Claims
- 1. A process for the preparation of coated plastic bottles which excel in both oxygen-barrier property and water resistance, which comprises coating at least one surface of a plastic bottle-forming parison, preform or sheet formed of a thermoplastic resin by melt molding with an aqueous latex of a copolymer consisting essentially of 99 to 70% by weight of vinylidene chloride and 1 to 30% by weight of at least one acrylic or methacrylic monomer and further including up to 100 parts by weight of at least one member selected from other ethylenically unsaturated monomers per 100 parts by weight of the total amount of said two monomers, said copolymer having an oxygen permeability constant of less than 9.times.10.sup.-14 cc.multidot.cm/cm.sup.2 .multidot.sec.multidot.cmHg as measured at a temperature of 20.degree. C. and a relative humidity of 100% and a water vapor permeability constant of less than 3.times.10.sup.13 g.multidot.cm/m.sup.2 .multidot.day as determined according to the method of JIS Z-0208, drying the coated parison, preform or sheet to form a coating layer, subjecting the so-formed coated structure to biaxially drawing blow molding or deep forming to introduce monoaxial or biaxial orientation in said plastic substrate, and then increasing the oxygen-barrier property and water resistance of the coated plastic bottle by subjecting the resultant bottle to aging at a temperature of 30.degree. to 120.degree. C. for 30 seconds to 7 days.
- 2. A process for the preparation of plastic bottles according to claim 1, wherein said copolymer consists essentially of 96 to 75% by weight of vinylidene chloride and 4 to 25% by weight of at least one acrylic or methacrylic monomer and further including up to 50 parts by weight of at least one member selected from other ethylenically unsaturated monomers per 100 parts by weight of the total amount of said two monomers.
- 3. A process for the preparation of plastic bottles according to claim 1, wherein said acrylic or methacrylic monomer is a monomer represented by the following formula: ##STR4## wherein R.sub.1 stands for a hydrogen atom, a halogen atom or a methyl group, and X stands for a nitrile group (--C.dbd.N) or a group ##STR5## in which Y stands for an amino group, a hydroxyl group, alkyloxy group, a cycloalkyloxy group, an aminoalkyloxy group, a hydroxylalkyloxy group, an alkoxyalkyloxy group, a haloalkyloxy group, a glycidyl group, an aryloxy group or an aralkyloxy group.
- 4. A process for the preparation of plastic bottles according to claim 1, wherein said copolymer further comprises a monomer represented by the following formula: ##STR6## wherein R.sub.1 stands for a hydrogen atom, a halogen atom or a methyl group, and R.sub.2 and R.sub.3 each stand for a hydroxyl group and these two hydroxyl groups may be dehydrated to form an oxirane ring.
- 5. A process for the preparation of plastic bottles according to claim 1, wherein said copolymer is a vinylidene chloride/alkoxyalkyl acrylate or methacrylate/alkyl acrylate or methacrylate/trichloroethylene copolymer.
- 6. A process for the preparation of plastic bottles according to claim 1, wherein the plastic bottle substrate is formed of polyethylene terephthalate or polypropylene.
- 7. The process of claim 1 wherein the resultant bottle is subjected to aging at a temperature of about 30.degree. C. for about 7 days.
- 8. The process of claim 1 wherein the resultant bottle is subjected to aging at a temperature of from about 40.degree. C. to about 48.degree. C. for from about 24 hours to about 5 days.
- 9. The process of claim 1 wherein the resultant bottle is subjected to aging at a temperature of about 60.degree. C. for from about 6 hours to about 24 hours.
Priority Claims (2)
Number |
Date |
Country |
Kind |
55-59505 |
May 1980 |
JPX |
|
55-59506 |
May 1980 |
JPX |
|
Parent Case Info
This is a continuation of application Ser. No. 386,039, filed June 7, 1982 which in turn is a division of application Ser. No. 258,772 filed Apr. 29, 1981, now issued as U.S. Pat. No. 4,370,368.
US Referenced Citations (4)
Divisions (1)
|
Number |
Date |
Country |
Parent |
258772 |
Apr 1981 |
|
Continuations (1)
|
Number |
Date |
Country |
Parent |
386039 |
Jun 1982 |
|