This invention relates to reinforcing flexible plastic sheet-form products, and more particularly to reinforcing the sheet-form bases of plastic fastener strips against tearing.
Many sheet-form products are economically produced in large volume by continuous molding or calendaring of plastic resins. In the touch fastener industry, molded plastic hook tape has displaced traditional woven fabric fasteners for many applications, simply because of lower production costs. However, molded, rolled or extruded resin fastener tapes are generally found to be more susceptible to tearing than are fastener tapes with woven or knit ground fabrics, particularly when notched such as by sewing the fastener tape to an underlying garment or other product.
Furthermore, the chain-like molecules of the resin forming the strip-form bases of products manufactured in continuous lengths can be found to become somewhat oriented toward the machine, or processing, direction by elongation or drawing of the material while still somewhat molten, further reducing the ability of the final product to resist tears propagating along the length of the tape.
Unfortunately, for many applications the fastener tape is ultimately sewn in place with at least one row of stitches extending along the length of the tape, forming a closely-spaced row of punctures or perforations extending along a direction most susceptible to tearing. It is along this weakened perforation line that load is transferred from the closure to the underlying substrate, through the thread passing through the punctures. Tears frequently result, extending along the stitch line and separating the fastener component from the rest of the product. This tearing may be readily evident, or result in a premature failure in use.
Various improvements have been suggested for increasing the longitudinal tear resistance of molded hook fastener tape. For example, surface features have been molded onto the surface of the base of the tape, between adjacent fastener elements, to help to impede tears propagating along the tape between rows of fastener elements. Strings, screens, yarns, paper and other materials have been laminated to, or embedded in, resin fastener tape bases. Resins of improved material properties have been considered, although for many applications the base resin is the same resin from which the fastener elements are formed, and so resin properties must be selected for fastener element formation and function as well as base tear resistance.
Further improvements in reinforcing plastic fastener tape, and other sheet-form or strip-form resin products, are desired, particularly for increasing tear resistance. Preferably, such improvements can be obtained without substantial increase in overall thickness, stiffness or cost of the final product.
We have found that particular fabric structures, bonded to the backside of a sheet-form resin base in certain configurations, can significantly increase the tear resistance of the resin base, while maintaining a base thinness and flexibility suitable for many applications. We have even found that the addition of such reinforcing fabrics can enhance the visual appearance and tactile feel of fastener tapes for many uses.
According to one aspect of the invention, a strip-form touch fastener component includes a resin base, a stem and a head disposed on the stem. The resin base has a front surface from which an array of fastener elements project. Each fastener element has a stem extending contiguously from the front surface of the base and formed of resin forming at least a portion of the base and a head disposed on the stem above the base and forming an overhang for releasably engaging fibrous loops. In addition, the strip form touch fastener component includes a reinforcing fabric that includes two distinct layers of yarn, an anchor layer and an outer layer. The reinforcing fabric is on a side of the resin base opposite the fastener elements. The anchor layer faces the resin base and includes filaments embedded within resin of the base to anchor the fabric to the base. The outer layer includes float filament sections extending generally along an outer surface of a back side of the fastener component, such sections connected to the back side of the fastener component only at their ends, and otherwise lying against the back side of the fastener component.
In preferred embodiments where the reinforced fastener product is to be attached to a garment or other article by sewing or stitching, the product has a stitch hole tear strength of at least 2.0 pounds.
In some embodiments, the float filament sections extend generally straight between their connected ends, and are preferably substantially free of resin of the base between their ends.
In some preferred embodiments, the float filament sections extend no more than about 0.3 millimeter from a back surface of the resin base, preferably more than about 0.03 millimeter, and preferably about 0.15 millimeter.
The float filament sections preferably have an average float length of at least about two millimeters, such as between about 2 and 10 millimeters.
Preferably, the average float length of the float filament sections is more than about 10 times as long as the nominal distance the float filament sections extend from a back surface of the resin base.
The float filament sections are preferably arranged in a pattern, such as of at least about 175 float filament sections per square centimeter of the back side of the fastener component.
The float filament sections may be sections of filaments of multifilament yarns of the reinforcing fabric, for example, and may extend in a direction generally across the strip-form fastener component.
In some embodiments, the yarns are multifilament yarns, with each yarn containing from 10 to 13 discrete filaments. The yarns may be between about 20 and 170 denier, with each filament between about 2 and 40 denier.
In some preferred embodiments, the reinforcing fabric is a knit fabric, such as a warp knit fabric. Preferably, the technical face of the fabric faces the resin base, with the technical back providing the float filament sections.
