Patent Application
20140053780
The present invention relates to the encapsulation of particles, and more specifically to particle encapsulation using a plasma polymerization process.
Particle encapsulation, in which a particle is surrounded or coated by at least one layer of a surface, has many beneficial uses. Unfortunately, current methods of encapsulation generally require a number of technical steps and result in encapsulated products with poor stability. In addition, most methods result in low product yields, due, in part, to the limited tolerance of the starting materials to industrial operating conditions and the numerous technical difficulties associated with the encapsulation process, with product recovery and inadequate recycling from the reaction systems.
Particle encapsulation, for example, offers a method in which a particle may be introduced to an environment in a more controlled manner. The control is generally imposed by varying different aspects of the coating, such as its composition. Such control generally falls into one of two categories: temporal control and distribution control. Temporal control introduces the particle to the environment over an extended time period or at a pre-specified time. Here, the aim is to match the rate of particle introduction to the rate of particle elimination from the environment. Thus, the particle concentration appears to be regulated and often for a much longer time. This technique is particularly beneficial when introducing a particle into a biologic system for therapeutic purposes, because the overall therapeutic index is improved.
Distribution control, on the other hand, provides for the introduction of a particle at at least one specific environmental location. Such control may be desired when the particle is not required or presents/encounters problems when introduced to the entire environment. In biologic systems, distribution control may reduce or eliminate the occurrence of undesirable side effects.
Current approaches to particle encapsulation include layer-by-layer assembly of polyelectrolytes, emulsion-solvent evaporation processes, formation of hydrogel films, and the preparation of systems based on thiolated polymers, sol-gel carriers, and granulation techniques. While current approaches do provide satisfactory results for introducing particles to an environment; these approaches are complex, involve a number of technical steps, generate large amounts of waste products, and are often inadequate in truly controlling the introduction of the particle into the environment.
Clearly, then, there remains a need to provide for more efficient compositions, systems and methods for introducing particles to an environment in which the particle introduction may be better controlled temporally and/or site-specifically.
The present invention solves the current problem associated with inefficient systems and methods of introducing particles to an environment. The present invention provides for a novel plasma polymerization approach for controlling the introduction and release of a particle to an environment.
Generally, and in one form, the present invention provides for the encapsulation of one or more particles using plasma enhanced chemical vapor depositions (PECVD). The PECVD coats particles with at least one layer of a coating material. PECVD is capable of controlling coating of the particle. In addition, the coating material controls particle introduction into an environment. The coating material and, hence, control of particle introduction into an environment, is dependent on the encapsulation process as well as the composition of the coating of the present invention. In one embodiment, the coating material is a polymeric film comprising at least one carbonaceous compound. The carbonaceous compound is a degradable or nondegradable carbon-containing compound capable of being polymerized on a surface of a particle and, as such, encapsulating the particle.
The present invention also provides for a system for encapsulating one or more particles comprising one or more particles, a rotatable reaction chamber in a plasma enhanced chemical reactor to accept one or more particles, and at least one carbonaceous compound to be used in the rotatable reaction chamber, wherein the carbonaceous compound is polymerized onto a surface of one or more particles forming a polymer film encapsulating one or more particles. The particle may be a pharmaceutical composition (e.g., drug), food, semiconductor material, amino acid, protein, carbonaceous compound, nucleic acid, vitamins, mineral, elemental molecule, fatty acid, lipid, photolabile compound, as examples. The carbonaceous compound is a carbon-containing monomer capable of polymerizing into a degradable or nondegradable polymer.
Reaction conditions that promote polymerization and/or encapsulation generally include power input, peak power, coating time, duty cycle, flow rate of the carbonaceous compound, reactor pressure, and quantity of particles. By altering one or more of the reaction conditions, polymerization is controlled. By controlling polymerization, one can ultimately control the release and rate of release of the encapsulated constituents into an environment. Aspects of the coating or polymer film that may be controlled include film growth, thickness, number, density and quality of one or more monomeric functional groups, hydrophilicity or hydrophobicity, wettability, linearity, cross-linking, and various combinations thereof.
In another form, the present invention is a method for encapsulating one or more particles comprising the step of polymerizing a carbonaceous compound onto a surface of one or more particles to form a polymer film encapsulating one or more particles, wherein the carbonaceous compound is polymerized in a rotatable reaction chamber of a plasma reactor using radio frequency power.
