Patent Application
20230332347
The invention relates to a water-repellent fabric and its preparation method, in particular to a fabric modified by polyamino acid grafting, belonging to the technical field of special functional textiles and their preparation.
With the improvement of people's living standards, people's requirements for modern textiles are becoming higher and higher. Therefore, textiles are becoming more functional. For example, it's hoped that textiles can be waterproof, windproof, antibacterial, anti-ultraviolet and of other functions. In order to meet people's demand for textiles, the surfaces of some natural or man-made fibers must be modified to make textiles functional.
At present, the surface modification of fiber mainly includes physical modification and chemical modification. Physical modification mainly includes y radiation induction, surface coating, ultrasonic impregnation and plasma treatment, etc., while chemical modification can mainly be divided into surface etching and surface grafting (atom transfer radical polymerization, etc.) according to different modes of action. Among them, y radiation induction, atom transfer radical polymerization and other treatment methods have the problems of difficult operation, complex process, strict equipment requirements, high cost and easy to damage fibers. In contrast, the method of coating modification on the surface of the fabrics is simple and easy to operate, which is to evenly coat one or more layers of polymer compounds that can form a film on the surface of the fabric. However, the durability of the water-accumulating function obtained by the coating treatment of the fabric is not good.
The invention applies the ring-opening polymerization method to the surface modification of fiber materials, and discloses a water-repellent fabric modified by polyamino acid grafting and its preparation method, which causes the fiber surface to initiate and induce the ring-opening polymerization of aniline acid anhydride monomers. By controlling the treatment process, a surface hydrophobic modified fabric is obtained on the premise that the strength, permeability, whiteness, hand feeling and other properties of the fabric (or fiber) are not affected. In view of the unsatisfactory durability of the water-repellent fabric at present, the present invention forms a hydrophobic graft chain, which can provide the water-repellent function and durable water repellency.
The technical scheme for realizing the purpose of the invention is: a polyamino acid-grafted modified water-repellent fabric, and the polyamino acid-grafted modified water-repellent fabric comprises a fabric and a polyamino acid graft chain on the fabric surface; the chemical structure of the polyamino acid graft chain is as follows.
Wherein, R1, R2, R3 are independently selected from H, —CH3, —CH2CH3 or —CF3; R4 is —CH3 or —CH2CH3; R5 is —CH2— or —CH2CH2CH2NH—; X is 0 or NH; n=3˜200.
The fabric of the invention is one or several of cotton fabric, linen fabric, wool fabric and silk fabric; the fiber in the fabric is any one or several of cotton, linen, wool, silk, etc. which is subject to polyamino acid grafting modification.
The preparation method of the polyamino acid-grafted modified water-repellent fabric includes the following steps: mixing the amino-pretreated fabric with aniline acid anhydride to obtain the polyamino acid-grafted modified water-repellent fabric; the aniline acid anhydride is as follows.
Wherein: R1, R2, R3 are independently selected from H, —CH3, —CH2CH3 or —CF3; R4 is —CH3 or —CH2CH3.
In the present invention, the amino-pretreated fabric is added to the reactor, and then aniline acid anhydride is added to initiate ring-opening polymerization on the surface of the fiber to graft and modify the fiber; the reaction temperature is 0˜80° C., preferably the room temperature ˜70° C., and the time is 1˜120 h, preferably 24˜60 h; preferably, the reaction temperature is a four-step temperature rise, such as room temperature +(30˜50° C.)+(50˜60° C.)+(60˜70° C.), and the temperature difference between adjacent steps is 5˜25° C.
Further, after the ring-opening polymerization on the surface of fiber is completed, the modified fabric is taken out, washed in water, and then dried to obtain the polyamino acid-grafted modified water-repellent fabric.
In the present invention, the amino-pretreated fabric is the fabric treated by amino silane coupling agent. The amino silane coupling agent is hydrolyzed in the mixed solvent of water/ethanol to obtain the hydrolysate, and the fabric is put into the hydrolysate for reaction to obtain the pretreated fabric with amino groups on the surface of fiber, which is the amino-pretreated fabric; the amino silane coupling agent is any of aminopropyltriethoxysilane, aminopropyltrimethoxysilane, aminoethylaminopropyltriethoxysilane, and aminoethylamino-propyltrimethoxysilane; the volume ratio of water and ethanol is 1:4˜20, preferably 1:8˜10, and the dosage of amino silane coupling agent is 0.5˜20% of the weight of the fabric, preferably 5˜15%; the hydrolysis time is 0.1˜24 h, preferably 1˜12 h; the hydrolysis temperature is 5˜45° C., preferably 20˜30° C.; the PH value required for hydrolysis is 7-11, preferably 8-10, which can be adjusted with conventional ammonia. The reaction temperature is room temperature ˜100° C., preferably 50˜60° C.; the reaction time is 30 min˜24 h, preferably 1 h˜3 h.