The technical back is preferably in an unnapped condition. The knit fabric preferably includes between about 20 and 60 courses per inch, more preferably between about 47 and 55 courses per inch. The knit fabric preferably includes between about 15 and 60 wales per inch, more preferably between about 32 and 38 wales per inch.
For some applications, the knit fabric is stabilized in a post-knit, cross-wale stretch condition.
According to another aspect of the invention, a strip-form touch fastener component includes a resin base with a front surface from which an array of fastener elements project. Each fastener element has a stem extending contiguously from the front surface of the base and formed of resin forming at least a portion of the base and a head disposed on the stem above the base and forming an overhang for releasably engaging fibrous loops. In addition, the strip form touch fastener component includes a reinforcing fabric directly laminated to a side of the resin base opposite the fastener elements. The fabric is a knit material with float filament sections extending generally along an outer surface of a back side of the fastener component. The float sections are connected to the back side of the fastener component only at their ends, and otherwise lie against the back side of the fastener component.
Various preferred embodiments of this aspect of the invention include features discussed above with respect to the first aspect of the invention.
Another aspect of the invention features a method of reinforcing a resin base of a plastic touch fastener component that has an array of fastener elements extending from a front surface of the resin base. The method includes providing a fabric, laminating the fabric, and forming an array of touch fastener elements. The technical back of the fabric includes an array of float sections of filaments. The fabric is laminated to a back surface of a resin sheet to form a laminate, with the technical face of the fabric facing the resin sheet and the float sections extending along an exposed surface of the laminate. The touch fastener elements are formed extending from a front surface of the resin sheet, each fastener element having a resin stem extending contiguously from resin of the front surface of the resin sheet.
In some implementations, the fabric is laminated to the resin sheet as the resin sheet is formed from molten resin.
In some cases, the fabric is laminated to the resin sheet by introducing both the fabric and moldable resin to a nip adjacent a rotating roller, applying pressure to infuse the resin into surface features of the fabric, and then cooling the resin to secure the resin to the fabric. The nip may be defined between two counter-rotating rollers or between the rotating roller and an extrusion nozzle, for example.
In some embodiments, the rotating roller defines an array of molding cavities, the applied pressure also forcing the resin into the molding cavities to form at least the stems of the fastener elements.
In some cases, the cavities are shaped to form complete, engageable fastener elements.
In the product as produced, the float filament sections preferably have ends secured to the laminate and extending generally straight between their ends, with the float filament sections preferably substantially free of resin of the sheet between their ends.
Prior to laminating, the fabric to the resin sheet, the fabric may be stretched across a width of the fabric, such as in a cross-wale direction.
In some cases, the lamination is performed in a continuous process defining a machine flow direction, with the stretching reorienting the float sections to increase their orientation toward a direction extending perpendicular to the machine flow direction. The fabric is, in some examples, stretched sufficiently to straighten the float sections of filaments.
For some applications, the fabric is stabilized in its stretched condition prior to laminating the fabric to the resin sheet.
Various other features of preferred embodiments of the method have been discussed above with respect to the product.
We use the term ‘float’ in its usual sense as understood in the textile industry. For a knit, a float or float segment or float yarn is a portion of yarn that extends for some distance across the fabric without being knitted in. In weaving, a float or float segment is a portion of yarn, such as a filling yarn, that extends over two or more adjacent perpendicular yarns, such as warp yarns, or vice versa. In either case, the float segment has a float length defined as the length of the yarn segment between anchor points.
Float yarn segments are typically found on the technical back of the product. The technical back is the rough side of a fabric, and with the exception of some pile fabrics, the side traditionally considered less aesthetically pleasing. In a knit, the float segments are generally found on the technical back. On most textile fabrics, the technical face, on the other hand, is generally the smoother face, with the more finished appearance.
The reinforced fastener products described herein can be particularly useful for applications where the product is to be attached to a garment or other article by sewing or stitching, or in other applications requiring increased tear resistance. The ‘exoskeleton’ of exposed, straight, preferably taut float yarns may also be more appealing than a smooth resin surface for some applications, in that it provides a “textile” appearance and “hand” to the back of the plastic substrate. The reinforcement methods and fabrics described herein are also useful for reinforcing non-fastening products and substrates.
The details of one or more embodiments of the invention are set forth in the accompanying drawings and the description below. Other features, objects, and advantages of the invention will be apparent from the description and drawings, and from the claims.
Like reference symbols in the various drawings indicate like elements.
