Patent Application
20130108817
The invention relates to compositions for producing polymethacrylimide foams (PMI foams) with particularly good mechanical properties, in particular with particularly advantageous tensile strain at break. The invention further relates to processes for production thereof, processing and use of the said foams. The invention in particular relates to novel materials which have markedly reduced tendency toward cracking when comparison is made with the prior art. This is equivalent to higher tensile strain at break when comparison is made with the prior art.
PMI foams, e.g. ROHACELL® from Evonik Röhm, are used as structural foam in composites and to this end are processed together with outer layers composed of fibres, mostly carbon fibres or glass fibres, and resins. The composites are often constructed at temperatures of 180° C., while the component is also intended for use at temperatures of −55° C. The different coefficients of thermal expansion (CTEs) of the outer layer and of the PMI foams produce cracks in the core on cooling, and this is a criterion that excludes the use of PMI foams in components of this type. The materials usually fail corresponding airline industry tests. There is therefore a high level of interest in foam materials with improved tensile strain at break, not only in processing industries such as the aerospace industry but also among producers of road vehicles or rail vehicles.
PMI foams have been known for a long time. The said foams with trademark ROHACELL® are used in particular in many applications in the sector of layer materials (laminates, composites, foam-composite products, sandwich structures, sandwich materials). Layer materials are mouldings composed of an external outer layer and of an internal core material. The outer layers used comprise materials which can tolerate extremely high tensile forces, monoaxially or multiaxially. Examples are glass textile and carbon-fibre textile, and also aluminium sheets, fixed to the core material by adhesive resins. Core materials used preferably comprise materials with low densities, typically in the range of 30 kg/m3 and 200 kg/m3.
Isotropic foams of this type are capable of tolerating shear forces in all spatial directions. An advantage is easy mechanical working by the tooling and machinery conventionally used for wood. Certain rigid foams, e.g. ROHACELL®, can moreover be thermoformed. A considerable advantage of closed-pore rigid foams is that penetration of resin, which would increase total weight, is prevented. DE2726260 describes the production of PMI foams which have excellent mechanical properties, even at high temperatures. The foams are produced by the casting process, i.e. monomers and necessary additives are mixed and polymerized in a cell. In a second step, the polymer is foamed by heating. However, these standard materials do not exhibit particularly high tensile strain at break.
Mechanically stable PMI foams crosslinked with allyl methacrylate are found in EP 356714. Again, these very strong foams exhibit only very low tensile strain at break. The same applies to the PMI foams which are disclosed in JP 2006 045532, crosslinked ionically by metal salts.
One particular field of development in recent years involves fine-pore foams based on PMI. These are described by way of example in EP 532023. However, the process described in that document has various serious disadvantages. The resultant foams, free from crosslinking agent, have only low heat resistance, and poor creep performance.
Fine-pore foams with crosslinking agent are likewise known and are found in EP 1 678 244. The said fine-pore materials can have tensile strain at break of up to 5.5%. It is possible to achieve fine-pore character via variation of blowing agents or by adding insoluble nucleating agents. The use of insoluble nucleating agents can produce relatively fine-pore materials, but the said nucleating agents require the use of antisettling agents, with attendant increased production cost. However, there have been no small-pore foams described with ultimate tensile strengths greater than 5.5%.
The only known solution to the problem of inadequate tensile strain at break was provided by the product ROHACELL® FX. The plasticizing effect in the said product was due to increased water absorption resulting from an additive system. However, PMI foams with high water content also exhibit marked impairment of mechanical or thermomechanical properties.
CN 100420702 describes PMI foams based on acrylonitrile. Although these exhibit good values for ultimate tensile strength, at the same time they exhibit a slightly reduced level of thermomechanical properties.
It was therefore an object of the present invention to find formulations for the production of PMI foams with particularly high ultimate tensile strength. The foams are moreover intended to have equally good or even improved thermomechanical properties, when comparison is made with the known PMI foams.
A particular object was to provide PMI foams with tensile strain at break values greater than 6.0%, very particularly greater than 9.0%.
Another object of the present invention was to provide PMI foams with reduced cracking. The said reduced cracking is to be ensured especially in the temperature range from −60° C. to 200° C.