In still another form, the present invention provides for methods and systems for controlling release of one or more particles into an environment, the system comprising one or more particles, a rotatable reaction chamber in a plasma enhanced chemical reactor to accept one or more particles, and at least one carbonaceous compound to be used in the rotatable reaction chamber, wherein the carbonaceous compound is polymerized onto a surface of one or more particles forming a polymer film encapsulating one or more particles, and wherein reaction conditions used in the rotatable reaction chamber control polymer film formation and release of one or more particles into the environment. Particles are released from the encapsulating polymer film by a number of processes that include dissolution of the particle, degradation of the polymer film, and/or passage of the particle through the polymer film.
In yet another form the present invention provides for compositions prepared by systems and methods of the present invention. Compositions include organic and inorganic compositions, such as pharmaceutical compositions, as examples.
Those skilled in the art will further appreciate the above-noted features and advantages of the invention together with other important aspects thereof upon reading the detailed description that follows in conjunction with the drawings.
For more complete understanding of the features and advantages of the present invention, reference is now made to the detailed description of the invention along with the accompanying figures, wherein:
Although making and using various embodiments of the present invention are discussed in detail below, it should be appreciated that the present invention provides many inventive concepts that may be embodied in a wide variety of contexts. The specific aspects and embodiments discussed herein are merely illustrative of ways to make and use the invention, and do not limit the scope of the invention.
In the description which follows like parts may be marked throughout the specification and drawing with the same reference numerals, respectively. The drawing figures are not necessarily to scale and certain features may be shown exaggerated in scale or in somewhat generalized or schematic form in the interest of clarity and conciseness.
Discovering new and improved techniques for particle encapsulation has become one of today's fastest growing areas of research. While many of these techniques have biologic, chemical, and pharmaceutical applications, other applicable fields include electronics, the food industry, optics, data management, agriculture, and material sciences, as examples. In general, the primary purpose of encapsulation is to be able to control and/or delay particle release into the environment. In the pharmaceutical and medical device industry, another purpose for particle encapsulation is to improve particle effectiveness when introduced into a biologic system and to reduce any negative consequences associated with introduction of the particle. In addition, the encapsulated constituents (e.g., particle) should reduce costs associated with its introduction, e.g., reduce dosing, reduce administration of concomitant agents or particles, and reduce the necessity for specialized personnel and/or equipment. The present invention is capable of accomplishing these and other tasks as is further described below.
Coating materials of the present invention are used to prepare coatings that encapsulate particles of the present invention. Coating materials are monomers or carbonaceous compounds (molecules containing at least one carbon) that, upon polymerization (e.g., by deposition), yield polymers or polymer films that are degradable or nondegradable. In many instances, monomers are carbonaceous compounds capable of forming at least one polymer or polymer film degradable by chemical and/or physical processes. Degradation of the polymer or polymer film is then dependant, in part, on the encapsulation process, as described herein. Monomers are also carbonaceous compounds capable of forming at least one polymer or polymer film that is not degradable. As such, the encapsulating polymer or polymer film is capable of releasing the particle via one or more processes, such as dissolution of all or a portion of the particle, chemical degradation of the encapsulating polymer, physical degradation of the encapsulating polymer, and/or passage of the all or a portion of the particle through the polymer (e.g., through pores, spaces, or openings in the polymer or polymer film). Release of a particle encapsulated by such a degradable or nondegradable polymer is also dependent, in part, on the encapsulation process, as described herein.
Degradable polymers include natural polymers (e.g., polysaccharides) as well as synthetic polymers, which are easy to manipulate (e.g., polyesters, polyanhydrides, polyamides, phosphorous-containing polymers). Examples of degradable coatings or polymer films prepared by the present invention are listed in TABLE 1. The coating materials that form such coatings or polymers are the monomeric subunits. Examples of these monomeric subunits include ethylene, vinyl alcohol, acrylic acid, carbophil, ethylene glycol, glycolic acid, saccharide, lactic acid, esters, ortho esters, phosphazenes, anhydrides, amides, as examples.
A degradable polymer generally releases its encapsulated particle into an environment through a process that includes degradation of the encapulating polymer. A degradable polymer, as with a nondegradable polymer, may also have pores, spaces, or openings through which all or portions of the particle may pass.
Degradation of a degradable polymer generally occurs via bond cleavage and/or erosion. For biologic systems, degradation often occurs via enzymatic cleavage or hydrolysis, in which the polymer backbone is cut using a chemical process. With erosion, a physical process occurs, generally involving surface erosion or bulk erosion.
