Patent Application
20220085307
The present invention relates to polyester films for foldable displays, hard coating films for foldable displays, laminated films for foldable displays, foldable displays, and mobile devices. The present invention further relates to foldable displays and mobile devices that are less likely to have image distortion caused by deformation of the film, even when the display is repeatedly folded, and to polyester films, hard coating films, and laminated films for such foldable displays.
Becoming thinner and lighter, mobile devices such as smart phones have become widely prevalent. While being required to have a variety of functions, mobile devices are also required to be convenient to use. It is taken for granted that prevailing mobile devices can be operated with one hand for simple tasks, and can be put into a clothes pocket. Thus, such mobile devices must have a small screen size, such as about 6 inches.
Tablet devices with a screen size of 7 to 10 inches are intended for use not only for video content and music, but also for business purposes, drawing, and reading, and thus have a high level of functionality. However, these devices cannot be operated with one hand and are not particularly portable, leaving some issues in regards to convenience.
In order to meet the above requirements, PTL 1 suggests a technique of making compact devices by connecting multiple displays. However, due to the remaining bezel portion, the image is split, and visibility decreases. Thus, this technique is not commonly used.
More recently, mobile devices equipped with a flexible or foldable display have been proposed. This technique enables conveniently carrying a mobile device equipped with a large screen display without problems of image splitting.
Conventional displays and mobile devices that have no folding structure can be protected by a non-flexible material, such as glass, that is applied to the surface of the display. However, a foldable display that uses a single screen spanning over a folding portion must be protected by, for example, a flexible and surface-protecting hard coating film. However, a foldable display is repeatedly folded at the point where a portion folds, and the film at that point deforms over time, causing image distortion on the display. In addition to the surface protection film, films are further used in various parts of a foldable display, such as a polarizing plate, a retardation film, a touchscreen substrate, a substrate of display cells such as organic EL, and protective materials on the back. These films are also required to be durable against repeated folding.
PTL 2 suggests a technique of partially altering the film thickness. However, this method is not suitable for mass production.
A technique to adjust the refractive index of a polyester film in the bending direction is also suggested (see PTL 3). However, the pencil hardness during the application of hard coating decreases with a decrease in the refractive index in the bending direction, thus lowering the surface protection functionality of the display. Additionally, while decreasing the refractive index in one direction reduces deformation that occurs when the display is folded, it makes the folding direction more uniaxially oriented, forming cracks or breaking the display at the folding portion.
PTL 1: JP 2010-228391A
PTL 2: JP 2016-155124A
PTL 3: WO2018/150940A
The present invention is intended to solve the problems that arise in conventional parts of displays as described above. The invention is intended to provide a polyester film for foldable displays, a hard coating film for foldable displays, and a laminated film for foldable displays that do not form creases or cracks in the folding portion, in order to provide a foldable display that is suitable for mass production and that is unlikely to have distortion of images on the folding portion after the display is repeatedly folded, and to provide a mobile device equipped with such a foldable display.
Specifically, the present invention includes the following subject matter.
Item 1. A polyester film for a foldable display, the polyester film having a thickness of 10 to 80 μm and satisfying the following conditions:
(1) the polyester film has a refractive index in the bending direction of 1.590 to 1.620,
(2) the polyester film has a refractive index in the direction of a folding portion of 1.670 to 1.700,
(3) the polyester film has a refractive index in the thickness direction of 1.520 or less, and
(4) the polyester film has a density of 1.380 g/cm3 or more, wherein the bending direction refers to a direction orthogonal to the folding portion of the polyester film to be folded.
Item 2. The polyester film for a foldable display according to Item 1, having a total light transmittance of 85% or more, a haze of 3% or less, and a maximum heat shrinkage of 6% or less.
Item 3. The polyester film for a foldable display according to Item 1 or 2, comprising an easy-to-adhere layer on at least one surface of the polyester film.
Item 4. The polyester film for a foldable display according to any one of claims 1 to 3, having an in-plane retardation (Re) of 3000 to 30000 nm.
Item 5. A hard coating film for a foldable display, comprising the polyester film for a foldable display of any one of Items 1 to 4, and a hard coating layer having a thickness of 1 to 50 μm on at least one surface of the polyester film.
Item 6. The hard coating film for a foldable display according to Item 5, having a total light transmittance of 85% or more.
Item 7. The hard coating film for a foldable display according to Item 5 or 6, wherein the polyester film has a modulus of elasticity in the bending direction of 2.7 GPa or less, and a modulus of elasticity in the direction of the folding portion of 4.5 GPa or more.
Item 8. The hard coating film for a foldable display according to any one of Items 5 to 7, having a haze of 3% or less.
Item 9. A laminated film for a foldable display, comprising the hard coating film of any one of Items 5 to 8, and an adhesive layer on the surface of the hard coating film opposite the surface on which the hard coating layer is present.
Item 10. The laminated film for a foldable display according to Item 9, wherein the adhesive layer has a thickness of 1 to 50 μm.
Item 11. A foldable display comprising the hard coating film for a foldable display of any one of Items 5 to 8,
wherein
the hard coating film is disposed as a surface protection film such that the hard coating layer becomes the front surface, and
the hard coating film is a single continuous film placed through the folding portion of the foldable display.
Item 12. A foldable display comprising the laminated film for a foldable display of Item 9 or 10,
wherein
the laminated film is disposed as a surface protection film such that the hard coating layer becomes the front surface, and
the laminated film is a single continuous film placed through the folding portion of the foldable display.
Item 13. A mobile device comprising the foldable display of Item 11 or 12.
While a foldable display using the polyester film, the hard coating film, or the laminated film for foldable displays according to the present invention maintains its suitability in mass production, the polyester film of the foldable display does not have cracks at the folding portion, deformation after being repeatedly folded, and image distortion at the folding portion of the display. A mobile device equipped with the above foldable display using a polyester film or hard coating film provides beautiful images and has a variety of functions, while being highly convenient, such as in portability.
The term “display” as used in the present invention refers to display devices in general. There are several types of displays, such as LCDs, organic EL displays, inorganic EL displays, LEDs, and FEDs; however, LCDs, organic ELs, and inorganic ELs, which have a foldable structure, are preferable. In particular, organic EL displays and inorganic EL displays, which can reduce the layer structure, are preferable; and organic EL displays, which have a wide color gamut, are even more preferable.
A foldable display is a single continuous display that can be folded in half or other ways when carried. The size of the fordable display can be reduced by half or even more by folding it, and thus the portability is improved. The foldable display preferably has a bend radius of 5 mm or less, and more preferably 3 mm or less. A bend radius of 5 mm or less enables the foldable display to be thin when folded. A smaller bend radius is better; however, the smaller the bend radius, the more easily creases form. The bend radius is preferably 0.1 mm or more, or can be even 0.5 mm or more or 1 mm or more. Even a bend radius of 1 mm or more can achieve a reduction in thickness sufficient for practical use in carrying the display. The bend radius of a folded display refers to a value measured at the point indicated by numerical reference 11 in the schematic diagram of
The polyester film for a foldable display according to the present invention may be used in any part of the components of a foldable display. The following describes a typical structure of a foldable display and the parts in which the polyester film according to the present invention is usable, taking an organic EL display as an example. The polyester film for a foldable display according to the present invention may be simply referred to below as “the polyester film according to the present invention.”
The essential component of a foldable organic EL display is an organic EL module. A foldable organic EL display may further optionally include, for example, a circularly polarizing plate, a touchscreen module, a surface protection film, and a back protection film.
A typical structure of an organic EL module includes an electrode, an electron transport layer, a light-emitting layer, a hole transport layer, and a transparent electrode. The polyester film according to the present invention can be used as a substrate on which an electrode is provided, and further an electron transport layer, a light-emitting layer, and a hole transport layer are provided. In particular, the polyester film according to the present invention can be preferably used as a substrate for a transparent electrode. In this case, because the substrate film is required to have a high level of barrier properties against water vapor or oxygen, the polyester film according to the present invention is preferably provided with a barrier layer such as a metal oxide layer. To enhance the barrier properties, multiple barrier layers may be provided, or multiple polyester films provided with a barrier layer may be used.
