POLYESTERS AND FIBERS MADE THEREFROM

Abstract
Disclosed herein are polyesters and fibers made therefrom. The fiber comprises a polymer, poly(trimethylene furandicarboxylate) (PTF), and PTF based copolymers.
Description
FIELD OF THE INVENTION

This invention relates in general to fibers prepared from polyesters and in particular poly(trimethylene-2,5-furandicarboxylate) (PTF) and PTF based blends and copolymers.


BACKGROUND INFORMATION

Synthetic fibers are found in many essential applications ranging from apparel to carpets to automobile interiors. Polypropylene (PP), polyethylene terephthalate (PET) and polyamides (nylon-6 and nylon-6,6) are frequently used polymers in such applications and while manufacturing routes and applications have been developed during the past several decades, these polymers are all derived from fossil fuel.


In the recent years sustainable routes have been developed for bioderived monomers and polymers. One such example is Sorona® polytrimethylene terephthalate (PTT) that is based on bio-derived 1,3-propanediol (Bio-PDO™) and terephthalic acid. The bio-content of the polymer resin is 37% by weight. Since terephthalic acid is derived from fossil fuel (naptha) there is an interest in new bio-derived aromatic monomers that are compatible with traditional polymerization routes. Furan 2,5-dicarboxylic acid (also referred to herein as 2,5-furandicarboxylic acid, or FDCA) meets this requirement since it is a bifunctional aromatic diacid made from sugar intermediates. The polymer produced from FDCA and Bio-PDO™ (PolyTrimethylene-2,5-Furandicarboxylate (PTF)), is thus 100% bioderived. These bio-derived polymers can be used to produce bio-derived fibers. There is substantial interest in 100% bio-derived polyester fibers because bio-derived polymers are resourced from renewable materials, and there is typically a reduced environmental footprint versus incumbent fibers.


SUMMARY OF THE INVENTION

In an aspect of the invention, there is a fiber comprising a polymer, wherein the polymer comprises poly(alkylene furandicarboxylate) obtained by polymerization of a reaction mixture comprising a furan dicarboxylic acid and a C2 to C12 aliphatic diol.


In an embodiment, a fiber of the present invention is obtained from a polymer composition which is a polymer blend comprising poly(trimethylene-2,5-furandicarboxylate), alternatively referred to herein as PTF, and a second poly(alkylene-furandicarboxylate) that is different from PTF, and wherein the second poly(alkylene-furandicarboxylate) is derived from furan dicarboxylic acid and an aliphatic diol selected from the group consisting of ethylene glycol and C4 to C12 aliphatic diols.


In one embodiment, a fiber of the present invention is obtained from a polymer blend comprising PTF and poly(alkylene terephthalate), wherein the poly(alkylene terephthalate) comprises a C2 to C12 aliphatic diol moiety.


In an embodiment, a fiber of the present invention is obtained from a copolymer comprising of 2,5-furandicarboxylate, terephthalate and 1,3 propane diol monomer units.


The molar ratio of 2,5-furan dicarboxylic acid to other diacids can be any range, for example the molar ratio can be greater than 1:100 or alternatively in the range of 1:100 to 100 to 1 or 1:9 to 9:1 or 1:3 to 3:1 or 1:1 in which the diol is added at an excess of 1.2 to 3 equivalents to total diacids charged.


In an aspect, there is a method of making a fiber comprising the steps:

    • a. providing a polymer composition, wherein the polymer comprises poly(alkylene furandicarboxylate) obtained by polymerization of a reaction mixture comprising a furan dicarboxylic acid and a C2 to C12 aliphatic diol; and
    • b. spinning the polymer composition to form fibers, such that the temperature applied to the polymer during spinning is in the range of about 180-265° C.





BRIEF DESCRIPTION OF THE DRAWINGS

The invention is illustrated by way of example and not limited to the accompanying figures.



FIG. 1 schematically illustrates an exemplary apparatus for spinning either spun-drawn or partially oriented yarn.



FIG. 2 is a schematic illustration of an exemplary press spinning unit.





DETAILED DESCRIPTION

Disclosed is a fiber comprising a polymer, wherein the polymer comprises poly(alkylene furandicarboxylate) derived from the polymerization of furan dicarboxylic acid and a C2 to C12 aliphatic diol.


Poly(alkylene-furandicarboxylate) can be prepared from a C2 to C12 aliphatic diol and from 2,5-furan dicarboxylic acid or a derivative thereof. In an embodiment, the aliphatic diol is a biologically derived C3 diol, such as 1, 3 propane diol.


Derivatives of 2,5-furan dicarboxylic acid suitable for use in the practice of the present invention include furan dicarboxylic acids wherein the hydrogen atoms at the 3 and/or 4 position(s) on the furan ring are replaced, independently of each other, with alkylene substituents such as, for example, —CH3, —C2H5, or a C3 to C25 straight-chain, branched or cyclic alkane group, optionally containing one to three heteroatoms selected from the group consisting of O, N, Si and S, and also optionally substituted with at least one member selected from the group consisting of —Cl, —Br, —F, —I, —OH, —NH2 and —SH.


One of ordinary skill in the art would also know that in the polymerization reaction described herein, carboxylic acid derivatives such as acid halides, carboxylic acid esters, and carboxylic acid anhydrides can be useful functional equivalents of either or both of the carboxylic acid moieties of the furan. That is, these functionally equivalent groups can be used to obtain the polymeric fiber of the presently claimed invention when reacted with C2 to C12 aliphatic diols. For convenience, the carboxylic acid groups of the furan dicarboxylic acid will be referred to as “acid” or “diacid” groups, but for the purposes of the present invention, such reference will also incorporate any conventional functional equivalent of a carboxylic acid.


As used herein, the terms “biologically-derived” and “bio-derived” are used interchangeably and refer to chemical compounds including monomers and polymers, that are obtained from plants and contain only renewable carbon—that is carbon obtained from a source that can be regenerated, for example, from crops—and not fossil fuel-based or petroleum-based carbon. Hence, bio-derived materials have less impact on the environment as their creation does not deplete diminishing fossil fuels and, upon degradation, releases carbon back to the atmosphere for use by plants once again.


Examples of suitable C2 to C12 aliphatic diol include, but are not limited to, ethylene glycol, diethylene glycol, 1,2-propanediol, 1,3-propanediol, 1,4-butanediol, 1,5-pentanediol, 1,6-hexanediol, 1,4-cyclohexanedimethanol, and 2,2-dimethyl-1,3-propanediol.


In a particular embodiment of the present invention, an aliphatic diol can be 1,3-propanediol (Bio-PDO™) that is biologically derived and is polymerized with a furan 2,5-dicarboxyl derivative, whereby the polymer shown below (poly(trimethylene-2,5-furandicarboxylate), known alternatively herein as PTF, can be obtained:




embedded image


where n=10-1000 or 50-500 or 25-185 or 80-185. Other variations of PTF can be obtained by using 1,2-propanediol, or by using mixtures of the two propanediols.


In a fiber of the present invention, the polymer can have a number average molecular weight (Mn) in the range of 10,000-12,000, or in the range of 10,000-13,000, or in the range of 10,000-14,000, or in the range of 10,000-15,000, or in the range of 10,000-16,000, or in the range of 10,000-17,000, or in the range of 10,000-18,000, or in the range of 10,000-19,000, or in the range of 10,000-20,000, or in the range of 10,000-21,000, or in the range of 4900-196,000. Desirable molecular weight for a polymer composition useful in the practice of the present invention can depend on the final application or use of the fiber. However, typical of most polymers, processing polymers having very high molecular weight can be difficult due to high melt viscosity of polymeric materials of higher molecular weight. Therefore, it can be desirable to balance difficulties in processing high molecular weight polymers with any improvement that can be obtained in the properties of high molecular weight polymers in the practice of the present invention.