Referring to
Male fastener component 100 is designed to, for example, strongly engage a low pile height, loop touch fastener component, particularly a loop component with loops formed of, for example, a high strength multifilament yarn or a high strength monofilament. High strength loops are desirable for fasteners for high strength applications requiring high cycle life, as the resist breakage at higher peel loads. Typically, high strength yarns and monofilaments are made by extrusion. Generally, the process includes a drawdown step to impart orientation on the yarn or monofilament so as to improve, for example, tenacity of the yarn or monofilament. High strength fibers may also be formed by other methods, for example, by solution spinning. Suitable high strength loop filament materials include, for example, polyamides, polyesters, polyurethanes, ultra-high molecular weight solution spun polyethylene (e.g., SPECTRA® polyethylene), aramids (e.g., KEVLAR®), acrylics and rigid rod polymers like poly(p-phenylene-2,6-benzobisoxazole).
The fastener elements of
In some embodiments, the mold roll 208 comprises a face-to-face assembly of thin, circular plates or rings (not shown) that are, for example, about 0.003 inch to about 0.250 inch (0.0762 mm-6.35 mm) thick, some having cutouts in their periphery defining mold cavities and others having solid circumferences, serving to close the open sides of the mold cavities and serve as spacers, defining the spacing between adjacent fastener element rows. A fully “built up” mold roll may have a width, for example, from about 0.75 inch to about 6 inches (1.91 to 15.24 cm) or more and may contain, for example, from about 50 to 1000 or more individual rings. Further details regarding mold tooling are described by Fisher, U.S. Pat. No. 4,775,310.
An alternate technique for molding fastener elements is shown in
The fastener elements can also be formed by first molding or otherwise forming an array of stems extending from a resin base, and then post-forming engageable heads on the stems, such as by heat and/or pressure applied to the ends of the stems in a subsequent operation. The fastener elements can also be formed by cut-and-stretch techniques, such as those taught by Nestegard et al., U.S. Pat. No. 4,895,569, the contents of which are hereby incorporated by reference.
Referring to
In one useful embodiment, pre-formed material 215 is a loose knit scrim, such as Knit 3901 from Velcro USA in Manchester, N.H., although Velcro USA loop products 3900, 3905, and 3400 may also be employed. These fabrics are 2 bar tricot knit fabrics, whose technical back sides are typically brushed or napped to raise the surface floats and create a hook-engageable loop surface. Knit 3901 is a similar 2 bar Tricot knit nylon fabric which generally must be brushed or napped before it can be employed as the functioning loop of a hook and loop closure. However, it has been found to function well as a reinforcement when at least partially encapsulated by, or bonded to, the base resin contiguous with the resin forming the hooks, without brushing or napping. Reinforcing the base with such a scrim has been found to improve the stitch tear strength of the product, providing a resin-base hook product practical for attachment by sewing or stitching.
Scrim 215 has two distinct layers of yarns, creating what is referred to in the textile trades as the technical face and the technical back of the fabric. The ground and top yarns of knit scrim 215 are 40 denier multifilament yarns, each yarn comprising 12 filaments. A variety of yarn deniers are available on the market. In this application deniers from 20-170, with a variety of filament counts may be used, including monofilaments. Finer denier yarns however, are preferred for creating thinner lighter weight fabrics. Each ground and top yarn filament in this example is 3.3 denier, however a variety of filament deniers could be employed ranging from micro denier to 40 denier per filament. The ground and top yarns can be of Nylon 6 or Nylon 6.6, for example, or other textile yarn materials such as polyester or polypropylene. In this example, the ground and top yarns are of regular tenacity filaments, with tenacities of approximately 4.5 grams per denier. High tenacity yarns may provide additional tear strength for more severe applications. These yarns are also considered yarns with regular elongation. High elongation yarns or even elastomeric stretch yarns such as “Spandex” or rubber may be useful for some applications.
Scrim 215 is a Tricot warp knit, but other acceptable knits may include Rachelle, Milanese, flat, or circular knits. Knits with laid in yarns may also increase tear strength. Woven or Malimo fabrics may also be employed to some advantage. Scrim 215 is fabricated on a 2 bar warp knitter, but multi bar machines, such as a 3 bar knitter could also be used. The scrim is made on a 32 gauge warp knit machine, with 32 needles per inch of fabric width, such that the product from the machine, prior to stretching or shrinking, has approximately 32 wales per inch. Similar fabrics can be made on courser gauge machines, such as 20 or 28 gauge, or finer machines, such as 36 gauge. The scrim is constructed with 47 to 55 courses (stitches) per inch, but acceptable fabrics, made by varying the courses from 20 to 60 courses per inch, can be made as needed for the application. This course count can also be varied somewhat in final finishing by compacting or stretching the fabric on a tenter frame. The scrim has about 32 to 38 wales (ends) per inch, but could be modified to contain anywhere from 15 to 60 wales per inch, by changing the machine gauge or stretching or compacting fabric width on the tenter frame. In the final product shown, there are about 185 float segments 240 per square centimeter on the back side of the fastener tape.
