Patent Application
20180154696
It is highly desirable for tires to have good wet skid resistance, low rolling resistance, and good wear characteristics. It has traditionally been very difficult to improve a tire's wear characteristics without sacrificing its wet skid resistance and traction characteristics. These properties depend, to a great extent, on the dynamic viscoelastic properties of the rubbers utilized in making the tire.
In order to reduce the rolling resistance and to improve the treadwear characteristics of tires, rubbers having a high rebound have traditionally been utilized in making tire tread rubber compounds. On the other hand, in order to increase the wet skid resistance of a tire, rubbers which undergo a large energy loss have generally been utilized in the tire's tread. In order to balance these two viscoelastically inconsistent properties, mixtures of various types of synthetic and natural rubber are normally utilized in tire treads.
Tires are sometimes desired with treads for promoting traction on snowy surfaces. Various rubber compositions may be proposed for tire treads. Here, the challenge is to reduce the cured stiffness of such tread rubber compositions, as indicated by having a lower storage modulus G′ at −20° C., when the tread is intended to be used for low temperature winter conditions, particularly for vehicular snow driving.
It is considered that significant challenges are presented for providing such tire tread rubber compositions for maintaining both their wet traction while promoting low temperature (e.g. winter) performance.
The present invention is directed to a pneumatic tire having a tread comprising a tread base layer and an outer cap layer disposed radially outward of the base layer,
the outer cap layer comprising an axially central zone and two lateral zones each disposed axially adjacent to the central zone;
the central zone comprising a central zone composition and lateral zones each comprising a lateral zone composition;
the central zone composition and the lateral zone composition each comprising, based on 100 parts by weight of elastomer (phr),
from about 50 to about 90 phr of a solution polymerized styrene-butadiene rubber having a glass transition temperature (Tg) ranging from −65° C. to −55° C. and functionalized with an alkoxysilane group and at least one functional group selected from the group consisting of primary amines and thiols;
from about 50 to about 10 phr of polybutadiene having a cis 1,4 content greater than 95 percent and a Tg ranging from −80 to −110° C.;
from 100 to 180 phr of precipitated silica; and
from 30 to 80 phr of a combination of a resin having a Tg of at least 30° C. and an oil wherein the weight ratio of the amount of silica to the total amount of resin and oil is less than 3;
wherein the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 2.
There is disclosed a pneumatic tire having a tread comprising a tread base layer and an outer cap layer disposed radially outward of the base layer,
the outer cap layer comprising an axially central zone and two lateral zones each disposed axially adjacent to the central zone;
the central zone comprising a central zone composition and lateral zones each comprising a lateral zone composition;
the central zone composition and the lateral zone composition each comprising, based on 100 parts by weight of elastomer (phr),
from about 50 to about 90 phr of a solution polymerized styrene-butadiene rubber having a glass transition temperature (Tg) ranging from −65° C. to −55° C. and functionalized with an alkoxysilane group and at least one functional group selected from the group consisting of primary amines and thiols;
from about 50 to about 10 phr of polybutadiene having a cis 1,4 content greater than 95 percent and a Tg ranging from −80 to −110° C.;
from 100 to 180 phr of precipitated silica; and
from 30 to 80 phr of a combination of a resin having a Tg of at least 30° C. and an oil wherein the weight ratio of the amount of silica to the total amount of resin and oil is less than 3;
wherein the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 2.
With reference now to
With reference to
The rubber compositions of the outer cap layer, including both the central zone composition and lateral zone composition, and the inner cap layer include from 50 to 90 phr of a styrene-butadiene rubber functionalized with an alkoxysilane group and at least one of a primary amine group and thiol group. In one embodiment, the styrene-butadiene rubber is obtained by copolymerizing styrene and butadiene, and characterized in that the styrene-butadiene rubber has a primary amino group and/or thiol group and an alkoxysilyl group which are bonded to the polymer chain. In one embodiment, the alkoxysilyl group is an ethoxysilyl group.