A fiber of the present invention can have a modulus in the range of 10-100 g/den, or in the range of 30-100 g/den, or in the range of 35-100 g/den, or in the range of 40-100 g/den, or in the range of 45-100 g/den, or in the range of 50-100 g/den, or in the range of 55-100 g/den.


A fiber of the present invention can have a tenacity in the range of about 0.2-5 g/den, or in the range of 0.8-5 g/den, or in the range of about 1.0-5 g/den, or in the range of 1.2-5 g/den, or in the range of 1.4-5 g/den, or in the range of 1.6-5 g/den, or in the range of 1.8-5, or in the range of 2.0-5 g/den, or in the range of 2.2-5 g/den, or in the range of 2.4-5 g/den, or in the range of about 2.6-5 g/den, or in the range of 2.8-5 g/den, or in the range of 3.0-5 g/den Typically, as the molecular weight of the polymer of the present invention increases, the tenacity will have a tendency to increase until a plateau is reached. Therefore tenacity, as it may relate to molecular weight of the polymer, can be manipulated by varying the molecular weight within the broad range described herein.


A fiber of the present invention can have a percent elongation in the range of 5-500, or in the range of 25-500, or in the range of 30-500, or in the range of about 35-500, or in the range of 40-500, or in the range of 45-500, or in the range of 50-500, or in the range of 55-500, or in the range of 60-500, or in the range of 65-500, or in the range of 70-500, or in the range of 75-500, or in the range of 80-500, or in the range of 85-500, or in the range of 90-500, or in the range of 95-500, or in the range of 100-500, or in the range of 150-500, or in the range of 200-500. Typically, as the molecular weight of the polymer of the present invention increases, the percent elongation will increase until a plateau is reached. Percent elongation, as it may relate to molecular weight of the polymer, therefore can be manipulated by varying the molecular weight within the broad range described herein.


A fiber of the present invention can be oriented or not oriented, and a polymer suitable for use in the practice of the present invention can be amorphous or crystalline. It can be useful to orient fibers in applications such as apparel or carpets. Alternatively, fibers that are not oriented can be useful in such applications as staple.


In one embodiment, a polymer as described herein has a heat of crystallization less than 1 J/g or less than 10 J/g or less than 100 J/g, as measured by differential scanning calorimetry with heating rates of 10° C./min. In one embodiment, the polymer consists essentially of poly(trimethylene-2,5-furandicarboxylate) (PTF) and is amorphous. Crystalline polymers can be suitable for preparing fibers of the present invention, and such fibers can be useful in such applications as apparel and carpets. Alternatively, amorphous polymers can provide fibers of the present invention that are suitable for use in such applications as disposable garments, for example medical gowns, protective apparel, disposable gloves, diapers.


In one embodiment, the polymer is a polymer blend comprising poly(trimethylene-2,5-furandicarboxylate) and a second poly(alkylene-furandicarboxylate) that is different from the PTF, wherein the poly(alkylene-furandicarboxylate) is obtained by polymerization of a furan dicarboxylic acid and an aliphatic diol selected from the group consisting of ethylene glycol, and C4 to C12 diols, or mixtures thereof. The polymers can be blended in any proportion in order to provide a fiber having properties desirable in a given fiber application. One of ordinary skill in the art would understand how to obtain desirable fiber properties by using different proportions of materials to achieve the properties needed from the blend. For example, a blend useful for preparing a fiber of the present invention can have from about 0.1 to about 99.9% or from about 5 to about 75% or from about 10 to about 50% by weight of PTF based on the total weight of the blend, in order to obtain a fiber having desirable modulus, elongation, tenacity, crystallinity.


In another embodiment, a fiber of the present invention is obtained from a polymer blend comprising poly(trimethylene-2,5-furandicarboxylate) and poly(alkylene terephthalate). The polymers can be blended in any proportion in order to provide a fiber having properties desirable in a given fiber application. One of ordinary skill in the art would understand how to obtain desirable fiber properties by blending different proportions of materials. For example, a blend useful for preparing a fiber of the present invention can have from about 0.1 to about 99.9% or alternatively from about 5 to about 75% or from about 10 to about 50% by weight of PTF based on the total weight of the blend, in order to obtain a fiber having desirable modulus, elongation, tenacity, crystallinity.


In another embodiment, a fiber of the present invention can be obtained from a random or block copolymer comprising 2,5-furandicarboxyl, terephthalate and Bio-PDO™ monomer units. The monomers can be reacted in any proportion in order to provide a fiber having properties desirable in a given fiber application. One of ordinary skill in the art would understand how to obtain desirable fiber properties by using different proportions of materials to achieve the properties of the fiber which are desired. For example, a copolymer useful for preparing a fiber of the present invention can have from about 0.1 to about 99.9% or alternatively from about 5 to about 75% or alternatively from about 10 to about 50% by weight of PTF-based repeat units based on the total weight of the copolymer, in order to obtain a fiber having desirable modulus, elongation, tenacity, crystallinity. PTF-based repeat units, as the term is used herein, include a diol and a furanyl dicarboxylate moiety.


The molar ratio of 2,5-furan dicarboxylic acid to other diacids can be any ratio that provides a fiber having the desirable properties for the intended fiber application. For example the molar ratio can be greater than 1:100 or alternatively in the range of from about 1:100 (2,5-furan dicarboxylic acid):(other acid) to 100:1 or 1:9 to 9:1 or 1:3 to 3:1 or 1:1 in which the diol is added at an excess of 1.2 to 3 equivalents to total diacids charged.


Other diols and polyols useful as monomers in the practice of the present invention include, for example, 1,4-benzenedimethanol, poly(ethylene glycol), poly(tetrahydrofuran), 2,5-di(hydroxymethyl)tetrahydrofuran, isosorbide, glycerol, pentaerythritol, sorbitol, mannitol, erythritol, and threitol.


Other polyfunctional aromatic acids suitable for use in the practice of the present invention include, for example, terephthalic acid, isophthalic acid, adipic acid, azelic acid, sebacic acid, dodecanoic acid, 1,4-cyclohexane dicarboxylic acid, maleic acid, succinic acid, naphthalene dicarboxylic acid, and 1,3,5-benzenetricarboxylic acid.


Hydroxy acids can be suitable comonomers having both hydroxyl and acid functionality for use in the practice of the present invention to form copolymers, and thereby form covalent linkages with acid and/or hydroxyl functional moieties in the polymerization mixture. Examples of suitable hydroxy acids include but are not limited to, glycolic acid, hydroxybutyric acid, hydroxycaproic acid, hydroxyvaleric acid, 7-hydroxyheptanoic acid, 8-hydroxycaproic acid, 9-hydroxynonanoic acid, or lactic acid; or those derived from pivalolactone, ε-caprolactone or L,L, D,D or D,L lactides.


Exemplary copolymers derived from 2,5-furan dicarboxylic acid, at least one of a diol or a polyol monomer, and at least one of a polyfunctional aromatic acid or a hydroxyl acid include, but are not limited to copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and terephthalic acid; copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and succinic acid; copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid; copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and adipic acid; copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and sebacic acid, copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and isosorbide; copolymer of 1,3-propanediol, 2,5-furandicarboxylic acid and isomannide.


The intrinsic viscosity of the poly(trimethylene-2,5-furandicarboxylate) is at least 0.3 dl/g, or at least 0.5 dl/g or at least 0.6 dl/g and most preferably at least 0.7 dl/g. The intrinsic viscosity of the disclosed polymer composition is up to about 0.52 dl/g, or up to 0.7 dl/g, or up to about 0.92 dl/g.