In the present invention, N-phenyl-tert-butyloxycarboxyglycine is subject to the cyclization reaction under nitrogen protection to obtain aniline acid anhydride; the N-phenyl-tert-butyloxycarboxyglycine is as follows.
Among them, R1, R2, R3 are independently selected from H, —CH3, —CH2CH3 or —CF3; R4 is —CH3 or —CH2CH3.
Specifically, N-phenyl-tert-butyloxycarbonylglycine is dissolved in anhydrous solvent, a cyclizing agent is added under the nitrogen protection, and then the cyclization reaction is carried out to generate aniline acid anhydride; the cyclizing agent is PCl3; the anhydrous solvent is anhydrous dichloromethane, anhydrous trichloromethane or anhydrous tetrachloroethane; it is preferred to add cyclizing agent in 2˜10 batches, preferably in 3˜5 batches; the temperature of adding cyclizing agent is −20˜45° C., preferably −5˜5° C.; the temperature of cyclization reaction is 5˜45° C., preferably 20˜30° C.; the time is 0.1 to 48 hours, preferably 12 to 24 hours.
In the present invention, N-phenyl amino acid reacts with Boc anhydride in the presence of acid-binding agent to obtain N-phenyl-tert-butyloxycarboxyglycine; the acid-binding agent is triethylamine or pyridine; the reaction temperature is 5˜45° C. and the time is 0.1˜24 h. Furthermore, the molar ratio of N-phenyl amino acid to Boc anhydride is 1:2.5. Preferably, the Boc anhydride solution is added dropwise to the mixture of N-phenyl amino acid solution and acid-binding agent for the addition-elimination reaction to obtain N-phenyl-N-tert-butyloxycarbonyl glycine; the adding time of Boc anhydride solution is 20˜120 min, preferably 30˜60 min. In N-phenyl amino acid solution, the solvent is water/1,4-dioxane, and the volume ratio of water and dioxane is 1:1˜2, preferably 1:1˜1.5; in Boc acid anhydride solution, the solvent is any of 1,4-dioxane, tetrahydrofuran or ether. The reaction temperature of N-phenyl amino acid with Boc acid anhydride is 5˜45° C., preferably room temperature; the reaction time is 0.1˜24 h, preferably 12˜18 h.
The invention discloses the application of the polyamino acid-grafted modified water-repellent fabric in the preparation of water-repellent materials; the water-repellent material has washing durability and degradability.
Compared with the prior art, the beneficial effects of the technical scheme provided by the invention are as follows.
The present invention discloses the preparation method of the hydrophobic fabric, including the following steps.
Addition-elimination reaction: N-phenyl amino acid undergoes addition-elimination reaction with Boc acid anhydride in mixed solvent to form the intermediate N-phenyl-tert-butyloxycarbonyglycine.
PCI3 cyclization: N-phenyl-tert-butyloxycarbonylglycine is cyclized by carbonyl group and Boc group under the action of the cyclizing agent PCI3 to form N-aniline acid anhydride.
Fabric pretreatment: The fabric is pretreated with the hydrolysate of amino silane coupling agent to introduce the active amino group to the fabric fiber surface.
Ring-opening polymerization: the ring-opening polymerization of N-aniline acid anhydride monomer is induced on the surface of the fiber to form graft chain.
The modified fabric is taken out, washed in water, and dried to obtain the polyamino acid-grafted modified hydrophobic fabric.
The raw materials involved in the present invention are commercially available conventional products, and the specific preparation method and test operation are conventional methods. Unless otherwise specified, they are carried out at room temperature and conventional environment. The fabrics used for amino pretreatment are conventional fabrics, untreated and hydrophilic.
With reference to the accompanying drawings and embodiment, the technical scheme of the present invention will be described in detail.
(1) Synthetize N-trifluorophenyl-N-tert-butyloxycarbonyl glycine.
