Polyamide Hot Melt Coating

Information

  • Patent Application
  • 20170158909
  • Publication Number
    20170158909
  • Date Filed
    February 20, 2017
    7 years ago
  • Date Published
    June 08, 2017
    7 years ago
Abstract
The present invention relates to a thermoplastic coating composition comprising at least one polyamide and at least one surface modifying agent, wherein the polyamide comprises a reaction product of: a) at least one dimerized fatty acid;b) at least one mono carboxylic acid;c) at least one linear dicarboxylic acid; andd) at least one linear diamine; wherein the surface modifying agent is selected from slip agents, anti-blocking agents or combinations thereof; wherein the surface modifying agent is contained in 0.1 to 10 wt-%, based on the total weight of the thermoplastic coating composition; and wherein the composition preferably has a coefficient of friction (COF) of 0.2 to 1.1 which is measured according to ASTM D 1894.
Description

The present invention relates to protective or decorative coatings for articles preferably having a wooden surface, a plastic surface or a wood-plastic-composite surface. Such coatings are commonly applied on the articles by employing solvent- or water-based lacquer. Thereby the solvent or water has to be evaporated after application by using special equipment, e.g., ovens or ventilated areas. To obtain a level coating of a desired thickness, several layers have to be applied, i.e., the application and evaporation step has to be repeated for several times. For example, when a wooden article like a pencil should be coated with those techniques a desired coating is only obtained after at least six repetitions. Such a process is time consuming and additionally requires an increased storage space for the manufacturer for the bulky ovens or ventilated areas.


Moreover, the obtained coatings should have specific characteristic in order to make the articles suitable for everyday use. The coating should be scratch resistant to a certain extent, i.e., have a sufficient surface hardness without brittleness. In particular, if the article is a consumer good the surface has to be appealing to the consumer, for example has to be level, even and able to have a desirable color. Additionally the coated article should have a good feel for the surface if the article is touched while used, e.g., a toy or pencil. Moreover, it is often desired that the surface of the coated articles is further processed, e.g. by printing of texts. Thus, ink should stick to the coating.


DE 102 04 288 A1 discloses a coating agent based on thermoplastic and elastic polyamide resins optionally containing fillers and/or further additives, characterized in that it further comprises a brittle polyamide resin and/or a polyester resin. However, this document rather discloses a general concept and there is a need for coatings based on polyamides which can fulfill the above needs.


The inventors of the present invention have surprisingly found that the above-mentioned needs can be fulfilled with the specific thermoplastic coating composition of the present invention. In particular, the inventors have found, without being bound by theory, that the employment of the specific polyamide of the present invention, which contains a balance of hard and soft segments in the same backbone, provides a sufficient surface hardness, without brittleness of the final coating. Additionally, by employing the surface modification agent improved anti-scratch properties and an appealing surface of the final coating are obtained.


The present invention relates in particular to:


a thermoplastic coating composition comprising at least one polyamide and at least one surface modifying agent, wherein the polyamide comprises a reaction product of:

    • a) at least one dimerized fatty acid;
    • b) at least one mono carboxylic acid;
    • c) at least one linear dicarboxylic acid; and
    • d) at least one linear diamine; and


      wherein the composition preferably has a coefficient of friction (in the following also referred to as “COF”) of 0.2 to 1.1, more preferably 0.4 to 1.0, and most preferably 0.5 to 0.95.


Use of the thermoplastic coating composition according to the present invention as a coating for articles preferably having a wooden surface, a plastic surface or a wood-plastic-composite surface and/or which are preferably consumer goods, more preferably writing utensils, packaging materials, toys, furniture, decorative plates, and housewares.


And a method of coating a substrate comprising the steps of

  • 1) melting the thermoplastic coating composition according to the present invention; and
  • 2) applying the melt of step 1) through an extruder upon a surface to be coated.


Further preferred embodiments are set out in the claims.


In the present specification the terms “a” and “an” and “at least one” are the same as the term “one or more” and can be employed interchangeably.


In the following “CX”, wherein X in an integer, refers to the amount of carbon atoms.


The polyamides can be prepared from different monomers. Preferably, the number average molecular weight is selected so that a polyamide is obtained which can be processed as melt at temperatures below 250° C. Dimerized fatty acid, mono carboxylic acid, linear dicarboxylic acid and linear diamines are used as components of the polyamide, which are generally known to the skilled person. Preferably acid terminated polyamides are employed, more preferably linear acid terminated polyamides.