Additives, including delusterants, heat stabilizers, viscosity boosters, optical brighteners, pigments, and antioxidants, can be used. TiO2 or other pigments can be added, such as described in U.S. Pat. Nos. 3,671,379, 5,798,433 and 5,340,909, EP 699 700 and 847 960, and WO 00/26301, which are incorporated herein by reference.


By “fibers”, reference is made to items recognized in the art as fibers, such as continuous filaments, monofilament, staple, etc. The fibers can be round or have other shapes, such as octalobal, delta, sunburst (also known as sol), scalloped oval, trilobal, tetra-channel (also known as quatra-channel), scalloped ribbon, ribbon, starburst, etc. They can be solid, hollow or multi-hollow. They can be used to prepare fabrics or textiles, carpets (from bulked continuous filaments and staple), and other products. Fabrics include knitted, woven and nonwoven fabrics.


The fibers may be produced from the PTF homopolymer or from blends comprising PTF and copolymers comprising of PTF repeat units. The fiber of the preset invention can have fiber denier of less than 1 or less than 50.


A fiber as disclosed herein can be, and more typically is, a continuous filament fiber. Alternatively, however, the fiber can be a discontinuous filament fiber that is composed of pieces of entangled filament, and such a fiber can have an length/diameter ratio (L/D) of about 20-60. Yarns as formed from such fibers are typically long unbroken lengths of continuous filament fiber in which the fibers are bonded or interlocked together and are typically not twisted. If desired, however, a yarn can be prepared from a fiber hereof by providing forward or reverse twist therein, and this is more often the case if the fiber used is a discontinuous filament fiber.


The advantage of PTF compared to existing polyesters, is that the PTF is 100% bio-derived and also allows for lower processing temperatures due to its relatively lower melting point. Further, PTF also lends itself to be spun at relatively low molecular weights.


Method of Preparation of Polymer

The various polymers used in a fiber hereof include polyesters, and also various copolymers (random or block), that may be made according to the selection of which monomers are used for polymerization.


The polymer can be prepared from a C2 to C12 aliphatic diol and from 2,5-furan dicarboxylic acid or a derivative thereof. Aliphatic diol is a biologically derived C3 diol, such as 1, 3 propane diol. Derivatives of 2,5-furan dicarboxylic acid suitable for use in the practice of the present invention include furan dicarboxylic acids wherein the hydrogen atoms at the 3 and/or 4 position(s) on the furan ring are replaced, independently of each other, with alkylene substituents such as, for example, —CH3, —C2H5, or a C3 to C25 straight-chain, branched or cyclic alkane group, optionally containing one to three heteroatoms selected from the group consisting of O, N, Si and S, and also optionally substituted with at least one member selected from the group consisting of —Cl, —Br, —F, —I, —OH, —NH2 and —SH.


A polymer for use herein can be made by a two-step process, wherein first a prepolymer is made having a 2,5-furandicarboxylate moiety within the polymer backbone. This intermediate product is preferably an ester composed of two diol monomers and one diacid monomer, wherein at least part of the diacid monomers comprises 2,5-FDCA, followed by a melt-polymerization of the prepolymers under suitable polymerization conditions. Such conditions typically involve reduced pressure to remove the excess of diol monomers. Esters of 2,5 furan dicarboxylic acid or the diacid itself or mixtures of both may be used.


For instance, in step (I) dimethyl-2,5-furandicarboxylate is reacted in a catalyzed transesterification process with about 2 equivalents of a diol, to generate the prepolymer while removing 2 equivalents of methanol. Dimethyl-2,5-furandicarboxylate is preferred, as this transesterification step generates methanol, a volatile alcohol that is easy to remove. However, as starting material, diesters of 2,5-FDCA with other volatile alcohols or phenols (e.g. having a boiling point at atmospheric pressure of less than 150° C., preferably less than 100° C., more preferably of less than 80° C.) may be used as well. Preferred examples therefore include ethanol, methanol and a mixture of ethanol and methanol. The aforementioned reaction leads to a polyester. Moreover, the diol monomers may if desired contain additional hydroxyl groups, such as glycerol, pentaerythritol or sugar alcohols. The furan diacid may also be used directly, or converted to the diester or can be added along with the diester.


Step (II) of this process is a catalyzed polycondensation step, wherein the prepolymer is polycondensed under reduced pressure, at an elevated temperature and in the presence of a suitable catalyst. In various embodiments of this process, the first step is a transesterification step, catalyzed by a specific transesterification catalyst at a temperature preferably in the range of from about 150-260° C., more preferably in the range of from about 180-240° C. and carried out until the starting ester content is reduced until it reaches the range of about 3 mol % to less than about 1 mol %. The transesterification catalyst may be removed, to avoid interaction in the second step of polycondensation, but typically is included in the second step. The selection of the transesterification catalyst is therefore effected by the selection of the catalyst used in the polycondensation step. Tyzor® organic titanates and zirconates catalysts such Tyzor® TPT, Tyzor® TBT can be used. Tin(IV) based catalysts, preferably organotin(IV) based catalysts such as alkyltin(IV) salts including monoalkyltin(IV) salts, dialkyl and trialkyltin(IV) salts and mixtures thereof, can also be used as transesterification catalysts, that are better than tin(II) based catalysts such as tin(II) octoate. These tin(IV) based catalysts may be used with alternative or additional transesterification catalysts. Antimony based catalysts can also be used.


Examples of alternative or additional transesterification catalysts that may be used in step 1 include one or more of titanium(IV) alkoxides or titanium(IV) chelates, zirconium(IV) chelates, or zirconium(IV) salts (e.g. alkoxides); hafnium(IV) chelates or hafnium(IV) salts (e.g. alkoxides). Other suitable transesterification catalysts are butyltin(IV) tris(octoate), dibutyltin(IV) di(octoate), dibutyltin(IV) diacetate, dibutyltin(IV) laureate, bis(dibutylchlorotin(IV)) oxide, dibutyltin dichloride, tributyltin(IV) benzoate and dibutyltin oxide, antimony oxides.


The active catalyst as present during the reaction may be different from the catalyst as added to the reaction mixture. The catalysts are used in an amount of about 0.01 mol % relative to initial diester to about 0.2 mol % relative to initial diester, more preferably in an amount of about 0.04 mol % of initial diester to about 0.16 mol % of initial diester.


The intermediate product is used as such in the subsequent polycondensation step. In this catalyzed polycondensation step, the prepolymer is polycondensed under reduced pressure, at an elevated temperature and in the presence of a suitable catalyst. The temperature is preferably in the range of about the melting point of the polymer to about 30° C. above this melting point, but preferably not less than about 180° C. The pressure should be reduced preferably gradually. It should preferably be reduced to as low as possible, more preferably below 1 mbar.


This second step is preferably catalyzed by a polycondensation catalyst such as one of those listed below, and the reaction is preferably carried out at mild melt conditions. Examples of suitable polycondensation catalysts include titanium(IV) alkoxides or titanium(IV) chelates, zirconium(IV) chelates, or zirconium(IV) salts (e.g. alkoxides); hafnium(IV) chelates or hafnium(IV) salts (e.g. alkoxides), tin(II) salts such as tin(II) oxide, tin(II) dioctoate, butyltin(II) octoate, or tin(II) oxalate. Various catalysts include tin(II) salts obtained by the reduction of the tin(IV) catalyst, e.g. alkyltin(IV), dialkyltin(IV), or trialkyltin(IV) salts, antimony based salts Additional catalyst can be added prior to the condensation reaction to increase reaction efficacy, which can be used as transesterification catalyst with a reducing compound. Reducing compounds used may be well-known reducing compounds, preferably phosphorus compounds.


