POLYCARBONATE RESIN COMPOSITION AND OPTICAL MOLDED PRODUCT INCLUDING THE SAME

Information

  • Patent Application
  • 20200239691
  • Publication Number
    20200239691
  • Date Filed
    April 18, 2019
    4 years ago
  • Date Published
    July 30, 2020
    3 years ago
Abstract
Provided are a polycarbonate resin composition comprising a polycarbonate resin, pentaerythritol tetrastearate, a black dye, and a blue dye, and an optical molded product comprising same.
Description
CROSS-REFERENCE TO RELATED APPLICATION(S)

This application claims the benefit of the filing date of Korean Patent Application No. 10-2018-0055589 filed with Korean Intellectual Property Office on May 15, 2018, the entire content of which is incorporated herein by reference.


TECHNICAL FIELD

The present invention relates to a polycarbonate resin composition having excellent thermal stability and optical properties, and an optical molded product including the same.


BACKGROUND ART

Polycarbonate resins are excellent in physical properties such as impact strength, dimensional stability, heat resistance, and transparency, and thus are used in many applications such as for exterior materials of electronic and electrical products, automobile parts, building materials, optical parts, and the like.


Recently, as the field of application of these polycarbonates has expanded, there has been a need to develop novel polycarbonates having improved thermal stability and optical properties while maintaining the physical properties inherent to polycarbonates.


In particular, when applied to optical products, since it is important to maintain a desired level of optical properties (excellent shielding rate or transmittance) without deformation of the product even under high temperature conditions, the development of technologies for simultaneously improving thermal stability and optical properties is needed.


Accordinaly, attempts have been made to introduce monomers having different structures into the main chain of polycarbonates by copolymerizing aromatic diols having different structures, or to obtain desired physical properties by using additional additives.


However, most technologies have a high production cost, and have limitations, for example, when the chemical resistance, heat resistance, and the like are increased, conversely, the optical properties are deteriorated, and when the optical properties are improved, the chemical resistance, heat resistance, and the like are decreased.


In addition, it is necessary to adjust the transparency of the polycarbonates depending on the applicable product group. For example, when applied to an optical product (for example, a lens) or the like, it is necessary to reduce the transmittance in a specific wavelength range in accordance with the purpose of use.


Therefore, there is still a need for research and development of a novel polycarbonate having excellent heat resistance while satisfying desired optical properties (excellent shielding rate or transmittance) depending on the products to which polycarbonate is applied.


DETAILED DESCRIPTION OF THE INVENTION
Technical Problem

An object of the present invention is to provide a polycarbonate resin composition having excellent heat resistance and excellent optical properties by introducing a specific additive and a combination of two kinds of dyes.


Another object of the present invention is to provide an optical molded product produced from the above-mentioned polycarbonate resin composition.


Technical Solution

In one aspect of the invention, a polycarbonate resin composition including: a polycarbonate resin having a melt flow rate (MFR) of 5 to 15 g/10 min according to ASTM D1238; pentaerythritol tetrastearate; a black dye; and a blue dye, wherein transmittance at 410 nm according to ASTM D1003 is 7% or less, and wherein a change in yellowness index expressed by General Equation 1 described later is 0.5 or less, is provided.


In another aspect of the invention, an optical molded product including the above-mentioned polycarbonate resin composition is provided.


Hereinafter, a copolycarbonate, a process for producing the same, and a molded product including the same according to specific embodiments of the invention will be described in more detail.


Unless explicitly specified otherwise in this specification, the terms are only for describing specific embodiments and are not intended to limit the present invention.


As used herein, the singular forms “a”, “an”, and “the” are intended to include the plural forms as well, unless the context clearly indicates otherwise.


The terms “comprises”, “comprising”, “includes”, and/or “including”, when used herein, specify the presence of stated features, regions, integers, steps, operations, elements, and/or components, but do not preclude the presence or addition of other features, regions, integers, steps, operations, elements, components, and/or groups thereof.


Terms including ordinal numbers such as “first”, “second”, etc. are used only for the purpose of distinguishing one component from another component, and are not limited by the ordinal numbers.


