Patent Application
20160046155
The present technology relates to a pneumatic tire.
Racing tires, from which high levels of steering stability are demanded when driving at high speed, may take the form of a tire having a “half-radial” structure, in which carcass cords are biased with respect to the radial direction of the tire, and the angle of the carcass cords with respect to the circumferential direction of the tire as measured at a central position in the widthwise direction of the tread is from 55 to 85°; in such tires, the carcass cords may be constituted by nylon fiber cords.
When nylon fiber cords are used as the carcass cords in a half-radial cord arrangement of this sort, the problem arises that the carcass cords become incapable of sufficiently demonstrating their inherent cord properties, leading to insufficient improvement in steering stability and durability, if setting (solidification) occurs while compression-directional tensile force is applied to the carcass cords when the tire is being molded or vulcanized.
Examples of the conventional art pertaining to pneumatic tires that focus upon carcass cord intermediate elongation are as follows.
One proposed pneumatic tire that ensures steering stability and durability while offering improved ride comfort is a pneumatic tire in which the intermediate elongation value of the carcass used in the shoulders and sides of the tire is greater than the intermediate elongation value of the carcass used at locations outside these areas (see Japanese Unexamined Patent Application Publication No. 2009-23442A).
In another proposed tire, steering stability and mass are ensured while noise occurrence is suppressed by increasing the intermediate elongation value of the carcass cords located in the area below the belt layer to from 3 to 5% greater than that of that of the carcass cords in other areas (see Japanese Unexamined Patent Application Publication No. 2006-281984A).
However, these proposed pneumatic tires differ from the tire having a “half-radial” structure constituting the focus of the present technology, in which the carcass cords are biased with respect to the radial direction of the tire and have an angle of 55 to 85° with respect to the circumferential direction of the tire as measured at a central position along the widthwise direction of the tread.
The present technology provides a pneumatic tire for uses such as racing that use nylon fiber cords as carcass cords in a half-radial cord arrangement, wherein the tire is capable of sufficiently exhibiting the inherent cord properties of the nylon fiber carcass cords and has superior steering stability and durability.
The pneumatic tire of the present technology has the arrangement described in (1) below:
(1) a pneumatic tire having a half-radial structure in which carcass cords are biased with respect to the radial direction of the tire and have an angle of 55 to 85° with respect to the circumferential direction of the tire as measured at a central position along the widthwise direction of the tread, the tire being characterized in that the carcass cords have an elastic modulus of 3 to 10 GPa and a twist coefficient α of 1,500 to 2,500, and a difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between a central section and side sections of the tire is not more than 1.0%; the twist coefficient α being N×√T;
N being the number of twists per 10 cm of length in the fiber cords; and
T being the fineness (dtex) of the fiber cords.
The pneumatic tire according to the present technology more preferably has the arrangement set forth in (2) or (3) below.
(2) The pneumatic tire according to (1), wherein the carcass cords are continuously disposed along the entire circumference of the tire in the circumferential direction of the tire with a bead interposed therebetween.
(3) The pneumatic tire according to (1), wherein ends of the carcass cords with a bead interposed therebetween extend to beneath a belt.
In accordance with the present technology as in a first aspect, it is possible to provide a pneumatic tire for uses such as racing that use nylon fiber cords as carcass cords in a half-radial cord arrangement, wherein the tire is capable of sufficiently exhibiting the inherent cord properties of the nylon fiber carcass cords and has superior steering stability and durability.
In accordance with the present technology as in a second or a third aspect in particular, a pneumatic tire is provided that exhibits the effects of the present technology in particular with greater reliability and more prominently.
The pneumatic tire of the present technology will now be described in detail.
The pneumatic tire according to the present technology is a pneumatic tire having a half-radial structure in which carcass cords are biased with respect to the radial direction of the tire and have an angle of 55 to 85° with respect to the circumferential direction of the tire as measured at a central position along the widthwise direction of the tread, the tire being characterized in that the carcass cords have an elastic modulus of 3 to 10 GPa and a twist coefficient α of 1,500 to 2,500, and a difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between a central section and side sections of the tire is not more than 1.0%.