Particularly preferred reducing compounds are organophosphorus compounds of trivalent phosphorus, in particular a monoalkyl or dialkyl phosphinate, a phosphonite or a phosphite. Examples of suitable phosphorus compounds are triphenyl phosphite, diphenyl alkyl phosphite, phenyl dialkyl phosphite, tris(nonylphenyl)phosphite, trilauryl phosphite, trioctadecyl phosphite, distearyl pentaerythritol diphosphite, tris(2,4-di-tert-butylphenyl)phosphite, diisodecyl pentaerythritol diphosphite, di(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, tristearylsorbitol triphosphite, tetrakis(2,4-di-tert-butylphenyl) 4,4′-diphenylenediphosphonite, 4,4′-isopropylidenediphenol alkyl (C12-15) phosphite, poly(dipropylene glycol) phenyl phosphite, tetraphenyl dipropylene glycol phosphite, tetraphenyl diisopropylene glycol phosphite, trisisodecyl phosphite, diisodecyl-phenyl phosphite, diphenyl isodecyl phosphite, and mixtures of these.


Other suitable catalysts therefore include tin(II) salts such as tin(II) dioctoate, butyl(II) octoate and other alkyltin(II) octoate compounds, prepared from the corresponding tin(IV) salt using e.g. a trialkyl phosphite, a monoalkyl diaryl phosphite, a dialkyl monoaryl phosphite or a triaryl phosphite. Preferably, the reducing compound is added in the melt of the prepolymer. The addition of the reducing compound at this stage will avoid discoloration of the polymer product and increase molecular weight of the polymer.


The catalysts are used in an amount of about 0.01 mol % relative to initial diester to about 0.2 mol % relative to initial diester, more preferably in an amount of about 0.04 mol % of initial diester, to about 0.16 mol % of initial diester.


In solid state polymerization (SSP) processes pellets, granules, chips or flakes of polymer are subjected for a certain amount of time to elevated temperatures (below melting point) in a hopper, a tumbling drier or a vertical tube reactor or the like. The presence of titanium based catalysts during SSP of the FDCA-based polymers has enabled the polymer to reach a number average molecular weight of 20,000 and greater. As compared to SSP as typically used to upgrade recycled PET, the temperature should be elevated but nonetheless remain (well) below the melting point of the polymer.


In an aspect, there is a method of making a fiber comprising providing a polymer composition comprising poly(alkylene furandicarboxylate) derived from furan dicarboxylic acid and a C2 to C2 aliphatic diol and spinning the polymer composition to form fibers, such that the highest temperature applied to the polymer during spinning is in the range of about 210-250° C.


In an embodiment, the highest temperature applied to the polymer during spinning is in the range of 210° C.-215° C., or in the range of 210-220° C., or in the range of 210-225° C., or in the range of 210-230° C., or in the range of 210-235° C., or in the range of 210-240° C., or in the range of 210-245° C., or in the range of 210-265° C.


In an embodiment, the step of providing a polymer composition comprises providing a polymer blend comprising poly(trimethylene-2,5-furandicarboxylate) and poly(alkylene-furandicarboxylate), as disclosed supra.


In another embodiment, the step of providing a polymer composition comprises providing a polymer blend comprising poly(trimethylene-2,5-furandicarboxylate) and poly(alkylene terephthalate), as disclosed supra.


In yet another embodiment, the step of providing a polymer composition comprises providing a copolymer derived from 2,5-furan dicarboxylic acid at least one of a diol or a polyol monomer, as disclosed supra.



FIG. 1 schematically illustrates an exemplary apparatus for spinning either spun-drawn or partially oriented yarn, which is useful in the process of the spinning disclosed fiber. An exemplary process using the exemplary apparatus shown in FIG. 1 is disclosed infra in Example 1.



FIG. 2 is a schematic illustration of an exemplary press spinning unit, which is useful in the process of the spinning disclosed fiber. An exemplary process using the exemplary apparatus shown in FIG. 2 is disclosed infra in Example 4.


As used herein, the terms “comprises,” “comprising,” “includes,” “including,” “has,” “having” or any other variation thereof, are intended to cover a non-exclusive inclusion. For example, a process, method, article, or apparatus that comprises a list of elements is not necessarily limited to only those elements but may include other elements not expressly listed or inherent to such process, method, article, or apparatus. Further, unless expressly stated to the contrary, “or” refers to an inclusive or and not to an exclusive or. For example, a condition A or B is satisfied by any one of the following: A is true (or present) and B is false (or not present), A is false (or not present) and B is true (or present), and both A and B are true (or present).


As used herein, the phrase “one or more” is intended to cover a non-exclusive inclusion. For example, one or more of A, B, and C implies any one of the following: A alone, B alone, C alone, a combination of A and B, a combination of B and C, a combination of A and C, or a combination of A, B, and C.


Also, use of “a” or “an” are employed to describe elements and described herein. This is done merely for convenience and to give a general sense of the scope of the invention. This description should be read to include one or at least one and the singular also includes the plural unless it is obvious that it is meant otherwise.


Unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Although methods and materials similar or equivalent to those described herein can be used in the practice or testing of embodiments of the disclosed compositions, suitable methods and materials are described below. All publications, patent applications, patents, and other references mentioned herein are incorporated by reference in their entirety, unless a particular passage is cited. In case of conflict, the present specification, including definitions, will control. In addition, the materials, methods, and examples are illustrative only and not intended to be limiting.


In the foregoing specification, the concepts have been disclosed with reference to specific embodiments. However, one of ordinary skill in the art appreciates that various modifications and changes can be made without departing from the scope of the invention as set forth in the claims below.


Benefits, other advantages, and solutions to problems have been described above with regard to specific embodiments. However, the benefits, advantages, solutions to problems, and any feature(s) that may cause any benefit, advantage, or solution to occur or become more pronounced are not to be construed as a critical, required, or essential feature of any or all embodiments.


It is to be appreciated that certain features are, for clarity, described herein in the context of separate embodiments, may also be provided in combination in a single embodiment. Conversely, various features that are, for brevity, described in the context of a single embodiment, may also be provided separately or in any sub combination. Further, reference to values stated in ranges include each and every value within that range.


The concepts disclosed herein will be further described in the following examples, which do not limit the scope of the invention described in the claims.


The examples cited here relate to tannin-based foams. The discussion below describes how PTF based polymers, copolymers and blends and fibers made therefrom are formed.


Examples
Methods
Molecular Weight by Size Exclusion Chromatography

A size exclusion chromatography system Alliance 2695™ from Waters Corporation (Milford, Mass.), was provided with a Waters 414™ differential refractive index detector, a multiangle light scattering photometer DAWN Heleos II (Wyatt Technologies, Santa Barbara, Calif.), and a ViscoStar™ differential capillary viscometer detector (Wyatt). The software for data acquisition and reduction was Astra® version 5.4 by Wyatt. The columns used were two Shodex GPC HFIP-806M™ styrene-divinyl benzene columns with an exclusion limit of 2×107 and 8,000/30 cm theoretical plates; and one Shodex GPC HFIP-804M™ styrene-divinyl benzene column with an exclusion limit 2×105 and 10,000/30 cm theoretical plates.


The specimen was dissolved in 1,1,1,3,3,3-hexafluoro-2-propanol (HFIP) containing 0.01 M sodium trifluoroacetate by mixing at 50° C. with moderate agitation for four hours followed by filtration through a 0.45 μm PTFE filter. Concentration of the solution was circa 2 mg/mL.


Data was taken with the chromatograph set at 35° C., with a flow rate of 0.5 ml/min. The injection volume was 100 μl. The run time was 80 min. Data reduction was performed incorporating data from all three detectors described above. 8 scattering angles were employed with the light scattering detector. No standard for column calibration was involved in the data processing.