One feature of the present invention is that degradation of a polymer or polymer film may be controlled. Similarly, the present invention is capable of controlling other characteristics of a polymer or polymer film that affect particle release. Hence, the present invention is capable of controlling the release of a particle into an environment. Such control occurs because the present invention is capable of altering one or more conditions of the polymer or polymer film. Coating conditions include altering the surface area of a coating, adjusting the cross-linking of the coating material, altering the wetness, hydrophilicity or hydrophobicity of the coating, changing the density of side groups or functional groups in the coating or coating material, and/or altering the overall thickness of the coating. These coating conditions may be altered for an encapsulation process involving degradable and/or nondegradable polymers. In some instances, encapsulation may include more than one polymer.
In one aspect of the present invention, coating materials such as allyl alcohol, perfluorohexane (C6F14) and methylmethacrylate are provided. Coatings or polymer films obtained by plasma polymerization of allyl alcohol and methyl methacrylate are hydrophilic. Coatings or polymer films obtained by plasma polymerization of perfluorohexane are hydrophobic. Chemical structures of (a) allyl alcohol, (b) perfluorohexane, and (c) methyl methacrylate are shown below.
With the present invention, the carbonaceous compound may be pretreated before use. For allyl alcohol—an oxygen containing organic monomer that is very soluble at pHs ranging from 1 to 10—as well as perfluorohexane (C6F14)—a perfluorocarbon compound that is sparingly soluble at pHs ranging from 1 to 10—the compounds were degassed by freeze-thaw cycles before use. A similar procedure was also performed for methyl methacrylate. Each carbonaceous compound is also handled in the proper manner based on its chemical composition, as is well known in the art. For examples, allyl alcohol and perfluorohexane were protected from light and stored at room temperature, while methyl methacrylate was protected from light and stored in the refrigerator at 4 degrees Centigrade.
Perfluorocarbon compounds, such as perfluorohexane, yield plasma polymerized fluorinated films that exhibit good adhesion to many organic and inorganic substrates, have low intermolecular forces, low friction coefficient, and are biocompatible. The present inventors have previously shown that a pulsed plasma polymerization process may be used with perfluorocarbon compounds to create polymers and polymers films. (See U.S. Pat. No. 5,876,753; U.S. Pat. No. 6,306,506; U.S. Pat. No. 6,214,423; all of which are herein incorporated by reference) Polymers of hexafluoropropylene oxide (C3F6O), perfluoro-2-butyltetrahydrofuran (PF2BTHF, C8F16O) and perfluoropropylene (C3F6) create excellent coatings or films that are capable of attaching to substrate surfaces.
Particles of the present invention are organic or inorganic molecules that may be surrounded or coated by at least one layer of a coating material. Generally, preferred particles are those that remain functional after coating. Functional particles may undergo some structural alteration(s) during coating; however, their general function remains. Particles may include pharmaceutical compositions (e.g., drugs), food, semiconductor materials, proteins, carbonaceous compounds, nucleic acids, vitamins, minerals, elemental molecules, fatty acids, lipids, photolabile compounds, as examples.
In various embodiments, a pharmaceutical composition, for example aspirin and/or ibuprofen, may be used as the particle. Aspirin, chemically referred to as acetyl salicylic acid, is an antipyretic, anti-inflammatory analgesic with a carboxylic acid backbone group rendering the molecule soluble in various solvents. Acetyl salicylic acid, shown below as structure (d), may be detected by UV-visible spectroscopy and is available in crystal form. While uniformly sized particles may be used with the present invention, it is not necessary. In some instances, particles of different sizes may be preferred. For crystals such as aspirin, uniformity may be obtained by grinding and sieving the crystals followed by drying under vacuum (e.g., 100 degrees Centigrade overnight).
Ibuprofen, chemically referred to as 4-isobutyl-α-methylphenylacetic acid, is an acidic, non-steroidal, anti-inflammatory composition with limited solubility in low pH (<7) solutions and high solubility at higher pH (>7) solutions. Ibuprofen has a carboxylic acid backbone group as shown in structure (e) and may be detected by UV-visible spectroscopy. For ibuprofen, crystals were sieved and used without drying.
PECVD provides for a solventless, pin-hole free, single-step encapsulation process in which the encapsulating or coating material may be modified depending on the process, itself. For example, the process is able to control encapsulation, and hence, particle introduction into an environment, by adjusting the side groups, thickness, wetness, surface area and/or composition of the coating material.