The mobile device preferably includes a touchscreen. An organic EL display for use preferably includes a touchscreen module on the organic EL display or between the organic EL module and the circularly polarizing plate. The touchscreen module includes a transparent substrate such as a film and a transparent electrode provided on the transparent substrate. The polyester film according to the present invention can be used as this transparent substrate. The polyester film used as a transparent substrate of a touchscreen is preferably provided with a hard coating layer or a refractive index adjustment layer.
The circularly polarizing plate suppresses the deterioration of image quality due to the reflection of external light by the components inside the display. A circularly polarizing plate includes a linear polarization plate and a retardation film. The linear polarization plate includes a protection film at least on the visible side of the polarizer. A protection film may be provided on the side opposite the visible side of the polarizer, and a retardation film may be directly stacked on the polarizer. The retardation film for use is a resin film with a phase difference such as polycarbonate or cyclic-olefin, or a resin film provided with a retardation layer composed of a liquid crystal compound. The polyester film according to the present invention can be used as a polarizer protection film or a resin film for a retardation film. In these cases, the slow axis direction of the polyester film according to the present invention is preferably parallel or orthogonal to the absorption axis direction of the polarizer. A deviation of up to 10 degrees, preferably 5 degrees, from this parallel or orthogonal relationship is permissible.
Because a shock applied to a display from above may break the circuitry of an organic EL module or a touchscreen module, a surface protection film is provided in most cases. The polyester film according to the present invention can be used as the surface protection film. The surface protection film includes a “cover window,” which is incorporated into the top surface of the display, and an “after film,” which can be attached, peeled off, and replaced with another by the user. The polyester film according to the present invention is usable in either case. The polyester film according to the present invention used as a surface protection film preferably has a hard coating layer stacked on at least the front surface of the polyester film. The polyester film is provided on the front surface of a foldable display with the hard coating layer on the viewing side. The hard coating layer may be provided on both surfaces of the polyester film.
A protection film is preferably provided also on the back of the display. The polyester film according to the present invention can be used as the protection film for the back.
The polyester film according to the present invention can be any film that is usable in the components of a foldable display at the folded portion, in addition to those described above. Among these, the polyester film according to the present invention is preferably used in cover window surface protection films, after-surface protection films, substrate films for touchscreen modules, or back protection films. The polyester film according to the present invention is more preferably used in cover window surface protection films, or after-surface protection films.
In a foldable display, the polyester film according to the present invention does not have to be used in all of the films described above. In a foldable display, films such as a polyimide film, a polyamide film, a polyamide-imide film, a polyester film that is not the polyester film according to the present invention, a polycarbonate film, an acrylic film, a triacetyl cellulose film, a cyclo-olefin polymer film, a polyphenylene sulfide film, and a polymethylpentene film are also usable according to suitability, in addition to the polyester film according to the present invention.
The polyester film according to the present invention may be a monolayered film composed of one or more types of polyester resins. If two or more types of polyester are used, the polyester film may be a multilayered film or ultra-multilayered lamination film with a repeating structure.
Examples of polyester resins for use in the polyester film include polyethylene terephthalate, polybutylene terephthalate, polyethylene-2,6-naphthalate, and polyester films composed of copolymers that contain the component of these resins as the main component. In particular, from the standpoint of mechanical properties, heat resistance, transparency, and price, drawn polyethylene terephthalate films are particularly preferable.
When a polyester copolymer is used in a polyester film, the dicarboxylic acid component of the polyester can be, for example, aliphatic dicarboxylic acids, such as adipic acid and sebacic acid; aromatic dicarboxylic acids, such as terephthalic acid, isophthalic acid, phthalic acid, and 2,6-naphthalene dicarboxylic acid; or multifunctional carboxylic acids, such as trimellitic acid and pyromellitic acid. The glycol component can be, for example, fatty acid glycols, such as ethylene glycol, diethylene glycol, 1,4-butanediol, propylene glycol, and neopentyl glycol; aromatic glycols, such as p-xylene glycol; alicyclic glycols, such as 1,4-cyclohexanedimethanol; or polyethylene glycols with an average molecular weight of 150 to 20,000. The mass ratio of the copolymer component of the copolymer is preferably less than 20 mass %. A mass ratio of less than 20 mass % is preferable because film strength, transparency, and heat resistance are retained.
In the production of a polyester film, at least one type of resin pellet preferably has an intrinsic viscosity of 0.50 to 1.0 dl/g. An intrinsic viscosity of 0.50 dl/g or more is preferable because such an intrinsic viscosity increases the shock resistance of the obtained film, and thus makes it unlikely for the internal circuitry of the display to be broken by an external shock. An intrinsic viscosity of 1.00 dl/g or less is preferable because it prevents filtration pressure of the molten fluid from becoming too high, thus making it easier to stably perform film production.
The polyester film preferably has a thickness of 10 to 80 μm, and more preferably 25 to 75 μm. A thickness of 10 μm or more provides a pencil hardness improvement effect and an impact resistance improvement effect, and a thickness of 80 μm or less is advantageous in weight reduction and provides excellent flexibility, processability, and handleability.
The surface of the polyester film according to the present invention may be smooth or uneven. However, a decreased level of optical properties due to unevenness is not preferable because the film is used for covering the surface of a display. The haze is preferably 3% or less, more preferably 2% or less, and most preferably 1% or less. A haze of 3% or less can improve the visibility of images. Although a lower haze is better, the lower limit of haze may be preferably 0.1% or more, or 0.3% or more, from the standpoint of stable production.
Given the purposes of reducing haze as described above, the surface should not be too uneven. However, to provide the film with moderate slipperiness for handleability, unevenness may be formed on the film surface by adding particles to the polyester resin layer of the surface layer, or by applying a particle-containing coating layer to the polyester resin layer during the film-forming process.
The method for adding particles to a polyester resin layer can be a known method. For example, particles can be added at any stage of polyester production and can be preferably added in the form of slurry prepared by dispersing the particles in, for example, ethylene glycol, in the esterification stage, after the completion of transesterification, or before the start of polycondensation to facilitate polycondensation. Alternatively, particles can be added by a method of blending slurry prepared by dispersing particles in ethylene glycol or water with a polyester material by using a kneading extruder equipped with a vent, or a method of blending dry particles with a polyester material by using a kneading extruder.
In particular, preferable is a method of homogeneously dispersing the aggregates of inorganic particles in a monomer solution, which is part of a polyester material, then filtering the dispersion, and adding the filtrate to the remainder of the polyester material before, during, or after esterification. Due to the low viscosity of the monomer solution, this method enables homogeneous dispersion of particles and high-precision filtration of the slurry in a simple manner while ensuring excellent particle dispersibility and low likelihood of the occurrence of new aggregates when particles are added to the remainder of the polyester material. From this viewpoint, it is particularly preferable to add particles to the remainder of the polyester material at a low temperature before esterification.
Additionally, the number of protrusions on the surface of the film can be further reduced by a method of preparing a particle-containing polyester beforehand, and kneading the particle-containing polyester pellets with particle-free pellets to extrude pellets (master batch method).
The polyester film may contain various additives within the range in which the desired total light transmission is maintained. Examples of additives include an antistatic agent, a UV absorber, and a stabilizer.
The polyester film has a total light transmittance of preferably 85% or more, and more preferably 87% or more. A transmittance of 85% or more sufficiently ensures visibility. Although a higher total light transmittance of the polyester film is better, the total light transmittance is preferably 99% or less, or may be 97% or less, from the standpoint of stable production.
The polyester film after heat treatment at 150° C. for 30 minutes has a maximum heat shrinkage of preferably 6% or less, and more preferably 5% or less. A heat shrinkage of 6% or less can reduce flatness errors, such as curling or undulation, during HC processing. Although a lower heat shrinkage is better, the heat shrinkage is preferably −1% or more, and more preferably 0% or more. A negative value means that the polyester film expanded after heating. A value below −1% may also lead to flatness errors.