Molecular Weight by Intrinsic Viscosity

Intrinsic viscosity (IV) was determined using the Goodyear R-103B Equivalent IV method, using T-3, Selar® X250, Sorona®64 as calibration standards on a Viscotek® Forced Flow Viscometer Modey Y-501C. Methylene chloride/trifluoro acetic acid was the solvent carrier.


Thermal Analysis

Glass transition temperature (Tg) and melting point (Tm) were determined by differential scanning calorimetry (DSC) performed according to ASTM D3418-08.



1H-NMR Spectroscopy


1H-NMR spectra were recorded on a 400 MHz NMR in either deuterated chloroform (CDCl3) or tetrachloroethane (tce-d2). Proton chemical shifts are reported in ppm downfield of TMS using the resonance of the deuterated solvent as internal standard.


Fiber Mechanical Properties

Fiber tenacity was measured on a Statimat ME fully automated tensile tester. The test was run according to an automatic static tensile test on yarns with a constant deformation rate according to ASTM D 2256.


Fiber Crystallinity Determination

Wide angle X-ray scattering (WAXS) is a non-disruptive technique to study fiber crystallinity. WAXS generates a diffraction pattern from which crystallinity is measured and depicted as a crystallinity index (CI). CI is defined as the ratio of the area of crystalline peaks to the total area after deconvolution of the crystalline peaks from the broad amorphous regions in the XRD pattern, CI takes a value between 0 and 1, i.e. 0 for a fully amorphous sample and 1 for a fully crystalline sample.


Measurements were made on a PANalytical X'Pert MPD dffractometer equipped with a Curved Graphite Monochromator producing Cu K-Alpha radiation (wavelength=1.5418). Measurement conditions: 0.5 degree divergence slit, 0.5 degree anti-scatter slit and 0.3 mm receiving slit, and generator setting of 45 k V, 40 mA. The data are collected in reflection geometry. The diffraction scan range is 4 to 40 degrees two-theta with a step size of 0.05 degrees. During the measurement the sample is rotated 2 seconds per revolution with a counting time of 5 seconds per step.


Materials

As used in the Examples below were: titanium(IV)isobutoxide (TBT catalyst), titanium(V)isopropoxide (TPT catalyst), ethylene glycol, 1-4-butanediol, polytetramethyleneglycol 1000 g/mol (PTMEG), trimethyltrimelitate (TMTM) obtained from Aldrich and used as received. 2,5-furandimethylester (FDME) was obtained from AstaTech and used as received. Ethylene copolymer Surlyn® 8920, Polytrimethylene terephthalate (Sorona®, PTT, J1156, 0.96IV) and bio 1,3-propane diol (Bio-PDO™) were provided from the DuPont company and was used as received. Dovernox-10 was obtained from Dovernox® and used as received,


Example 1: Synthesis, Solid Phase Polymerization, and Fiber Spinning of Polytrimethylene-2,5-Furandicarboxylate (PTF) and Resulting Properties
A. Polycondensation of Bio-PDO™ and FDME (PTF Pre-Polymer)



embedded image


2,5-furandimethylester (2557 g), 1,3-propanediol (1902 g), titanium (IV) isopropoxide (2 g), Dovernox-10 (5.4 g) were charged to a 10-lb stainless steel stirred autoclave (Delaware valley steel 1955, vessel #: XS 1963) equipped with a stirring rod and condenser. A nitrogen purge was applied and stirring was commenced at 30 rpm to form a slurry. While stirring, the autoclave was subject to three cycles of pressurization to 50 psi of nitrogen followed by evacuation. A weak nitrogen purge (approximately 0.5 L/min) was then established to maintain an inert atmosphere. While the autoclave was heated to the set point of 240° C. methanol evolution began at a batch temperature of 185° C. Methanol distillation continued for 120 minutes during which the batch temperature increased from 185° C. to 238° C. When the temperature leveled out at 238° C., a second charge of titanium (IV) isopropoxide (2 g) was added. At this time a vacuum ramp was initiated that during 60 minutes reduced the pressure from 760 torr to 300 torr (pumping through the column) and from 300 torr to 0.05 torr (pumping through the trap). The mixture, when at 0.05 torr, was left under vacuum and stirring for 5 hours after which nitrogen was used to pressurize the vessel back to 760 torr.


The formed polymer was recovered by pushing the melt through an exit valve at the bottom of the vessel and into a water quench bath. The thus formed strand was strung through a pelletizer, equipped with an air jet to dry the polymer free from moisture, cutting the polymer strand into chips approximately ¼ inch long and approximately ⅛ inch in diameter. Yield was approximately 2724 g (approximately 5 lbs). Tg was ca. 58° C. (DSC, 5° C./min, 2nd heat), Tm was ca. 176° C. (DSC, 5° C./min, 2nd heat). 1H-NMR (TCE-d) δ: 7.05 (s, 2H), 4.40 (m, 4H), 2.15 (m, 2H). Mn (SEC) approximately 10 300 D, PDI 1.97. IV approximately 0.55 dL/g.


Using the same synthetic setup as described above, four other polymerizations were conducted. The summarized reaction setup, and obtained molecular weight characteristics are captured in the Table 1 below.









TABLE 1







Characteristics of PTF pre-polymers.














Batch
Condensation






Reaction
temp.
time

Mn

IV


#
(° C.)
(hrs)
Additive
(g/mol)1
PDI1
(dL/g)2
















PTF_1p
223
5
N/A
4 300
1.87
0.28


PTF_2p
228
7
N/A
5 400
1.89
0.35


PTF_3p
238
5
D-103
10 300 
1.97
0.55


PTF_4p
248
4
D-103
9100
2.04
0.57






1from SEC,




2from intrinsic viscosity,




3Dovernox-10 (D-10).







B. Solid Phase Polymerization of PTF Pre-Polymers

In order to increase the molecular weight of the PTF pre-polymers (described in section 1A above) solid phase polymerization was conducted. The quenched and pelletized PTF pre-polymer was initially crystallized by placing the material in a vacuum oven, subsequently heating the pellets under vacuum and a weak nitrogen purge to 120° C. for 120 minutes. At this time the oven temperature was increased to approximately 163° C. and the pellets left under vacuum/nitrogen purge condition to build molecular weight. The oven was turned off and the pellets allowed to cool and analyzed with SEC and IV, for a summary of conditions and obtained molecular weights see Table 2 below.









TABLE 2







Characteristics of solid phased PTF polymers.














PTF pre-
SPP
SPP reaction






polymer
temp.
time
Mn

IV


Polymer
used
(° C.)
(hrs)
(g/mol)1
PDI1
(dL/g)2





PTF_1
PTF_1p
163
423
11 500
1.91
0.52


PTF_2
PTF_2p
163
423
13 900
2.09
0.70


PTF_3
PTF_3p
163
256
18 100
1.95
0.78


PTF_4
PTF_4p
165
290
n/a
n/a
0.92






1from SEC,




2from intrinsic viscosity.







C. Fiber Spinning and Fiber Properties

Pellets of polymer prepared as described above (Example 1A and 1B) were melt spun into spun-drawn, or partially oriented fibers. The pellets were fed using a K-Tron weight loss feeder to a 28 millimeter diameter twin screw extruder operating at ca. 30-50 rpm to maintain a die pressure between 400-1100 psi. The extruder has nine heated barrel zones and the polymer was extruded with the following temperature settings: 100/150/230/230/230/230/230/230/230° C. A Zenith metering pump conveyed the melt to the spinneret at a throughput of approximately 10.5 g/min, the transfer line temperature was held at 240° C.