In a 3 bar knit, the third yarn could be employed to form a float pattern that overlaps the float pattern of the second yarn, such that each float segment of the final product overlaps another float segment in a direction extending across the width of the fabric (i.e., with each wale being crossed by floats of each of the second and third yarns).
The technical back of the fabric could be brushed or napped to raise the float yarns 240 from the side of the fabric and lengthen the length of the float segments, to create a pile for use as a loop fastener, but for use as a reinforcement (and to keep the product advantageously thin) we prefer to leave the float yarns lying on the surface of the fabric. Thus, the scrim is preferably unnapped, with the unnapped pile yarn from the Bar 2 top beam laying on surface of the ground fabric. The unnapped pile yarn floats back and forth across the ground fabric, which is believed to improve tear strength in the final product, particularly when exposed on the back side of the laminate and not bonded against the surface of the fabric.
Longer floats are believed to improve the tear strength more than shorter floats. The length of the float is changed by modifying the motion of Bar 2. Longer floats traverse more ends of the fabric ground, bridging potential tear lines between adjacent wales. The frequency of floats in the fabric length direction can be changed by modifying the courses per inch of fabric. Increasing the stitches per inch increases the floats per inch, and can also increase the float angle ψ in relation to the wales. A float angle approaching 90 degrees is thought to provide the highest tear resistance. Decreasing the stitches per inch decreases the floats per inch. A more open knit product, with fewer stitches per inch, may have a smaller float angle, and it is thought that this construction would provide less favorable tear resistance improvement than the higher float angles. In the example shown in
As shown in
The scrim is knitted 160 inches wide and then slit into two 80-inch widths for further processing. Of course, after removal from the knitting machine, the knit tends to relax to a narrower overall width. If the scrim fabric is dyed or washed prior to finishing, the fabric width is substantially reduced due to shrinkage in wet processing and relaxation of the fabric stitch. Dyed fabrics are stretched out in width on a tenter frame approximately 45 percent as they are coated. If scrim is processed without dyeing, such shrinkage and tightening does not occur until the fabric is heated on the tenter frame. The undyed fabric in this case is stretched enough to eliminate wrinkling, and the edges are pinned to the rails on the tenter frame. The fabric passes through the oven and is coated in its pinned state. Shrinkage occurs in the oven, providing further tightening of the fabric. The scrim fabric is preferably stretched sufficiently to eliminate widthwise stretchiness in the width direction. The scrim in this example is stretched to an overall width of about 72 inches.
A stiffening agent or coating is applied to the technical face of the fabric while on the tenter frame in its stretched state. This coating aids in the processing of the fabric during lamination. The coating should be applied so as not to encapsulate the float, bind the float to the ground surface of the fabric, or make the float rigid. The coating may be applied in foam form, in a light application to minimize wicking through to the technical back of the fabric. The foam is preferably applied to the technical face of the product, such as with a parabolic applicator. A useful acrylic binder is Vinamul Duracryl 69A, available from National Starch and Chemical of Bridgewater, N.J. Applying such a binder at a rate of 0.02 to 0.03 pounds per lineal yard has been found to give the fabric sufficient stability during lamination, while not inhibiting bonding to the hook resin. In certain cases where an unstabilized, greige fabric is acceptable, uncoated scrim material may also be used. More details about methods and equipment for stabilizing lightweight fabrics with binders can be found in Shepard et al, U.S. Pat. No. 6,342,285, the contents of which are incorporated herein by reference.
The scrim fabric may be stretched sufficiently in width that the float pile yarns are reoriented to increase the float angle ψ of the exposed float yarn segments with respect to the wale direction. It is believed that this reorientation may improve tear reinforcement properties by helping to absorb energy and/or redirect tear-inducing forces in the final product. It may also be that making the floating stitches more straight and taut as laminated to the resin enables the exposed stitches to bear and redirect potentially tearing loads at much lower resin strains. The arrangement of floating stitch sections forms, in a sense, an external, textile, reinforcing skeleton for the product.