The polyester film for a foldable display according to the present invention can impart sufficient pencil hardness to a hard coating film formed by laminating a hard coating layer on the polyester film. In the case of conventional polyester films, a hard coating film formed by laminating a hard coating layer on such a conventional polyester film shows a decrease in pencil hardness seemingly due to deformation of the film in the thickness direction in pencil hardness evaluation of the hard coating film. The present invention can achieve a high level of hardness in pencil hardness evaluation of hard coating films by setting the indentation depth of the film in the thickness direction so as to fall within a specific range after unloading a test force with a dynamic ultra-micro hardness tester, described later. The indentation depth of the film in the thickness direction after unloading a test force is preferably 1.5 μm or less, more preferably 1.4 μm or less, and still more preferably 1.3 μm or less. When the indentation depth is 1.5 μm or less after unloading a test force (the final amount of deformation under load), the hard coating film formed by laminating a hard coating layer becomes resistant to deformation in the thickness direction and shows a high level of pencil hardness in pencil hardness evaluation. A hard coating film with a high level of pencil hardness makes it unlikely for the display surface to have scratches and dents, increasing the display visibility. A lower indentation depth is better after unloading a test force; however, from the standpoint of stable production and saturation of the effects, the indentation depth is preferably 0.3 μm or more, and more preferably 0.5 μm or more.
In order to decrease the indentation depth after unloading a test force, it is effective to adjust the refractive index in the thickness direction to 1.520 or less. The means to adjust the refractive index to 1.520 or less includes, for example, the following condition settings within the range in which other physical properties and the refractive index in the bending direction and in the folding direction can be regulated so as to fall within preferable ranges: adjusting the draw ratio in the bending direction or in the folding direction to a high value, setting a low draw temperature in the bending direction or in the folding direction, and setting a high heat fixation temperature. These are described later.
The polyester film that serves as a substrate of a hard coating film or laminated film has a modulus of elasticity in the bending direction of preferably 2.7 GPa or less, more preferably 2.6 GPa or less, and still more preferably 2.5 GPa or less. Reducing the modulus of elasticity in the bending direction reduces the stress applied to the hard coating layer when the hard coating film (laminated film) is bent. The lower the modulus of elasticity in the bending direction, the better the flexibility. However, to avoid damaging the flatness of the display surface, the modulus of elasticity in the bending direction is preferably 1.8 GPa or more. The polyester film that serves as a substrate of a hard coating film or laminated film has a modulus of elasticity in the folding direction of preferably 4.5 GPa or more, more preferably 4.6 GPa or more, and still more preferably 4.7 GPa or more. The flatness of the display surface can be maintained during display preparation by increasing the modulus of elasticity in the folding direction. Although a higher modulus of elasticity in the folding direction is better, the modulus of elasticity in the folding direction is preferably 8.0 GPa or less from the standpoint of film formability.
The surface of the polyester film according to the present invention can be subjected to treatment for improving adhesion with a resin for forming, for example, a hard coating layer. The non-hard coating surface of the hard coating film according to the present invention can be coated with a tackifier or subjected to treatment for improving adhesion with another hard coating layer.
Examples of surface treatment methods include unevenness-forming treatment by sandblasting, solvent treatment, etc.; and oxidation treatment such as corona discharge, electron beam irradiation, plasma treatment, ozone-UV irradiation, flame treatment, chromic-acid treatment, and hot-air treatment. These methods can be used without any restriction.
Adhesion can also be improved by an adhesion-improving layer, such as an easy-to-adhere layer. For the easy-to-adhere layer, resins such as acrylic resins, polyester resins, polyurethane resins, and polyether resins can be used without any restriction. The easy-to-adhere layer can be formed by a typical coating technique, preferably an “in-line coating technique.”
The polyester film described above can be produced, for example, by performing a polymerization step of homogenously dispersing inorganic particles in a monomer solution, which is part of a polyester material, filtering the dispersion, and adding the filtrate to the remainder of the polyester material to polymerize a polyester; and a film-forming step of melting and extruding the polyester into a sheet form through a filter, and cooling and drawing the sheet to form a substrate film.
Below, the method for producing a biaxially oriented polyester film is described with an example in which pellets of polyethylene terephthalate (“PET” below) are used as a material of a substrate film. However, the method is not limited to this example. Additionally, the example is not intended to limit the number of layers, such as a monolayer or a multilayer.
After a predetermined proportion of PET pellets is mixed and dried, the mixture is fed into a known extruder for melting and laminating, and then extruded from the slit die into a sheet form, followed by cooling and solidifying the sheet on a casting roll to form an unstretched film. A monolayer can be produced with a single extruder. A multilayered film (i.e., including two or more layers) can be produced by laminating multiple film layers that each constitute an outermost layer using two or more extruders, a multilayered manifold, or a confluence block (e.g., confluence blocks with a square joint), extruding a sheet of two or more layers from the outlet, and cooling the sheet on a casting roll to prepare an unstretched film.
In this case, it is preferable to perform high-precision filtration to remove foreign matter that may be present in the resin at any portion of the extruder at which the molten resin is maintained at about 280° C. during melt-extrusion. The filter material for use in high-precision filtration of a molten resin can be any material; however, a filter material made of sintered stainless steel is preferable because it is excellent in removing aggregates composed mainly of Si, Ti, Sb, Ge, or Cu and organic matter with a high melting point.
Additionally, the filter material has a filtered particle size (initial filtration efficiency: 95%) of preferably 20 μm or less, particularly preferably 15 μm or less. A filtered particle size (initial filtration efficiency: 95%) exceeding 20 μm may lead to insufficient removal of foreign matter with a size of 20 μm or more. Although high-precision filtration of molten resin using a filter material with a filtered particle size of 20 μm or less (initial filtration efficiency: 95%) may reduce productivity, such a filter material is preferable from the standpoint of obtaining a film that has fewer protrusions caused by coarse particles.
In the present invention, the refractive index of the polyester film at least either in the longitudinal direction (machine direction) or in the width direction is preferably 1.590 to 1.620, and more preferably 1.591 to 1.600. The refractive index of the polyester film in the bending direction is preferably 1.590 to 1.620, and more preferably 1.591 to 1.600. The term “bending direction” as used here refers to a direction that is orthogonal to the folding portion (reference numeral 21) assumed in the use of a foldable display, as indicated by reference numeral 22 on a polyester film (reference numeral 2) shown in
Fatigue due to compressive stress applied to the inside of the display when the display is folded can be reduced by controlling the refractive index of the polyester film at least either in the longitudinal direction (machine direction) or in the width direction, more preferably the refractive index of the polyester film in the bending direction, so as to fall within the ranges above. Fatigue due to compressive stress is thought to occur mainly in the crystalline portions; fewer crystals in the bending direction causes less fatigue. Thus, lowering the refractive index is thought to reduce the amount of crystals oriented in the bending direction and reduce compressive fatigue.
Additionally, the creep phenomenon caused by tensile stress applied to the outer side of the folded display can be reduced by decreasing the refractive index. Fatigue due to tensile stress is thought to occur mainly in the amorphous portions; repeatedly applied stress causes the molecular chains to align, thus deforming the film. It is inferred that having fewer molecular chains aligned in the bending direction leads to less deformation caused by such an alignment of molecular chains. Because fatigue due to tension can be reduced by decreasing amorphous portions, higher crystallinity (i.e., density) is preferable.
In the present invention, the draw ratio of an unstretched polyester sheet either in the longitudinal direction (machine direction) or in the width direction is preferably 1.2-fold to 2.0-fold, and more preferably 1.7-fold to 2.0-fold. The draw direction is preferably the bending direction. A draw ratio of 1.2-fold or more is preferable due to there being no deformation during post-processing, such as hard-coating application, while a draw ratio of 2.0-fold or less is preferable because the film thickness does not become uneven. The draw temperature is preferably 75 to 120° C., and more preferably 75 to 105° C. The heating method for use during drawing can be a known technique, such as a hot-air heating method, a roll heating method, or an infrared heating method. A draw temperature of 75 to 120° C. can prevent the film from having great unevenness in the thickness caused by drawing at a draw ratio within the range described above. Additionally, the refractive index in the thickness direction can be reduced by drawing the film at temperatures as low as possible within the above range in which the film does not have great unevenness in the thickness.
