Polyacrylate and Polymethacrylate ester based hydrogel adhesives

Abstract

A hydrogel adhesive made of a polymer formed by polymerizing a water soluble long chain (meth)acrylate ester monomer (structure I); a hydrogel adhesive made of a copolymer formed by copolymerizing a first water soluble long chain (meth)acrylate ester monomer (structure I) with a second water soluble monomer (structure II); biomedical devices having such hydrogel adhesives; a method of preparing hydrogel adhesives; and a method of adhering biomedical devices to skin.

Description

FIELD OF THE INVENTION

This invention relates to hydrogel adhesives and, more particularly, to polyacrylate and polymethacrylate ester based hydrogel adhesives used with biomedical devices.

BACKGROUND OF THE INVENTION

In the medical field, when a biomedical electrode is used on a patient, it is generally provided with a metallic plate attached to conductive wires which are, in turn, attached to a monitoring apparatus. To improve conductivity between the skin and the electrode, a composition, usually a paste, a gel, or a cream, is applied between the metallic plate and the skin. The use of such a composition is often messy and offensive to the patient. In addition, the composition must be removed from the skin after use, either by wiping or by the use of solvents, both of which are also offensive. Furthermore, the electrode is usually secured to the patient by tape having a conventional pressure sensitive adhesive (PSA) thereon. Removal of the tape causes discomfort to the patient, and the composition of the adhesive of the tape may induce an allergic reaction in the patient.

To circumvent these difficulties, electrically conductive hydrogel adhesives have been developed. These hydrogel adhesives have replaced pastes, gels, and creams because they advantageously provide both conductivity and clean, residue-free removal from the skin surface after use. In addition, depending on the particular application and electrode design and on the nature of the hydrogel adhesive, hydrogel adhesives can be used alone--without a conventional PSA to secure the electrode to the skin. This is a result of the hydrogel's own specific adhesive properties.

Hydrogel adhesives differ from conventional PSA's in several respects. PSA's generally consist of polyacrylate polymer, or a polyolefin polymer combined with a tackifier additive. Monomers used to prepare polyacrylate PSA's are long chain esters of acrylic acid such as octyl acrylate. These particular polymers are inherently tacky and adhesive in nature. Polyolefin-based PSA's are prepared from rubber-like polymers such as polybutylene. Because these polymers are not inherently tacky, a tackifier is blended into the polymer base. Terpenes are generally used as tackifiers in these compositions. Most significantly, a conventional PSA contains no solvent, is non-aqueous, and will not dry out. These polymers are inherently adhesive and do not depend upon a swollen, crosslinked, watery formulation to provide tackiness and peel adhesion. They cannot be made electrically conductive by addition of water and electrolyte and they tend to be less skin friendly than hydrogel adhesives. Examples of typical PSA's are the adhesives coated on "Scotch" brand cellophane tape, masking tape, medical adhesive tape, and "Band-Aid" brand adhesive-bandages.

Hydrogel skin adhesives have proven useful in a variety of applications involving biomedical electrodes. Examples of such applications include use with electrocardiographic (ECG) electrodes, electrosurgical grounding pads, defibrillation electrodes, transcutaneous nerve stimulation electrodes, and iontophoretic drug delivery electrodes. Non-electrode applications are also becoming increasingly important. Examples include use with transdermal drug delivery patches, as adhesives for ostomy devices, as wound dressings, and with medical tapes.

Hydrogel skin adhesive compositions are generally composed of a crosslinked water soluble polymer network swollen with water as a solvent component. Humectant materials are usually added as co-solvents to provide slow drying or non-drying characteristics to the hydrogel adhesive. Humectant materials are usually polyols such as glycerol, sorbitol, or propylene glycol, or low molecular weight polyethylene oxide diols such as PEG 400 or PEG 600. Other additives can also be added to hydrogel adhesives for specific purposes. Examples include electrolytes such as sodium chloride for electrical conductivity, preservatives such as methyl paraben to prevent microbiological degradation, buffering agents such as sodium dihydrogen phosphate for pH control, and water soluble polymers such as polyacrylamide for viscosity modification.