The scrim fabric is preferably laminated to the plastic hook resin with the technical face of the fabric embedded in the resin, or at least bonded to the resin by solidification of the resin in contact with surface features of the fabric, and the unnapped pile float exposed on the backside of the final product and free of the hook resin, such that the floating stitches on the technical back do not become encapsulated in the plastic, but are only held at the ends of the stitch. The central portions of the floating stitches are thus free to reorient to help carry loads that might otherwise cause local resin yielding and lead to tear propagation. The technical face of the fabric provides an effective barrier for the hook resin, keeping the resin from flooding the floats.
“Stitch Hole Tear Strength” is measured according to the following test method, on un-engaged fastener components. A line of holes is made along the center of width of each eight-inch by one-inch test sample, with a 0.044 inch, medium ball needle, at a stitch rate of 11 to 13 stitch holes per inch, without thread, starting around three inches from a first end of the sample. The sample is then conditioned for at least 20 hours at 69.8 to 77 degrees Fahrenheit and 45 to 55 percent relative humidity. A straight line is cut from the first end of the sample to the nearest hole, forming two separate tabs. The sample is then held by the tabs and torn by moving the two tabs apart by motion within the plane of the sample and perpendicular to the line of holes, at a separation speed of 11.5 to 12.5 inches per minute, until the sample exhibits a total tear length of about five inches. Disregarding data from the first and last 12-second period of the loading, the five highest load peaks are averaged and reported to the nearest 0.1 pound increment.
A number of embodiments of the invention have been described. Nevertheless, it will be understood that various modifications may be made without departing from the spirit and scope of the invention. Accordingly, other embodiments are within the scope of the following claims.
Number | Name | Date | Kind |
---|---|---|---|
3387345 | Savoir | Jun 1968 | A |
3426363 | Girard | Feb 1969 | A |
4165555 | Boxer et al. | Aug 1979 | A |
4402690 | Redfern | Sep 1983 | A |
4410327 | Baggaley | Oct 1983 | A |
4770917 | Tochacek et al. | Sep 1988 | A |
4870725 | Dubowik | Oct 1989 | A |
4984339 | Provost et al. | Jan 1991 | A |
5176670 | Roessler et al. | Jan 1993 | A |
5260015 | Kennedy et al. | Nov 1993 | A |
5318741 | Thomas | Jun 1994 | A |
5325569 | Goulait et al. | Jul 1994 | A |
5326415 | Thomas et al. | Jul 1994 | A |
5326612 | Goulait | Jul 1994 | A |
5368549 | McVicker | Nov 1994 | A |
5369852 | Higashinaka | Dec 1994 | A |
5369853 | Okawa et al. | Dec 1994 | A |
5392498 | Goulait et al. | Feb 1995 | A |
5399177 | Blaney et al. | Mar 1995 | A |
5399418 | Hartmanns et al. | Mar 1995 | A |
5518795 | Kennedy et al. | May 1996 | A |
5540673 | Thomas et al. | Jul 1996 | A |
5607345 | Barry et al. | Mar 1997 | A |
5615460 | Weirich et al. | Apr 1997 | A |
5620769 | Wessels et al. | Apr 1997 | A |
5655268 | Keyaki et al. | Aug 1997 | A |
5669120 | Wessels et al. | Sep 1997 | A |
5688579 | Konsti et al. | Nov 1997 | A |
5744080 | Kennedy et al. | Apr 1998 | A |
5845375 | Miller et al. | Dec 1998 | A |
5851467 | Murasaki | Dec 1998 | A |
5974635 | Murasaki | Nov 1999 | A |
5985407 | Murasaki | Nov 1999 | A |
6039911 | Miller et al. | Mar 2000 | A |
6131251 | Provost | Oct 2000 | A |
6143222 | Takizawa et al. | Nov 2000 | A |
6163939 | Lacey et al. | Dec 2000 | A |
6174476 | Kennedy et al. | Jan 2001 | B1 |
6248419 | Kennedy et al. | Jun 2001 | B1 |
6332250 | Igaue et al. | Dec 2001 | B1 |
6484371 | Romanko et al. | Nov 2002 | B1 |
6737147 | Kennedy et al. | May 2004 | B2 |
6849142 | Goulait | Feb 2005 | B1 |
Number | Date | Country |
---|---|---|
2 786 372 | Jun 2000 | FR |
Number | Date | Country | |
---|---|---|---|
20050081342 A1 | Apr 2005 | US |