The primary amino group and/or thiol group may be bonded to any of a polymerization initiating terminal, a polymerization terminating terminal, a main chain of the styrene-butadiene rubber and a side chain, as long as it is bonded to the styrene-butadiene rubber chain. However, the primary amino group and/or thiol group is preferably introduced to the polymerization initiating terminal or the polymerization terminating terminal, in that the disappearance of energy at a polymer terminal is inhibited to improve hysteresis loss characteristics.
Further, the content of the alkoxysilyl group bonded to the polymer chain of the (co)polymer rubber is preferably from 0.5 to 200 mmol/kg of (styrene-butadiene rubber. The content is more preferably from 1 to 100 mmol/kg of styrene-butadiene rubber, and particularly preferably from 2 to 50 mmol/kg of styrene-butadiene rubber.
The alkoxysilyl group may be bonded to any of the polymerization initiating terminal, the polymerization terminating terminal, the main chain of the (co)polymer and the side chain, as long as it is bonded to the (co)polymer chain. However, the alkoxysilyl group is preferably introduced to the polymerization initiating terminal or the polymerization terminating terminal, in that the disappearance of energy is inhibited from the (co)polymer terminal to be able to improve hysteresis loss characteristics.
The styrene-butadiene rubber can be produced by polymerizing styrene and butadiene in a hydrocarbon solvent by anionic polymerization using an organic alkali metal and/or an organic alkali earth metal as an initiator, adding a terminating agent compound having a primary amino group protected with a protective group and/or a thiol group protected with a protecting group and an alkoxysilyl group to react it with a living polymer chain terminal at the time when the polymerization has substantially completed, and then conducting deblocking, for example, by hydrolysis or other appropriate procedure. In one embodiment, the styrene-butadiene rubber can be produced as disclosed in U.S. Pat. No. 7,342,070. In another embodiment, the styrene-butadiene rubber can be produced as disclosed in WO 2007/047943.
In one embodiment, and as taught in U.S. Pat. No. 7,342,070, the styrene-butadiene rubber is of the formula (I) or (II)
wherein P is a (co)polymer chain of a conjugated diolefin or a conjugated diolefin and an aromatic vinyl compound, R1 is an alkylene group having 1 to 12 carbon atoms, R2 and R3 are each independently an alkyl group having 1 to 20 carbon atoms, an allyl group or an aryl group, n is an integer of 1 or 2, m is an integer of 1 or 2, and k is an integer of 1 or 2, with the proviso that n+m+k is an integer of 3 or 4,
wherein P, R1, R2 and R3 have the same definitions as give for the above-mentioned formula I, j is an integer of 1 to 3, and h is an integer of 1 to 3, with the provision that j+h is an integer of 2 to 4.
The terminating agent compound having a protected primary amino group and an alkoxysilyl group may be any of various compounds as are known in the art. In one embodiment, the compound having a protected primary amino group and an alkoxysilyl group may include, for example, N,N-bis(trimethylsilyl)aminopropylmethyldimethoxysilane, 1-trimethylsilyl-2,2-dimethoxy-1-aza-2-silacyclopentane, N,N-bis(trimethylsilyl)aminopropyltrimethoxysilane, N,N-bis(trimethylsilyl)aminopropyltriethoxysilane, N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane, N,N-bis(trimethylsilyl)aminoethyltrimethoxysilane, N, N-bis(trimethylsilyl)-aminoethyltriethoxysilne, N,N-bis(trimethylsilyl)aminoethylmethyldimethoxysilane, N,N-bis(trimethylsilyl)aminoethylmethyldiethoxysilane, etc., and preferred are 1-trimethylsilyl-2,2-dimethoxy-1-aza-2-silacyclopentane, N,N-bis(trimethylsilyl) aminopropylmethyldimethoxysilane and N,N-bis(trimethylsilyl)aminopropylmethyldiethoxysilane. In one embodiment, the compound having a protected primary amino group and an alkoxysilyl group is N,N-bis(trimethylsilyl)aminopropyltriethoxysilane.