For instance, a first component can be referred to as a second component, or similarly, the second component can be referred to as the first component, without departing from the scope of the present invention.


In the case of a polycarbonate resin, it is necessary to adjust the transparency of a polycarbonate according to the applied product group. For example, when applied to an optical product (for example, a lens) or the like, it is necessary to reduce the transmittance in a specific wavelength range in accordance with the purpose of use.


However, when an additive is used for the purpose of simply increasing the shielding rate, there is a problem that the heat resistance is remarkably lowered under high temperature conditions, and deformation or discoloration of the polymer occurs during the production process.


In this regard, the present inventors have realized low transmittance in a specific wavelength range and a low change in yellowness index under high temperature conditions by using a specific additive and two types of dyes having excellent absorption rates at a predetermined wavelength in combination, and thus have developed a polycarbonate resin composition having excellent heat resistance and a high shielding rate in a specific wavelength range.


When a product is produced using the above-mentioned polycarbonate resin composition of the present invention, the degree of denaturation and hue change of the polymer is remarkably small even during high temperature injection molding conditions in the production process.


In addition, even if the product is actually used and subjected to high temperature environments, it can exhibit excellent physical properties without deformation.


In particular, when used as a lens, it can exhibit an excellent shielding rate in a specific visible light region (410 nm), and thus can be used for a wide range of applications such as general use, industrial use, sports use, special use, and the like, which is preferable.


The polycarbonate resin composition according to one embodiment of the present invention satisfies a transmittance at 410 nm of 7% or less according to ASTM D1003.


By simultaneously satisfying both the transmittance in the above range and the change in yellowness index described later, it is possible to satisfy all the above-mentioned physical properties when applied to a product.


When the transmittance at 410 nm is more than 7%, there is a problem that it is not possible to apply to various optical molded products such as general use, industrial use, sports use, and special use.


Further, the transmittance at 410 nm can preferably satisfy 5% or less, and more preferably 4.5% or less. In this case, effects intended by the present invention can be increased.


The polycarbonate resin composition according to one embodiment of the invention satisfies a change in yellowness index represented by the following General Equation 1 of 0.5 or less, and by simultaneously satisfying the change in yellowness index (ΔYI) and the transmittance in the above range, it is possible to satisfy all the physical properties when applied to products.





ΔYI=YI (340° C.)−YI (285° C.)   [General Equation 1]


Herein, YI is the yellowness index value measured according to ASTM D1925 at the corresponding temperature.


When a product is produced using the polycarbonate resin composition, the parameter of change in yellowness index (ΔYI) in the above range means an index showing excellent heat resistance even in a high temperature injection process. This means that even when there is a temperature change at high temperatures from 285° C. to 340° C., it shows a remarkably low change in yellowness index, and thus exhibits excellent heat resistance not only in the product manufacturing process but also even if the product is used while subjected to high temperature environmental conditions.


When the change in yellowness index is more than 0.5, the heat resistance is lowered and the transmittance is lowered, which is not suitable for use as a lens.


Further, the change in yellowness index can preferably satisfy 0.3 or less, and more preferably 0.1 or less. In this case, effects intended by the present invention can be increased.


A polycarbonate resin composition according to one embodiment of the present invention includes: a polycarbonate resin; pentaerythritol tetrastearate; a black dye; and a blue dye, thereby satisfying the above-mentioned specific parameter values.


In the following, specific properties of each component will be described in more detail.


Polycarbonate Resin


As used herein, the term “polycarbonate” refers to a polymer that is prepared by reacting a diphenol-based compound, a phosgene, a carbonate ester, or a combination thereof.


The polycarbonate is excellent in heat resistance, impact resistance, mechanical strength, transparency, and the like, and thus is widely used in the preparation of a compact disk, a transparent sheet, a packaging material, an automobile bumper, a UV-blocking film, an optical lens, and the like.