2500 mL single neck flask with magnetic stirrer. 52 g of N-(Trifluoromethyl) phenylglycine was taken to dissolve in the mixed solution of 800 mL of water/1,4-dioxane (the volume ratio of water and dioxane is 1:1) until it was completely transparent, then 184 mL of triethylamine solution was added with a syringe, and 400 mL of 1,4-dioxane solution containing 142 g of Boc acid anhydride was added dropwise for 40 min. The reaction happened after stirring at room temperature for 16 h, extract twice with 500 mL of n-hexane, add 800 mL of 1 N HCl solution to make it acidic, and then extract the product with 2×300 mL of ethyl acetate solution. Combined with organic phase, the organic layer was washed with 800 mL saline, washed with deionized water three times, dried with anhydrous magnesium sulfate, filtered, and distilled under reduced pressure to remove the solvent and obtain 45.3 g black-brown viscous product with a yield of 61.1%.
(2) Synthetize N-Trifluoromethyl Aniline Acid Anhydride.
Under nitrogen atmosphere, the product from above (1) was dissolved in 900 mL of anhydrous dichloromethane, the solution was cooled to 0° C. in a low-temperature reactor, and 46.0 g of PCl3 solution was added into the reaction solution in three batches (16 g+15 g+15 g) through a syringe, with an interval of 15 min. The reaction solution was stirred at 0° C. for 1 h, and then transferred to room temperature for reaction for 15 hours. The solvent was removed in vacuum, and the obtained solid was dissolved in 300 mL of anhydrous dichloromethane, filtered, and the filtrate was evaporated to obtain about 23.3 g of light yellow crude product solid, with a yield of 69%. 23.0 g of light yellow solid was recrystallized in the mixed solution of anhydrous dichloromethane/n-hexane, and finally 12.9 g of white solid product (p-trifluorophenyl) aniline acid anhydride for polymerization was obtained, with a yield of 49.1%.
(3) Fabric Pretreatment.
The amino silane coupling agent aminopropyltriethoxysilane was dissolved in the mixed solution of water/ethanol (the volume ratio of water and ethanol was 1:9), the pH of the solution was adjusted to 10 with 10% ammonia, and the transparent hydrolysate of the amino silane coupling agent was obtained by hydrolysis at room temperature for 3 h, and then a 300 g round cotton fabric was subjected to water bath reaction in the above-mentioned 400 mL amino silane coupling agent hydrolysate (the amount of the amino silane coupling agent is 6% of the weight of the fabric) with the water bath temperature of 50° C. and the reaction time of 120 min. After the reaction was completed, the fabric was taken out, washed three times, dried at 60° C. and baked at 120° C. for 3 min to obtain the pretreated cotton fabric.
(4) Preparation of Water-Repellent Fabric.
3.1 g of the white solid product N-trifluoromethyl aniline acid anhydride in step (2) was taken and completely dissolved in 450 mL of N, N-dimethyl formamide (DMF) solution. And the pretreated fabric was added into the DMF solution for reaction at room temperature for 4 h. Then it was heated to 50° C. for reaction for 8 h, then to 60° C. for reaction for 12 h, finally to 70° C. for reaction for 12 h, and the total grafting reaction time was 48 h. After the reaction was completed, the fabric was taken out to terminate the reaction, washed three times, cleaned by conventional ultrasonic for 15 min, and then dried at 60° C. to obtain water-repellent cotton fabric. The structure diagram is shown in
(5) Soaping Fastness Test
After the treated fabric was soaped in accordance with GB/T 3921˜2008 Textiles—Tests for color fastness—Color fastness to washing with soap or soap and soda, the grafted modified fabric was tested for soaping durability.
(6) Contact Angle Test.
DSA100 Automatic Microscopic Droplet Wettability Tester from German Kruss was used to test the wettability of coated fabric before and after the soaping. Water was selected as the test droplet, and the volume of the droplet was 5 μL and the average of five tests was taken. The contact angles of acid anhydride on the finished fabric surface by the ring-opening polymerization before and after soaping were 145.4° and 141.6°, respectively. The hydrophobic property of the finished fabric was still available after soaping, indicating that the finishing durability was good.
(7) Degradability Test.