In one embodiment, the compound having a protected primary amino group and an alkoxysilyl group may be any compound of formula III
RN—(CH2)xSi(OR′)3, III
wherein R in combination with the nitrogen (N) atom is a protected amine group which upon appropriate post-treatment yields a primary amine, R′ represents a group having 1 to 18 carbon atoms selected from an alkyl, a cycloalkyl, an allyl, or an aryl; and X is an integer from 1 to 20. In one embodiment, at least one R′ group is an ethyl radical. By appropriate post-treatment to yield a primary amine, it is meant that subsequent to reaction of the living polymer with the compound having a protected primary amino group and an alkoxysilyl group, the protecting groups are removed. For example, in the case of bis(trialkylsilyl) protecting group as in N,N-bis(trimethylsilyl)aminopropyltriethoxysilane, hydrolysis is used to remove the trialkylsilyl groups and leave the primary amine.
In one embodiment, the rubber composition includes from about 50 to about 90 phr of the styrene-butadiene rubber functionalized with an alkoxysilane group and a primary amine group or thiol group.
Suitable styrene-butadiene rubbers functionalized with an alkoxysilane group and a primary amine group are available commercially, such as HPR 340 from Japan Synthetic Rubber (JSR).
In one embodiment, the solution polymerized styrene-butadiene rubber is as disclosed in WO 2007/047943 and is functionalized with an alkoxysilane group and a thiol, and comprises the reaction product of a living anionic polymer and a silane-sulfide modifier represented by the formula IV
(R4O)xA4ySi—R5—S—SiR43 IV
wherein Si is silicon; S is sulfur; O is oxygen; x is an integer selected from 1, 2 and 3;y is an integer selected from 0, 1, and 2; x+y=3;R4 is the same or different and is (C1-C16) alkyl; and R1 is aryl, and alkyl aryl, or (C1-C16) alkyl. In one embodiment, R5 is a (C1-C16) alkyl. In one embodiment, each R4 group is the same or different, and each is independently a C1-C5 alkyl, and R5 is C1-C5 alkyl.
The solution polymerized styrene-butadiene rubber in the outer cap layer and inner cap layer has a glass transition temperature in a range from −65° C. to −55° C. A reference to glass transition temperature, or Tg, of an elastomer or elastomer composition, where referred to herein, represents the glass transition temperature(s) of the respective elastomer or elastomer composition in its uncured state or possibly a cured state in a case of an elastomer composition. A Tg can be suitably determined as a peak midpoint by a differential scanning calorimeter (DSC) at a temperature rate of increase of 10° C. per minute, for example according to ASTM D7426 or equivalent.
Suitable styrene-butadiene rubbers functionalized with an alkoxysilane group and a thiol group are available commercially, such as Sprintan® SLR 3402 from Styron.
Another component of the rubber compositions of the outer cap layer and inner cap layer is from about 50 to about 10 phr of polybutadiene having a cis 1,4 content greater than 95 percent and a Tg ranging from −80 to −110° C. Suitable polybutadiene rubbers may be prepared, for example, by organic solution polymerization of 1,3-butadiene. The BR may be conveniently characterized, for example, by having at least a 90 percent cis 1,4-content and a glass transition temperature Tg in a range of from about −95° C. to about −105° C. Suitable polybutadiene rubbers are available commercially, such as Budene® 1229 from Goodyear and the like, having a Tg of −108° C. and cis 1,4, content of 96%.
The rubber compositions may also include a processing oil. Processing oil may be included in the rubber composition as extending oil typically used to extend elastomers. Processing oil may also be included in the rubber composition by addition of the oil directly during rubber compounding. The processing oil used may include both extending oil present in the elastomers, and process oil added during compounding. Suitable process oils include various oils as are known in the art, including aromatic, paraffinic, naphthenic, and low PCA oils, such as MES, TDAE, and heavy naphthenic oils, and vegetable oils such as sunflower, soybean, and safflower.