The crosslinked water soluble polymer network can be formed by polymerization of a large variety of water soluble monomers in the presence of difunctional crosslinking agents by free radical polymerization techniques initiated by thermal or photochemical methods. Crosslinking of previously formed water soluble polymers can also be effected by complexation with difunctional species, such as divalent metal cations or difunctional organic reactants, or by exposure to ionizing radiation such as gamma-rays or electron beams. Many naturally occurring polymers such as gelatin can be reversibly and non-covalently crosslinked by manipulating gelation temperatures.

Examples of water soluble monomers subject to free radical polymerization for use as a hydrogel are acrylic acid, methacrylic acid, acrylamide, methacrylamide, and vinyl pyrrolidone. Diacrylate esters of polyethylene oxides are typical free radical crosslinking agents used in these compositions. Examples of hydrogel formation by the crosslinking of water soluble polymers are the crosslinking of carboxymethylcellulose by reaction with aluminum ion, the crosslinking of prepolymer polyisocyanates by reaction with water and organic diols, and the crosslinking of polyvinylpyrrolidone by electron beam radiation. Examples of naturally occurring polymers which form gels by thermal gelation are gelatin and karaya gum. There are thus a large number of hydrogel adhesives of diverse types.

One of the critical properties determining the usefulness of a hydrogel adhesive is its peel adhesion strength. High peel strength allows the hydrogel adhesive to be used without an accompanying PSA in many applications. Hydrogel skin adhesives with high peel strength provide a more secure attachment of electrodes (or other devices) to the patient. Correspondingly, low peel strength provides a less secure attachment, allowing easier removal of the hydrogel adhesive from the patient. Depending on the particular application, varying hydrogel adhesive peel strengths are required.

Another useful property of hydrogel adhesives is repositionability. "Repositionability" is defined as the ability of the adhesive hydrogel to be removed from one area of the skin and to be attached to another area without loss of peel adhesion properties. Other properties of hydrogel adhesives include tack adhesion and creep compliance.

The properties of a given hydrogel adhesive depend in large measure upon the nature of the crosslinked water soluble polymer that comprises the hydrogel adhesive. Presently, the nature of the crosslinked water soluble polymer used in the hydrogel adhesive fixes the properties of that adhesive. In order to vary the peel strength or repositionability of the adhesive, for example, different water soluble polymers may be used. Development of hydrogel adhesive properties is thus an empirical process at present. A water soluble polymer system that allows broad variation of hydrogel adhesive properties without changing the type of polymer is desirable.

SUMMARY OF THE INVENTION

The present invention provides a hydrogel adhesive made of a polymer formed by polymerizing a monomer having the structure (I) ##STR1## where R.sub.1 is selected from H and CH.sub.3 ; R.sub.2 is selected from a straight or branched chain alkyl radical of 2-12 carbon atoms, a straight or branched chain aliphatic ester radical of 5-12 carbon and oxygen atoms, and a straight or branched chain ether radical of 3-12 carbon and oxygen atoms; X is an ionic group selected from SO.sub.3.sup.-, COO.sup.-, and ##STR2## where R.sub.3, R.sub.4, and R.sub.5 are independently selected from H and alkyl groups of 1-4 carbon atoms.

Also provided is a method of adhering a biomedical device to skin by disposing between the device and the skin the above hydrogel adhesive and applying sufficient pressure to the device to adhere it to the skin. A biomedical device with a surface adapted to be adhered to the skin of a patient, wherein the surface has the above hydrogel adhesive disposed thereon, is also provided by the present invention.

Also provided is a method of preparing the above hydrogel adhesive by polymerizing monomer (I) in the presence of multifunctional crosslinking agents by free radical polymerization techniques using an initiator.

The invention further provides a compound that is a copolymer formed by copolymerizing a first water soluble monomer having the structure (I) with a second water soluble monomer having the structure (II)

CH.sub.2 .dbd.CH--Y (II)

where Y is selected from ##STR3## where R.sub.6 and R.sub.7 are independently selected from H and alkyl groups of 1-3 carbon atoms.

Also provided is a hydrogel adhesive comprising a copolymer formed by copolymerizing the first and second water soluble monomers (I) and (II) above.

Also provided is a method of adhering a biomedical device to skin by disposing between the device and the skin a hydrogel adhesive made from monomers (I) and (II), as described above, and applying sufficient pressure to the device to adhere it to the skin.

