general waste, an industrial waste and an incinerating ash, over the coke; initiating power supply at a low voltage with lower ends of the electrodes positioned near the bottom of the furnace; lifting upwards the lower ends of the electrodes while the power is stabilized; charging an additional amount of the material to be processed; and applying an operational voltage higher than the low voltage applied during the stable power supply to cause plasma generation below the electrodes and to thereby melt-process the material to be processed, the voltage applied to the electrodes positioned near the bottom of the furnace during the stable power phase can be made sufficiently low to prevent the generation of submerged plasma, which would otherwise damage the bottom of the furnace. Subsequently, the electrodes are lifted upwards such that stable plasma is generated at the lower ends of the electrodes upon application of the operational voltage. As a result, effective melt-processing of the materials to be processed is achieved.
According to one embodiment of the present invention, in which the low voltage applied during the stable power supply is 70 V and the operational voltage is in a range of 100 to 200 V, the plasma generation during the sable power phase can be minimized to prevent damage to the bottom of the furnace. In addition, the material to be processed can be prevented from being agitated during application of the operational voltage. As a result, stable plasma generation and, thus, effective melt-processing of incineration ashes are achieved.
According to one embodiment of the present invention, in which a manganese ion source is added to the material to be processed that is charged, permanent plasma can be generated in the upper portion of the furnace.
According to one embodiment of the present invention, which comprises a metal layer disposed on the bottom of the furnace; a plurality of graphite electrodes vertically movable by an electrode elevator; a power source; and an electrode power controller in electrical communication with the power source to control the current and voltage of the power supplied to the plurality of the graphite electrodes. A plasma electric melting furnace, therefore, can be realized that is structurally simple while achieving efficient plasma melting processing of the materials to be processed.
Embodiments of the present invention will now be described with reference to the accompanying drawings.
The plasma electric melting furnace 1 includes a metal layer 2 disposed at the bottom of the furnace. Also arranged in the plasma electric melting furnace 1 are a plurality of graphite electrodes 3 that are vertically movable by an electrode elevator 4. Electric power is supplied to the graphite electrodes 3 via clamps 7 with the electric current and voltage being controlled by a power controller 6.
In a typical electric furnace, submerged arc plasma is generated at the bottom of the furnace. The plasma generated at the bottom of the furnace can damage the furnace bottom and is thus undesirable. High-voltage operation will be required in order for the plasma to reach to the top portion of the furnace. Such high-voltage operation, however, agitates the incineration ash in the furnace and causes the ash to emit undesired dust and gaseous components that diffuse out from the furnace to contaminate work environments. According to the present invention, the power is stabilized at a low voltage to minimize the plasma generation at the bottom of the furnace. When the power was stabilized, the voltage was increased to an operational voltage. In this manner, a plasma zone was formed below the tips of the electrodes without agitating the incinerator ash.
During the operation under the operational voltage, 50 kg of manganese slug was charged when necessary. Charging a manganese ion source, such as Mn ore and ferromanganese slug, allows generation of permanent plasma in the upper portion of the furnace. In addition, 200 kg of the material to be processed 9, 70 kg of silica sand, and 35 kg of manganese slug were charged and the operation was continued. Plasma was generated throughout the furnace and the material to be processed was effectively melt-processed.
The applied voltage, power consumption, and presence or absence of plasma during the stable power phase and the operational voltage phases are shown in Table 1 below.
According to the plasma melting method of the present invention for processing a material to be processed, a stable plasma atmosphere at a temperature of 1500° C. or higher can be achieved during operation. This provides fast melting and volume reduction of the incineration ash and also helps make the incineration ash harmless during the melt-processing of incineration ashes.
In addition to the materials to be processed, such as general wastes, industrial wastes and incineration ashes, other materials were processed by the method of the present invention. Specifically, similar procedures were conducted by charging, instead of the material to be processed, briquettes obtained for example by dispersing polychlorinated biphenyl and a surfactant in an inorganic powder by sonication. As a result, the briquettes dissolved quickly and the resulting emission met the environmental standards. This demonstrates that the furnace of the present invention can also serve as a safe furnace for decomposing PCV.
It is speculated that in the future, the plasma melting method of the present invention for processing a material to be processed is used to melt the low level radioactive wastes. The molten product is then vitrified by encapsulating in a slug.
As set forth, according to the plasma melting method of the present invention for processing a material to be processed and the plasma electric melting furnace, the voltage applied to the electrodes positioned near the bottom of the furnace during the stable power phase is sufficiently low to prevent the generation of submerged plasma, which would otherwise damage the bottom of the furnace. Subsequently, the electrodes are lifted upwards such that stable plasma is generated at the lower ends of the electrodes upon application of the operational voltage. This enables effective melt-processing of the materials to be processed.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2016-096843 | May 2016 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2017/016005 | 4/21/2017 | WO | 00 |