The refractive index of the polyester film in the direction orthogonal to the direction in which the refractive index is 1.590 to 1.620 is preferably 1.670 to 1.700. Specifically, the refractive index in the direction orthogonal to the bending direction (the direction of the folding portion) is preferably 1.670 to 1.700. A refractive index of 1.670 to 1.700 can reduce deformation that occurs when the film is folded in the bending direction. A refractive index of 1.700 or less can suppress the formation of cracks or fracture in the direction of the folding portion. A refractive index of 1.670 or more can increase flexibility in the bending direction and increase the surface hardness. A refractive index of 1.680 to 1.695 is more preferable. The refractive index in the direction orthogonal to the bending direction can be adjusted by, for example, the draw ratio, drawing preheating temperature, draw temperature, multi-stage drawing, and film relaxation. The draw ratio is preferably 4.0 to 6.0-fold, more preferably, 4.4 to 6.0-fold. The drawing preheating temperature in the direction orthogonal to the bending direction is preferably 70 to 110° C. In performing multi-stage drawing in the direction orthogonal to the bending direction, it is preferable to set the draw ratio in the second and subsequent states higher than the draw ratio in the first stage. Film relaxation may be performed by 1 to 10% either in the machine direction (longitudinal direction) or in the vertical direction (width direction), or both.
The refractive index in the thickness direction is preferably 1.520 or less. This is because a refractive index in the thickness direction of 1.520 or less can suppress the reduction in hardness of the film surface even when the refractive index in the bending direction is designed to be low, and can thus achieve both flexibility and surface hardness. A refractive index in the thickness direction of 1.520 or less can reduce the indentation depth in the thickness direction after unloading a test force and can increase the hardness of film surface, in particular the pencil hardness of a hard coating film formed by laminating a hard coating layer. The refractive index in the thickness direction is more preferably 1.515 or less, still more preferably 1.510 or less, particularly preferably 1.505 or less, and most preferably 1.500 or less. A lower refractive index in the thickness direction is preferable; however, from the standpoint of stable production, the refractive index in the thickness direction is preferably 1.3 or more, and may be even 1.4 or more. The refractive index in the thickness direction is particularly preferably 1.410 or more. The refractive index in the thickness direction within these ranges can be achieved by increasing the draw ratio in both the bending direction and the folding direction. In order to control the refractive index in the thickness direction after controlling the refractive index in the bending direction and in the width direction so as to fall within their preferable ranges, it is preferable to set the conditions while checking the balance of each process condition in the film forming process.
The refractive index in the thickness direction can be controlled so as to fall within the above ranges by drawing preheating temperature, draw temperature, or draw ratio in the bending direction; or drawing preheating temperature, draw temperature, multi-stage drawing, high-ratio drawing, or temperature setting for heat fixation in the direction of the folding portion. The drawing preheating temperature in the bending direction is preferably 70° C. to 110° C. The draw temperature in the bending direction is preferably 75 to 120° C. The draw ratio in the bending direction is preferably 1.2-fold to 2.0-fold, and more preferably 1.7-fold to 2.0-fold. The refractive index in the thickness direction can be effectively reduced, while the flexibility in the bending direction is maintained, by performing drawing with a low draw ratio at a low draw temperature. The drawing preheating temperature in the direction of the folding portion is also preferably 75° C. to 110° C. The draw temperature is preferably 75 to 120° C. The draw ratio in the folding portion is preferably 4.0-fold to 6.0-fold, and more preferably 4.4-fold to 6.0-fold. The refractive index in the thickness direction can be effectively reduced while the refractive index in the bending direction is maintained or reduced. High-ratio drawing may be performed by multi-stage drawing. In this case, setting the draw ratio in the second stage higher than the draw ratio in the first stage is preferable because this enables effective control of the refractive index. The method of performing drawing again after a crystallization step can also be used. Accelerated drawing, in which the drawing rate is increased from the beginning toward the latter half of the drawing process, may be used.
The heat fixation temperature is preferably 180 to 240° C. Heat fixation facilitates crystallization oriented in the drawing direction and reduces the refractive index in the thickness direction. Although it is not necessarily clear why the hardness of film surface is increased by reducing the refractive index in the thickness direction, it is presumed that aromatic moieties such as benzene rings in the molecular chains are oriented in the plane direction, and this has the effect of suppressing deformation caused by stress applied in the thickness direction.
The density of the polyester film is preferably 1.380 g/cm3 or more, and more preferably 1.383 g/cm3 or more. A density of 1.380 g/cm3 or more can increase flexibility and can increase the hardness of film surface, in particular the pencil hardness of a hard coating film formed by laminating a hard coating layer on the polyester film. A higher density is better. Although it somewhat depends on, for example, whether particles are present in the film, the density of the polyester film is preferably 1.40 g/cm3 or less, and more preferably 1.395 g/cm3 or less. Setting the heat fixation temperature during film formation to 180 to 240° C. facilitates crystallization and thus effectively increases the density. A density of 1.380 g/cm3 or less results in insufficient crystallization, making it likely for the film to deform due to bending. A density of 1.380 g/cm3 or less also increases heat shrinkage, leading to poor processability during the application of hard coating.
The bending direction of the polyester film is preferably the longitudinal direction (machine direction). This makes it easier to decrease the refractive index in the bending direction in the second stretching in biaxial stretching and increase flexibility. More specifically, a preferable polyester film can be obtained by drawing an unstretched polyester sheet in the longitudinal direction in a draw ratio of 1.2 to 2.0-fold, more preferably 1.7 to 2.0-fold. Additionally, in a preferable embodiment, the film is also drawn in the width direction in a draw ratio of 4.0 to 6.0-fold, more preferably 4.4 to 6.0-fold.
In a particularly preferable embodiment of the present invention, the polyester film satisfies the following four characteristics simultaneously:
(1) the polyester film has a refractive index in the bending direction of 1.590 to 1.620,
(2) the polyester film has a refractive index in the direction of a folding portion of 1.670 to 1.700,
(3) the polyester film has a refractive index in the thickness direction of 1.520 or less, and
(4) the polyester film has a density of 1.380 g/cm3 or more.
However, the resulting film may not satisfy the four characteristics simultaneously in the case of a combination of conditions that are not the best options within the individual preferable production conditions (e.g., a combination of a draw ratio in the bending direction of 1.4-fold or less, a draw ratio in the direction of the folding portion of less than 4.4-fold, and a heat fixation temperature of 220° C. or less), among the combinations within the scope of the preferable production conditions. In such a case, the four characteristics may be achieved simultaneously by fine-tuning some conditions or a combination of them, such as increasing the draw ratio in the bending direction to 1.7-fold or more, increasing the draw ratio in the direction of the folding portion to 4.4-fold or more, increasing the heat fixation temperature to about 230° C., and/or decreasing the draw temperature in the bending direction and/or the direction of the folding portion.
To adjust film formability, film strength, thermal dimensional stability, and poor appearance, any film forming method, such as drawing, relaxation, heat fixation, and surface treatment, may be used. In a particularly preferable embodiment of the present invention, the refractive index and density of the film are controlled so as to fall within the preferable ranges above. Controlling the refractive index and density so as to fall within the preferable ranges above provides a polyester film that is suitable for foldable displays and that exhibits excellent flex resistance and surface hardness, in particular a high level of pencil hardness of a hard coating film formed by laminating a hard coating layer on the polyester film, as compared with conventional films.
Specifically, for example, after PET pellets are sufficiently dried in a vacuum, they are fed into an extruder, and then melted and extruded in a sheet form at about 280° C., followed by cooling and solidifying the sheet to form an unstretched PET sheet. The obtained unstretched sheet is drawn 1.2-fold to 2.0-fold, more preferably 1.7-fold to 2.0-fold in the longitudinal direction, with rolls heated to 75 to 120° C. to obtain a uniaxially oriented PET film. The film is then held with clips at its ends, guided into a hot-air zone heated to 75 to 120° C., and dried, followed by drawing 4.0-fold to 6.0-fold, more preferably 4.4-fold to 6.0-fold in the width direction. Subsequently, the film is guided into a heat treatment zone at 180 to 240° C. and treated with heat for 1 to 60 seconds. During the heat treatment step, the film may optionally be subjected to relaxation treatment by 0 to 10% in the width or longitudinal direction.