The objects are achieved via a novel process for producing foamable crosslinked polymers, in particular of PMI foams, where the polymer comprises (meth)acrylic acid, (meth)acrylonitrile and a (meth)acrylic diester of a diol which has a molar mass of at least 250 g/mol.
In particular, the mixture for producing the polymer in the process according to the invention is composed at least of from 30 to 70% by weight of (meth)acrylic acid, from 30 to 60% by weight of (meth)acrylonitrile, from 0.01 to 15% by weight of (meth)acrylic diester of a diol which has a molar mass of at least 250 g/mol, from 0.01 to 15% by weight of blowing agent and from 0.01 to 2.0% by weight of polymerization initiators.
The expression (meth)acrylic acid means methacrylic acid, acrylic acid or a mixture of the two. The expression (meth) acrylonitrile means methacrylonitrile, acrylonitrile or a mixture of the two. An expression such as alkyl (meth)acrylate has a corresponding meaning. It means the alkyl ester of methacrylic acid, of acrylic acid or of a mixture of the two.
The diol from which the (meth)acrylic diester is formed is a polyetherdiol, a polyesterdiol, an OH-functional oligo(meth)acrylic telechelic compound or a polyolefindiol, preferably a polyetherdiol. The (meth)acrylic diesters can be produced from the diols by way of known processes, such as transesterification with (meth)acrylic esters or esterification with (meth)acrylic acid or with (meth)acryloyl halides.
The diols have a minimum molar mass of 250 g/mol, preferably of 400 g/mol. The maximum molar mass of the diols is 5000 g/mol, preferably 2000 g/mol and particularly preferably 1500 g/mol.
The polyetherdiols can involve polyethylene oxide, polypropylene oxide, polymethylene oxide or polytetrahydrofuran.
The polyesterdiols preferably involve short-chain amorphous polyesterdiols, produced from diacids and from diols, or involve polyesterdiols, where these can be produced by way of a ring-opening polymerization reaction, an example being polylactide or polyglycolide, or involve polylactic acid.
Oligo(meth)acrylate telechelic compounds are available by way of example by way of a controlled free-radical polymerization reaction, for example atom transfer radical polymerization (ATRP).
The polyolefins that can be used according to the invention are non-crystalline, short-chain polyolefins, such as atactic polypropylene, polybutadiene, hydrogenated polybutadiene, EPDM, EPM or APAOS (amorphous poly-alpha-polyolefins).
An initially low level of crosslinking stabilizes the PMI foam during the foaming procedure, thus permitting the production of homogeneous foams. At the same time, the heat resistance and the creep performance of the foam are improved by crosslinking agents. Surprisingly, it has been found that when the crosslinking agents used are exclusively or to some extent long-chain compounds, the resultant PMI foams have particularly good tensile strain at break. The creep performance (creep) is measured according to the invention in compliance with DIN 53425, ASTM D621 and D2990 at 180° C., with a measurement time of two hours and with a suitable pressure that depends on the density of the material.
The process according to the invention provides further advantages in comparison with the processes of the prior art:
Blowing agents that can be used comprise the following compounds and mixtures thereof: formamide, formic acid, urea, itaconic acid, citric acid, dicyandiamide, water, monoalkylureas, dimethylurea, 5,5′-azobis-5-ethyl-1,3-dioxane, 2,2′-azobis(N-butylisobutyramide), 2,2′-azobis(N-diethylisobutyramide), 2,2′,4,4,4′,4′-hexamethyl-2,2′-azopentane, 2,2′-azobis(2-methylpropane), dimethyl carbonate, di-tert-butyl carbonate, acetone cyanohydrin carbonate, methyl oxyisobutyrate carbonate, N-methylurethane, N-ethylurethane, N-tert-butylurethane, urethane, oxalic acid, maleic acid, oxyisobutyric acid, malonic acid, cyanoformamide, dimethylmaleic acid, tetraethyl methanetetracarboxylate, N-butyl oxamate, trimethyl methanetricarboxylate, triethyl methanetricarboxylate, and also monohydric alcohols composed of from 3 to 8 carbon atoms, e.g. 1-propanol, 2-propanol, 1-butanol, 2-butanol, tert-butanol and isobutanol.