Also provided is a biomedical device with a surface adapted to be adhered to the skin of a patient, wherein the surface has a hydrogel adhesive made from monomers (I) and (II) as described above.

Also provided is a method of preparing a hydrogel adhesive by copolymerizing monomers (I) and (II) in the presence of multifunctional-crosslinking agents by free radical polymerization techniques using an initiator.

BRIEF DESCRIPTION OF THE DRAWING

The invention is best understood from the following detailed description when read in connection with the accompanying drawing, in which:

FIG. 1 is a graph depicting properties of a set of hydrogel adhesives prepared from exemplary formula (I) and formula (II) monomers;

FIG. 2 is a graph depicting properties of another set of hydrogel adhesives prepared from further exemplary formula (I) and formula (II) monomers;

FIG. 3 is a graph depicting properties of another set of hydrogel adhesives prepared from further exemplary formula (I) and formula (II) monomers;

FIG. 4 is a graph depicting properties of another set of hydrogel adhesives prepared from further exemplary formula (I) and formula (II) monomers;

FIG. 5 is a graph depicting properties of a set of hydrogel adhesives-prepared from two exemplary formula (I) monomers; and

FIG. 6 is a cross-sectional view illustrating an exemplary biomedical electrode including a hydrogel adhesive of the present invention.

DESCRIPTION OF THE INVENTION

The present invention involves hydrogel adhesives having variable properties depending on the relative proportions of the first and second water soluble monomers used in the formulation of the adhesive. The general formula for the first monomer is given above as formula I.

Two specific monomers within the scope of general formula I are potassium-3-sulfopropyl acrylate (SPAK) and 2-carboxyethylacrylate (CEA). CEA is particularly preferred when it is in the form of a partially neutralized alkali metal salt. The structures for these water soluble monomers are: ##STR4##

The two formula I monomers given above are acrylate ester monomers. Other monomers having the general structure of formula I are methacrylate ester monomers such as 2-sulfoethylmethacrylate (SEMA), potassium-3-sulfopropyl methacrylate (SPMAK), and methacryloxyethyl trimethylammonium chloride (MAETAC).

The general formula for the second monomer used in the hydrogel adhesive compositions of the present invention is given above as formula II. The second monomer has a pendant chain smaller in molecular size than that of the first monomer. Examples of monomers of formula II are acrylic acid, acrylamide, alkylated acrylamides, vinyl pyrrolidone, vinyl sulfonic acid, and vinyl phosphonic acid.

A hydrogel adhesive formed by polymerizing a formula I monomer without a formula II monomer (a homopolymer of the formula I monomer) will possess certain adhesive properties. By adding increasing amounts of the formula II monomer and polymerizing to form a copolymer of formula I and II monomers, the adhesive properties vary, depending on the relative proportions of the formula I and II monomers.

The preparation and composition of an adhesive hydrogel using a homopolymer of SPAK (100% of first water soluble polymer--SPAK; 0% of second water soluble polymer) is first described below. This serves as a general description of the procedure used to formulate the adhesive poly(meth)acrylate ester hydrogels of the invention. (The final composition of the hydrogel formed of the homopolymer of SPAK is given as Example 1 in Table 1; the compositions of all other examples disclosed herein are presented in the accompanying Tables 1-6 as Examples 2-34.)

A mixture of potassium chloride (0.5 g) and potassium-3-sulfopropylacrylate (35.0 g) was dissolved in 40.5 g of distilled water with stirring. Polyacrylamide N-300 LMW (2.0 g) (available from American Cyanamid Co. of Wayne, N.J. 07470) was then added and dispersed into the above solution with vigorous stirring. The polyacrylamide dissolved slowly over a period of a few hours with a corresponding increase in the viscosity of the solution. Glycerin (20.0 g); a 3% solution of N,N'methylenebis acrylamide in propylene glycol (1.2 g); and Darocur 1173 (0.8 g) (available from EM Industries Inc. of Hawthorne, N.Y. 10532) were then added sequentially, with stirring, resulting in a moderately viscous, homogeneous solution.