Examples of the diphenol-based compound can include hydroquinone, resorcinol, 4,4′-dihydroxydiphenyl, 2,2-bis(4-hydroxyphenyl)propane (also referred to as “bisphenol-A”), 2,4-bis(4-hydroxyphenyl)-2-methylbutane, bis(4-hydroxyphenyl)methane, 1,1-bis(4-hydroxyphenyl)cyclohexane, 2,2-bis(3-chloro-4-hydroxyphenyl)propane, 2,2-bis(3,5-dimethyl-4-hydroxyphenyl)propane, 2,2-bis(3,5-dichloro-4-hydroxyphenyl)propane, 2,2-bis(3,5-dibromo-4-hydroxyphenyl)propane, bis(4-hydroxyphenyl)sulfoxide, bis(4-hydroxyphenyl)ketone, bis(4-hydroxyphenyl)ether, and the like.


Preferably, 4,4′-dihydroxydiphenyl or 2,2-bis(4-hydroxyphenyl)propane can be used. In this case, the structure of the polycarbonate resin is represented by the following Chemical Formula 1.




embedded image


In Chemical Formula 1, a is an integer of 1 or more.


The polycarbonate resin can be a mixture of copolymers prepared from two or more diphenols.


Also, the polycarbonate can include a linear polycarbonate, a branched polycarbonate, a polyester carbonate copolymer resin, and the like.


The linear polycarbonate can include a polycarbonate or the like which is prepared from bisphenol-A.


The branched polycarbonate can include those prepared by reacting a polyfunctional aromatic compound such as trimellitic anhydride and trimellitic acid with diphenols and carbonates.


The polyfunctional aromatic compound can be included in an amount of 0.05 to 2 mol %, based on the total amount of the branched polycarbonate.


The polyester carbonate copolymer resins can include those prepared by reacting a difunctional carboxylic acid with diphenols and carbonates.


The carbonates can include diaryl carbonates such as diphenyl carbonate and ethylene carbonate or the like.


The polycarbonate resin according to one embodiment of the invention satisfies a melt flow rate (MFR) of 5 to 15 g/10 min according to ASTM D1238.


When a polycarbonate resin having a melt flow rate in the above range is used, excellent physical properties can be realized at the time of application of the product by using it in combination with other components.


The melt flow rate is measured at 300° C. under a load of 1.2 kg according to ASTM D1238.


When the melt flow rate is less than 5 g/min, the processability can be decreased and the productivity can be reduced. When the melt flow rate is greater than 15 g/min, the resin flow can be excessive under the relevant processing conditions, which can cause surface defects in the molded product.


Further, the melt flow rate can preferably satisfy 6 to 13 g/10 min, and more preferably 7 to 10 g/10 min. In this case, effects intended by the present invention can be increased.


Preferably, the polycarbonate resin has a weight average molecular weight of 10,000 g/mol to 50,000 g/mol, and preferably 25,000 g/mol to 35,000 g/mol.


Within the above range, the moldability and processability are excellent.


Pentaerythritol Tetrastearate (PETS)


The pentaerythritol tetrastearate component according to one embodiment of the invention is a component having an auxiliary function to achieve excellent thermal stability and simultaneously improve shielding properties in a specific wavelength range, and it can be used in combination with a black dye and a blue dye to be described later to maximize its effects.


The pentaerythritol tetrastearate can be contained in an amount of 0.05 to 5 parts by weight, preferably 0.1 to 1 part by weight, based on 100 parts by weight of the polycarbonate resin.


When the pentaerythritol tetrastearate is contained within the above range, it is possible to achieve excellent heat resistance and shielding properties, and it is preferable for realizing heat resistance and auxiliary shielding effects in a specific wavelength range.


On the other hand, when the content is less than 0.05 parts by weight, it is difficult to realize a desired effect with a small amount, and when the content is greater than 5 parts by weight, the mechanical strength can be lowered.


Dye


In the embodiment of the invention, a black dye and a blue dye are used in combination, which are further used in combination with a component for improving the shielding property in a specific wavelength region, i.e., the above-mentioned PETS component, thereby simultaneously realizing shielding performance and heat resistance improving effects.