The dimerized fatty acids (compound a)), sometimes referred to in the literature as “dimer acids”, are complex mixtures resulting from the polymerization of fatty acids. These dimerized fatty acids are obtained by coupling unsaturated long chain monobasic fatty acids, e.g. linoleic acid, stearic acid or oleic acid. A mixture of polymeric fatty acids can be employed as well and are those commercially available from the polymerization of tall oil fatty acids. These polymeric fatty acids preferably have the following typical composition: C18 monobasic acids (monomer) about 0 to 5 wt.-%, C36 dibasic acids (dimer) 60 to 95 wt.-%, sometimes up to about 98 wt.-%, C54 and higher polybasic acids (trimer) about 1 to 35 wt.-%, based on the total weight of the polymeric fatty acid. The relative ratios of monomer, dimer and trimer in the polymeric fatty acids depend on the nature of the starting material, the conditions of polymerization and the degree of purification. Purer grades of polymeric fatty acids are obtained by distillation and contain at least 70%, preferably 80% and frequently up to 95% or even 98 wt.-% of the total weight of the dimerized fatty acid. The dimerized fatty acids may be unhydrogenated or hydrogenated.


In addition to the dimerized fatty acids, at least one mono carboxylic acid (compound b)) is employed in the preparation of the polyamide according to the present invention. In preferred embodiments the at least one mono carboxylic acid b) is selected from the group consisting of linear and branched C3 to C24 mono carboxylic acids or combinations thereof, more preferably from linear and branched C12 to C18 mono carboxylic acids or combinations thereof, most preferably from linear C14 to C18 mono carboxylic acids or combinations thereof. The carboxylic acids b) can be saturated or unsaturated, preferably they are saturated.


Furthermore, in the preparation of the polyamide at least one linear dicarboxylic acid is employed (compound c)). In preferred embodiments the at least one linear dicarboxylic acid c) is selected from the group consisting of linear C6 to C18 dicarboxylic acids and combinations thereof, more preferably from linear C10 to C14 dicarboxylic acids and combinations thereof, most preferably compound c) is a linear C14 dicarboxylic acid. The dicarboxylic acids c) can be saturated or unsaturated, preferably they are saturated.


The at least one linear diamine (compound d)) is preferably selected from one or more linear aliphatic diamines, more preferably the linear aliphatic diamines have C1 to C10 carbon atoms. Specific examples are 1,2-ethylenediamine, 1,3-diaminopropane, 1,4-diaminobutane and 1,6-hexamethylene diamine. In most preferred embodiments the linear diamine is 1,2-ethylenediamine.


The polyamides according to the invention may be prepared by conventional condensation methods and the equivalent ratio of NH2 groups of d) to the sum of the COOH groups of a) to c) is preferably from 1.2:1 to 1:1.2., more preferably 1:1.2. In the majority of cases, it is preferred that residual acid groups or residual amino groups be present after the condensation, more preferred are residual acid groups.


When choosing the monofunctional, difunctional or trifunctional raw materials as monomers, the amount shall be selected so that preferably meltable, for example uncrosslinked polyamides shall be obtained. For example, if crosslinking/gelling occurs, then lowering the fraction of trifunctional components can result in polymers that do not tend to gel.


In preferred embodiments a) to c) are employed in the preparation of the polyamide as follows a) is present in 50 to 85 wt.-%; b) is present in 0.5 to 3 wt.-%; and c) is present in 5 to 30 wt.-%, based on the total weight of the polyamide. In further preferred embodiment in addition to the before mentioned ranges for a) to c), d) is present in 5 to 25 wt.-%, more preferred in 8 to 20 wt.-%.


In preferred embodiment of the present invention the surface modifying agent is selected from slip agents, anti-blocking agents or combinations thereof, preferably the surface modifying agent is selected from alumina, silica, glass microspheres, waxes, perfluoro compounds, poly(meth)acrylates, fatty acid amides, polysiloxanes and combinations thereof. In more preferred embodiments one or more slip agents are employed as surface modifying agent. In more preferred alternative embodiments anti-blocking agents are employed as surface modifying agent.