The finished composition was coated onto a polycarbonate film having a thickness of 2.5 mil, using a 30 mil wet-film applicator. The coating was cured with a Fusion 200 W/in. UV lamp (H-bulb) at a bulb height of approximately 12 inches with a UV dosage of 0.69 J/cm.sup.2. A hydrogel adhesive was thus formed of a homopolymer of SPAK.

To measure peel adhesion, the coated hydrogel adhesive films were attached to a 1/8 inch thick polyethylene foam substrate and pulled off at a 90.degree. angle at a rate of 6 inches per minute. The results are reported as grams per 7/8 inch width of sample. Other properties measured were tack adhesion, creep compliance, and repositionability. Tack adhesion was measured using a Polyken Tack instrument (2 sec. dwell, 1 cm/sec. speed, 20 grams force). Repositionability was measured by repeatedly pulling the adhesive off the foam substrate and measuring changes in peel adhesion.

In the description given above for the formation of an adhesive hydrogel, the distilled water serves as a solvent and potassium chloride is added as an electrolyte to provide electrical conductivity to the compositions of the invention when they are used as biomedical electrode adhesives. Potassium hydroxide is used to partially neutralize acrylate monomers containing carboxylic acid groups such as acrylic acid. Polyacrylamide polymer (PAAm N-300 LMW) serves as a viscosity modifier. Glycerin serves as a humectant. Used as a cross-linking monomer for the hydrogel homopolymer is N,N'-methylenebis acrylamide (MBA) which, as described above, is added as a 3% solution in propylene glycol. (Although a difunctional cross-linking agent is used in this example, other multifunctional agents can be used. Thus, in this application, the term "multifunctional" includes difunctional, trifunctional, tetrafunctional, etc.) Darocur 1173 (2-hydroxy-2-methyl-1-phenyl-propane-1-one) serves as the photoinitiator in the UV polymerization reaction.

The homopolymer of SPAK in the form of an adhesive hydrogel, synthesized as described in Example 1, exhibits a low peel strength (thereby minimizing risk of injury and discomfort to the patient) of 40 g as shown in Table 1, Example 1. The homopolymer also has good repositionability when attached to the skin. In terms of repositionability, the homopolymer of SPAK is superior to other hydrogel homopolymers such as polyacrylic acid.

Repositionability and low peel strength properties of hydrogel skin adhesives such as that formed of the SPAK homopolymer are important in biomedical applications such as diagnostic ECG electrodes, wound dressings, and medical tapes used to secure devices such as intravenous catheters to the body. Medical applications in the pediatric, neonatal, geriatric, and operating room areas are particularly relevant because of the high degree of skin sensitivity typically exhibited by patients within these hospital groupings.

To vary the properties of the hydrogel adhesive and provide greater peel strength, increased amounts (from 0% in the preceding example) of the second water soluble monomer are added and polymerized with the first monomer.

The preparation and composition of an adhesive hydrogel using a copolymer of SPAK and acrylic acid (AA) is next described. This serves as a description of the procedure used to formulate the adhesive copolymer poly(meth)acrylate ester hydrogels of the invention. The final composition of the hydrogel formed of the copolymer of this example is given as Example 4 in Table 1.

A mixture of potassium chloride (0.5 g) and potassium hydroxide (8.96 g) was dissolved in 34.54 g of distilled water with stirring while cooling to below 30 degrees C. Using an addition funnel, acrylic acid (19.38 g) was charged slowly and the temperature was maintained below 40 degrees C. After adding and dissolving potassium-3-sulfopropylacrylate (15.62 g) , polyacrylamide N-300 LMW (2.0 g) was then added and dispersed into the above solution with vigorous stirring. The polyacrylamide dissolved slowly over a period of a few hours with a corresponding increase in the viscosity of the solution. Glycerin (17.0 g); a 3% solution of N,N'methylenebis acrylamide in propylene glycol (1.2 g); and Darocur 1173 (0.8 g) were then added sequentially, with stirring, resulting in a moderately viscous, homogeneous solution.

In the description given above in Example 4 for the formation of an adhesive hydrogel, as in Example 1, the distilled water serves as a solvent and potassium chloride is added as an electrolyte to provide electrical conductivity. Potassium hydroxide, polyacrylamide polymer, glycerin, MBA, and Darocur 1173 serve the same functions as indicated in Example 1.