With the present invention, both pulsed and the more conventional continuous-wave (CW) plasma approaches may be used. For example, the present inventors have shown that using a pulsed plasma approach provides excellent film chemistry control during polymer formation and control of film thickness (Susut C and Timmons R B, Plasma enhanced chemical vapor depositions to encapsulate crystals in thin polymeric films: a new approach to controlling drug release rates, International Journal of Pharmaceutics, 2004, in press; herein incorporated by reference). Pulsed applications may limit undesirable plasma-induced chemical changes to particles. In addition, under pulsed reaction conditions, significant film formation occurs during plasma off periods (and undesirable high energy reactions between ion-radical and particle are minimized).
A 360° rotatable plasma reactor was employed to help achieve uniform and complete coating of particles. A cylindrical Pyrex glass reactor of 5 centimeter internal diameter and 45 centimeter in length was used as the plasma chamber. Radio frequency (RF) power to the reactor was provided through two concentric metal rings separated by a distance of 20 centimeter. The volatile reaction products and unreacted monomer were collected in a liquid nitrogen cold trap located downstream of the reactor. A butterfly valve controller with pressure transducer (MKS Baratron Model 252A) was used both to monitor and control pressure in the reactor. The flow rate of the monomer was controlled and monitored by a flowmeter placed upstream of the reactor. Ferrofluidic valves, inserted at both ends of the reactor tube, permitted complete rotation of the reactor chamber under vacuum conditions. The rotation rate was controlled with a variable speed motor (Dayton Model 4Z827D) connected by pulley to the reactor.
A schematic of a plasma reactor of the present invention, with its associated electronics, is shown in
Carbonaceous compounds of the present invention were deposited onto particles using a reactor, similar to one described above. Those skilled in the art will appreciate that the features described may also be modified as needed. For most reactions, the rotation rate was kept steady (e.g., 4 rev/minute for acetylsalicylic acid crystal particles or 3 rev/minute for ibuprofen crystal particles). The lower rotation rate for ibuprofen minimized the adsorption of the smaller particles on the walls of the reactor chamber by electrostatic forces. The quantity of particles placed in the reaction chamber, in each run, was, in some cases, used as a variable and this effect was evaluated.
Self-aggregation and/or electrostatic forces were reduced by several methods, including increasing the monomer flow rate, decreasing the rotation rate of the reactor chamber and/or limiting the peak power to 100 Watts or less. Applying vibration to the reactor walls as well as applying a surface treatment to minimize adhesions may also be employed. In addition, it is also possible to recover coated particles that have adhered to the reactor wall. In general, the percent recovery (ratio of the amount of recovered particles that are coated vs. total amount of particles introduced into the reactor) may typically range from 50% to 99%. One skilled in the art will appreciate that other typical ranges may apply.
Before each coating, the reactor chamber was pre-cleaned (e.g., with soap and water and acetone). It was then vacuumed to a background pressure (e.g., approximately 10 mTorr). Next, the reactor was treated with an oxygen plasma discharge (e.g., 100 Watts at 100 mTorr pressure, operated at a duty cycle of ⅓ ms/ms or ⅕ ms/ms). Pre-cleaning removes polymer residues from the chamber due to previous coatings. After the oxygen plasma discharge, particles would be placed into the reactor. The two ends of the chamber were stoppered (e.g., with glass wool) to keep the particles in the chamber during coating. The reactor chamber was then evacuated to the background pressure.
In general, and for example coatings provided herein, the reaction chamber was rotated constantly. Using the pulsed plasma approach, significant polymer film formation occurred during plasma off periods, a time when undesirable high energy reactions between ion-radical and particles are minimized. A process of continuous wave plasma polymerization may also be employed to encapsulate particles.
The average power employed under pulsed plasma conditions was calculated according to the formula shown below (1), where τon and τoff are the plasma on and off times and Ppeak is the peak power. By using pulsed plasma polymerization, the average power employed during film formation was often much lower than the power employed under continuous wave reaction conditions, because of the relatively longer plasma off times compared to plasma on times.
Deposition (polymerization) of the coating or polymer film of the present invention was controlled by altering a number of variables associated with the plasma reactor. Variables included duty cycle, power input, peak power, flow rate of the monomer, pressure of the reactor, coating time period and quantity of particles introduced into the reaction chamber at a time.