Anti-blocking agents are known to the skilled person and the commonly known can be employed. In particular useable in the present invention are anti-blocking agents selected from alumina, hydrated alumina (Al2O3*3H2O); silicate like magnesium silicate, aluminum silicate, sodium silicate, potassium silicate, mica, calcium carbonate (CaCO3), silica, talc, clay, wollastonite, feldspar, glass microspheres, ceramic microspheres, thermoplastic microspheres, baryte and wood flour or combinations thereof, more preferably the anti-blocking agents are selected from alumina, silica, glass microspheres and combinations thereof. Exemplary alumina and silica compounds are commercially obtainable from Cabot Cooperation, Boston, e.g., under the tradenames SpectrAl® and CAB-O-SIL® or from Evonik Industries AG, Essen under the tradenames AEROXIDE® and AEROSIL®.


Slip agents are known to the skilled person and the commonly known can be employed. In particular useable in the present invention are slip agents selected from waxes, perfluoro compounds, polysiloxanes, fatty acid amides and poly(meth)acrylates or combinations thereof.


The slip agent is preferably selected from waxes, perfluoro compounds, polysiloxanes, fatty acid amides, and combinations thereof, more preferably from microcrystalline waxes, polysiloxanes and fatty acid amides or combinations thereof.


Exemplary waxes suitable as slip agents comprise polyethylene wax, microcrystalline wax, paraffin wax, beeswax, carnauba wax, montan wax, candelilla wax, synthetic wax, or combinations thereof, preferably the wax is a microcrystalline wax.


The term “microcrystalline wax” is known to the skilled person and refers to a petroleum-derived wax. This microcrystalline wax is a solid at room temperature, and contains substantial proportions of branched and cyclic (naphthenes, alkyl- and naphthene substituted aromatics) hydrocarbons, in addition to saturated straight alkanes. Microcrystalline wax has a crystal lattice micro-structure characterized by the presence of strongly branched isoparaffins and naphthenes, which inhibit crystallization. Microcrystalline wax is produced from a combination of heavy oil distillates and from the sediments of paraffinic crude oil (settling waxes). Microcrystalline wax excludes animal wax, vegetal wax, bacterial wax, mineral wax, and synthetic wax. The microcrystalline paraffin wax preferably has a molecular weight of about 500 to 800 g/mol and/or a dropping point measured according to DIN ISO 2176 of 60° C. to 100° C. Commercially available microcrystalline waxes are generally a mixture of straight and branched chain paraffins characterized by a higher molecular weight and a smaller crystal structure compared to other waxes. Suitable commercially available microcrystalline paraffin waxes are commercially available, e.g. under the tradename Parapi 90F from Acrites y Parafinas Industries, Mexico, under the tradename Multiwax from Witco Chemical Co or under the tradename Sasolwax, e.g., Sasolwax 0907 from Sasol Wax GmbH, Hamburg.


The methods for the preparation of fatty acid amides employed are generally known in the art. For example, fatty acid esters are commonly prepared by the reaction of an alcohol and a fatty acid or a fatty acid derivative, such as a fatty acid halide.


Exemplary fatty acid amides are saturated fatty acid monoamide (e.g., lauramide, palmitamide, arachidamide behenamide, stearamide, ethylenebis-12-hydroxy stearamide); unsaturated fatty acid monoamide (e.g., oleamide, erucamide, recinoleamide); and N-substituted fatty acid amide (e.g., N-stearyl stearamide, N-behenyl behenamide, N-stearyl behenamide, N-behenyl stearamide, N-oleyl oleamide, N-oleyl stearamide, N-stearyl oleamide, N-stearyl erucamide, erucyl erucamide, and erucyl stearamide, N-oleyl palmitamide); methylol amide (e.g., methylol stearamide, methylol behenamide); saturated fatty acid bis-amide (e.g., methylene bis-stearamide, ethylene bis-stearamide, ethylene bis-isostearamide, ethylene bis-hydroxystearamide, ethylene bis-behenamide, hexamethylene bis-stearamide, hexamethylene bis-behenamide, hexamethylene bis-hydroxystearamide, N,N′-distearyl adipamide, N,N′-distearyl sebacamide); unsaturated fatty acid bis-amide (e.g., ethylene bis-oleamide, hexamethylene bis-oleamide, N,N′-dioleyl adipamide, N,N′-dioleyl sebacamide; saturated or unsaturated fatty acid tetra amide, stearyl erucamide, ethylene bis stearamide and ethylene bis oleamide).