The rubber compositions of the outer cap layer include a combination of processing oil and resin in an amount ranging from 30 to 80 phr. In one embodiment, the rubber composition includes a combination of processing oil and resin in an amount ranging from 30 to 50 phr. In one embodiment, the rubber composition includes a combination of processing oil and resin in an amount ranging from 50 to 80 phr.
In one embodiment, the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 2. In one embodiment, the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2 and less than 4, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 2 and greater than 1. In one embodiment, the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2.2 and less than 4, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 1.8 and greater than 1. In one embodiment, the weight ratio of resin to oil in one of the central zone composition and lateral zone composition is greater than 2.5 and less than 4, and the weight ratio of resin to oil in the other of the central zone composition and lateral zone composition is less than 1.5 and greater than 1.
In one embodiment, the weight ratio of resin to oil in the central zone composition is greater than 2, alternatively greater than 2 and less than 4, alternatively greater than 2.2 and less than 4, alternatively greater than 2.5 and less than 4, and the weight ratio of resin to oil in the lateral zone composition is less than 2, alternatively less than 2 and greater than 1, alternatively less than 1.8 and greater than 1, alternatively less than 1.5 and greater than 1.
In one embodiment, the weight ratio of resin to oil in the lateral zone composition is greater than 2, alternatively greater than 2 and less than 4, alternatively greater than 2.2 and less than 4, alternatively greater than 2.5 and less than 4, and the weight ratio of resin to oil in the central zone composition is less than 2, alternatively less than 2 and greater than 1, alternatively less than 1.8 and greater than 1, alternatively less than 1.5 and greater than 1.
The rubber composition of the inner cap layer includes from 25 to 50 phr of processing oil, but is essentially free of resin. By essentially free, it is meant that no resin is added to the rubber composition of the inner cap layer; however, understanding that some residual resin may be included in the mixing process via contamination of the mixing equipment, the inner cap layer rubber composition includes less than 1 phr of resin. In another embodiment, the inner cap layer rubber composition includes less than 0.5 phr of resin.
The resin used in the rubber compositions of the outer cap layer have a Tg greater than 30° C. The resin is selected from the group consisting of hydrocarbon resins, phenol/acetylene resins, terpene phenol resins, rosin derived resins and mixtures thereof.
Representative hydrocarbon resins include coumarone-indene-resins, petroleum resins, terpene polymers, alphamethyl styrene resins and mixtures thereof.
Coumarone-indene resins are commercially available in many forms with melting points ranging from 10 to 160° C. (as measured by the ball-and-ring method). Preferably, the melting point ranges from 30 to 100° C. Coumarone-indene resins are well known. Various analysis indicate that such resins are largely polyindene; however, typically contain random polymeric units derived from methyl indene, coumarone, methyl coumarone, styrene and methyl styrene.
Petroleum resins are commercially available with softening points ranging from 10° C. to 120° C. Preferably, the softening point ranges from 30 to 100° C. Suitable petroleum resins include both aromatic and nonaromatic types. Several types of petroleum resins are available. Some resins have a low degree of unsaturation and high aromatic content, whereas some are highly unsaturated and yet some contain no aromatic structure at all. Differences in the resins are largely due to the olefins in the feedstock from which the resins are derived. Conventional derivatives in such resins include dicyclopentadiene, cyclopentadiene, their dimers and diolefins such as isoprene and piperylene.
Terpene polymers are commercially produced from polymerizing a mixture of beta pinene in mineral spirits. The resin is usually supplied in a variety of melting points ranging from 10° C. to 135° C.
Phenol/acetylene resins may be used. Phenol/acetylene resins may be derived by the addition of acetylene to butyl phenol in the presence of zinc naphthlate. Additional examples are derived from alkylphenol and acetylene.
Terpene-phenol resins may be used. Terpene-phenol resins may be derived by copolymerization of phenolic monomers with terpenes such as limonenes and pinenes.
