Poly [2,5-bis(polysulphano)-1,3,4-thiadiazoles]

Abstract

Poly[2,5-bis(polysulphano)-1,3,4-thiadiazoles] of the formula ##STR1## wherein X signifies a number from 1 to 10 andn signifies a number from 2 to 1,000.

Description

The present invention provides poly[2,5-bis(polysulphano)-1,3,4-thiadiazoles] and a method for the preparation thereof. The thiadiazoles according to the invention have the formula ##STR2## wherein X signifies a number from 1 to 10, preferably 1 to 3 and

n signifies a number from 2 to 1,000, preferably 2 to 100 and particularly from 4 to 50.

The said polymeric thiadiazoles are solid substances having melting points in the range of from 100.degree. to 200.degree. C. They are generally yellow in colour.

The thiadiazoles of formula (I) can be prepared by reacting 2,5-dimercapto-1,3,4-thiadiazole with a dichloropolysulphane. The reaction is generally conducted at temperatures of from 0.degree. to 100.degree. C., preferably from 20.degree. to 50.degree. C., in a strongly alkaline aqueous medium. The two starting materials are generally used in approximately equimolar quantities; an excess of one of the two components is, of course, possible. Both starting materials are generally soluble in the reaction medium; the polymer obtained is insoluble. The latter therefore precipitates out during the reaction and can easily be separated.

The reaction can be represented by means of the following reaction equation: ##STR3## 2,5-dimercapto-1,3,4-thiadiazole (II) is known, as are the dichloropolysulphanes. S.sub.2 Cl.sub.2 is commercially available and dichloropolysulphanes having a higher sulphur content are prepared therefrom by heating with elemental sulphur.

To prepare the poly[2,5-bis(polysulphano)-1,3,4-thiadiazoles] according to the invention, 2,5-dimercapto-1,3,4-thiadiazole can first of all be dissolved in water or in a solvent mixture containing predominantly water, for example, a mixture of water and alcohols in the presence of a strong base, for example, sodium hydroxide solution. The salt of the formula (II) given above is formed when the base is NaOH. The dichloropolysulphane is then added in the appropriate quantity and the mixture is optionally warmed. The polymerisation reaction is exothermic, so that if necessary cooling must be carried out during the reaction. The polymer formed of formula (I) is insoluble in the reaction medium; it precipitates out and can be isolated directly.

Particular dimeric derivatives of 2-mercapto-1,3,4-thiadiazole are described in the British Patent Specification 959 182. Here also alkaline solutions of 2-mercapto-1,3,4-thiadiazole are a starting material, however other coreactants are used.

The poly[2,5-bis(polysulphano)-1,3,4-thiadiazoles] according to the invention can be employed for the vulcanisation of sulphur-free polychloroprenes. The preferred vulcanisation system used for this contains thiophosphate in addition to the compound of formula (I). Using this combination, vulcanisates are obtained having properties corresponding to those achieved with the best vulcanisation systems currently available.

EXAMPLE 1

75 g (0.5 mol) of 2,5-dimercapto-1,3,4-thiadiazole is added in portions, with cooling in ice and stirring, and to a solution of 40 g (1 mol) of NaOH in 280 ml of water. Under these conditions no warmth is retained and a dark solution is formed. To this solution 67.5 g (0.5 mol) of disulphur dichloride is added dropwise, without previous working up, over approx. 40 min, while the temperature is maintained at between 10.degree. and 30.degree. C. by cooling with ice water. When addition is complete, stirring is continued for one hour at room temperature and the product, which is insoluble in water, is filtered off. The yellow solid is washed with water and dried in a vacuum at approx. 80.degree. C.

Yield: approx. 95 g (corresponding to approx. 90% of theoretical, referred to 2,5-dimercapto-1,3,4-thiadiazole), melting point 146.degree.-168.degree. C.

(C.sub.2 N.sub.2 S.sub.5).sub.n : calculated: C 11.3% H 0.00% N 13.2%, S 75.2%, Cl 10.0%

EXAMPLE 2

To the aqueous solution of the disodium salt of 2,5-dimercapto-1,3,4-thiadiazole, prepared as in Example 1, 83.5 g (0.5 mol) of S.sub.3 Cl.sub.2 (prepared from 67.5 g of S.sub.2 Cl.sub.2 and 16 g of sulphur) is added dropwise over approx. 1 hour, while the temperature is maintained at between 10.degree. and 30.degree. C. by cooling with ice water. When addition is complete, stirring is continued for one hour at room temperature and the product, which is insoluble in water, is filtered off. The yellow solid is washed with water and dried in a vacuum at approx. 80.degree. C.

