The present invention belongs to the technical field of high polymer materials, and in particular to a polyamide molding composite material, a preparation method and use thereof.
LED light source mainly consists of a semiconductor chip, an LED light source reflection support, gold wire, and a packaging adhesive. The LED light source reflection support is the “framework” of an LED light source, and also is a functional element. LED packaging process is to assemble other materials and components therein through die bonding, wire welding, and packaging adhesive cure. The LED reflection support needs to reflect the light emitted from an LED chip through a certain angle to reduce light loss, and to enable the light to transmit through packaging materials such as an epoxy resin or a silica gel, thus forming a light source for LED illumination or display. The LED reflection support material is a core material of LED illumination and directly concerns the performance and service life of the LED light source.
Several points need to be considered in the selection of the LED reflection support material at the present stage.
First, in the whole packaging process, the LED reflection support needs to be exposed at 150-200° C. for 6-10 h; meanwhile, the packaged lamp beads need to be treated with a surface mount technology (SMT) when prepared to a display screen; the LED support or lamp bead is required to be free of deformation and free of damage under a load during the packaging or SMT process. Moreover, there is a higher demand for the tightness of the LED support material.
Second, in recent years, the LED display screen light source has gradually developed into a small-pitch display screen having a dot pitch of P2.5 below such that research & development and manufacturing of the LED display screen are unremittingly experiencing a great challenge. The small-pitch display screen support is gradually developed into thin wall, multi-mold cavity, and small size, which is more demanding for the mobility of the LED reflection support material, formability of the excessive mold cavities, mechanical strength, and the like.
Third, during use, the LED luminaire or display screen is often affected by severe weather such as high temperature, typhoon, rainstorm, thunder and lightning under different environment. To ensure luminaire or display screen safe and sound in severe weather, there is a higher demand for the dimensional stability of the materials used, and other performances.
Fourth, in the field of LED display application, to ensure the display image clear and keen, the display brightness and contrast ratio are very important indicators. Currently, the solution used on the market more is the LED support produced by the LED reflection support material; the support surface needs to be silk screen printed with black ink; the process is tedious, efficiency is affected and cost is high; however, the surfaces of its side and reflection cup are still white, which reduces the contrast ratio and gray scale displayed by the LED display screen.
Fifth, in terms of light source: on one hand, the wavelength capable of being perceived by ordinary people's eyes ranges within 780-400 nm. Short-wave blue ray having a wavelength of 400-450 nm causes the most serious extent of harm to retina; the blue ray at such a wavelength will increase the amount of toxins in the macular region of eyes, thereby seriously threatening people's eyes health. On the other hand, the light source of the LED full-color display screen consists of three chips, i.e. red (R), green (G), and blue (B), of which the brightness of the blue ray chip is the lowest, i.e., the contrast ratio is the highest. Therefore, the overall contrast ratio of the LED display screen will be directly affected by the reflectivity of chip-based blue ray. LED screen anti blue-ray has popularized to the LED screens of various mobile phones and TVs; ordinary means are to paint an anti-blue ray film on the surface of the screen, but the means has the shortcomings of weak film and high costs, respectively.
Those skilled in the art are mainly focused on the aforesaid first and second points in terms of the improvement of the LED reflection support material. Water absorption rate and size stability of the polyamide molding composite material are concerned less. Moreover, the contrast ratio and gray scale of the LED display screen support are not improved by improving the contrast ratio and gray scale of the material per se.
The objective of the present invention is to overcome the technical shortcomings, and to provide a semi-aromatic polyamide molding composite material; the present invention has a high contrast ratio and a high gray scale and thus, can meet the requirements for the packaging process and long-term reliability.
Another objective of the present invention is to provide use of the aforesaid semi-aromatic polyamide molding composite material.
The present invention is achieved by the following technical solution.
A semi-aromatic polyamide molding composite material includes the following components in parts by weight:
The X unit is not 10T.
The PA10T/X resin is selected from at least one of the group consisting of PA10T/10I, PA10T/6T, PA10T/66, PA10T/1010, PA10T/610, PA10T/612, and PA10T/12T.
Preferably, a crystallization peak width at half maximum ΔT1/2 of the semi-aromatic polyamide molding composite material is measured to be 5-8° C. by differential scanning calorimetry at a cooling rate of 20° C./min after being heated up to 345° C.