A large number of useful fatty acid amides are commercially available from Humko Chemical Company, Memphis, Tenn., USA under the Kemamide tradename and include, for example, Kemamide B (behenamide/arachidamide), Kemamide W40 (N,N′-ethylenebisstearamide), Kemamide P181 (oleyl palmitamide), Kemamide S (stearamide), Kemamide U (oleamide), Kemamide E (erucamide), Kemamide O (oleamide), Kemamide W45 (N,N′-ethylenebisstearamide), Kenamide W20 (N,N′-ethylenebisoleamide), Kemamide E180 (stearyl erucamide), Kemamide E221 (erucyl erucamide), Kemamide S180 (stearyl stearamide), Kemamide S221 (erucyl stearamide), and the like. In addition, useful fatty amides are commercially available from Croda Universal Ltd., Hull East Yorkshire, England, under the Crodamide tradename and include, for example, Crodamide OR (oleamide), Crodamide ER (erucamide), Crodamide SR (stereamide), Crodamide BR (behenamide), Crodamide 203 (oleyl palmitamide), Crodamide 212 (stearyl erucamide), and from Clariant AG, Muttenz, Switzerland, for example Licowax C (N,N′-ethylenebisstearamide).


Preferred fatty acid amides are selected from lauramide, palmitamide, arachidamide, behenamide, stearamide, ethylenbis-12-hydroxystearamide, oleamide, erucamide, recinoleamide, N-stearyl stearamide, N-behenyl behenamide, N-stearyl behenamide, N-behenyl stearamide, N-oleyl oleamide, N-oleyl stearamide, N-stearyl oleamide, N-stearyl erucamide, erucyl stearamide, erucyl erucamide, N-oleyl palmitamide, methylol stearamide, methylol behenamide, methylene bis-stearamide, ethylene bis-stearamide, ethylene bis-isostearamide, ethylene bis-hydroxystearamide, ethylene bis-behenamide, hexamethylene bis-stearamide, hexamethylene bis-behenamide, hexamethylene bis-hydroxystearamide, N,N′-distearyl adipamide, and N,N′-distearyl sebacamide, ethylene bis-oleamide, hexamethylene bis-oleamide, N,N′-dioleyl adipamide, and N,N′-dioleyl sebacamide and combinations thereof. In more preferred embodiments the fatty acid amide is selected from erucamide, behenamide, stearamide, oleamide and combinations thereof.


When employing poly(meth)acrylates, polymers or copolymers of alkyl acrylates having an alkyl radical chain length of 2 to 8 carbon atoms, such as ethyl acrylate, 2-ethylhexyl acrylate or n-butyl acrylate are preferred. The poly(meth)acrylates preferably have a number average molecular weight of 500 to 100,000 g/mol, more preferably 2,500 to 80,000 g/mol, most preferably 10,000 to 50,000 g/mol.


With regard to the polysiloxanes preferred compounds are selected from polydimethylsiloxanes, polymethylalkylsiloxanes, and polyether- or polyester-modified polydimethyl- or polymethylalkylsiloxanes or polyester-modified hydroxypolymethylsiloxane or a combination thereof. In some embodiments, the siloxane is a cross-linked siloxane. In the before mentioned compounds, “alkyl” preferably refers to alkanes having C1 to C10, more preferably C1 to C6, most preferably C1 to C4 carbon atoms. In some embodiments, the siloxane may be a silsesquioxane having the chemical formula RSiO3/2 where R is a hydrocarbon. In preferred embodiments, the hydrocarbon is a C1 to 10 hydrocarbyl, a C1 to 4 hydrocarbyl or a C1 to 2 hydrocarbyl. In one embodiment, the siloxane may be methylsilsesquioxane (MSQ). The polysiloxanes preferably have a number average molecular weight of 300 to 100,000 g/mol, more preferably 2,500 to 80,000 g/mol, most preferably 10,000 to 50,000 g/mol. Examples of commercially available siloxanes include Tospearl® 105, 120, 130, 145, 240, 1110A, 2000, 3000 from Momentive Performance Materials Inc., Albany, USA. Additionally BYK-300, BYK-301/302, BYK-306, BYK-307, BYK-310, BYK-313, BYK-315, BYK-330, BYK-331, BYK-333, BYK-337, BYK-342, BYK-370, BYK-371, BYK-375, BYK-377, BYK-378, BYK-UV3500, and BYK-UV3510 (all of which are manufactured by BYK Additives and Instruments GmbH, Wesel, Germany).