The finished composition was coated onto a polycarbonate film having a thickness of 2.5 mil, using a 30 mil wet-film applicator. The coating was cured as in Example 1. A hydrogel adhesive was thus formed of a copolymer of SPAK and acrylic acid. Peel adhesion, tack adhesion, creep compliance, and repositionability of the adhesive were then measured as in Example 1. The peel adhesion characteristics of a set of hydrogel adhesive copolymers prepared from acrylic acid as the second water soluble monomer and SPAK as the first are shown as Examples 1-7 in Table 1 and in FIG. 1. The peel adhesion values exhibited by both of the homopolymers (40 g for the SPAK homopolymer and 30 g for the AA homopolymer) are low but adequate, for example, on applications on highly sensitive skin. The peel adhesion values of the copolymers are higher, however than each of the homopolymers and increase to a peak level at a SPAK concentration of approximately 30-70 weight percent of the total monomer. The peak peel adhesion values for the copolymer are approximately 460 g, over ten times that of either of the homopolymers. The magnitude of the increased peel adhesion of copolymers having 25-75 weight % SPAK of total monomer (75-25 weight % AA of total monomer, respectively) over the homopolymers is unexpected. (See FIG. 1.)

That the increase and peak in peel strength is unexpected is illustrated partly by the more linear variation in the tack adhesion of the same compositions as shown in FIG. 1. Given this more linearized plot, linear variance of peel adhesion would also be expected. The variation in tack adhesion is almost linear and decreases as the concentration of SPAK in the copolymer increases.

The SPAK/AA copolymer in hydrogel adhesive form is a particularly useful composition because it provides a continuum of hydrogel adhesives which can be used in a broad spectrum of applications. The applications can have requirements varying from a relatively weak, skin-friendly, repositionable adhesive (where a composition having a concentration close to either 100% SPAK or 0% SPAK would be appropriate) to an aggressive, very strong adhesive, desirable in such dynamic or long-term applications as ECG or Holter monitoring (where a 30-70% SPAK composition would be appropriate). Any intermediate adhesive characteristics which may be desired can also be produced. One should also appreciate that by varying the concentrations of the various components in the compositions, the peel adhesion peak can be shifted anywhere in the range of 10-90% by weight SPAK of total monomer.

Other monomers can also be used as the second water soluble monomer. Hydrogel adhesive copolymers prepared from acrylamide as the second monomer (AAM) and SPAK as the first possess synergistic adhesion properties analogous to those observed for SPAK/AA copolymers. (See the compositions and their corresponding adhesion data in Examples 8-12 in Table 2 and FIG. 2.) Similar to the other homopolymers described above, the peel adhesion exhibited by the AAM homopolymer (0% SPAK) is very low. Nevertheless, the peel adhesion of the copolymer increases and peaks at a SPAK concentration of approximately 20-70 weight percent of total monomer.

Although acrylic acid and acrylamide are the only specific examples of the second monomer given, alkylated acrylamides are reasonable extensions of acrylamide because they have similar polarity and size. Vinyl pyrrolidone is also similar in size and polarity to dialkylated acrylamides. Sulfonic acid and phosphoric acid groups are reasonable extensions of the carboxylic acid group because they are also similar in size and polarity especially when neutralized to their anionic form. All of these monomers are within the scope of Formula II.

Turning to the second of the two formula I monomers which specifically illustrate the advantageous properties of the acrylate ester hydrogels of the present invention, CEA, it should be noted that the CEA which was used in the examples described herein is not a pure material. The CEA (or 2-carboxyethylacrylate) was obtained from Radcure Specialties Inc. of Louisville, Ky. It consists of a mixture of approximately 20% AA, 40% CEA, and 40% of a mixture of polyester trimers and tetramers having the following structure: ##STR5## where n=O for CEA, n=1 for trimer, and n=2 for tetramer. Therefore, all of the hydrogel polymers and copolymers of CEA contain substantial quantities of polyester trimer and tetramer units and AA units as well as CEA. All numbers in the examples are corrected to account for the presence of these other substances.