The sample of water-repellent fabric was cut into round fabrics with a diameter of about 10 mm, washed with ethanol and deionized water sequentially, and then dried in vacuum for 24 hours at 37° C. for standby. Papain was used as proteolytic enzyme. The protease was activated in 0.01M cysteine, 0.04M EDTA buffer solution (pH8.0), and the concentration was 1 mg enzyme/ml solution. A pipette was used to remove 3 mL of enzyme solution and added into the corresponding orifice of the culture plate. Then the round fabric was weighed and placed into the orifice of the culture plate to ensure that the sample was completely immersed in the enzyme solution. After degradation for a certain time, samples were taken out and cleaned with a large amount of deionized water, then vacuum dried at 37° C. for 24 h, and weighed and recorded.
The calculating formula of weight loss rate is as follows.
The mass residual rate of the water-repellent fabric was 30.3% after 72 h degradation.
(1) Synthetize N-phenyl-N-tert-butyloxycarbonyl glycine.
2500 mL single neck flask with magnetic stirrer. 40 g of N-phenylglycine was taken to dissolve in the mixed solution of 800 mL of water/1, 4-dioxane (the volume ratio of water and dioxane is 1:1) until it was completely transparent, then 184 mL of triethylamine solution was added with a syringe, and 400 mL of 1,4-dioxane solution containing 142 g of Boc acid anhydride was added dropwise for 40 min. The reaction happened after stirring at room temperature for 16 h, extract the solvent twice with 500 mL of n-hexane, add 800 mL of 1 N HCl solution to make it acidic, and then extract the product with 2×300 mL of ethyl acetate solution. Combined with organic phase, the organic layer was washed with 800 mL saline, washed with deionized water three times, dried with anhydrous magnesium sulfate, filtered, and distilled under reduced pressure to remove the solvent and obtain 42.4 g black-brown viscous product with a yield of 64.3%.
(2) Synthetize N-aniline Acid Anhydride.
Under nitrogen atmosphere, the product from above (1) was dissolved in 900 mL of anhydrous trichloromethane, the solution was cooled to 0° C. in a low-temperature reactor, and 46.0 g of PCl3 solution was added into the reaction solution in three batches (16 g+15 g+15 g) through a syringe, with an interval of 15 min. The reaction solution was stirred at 0° C. for 1 h, and then transferred to room temperature for reaction for 16 hours. The solvent was removed in vacuum, and the obtained solid was dissolved in 300 mL of anhydrous dichloromethane, filtered, and the filtrate was evaporated to obtain about 21.0 g of light yellow crude product solid, with a yield of 70%. 21.0 g of light yellow solid was recrystallized in the mixed solution of anhydrous trichloromethane/n-hexane, and finally 10.1 g of white solid product for polymerization was obtained, with a yield of 47.6%. See
(3) Fabric Pretreatment.
The amino silane coupling agent aminopropyltriethoxysilane was dissolved in the mixed solution of water/ethanol (the volume ratio of water and ethanol was 1:9), the pH of the solution was adjusted to about 10 with 10% ammonia, and the transparent hydrolysate of the amino silane coupling agent was obtained by hydrolysis at room temperature for 3 h, and then a 300 g round linen fabric was subjected to water bath reaction in the above-mentioned 400 mL amino silane coupling agent hydrolysate (the amount of the amino silane coupling agent is 6% of the weight of the fabric) with the water bath temperature of 50° C. and the reaction time of 120 min. After the reaction was completed, the fabric was taken out, washed three times, dried at 60° C. and baked at 120° C. for 3 min to obtain the pretreated linen fabric.
(4) Preparation of Water-Repellent Linen Fabric.
3.1 g of the white solid product N-aniline acid anhydride in step (2) was taken and completely dissolved in 450 mL of N, N-dimethyl formamide (DMF) solution. And the pretreated fabric was added into the DMF solution for reaction at room temperature for 4 h. Then it was heated to 50° C. for reaction for 8 h, then to 60° C. for reaction for 12 h, finally to 70° C. for reaction for 12 h, and the total grafting reaction time was 48 h. After the reaction was completed, the linen fabric was taken out to terminate the reaction, washed three times, cleaned by conventional ultrasonic for 15 min, and then dried at 60° C. to obtain water-repellent linen fabric. The infrared spectrum of the tested fabric surface is shown in
(5) Soaping Fastness Test
After the treated fabric was soaped in accordance with GB/T 3921˜2008 Textiles—Tests for color fastness—Color fastness to washing with soap or soap and soda, the grafted modified fabric was tested for soaping durability.
(6) Contact Angle Test.