The perfluor compound is preferably selected from perfluoroalkane, perfluorocarboxylic acid ester, a perfluoro organic compound and fluorinated polymer or combinations thereof. Particularly preferred are polytetrafluorethylene, perfluoralkoxyalkane, polyvinylidene fluoride, and combinations thereof.


In preferred embodiments, the surface modifying agent is contained in 0.1 to 10 wt.-%, more preferably 0.1 to 3 wt.-%, most preferably 0.1 to 0.5 wt.-%, in the coating composition based on the total weight of the thermoplastic coating composition. In more preferred embodiments the surface modifying agent is a slip agent and is contained in 0.1 to 10 wt.-%, more preferably 0.1 to 3 wt.-%, most preferably 0.1 to 0.5 wt.-%, in the coating composition, based on the total weight of the thermoplastic coating composition. In alternative, more preferred embodiments, the surface modifying agent is an anti-blocking agent and is contained in 0.1 to 10 wt.-%, more preferably 0.1 to 3 wt.-%, most preferably 0.1 to 0.5 wt.-%, in the coating composition, based on the total weight of the thermoplastic coating composition.


The thermoplastic coating composition according to the present invention preferably further comprises at least one additive, which is/are known in the art. The term “additive” includes fillers, which are different from the surface modifying agent of the present invention, dyes, thixotropic agents (e.g., urea derivatives, fibrillated or pulp short fibers), color pastes and/or pigments, conductivity additives (e.g., conductivity carbon blacks or lithium perchlorate), plasticizers, tackifiers, further polymers, which are different from the polyamide according to the present invention, stabilizers, adhesion promoters, rheological additives, catalysts, moisture scavengers and any combination thereof. More preferably the additive is selected from antioxidants, fillers, which are different from the surface modifying agent, dyes, color pastes and/or pigments, plasticizers, further polymers, different from the polyamide, tackifiers, and combinations thereof.


The coating composition according to the present invention preferably comprises 0.1 to 20 wt.-% of additives, based on the total weight of the coating composition. In more preferred embodiments 1 to 10 wt.-%, most preferably 1 to 5 wt.-%, are contained. In even more preferred embodiments the additives contained in the above mentioned ranges are selected from dyes, color pasts and/or pigments, stabilizers, adhesion promoters, plasticizers, tackifiers, polymers, which are different from the polyamide according to the invention, catalysts, moisture scavengers and combinations thereof.


In further preferred embodiments the coating composition according to the present invention comprises 0.1 to 20 wt.-%, more preferred 1 to 10 wt.-%, most preferred 1 to 5 wt.-%, based on the total weight of the coating composition, of additives selected from dyes, color pastes, pigments or combinations thereof.


The coating compositions according to the invention may contain tackifiers, such as, e.g., resins derived from abietic acid, abietic acid esters, other rosin esters, polyterpene resins, terpene/phenolic resins, styrenated terpenes, poly-α-methylstyrene, α-methylstyrene-phenolic or aliphatic, aromatic or aromatic/aliphatic hydrocarbon resins or coumarone/indene resins or resins derived from low molecular weight polyamides. These tackifying resins may optionally contain OH groups, to improve compatibility of the different components.


The coating composition according to the present invention preferably comprises 0.1 to 20 wt.-% of at least one tackifier, based on the total weight of the coating composition. In more preferred embodiments 1 to 10 wt.-%, most preferably 1 to 5 wt.-%, are contained.


The coating compositions according to the invention may contain further polymers, different from the polyamide according to the present invention. These are preferably selected from EVA, polyurethane polymers, rubber type polymers, styrene copolymers, polyester copolymers, polycarbonates, acrylics, thermoplastic polyurethanes and combinations thereof.


The coating composition according to the present invention preferably comprises 0.1 to 20 wt.-% of at least one further polymer, different from the polyamide according to the present invention, based on the total weight of the coating composition. In more preferred embodiments 1 to 10 wt.-%, most preferably 1 to 5 wt.-%, are contained.