The initiators used comprise compounds and initiator systems which can initiate free-radical polymerization reactions. Known classes of compound are peroxides, hydroperoxides, peroxodisulphates, percarbonates, perketals, peroxyesters, hydrogen peroxide and azo compounds. Examples of initiators are hydrogen peroxide, dibenzoyl peroxide, dicyclohexyl peroxodicarbonate, dilauroyl peroxide, methyl ethyl ketone peroxide, acetylacetone peroxide, di-tert-butyl peroxide, tert-butyl hydroperoxide, cumene hdyroperoxide, tert-butyl peroctanoate, tert-butyl 2-ethylperhexanoate, tert-butyl perneodecanoate, tert-amyl perpivalate, tert-butyl perpivalate, tert-butyl perbenzoate, lithium peroxodisulphate, sodium peroxodisulphate, potassium peroxodisulphate and ammonium peroxodisulphate, azoisobutyronitrile, 2,2-azobisiso-2,4-dimethylvaleronitrile, 2,2-azobisisobutyronitrile, 2,2′-azobis(2-amidinopropane) dihydrochloride, 2-(carbamoylazo)isobutyronitrile and 4,4′-azobis(cyanovaleric acid). Redox initiators (H. Rauch-Puntigam, Th. Völker, Acryl—and Methacrylverbindungen [Acrylic and methacrylic compounds], Springer, Heidelberg, 1967 or Kirk-Othmer, Encyclopedia of Chemical Technology, Vol. 1, pp. 286 ff., John Wiley & Sons, New York, 1978) are equally suitable. It can be advantageous to combine initiators and initiator systems with different decomposition properties in respect of time and temperature. The amounts preferably used of the initiators are from 0.01 to 2% by weight, particularly from 0.15 to 1.5% by weight, based on the total weight of the monomers.
The mixture can moreover comprise from 0 to 35% by weight of other vinylically unsaturated monomers, from 0 to 10% by weight of another crosslinking agent and from 0 to 20% by weight of conventional additives. According to the invention, the mixture is polymerized in bulk to give a sheet. This can take place batchwise in the cell process or continuously by charging or extruding the material into suitable tooling for shaping processes.
Examples of the other vinylically unsaturated monomers are: acrylic or methacrylic acid, and also esters thereof with lower alcohols having from 1 to 4 carbon atoms, styrene, maleic acid or its anhydride, itaconic acid or its anhydride, vinylpyrrolidone, vinyl chloride and/or vinylidene chloride. The proportion of the comonomers which cannot be cyclized to give anhydride or imide, or which are very difficult to cyclize to give anhydride or imide, is not to exceed 30% by weight, preferably 20% by weight and particularly preferably 10% by weight, based on the weight of the monomers.
The other crosslinking agents that can be used alongside the (meth)acrylic diesters of the long-chain diols can be divided into two groups: covalent crosslinking agents (D1), i.e. copolymerizable polyunsaturated compounds. Examples of monomers of this type that may be used are allyl acrylate, allyl methacrylate, allylacrylamide, allylmethacrylamide, methylenebis(meth)acrylamide, diethylenebis(allyl carbonate), ethylene glycol diacrylate or ethylene glycol dimethacrylate, diethylene glycol diacrylate or diethylene glycol dimethacrylate, triethylene glycol diacrylate or triethylene glycol dimethacrylate, tetraethylene glycol diacrylate or tetraethylene glycol dimethacrylate, tripropylene glycol diacrylate or tripropylene glycol dimethacrylate, 1,3-butanediol diacrylate or 1,3-butanediol dimethacrylate, 1,4-butanediol diacrylate or 1,4-butanediol dimethacrylate, neopentyl diol diacrylate or neopentyl diol dimethacrylate, hexane-1,6-diol diacrylate or hexane-1,6-diol dimethacrylate, trimethylolpropane diacrylate or trimethylolpropane dimethacrylate, trimethylolpropane triacrylate or trimethylolpropane trimethacrylate, pentaerythritol triacrylate or pentaerythritol trimethacrylate, pentaerythritol tetraacrylate or pentaerythritol tetramethacrylate, the pentaerythritol derivatives derived from respective tri- and tetrafunctional compounds, optionally also in the form of technical mixture, and also triallyl cyanurate or triallyl isocyanurate. Ionic crosslinking agents (D2) are another group that can be used. These are polyvalent metal cations which form ionic bridges between the acid groups of the copolymers. Examples are inter alia the acrylates or methacrylates of the alkaline earth metals or of zinc. Preference is given to Zn (meth)acrylate and to Mg (meth)acrylate. The (meth)acrylate salts can also be produced by dissolving, for example, ZnO or MgO in the monomer mixture.