The black dye can be specifically a compound of C.I. Pigment Black 32 (perylene black), and commercially available products can be BK32 (ThermoPlast Black X70) from BASF.


The black dye can effectively block light in the entire wavelength range, and when using it in combination with the PETS component and the blue dye, it is possible to achieve a shielding property that is suitable for application to lenses, which is preferable.


The black dye can be contained in an amount of 1.0*10−4 to 1.0*10−1 parts by weight, preferably 1.0*10−4 to 1.0*10−2 parts by weight, and more preferably 1.1*10−3 to 2.0*10−3 parts by weight, based on 100 parts by weight of the polycarbonate resin.


When the black dye is contained within the above range, the shielding properties suitable for application to a lens can be realized.


On the other hand, when the content is less than 1.0*10−4 parts by weight, it is difficult to realize a desired effect with a small amount. When the content is greater than 1.0*10−1 parts by weight, permeability can be reduced due to an excessive amount.


Specifically, the blue dye can be a compound of the following Chemical Formula 2 (CAS No. 81-48-1), and commercially available products can be Blue G (Macrolex Violet B Gran) from Lanxess.




embedded image


The blue dye can preferably be a reddish blue series dye.


The blue dye plays a role in improving the degree of yellowing of the resin, and at the same time, when used in combination with the PETS component and the black dye, it is possible to realize heat resistance and a shielding property suitable for application to a lens, which is preferable.


Furthermore, when used in further combination with a light absorber or the like, visible light in the range of 425 to 450 nm can be effectively controlled.


The blue dye can be contained in an amount of 1.0*10−4 to 1.0*10−1 parts by weight, preferably 1.0*10−4 to 1.0*10−2 parts by weight, more preferably 1.5*10−3 to 2.5*10−3 parts by weight, based on 100 parts by weight of the polycarbonate resin.


When the blue dye is contained within the above range, excellent shielding properties can be realized, and the degree of yellowing of the resin can be improved, which is preferable.


On the other hand, when the content is less than 1.0*10−4 parts by weight, it is difficult to realize a desired effect with such a small amount. When the content is greater than 1.0*10−1 parts by weight, it can be disadvantageous for commercial application due to the phenomenon in which the YI is decreased and the transmittance is reduced.


The polycarbonate resin composition according to one embodiment of the present invention includes the above-mentioned components and satisfies specific parameters (transmittance and ΔYI), thereby realizing heat resistance and excellent optical properties (shielding property at 410 nm). As a result, the degree of denaturation and hue change of the polymer is remarkably small even under high-temperature injection molding conditions in the manufacturing process.


Further, even if the product is actually used while subjected to high temperature environments, it can exhibit excellent physical properties without deformation.


In addition, if necessary, the resin composition can further include at least one additive selected from the group consisting of an antioxidant, a heat stabilizer, a plasticizer, an antistatic agent, a nucleating agent, a flame retardant, a lubricant, an impact-reinforcing agent, a fluorescent brightener, an ultraviolet absorber, and a radiation absorber.7


Optical Molded Product


In another embodiment of the invention, an optical molded product including the above-mentioned resin composition is provided.


Preferably, the optical molded product is a lens, and is suitable for use in an illumination lens or a spectacle lens.


The polycarbonate resin composition according to the present invention is excellent in heat resistance and shielding properties, and thus can be effectively used as an optical molded product.


The method for preparing a molded product can be carried out by methods commonly used in the art.


For example, the molded product can be preferably prepared by mixing the above-mentioned polycarbonate resin, pentaerythritol tetrastearate, a black dye, and a blue dye, and optionally, an additive, melt-kneading the mixture to prepare pellets, and then subjecting the pellets to injection molding in a desired form.


The melt kneading can be carried out by a method commonly used in the art, for example, a method using a ribbon blender, a Henschel mixer, a Banbury mixer, a drum tumbler, a single screw extruder, a twin screw extruder, a co-kneader, a multi-screw extruder, and the like.


The temperature of the melt-kneading can be suitably adjusted as needed.