The value of the twist coefficient α is calculated according to the formula α=N×√T, with N being the number of twists per 10 cm of length of the fiber cords, and T being the fineness (dtex) of the fiber cords.
An embodiment of the pneumatic tire according to the present technology will now be described with reference to
In
The carcass layer 4 is constituted by aligned multiple carcass cords coated by a carcass compound, and the carcass cords are formed from nylon fibers. The carcass cords are disposed on a bias with respect to the radial direction of the tire to form a “half-radial” carcass layer; in the carcass layer 4, the angle θ of the carcass cords to the circumferential direction of the tire is from 55 to 85° as measured at a central position along the widthwise direction of the tread. Meanwhile, the belt layers 6 are disposed in the tread section 1 around the entire circumference of the tire to the outer circumferential side of the carcass layer 4. These belt layers 6 include reinforcing cords that are biased with respect to a tire circumferential direction and the reinforcing cords are disposed between the layers so as to intersect each other.
An angle θ of the carcass cords to the circumferential direction of the tire of less than 55° is undesirable, as the angle of the carcass cords may change due to lift during vulcanization molding, excessively increasing tread rigidity compared to side rigidity and negatively affecting ride comfort. An angle θ exceeding 85° is also not preferable, as this angle will reduce rigidity and steering stability.
In the present technology, it is essential that the carcass cords have an elastic modulus of 3 to 10 GPa and a twist coefficient α of 1,500 to 2,500, and a difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between the central section and the side sections of the tire be not more than 1.0%.
Specifically, if the elastic modulus of the carcass cord is less than 3 GPa, there will be insufficient improvement in steering stability. The elastic modulus exceeding 10 GPa is also undesirable, as this elastic modulus will reduce the fatigue resistance of the cords, and thus tire durability.
If the twist coefficient of the carcass cord is less than 1,500, the fatigue resistance of the cords will decrease, reducing tire durability. If the twist coefficient exceeds 2,500, the elastic modulus of the cords will decrease, inhibiting sufficient improvement in steering stability.
A difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between the central section and the side sections of the tire exceeding 1.0% will inhibit tensile force from being placed upon the cords in the side sections of the carcass, creating areas within the structure of the tire where the codes are slackened, with the result that steering stability and durability cannot be improved. A preferred minimum value for the difference in intermediate elongation is 0%.
An overview of a method for manufacturing the pneumatic tire according to the present technology will now be described.
The nylon carcass cords forming part of the pneumatic tire according to the present technology can be obtained by modifying manufacturing conditions to yield an elastic modulus of 3 to 10 GPa, and carcass cords having a twist coefficient α of 1,500 to 2,500 can be obtained by setting the number of twists according to the fineness of the cords to impart the predetermined twist.
To obtain a difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between the central section and the side sections of the tire of no more than 1.0%, a carcass structure that allows for more secure anchoring of the ends of the carcass cords can be selected for use in the process of molding and vulcanizing the tire.
To this end, the method of manufacturing the pneumatic tire according to the present technology preferably involves forming the tire by disposing the carcass cords so that the carcass cords are continuously disposed around the entire circumference of the tire along the circumferential direction of the tire with the beads interposed therebetween, as disclosed in Unexamined Japanese Patent Application Publication H10-225997, or disposing nylon carcass cords so that the ends of the carcass cords wrap around the beads and back up to underneath the belt layers 6, followed by vulcanizing and molding the tire.
The specific arrangement and effects of the pneumatic tire according to the present technology will now be described with reference to examples.
Using a test tire size of 225/50 R16 92V, five tires were prepared for each working example and comparative example and mounted on JATMA standard rims to create test tires.
The specifications for the carcass structures of the pneumatic radial tires according to the various working examples and comparative examples were as shown in table 1. The carcass structure described as “conventional” is the structure illustrated in
The test tires were evaluated for steering stability, ride comfort, load durability, and tire weight according to the testing/evaluation methods described in sections (B) through (D) hereafter; results are shown in table 1.
The difference in intermediate elongation at 2.0 cN/dtex in the carcass cords between the central section and the side sections in the present technology is determined according to the method described in section (A) hereafter.