With the present invention, suitable plasma on/off times (duty cycles) were generally in the millisecond range. As used herein, duty cycles are reported as on/off times per cycle and provided in units of ms/ms. Suitable peak powers ranged from about 25 W to about 100 Watts. Suitable coating periods were typically between about 20 minutes and 1 hour. In some cases, self-aggregation of particles may help determine the coating time period. The amount of particles coated at a time typically ranged from about 0.5 grams to about 4.0 grams. Flow rates were about 1.5 cm3 (STP)/minute to about 2.00 cm3 (STP)/minute. The pressure of the reactor typically varied from about 150 mTorr to about 350 mTorr. Those skilled in the art will appreciate that, while typical ranges and values are provided, there is no reason that other values may not be applied, as needed.
To help characterize the coating or polymer film deposited by the present invention, replicate runs of certain carbonaceous compounds were provided in which the carbonaceous compound was deposited on one or more solid substrates, such as silicon wafers and KBr surfaces. The FT-IR spectra were collected with a Bruker Vector 22 spectrophotometer using 4 cm1 resolution. Spectra were recorded in absorption mode on polymer films deposited on KBr discs. The thickness of the films deposited on silicon wafers were measured using a Tencor Alpha Step 200 profilometer. A syringe needle was employed to scribe a scratch on the films. Thickness calculations were based on the difference between the height of the film and original height of the substrate.
Particle Introduction and Release into an Environment
The environmental conditions for introduction of one or more particles into an environment may also be manipulated to alter particle release. For example, in one aspect of the present invention, the environment for acetyl salicylic acid was 0.1 M HCl solution (to simulate gastric fluid). For ibuprofen, the environment was a pH 7.0 phosphate buffered solution (to simulate intestinal fluid).
The quantity of particles introduced into an environment was assessed using a UV-visible spectrophotometer (Janco). The maximum absorption wavelength for acetylsalicylic acid was determined to be 276 nm. Absorbance versus time measurements were taken periodically using 1-cm quartz cuvettes. Stock solutions were prepared with 10 mg of particles in 100 ml of solution. Each solution was stirred constantly in a 100 ml volumetric flask. At the end of each period, an aliquot was transferred into a cuvette; the liquid was returned to the volumetric flask as soon as the absorbance data were taken. The maximum absorption wavelength for ibuprofen was determined to be 264 nm. With the exception of pH change, the same procedures as employed for acetyl salicylic acid were followed for ibuprofen. For kinetic analysis, model fittings were performed using Microsoft Excel.
Silica gel, polyester-backed TLC plates of thickness 250 μm were used to analyze the separation and/or breakdown of compounds after polymerization and after particle release into an environment. Before use, TLC plates were dried in an oven for about 1 hour at 110 degrees Centigrade to remove adsorbed atmospheric moisture.
For calculations, the distinction between different components in a mixture was determined by a physical constant called retention factor (RF) which is based on the preferential interaction between the compound and the TLC plate. It is known that each compound generally has a different retention factor. If a compound is converted, separated, or structurally altered during plasma polymerization, it will generally have a different RF value. Thus, free particles and encapsulated particles were prepared by dissolving 10 mg of each in 1 ml of dichloromethane.
All TLC solutions were freshly made and aliquots of 5 μl were applied as spots approximately 1 cm apart onto 5×17 cm silica gel TLC plates. A chloroform-acetone (4+1) solvent system was used. Plates were air-dried and analyzed by iodine vapor. Retention factors were calculated for each encapsulated particle and compared to the value obtained for unencapsulated (i.e., free) particle. These values were compared to those known in the literature.
Allyl alcohol was used as a representative carbonaceous compound for coating particles of the present invention. It was determined that as the RF duty cycle was reduced, the retention of the monomer's oxygen content increased, leading to an increase in the hydrophilicity of the coating or polymer film (also referred to herein as film). An increase in the plasma off time also caused an increase in the —OH group incorporation in the coating thus increasing surface density of polar groups. In addition, significant polymer film growth occurred during the plasma off times. Deposition per pulse cycle was shown to increase at constant on time and power, as the off time increased.