Resins derived from rosin and derivatives may be used in the present invention. Gum and wood rosin have much the same composition, although the amount of the various isomers may vary. They typically contain about 10 percent by weight neutral materials, 53 percent by weight resin acids containing two double bonds, 13 percent by weight of resin acids containing one double bond, 16 percent by weight of completely saturated resin acids and 2 percent of dehydroabietic acid which contains an aromatic ring but no unsaturation. There are also present about 6 percent of oxidized acids. Representative of the diunsaturated acids include abietic acid, levopimaric acid and neoabietic acid. Representative of the monounsaturated acids include dextroplmaris acid and dihydroabietic acid. A representative saturated rosin acid is tetrahydroabietic acid.
In one embodiment, the resin is derived from styrene and alphamethylstyrene. It is considered that, in one aspect, its glass transition temperature (Tg) characteristic combined with its molecular weight (Mn) and molecular weight distribution (Mw/Mn) provides a suitable compatibility of the resin in the rubber composition, the degree of compatibility being directly related to the nature of the rubber composition.
The presence of the styrene/alphamethylstyrene resin with a rubber blend which contains the presence of the styrene-butadiene elastomer is considered herein to be beneficial because of observed viscoelastic properties of the tread rubber composition such as complex and storage modulus, loss modulus tan delta and loss compliance at different temperature/frequency/strain as hereinafter generally described.
The properties of complex and storage modulus, loss modulus, tan delta and loss compliance are understood to be generally well known to those having skill in such art. They are hereinafter generally described.
The molecular weight distribution of the resin is visualized as a ratio of the resin's molecular weight average (Mw) to molecular weight number average (Mn) values and is considered herein to be in a range of about 1.5/1 to about 2.5/1 which is considered to be a relatively narrow range. This believed to be advantageous because of the selective compatibility with the polymer matrix and because of a contemplated use of the tire in wet and dry conditions over a wide temperature range.
A suitable measurement of Tg for resins is DSC according to ASTM D6604 or equivalent.
The styrene/alphamethylstyrene resin is considered herein to be a relatively short chain copolymer of styrene and alphamethylstyrene with a styrene/alphamethylstyrene molar ratio in a range of about 0.40 to about 1.50. In one aspect, such a resin can be suitably prepared, for example, by cationic copolymerization of styrene and alphamethylstyrene in a hydrocarbon solvent.
Thus, the contemplated styrene/alphamethylstyrene resin can be characterized, for example, by its chemical structure, namely, its styrene and alphamethylstyrene contents and softening point and also, if desired, by its glass transition temperature, molecular weight and molecular weight distribution.
In one embodiment, the styrene/alphamethylstyrene resin is composed of about 40 to about 70 percent units derived from styrene and, correspondingly, about 60 to about 30 percent units derived from alphamethylstyrene. In one embodiment, the styrene/alphamethylstyrene resin has a softening point according to ASTM No. E-28 in a range of about 80° C. to about 145° C.
Suitable styrene/alphamethylstyrene resin is available commercially as Resin 2336 from Eastman or Sylvares SA85 from Arizona Chemical.
The phrase “rubber or elastomer containing olefinic unsaturation” is intended to include both natural rubber and its various raw and reclaim forms as well as various synthetic rubbers. In the description of this invention, the terms “rubber” and “elastomer” may be used interchangeably, unless otherwise prescribed. The terms “rubber composition,” “compounded rubber” and “rubber compound” are used interchangeably to refer to rubber which has been blended or mixed with various ingredients and materials, and such terms are well known to those having skill in the rubber mixing or rubber compounding art.
The vulcanizable rubber compositions of the outer cap layer may include from about 100 to about 180 phr of silica. The vulcanizable rubber composition of the inner cap layer may include from about 70 to about 120 phr of silica.
In the rubber compositions of the outer cap layer, including the central zone composition and the lateral zone composition, the weight ratio of the amount of silica to the total amount of resin and oil is less than 3. In one embodiment in the rubber compositions of the outer cap layer, the weight ratio of the amount of silica to the total amount of resin and oil is less than 3 and greater than 1. In one embodiment in the rubber compositions of the outer cap layer, the weight ratio of the amount of silica to the total amount of resin and oil is less than 2.5 and greater than 1. The weight ratio of the amount of silica to the total amount of resin and oil in the central zone composition and lateral zone composition may be the same or different, within the stated ranges.