CEA copolymers with AA or AAM (Examples 13-24, Tables 3 and 4, and FIGS. 3 and 4) exhibit adhesive behavior similar to that of the SPAK examples discussed above. The CEA as purchased (with 20% AA), which exhibits a 230 g peel adhesion, also possesses desirable repositionability properties. Copolymers of CEA with AA or AAM exhibit a surprising peel adhesion behavior within a useful range of peel adhesion values. In particular, peel adhesion values are surprisingly high when CEA is 20-75 weight % of the total monomer. The surprising peel adhesion behavior of CEA copolymers demonstrates that esters of longer chain length than SPAK or pure CEA also confer advantageous adhesion properties on the hydrogels of the present invention. Because the CEA used in the examples contains 40% of a mixture of trimer and tetramer which have 7 and 12 chain atoms, respectively, extrapolation to pure alkyl groups and ether groups is reasonable because these groups have similar hydrophobicity and polarity to the ester groupings present in CEA trimer and tetramer. Therefore, these groups are included in the general formula I for the first water soluble monomer.

Hydrogel copolymer adhesives prepared from various ratios of SPAK and CEA together (i.e., two Formula I monomers) do not exhibit the surprising peel adhesion characteristics. Instead, a nearly linear relationship between the peel adhesion and the tack adhesion of the two homopolymers is observed (Examples 25-28, Table 5, and FIG. 5). Because both SPAK and CEA are long-chain acrylate ester monomers, it is evident that only copolymers which combine long-chain acrylate ester monomers with monomers of small molecular size, such as AA or AAM, will exhibit the synergistic peel adhesion properties.

Hydrogel adhesive polymers were also prepared from methacrylate ester monomers as the Formula I monomers (Table 6) such as 2-sulfoethylmethacrylate (SEMA, Examples 29, 33, and 34) and potassium-3-sulfopropyl methacrylate (SPMAK, Examples 30 and 32). Methacrylate ester monomers are much less reactive to UV free radical initiation than are acrylate ester monomers such as SPAK and CEA; therefore, the formation of polymers comprising these compounds was initiated using thermal free radical initiator procedures. The thermal initiator used was V-50 (2,2'-azobis (2-amidinopropane) dihydrochloride) (available from Wako Chemicals, USA Inc. of Richmond, Va.). The methacrylate monomers formed hydrogel adhesive polymers which were tacky and adhesive to the touch and may be as useful as the corresponding acrylate polymer hydrogels.

A cationic-terminated, methacrylate ester-based hydrogel adhesive was prepared by thermal initiation of the methacryloxyethyl trimethylammonium chloride monomer (MAETAC, Examples 31 and 34) having the following structure: ##STR6##

The resulting hydrogel polymer was also tacky and adhesive to the touch and appears to be as useful as all of the preceding examples.

A particularly useful application of the hydrogel adhesives of the present invention is with biomedical electrodes. The adhesives are useful in a wide variety of electrodes assuming varying construction. FIG. 6 is an exemplary embodiment of one of these electrodes.

In FIG. 6, a support member 1, which is circular in shape in this exemplary embodiment, is made of a plastic substance. Electrode 2 is incorporated in support member 1 so as to protrude from both sides of support member 1. An electrically conductive hydrogel adhesive 3, having a composition according to the present invention, is superposed on surface 4 of support member 1 and is adapted to be adhered to the skin of a patient. Hydrogel adhesive 3 should be applied to surface 4 in a thickness sufficient to cover the portion of electrode 2 protruding from surface 4 of support member 1.

In use, electrode 2 is connected to a measuring instrument (not shown) and the electrically conductive hydrogel adhesive 3 is pressed against the patient with sufficient pressure to adhere the biomedical electrode to the patient.

Although illustrated and described herein with reference to certain specific embodiments, the present invention is nevertheless not intended to be limited to the details shown. Rather, various modifications may be made in the details within the scope and range of equivalents of the claims and without departing from the spirit of the invention.