Referring to FIG. 1 the molten polymer from the metering pump was forced through a 4 mm glass bead, one 50 mesh, and five 200 mesh screens, to a 10 hole (d/l, 12/30 mills) or 17 hole (d/l, 12/48 mills or d/l, 15/90 mills) round spinneret, 301, heated to 240° C. The filament stream leaving the spinneret, 302, were passed through an air quench zone, 303, where they were impinged upon a transverse air stream at 21° C. The filaments were then passed over a spin finish head, 304, where a spin finish was applied (1 wt % finish on yarn), and the filaments were converged to form a yarn. The yarn so formed was conveyed via a tensioning roll, 305, onto two non-heated feed rolls (godets), 306, and then onto two non-heated draw rolls (godets), 308, via a steam jet, 307, operating at a temperature of 130° C. and a pressure of 30 psi. From the draw rolls, 308, the filaments were passed onto two annealing rolls (godets), 309, and to a pair of let-down rolls, 310, and collected on a winder, 311. The spinneret pack (top and band) was set at 240° C., and the die at 240° C. For spinning partially oriented yarn a winder, 312, was added after the feed rolls, 306, and non-drawn yarn collected at various wind-up speeds.


Additional spinning conditions and resulting fiber properties are summarized in Tables 3-11 below.









TABLE 3







Conditions for spinning spun drawn and partially oriented PTF yarn from 3 different spinnerets


using steam assisted draw (Tsteam = 130° C.) with optionally heated annealing rolls.






















Feed roll
Draw roll

Annealing
Annealing
Wind-up







speed
speed
Draw
roll speed
roll temp
speed


Sample
Polymer
Spinneret
Denier
dpf
(m/min)
(m/min)
ratio
(m/min)
(° C.)
(m/min)




















1.1
PTF-1
10 hole,
39
3.9
700
2100
3.0
2100
n/a
2100


1.2
PTF-1
d/l 12/30
38
3.8
750
2100
2.8
2100
n/a
2100


1.3
PTF-1
mills
39
3.9
807
2100
2.6
2100
n/a
2100


1.4
PTF-1

115
11.5
700
n/a
n/a
n/a
n/a
700


1.5
PTF-2

38
3.8
700
2100
3.0
2100
n/a
2100


1.6
PTF-2

111
11.2
700
n/a
n/a
n/a
n/a
700


1.7
PTF-2
17 hole,
39
2.3
807
2100
2.6
2100
n/a
2100


1.8
PTF-2
d/l 12/48
30
1.8
750
2100
2.8
2100
n/a
2100


1.9
PTF-2
mills
39
2.3
583
2100
3.6
2100
n/a
2100


1.10
PTF-2

31
1.8
700
2100
3.0
2130
90
2220


1.11
PTF-3
17 hole,
40
2.3
807
2100
2.6
2100
n/a
2100


1.12
PTF-3
d/l 15/90
40
2.3
700
2100
3.0
2100
n/a
2100


1.13
PTF-3
mills
36
2.1
700
2100
3.0
2130
90
2240


1.14
PTF-3

117
6.9
700
n/a
n/a
n/a
n/a
700


1.15
PTF-3

91
5.4
900
n/a
n/a
n/a
n/a
900


1.16
PTF-3

18
1.0
2000
n/a
n/a
n/a
n/a
2000
















TABLE 4







Mechanical properties of spun drawn and partially oriented (POY) PTF yarn.



















Draw
Line
Modulus
Tenacity
Elongation


Sample
Polymer
Denier
dpf
ratio
speed
(g/den)
(g/den)
(%)


















1.1
PTF-1
39
3.9
3.0
2100
36.4
1.1
27.4


1.2
PTF-1
38
3.8
2.8
2100
38.3
1.0
24.9


1.3
PTF-1
39
3.9
2.6
2100
n/a
n/a
n/a


1.4
PTF-1
115
11.5
POY
700
n/a
n/a
n/a


1.5
PTF-2
38
3.8
3.0
2100
40.1
1.6
31.9


1.6
PTF-2
111
11.2
POY
700
n/a
n/a
n/a


1.7
PTF-2
39
2.3
2.6
2100
36.3
1.5
43.3


1.8
PTF-2
30
1.8
2.8
2100
45.8
1.9
34.9


1.9
PTF-2
39
2.3
3.6
2100
41.8
1.6
23.3


1.10
PTF-2
31
1.8
3.0
2130
32.4
1.4
46.4


1.11
PTF-3
40
2.3
2.6
2100
51.7
2.3
18.9


1.12
PTF-3
40
2.3
3.0
2100
51.5
2.5
17.4


1.13
PTF-3
36
2.1
3.0
2240
36.9
2.2
30.2


1.14
PTF-3
117
6.9
n/a
700
26.3
0.8
194.3 


1.15
PTF-3
91
5.4
n/a
900
27.3
0.9
177.7 


1.16
PTF-3
18
1.0
n/a
2000
47.5
2.0
62.4









As seen in table 4, PTF of varying molecular weights can be successfully spun into fibers at various draw ratios to produce filaments with a steam assisted draw. Obtained filaments are strong, pliable and have measured mechanical properties similar to commercial fibers based on PET or Sorona®. One unexpected result was the ability to successfully spin the low molecular weight PTF grade (PTF-1). Another unexpected finding are the relatively high fiber mechanical despite a low crystalline content of the filaments. All measured crystallinity indexes using WAXS were close to zero.









TABLE 5







Conditions for spinning spun drawn PTF yarn from a 17 hole, d/l 15/60 mills


spinneret using heated draw rolls, and obtained fiber mechanical properties.

























Feed
Draw

Annealing
Feed
Draw
Annealing
Wind-









roll
roll

roll
roll
roll
roll
up


Elongation






speed
speed
Draw
speed
temp
temp
temp
speed
Modulus
Tenacity
at break


Sample
Polymer
Denier
dpf
(m/min)
(m/min)
ratio
(m/min)
(° C.)
(° C.)
(° C.)
(m/min)
(g/den)
(g/den)
(%)
























1.17
PTF_4
38
2.2
954
2100
2.2
2100
60
90
n/a
2100
35.7
3.06
40.3


1.18
PTF_4
38
2.2
1050
2100
2.0
2100
60
90
n/a
2100
36.3
2.98
45.7


1.19
PTF_4
37
2.1
1050
2100
2.0
2100
60
100
n/a
2100
31.9
2.61
61.6


1.20
PTF_4
37
2.1
954
2100
2.2
2100
60
100
n/a
2100
32.3
2.62
53.6
















TABLE 6







Conditions for spinning spun drawn PTF yarn from a 17 hole, d/l 15/60 mills spinneret using heated draw rolls


and a two stage draw with optionally heated annealing rolls, and obtained fiber mechanical properties.


























Feed
Draw

Annealing

Feed
Draw
Annealing
Wind-









roll
roll
Draw
roll
Draw
roll
roll
roll
up


Elongation


Sam-
Poly-


speed
speed
ratio
speed
ratio
temp
temp
temp
speed
Modulus
Tenacity
at break


ple
mer
Denier
dpf
(m/min)
(m/min)
initial
(m/min)
final
(° C.)
(° C.)
(° C.)
(m/min)
(g/den)
(g/den)
(%)

























1.17
PTF_4
34
2
954
2100
2.2
2300
2.4
60
110
n/a
2300
30.2
1.93
57.3


1.18
PTF_4
35
2.05
840
2100
2.5
2200
2.6
60
110
n/a
2200
30.0
1.70
52.1


1.19
PTF_4
28
1.6
900
2100
2.33
2700
3.0
60
110
n/a
2700
37.6
2.24
34.2


1.20
PTF_4
27
1.5
900
2100
2.33
2900
3.2
60
110
n/a
2900
40.9
2.40
26.7


1.17
PTF_4
26
1.5
900
2100
2.33
2900
3.2
60
110
110
2920
29.1
1.37
40.4









As seen in Table 5 and 6, PTF can be successfully spun into fibers using heated draw rolls and using two-staged draw to produce filaments. Obtained filaments are strong, pliable and have measured mechanical properties similar to commercial fibers based on PET or Sorona®. All measured crystallinity indexes using WAXS were close to zero.