In the rubber composition of the inner cap layer, the weight ratio of the amount of silica to the amount of oil is greater than 3. In one embodiment in the rubber composition of the inner cap layer, the weight ratio of the amount of silica to the amount of oil is greater than 3 and less than 6. In one embodiment in the rubber composition of the inner cap layer, the weight ratio of the amount of silica to the amount of oil is greater than 3.5 and less than 6.
The commonly employed siliceous pigments which may be used in the rubber compound include conventional pyrogenic and precipitated siliceous pigments (silica), although precipitated silicas are preferred. The conventional siliceous pigments preferably employed in this invention are precipitated silicas such as, for example, those obtained by the acidification of a soluble silicate, e.g., sodium silicate.
Such conventional silicas might be characterized, for example, by having a BET surface area, as measured using nitrogen gas, preferably in the range of about 40 to about 600, and more usually in a range of about 50 to about 300 square meters per gram. The BET method of measuring surface area is described in the Journal of the American Chemical Society, Volume 60, Page 304 (1930).
The conventional silica may also be typically characterized by having a dibutylphthalate (DBP) absorption value in a range of about 100 to about 400, and more usually about 150 to about 300.
The conventional silica might be expected to have an average ultimate particle size, for example, in the range of 0.01 to 0.05 micron as determined by the electron microscope, although the silica particles may be even smaller, or possibly larger, in size.
Various commercially available silicas may be used, such as, only for example herein, and without limitation, silicas commercially available from PPG Industries under the Hi-Sil trademark with designations 210, 243, etc.; silicas available from Rhodia, with, for example, designations of Z1165MP and Z165GR and silicas available from Degussa AG with, for example, designations VN2 and VN3, etc.
The vulcanizable rubber compositions may include from about 5 to about 50 phr of carbon black.
Commonly employed carbon blacks can be used as a conventional filler. Representative examples of such carbon blacks include N110, N121, N134, N220, N231, N234, N242, N293, N299, S315, N326, N330, M332, N339, N343, N347, N351, N358, N375, N539, N550, N582, N630, N642, N650, N683, N754, N762, N765, N774, N787, N907, N908, N990 and N991. These carbon blacks have iodine absorptions ranging from 9 to 145 g/kg and DBP number ranging from 34 to 150 cm3/100 g.
It may be preferred to have the rubber composition for use in the outer cap layer and inner cap layer to additionally contain a conventional sulfur containing organosilicon compound. Examples of suitable sulfur containing organosilicon compounds are of the formula:
Z-Alk-Sn-Alk-Z V
in which Z is selected from the group consisting of
where R6 is an alkyl group of 1 to 4 carbon atoms, cyclohexyl or phenyl; R7 is alkoxy of 1 to 8 carbon atoms, or cycloalkoxy of 5 to 8 carbon atoms; Alk is a divalent hydrocarbon of 1 to 18 carbon atoms and n is an integer of 2 to 8.
The preferred sulfur containing organosilicon compounds are the 3,3′-bis(trimethoxy or triethoxy silylpropyl) sulfides. The most preferred compounds are 3,3′-bis(triethoxysilylpropyl) disulfide and 3,3′-bis(triethoxysilylpropyl) tetrasulfide. Therefore, as to formula V, preferably Z is
where R7 is an alkoxy of 2 to 4 carbon atoms, with 2 carbon atoms being particularly preferred; alk is a divalent hydrocarbon of 2 to 4 carbon atoms with 3 carbon atoms being particularly preferred; and n is an integer of from 2 to 5 with 2 and 4 being particularly preferred.
In another embodiment, suitable sulfur containing organosilicon compounds include compounds disclosed in U.S. Pat. No. 6,608,125. In one embodiment, the sulfur containing organosilicon compounds includes 3-(octanoylthio)-1-propyltriethoxysilane, CH3(CH2)6C(═O)—S—CH2CH2CH2Si(OCH2CH3)3, which is available commercially as NXT™ from Momentive Performance Materials.