DSA100 Automatic Microscopic Droplet Wettability Tester from German Kruss was used to test the wettability of coated fabric before and after the soaping. Water was selected as the test droplet, and the volume of the droplet was 5 μL and the average of five tests was taken. The contact angles of acid anhydride on the finished fabric surface by the ring-opening polymerization before and after soaping were 141.2° and 140.1°, respectively. The hydrophobic property of the finished fabric was still available after soaping as shown in
(7) Degradability Test.
The sample of water-repellent fabric was cut into round fabrics with a diameter of about 10 mm, washed with ethanol and deionized water sequentially, and then dried in vacuum for 24 hours at 37° C. for standby. Papain was used as proteolytic enzyme. The protease was activated in 0.01M cysteine, 0.04M EDTA buffer solution (pH8.0), and the concentration was 1 mg enzyme/ml solution. A pipette was used to remove 3 mL of enzyme solution and added into the corresponding orifice of the culture plate. Then the round fabric was weighed and placed into the orifice of the culture plate to ensure that the sample was completely immersed in the enzyme solution. After degradation for a certain time, samples were taken out and cleaned with a large amount of deionized water, then vacuum dried at 37° C. for 24 h, and weighed and recorded.
The calculating formula of weight loss rate is as follows.
The mass residual rate of the water-repellent fabric was 38.1% after 72 h degradation.
The N-aniline acid anhydride in step (4) was replaced with N-trifluoromethyl aniline acid anhydride anhydride, and the rest remained unchanged. The surface contact angles of water-repellent linen fabric before and after soaping were 141.9° and 139.3°, respectively.
(1) For the silk fabric pretreated with aminopropyltriethoxysilane prepared according to step (3) of embodiment 2, the linen fabric was replaced with mulberry silk fabric, while the rest remained unchanged.
0.25 g of the N-aniline acid anhydride (prepared in Embodiment 2) was taken and dissolved in 45 mL tetrahydrofuran (THF), and the silk fabric pretreated with aminopropyltriethoxysilane was added to the THF solution for reaction at room temperature for 2 h. Then it was heated to 30° C. for reaction for 4 h, then to 50° C. for reaction for 12 h, finally to 60° C. for reaction for 12 h, and the total grafting reaction time was 24 h. After the reaction was completed, the fabric was taken out to terminate the reaction, washed three times, cleaned by conventional ultrasonic for 15 min, and then dried at 60° C. to obtain water-repellent silk fabric. The graft chain structure of polyamino acid on the surface of the fiber is as follows (wavy line is fiber, n is 30˜70).
(2) Soaping Fastness Test
After the treated fabric was soaped in accordance with GB/T 3921˜2008 Textiles—Tests for color fastness—Color fastness to washing with soap or soap and soda, the grafted modified silk fabric was tested for soaping durability.
(3) Contact Angle Test.
DSA100 Automatic Microscopic Droplet Wettability Tester from German Kruss was used to test the wettability of coated fabric before and after the soaping. Water was selected as the test droplet, and the volume of the droplet was 5 μL and the average of five tests was taken. The contact angles of acid anhydride on the finished fabric surface by the ring-opening polymerization before and after soaping were 142.7° and 139.8°, respectively. The hydrophobic property of the finished fabric was still available after soaping as shown in
(4) Degradability Test.
The sample of water-repellent fabric was cut into round fabrics with a diameter of about 10 mm, washed with ethanol and deionized water sequentially, and then dried in vacuum for 24 hours at 37° C. for standby. Papain was used as proteolytic enzyme. The protease was activated in 0.01M cysteine, 0.04M EDTA buffer solution (pH8.0), and the concentration was 1 mg enzyme/ml solution. A pipette was used to remove 3 mL of enzyme solution and added into the corresponding orifice of the culture plate. Then the round fabric was weighed and placed into the orifice of the culture plate to ensure that the sample was completely immersed in the enzyme solution. After degradation for a certain time, samples were taken out and cleaned with a large amount of deionized water, then vacuum dried at 37° C. for 24 h, and weighed and recorded.
The calculating formula of weight loss rate is as follows.
The mass residual rate of the water-repellent silk fabric was 22.8% after 72 h degradation. See
Controls 1
(1) Preparation of Water-Repellent Silk Fabric.