The PA10T/X resin in the present invention may be a commercially available product, and also may be synthesized by the following method. To achieve more precise experiment, the PA10T/X used in the examples and comparative examples of the present invention is a homemade sample; raw materials such as reactive monomers and end-capping reagents are commercially available products.
The PA10T/X resin has a number-average molecular weight of 1,500-28,000. The number-average molecular weight is tested by a conventional method, specifically as follows: the number-average molecular weight (Mn) of the PA10T/X resin sample is determined by gel permeation chromatography (GPC). Agilent HPLC-1260 high performance liquid chromatograph, preparation: Eppendorf column oven, Shodex KF-801, 802, 802.5 and 803 GPC columns, differential detector, and G7129A automatic sampler. The molecular weight of the resin is determined at a column temperature of 40° C. using hexafluoroisopropanol as a mobile phase. Data is processed using the cirrus software of a chromatographic work station to obtain the number-average molecular weight distribution Mn.
Preferably, in the resin matrix of the semi-aromatic polyamide molding composite material, the wollastonite has an average diameter of 6-13 μm and an average length of 80-120 μm. Wollastonite is a kind of powder having a certain length-to-diameter ratio, and its length and diameter almost keep the same during the shear melting process of a screw; its microstructure is fibrous. Experiments show that two substances, PA10T and wollastonite (average diameter of 17 μm and average length of 180 μm) are blended by a shear melting process, and then the resin is dissolved out with a solvent; average diameter and average length of wollastonite are tested. It has been found that the diameter of wollastonite is kept the same and its average length changes about 0.5% during the shear process of the screw.
The toner is at least one or a mixture of toners selected from the group consisting of a carbon black toner, a black toner, and an amorphous carbon toner.
Preferably, the toner is selected from an amorphous carbon toner.
Preferably, the semi-aromatic polyamide molding composite material has the reflectivity of less than 4.5% under a 460 nm light source, and more preferably, the semi-aromatic polyamide molding composite material has the reflectivity of less than 3.8% under a 460 nm light source.
The semi-aromatic polyamide molding composite material further includes 0-3 parts of an antioxidant in part by weight; the antioxidant is selected from at least one of the group consisting of hindered phenol antioxidants, hindered amine antioxidants, phosphite ester antioxidants, mercaptan antioxidants, and thiodipropionate antioxidants.
The semi-aromatic polyamide molding composite material of the present invention is for use in preparing an LED display screen light source reflection support.
A method for preparing the semi-aromatic polyamide molding composite material of the present invention includes the following steps: adding components to a blender mixer for uniform mixing, extruding and pelleting the mixed components with a twin-screw extruder to obtain the semi-aromatic polyamide molding composite material, where the screw temperature ranges from 280°° C. to 330° C., and the revolving speed is 450 r/min.
The present invention has the following beneficial effects.
The reflectivity under a 460 nm light source is mainly correlated to the surface roughness (when the surface roughness of an object becomes larger within a certain range, the ray of light emitted from a light source will generate diffuse reflection on the surface of the object, and finally, the energy of the ray of light received on a receiving end is less) and whiteness of materials (the lower the whiteness is, the lower the reflectivity is). The effect of the LED display screen light source reflection support on the gray scale and contrast ratio of the LED display screen mainly lies in whiteness and reflectivity of the light source reflection support. Based on the principle, the semi-aromatic polyamide molding composite material of the present invention is to control the whiteness to be less than 26.5, and to control the reflectivity under a 460 nm light source to be less than 6% (to improve the gray scale and contrast ratio) through the following three aspects. Moreover, the semi-aromatic polyamide molding composite material of the present invention has the advantages of long-term packaging stability (tightness) and low blue ray of the LED screen packaged.
First, compared with other inorganic fillers, wollastonite enables the surface roughness of the semi-aromatic polyamide molding composite material workpiece to a reasonable range of reducing reflection of a 460 nm light, i.e., the reflectivity under a 460 nm light source is reduced; and meanwhile, the tightness with hardware is improved. The preferable size distribution of the wollastonite in the resin matrix can further reduce the reflectivity under a 460 nm light source (to reduce the blue ray of the LED display screen), and improve its tightness with hardware.