Next, the molded product can be produced by applying a molding process such as an injection molding process, an injection compression molding process, an extrusion molding process, a vacuum molding process, a blow molding process, a press molding process, an air-pressure molding process, a foam molding process, a thermal bending molding process, a compression molding process, a calendar molding process, a rotary molding process, or the like, using the melt-kneaded product or pellets of the resin composition according to the present invention as a raw material.


When the injection molding method is used, it is subjected to high temperature conditions from 200 to 400° C. However, since the resin composition according to the present invention is excellent in heat resistance, modification or yellowing of the polymer does not substantially occur in the melt-kneading step or the injection step described above, which is preferable.


The thickness of the molded product can be appropriately adjusted in accordance with the purpose of use, and the shape of the light guide plate can be a flat plate or a curved shape in accordance with the purpose of use.


Advantageous Effects

According to the present invention, it is possible to provide a polycarbonate resin composition having excellent heat resistance and excellent optical properties by introducing a specific additive and two kinds of dyes.


Further, according to the present invention, it is possible to provide an optical molded product produced from a polycarbonate resin composition capable of exhibiting excellent optical properties even under high temperature conditions.







DETAILED DESCRIPTION OF THE EMBODIMENTS

Hereinafter, preferred examples are presented to facilitate understanding of the present invention.


However, the following examples are given for illustrative purposes only, and the scope of the present invention is not intended to be limited to or by these examples.


EXAMPLES AND COMPARATIVE EXAMPLES
Preparation of Polycarbonate Resin Composition
Examples 1 and 2, Comparative Examples 1 to 8

A polycarbonate resin composition was prepared by mixing the respective additive components in the amounts shown in Table 1 based on 100 parts by weight of the polycarbonate resin composition.












TABLE 1







Classification





(component/content)
PC resin
Additive
Dye














Parts by weight
A
B
C
D
E
F
G





Example 1
a-1/
b-1/
c-1/0.12
d-1/
e-1/
f-1/0.00014




99.404957
0.075
c-2/0.12
0.05
0.35
f-2/0.0002



Example 2
a-1/
b-1/
c-1/0.12
d-1/
e-1/
f-1/0.00017




99.404957
0.075

0.05
0.35
f-2/0.0002



Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-1/

g-1/0.00014


Example 1
99.404957
0.075

0.05
0.35

g-2/0.0002


Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-1/

g-2/0.0002


Example 2
99.404957
0.075

0.05
0.35




Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-1/

g-3/0.0002


Example 3
99.404957
0.075

0.05
0.35




Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-1/

g-1/0.00014


Example 4
99.404957
0.075

0.05
0.35

g-3/0.0002


Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-2/
f-1/0.00014



Example 5
99.404957
0.075

0.05
0.35
f-2/0.0002



Comparative
a-1/
b-1/
c-1/0.12
d-1/
e-3/
f-1/0.00017



Example 6
99.404957
0.075

0.05
0.35
f-2/0.0002





A (PC resin): a-1: Bisphenol A type of linear polycarbonate of Mw 32,000 and MFR (300° C., 1.2 kg) of 8 g/10 min (LG Chem)


B (antioxidant): b-1 PEP36 (ADEKA)


C (light absorber): c-1: UV3638 (Solvay), c-2: B-Cap (Clariant)


D (chain extender): d-1: ADR4370F (4468) (BASF)


E (additive): e-1: Pentaerythritol tetrastearate/e-2: GMS(glycerol mono stearate)/e-3: GTS (glycerol tri stearate)


F (dye): f-1 (Blue, Reddish Blue): Blue G/f-2(black) (Lanxess): BK32 (BASF)


G (dye): g-1 (Blue): BL12 (CAS No. 61969-44-6) (Lanxess), g-2 (red): RP04 (CAS No. 6829-22-7) (Lanxess), g-3 (Greenish Blue): Violet 3R (Lanxess)






Experimental Example

Pellet samples were prepared by melt-kneading the resin compositions prepared in the examples and comparative examples at a rate of 55 kg per hour in a twin screw extruder (L/D=36, Φ=45, barrel temperature 240° C.), and the properties of the prepared samples were measured by the following methods.