The coating compositions according to the invention may contain plasticizers, provided that these plasticizers do not interfere with the capability of the composition to be applied as a coating—such as phthalates, benzoates, sucrose esters and sulphonamides. By way of example there may be mentioned the liquid phthalate plasticizers, plasticizers based on aromatic esters, such as, e.g., esters of benzoic acid, or also solid plasticizers such as dicyclohexyl phthalate, cyclohexane dimethanol dibenzoate and the like. Also suitable are other plasticizers such as sucrose acetate isobutyrate, ortho-/para-toluene sulphonamide or N-ethyl-ortho-toluene sulphonamide.


The coating composition according to the present invention preferably comprises 0.1 to 20 wt.-% of plasticizers, based on the total weight of the coating composition. In more preferred embodiments 1 to 10 wt.-%, most preferably 1 to 5 wt.-% are contained.


As stabilizers different components can be used such as antioxidants, UV stabilizers, hydrolysis stabilizers. Examples for these components are sterically hindered phenols of high molecular weight, sulphur-containing and phosphorus-containing phenols or amines. This include sterically hindered phenols, polyfunctional phenols, thioether, substituted benzotriazoles, hindered benzophenone and/or sterically hindered amines. Examples of hydrolysis stabilizers include oligomeric and/or polymeric aliphatic or aromatic carbodiimides. Such components are commercially available and known to the skilled person.


As adhesion promoters, are preferably selected from the group consisting of 1,4-cyclohexylene dimethylene terephthalate, 1,4-cyclohexylene dimethylene isophthalate, alkylene-maleic anhydride copolymers, n-alkylglutarimide/acrylic copolymers, ethylene-1,4-cyclohexylene dimethylene terephthalate, ethylene-ethyl acrylate, ethylene-1,3-phenylene oxyethylene terephthalate, ethylene-methyl acrylate copolymer resins, ethylene-1,3-phenylene oxyethylene isophthalate, ethylene-vinyl acetate copolymers, ethylene-vinyl acetate-vinyl alcohol copolymers, and combinations thereof


The coating composition according to the present invention preferably comprises 0.1 to 20 wt.-% of a compound selected from stabilizer and adhesion promoters or a combination thereof, based on the total weight of the coating composition. In more preferred embodiments 1 to 10 wt.-%, most preferably 1 to 5 wt.-% are contained.


In preferred embodiments the thermoplastic coating composition according to the invention has a ring and ball softening point of 90 to 220° C., preferably 110 to 190° C., most preferably 140 to 170° C.


Furthermore, the present invention relates to the use of the thermoplastic coating composition according to the present invention as coating for articles preferably having a wooden surface, a plastic surface or a wood-plastic-composite surface and/or which are preferably consumer goods, more preferably writing utensils, packaging materials, toys, furniture, decorative plates, and housewares. The before mentioned object upon which the coating is to be applied can have a wooden, plastic or wood-plastic composite surface. In preferred embodiments the thermoplastic coating composition according to the present invention is used in writing utensils like pencils, color pencils, pens, felt pen, ball points, fineliner pen, rollerball pen, in more preferred embodiments the before mentioned specific examples of writing utensils have a wooden surface. Most preferably, the coating is a coating for writing utensils, preferably pencils, more preferably wooden pencils.


In further preferred embodiments the thermoplastic coating composition is used as coating in wooden toys and housewares like brooms, cutlery, tableware.


Furthermore, the present invention relates to a method of coating a substrate comprising the steps of

  • 1) melting the thermoplastic coating composition according to the present invention; and
  • 2) applying the melt of step 1) through an extruder upon a surface to be coated.


In preferred embodiment the method according to the present invention further comprises the step

  • 3) cooling the coated surface of step 2) with air. In more preferred embodiments the temperature of the air is 5 to 25° C.


In more preferred embodiments of the method of the present invention the surface to be coated is the surface of a pencil.


Measurement Methods

Molecular weight determination (Mw and Mn)


The respective compounds/compositions were analyzed for molecular weight and molar mass distribution by Gel Permeation Chromatography (GPC) under the same chromatographic condition. The samples to be measured were dissolved under heat in dichloromethane, diluted with tetrahydrofuran and after filtration over a Styragel®-column analyzed in combination with a PL-gel-mix-column. As eluent, tetrahydrofuran was employed, the detection was made via RI- and UV-detectors. The temperature of the column compartment was 35° C. The calculated weight average molecular weight (Mw) and number average molecular weight (Mn) at the peak maximum (Mp) in the obtained graphs refer to external calibration with polystyrene-standards.