Yield: approx. 108 g (corresponding to approx. 90% of theoretical, referred to 2,5 -dimercapto-1,3,4-thiadiazole), melting point 133.degree.-148.degree. C.

(C.sub.2 N.sub.2 S.sub.6).sub.x : calculated: C 9.8%, H 0.00%, N 11.5%, S 78.7%, C10.0% given: C 10.0%, H 0.5%, N 11.1%, S 76.6%, Cl 10.16%

EXAMPLE 3

Vulcanisation of sulphur- free polychloroprene:

The following rubber mixtures were prepared (numerical data in the Table are parts by weight):

TABLE I______________________________________ Composition A B C D E F G______________________________________Polychloroprene 100 100 100 100 100 100 100Magnesium oxide 2 2 2 2 2 2 2Octylated 2 2 2 2 2 2 2diphenylaminePentaerythritol 1 1 1 1 1 1 1bis-tetrahydro-benzaldehydeacetalStearic acid 0.5 0.5 0.5 0.5 0.5 0.5 0.5Antiozonant wax 2 2 2 2 2 2 2Polyethylene wax 3 3 3 3 3 3 3Carbon black 20 20 20 20 20 20 20N550Carbon black 10 10 10 10 10 10 10N330Durex O (carbon 15 15 15 15 15 15 15black)Dioctyl sebacate 5 5 5 5 5 5 5Highly aromatic 15 15 15 15 15 15 15plasticising oilCalcium oxide 6 6 6 6 6 6 6ZnO 6 6 6 6 6 6 6Dialkyldithio- 1 1 2 -- -- -- --phosphorylaminesaltPoly-[2,5-bis 0.9 2.7 0.9 2.7 1.8 1.8 --(polysulphono)]-1,3,4-thiadiazoleDialkyldithio- -- -- -- -- 1 2 --phosphorylaminesaltDiethylurea -- -- -- -- -- -- 1.25______________________________________ Moulded bodies made from a mixture were vulcanised at 170.degree. C. for 10 minutes and the following values were measured: TABLE 2______________________________________ A B C D E F G______________________________________Density (g/mm.sup.3) 1.33Hardness 57 65 57 65 61 57 59(Shore A)Elasticity (%) 44 48 44 49 45 45 49Tear strength 19.2 14.8 19.2 14.9 17.9 20.1 14.1Modulus 100 2.2 3.2 2.2 3.5 2.7 2.4 3.5(MPa)Modulus 300 10 10 9.1 11.1 9.8 8.8 --(MPa)Tensile 14.2 12.3 12.9 11 12.6 12.1 10.3strength (MPa)Elongation (%) 430 370 430 300 400 415 265______________________________________ After storage in hot air at 100.degree. C. for 7 days: TABLE 3______________________________________ A B C D E F G______________________________________Hardness (Shore A) 63 71 62 70 66 64 62(.degree.ShA)Elasticity (%) 45 48 45 47 46 46 53Tear strength 19.8 15 19.7 16.0 16.6 19.1 14.5(N/mm)Modulus 100 (MPa) 3.1 5 5 4.9 3.9 3.6 2.7Modulus 300 (MPa) 11 -- -- -- -- -- 9.7Tensile strength 12.1 9.6 10.8 9.2 8.9 10.4 10.8(MPa)Elongation (%) 335 205 300 200 225 280 335______________________________________

Claims

1. Poly[2,5-bis(polysulphano)-1,3,4-thiadiazoles] of the formula ##STR4## wherein X signifies a number from 2 to 10 and

n signifies a number from 2 to 1,000.

2. Method for the preparation of the polythiadiazoles of formula (I) of claim 1, characterised in that 2,5-dimercapto-1,3,4-thiadiazole is reacted in a strongly alkaline aqueous medium with dichloropolysulphane at temperatures of from 0.degree. to 100.degree. C.

3. A method of using the polythiadiazoles of formula (I) of claim 1, wherein said polythiadiazoles are added to a mixture containing sulphur-free polychloroprene as a vulcanising agent for the vulcanisation of said sulphur-free polychloroprene.