The conventional additives can by way of example involve antistatic agents, antioxidants, demoulding aids, lubricants, dyes, flame retardants, flow improvers, fillers, light stabilizers and organophosphorus compounds, such as phosphites or phosphonates, pigments, release agents, weathering stabilizers and/or plasticizers.
The mixture used for the production of foamable crosslinked polymers via polymerization in bulk to give a sheet in the process according to the invention preferably involves a mixture of from 30 to 70% by weight of methacrylic acid, from 30 to 60% by weight of methacrylonitrile, from 0.01 to 15% by weight of a methacrylic diester of a diol which has a molar mass of at least 250 g/mol, where this in particular involves a polyether dimethacrylate, from 0.01 to 15% by weight of blowing agent, from 0.01 to 10% by weight of another crosslinking agent, from 0.01 to 2% by weight of polymerization initiators and from 0 to 30% by weight of other vinylically unsaturated monomers, and also from 0 to 20% by weight of conventional additives.
After the polymerization of the mixture in bulk to give a sheet, the polymer is optionally heat-conditioned and then foamed at temperatures of from 150 to 250° C.
The present invention equally provides the poly(meth)acrylimide foam which is obtained by foaming of the polymer described. The tensile strain at break of the said PMI foam according to ISO 527-2 is greater than 7,0%, in particular greater than 9.0% and particularly preferably greater than 10.0%.
The foams according to the invention can then be processed to give layer materials. The said layer materials comprise a layer of the PMI foam in a layer which is preferably central, surrounded by unfoamed polymers or by other materials, such as textiles or wood.
The foams or the layer materials produced therefrom can by way of example be included in the structure of the following: tubes, loudspeakers, antennas, X-ray tables, machine parts, motor vehicles, rail vehicles, watercraft, aircraft, spacecraft.
The examples given below are provided for illustration of the present invention, but do not restrict the invention to the features disclosed herein.
Tensile strain at break and ultimate tensile strength were determined by means of tensile tests according to ISO 527-2.
Density is measured according to ISO 845.
Heat resistance was determined according to DIN 53424.
Creep performance (creep) was measured in compliance with DIN 53425, and ASTM D621 and D2990 at 180° C., with a measurement time of two hours and a pressure of 0.7 MPa.
355 g of tert-butanol were added as blowing agent to a mixture of 2487 g of metahcrylic acid, 2538 g of methacrylonitrile and 102 g of tert-butyl methacrylate. 2 g of tert-butyl perpivalate, 1.8 g of tert-butyl 2-ethylperhexanoate, 5.1 g of tert-butyl perbenzoate, 5.2 g of cumyl perneodecanoate, 11.2 g of magnesium oxide and 15.2 g of release agent (Moldwiz INT 20E) were also added to the mixture. 77.2 g of methacrylic diester of polyethylene glycol 400 were added as crosslinking agent.
The said mixture was polymerized for 89 h at 39° C. in a cell formed from two glass plates measuring 50×50 cm with a peripheral seal of thickness 28 mm. For the final polymerization reaction, the polymer was then subjected to a heat-conditioning programme extending from 40° C. to 115° C., for 32 h.
The subsequent foaming by the hot-air process took 2 h at 217° C. The density of the resultant foam is 105 kg/m3. Tensile strain at break is 7.2% and ultimate tensile strength is 6.0 MPa. The creep test at 0.7 MPa (2 h/180° C.) is passed at 0.07% compaction. A further specimen was foamed at 205° C. for 2 h. The density of the resultant foam is 145 kg/m3. Tensile strain at break is 8.3% and ultimate tensile strength is 9.0 MPa.