In another embodiment, suitable sulfur containing organosilicon compounds include compounds disclosed in U.S. Publication 2006/0041063. In one embodiment, the sulfur containing organosilicon compounds include the reaction product of hydrocarbon based diol (e.g., 2-methyl-1,3-propanediol) with 5-[3-(triethoxysilyl)propyl] thiooctanoate. In one embodiment, the sulfur containing organosilicon compound is NXT-Z™ from Momentive Performance Materials.
In another embodiment, suitable sulfur containing organosilicon compounds include those disclosed in U.S. Patent Publication No. 2003/0130535. In one embodiment, the sulfur containing organosilicon compound is Si-363 from Degussa.
The amount of the sulfur containing organosilicon compound of formula V in a rubber composition will vary depending on the level of other additives that are used. Generally speaking, the amount of the compound of formula V will range from 0.5 to 20 phr. Preferably, the amount will range from 1 to 10 phr.
It is readily understood by those having skill in the art that the rubber composition would be compounded by methods generally known in the rubber compounding art, such as mixing the various sulfur-vulcanizable constituent rubbers with various commonly used additive materials such as, for example, sulfur donors, curing aids, such as activators and retarders and processing additives, fillers, pigments, fatty acid, zinc oxide, waxes, antioxidants and antiozonants and peptizing agents. As known to those skilled in the art, depending on the intended use of the sulfur vulcanizable and sulfur-vulcanized material (rubbers), the additives mentioned above are selected and commonly used in conventional amounts. Representative examples of sulfur donors include elemental sulfur (free sulfur), an amine disulfide, polymeric polysulfide and sulfur olefin adducts. Preferably, the sulfur-vulcanizing agent is elemental sulfur. The sulfur-vulcanizing agent may be used in an amount ranging from 0.5 to 8 phr, with a range of from 1.5 to 6 phr being preferred. Typical amounts of antioxidants comprise about 1 to about 5 phr. Representative antioxidants may be, for example, diphenyl-p-phenylenediamine and others, such as, for example, those disclosed in The Vanderbilt Rubber Handbook (1978), pages 344 through 346. Typical amounts of antiozonants comprise about 1 to 5 phr. Typical amounts of fatty acids, if used, which can include stearic acid comprise about 0.5 to about 3 phr. Typical amounts of zinc oxide comprise about 2 to about 5 phr. Typical amounts of waxes comprise about 1 to about 5 phr. Often microcrystalline waxes are used. Typical amounts of peptizers comprise about 0.1 to about 1 phr. Typical peptizers may be, for example, pentachlorothiophenol and dibenzamidodiphenyl disulfide.
Accelerators are used to control the time and/or temperature required for vulcanization and to improve the properties of the vulcanizate. In one embodiment, a single accelerator system may be used, i.e., primary accelerator. The primary accelerator(s) may be used in total amounts ranging from about 0.5 to about 4, preferably about 0.8 to about 1.5, phr. In another embodiment, combinations of a primary and a secondary accelerator might be used with the secondary accelerator being used in smaller amounts, such as from about 0.05 to about 3 phr, in order to activate and to improve the properties of the vulcanizate. Combinations of these accelerators might be expected to produce a synergistic effect on the final properties and are somewhat better than those produced by use of either accelerator alone. In addition, delayed action accelerators may be used which are not affected by normal processing temperatures but produce a satisfactory cure at ordinary vulcanization temperatures. Vulcanization retarders might also be used. Suitable types of accelerators that may be used in the present invention are amines, disulfides, guanidines, thioureas, thiazoles, thiurams, sulfenamides, dithiocarbamates and xanthates. Preferably, the primary accelerator is a sulfenamide. If a second accelerator is used, the secondary accelerator is preferably a guanidine, dithiocarbamate or thiuram compound.