Plasma polymerized allyl alcohol films were examined as a function of power, coating time and pulsed or continuous wave modes. Some results are illustrated in
Regarding FT-IR analysis of the films with changing RF duty cycles, there was a progressive increase in the retention of the monomer's oxygen content with decreasing RF duty cycles. In addition there was a continual shift in the O-H stretching frequency to lower wave numbers with increased O-H incorporation as a result of H-bonding. The trends mentioned above applied for duty cycles from ½ ms/ms and ⅕ ms/ms; similar trends occurred for RF duty cycles less than ⅕ ms/ms. In addition, there was a slight increase in the retention of the monomer's oxygen content with duty cycles from ½ to ⅕ ms/ms.
Some of the reaction and coating conditions for coating particles of acetylsalicylic acid with one or more carbonaceous compounds of allyl alcohol are illustrated in TABLE 2. Polished Si substrates were also coated and profilometer measurements were made. Pressure in the reactor was about 160 mTorr with a constant rotation rate of about 4 rev/min. The approximate quantity of particles introduced into the reaction chamber for each run (e.g., AA1, AA2, etc) was about 4 grams. Actual particle sizes ranged from about 1 to about 100 microns; mean size was approximately 30 microns, as observed by light scattering measurements.
TABLE 2 shows the variations in film thickness. For pulsed plasma polymerization of allyl alcohol, the energy efficiency of film formation (mA°/J) increased with decreasing power input (samples AA1, AA5 and AA2). Ablation reactions may be significant at higher power inputs. Changing the coating time (other variables held constant) effected film thickness. For example, when coating time was doubled, the film thickness increased by a factor of 2. Decreasing the duty cycle increased the energy efficiency of film formation and indicated that there was significant film growth during plasma off periods.
The duration of the plasma coating time had an effect on particle release rate.
As described above, the present invention is used to control the characteristics of a coating or polymer film deposited on a particle using a pulsed or continuous wave radio frequency. The control factors include coating time, peak power input and pulsed plasma duty cycle. The present invention also controls polymer film thickness and polymer film cross-linking, as well as the rate of release of the particle from the polymer film.
Some of the reaction and coating conditions for coating particles of ibuprofen with allyl alcohol are illustrated in TABLE 3. IA1, IA2, IA3, and IA4 were performed under pulsed conditions and IA5 and IA6 were performed under continuous wave conditions. The pressure in the reactor was about 260 mTorr with a constant rotation of about 3 rev/min. Approximately 0.8 grams of crystals were used each time; crystals were typically smaller than 35 μm.
TABLE 3 shows that increasing the power under continuous-wave conditions effects the energy efficiency of film formation; increased power decreased the energy efficiency of polymer film formation. Note that for each run, total CW power input was comparable to the power used in the pulsed experiments, because the average power under pulsed plasma conditions corresponded to ⅙th or ¼th of the peak power reported.
The release rates of encapsulated ibuprofen were examined as a function of peak power, coating time and plasma duty cycle. Both CW and pulsed conditions were evaluated and some of the results shown in
In general, the rate of release of ibuprofen was faster than the rate of release of acetyl salicylic acid. This faster rate is largely a reflection of the higher solubility of ibuprofen.
Increasing the coating time increased the time required to complete particle release (see
When depositing the polymer film using CW conditions with different peak powers (10 W and 25 W, TABLE 3), the release rate was also affected as shown in
Plasma polymerization characteristics of perfluorocarbons have been provided by the present inventors (see U.S. Pat. Nos. 5,876,753; 6,306,506; 6,214,423; 6,329,024; 6,482,531). CFx radicals, especially CF2 radicals and F atoms in gas phase are important for polymer film formation. CF2 radicals are generally thought to be responsible for the formation of the linear portion of deposited fluorocarbon polymer films, whereas quaternary C-CFn type radicals are involved in cross-linking. The same holds true for perfluorohexane. Films produced by plasma polymerization of perfluorocarbons vary from a highly cross-linked structure at high plasma duty cycle to a more linear CF2 dominated structure at low plasma duty cycle. Decreasing the duty cycle reduces the cross-linkages. Similarly, as the peak power is decreased, a more linear polymer structure is observed; CF2 content increases at low peak power.
Coatings produced using perfluorocarbons are generally highly hydrophobic. A rough and fibrous-like morphology appears to be responsible for this, because high power inputs accompanied by relatively long plasma off times resulted in fibrous-like ultrahydrophobic surfaces on the polymers films. With the present invention, plasma polymerization of a hydrophobic polymer film, such as perfluorohexane, can also be manipulated to control the introduction and release of a particle into an environment.
Plasma polymerized perfluorohexane films were examined as a function of peak power and plasma duty cycle. (See
Some of the reaction and coating conditions for coating particles of acetylsalicylic acid with perfluorohexane are illustrated in TABLE 4.
