Patent Application
20130040227
This disclosure relates to a Pt—Ni catalyst which demonstrates an unusually high oxygen reduction mass activity. The catalyst may be particularly useful as a fuel cell catalyst and more specifically as a fuel cell cathode catalyst.
U.S. Pat. No. 5,879,827, the disclosure of which is incorporated herein by reference, discloses nanostructured elements comprising acicular microstructured support whiskers bearing acicular nanoscopic catalyst particles. The catalyst particles may comprise alternating layers of different catalyst materials which may differ in composition, in degree of alloying or in degree of crystallinity.
U.S. Pat. No. 6,482,763, the disclosure of which is incorporated herein by reference, discloses fuel cell electrode catalysts comprising alternating platinum-containing layers and layers containing suboxides of a second metal that display an early onset of CO oxidation.
U.S. Pat. Nos. 5,338,430, 5,879,828, 6,040,077 and 6,319,293, the disclosures of which are incorporated herein by reference, also concern nanostructured thin film catalysts.
U.S. Pat. Nos. 4,812,352, 5,039,561, 5,176,786, and 5,336,558, the disclosures of which are incorporated herein by reference, concern microstructures.
U.S. Pat. No. 7,419,741, the disclosure of which is incorporated herein by reference, discloses fuel cell cathode catalysts comprising nanostructures formed by depositing alternating layers of platinum and a second layer onto a microstructure support, which may form a ternary catalyst.
U.S. Pat. No. 7,622,217, the disclosure of which is incorporated herein by reference, discloses fuel cell cathode catalysts comprising microstructured support whiskers bearing nanoscopic catalyst particles comprising platinum and manganese and at least one other metal at specified volume ratios and Mn content, where other metal is typically Ni or Co.
This disclosure relates to a Pt—Ni catalyst which demonstrates an unusually high oxygen reduction mass activity. In some embodiments, the Pt—Ni catalyst is a Pt—Ni binary alloy. In some embodiments, the catalyst may be characterized as having a Pt fcc lattice parameter of less than 3.71 Angstroms or 0.371 nm. In some embodiments the catalyst has a Pt fcc lattice parameter of less than 3.72 Angstroms or 0.372 nm. In some embodiments the catalyst has a Pt fcc lattice parameter of less than 3.73 Angstroms or 0.373 nm. In some embodiments the catalyst has a Pt fcc lattice parameter of between 3.69 Angstroms (or 0.369 nm) and 3.73 Angstroms (or 0.373 nm). In some embodiments the catalyst has a Pt fcc lattice parameter of between 3.70 Angstroms (or 0.370 nm) and 3.72 Angstroms (or 0.372 nm). In some embodiments, the catalyst may be characterized as having a composition of close to PtxNi(1-x), where x is between 0.2 and 0.4. In some embodiments x is between 0.21 and 0.34. In some embodiments x is between 0.22 and 0.38. In some embodiments x is between 0.22 and 0.33. In some embodiments x is between 0.26 and 0.33. In some embodiments x is between 0.28 and 0.32.
In some embodiments the catalyst comprises nanostructured elements comprising microstructured support whiskers bearing a thin film of nanoscopic catalyst particles comprising a catalyst material described above.
The catalyst may be particularly useful as a fuel cell catalyst and more specifically as a fuel cell cathode catalyst.
In this application:
“membrane electrode assembly” means a structure comprising a membrane that includes an electrolyte, typically a polymer electrolyte, and at least one but more typically two or more electrodes adjoining the membrane;
“nanostructured element” means an acicular, discrete, microscopic structure comprising a catalytic material on at least a portion of its surface;
“nanoscopic catalyst particle” means a particle of catalyst material having at least one dimension equal to or smaller than about 15 nm or having a crystallite size of about 15 nm or less, as measured from diffraction peak half widths of standard 2-theta x-ray diffraction scans;
“thin film of nanoscopic catalyst particles” includes films of discrete nanoscopic catalyst particles, films of fused nanoscopic catalyst particles, and films of nanoscopic catalyst grains which are crystalline or amorphous; typically films of discrete or fused nanoscopic catalyst particles, and most typically films of discrete nanoscopic catalyst particles;
“acicular” means having a ratio of length to average cross-sectional width of greater than or equal to 3;
“discrete” refers to distinct elements, having a separate identity, but does not preclude elements from being in contact with one another;
“microscopic” means having at least one dimension equal to or smaller than about a micrometer;
“planar equivalent thickness” means, in regard to a layer distributed on a surface, which may be distributed unevenly, and which surface may be an uneven surface (such as a layer of snow distributed across a landscape, or a layer of atoms distributed in a process of vacuum deposition), a thickness calculated on the assumption that the total mass of the layer was spread evenly over a plane covering the same area as the projected area of the surface (noting that the projected area covered by the surface is less than or equal to the total surface area of the surface, once uneven features and convolutions are ignored);
“bilayer planar equivalent thickness” means the total planar equivalent thickness of a first layer (as described herein) and the next occurring second layer (as described herein).