The polyester film has an intrinsic viscosity of preferably 0.50 to 1.0 dl/g. An intrinsic viscosity of 0.50 dl/g or more is preferable because such an intrinsic viscosity increases the shock resistance of the film, and thus makes it unlikely for the internal circuitry of a display to become disconnected by an external shock. An intrinsic viscosity of 1.00 dl/g or less is preferable because it prevents filtration pressure of the molten fluid from becoming too high, thus stabilizing film production.
When a polymer film with birefringence placed on the viewing side in view from the display module is observed from an oblique direction, coloring or iridescent color unevenness (rainbow unevenness) may appear. This occurs for the following reason. Some of the light emitted from the display module is reflected at the interface, thereby producing polarization components. The polarization components that pass through the polyester film are converted into linearly polarized light that is orthogonal to the original polarized light or elliptically polarized light due to in-plane retardation (Re), which is the product of the birefringence and the thickness of the polymer film. Some of the polarization components of the converted polarized light are removed due to the reflection, for example, at the interface between the film and air. The coloring and rainbow unevenness can be prevented by setting the in-plane retardation (Re) of the polyester film to 3000 nm or more. This is because of the following reason. The pattern of the conversion of polarization components into linearly polarized light or elliptically polarized light relies on the wavelength and in-plane retardation (Re). This pattern can be repeated in a short wavelength cycle by setting a high in-plane retardation (Re). As a result, the shape of the envelope of the transmitted light spectrum can approximate the emission spectrum of the light source, and it becomes indistinguishable to the human eyes.
The lower limit of in-plane retardation (Re) is preferably 4500 nm, and more preferably 6000 nm.
From the standpoint of visibility (reduced rainbow unevenness), the upper limit of in-plane retardation (Re) is preferably 30000 nm. The upper limit of in-plane retardation (Re) is more preferably 20000 nm, still more preferably 15000 nm, particularly preferably 12000 nm, and most preferably 10000 nm.
The in-plane retardation (Re) of the polyester film in the present invention can be determined by measuring the refractive index in the biaxial direction and the thickness, or by using a commercially available automatic birefringence analyzer, such as a KOBRA-21ADH (Oji Scientific Instruments). The slow axis direction can be determined by using a molecular orientation analyzer (e.g., MOA-6004, molecular orientation analyzer, produced by Oji Scientific Instruments).
The OLED light source used in foldable displays has a wide emission spectrum. Thus, the shape of the envelope of the transmitted light spectrum can approximate the emission spectrum of the light source with only a simple structure by setting the in-plane retardation (Re) of the polyester film to within the above ranges.
When a polarization plate is disposed on the viewing side in view from the display module, the polyester film according to the present invention is also preferably disposed on the viewing side in view from the polarization plate; this is preferable from the standpoint of increased visibility and sufficient antireflection functionality.
The angle made by the absorption axis of the polarization plate with the slow axis of the polymer film is, although not particular limited to, preferably 0° or 90° from the standpoint of convenience in cutting out the polarization plate and the polymer film. Additionally, even if the in-plane retardation (Re) is relatively low, the angle made by the absorption axis of the polarization plate with the slow axis of the polymer film is preferably 0° from the standpoint of easily reducing coloring or rainbow unevenness. In this case, it is preferable to allow a deviation of ±20° from 0 or 90, and it is more preferable to allow a deviation of ±10° from 0 or 90°. On the other hand, to additionally prevent blackout that occurs when the screen is viewed through polarized sunglasses, the angle is preferably more than 20° to less than 70°, and more preferably 30 to 600.
In the present invention, it is also preferable to laminate an easy-to-adhere layer on the polyester film in order to improve the adhesiveness between the polyester film and the hard coating layer or other layers. The easy-to-adhere layer can be obtained by applying a coating solution for forming an easy-to-adhere layer to one or both surfaces of an unstretched or longitudinal, uniaxially oriented film, optionally performing heat treatment to dry the applied coating, and drawing the film in at least one direction in which the film is not stretched. Heat treatment can also be performed after biaxial drawing is performed. It is preferable to control the final amount of the applied easy-to-adhere layer to 0.005 to 0.20 g/m2. An amount of the applied easy-to-adhere layer of 0.005 g/m2 or more is preferable because it provides adhesiveness. An amount of the applied easy-to-adhere layer of 0.20 g/m2 or less is preferable because it provides blocking resistance.
Examples of resins to be contained in the coating solution for use in laminating an easy-to-adhere layer include polyester-based resins, polyether-polyurethane-based resins, polyester polyurethane resins, polycarbonate polyurethane resins, and acrylic resin; these resins can be used without any particular limitation. Examples of crosslinking agents to be contained in the coating solution for forming an easy-to-adhere-layer include melamine compounds, isocyanate compounds, oxazoline compounds, epoxy compounds, and carbodiimide compounds. These crosslinking agents can also be used in a combination of two or more. Due to the nature of in-line coating, these are preferably applied in the form of an aqueous coating solution, and the resins and the crosslinking agents are preferably water-soluble or water-dispersible resins or compounds.
To impart smoothness to the easy-to-adhere layer, it is preferable to add particles. The fine particles preferably have a mean particle size of 2 μm or less. Particles having a mean particle size of more than 2 μm are more likely to come off from the easy-to-adhere layer. Examples of particles to be contained in the easy-to-adhere layer include inorganic particles, such as titanium oxide, barium sulfate, calcium carbonate, calcium sulfate, silica, alumina, talc, kaolin, clay, calcium phosphate, mica, hectorite, zirconia, tungsten oxide, lithium fluoride, and calcium fluoride, and organic polymer particles, such as styrene-based particles, acrylic-based particles, melamine-based particles, benzoguanamine-based particles, and silicone-based particles. These may be singly added to the easy-to-adhere layer, or added in a combination of two or more types.
The method for applying the coating solution for use may be a known method as in the coating layer described above. Examples of methods for applying the coating solution include reverse roll coating, gravure coating, kiss coating, roll brush, spray coating, air-knife coating, wire-bar coating, and pipe doctor. These methods can be used singly or in combination.
When the polyester film according to the present invention is used as a surface protection film for a foldable display by positioning the polyester film on the surface of the display, the polyester film preferably has a hard coating layer on at least one surface of the film. The hard coating layer is preferably used in a display by positioning on the surface of the polyester film that is the front surface of the display. The resin for forming a hard coating layer can be any resin, without particular limitations, such as acrylic resins, siloxane resins, inorganic hybrid resins, urethane acrylate resins, polyester acrylate resins, and epoxy resins. These resins may also be used in a combination of two or more. The resin for use may contain particles such as inorganic filler or organic filler.
The film thickness of the hard coating layer is preferably 1 to 50 μm. A film thickness of 1 μm or more is preferable because it ensures sufficient curing and leads to a high level of pencil hardness. A film thickness of 50 μm or less suppresses curling caused by hardening and contraction of the hard coating, thus increasing film handleability.
The method for forming a hard coating layer for use may be, for example, a Mayer bar, gravure coater, die coater, or knife coater. These methods can be used without any particular limitation and can be suitably selected according to viscosity and film thickness.
The method for curing the hard coating layer for use may be a method using energy beams such as UV light or electron beams, or a method using heat. From the standpoint of minimizing damage to the film, a method using energy beams such as UV light or electron beams is preferable.
The pencil hardness of the hard coating layer is preferably 3H or higher, and more preferably 4H or higher. A pencil hardness of 3H or higher prevents the hard coating layer from being easily scratched, while not decreasing visibility. Although a higher level of pencil hardness of the hard coating layer is generally better, the pencil hardness may be 9H or lower, or 8H or lower; even a hard coating layer with a pencil hardness of 6H or lower is usable in practice without problems.
The hard coating layer in the present invention can be used for the purpose of protecting a display by increasing the pencil hardness of the surface as described above, and preferably has high transmittance. The hard coating film has a total light transmittance of preferably 85% or more, more preferably 87% or more, and still more preferably 88% or more. A transmittance of 85% or more ensures sufficient visibility. In general, a higher total light transmittance of the hard coating film is preferable. However, from the standpoint of stable production, the total light transmittance of the hard coating film is preferably 99% or less, and may be 97% or less. In general, the hard coating film preferably has a lower haze, and preferably a haze of 3% or less. The hard coating film has a haze of more preferably 2% or less, and most preferably 1% or less. A haze of 3% or less can improve the visibility of images. Although a lower haze is generally better, the haze of the hard coating film is preferably 0.1% or more, or may be 0.3% or more, from the standpoint of stable production.