(1) Melt Flow Rate (MFR, g/min)


The melt flow rate was measured at 300° C. under a load of 1.2 kg using a Melt Indexer G-02 (manufactured by Toyoseiki) in accordance with ASTM D1238, and the results are shown in Table 2 below.


(2) Transmittance (%)


The transmittance at 410 nm was measured under the transmission condition of 350 to 1050 nm using a HunterLab instrument in accordance with ASTM D1003, and the results are shown in Table 2 below.


(3) Change in Yellowness Index (ΔYI)


The yellowness index was measured under the transmission condition of 350 to 1050 nm using HunterLab equipment in accordance with ASTM D1925.


The yellowness index was measured at 285° C. and 340° C. while heating from 285° C. to 340° C. for 20 minutes, and change in yellowness index was calculated according to the following General Equation 1. The results are shown in Table 2 below.





ΔYI=YI (340° C.)−YI (285° C.)   [General Equation 1]













TABLE 2








Transmittance at




Classification
410 nm (%)
ΔYI









Example 1
4.4
0.23



Example 2
4.6
0.25



Comparative
8.7
0.25



Example 1



Comparative
7.8
0.26



Example 2



Comparative
8.4
0.25



Example 3



Comparative
7.2
0.26



Example 4



Comparative
4.5
2.46



Example 5



Comparative
5.2
2.67



Example 6










As shown in Table 2, it was confirmed that in the case of the examples according to the present invention, heat resistance and excellent optical properties can be simultaneously realized by introducing a specific additive and two kinds of dyes.


It was also confirmed that in the case of the comparative examples deviating from the combination of components limited by the present invention, the heat resistance is decreased under high temperature conditions and change in yellowness index is remarkably increased or the transmittance at 410 nm is increased, which is unsuitable for optical molded products, particularly lenses.

Claims
  • 1. A polycarbonate resin composition, comprising a polycarbonate resin having a melt flow rate (MFR) of 5 to 15 g/10 min according to ASTM D1238, pentaerythritol tetrastearate, a black dye, and a blue dye, wherein: transmittance at 410 nm according to ASTM D1003 is 7% or less, andwherein a change in yellowness index (ΔYI) expressed by the following ΔYI=YI (340° C.)−YI (285° C.)   [General Equation 1]wherein YI is the yellowness index value measured according to ASTM D1925 at the corresponding temperature.
  • 2. The polycarbonate resin composition according to claim 1, wherein the polycarbonate resin includes a repeating unit of the following Chemical Formula 1:
  • 3. The polycarbonate resin composition according to claim 1, wherein the polycarbonate resin has a weight average molecular weight of 10,000 g/mol to 50,000 g/mol.
  • 4. The polycarbonate resin composition according to claim 1, wherein the black dye is C.I. Pigment Black 32.
  • 5. The polycarbonate resin composition according to claim 1, wherein the blue dye is a compound of the following Chemical Formula 2:
  • 6. The polycarbonate resin composition according to claim 1, wherein the pentaerythritol tetrastearate is present in an amount from 0.05 to 5 parts by weight, the black dye is present in an amount from 1.0×10−4 to 1.0×10−1 parts by weight, and the blue dye is contained present in an amount of amount from 1.0×10−4 to 1.0×10−1 parts by weight, based on 100 parts by weight of the polycarbonate resin.
  • 7. The polycarbonate resin composition according to claim 1, wherein the polycarbonate resin composition further comprises at least one additive selected from the group consisting of an antioxidant, a heat stabilizer, a plasticizer, an antistatic agent, a nucleating agent, a flame retardant, a lubricant, an impact-reinforcing agent, an ultraviolet absorber, and a fluorescent brightener.
  • 8. An optical molded product comprising the polycarbonate resin composition according to claim 1.
  • 9. The optical molded product according to claim 8, wherein the optical molded product is a lens.
Priority Claims (1)
Number Date Country Kind
10-2018-0055589 May 2018 KR national
PCT Information
Filing Document Filing Date Country Kind
PCT/KR2019/004713 4/18/2019 WO 00