Claims
- 1. A biaxially oriented polyester film for laminating a metal plate to be used for manufacturing a vessel or can comprising a copolyethylene terephthalate which contains a lubricant having an average particle of diameter of no greater than 2.5 .mu.m and has a melting point of from 210.degree. to 245.degree. C., said film having a thickness of from 10 to 75 .mu.m, a plane orientation coefficient of from 0.10 to 0.16, a thermal shrinkage at 150.degree. C. of no higher than 10%, a density of lower than 1.385 g/cm.sup.3, a refractive index in a direction of thickness of from 1.495 to 1.530, and a film plane refractive index of from 1.61 to 1.66 in all directions, wherein a current value measured in a rust prevention test on a vessel or can prepared by deep drawing from a metal plate on which said film is laminated is no higher than 0.2 mA, said current value being measured in accordance with the test method as described in the Resistance to Impact Fracture test recited in the specification.
- 2. A polyester film according to claim 1, wherein said lubricant is spheric monodispersed lubricant having an average particle diameter of no greater than 2.5 m and a particle diameter ratio, defined as a ratio of long diameter/short diameter, of from 1.0 to 1.2.
- 3. A biaxially oriented polyester film according to claim 1, wherein a current value measured in a test of resistance to impact fracture on a vessel or deep drawing from a metal plate on which said film is laminated is no higher than 0.2 mA.
- 4. A biaxially oriented polyester film according to claim 1, wherein a current value measured in a test of resistance to thermal embrittlement on a vessel or can prepared by deep drawing from a metal plate on which said film is laminated is no higher than 0.2 mA.
- 5. A biaxially oriented polyester film according to claim 1 wherein the lubricant is mono-dispersed in the copolyethylene terephthalate as spherical particles selected from the group consisting of silica, titania, zirconia, calcium carbonate, barium sulfate and silicone.
Priority Claims (2)
Number |
Date |
Country |
Kind |
1-221571 |
Aug 1989 |
JPX |
|
1-248863 |
Sep 1989 |
JPX |
|
Parent Case Info
This application is a continuation application of Ser. No. 08/020,450, filed Feb. 22, 1993, now abandoned, which in turn is a continuation application of Ser. No. 07/874,208, filed Apr. 27, 1992, now abandoned, which in turn is a continuation application of Ser. No. 07/575,652, filed Aug. 30, 1990, now abandoned.
US Referenced Citations (2)
Number |
Name |
Date |
Kind |
4115617 |
Mitsuishi et al. |
Sep 1978 |
|
4818581 |
Katoh et al. |
Apr 1989 |
|
Foreign Referenced Citations (1)
Number |
Date |
Country |
0312303 |
Apr 1989 |
EPX |
Non-Patent Literature Citations (2)
Entry |
Database WPIL, accession No. 89-266608 [37], Derwent Publications Ltd, London, GB; & JP-A-1 192 546 (Nippon Steel) *Whole abstract*. |
Database WPIL, accession No. 89-266607 [37], Derwent Publications Ltd, London, GB; & JP-A-1 192 545 (Nippon Steel) * Whole abstract*. |
Continuations (3)
|
Number |
Date |
Country |
Parent |
20450 |
Feb 1993 |
|
Parent |
874208 |
Apr 1992 |
|
Parent |
575652 |
Aug 1990 |
|