Second, the color of material is adjusted with a toner to obtain the black with good light absorption effect; preferably, the amorphous carbon toner can further reduce the whiteness and improve the light absorption, thereby reducing the reflectivity under a 460 nm light source.
Third, through experimental findings, the crystallization peak width at half maximum of the semi-aromatic polyamide molding composite material also will obviously affect the reflectivity under a 460 nm light source of the composite material; when the crystallization peak width at half maximum ΔT1/2 of the composite material is 4-11° C., the surface of the prepared workpiece has a low reflectivity under a 460 nm light source. In the technical solution of the present invention, the crystallization peak width at half maximum of the semi-aromatic polyamide molding composite material is mainly adjusted by the amount and specification of the toner and wollastonite added, and also can be obtained by adjusting the number-average molecular weight of the semi-aromatic polyamide resin. On the other hand, the excellent tightness is achieved by adjusting the crystallization peak width at half maximum of the PA10T/X molding composite material, the specification of the wollastonite, and surface roughness.
The semi-aromatic polyamide molding composite material of the present invention has no need for painting a light-absorbing paint or matting additionally, and thus reduces the cost of the LED display screen light source support.
The present invention will be further described with reference to the detailed examples. The following examples will help those skilled in that art further understand the present invention, but are not construed as limiting the scope of the present invention in any form. It should be indicated that those skilled in the art can further make several deformations and improvements in the premise of not departing from the inventive concept. These all fall within the protection scope of the present invention.
Raw materials used in the examples and comparative examples are as follows.
Monomers used in the polymerization of the following polyamides are commercially available products which are polymerized pure.
Methods for preparing the semi-aromatic polyamide molding composite materials in examples and comparative examples: PA10T/X resin, wollastonite, toner and antioxidants were added to a blender mixer and mixed well, extruded and pelleted with a twin-screw extruder to obtain the semi-aromatic polyamide molding composite material, where the screw temperature ranged from 280°° C. to 330° C., and the revolving speed was 450 r/min.
As can be seen from Examples 1-6, when the crystallization peak width at half maximum of the semi-aromatic polyamide molding composite material is controlled within the preferable range by adjusting the amount of the wollastonite added, the tightness grade is higher and the reflectivity is low.
As can be seen from Examples 4/7-10, whiteness and reflectivity are reduced by adjusting the amount of the toner used.
As can be seen from Examples 4/13-17, preferably, the wollastonite has an average diameter of 6-14 μm and an average length of 80-120 μm; even though the crystallization peak width at half maximum of the composite material is not within the range of 5-8° C., the tightness grade may be further increased and the reflectivity is reduced; the toner is preferably an amorphous carbon toner.
As can be seen from Examples 4/18-24, by adjusting wollastonite and toner, the semi-aromatic polyamide resin having different initial crystallization peak widths at half maximum enables the crystallization peak width at half maximum to be within different ranges, thus obtaining semi-aromatic polyamide molding composite materials having different tightness grades and reflectivity.
As can be seen from Comparative Examples 1/2/3, in the PA10T/X repeating unit, the X content significantly affects the tightness grade; due to the change of the surface property, the reflectivity also increases therewith, and the tightness is affected significantly.
As can be seen from Comparative Example 4, wollastonite may not be replaced by talc powder.
As can be seen from Comparative Example 5, too low content of wollastonite may not enable the crystallization peak width at half maximum to be adjusted to be 4-11° C.; the tightness grade is not only poor, but also the reflectivity is high.
As can be seen from Comparative Example 6, even though the crystallization peak width at half maximum ranges from 4° C. to 11° C., the tightness grade and reflectivity are poor when the content of wollastonite is excessive. This is because too much wollastonite damages the surface structure of the composite material; moreover, as wollastonite is a kind of white powder, too much amount may increase the whiteness on the contrary.
As can be seen from Comparative Example 7, too low content of the toner may lead to a too high whiteness and a high reflectivity.
As can be seen from Comparative Example 8, too much toner added may lead to the enrichment of too much toner onto the surface, thereby affecting the tightness and reflectivity.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202111097912.1 | Sep 2021 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2022/118970 | 9/15/2022 | WO |