(A) Method of Determining Difference in Intermediate Elongation at 2.0 cN/dtex in Carcass Cords between Central Section and side sections
Samples for determining the intermediate elongation at 2.0 cN/dtex between the central section and the side sections in the same carcass cord in the finished pneumatic tire following vulcanization and molding were taken according to the following guidelines.
For the central section, a sample cord piece of a length capable of being subjected to a tensile test between two left and right grips spaced a total of 10 cm apart was taken from an area centered on the tire equatorial line. If a sample cord piece long enough to be tested between two left and right grips spaced a total of 10 cm apart could not be taken, the grip spacing was reduced in increments of 0.5 cm until tensile testing was possible at the length of the obtainable sample cord piece. Care was taken to obtain testable sample cord pieces that were as long as possible. If a rubber adhered to the sample cord piece, the rubber was carefully removed (likewise hereafter).
For the side section, if the tire had a carcass structure comprising a section of the carcass that was turned up around the bead section, a sample cord piece long enough to be tensile tested at a grip spacing of 10 cm was taken from the turned-up carcass section. If a sample cord piece long enough to be tested between grips spaced a total of 10 cm apart could not be taken, the grip spacing was reduced in increments of 0.5 cm until tensile testing was possible at the length of the obtainable sample cord piece. Care was taken to obtain testable sample cord pieces that were as long as possible.
If the tire had a carcass structure comprising only turned-down sections, a sample cord piece long enough to be tensile tested at a grip spacing of 10 cm was taken from the turned-down carcass section. If a sample cord piece long enough to be tested between grips spaced a total of 10 cm apart could not be taken, the grip spacing was reduced in increments of 0.5 cm until tensile testing was possible at the length of the obtainable sample cord piece. Care was taken to obtain testable sample cord pieces that were as long as possible.
The sample cord pieces were colored at two locations corresponding to the testing length (grip spacing) so as to make pre- and post-testing length apparent.
The sample cord pieces were placed in a tensile test machine with grips set 10 cm apart so that the colored locations were aligned therewith, and tensile testing was performed by applying tensile force equivalent to 2.0 cN/dtex as determined according to the fineness (dtex) of the test cords at a rate of 300±20 mm/min. The testing was performed in a constant atmosphere of 20° C.±2° C. temperature and 65±2% relative humidity. After the tensile force was released, the sample cord piece was removed, the distance between the colored locations was determined, and elongation (%) was determined on the basis of the measured values.
Elongation (%) was calculated to one decimal place according to the following formula.
Elongation (%)=(post-tensile test core length/original cord length)×100
Testing was performed five times, an average value was determined, and the average value was rounded to a single decimal place to determine the elongation (%) of the sample.
The test described above was performed on the central section and the two side sections of the carcass cords, and the difference in values for elongation (%) so obtained was taken as the difference (%) in intermediate elongation at 2.0 cN/dtex between the central section and the side sections of the carcass cords.
The test tires were mounted on a 2,000 cc passenger vehicle, and five test drivers drove the vehicle on a slalom test course with pylons set at fixed intervals and evaluated driving feel.
Evaluation results were expressed as index values against 100 for a conventional tire. The higher the index value is, the more superior steering stability was.
The test tires were mounted on a 2,000 cc passenger vehicle, and five test drivers drove the vehicle on a straight test course having an uneven surface at 50 km/h and evaluated driving feel. Evaluation results were expressed as index values against 100 for a conventional tire. The higher the index value is, the more superior ride comfort was.
After completing a load durability test according to JIS D-4230 at a drum diameter of 1707 mm, the load was increased at a rate of 20%/5 hours, and testing was continued until the tire ruptured. Durability was evaluated by determining the total length of time until the test tire ruptured. Evaluation results are expressed as index values against 100 for a conventional tire (conventional example 1); the higher the index value is, the better the load durability of the tire was.
As is clear from the results shown in table 1, the pneumatic tire of the present technology exhibits a superb balance of superior ride comfort, steering stability, and durability.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2013-072741 | Mar 2013 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2014/059254 | 3/28/2014 | WO | 00 |