It is an advantage of the present disclosure to provide catalysts for use in fuel cells.
The present disclosure provides a Pt—Ni catalyst which demonstrates an unusually high oxygen reduction mass activity. In some embodiments, the catalyst may be characterized as having Pt fcc lattice parameter of less than 3.71 Angstroms. In some embodiments, the catalyst may be characterized as having a composition of close to PtxNi(1-x), where x is between 0.2 and 0.4. The catalyst may be particularly useful as a fuel cell catalyst and more specifically as a fuel cell cathode catalyst.
This disclosure describes a specific Pt alloy crystal structure and lattice parameter that gives a significant increase in oxygen reduction activity when used as a fuel cell cathode catalyst. The activity with a PtNi alloy having a high atomic percentage of Ni is seen to dramatically increase as the atomic percentage changes over a very small range of about 60% to about 65% as measured by electron microprobe, or 65% to about 73% as measured gravimetrically (preferred), or 73% to about 78% as determined by X-ray fluorescence, and the fcc lattice parameter drops below 3.71 Angstroms. The low value of the lattice parameter is believed to be critical.
This disclosure, demonstrated with a PtNi binary alloy, allows the oxygen reduction activity to be doubled over standard catalyst compositions, e.g., NSTF Pt68.7Co28.5Mn2.7 ternary catalyst. The current mass activity value measured with the new PtNi alloy at a lattice parameter of ˜3.71 Angstroms, is 0.32 A/mgPt, using only 0.10 mgPt/cm2.
This disclosure has the potential to double the current best NSTF catalyst ORR activity, thereby directly improving high current density performance and ultimately the stack size and costs, the operating efficiency at low power operating conditions and hence vehicle fuel efficiency, and indirectly affect other factors such as water management and break-in conditioning.
Objects and advantages of this disclosure are further illustrated by the following examples, but the particular materials and amounts thereof recited in these examples, as well as other conditions and details, should not be construed to unduly limit this disclosure.
Unless otherwise noted, all reagents were obtained or are available from Aldrich Chemical Co., Milwaukee, Wis., or may be synthesized by known methods.
Pt binary and ternary alloys of varying compositions described below were made by sputter deposition of individual multi-layers of the respective elements onto NSTF whisker support films, as described in the prior art cited above, e.g., U.S. Pat. No. 7,419,741. The catalysts were applied to proton exchange membranes having an equivalent weight of approximately 850, and a thickness of 20 microns. On the anode side, the catalyst loading was generally 0.05 or 0.1 mg-Pt/cm2 of PtCoMn in the composition Pt68.7Co28.5Mn2.7. On the cathode side, the Pt loading in the various alloys was 0.10 mg/cm2 for most of the data below, and 0.15 mg/cm2 of Pt for four of the PtNi examples. The catalysts were transferred to the surface of the membrane by hot roll lamination, and the subsequent catalyst coated membranes tested in 50 cm2 fuel cells after addition of gas diffusion layers. The cathode catalysts' activities for oxygen reduction were measured according to protocols specified by the Dept. of Energy.
The catalyst alloy compositions were determined by multiple methods, including the initial sputter deposition calibration files (designated as gravimetric in
The catalyst alloy structural properties were measure by X-ray diffraction (XRD) before the catalysts were applied to the membranes and tested in fuel cells.
Various modifications and alterations of this disclosure will become apparent to those skilled in the art without departing from the scope and principles of this disclosure, and it should be understood that this disclosure is not to be unduly limited to the illustrative embodiments set forth hereinabove.
This invention was made with Government support under Cooperative Agreement DE-FG36-07G017007 awarded by DOE. The Government has certain rights in this invention.
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/US11/33949 | 4/26/2011 | WO | 00 | 10/25/2012 |
| Number | Date | Country | |
|---|---|---|---|
| 61328049 | Apr 2010 | US |