The fluorine-containing water-repellant finishing agent E-061, purchased from 3M Company, was diluted into a finishing solution with a mass concentration of 30 g/L with deionized water. The mulberry silk fabric was moistened with distilled water and put into the finishing solution (bath ratio 1:20), and soaked for 15 min.
Finishing process flow: two soakings and two rollings (rolling rate: 80%)→pre-baking (90° C., 3 min)→baking (155° C., 2 min)→finishing silk fabric.
(2) Soaping Fastness Test
After the treated fabric was soaped in accordance with GB/T 3921˜2008 Textiles—Tests for color fastness—Color fastness to washing with soap or soap and soda, the grafted modified silk fabric was tested for soaping durability.
(3) Contact Angle Test.
DSA100 Automatic Microscopic Droplet Wettability Tester from German Kruss was used to test the wettability of coated fabric before and after the soaping. Water was selected as the test droplet, and the volume of the droplet was 5 μL and the average of five tests was taken. The contact angles of acid anhydride on the finished fabric surface before and after soaping were 136.8° and 108.1°, respectively. After soaping, the contact angle decreased a lot, the hydrophobic property decreased, and the finishing durability was poor.
(4) Degradability Test.
The sample of water-repellent fabric was cut into round fabrics with a diameter of about 10 mm, washed with ethanol and deionized water sequentially, and then dried in vacuum for 24 hours at 37° C. for standby. Papain was used as proteolytic enzyme. The protease was activated in 0.01M cysteine, 0.04M EDTA buffer solution (PH8.0), and the concentration was 1 mg enzyme/ml solution. A pipette was used to remove 3 mL of enzyme solution and added into the corresponding orifice of the culture plate. Then the round fabric was weighed and placed into the orifice of the culture plate to ensure that the sample was completely immersed in the enzyme solution. After degradation for a certain time, samples were taken out and cleaned with a large amount of deionized water, then vacuum dried at 37° C. for 24 h, and weighed and recorded.
The calculating formula of weight loss rate is as follows.
Wherein: Wo is the mass of the fabric before degradation, Wi is the mass after degradation.
The mass residual rate of the water-repellent silk fabric was 98.1% after 72 h degradation. See
The mass residual rate of the untreated mulberry silk fabric was 16.1% after 72 h degradation.
When the above mulberry silk fabric was replaced with silk fabric pretreated with aminopropyltriethoxysilane (Embodiment 3), and the rest remained unchanged, the contact angles of acid anhydride on the finished fabric surface of the silk fabric treated with E-061 before and after soaping were 137.3° and 106.5°, respectively. After soaping, the contact angle decreased a lot, the hydrophobic property decreased, and the finishing durability was poor.
Controls 2
On the basis of embodiment 2, the condition of reaction time of 4 h at room temperature, 8 h at 50° C., 12 h at 60° C., and 12 h at 70° C., and the total grafting reaction time of 48 h was replaced by 48 h at room temperature; and the rest remained unchanged, the water contact angles on the surface of the water-repellent linen fabric before and after soap washing were 134.7° and 130.5°, respectively.
On the basis of embodiment 2, the condition of reaction time of 4 h at room temperature, 8 h at 50° C., 12 h at 60° C., and 12 h at 70° C., and the total grafting reaction time of 48 h was replaced by 48 h at 60° C.; and the rest remained unchanged, the water contact angles on the surface of the water-repellent linen fabric before and after soap washing were 130.9° and 122.3°, respectively.
The present invention can initiate and induce the ring-opening polymerization of aniline-containing acid anhydride on the surface of the pretreated fiber to form a graft chain, and has good water repellency, especially excellent washing durability and degradability. The existing ring-opening polymerization method for grafting modification of material surface is mainly about the grafting modification of the surfaces of silicon-based materials or metal materials. There are few literature reports on the research of using ring-opening polymerization method to obtain modification and functionality on the fiber surface. The ring-opening polymerization of the present invention changes from a ring compound monomer to a linear polymer through ring-opening reaction, and the reaction conditions are relatively mild; the side reaction is less than the polycondensation reaction, and it is easy to obtain the high molecular weight polymer, and the ring-opening polymerization does not release as much energy as the addition reaction. The thermal effect of the polymerization process is caused by the change of the ring tension, which can control the chemical composition of the surface of the base material to obtain the modification and functionality.
| Number | Date | Country | Kind |
|---|---|---|---|
| 202011043939.8 | Sep 2020 | CN | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/CN2021/074016 | 1/27/2021 | WO |