Melt Viscosity

Melt viscosity was measured using a Brookfield Viscometer model RVDV-1+ with a Model 106 temperature controller and Thermosel unit, calibrated with viscosity standard oil. 10 to 12 g of adhesive was weighed into a disposable aluminum viscometer tube. The tube was inserted into the Viscometer and left to equilibrate for 30 minutes at 210° C. The preheated spindle no. 27 was inserted into the adhesive and allowed to rotate for 30 minutes at 210° C.; the speed of rotation was changed according to the viscosity range measured. The initial viscosity V1 at 210° C. was then measured.


Coefficient of Friction

The coefficient of friction (COF) was measured after the coating has been applied and the article has been allowed to cool to room temperature (also referred to as “immediate”) or after 3 days after the preparation of the article (also referred to as “3 days”) according to ASTM D 1894.


Ring and Ball Softening Point

The ring and ball softening point of the coating composition was measured in accordance with ASTM E 28.







EXAMPLES

The thermoplastic coating composition according to the present invention can be prepared as follows. The following examples are for illustrative purposes only and are not intended to limit the scope of the invention.


General Preparation Method

In a 5-neck round bottom flask with mechanical stirrer and under inert atmosphere (nitrogen gas) all acid components (components a) to c)), an optional acid catalyst and antioxidants were added at room temperature (about 25° C.) and heated to 120° C. Then the linear diamine (compound d)) was drop wise added. The system was heated to 220° C. for about 1 hour and the water was distilled off under vacuum (30 mbar). Subsequently, nitrogen gas was supplied into the flask to restore atmospheric pressure and the temperature was cooled to 200° C. Then the modifying agent was added to the mixture. After 30 minutes under stirring the final molten mixture was carefully poured out of the flask into a wide non-sticky tray and allowed to cool to room temperature in order to obtain the final coating composition.


Polyamide 1 (P1)

For polyamide 1, 85.2 wt.-% dimer fatty acid (36 carbon atoms), 1 wt.-% stearic acid (18 carbon atoms) and 3.2 wt.-% sebacic acid (10 carbon atoms) were reacted according to the above mentioned procedure with 10 wt.-% of 1,2-ethylene diamine.


Polyamide 2 (P2)

For polyamide 2, 80.5% wt.-% dimer fatty acid (36 carbon atoms), 1% wt.-% stearic acid (18 carbon atoms, linear mono carboxylic acid) and 7 wt.-% tetradecandioic acid (14 carbon atoms, dicarboxylic acid) were reacted according to the above mentioned procedure with 10 wt.-% of 1,2-ethylene diamine.









TABLE 1







(examples and comparative example)
















Ring & ball
Viscosity at


Ex.
Polyamide
Surface modifying agent
COF
softening point
210° C.





1
P1 (99.3 wt.-%)
microcrystalline paraffin
0.34 (3 days)
156.2° C.
7600 mPas




wax (0.2 wt.-%)


2
P1 (98.4 wt.-%)
high surface area fumed
0.34 (3 days)
155.3° C.
7975 mPas




alumina (1.0 wt.-%);




microcrystalline paraffin




wax (0.1 wt.-%)


3
P1 (99.0 wt.-%)
stearyl erucamide
1.01(immediate)
Not
Not




(0.5 wt.-%)
0.21 (3 days)
measured
measured


C4
P2 (99.5 wt.-%)
none
1.15(immediate)
163.5° C.
7900 mPas





0.87 (3 days)


5
P2 (99.2 wt.-%)
microcrystalline paraffin
0.76(immediate)
163.7° C.
8850 mPas




wax (0.3 wt.-%)
0.36 (3 days)


6
P2 (98.7 wt.-%)
microcrystalline paraffin
0.51 (immediate)
163.8° C.
7875 mPas




wax (0.3 wt.-%);
0.39 (3 days)




behenamide (0.5 wt.-%)










Example C4 is a comparative example. All examples additionally contained 0.1 wt.-% Irganox 1010 (BASF AG, Ludwigshafen, Germany) and 0.4 wt.-% Ralox 46 (Raschig GmbH, Ludwigshafen, Germany), both are antioxidants. COF and ring & ball softening point were measured as defined above.


From the experiments, it can be seen that a desired coating, having a low coefficient of friction, is only obtained by employing specific polyamides of the present invention in combination with at least one surface modifying agent.