For TABLE 4, the flow rate of the monomer was about 1.5 cm3 (STP)/min and pressure in the reactor was about 130 mTorr with a constant rotation rate of about 4 rev/min. For AP3, rather than a single run, about 4 grams were introduced into the chamber and one gram of sample was removed every 30 minutes, signified as AP3(1), AP3(2), AP3(3), AP3(4), for a total of two hours.
Referring to TABLE 4, the duration of plasma coating times were observed to have an effect on particle release rates (see AP1 and AP2). For AP3 runs, the effect of coating time on quantity of particles was evaluated. The results are indicated as percent release versus immersion time in the simulated gastric solution (
Some of the reaction and coating conditions for coating particles of ibuprofen with perfluorohexane are illustrated in TABLE 5
For TABLE 5, the flow rate of the monomer was about 2.0 cm3 (STP)/min and the pressure in the reactor was about 300 mTorr with a constant rotation rate of about 3 rev/min. Polished silicon wafer substrates were also coated and profilometer measurements were made.
With pulsed plasma polymerization of perfluorohexane, increasing the peak power decreased the energy efficiency of film formation, similar to allyl alcohol film formation. Changing the coating time (other variables held constant) greatly effected film thickness. For example, doubling the coating time, doubled film thickness.
Films formed by the polymerization of methyl methacrylate have polyester groups that are biocompatible. Such polymer films are typically very stable in phosphate buffered solutions (pH=7.4) and resist hydrolysis. Through X-ray photoelectron spectroscopy (XPS) analysis, it was observed that oxygen content in such films increased as the peak power decreased. As peak power increased, the deposition rate was observed to decrease. In addition, polymer film growth occurred during the off periods with pulsed plasma deposition. Comparison of coatings produced under pulsed plasma and CW conditions, showed that more ester groups were incorporated with pulsed polymerization and ester groups retention was enhanced as the average power was reduced.
Some of the reaction and coating conditions for coating particles of acetylsalicylic acid with methyl methacrylate are illustrated in TABLE 6. For TABLE 6, the flow rate of the monomer was about 2.0 cm3 (STP)/min and the pressure in the reactor was about 230 mTorr with a constant rotation rate of about 3 rev/min. Polished silicon wafer substrates were also coated and profilometer measurements were made.
As with the other carbonaceous compounds, TABLE 6 shows that increasing the peak power from 50 W to 100 W increased the film thickness but decreased the overall energy efficiency of a polymer film of methyl methacrylate. In TABLE 6, N/A represents those samples where the tackiness of methyl methacrylate did not allow for the measurement of film thickness or energy efficiency.
As with polymer films of polyallyl alcohol and polyperfluorohexane,
Some of the reaction and coating conditions for coating particles of ibuprofen with methyl methacrylate are illustrated in TABLE 7.
For TABLE 7, the flow rate of the monomer was about 2.0 cm3 (STP)/min and the pressure in the reactor was about 300 mTorr with a constant rotation rate of about 4 rev/min. The amount of crystals used with IM1 and IM2 was about 0.5 gram and about 1 gram used for IM3 and IM4. Polished silicon wafer substrates were also coated and profilometer measurements were made.
Referring now to
Using thin-layer chromatography, it was observed that particles of the present invention were not degraded or converted to other compounds of different molecular weight or Rf value as a result of plasma deposition; no additional spots other than those corresponding to the particle were observed on any of the TLC plates.
For
The above examples illustrate that plasma deposition (polymerization) of at least one carbonaceous compound on the surface of a particle results in the encapsulation of that particle with a polymer film. The carbonaceous compound may be hydrophilic and/or hydrophobic, capable of forming a hydrophilic or hydrophobic polymer film, respectively. As described herein, plasma deposition is used to control aspects of the coating or polymer film (e.g., surface area, cross-linking, wettability, extent of hydrophilicity or hydrophobicity, number and/or density of side groups, overall thickness) via reaction conditions such as power input, peak power, coating time, pulsed plasma duty cycle, as examples. The control of polymerization directly effects and, thus, controls the introduction of the encapsulated particle into the environment. This introduction is typically a function of the rate of release, including the initial rate of release of the particle and the total time for complete particle release, as examples.