TABLE 1__________________________________________________________________________ Example NumberComposition (% by weight) 1 2 3 4 5 6 7__________________________________________________________________________Distilled Water 40.05 29.77 32.86 34.54 36.36 37.95 39.05Potassium Chloride 0.5 0.5 0.5 0.5 0.5 0.5 0.5Potassium Hydroxide -- 16.12 11.49 8.96 6.24 3.85 2.19Acrylic Acid -- 35 24.95 19.38 13.4 8.29 4.7SPAK 35 -- 10.05 15.62 21.6 26.71 30.03PAAm N-300 LMW 2 2 2 2 2 2 2Glycerin 20 14.61 16.15 17 17.9 18.7 19.263% MBA/PG 1.2 1.2 1.2 1.2 1.2 1.2 1.2Darocur-1173 0.8 0.8 0.8 0.8 0.8 0.8 0.8Ave.Peel Force (g) 40 30 85 460 225 150 120Tack Force (g) 63 408 375 310 233 175 144__________________________________________________________________________ TABLE 2______________________________________ Example NumberComposition (% by weight) 8 9 10 11 12______________________________________Distilled Water 40.5 40.5 40.5 40.5 40.5Potassium Chloride 0.5 0.5 0.5 0.5 0.5Acrylamide 35 24.85 19.26 13.29 8.2SPAK -- 10.15 15.74 21.72 26.8PAAm N-300 LMW 2 2 2 2 2Glycerin 20 20 20 20 203% MBA/PG 1.2 1.2 1.2 1.2 1.2Darocur-1173 0.8 0.8 0.8 0.8 0.8Ave.Peel Force (g) 50 210 240 160 60Tack Force (g) 420 330 315 250 93______________________________________ TABLE 3__________________________________________________________________________ Example NumberComposition (% by weight) 13 14 15 16 17 18 19__________________________________________________________________________Distilled Water 31.06 31.39 31.72 32.21 33.27 33.95 35.11Potassium Chloride 0.5 0.5 0.5 0.5 0.5 0.5 0.5Potassium Hydroxide 14.44 13.36 12.82 12.03 10.69 9.62 7.93AA (including the 20% AA 29.4 25.66 23.8 21 16.34 12.6 7 20%in the CEA as purchased)CEA (including the 5.6 9.34 11.2 14 18.66 22.4 28tri- and tetra-mers)PAAm N-300 LMW 2 2 2 2 2 2 2Glycerin 15 15.75 15.96 16.26 16.54 16.93 17.463% MBA/PG 1.2 1.2 1.2 1.2 1.2 1.2 1.2Darocur-1173 0.8 0.8 0.8 0.8 0.8 0.8 0.8Ave.Peel Force (g) 70 160 540 390 290 280 230Tack Force (g) 406 366 384 244 261 117 138__________________________________________________________________________ TABLE 4______________________________________Composition Example Number(% by weight) 20 21 22 23 24______________________________________Distilled Water 39.21 38.49 37.6 36.72 36Potassium Chloride 0.5 0.5 0.5 0.5 0.5Potassium Hydroxide 1.62 2.7 4.04 5.37 6.44Acrylamide 27.92 23.22 17.37 11.56 6.92CEA (including tri- 5.66 9.42 14.1 18.75 22.46and tetra-mers)AA (20% of CEA as 1.42 2.36 3.53 4.69 5.62purchased)PAAm N-300 LMW 2 2 2 2 2Glycerin 19.67 19.31 18.86 18.42 18.063% MBA/PG 1.2 1.2 1.2 1.2 1.2Darocur-1173 0.8 0.8 0.8 0.8 0.8Ave.Peel Force (g) 200 350 190 190 180Tack Force (g) 480 351 206 240 183______________________________________ TABLE 5______________________________________ Example NumberComposition (% by weight) 25 26 27 28______________________________________Distilled Water 36 37.34 38.38 39.02Potassium Chloride 0.5 0.5 0.5 0.5Potassium Hydroxide 6.6 4.44 3.04 1.9CEA (including tri- & 23.30 15.50 10.72 6.63tetra-mers)AA (20% of CEA as 5.83 3.88 2.68 1.66purchased)SPAK 5.87 15.62 21.6 26.71PAAm N-300 LMW 2 2 2 2Glycerin 17.9 18.72 19.08 19.583% MBA/PG 1.2 1.2 1.2 1.2Darocur-1173 0.8 0.8 0.8 0.8Ave.Peel Force (g) 125 85 80 85Tack Force (g) 80 104 68 91______________________________________ TABLE 6______________________________________ Example NumberComposition (% by weight) 29 30 31 32 33 34______________________________________Distilled Water 38.7 42.7 47.67 39.87 37.51 39.9Potassium Chloride 0.5 0.5 0.5 0.5 0.5 0.5Potassium Hydroxide 5.95 -- -- 3.59 6.84 3.25Acrylic Acid -- -- -- 7.92 -- --SEMA 35 -- -- -- 20.09 14.34CEA (including tri- & -- -- -- -- 11.93 --tetra-mersAA (20% of CEA as -- -- -- -- 2.98 --purchased)SPMAK -- 35 -- 27.08 -- --MAETAC -- -- 35 -- -- 20.66Glycerin 18.45 20.4 15.43 19.04 17.95 19.153% MBA/PG 1.2 1.2 1.2 1.8 1.8 1.8V-50 0.2 0.2 0.2 0.2 0.4 0.4______________________________________