Claims
  • 1. A thermoplastic coating composition comprising: at least one polyamide, wherein the polyamide comprises a reaction product of: a) at least one dimerized fatty acid;b) at least one mono carboxylic acid;c) at least one linear dicarboxylic acid; andd) at least one linear diamine; and0.1 to 10 wt-%, based on the total weight of the thermoplastic coating composition of at least one surface modifying agent selected from slip agents, anti-blocking agents or combinations thereof.
  • 2. The thermoplastic coating composition according to claim 1, wherein the composition preferably has a coefficient of friction (COF) of 0.2 to 1.1 measured according to ASTM D 1894.
  • 3. The thermoplastic coating composition according to claim 1, wherein the at least one mono carboxylic acid b) is selected from the group consisting of linear C3 to C24 mono carboxylic acids, branched C3 to C24 mono carboxylic acids or combinations thereof.
  • 4. The thermoplastic coating composition according to claim 1, wherein the at least one mono carboxylic acid b) is selected from the group consisting of linear C12 to C18 mono carboxylic acids, branched C12 to C18 mono carboxylic acids or combinations thereof.
  • 5. The thermoplastic coating composition according to claim 1, wherein the at least one linear dicarboxylic acid c) is at least one linear C6 to C18 dicarboxylic acid.
  • 6. The thermoplastic coating composition according to claim 1, wherein the at least one linear dicarboxylic acid c) is at least one linear C10 to C14 dicarboxylic acid.
  • 7. The thermoplastic coating composition according to claim 1, wherein the at least one linear diamine d) is at least one linear aliphatic diamine having C1 to C10 carbon atoms.
  • 8. The thermoplastic coating composition according to claim 1, wherein the at least one linear diamine d) is at least one linear aliphatic diamine having C2 to C6 carbon atoms.
  • 9. The thermoplastic coating composition according to claim 1, wherein the at least one linear diamine d) is 1,2-ethylene diamine.
  • 10. The thermoplastic coating composition according to claim 1, wherein the equivalent ratio of NH2 groups of d) to the sum of the COOH groups of a) to c) is from 1.2:1 to 1:1.2.
  • 11. The thermoplastic coating composition according to claim 1, wherein the surface modifying agent is selected from alumina, silica, glass microspheres, wax, a perfluoro compound, a poly(meth)acrylate, a fatty acid amide, a polysiloxane and combinations thereof.
  • 12. The thermoplastic coating composition according to claim 1, comprising 0.1 wt.-% to 3 wt.-% surface modifying agent based on the total weight of the thermoplastic coating composition.
  • 13. The thermoplastic coating composition according to claim 1, further comprising 0.1 to 20 wt.-%, based on the total weight of the thermoplastic coating composition, of at least one additive different from the surface modifying agent and selected from antioxidants, fillers, pigments, plasticizers, polymers different from the polyamide, tackifiers, and combinations thereof.
  • 14. The thermoplastic coating composition according to claim 1, further comprising 0.1 to 10 wt.-%, based on the total weight of the thermoplastic coating composition, of pigments.
  • 15. The thermoplastic coating composition according to claim 1, having a ring and ball softening point of 90 to 220° C. or of 110 to 190° C. or of 140 to 170° C.
  • 16. An article having an exterior surface and comprising on at least a portion of the surface a coating of the thermoplastic coating composition according to claim 1.
  • 17. The article of claim 16 being a writing utensil, a wooden pencil, a packaging material, a toy, furniture, a decorative plate, or a houseware.
  • 18. An article having an exterior surface selected from a wooden surface, a plastic surface or a wood-plastic-composite surface and comprising on at least a portion of the surface a coating of the thermoplastic coating composition according to claim 1.
  • 19. A method of coating a surface comprising the steps of: providing an article having an external surface;providing the thermoplastic coating composition according to claim 1;melting the thermoplastic coating composition;applying the melted thermoplastic coating composition through an extruder at least a portion of the external surface of the article to form a finished coating; andcooling the coating to a solid state.
  • 20. The method of claim 19 wherein the article is a writing utensil, a wooden pencil, a packaging material, a toy, furniture, a decorative plate, or a houseware and the finished coating is provided by a single application of the melted thermoplastic coating composition to the portion of the external surface of the article.
Priority Claims (1)
Number Date Country Kind
14182296.5 Aug 2014 EP regional
Continuations (1)
Number Date Country
Parent PCT/EP2015/069443 Aug 2015 US
Child 15437050 US