With the present invention, plasma deposition is capable of controlling particle introduction into an environment. The control depends, in part, on one or more plasma deposition variable(s) (e.g., reaction conditions) that may be altered. Some of the variables and their effects on the rate of particle release are illustrated in TABLE 8.
With the present invention, a polymeric film functions similar to a permeation barrier between a particle and an environment. When an encapsulated particle is introduced to an environment, typically there is dissolution of all or part of the particle into the environment. As such, altering reaction conditions such as power input, coating time, and/or duty cycle during plasma deposition of the present invention, will alter particle dissolution. For example, as illustrated, increases in coating or polymer film thickness reduced the rate of release of a particle encapsulated by a polymer film. Increasing the power input or plasma duty cycle during coating reduced the porosity of the polymer film, increased the extent of cross-linking of the polymer film, and reduced the rate of release of the particle encapsulated by the polymer film.
Kinetic analyses of release rates were performed using either zero-order or first-order kinetics. For zero-order kinetics, there is typically an initial diffusion of water into the encapsulated particle followed by a saturated solution in which both liquid and undissolved solid remain in equilibrium. This process obeys equation (2), where Mr is the amount of particle released at time t; M0 is the total amount of particle before dissolution; k0 is the zero-order release constant and t is time.
Zero-order kinetic data for acetylsalicylic acid crystal particles coated with polyallyl alcohol are shown in
For first-order kinetics, there is typically an initial, rapid influx of a solution into the encapsulated particle. The particle is then solubilized followed by a slower diffusion phase as the particle diffuses out of the encapsulated coating and the solution inside the coating becomes less concentrated with time. The equation used for first-order kinetics is shown as equation (3), where Mt is the amount of particle remaining at time t; M0 is the total amount of particle before dissolution; k1 is the first-order release constant; and t is time.
First-order kinetic data for acetylsalicylic acid crystal particles coated with polyallyl alcohol are shown in
The above figures indicate that particle release rates are more in accord with first-order rather than zero-order kinetics. The first-order rate constants were 0.12 to 0.0054 min−1, representing a factor in excess of 20 for the variation of release rates.
The data also show that there is room for further control of release rates, for example, by using longer coating time periods, possibly in combination with other reaction conditions, such as higher power inputs. While all potential possibilities for altering reaction conditions are not presented, the possibilities are obvious to one of ordinary skill in the art.
Kinetic analyses were similarly performed for particles of acetylsalicylic acid crystals coated with a polymer film of polymethyl methacrylate or polyperfluorohexane. With these coatings, particle release also appeared to involve first-order rather than zero-order kinetics. TABLE 9 summarized some of the analyses.
Light scattering measurements for particles of acetylsalicylic acid molecules are shown in
The present invention shows that deposition of a polymer film or coating using plasma polymerization is a new and improved way to introduce and control the release of a particle into an environment. Using systems, methods, and compositions of the present invention, one can prepare any encapsulated particle coated with any degradable and/or nondegradable polymer and alter particle release rates to control particle introduction into an environment. The control of particle introduction into the environment may be a temporal and/or site-specific control. For example, polymer film deposition may be controlled by altering reaction conditions, such as power input, peak power, coating time, duty cycle, flow rate of the carbonaceous compound, reactor pressure, and/or quantity of particles during preparation of the coated particles. These conditions control aspects of the coating or polymer film, including polymer film growth, polymer film thickness, the density of polar groups in the polymer film, the number of functional groups in the polymer film, the hydrophilicity or hydrophobicity of the polymer film, wettability of the polymer film, linearity of the polymer film, and extent of cross-linkages in the polymer. In this way, a polymer film of the present invention may be finely tuned in order to obtain any required combination of temporal and/or site-specific release of particles into an environment.
The present invention also provides for compositions prepared by systems and methods described herein. Such compositions, systems, and/or methods may include one or more carbonaceous compounds as well as one or more different types of particles. Indeed, such variations may be specifically manufactured to optimally control release of one or more particles into an environment. Optimally control may include combining particles with similar or different coatings, wherein the differences include the coating composition, thickness, number and/or type of functional group, hydrophobicity, hydrophilicity, wettability, linearity, cross-linking, and combinations thereof. With the present invention, one or more different compositions may also be combined to yield a desired particle release property.
While specific alternatives to steps of the invention have been described herein, additional alternatives not specifically disclosed but known in the art are intended to fall within the scope of the invention. Thus, it is understood that other applications of the present invention will be apparent to those skilled in the art upon reading the described embodiment and after consideration of the appended claims and drawing.