593 g of tert-butanol were added as blowing agent to a mixture of 2421 g of methacrylic acid and 2471 g of methacrylonitrile. 2 g of tert-butyl perpivalate, 1.8 g of tert-butyl 2-ethylperhexanoate, 4.9 g of tert-butyl perbenzoate, 5.1 g of cumyl perneodecanoate, 10.9 g of magnesium oxide and 14.8 g of release agent (Moldwiz INT 20E) were also added to the mixture. 75.1 g of methacrylic diester of polyethylene glycol 400 were added as crosslinking agent.
The said mixture was polymerized for 118 h at 39° C. in a cell formed from two glass plates measuring 50×50 cm with a peripheral seal of thickness 28 mm. For the final polymerization reaction, the polymer was then subjected to a heat-conditioning programme extending from 40° C. to 115° C., for 32 h.
The subsequent foaming by the hot-air process took 2 h at 188° C. The density of the resultant foam was 150 kg/m3. Tensile strain at break is 9.7% and ultimate tensile strength is 9.1 MPa. The creep test at 0.7 MPa (2 h/180° C.) is reliably passed at 0.36% compaction.
340 g of tert-butanol were added as blowing agent to a mixture of 2379 g of methacrylic acid, 2428 g of methacrylonitrile and 97 g of tert-butyl methacrylate. 1.9 g of tert-butyl perpivalate, 1.8 g of tert-butyl 2-ethylperhexanoate, 4.8 g of tert-butyl perbenzoate, 5.0 g of cumyl perneodecanoate, 10.7 g of magnesium oxide and 14.5 g of release agent (Moldwiz INT 20E) were also added to the mixture. 73.8 g of methacrylic diester of polyethylene glycol 400 were added as crosslinking agent.
The said mixture was polymerized for 90 h at 39° C. in a cell formed from two glass plates measuring 50×50 cm with a peripheral seal of thickness 28 mm. For the final polymerization reaction, the polymer was then subjected to a heat-conditioning programme extending from 40° C. to 115° C., for 32 h.
The subsequent foaming by the hot-air process took 2 h at 212° C. The density of the resultant foam was 99 kg/m3. Tensile strain at break is 13.0% and ultimate tensile strength is 6.0 MPa. A further specimen was foamed at 210° C. for 2 h. The density of the resultant foam was 114 kg/m3. The creep test at 0.7 MPa (2 h/180° C.) was reliably passed, with compaction of only 0.45%.
360 g of tert-butanol were added as blowing agent to a mixture of 2520 g of methacyrlic acid, 2572 g of methacrylonitrile and 103 g of tert-butyl methacrylate. 2.1 g of tert-butyl perpivalate, 1.9 g of tert-butyl 2-ethylperhexanoate, 5.1 g of tert-butyl perbenzoate, 5.3 g of cumyl perneodecanoate, 10.3 g of magnesium oxide and 15.4 g of release agent (Moldwiz INT 20E) were also added to the mixture. 5.1 g of allyl methacrylate were added as crosslinking agent.
The said mixture was polymerized for 88 h at 39° C. in a cell formed from two glass plates measuring 50×50 cm with a peripheral seal of thickness 28 mm. For the final polymerization reaction, the polymer was then subjected to a heat-conditioning programme extending from 40° C. to 120° C., for 32 h.
The subsequent foaming by the hot-air process took 2 h at 200° C. The density of the resultant foam is 114 kg/m3.
Tensile strain at break is 5.5% and ultimate tensile strength is 3.7 MPa. A further specimen was foamed at 190° C. for 2 h. The density of the resultant foam is 148 kg/m3. Tensile strain at break is 5.4% and ultimate tensile strength is 7.6 MPa.
| Number | Date | Country | Kind |
|---|---|---|---|
| 10 2010 040 010.6 | Aug 2010 | DE | national |
| 10 2010 040 286.9 | Sep 2010 | DE | national |
| Filing Document | Filing Date | Country | Kind | 371c Date |
|---|---|---|---|---|
| PCT/EP2011/060888 | 6/29/2011 | WO | 00 | 1/4/2013 |