The hard coating layer may have further functions added. For example, a hard coating layer with additional functionality, such as an anti-glare layer, anti-glare anti-reflective layer, anti-reflective layer, low-reflection layer, or antistatic layer having the predetermined pencil hardness above, can also be preferably used in the present invention.
The polyester film used as a substrate film of a touchscreen module may also be provided with a hard coating layer. For example, when an ITO layer is used as a transparent electrode layer of a touchscreen module, a refractive index adjustment layer is preferably provided between the substrate film and the transparent electrode layer to make the electrode pattern less visible. In this case, the hard coating layer itself may serve as a refractive index adjustment layer, or a separate refractive index adjustment layer may be laminated.
The polyester film, which is the substrate of a laminated film, preferably has an adhesive layer on the surface opposite the surface having the hard coating layer formed. The material that constitutes the adhesive layer is not particularly limited. Examples of usable materials include conventional tackifiers, such as rubber-based tackifiers, acrylic-based tackifiers, and polyolefin-based tackifiers. Rubber-based tackifiers include natural rubber, butadiene rubber, isoprene rubber, and styrene-based block copolymer elastomers such as SBS, SIS, SEBS, and SEPS. Acrylic-based tackifiers include cross-linked copolymers such as methyl (meth)acrylate, ethyl (meth)acrylate, butyl (meth)acrylate, pentyl (meth)acrylate, hexyl (meth)acrylate, and 2-ethylhexyl (meth)acrylate. Crosslinking agents include isocyanate compounds, epoxy compounds, metal-chelating agents, and compounds containing multiple double bonds. Polyolefin-based tackifiers include ethylene-propylene rubber such as EPM and EPDM, products containing ethylene-propylene rubber as a soft segment and polyethylene or polypropylene as a hard segment, and blends of ethylene-propylene rubber with polyethylene or polypropylene. Tackiness can be adjusted by adding a known tackiness-imparting agent, a softener, or like agent to the adhesive layer. Tackiness can also be adjusted by adjusting the molecular weight of the base polymer for use. The adhesive layer may further contain other components. Examples of other components include additives (i.e., adjuvants) such as dyes, pigments, antistatic agents, antioxidants, light stabilizers, UV light absorbers, neutralizers, nucleating agents, epoxy stabilizers, lubricants, antimicrobial agents, flame retardants, and plasticizers.
The adhesive layer has a film thickness of 1 μm to 50 μm, preferably 2 μm to 40 μm, and more preferably 4 μm to 30 μm.
After a tackifier solution is applied and dried (or after a monomer or oligomer is applied in the case of an acrylic-based tackifier), a method such as curing by radiation may be performed, and a substrate-free optical clear adhesive (OCA) sheet may be transferred.
Adhesive strength (peel strength) is preferably changed depending on the material to which the adhesive layer is adhered. For foldable displays, the adhesive strength on glass after 24 hours is preferably 10 to 40 N/25 mm because weak adhesive strength causes the bending portion to be lifted.
The adhesive layer may have a release film on its surface (the opposite surface of the polyester film).
The release film for use in the adhesive sheet can be selected from a wide range of films used as release films. The resin for the substrate film is not particularly limited, and resins that can serve as a resin film, such as polyester, polycarbonate, polyamide, polyimide, polyamide-imide, polystyrene, triacetyl cellulose, polypropylene, and cyclic polyolefin, can be used without any limitation. Of these, from the standpoint of mechanical strength, heat resistance, and supply stability, polyester is preferable, and polyethylene terephthalate is more preferable. The film may be an unstretched film or a stretched film. If the film is a stretched film, it may be a uniaxially stretched film or biaxially stretched film. In particular, a biaxially stretched polyethylene terephthalate film is preferable.
A substrate film having releasing properties can be used as a release film as is. To adjust releasing properties, surface treatment, such as corona treatment, plasma treatment, or flame treatment, may also be performed.
Additionally, the substrate film may have a release layer formed on it. Examples of release layers include silicone-based release layers, amino-resin-based release layers, alkyd-resin-based release layers, and long-chain-acrylic-resin-based release layers. The composition and type of the release layer can be suitably selected according to required release force.
If a release layer is provided, an easy-to-adhere layer may be formed on the substrate film. The easy-to-adhere layer for use can be those conventionally used in substrate films, such as polyester-based layers, acrylic-based layers, or polyurethane-based layers. The easy-to-adhere layer for use can be selected according to the substrate film or release layer for use.
An antistatic layer for a release film may be provided. Examples of antistatic agents for a release layer include quaternary ammonium salts, conductive polymers such as polyaniline and polythiophene, needle-shaped metal filler, conductive fine high-refractive-index particles, such as fine tin-doped-indium-oxide particles, fine antimony-doped-tin-oxide particles, and combinations thereof. The binder resin for use includes polyester, polyurethane, polyamide, and acrylic. An antistatic layer is provided on the release surface; an antistatic layer may be present as an underlayer of the release layer or may be provided on the surface opposite the release surface.
The following describes the present invention with reference to Examples and Comparative Examples. First, the methods for evaluating characteristic values used in the present invention are described below.
A film or polyester resin was crushed, dried, and dissolved in a mixed solvent of phenol and tetrachloroethane in a ratio of phenol to tetrachloroethane of 60/40 (mass ratio). This solution was then centrifuged to remove inorganic particles. The flow time of the solution with a concentration of 0.4 (g/dl) and the flow time of the solvent alone were measured with an Ubbelohde viscometer at 30° C. From the time ratio, the intrinsic viscosity was calculated by using the Huggins equation with the assumption of Huggins's constant being 0.38.
A polyester film sample with a size of 20 mm in the width direction×110 mm in the machine direction was prepared. The sample was folded 200,000 times at a rate of 1 time/second with a DLDMLH-FS tension-free U-shape folding tester (produced by Yuasa System Co., Ltd.) with the bend radius set to 1.5 mm. During the process, the sample was fixed at 10 mm from both ends of the long side, and the area to be folded was 20 mm×90 mm.
A: No cracks or deformation can be confirmed on the sample.
B: The sample has a crack or a crease, and the maximum height of the lifted portion is 5 mm or more when it is placed horizontally.
In the same manner as in the above bending test, a sample was folded 200,000 times at a rate of 1 time/second with the bend radius set to 0.5 mm.
A: No defect is observed on the film surface of the outer side of the folded portion.
B: The display has been broken, or creases (cracks) can be observed on the film surface of the outer side of the folded portion.
In the same manner as in the above bending test, a sample was folded 200,000 times at a rate of 1 time/second with the bend radius set to 3.0 mm. When a sample had a hard coating layer only on one surface, the test was performed with the hard coating layer present on the inner side, and also performed with the hard coating layer present on the outer side.
A: There is no crack on the hard coating layer, and no deformation of the hard coating film can be confirmed.
B: The sample is broken, cracks can be confirmed on the hard coating layer, or deformation of the hard coating film can be confirmed.
In accordance with JIS K 7142:2008 (Plastic: Determination of Refractive Index (method A)), the refractive index in the longitudinal direction, the refractive index in the width direction, and the refractive index in the thickness direction were determined with an Abbe refractometer (NAR-4T, produced by Atago Co., Ltd., measurement wavelength: 589 nm).
Pencil hardness was measured under a load of 750 g at a rate of 1.0 mm/s with the pencil hardness of a hard coating film as a sample in accordance with JIS K 5600-5-4:1999. In the present invention, a pencil hardness of 3H or more was rated as passing.
Total light transmittance and haze were measured with a NDH5000 haze meter (produced by Nippon Denshoku Industries Co., Ltd.).
Density was measured in accordance with the method described in JIS K 7112:1999 (density-gradient tube method) (unit: g/cm3).
The tensile modulus of elasticity of a polyester film in the bending direction and in the folding direction was measured at 23° C. in accordance with JIS K7127:1999.