Claims

1. A hydrogel adhesive comprising a copolymer formed by copolymerizing and cross-linking a first water soluble monomer having the structure (I) ##STR7## where, R.sub.1 is selected from the group consisting of H and CH.sub.3 ;

R.sub.2 is selected from the group consisting of a straight or branched chain alkyl radical of 2-12 carbon atoms, a straight or branched chain aliphatic ester of 5-12 carbon and oxygen atoms, and a straight or branched chain ether radical of 3-12 carbon and oxygen atoms;

X is an ionic group selected from the group consisting of SO.sub.3.sup.-, COO.sup.- and ##STR8## where R.sub.3, R.sub.4, and R.sub.5 are independently selected from the group consisting of H and alkyl groups of 1-4 carbon atoms;

with a second water soluble monomer having the structure (II)

CH.sub.2 .dbd.CH--Y (II)

where Y is selected from the group consisting of ##STR9## where R.sub.6, R.sub.7 are independently selected from the group consisting of H and alkyl groups of 1-3 carbon atoms;

in the presence of water, a multifunctional cross-linking agent, and a humectant;

wherein said first water soluble monomer is selected from the group consisting of potassium-3-sulfopropyl acrylate, potassium-3-sulfopropyl methacrylate, 2-carboxyethylacrylate, 2-sulfoethylmethacrylate, and methacryloxyethyl trimethylammonium chloride; and

wherein said second water soluble monomer is selected from the group consisting of acrylic acid, acrylamide, alkylated acrylamides, vinyl pyrrolidone, vinyl sulfonic acid, and vinyl phosphonic acid.

2. A hydrogel adhesive as claimed in claim 1 wherein said first water soluble monomer comprises 10-90 weight % of total monomer weight.

3. A hydrogel adhesive as claimed in claim 1 wherein said first water soluble monomer is selected from the group consisting of potassium-3-sulfopropyl acrylate and potassium-3-sulfopropyl methacrylate, said second water soluble monomer is acrylic acid, and said first water soluble monomer comprises 10-90 weight % of total monomer weight.

4. A hydrogel adhesive as claimed in claim 1 wherein said first water soluble monomer is selected from the group consisting of potassium-3-sulfopropyl acrylate and potassium-3-sulfopropyl methacrylate, and said second water soluble monomer is acrylamide, and said first water soluble monomer comprises 20-70 weight % of total monomer weight.

5. A hydrogel adhesive as claimed in claim 1 wherein said first water soluble monomer is 2-carboxyethylacrylate, said second water soluble monomer is acrylic acid, and said first water soluble monomer comprises 20-75 weight % of total monomer weight.

6. A hydrogel adhesive as claimed in claim 1 wherein said first water soluble monomer is 2-carboxyethylacrylate, said second water soluble monomer is acrylamide, and said first water soluble monomer comprises 10-50 weight % of total monomer weight.

7. The hydrogel adhesive as claimed in claim 1, further comprising an electrolyte, a neutralizing agent, a viscosity modifier, and a photoinitiator.

8. The hydrogel adhesive as claimed in claim 7, wherein said electrolyte is potassium chloride, said neutralizing agent is potassium hydroxide, said viscosity modifier is polyacrylamide polymer, said humectant is glycerin, said cross-linking agent is N,N'-methylenebis acrylamide in a 3% solution in propylene glycol, and said photoinitiator is 2-hydroxy-2-methyl-1-phyenyl-propane-1-one.