Example 2: Partially Oriented PTF Yarn

Partially oriented yarn is produced by directly winding the yarn after the feed roll without any drawing winder, These non-drawn yarns were collected at various wind-up speeds.









TABLE 7







Conditions for spinning partially oriented PTF


yarn from a 17 hole, d/l 15/60 mills spinneret.
















Feed roll speed
Wind-up speed


Sample
Polymer
Denier
dpf
(m/min)
(m/min)















2.1
PTF_4
161
9.4
500
500


2.2
PTF_4
78
4.5
1000
1000
















TABLE 8







Conditions for heated drawn yarn from a partially oriented PTF


yarn precursor, spun from a 17 hole, d/l 15/60 mills spinneret.






















Feed
Draw

Feed
Draw

Wind-







Pre
roll
roll

roll
roll
Post
up


Elongation




draw
speed
speed
Draw
temp
temp
draw
speed
Modulus
Tenacity
at break


Sample
Polymer
denier
(m/min)
(m/min)
ratio
(° C.)
(° C.)
denier
(m/min)
(g/den)
(g/den)
(%)






















2.3
PTF_4
161
100
280
2.8
60
110
62
280
24.0
0.69
88.7


2.4
PTF_4
78
100
280
2.8
60
110
25
280
29.5
0.67
35.8


2.5
PTF_4
78
100
280
2.8
60
115
22
280
28.8
0.59
20.2









Table 7 shows that PTF can be converted into Partially Oriented Yarn (POY). On drawing the POY using heated draw rolls in a low line speed process, filaments are produced that are pliable and with relatively high mechanical strength (Table 8). All measured crystallinity indexes using WAXS were close to zero.


Example 3: Single Filaments from a Polymer Blend of PTF and Surlyn®8920 Ethylene Copolymer

A compound of PTF_4 and Surlyn®8920 pellets were made prior to melt spinning. Here PTF_4 pellets and Surlyn®8920 pellets were fed to provide a concentration of 10 or 20% of Surlyn®8920 based upon the total weight of the blend. The thus combined pellets were mixed in a plastic bag by shaking and tumbling by hand.


The thus mixed batch was placed into a K-Tron T-20 (K-Tron Process Group, Pittman, N.J.) weight loss feeder feeding a PRISM laboratory co-rotating twin screw extruder (available from Thermo Fisher Scientific, Inc.) equipped with a barrel having four heating zones and a diameter of 16 millimeter fitted with a twin spiral P1 screw. The extruder was fitted with a 3/16″ diameter circular cross-Section single aperture strand die. The nominal polymer feed rate was 8 lbs/hr. The first barrel Section was set at 180° C. and the subsequent three barrel Sections and the die were set at 230° C. The screw speed was set at 150 rpm. The melt temperature of the extrudate was determined to be 236° C. by inserting a thermocouple probe into the melt as it exited the die. The thus extruded monofilament strand was quenched in a water bath. Air knives dewatered the strand before it was fed to a cutter that sliced the strand into about 2 mm length blend pellets.


The thus prepared compound was dried and fed into the melt spinning extruder to provide a final concentration of Surlyn®8920 as provided in Table 9.


Table 9 shows feasibility of producing spun yarn using PTF with nucleating agents such as Surlyn® 8920 to produce filaments that are strong, pliable and have measured mechanical properties similar to commercial fibers based on PET or Sorona®. While filaments with 2 wt % Surlyn®8920 had measured crystallinity indexes using WAXS close to zero filaments with 4 wt % Surlyn®8920 had a measured crystallinity of 0.05 (sample 3.8) demonstrating an ability to nucleate PTF crystallization in a spinning operation.









TABLE 9







Conditions for spinning Surlyn ® 8920 nucleated spun drawn PTF yarn from a 17 hole,


d/l 15/60 mills spinneret using heated draw rolls, and obtained fiber mechanical properties.



























Feed
Draw

Annealing
Feed
Draw
Annealing
Wind-


Elon-




Surlyn ®


roll
roll

roll
roll
roll
roll
up
Modu-
Tenac-
gation


Sam-
Poly-
conc.
Deni-

speed
speed
Draw
speed
temp
temp
temp
speed
lus
ity
at break


ple
mer
(wt %)
er
dpf
(m/min)
(m/min)
ratio
(m/min)
(° C.)
(° C.)
(° C.)
(m/min)
(g/den)
(g/den)
(%)

























3.1
PTF_4
2
37
2.1
950
2100
2.2
2100
60
90
n/a
2100
34.2
2.85
49.0


3.2
PTF_4
2
37
2.1
1050
2100
2.0
2100
60
90
n/a
2100
34.6
2.71
49.7


3.3
PTF_4
2
37
2.1
1050
2100
2.0
2100
60
100
n/a
2100
29.6
2.10
64.8


3.4
PTF_4
2
37
2.1
950
2100
2.2
2100
60
100
n/a
2100
30.0
2.19
60.9


3.5
PTF_4
2
37
2.1
945
2080
2.2
2100
60
110
n/a
2100
29.1
1.83
80.9


3.6
PTF_4
2
37
2.1
830
2080
2.5
2100
60
110
n/a
2105
27.4
1.56
72.5


3.7
PTF_4
4
37
2.1
950
2100
2.2
2100
60
90
n/a
2100
32.5
2.59
42.3


3.8
PTF_4
4
37
2.1
1050
2100
2.0
2100
60
90
n/a
2100
34.2
2.62
47.8


3.9
PTF_4
4
37
2.1
1050
2100
2.0
2100
60
100
n/a
2100
30.1
2.12
59.6


3.10
PTF_4
4
37
2.1
950
2100
2.2
2100
60
100
n/a
2100
30.7
2.10
58.2


3.11
PTF_4
4
37
2.1
945
2080
2.2
2100
60
110
n/a
2100
27.5
1.76
91.0


3.12
PTF_4
4
36
2.1
830
2080
2.5
2100
60
110
n/a
2100
27.0
1.67
76.7









Example 4: Single Filaments from a PTF Copolymer Containing Polytetramethylene Glycol (PTMEG) (PTF-Co-PTMEG), and Polyalkylene Furandicarboxylate Polymers

A. Preparation of a PTF Copolymer (PTF-Co-PTMEG)


Bio-PDO™ (110.6 g, 1.454 mol), FDME (133.8 g, 0.727 mol), PTMEG (1.5 g, 1.5 mmol), and TMTM (162 mg, 0.63 mmol), were charged to a pre-dried three necked 500 mL kettle reactor. An overhead stirrer and a distillation condenser were attached. The reactants were stirred at a speed of 50 rounds per minute (rpm) and the reaction mass was kept under nitrogen (g) (N2) purge atmosphere, the condenser was kept at 23° C. The contents were degassed three times by evacuating down to 100 Torr and refilling back with N2 gas. TBT catalyst [0.3 g or 0.31 mL] was added after the first evacuation. The flask was immersed into a preheated metal bath set at 160° C. and allowed to equilibrate for 20 minutes to melt the solids. The temperature was increased to 180° C. and held for 60 minutes after which the temperature was increased to 210° C. and held for an additional 60 minutes to complete the ester interchange and distillation of methanol. The nitrogen purge was closed and a vacuum ramp started, after about 60 minutes the vacuum reached a value of 50-60 mTorr. The temperature was increased to 230° C. and the reaction held under vacuum for 3 hours with stirring at 50-180 rpm. The torque was monitored (readings at 180 rpm) and the polymerization was stopped by removing the heat source. The over head stirrer was stopped and elevated from the floor of the reaction vessel before the vacuum was turned off and the system purged with N2 gas. The kettle reactor was separated and the product decanted and allowed to cool under a purge of nitrogen. The recovered polymer was chopped into pellets using a Wiley mill that was cooled with liquid nitrogen. The so produced polymer pellets were dried under vacuum and a weak nitrogen stream at 120° C. for 24 hours. The recovered yield was approximately 70%, or approximately 100 g. Tg was approximately 55° C., Tm was approximately 161° C. (second heating, 10° C./min). 1H-NMR (tce-d) δ: 7.20 (m, 2H), 4.55-4.35 (m, 4H), 3.37 (m, 4H), 2.30-2.20 (m, 2H), 1.55 (m, 4H). Intrinsic viscosity: 0.55 dL/g.