(8) Indentation Depth after Test Force is Unloaded
A sample was cut to a size of about 2 cm×2 cm, and the surface opposite the surface to be measured was immobilized on a micro cover glass (18×18 mm, produced by Matsunami Glass Ind., Ltd.) with an adhesive (Cemedinet High-super 30). After being adhered and immobilized, the sample was allowed to stand for at least 12 hours at room temperature. Thereafter, the sample was measured for indentation depth (μm) after a test force was unloaded with a DUH-211 dynamic ultra-micro hardness tester (Shimadzu Corporation) under the following conditions.
Test mode: loading-unloading test
Indenter for use: edge angle: 1150, triangular pyramid indenter
Indenter elasticity: 1.140×108 N/mm2
Indenter Poisson's ratio: 0.07
Test force: 50 mN
Loading rate: 4.44 mN/sec
Loading retention time: 2 sec
Unloading retention time: 0 sec
A sample film was cut to a size of 10 mm (length)×250 mm (width), and a long side was aligned with the direction to be measured and marked at intervals of 200 mm. Distance A, which is between the marks, was measured under constant tension of 5 g. Subsequently, the sample film was allowed to stand in atmosphere at 150° C. in an oven for 30 minutes without a load, and then taken out of the oven, followed by cooling to room temperature. Thereafter, distance B, which is between the marks, was measured under constant tension of 5 g, and the heat shrinkage (%) was determined by using the following formula. The heat shrinkage was measured at three evenly separated points in the width direction of the sample film, and the average of the values at the three points was taken as the heat shrinkage (%).
Heat shrinkage (%)=[(A−B)×100]/A
The sample film was cut so that the vertical and horizontal directions were different for both the bending direction and the folding direction, and measurement was performed. The data of the direction larger in measurement value was taken as the maximum heat shrinkage (%).
In-plane retardation refers to a parameter defined as the product (ΔN×d) of anisotropy of the refractive indices of two axes orthogonal to each other on the film (ΔN=|Nx−Ny|) and the film thickness d (nm), and is a measure of optical isotropy or anisotropy. The anisotropy (AN) of refractive indices of two axes was determined by the following method. The axis orientation directions of a film were determined by using two polarization plates. The film was cut to a rectangle of 4 cm×2 cm such that the axis orientation directions were orthogonal to each other, and the cut piece was taken as a measurement sample. For this sample, the refractive indices (Nx,Ny) of the two axes that are orthogonal to each other and the refractive index in the thickness direction (Nz) were determined with an Abbe refractometer (NAR-4T, produced by Atago Co., Ltd.). The absolute value of the difference between the refractive indices of the two axes (|Nx−Ny|) was taken as the anisotropy (ΔN) of the refractive indices. The thickness d (nm) of the film was measured with an electric micrometer (Millitron 1245D, produced by Feinpruf GmbH), and the value was converted to the unit nm. From the product (ΔN×d) of the anisotropy (AN) of refractive indices and the film thickness d (nm), in-plane retardation (Re) was determined. Of the oriented axes, the axis showing a larger refractive index is defined as a slow axis.
A polyester film according to the present invention was adhered to the surface of an OLED tablet (Samsung Galaxy Tab S3SM-T820, 9.7-inch, 32 GB tablet) by using water with the bending direction aligned with the longitudinal direction of the tablet. The OLED tablet was set to white screen display (R=0, G=0, B=0) and visually observed by changing the angle from an oblique direction to the normal direction of the display screen, while the display screen was rotated in the in-plane direction, and it was determined whether rainbow unevenness was present as described below. Color irregularities observed only on the tablet used were excluded from the determination.
A: No rainbow unevenness is observed in any direction.
B: Very light rainbow unevenness is observed in some direction.
C: Light rainbow unevenness is observed over a slightly wide area in some direction.
D: Rainbow unevenness is clearly observed over a wide area in some direction.
The esterification reactor for use was a continuous esterification reactor composed of a three-stage complete mixing tank equipped with a stirrer, a partial condenser, a feedstock inlet, and a product outlet. Slurry of TPA in an amount of 2 tons/hr, 2 mol of EG per mol of TPA, and antimony trioxide in an amount of 160 ppm on an Sb atom basis relative to a produced PET was continuously supplied to the first esterification reaction vessel of the esterification reactor, and allowed to react at 255° C. under ordinary pressure with an average residence time of 4 hours. Subsequently, the reaction product in the first esterification reaction vessel was continuously taken out of the system and supplied to the second esterification reaction vessel. EG distilled from the first esterification reaction vessel in an amount of 8 mass % of the produced polymer (produced PET) was then supplied to the second esterification reaction vessel, and an EG solution containing magnesium acetate in an amount of 65 ppm on a Mg atom basis relative to the produced PET, and an EG solution containing TMPA in an amount of 20 ppm on a P atom basis relative to the produced PET, were further added thereto, followed by a reaction at 260° C. under ordinary pressure with an average residence time of 1.5 hours. Subsequently, the reaction product in the second esterification reaction vessel was continuously taken out of the system and supplied to the third esterification reaction vessel, and an EG solution containing TMPA in an amount of 20 ppm on a P atom basis relative to the produced PET was further added thereto, followed by a reaction at 260° C. under ordinary pressure with an average residence time of 0.5 hours. The esterified reaction product generated in the third esterification reaction vessel was continuously supplied to a three-stage continuous polycondensation reactor to perform polycondensation, and filtered through a sintered stainless-steel filter material (nominal filtration accuracy: 5-μm particles are 90% cut), thereby obtaining polyethylene terephthalate pellet (a) with an intrinsic viscosity of 0.62 dl/g.
Polyethylene terephthalate pellet (b) was obtained in the same manner as above by adjusting the intrinsic viscosity to 0.580 dl/g, except that the residence time of the third esterification reaction was adjusted in the production step of polyethylene terephthalate pellet (a).
Polyethylene terephthalate pellet (c) with an intrinsic viscosity of 0.75 dl/g was obtained by subjecting polyethylene terephthalate pellet (a) to solid-state polymerization at 220° C. under a reduced pressure of 0.5 mmHg for a different period of time with a rotary vacuum polymerizer.
72.96 parts by mass of 1,3-bis(methylisocyanate) cyclohexane, 12.60 parts by mass of dimethylol propionic acid, 11.74 parts by mass of neopentyl glycol, 112.70 parts by mass of polycarbonate diol with a number average molecular weight of 2000, and as solvents, 85.00 parts by mass of acetonitrile and 5.00 parts by mass of N-methylpyrrolidone, were placed in a four-necked flask equipped with a stirrer, a Dimroth condenser, a nitrogen-feeding tube, a silica-gel-drying tube, and a thermometer, and stirred in a nitrogen atmosphere at 75° C. for 3 hours; the reaction mixture was confirmed to have reached a predetermined amine equivalent. Subsequently, after this reaction mixture was cooled to 40° C., 9.03 parts by mass of triethyl amine was added, thereby obtaining a polyurethane prepolymer D solution. Subsequently, 450 g of water was added to a reactor equipped with a homogenizing disperser capable of high-speed stirring, and the temperature was adjusted to 25° C., followed by dispersing an isocyanate-terminated prepolymer in water with stirring at 2000 min−1. Thereafter, some acetonitrile and water were removed under reduced pressure, thereby preparing water-soluble polyurethane resin (A) with a solids content of 35 mass %.
200 parts by mass of isophorone diisocyanate and 4 parts by mass of 3-methyl-1-phenyl-2-phosphorene-1-oxide (carbodiimidized catalyst) were added to a flask equipped with a thermometer, a nitrogen-gas-feeding tube, a reflux condenser, a dropping funnel, and a stirrer, and stirred in a nitrogen atmosphere at 180° C. for 10 hours, thereby obtaining an isocyanate-terminated isophorone carbodiimide (degree of polymerization: 5). Subsequently, 111.2 g of the obtained carbodiimide and 80 g of polyethylene glycol monomethyl ether (molecular weight: 400) were reacted at 100° C. for 24 hours. Water was gradually added thereto at 50° C., thereby obtaining transparent yellowish water-soluble carbodiimide compound (B) with a solids content of 40 mass %.
The following coating materials were mixed, thereby preparing a coating solution.