The mixing of the rubber composition can be accomplished by methods known to those having skill in the rubber mixing art. For example, the ingredients are typically mixed in at least two stages, namely, at least one non-productive stage followed by a productive mix stage. The final curatives including sulfur-vulcanizing agents are typically mixed in the final stage which is conventionally called the “productive” mix stage in which the mixing typically occurs at a temperature, or ultimate temperature, lower than the mix temperature(s) than the preceding non-productive mix stage(s). The terms “non-productive” and “productive” mix stages are well known to those having skill in the rubber mixing art. The rubber composition may be subjected to a thermomechanical mixing step. The thermomechanical mixing step generally comprises a mechanical working in a mixer or extruder for a period of time suitable in order to produce a rubber temperature between 140° C. and 190° C. The appropriate duration of the thermomechanical working varies as a function of the operating conditions, and the volume and nature of the components. For example, the thermomechanical working may be from 1 to 20 minutes.
The rubber composition may be incorporated in a variety of rubber components of the tire. For example, the rubber component may be a tread (including tread outer cap layer and tread inner cap layer), sidewall, apex, chafer, sidewall insert, wirecoat or innerliner. Preferably, the compound is a tread.
The pneumatic tire of the present invention may be a race tire, passenger tire, aircraft tire, agricultural, earthmover, off-the-road, truck tire, and the like. Preferably, the tire is a passenger or truck tire. The tire may also be a radial or bias, with a radial being preferred.
Vulcanization of the pneumatic tire of the present invention is generally carried out at conventional temperatures ranging from about 100° C. to 200° C. Preferably, the vulcanization is conducted at temperatures ranging from about 110° C. to 180° C. Any of the usual vulcanization processes may be used such as heating in a press or mold, heating with superheated steam or hot air. Such tires can be built, shaped, molded and cured by various methods which are known and will be readily apparent to those having skill in such art.
The following examples are presented for the purposes of illustrating and not limiting the present invention. All parts are parts by weight unless specifically identified otherwise.
This example illustrates the advantage of a rubber composition according to the invention. Rubber compounds were mixed according to the formulations shown in Table 1, with amounts given in phr. Compounds also containing standard amounts of additives including curatives, coupling agents, and antidegradants.
The compounds were cured and tested for physical properties as shown in Table 2.
1Solution polymerized SBR with styrene content of 15% and 1,2-vinyl content of 30%, Tg = −60° C., as SLR3402 from Styron.
2High cis 1,4-polybutadiene rubber as Budene1229 ™ from The Goodyear Tire & Rubber Company having a Tg of about −106° C. having a vinyl 1,2-content of less than about 4 percent and a cis 1,4-content of more than about 96 percent
3Precipitated silica as HiSil315G-D ™ from PPG having a BET (nitrogen) surface area of about 125 m2/g
4Silica coupler comprised of a bis(3-triethoxysilylpropyl) polysulfide containing an average in a range of from about 2 to about 2.6 connecting sulfur atoms in its polysulfidic bridge as Si266 ™ from Evonik
5Traction resin A as copolymer of styrene and alphamethylstyrene (styrene- alphamethylstyrene copolymer) having a softening point of about 80° C. to about 90° C. obtained as Sylvares SA85 ™ from Arizona Chemicals
6Fatty acids comprised of stearic, palmitic and oleic acids
7mixed p-phenylene diamine type
8Sulfenamide, dithiocarbamate and diphenylguanidine type
1Data according to Automated Testing System instrument by the Instron Corporation. Such instrument may determine ultimate tensile, ultimate elongation, modulii, etc. Data reported in the Table is generated by running the ring tensile test station which is an Instron 4201 load frame.
2Dynamic properties were determined by means of a GABO Eplexor tester. The test specimen is subjected to 0.25% sinusoidal deformation at 1 Hz and the temperature is varied.
While certain representative embodiments and details have been shown for the purpose of illustrating the subject invention, it will be apparent to those skilled in this art that various changes and modifications can be made therein without departing from the scope of the subject invention.