Water: 16.97 parts by mass
Isopropanol: 21.96 parts by mass
Polyurethane resin (A): 3.27 parts by mass
Water-soluble carbodiimide compound (B): 1.22 parts by mass
Particles: 0.51 parts by mass
(silica sol with a mean particle size of 40 nm, solids concentration: 40 mass %)
Surfactant: 0.05 parts by mass
(silicone-based surfactant, solids concentration: 100 masse)
0.1 parts by weight of a leveling agent (produced by BYK-Chemie Japan, BYK307, concentration: 100%) were added to 100 parts by weight of a hard coating material (produced by JSR Corporation, OPSTAR® Z7503, concentration: 75%), and the mixture was diluted with methyl ethyl ketone, thereby preparing a hard coating solution a with a solids concentration of 40 wt %.
Polyethylene terephthalate pellet (a) was supplied to an extruder and melted at 285° C. This polymer was filtered through a sintered stainless-steel filter material (nominal filtration accuracy: 10-μm particles are 95% cut) and extruded from the outlet into a sheet form. The sheet-form polymer was then brought into contact with a casting drum (surface temperature: 30° C.) by using an electrostatic application casting method to solidify the polymer by cooling, thereby preparing an unstretched film. The unstretched film was uniformly heated to 75° C. by using heating rolls, and then heated to 85° C. using a non-contact heater, followed by roll drawing (drawing in the longitudinal direction) to a 1.4-fold film. Subsequently, the coating solution for forming an easy-to-adhere layer was applied to both surfaces of the obtained uniaxially stretched film by roll coating, and then dried at 80° C. for 20 seconds. Adjustment was made so that the amount of the applied coating solution for forming an easy-to-adhere layer was 0.06 g/m2 after final drying (after being biaxially drawn). Thereafter, the film was guided to a tenter, preheated at 105° C., and laterally stretched 4.0-fold at 95° C. With the width fixed, the film was subjected to heat fixation at 230° C. for 5 seconds, and further relaxed by 4% in the width direction at 180° C., thereby obtaining a polyethylene terephthalate film with a thickness of 50 μm. Hard coating solution a was applied to one surface of the prepared film by using a Meyer bar such that the thickness of the film after drying was 5 μm, and dried at 80° C. for 1 minute, followed by irradiating the film with UV light (integrated light intensity: 200 mJ/cm2), thereby obtaining a hard coating film. Thereafter, a double-sided adhesive sheet (produced by LINTEC Corporation, trade name: OPTERIA MO-3006C, thickness: 25 μm) was applied to the surface of the polyethylene terephthalate film on which the hard coating layer was not stacked, thereby obtaining a laminated film. Tables 1 and 2 show the evaluation results.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the draw ratio in the longitudinal direction was changed as shown in Table 1.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the draw ratio in the width direction was changed to 4.4-fold, and the heat fixation temperature was changed to 220° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 4, except that the draw ratio in the longitudinal direction was changed as shown in Table 1.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the draw ratio in the width direction was changed to 5.5-fold, and the heat fixation temperature was changed to 190° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 7, except that the draw ratio in the longitudinal direction was changed as shown in Table 1.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 5, except that in the production step of Example 5, the film was drawn in the longitudinal direction, and then subjected to relaxation heat treatment by 10% at 100° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 5, except that in the production step of Example 5, the film was released from the clips at 200° C. after heat fixation, and the film was subjected to relaxation heat treatment in the longitudinal direction and in the width direction. In the longitudinal direction, the tenter rate and the take-up roll rate were adjusted to achieve a relaxation rate of 3%. The relaxation in the width direction was set to be free.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the temperature during drawing in the longitudinal direction was changed to 75° C., and the heat fixation temperature was changed to 220° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that drawing was performed by changing the temperature during drawing in the longitudinal direction to 75° C. and the draw ratio to 1.2-fold, and then drawing was performed by changing the draw ratio in the width direction to 5.0-fold.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 3, except that the drawing in the longitudinal direction in Example 3 was changed to two-stage drawing, and the draw ratio in the first stage was 1.2-fold, and the draw ratio in the second stage was 1.67-fold. The total draw ratio in the longitudinal direction was about 2.0-fold.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 5, except that the preheating temperature during the drawing in the width direction was changed to 95° C., and the heat fixation temperature was changed to 190° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 2, except that the drawing in the width direction in Example 2 was changed to two-stage drawing, with the draw ratio in the first stage of 1.5-fold, and the draw ratio in the second stage of 4.0-fold, and the heat fixation temperature was changed to 190° C. The total draw ratio in the width direction was 6.0-fold.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 2, except that the thickness was changed as shown in Table 2. Although the polyester film obtained in Example 17 did not necessarily show good results in rainbow unevenness observation, the polyester film of the present invention can be used in any part of a foldable display. For example, the polyester film obtained in Example 17 can be preferably used in a back protection film of a foldable display, in which rainbow unevenness does not matter.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that in the production step of Example 1, relaxation heat treatment in the width direction was not performed.
In the same manner as in Example 1, an unstretched film was prepared, and then the unstretched film was preheated at 75° C. with a tenter, followed by laterally drawing the film 1.4-fold at 85° C. The coating solution for forming an easy-to-adhere layer was applied to the both surfaces of the obtained uniaxially stretched film by roll coating and dried at 80° C. for 20 seconds. Adjustment was made so that the amount of the applied coating solution for forming an easy-to-adhere layer was 0.06 g/m2 after final drying (after being biaxially drawn). The film was uniformly heated to 105° C. by using heating rolls, and then heated to 95° C. using a non-contact heater, followed by roll drawing (drawing in the longitudinal direction) to a 4.0-fold film. With the width fixed, the film was subjected to heat fixation at 230° C. for 5 seconds, thereby obtaining a polyethylene terephthalate film with a thickness of 50 μm. The subsequent steps were performed in the same manner as in Example 1, thereby obtaining a hard coating film and a laminated film.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that drawing in the longitudinal direction was not performed, and only lateral uniaxial drawing in the width direction was performed.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 7, except that drawing in the longitudinal direction was not performed, and only lateral uniaxial drawing in the width direction was performed.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the heat fixation temperature was changed to 220° C., and the PET pellet shown in Table 1 was used, while the thickness was changed as shown in Table 2. In Comparative Examples 3 to 7, the heat fixation temperature was lower than that of Example 1, and the combination of the draw ratio in the longitudinal direction and the draw ratio in the width direction was not the best, given the preferable range of each draw ratio. Thus, as shown in Table 2, the refractive index in the thickness direction was increased, the indentation depth after unloading the test force was large, and the pencil hardness after lamination of the hard coating layer was also lower than in the Examples.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the draw ratio in the longitudinal direction was changed to 2.7-fold, and the heat fixation temperature was changed to 220° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the draw ratio in the longitudinal direction was changed to 3.4-fold.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 4, except that the heat fixation temperature was changed to 100° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 13, except that the drawing temperature in the longitudinal direction was changed to 130° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 1, except that the preheating temperature in the width direction was changed to 120° C.
A polyester film, a hard coating film, and a laminated film were prepared in the same manner as in Example 13, except that the draw ratio in the width direction was changed to 5.5-fold, and the heat fixation temperature was changed to 230° C.
The laminated films of the Examples and Comparative Examples were each laminated on an organic EL module via a 25-μm-thick adhesive layer, thereby preparing foldable smartphone-type displays that can be folded in half at their center, with a radius of 3 mm, which corresponds to the bend radius in
While maintaining its suitability in mass production, a foldable display using the polyester film, the hard coating film, or the laminated film for foldable displays according to the present invention is unlikely to deform after the polyester film or the hard coating film positioned on the front surface of the foldable display is repeatedly folded, thus not causing image distortion at the folding portion of the display. In particular, a mobile device or image display device equipped with a foldable display using the polyester film, hard coating film, or laminated film according to the present invention as a surface protection film provides beautiful images and has a variety of functionality, while being highly convenient such as in portability.
| Number | Date | Country | Kind |
|---|---|---|---|
| 2019-021187 | Feb 2019 | JP | national |
| 2019-083808 | Apr 2019 | JP | national |
| 2019-090528 | May 2019 | JP | national |
| 2019-099158 | May 2019 | JP | national |
| 2019-130038 | Jul 2019 | JP | national |
| Filing Document | Filing Date | Country | Kind |
|---|---|---|---|
| PCT/JP2020/001043 | 1/15/2020 | WO | 00 |