B. Press Spinning and Properties of a Single Filament from a PTF Copolymer


Referring to FIG. 2 below the polymer prepared above (PTF copolymer, Example 2.1), 401, was charged to a steel cylinder, 402, and topped of with a Teflon® PTFE plug, 403. A hydraulically driven piston, 404, compressed the pellets, 401, into a melting zone provided with a heater and heated to 215° C., 405, where a melt, 406, was formed, and the melt then forced into a separately heated, 407, round cross-Section single-hole spinneret (12 mills diameter, 36 mills length), 408, heated to 215° C. Prior to entering the spinneret, the polymer passed through a filter pack containing one 50 and three 200 mesh screens, not shown. The melt was extruded into a single strand of fiber, 409, at a rate of 0.4 g/min. The extruded fiber was passed through a transverse air quench zone, 410, and thence to a wind-up, 411. Optionally a draw step was included in which the filament was fed onto a cold feed roll, over a heated pin and onto a cold draw roll, and to a wind-up. A summary of conditions is given in Table 10 below. Table 10 shows feasibility of producing a spun single filament from a copolymer of FDCA, Bio-PDO® and PTMEG. While the incorporation of 1 wt % PTMEG accelerates the ability of PTF to crystallize in a DSC pan during a 10° C./min heating scan the produced single filament was shown to be amorphous since the measured crystallinity index (WAXS) was close to zero.


C. Preparation of a Polyester Control of 2,5-Furandimethylester, and Ethylene Glycol (PEF)


Ethylene glycol (84.2 g, 1.357 mol) and FDME (125 g, 0.678 mol) were polymerized in the same setup as used in A above using Tyzor®TPT as catalyst (76 μL). The only difference was that the ester interchange was made at 180° C. for 60 minutes and 200° C. for 60 minutes. The recovered polymer yield was approximately 63 g. Tg was approximately 89° C., Tm was approximately 214° C. (second heating, 10° C.). 1H-NMR (tce-d) δ: 7.30 (m, 2H), 4.70-4.30 (m, 4H). Mn (SEC) approximately 20100 g/mol, PDI (SEC) 1.93.


D, Preparation of a Polyester Control of 2,5-Furandimethylester, and 1,4-Butanediol (PBF)


1,4-butanediol (122.3 g, 1.357 mol) and FDME (125 g, 0.678 mol) were polymerized in the same setup as used in A above using Tyzor©TPT as catalyst (84 μL). The recovered polymer yield was approximately 66 g. Tg was approximately 39° C., Tm was approximately 169° C. 1H-NMR (tce-d) δ: 7.30 (m, 2H), 4.70-4.30 (m, 4H), 2.0 (m, 4H). Mn (SEC) approximately 33700 g/mol, PDI (SEC) 1.68.


As shown in Table 11, various poly alkylene furandicarboxylate polymers were successfully drawn to create POYs or drawn yarn to provide fibers with mechanical properties similar to commercial fibers, one example being Sorona® J1156.









TABLE 10







Conditions for press spinning a nucleated and partially oriented, or drawn,


PTF copolymer filament from a single hole, d/l 12/36 mills spinneret.
























Feed
Draw

Feed
Draw
Hot
Wind-

Tenacity
Elongation





Flow
roll
roll

roll
roll
pin
up

at max
at max





rate
speed
speed
Draw
temp
temp
temp
speed
Modulus
load
load


Sample
Polymer
Denier
(g/min)
(m/min)
(m/min)
ratio
(° C.)
(° C.)
(° C.)
(m/min)
(g/den)
(g/den)
(%)























4.1
PTF-co-
2.1
0.4
n/a
n/a
n/a
n/a
n/a
n/a
1000
23.9
1.2
249



PTMEG


4.2
PTF-co-
1.5
0.4
n/a
n/a
n/a
n/a
n/a
n/a
1420
22.0
1.5
211



PTMEG


4.3
PTF-co-
11.2
0.4
200
350
1.75
23
23
140
333
24.1
0.9
249



PTMEG


4.4
PTF-co-
9.8
0.4
200
450
2.25
23
23
140
430
29.3
1.3
156



PTMEG
















TABLE 11







Conditions for press spinning poly alkylene furandicarboxylate polymers in partially


oriented, or drawn, filament from a single hole, d/l 12/36 mills spinneret.
























Feed
Draw

Feed
Draw
Hot
Wind-

Tenacity
Elongation





Flow
roll
roll

roll
roll
pin
up

at max
at max





rate
speed
speed
Draw
temp
temp
temp
speed
Modulus
load
load


Sample
Polymer
Denier
(g/min)
(m/min)
(m/min)
ratio
(° C.)
(° C.)
(° C.)
(m/min)
(g/den)
(g/den)
(%)























5.1
PEF
10
0.8
n/a
n/a
n/a
n/a
n/a
n/a
700





5.2
PTF_3
9.7
0.8
n/a
n/a
n/a
n/a
n/a
n/a
700
26
0.7
3.5


5.3
PTF_3
9
0.8
249
703
2.8
RT
RT
n/a
700
35
2
87


5.4
PBF
11.2
0.8
n/a
n/a
n/a
n/a
n/a
n/a
700
18
1.9
200


5.5
PBF
10.2
0.8
250
696
2.8
RT
RT
n/a
655
47
3.7
47


5.6
Sorona ®
10
0.8
n/a
n/a
n/a
RT
RT
n/a
700
19
1.7
370



J1156


5.7
Sorona ®
14
0.8
250
700
2.8
RT
RT
n/a
659
24
3.2
160



J1156





RT: Room Temperature





Claims
  • 1. A fiber comprising a polymer, wherein the polymer comprises poly(alkylene furandicarboxylate) obtained by polymerization of reaction mixture comprising furan dicarboxylic acid and a C2 to C12 aliphatic diol.
  • 2. The fiber of claim 1 wherein the poly(alkylene furandicarboxylate) has a number average molecular weight (Mn) in the range of from about 10,000 to about 40,000.
  • 3. The fiber of claim 1 wherein the fiber is oriented.
  • 4. The fiber of claim 1, wherein the polymer has a crystallinity of 100 J/g or less, as measured by differential scanning calorimetry.
  • 5. The fiber of claim 1, wherein an aliphatic diol comprises a C3 diol and the resulting polymer is poly(trimethylene-furandicarboxylate).
  • 6. The fiber of claim 1, wherein the polymer is a polymer blend comprising (1) poly(trimethylene-2,5-furandicarboxylate) and (2) a second poly(alkylene-furandicarboxylate), wherein the poly(alkylene-furandicarboxylate) is derived from furan dicarboxylic acid or its functional equivalent and an aliphatic diol selected from the group consisting of ethylene glycol, and C4, to C12, diols, and wherein the blend comprises 0.1 to about 99.9% by weight of poly(alkylene-furandicarboxylate) based on the total weight of the blend.
  • 7. The fiber of claim 1, wherein the polymer is a polymer blend comprising (1) poly(trimethylene-2,5-furandicarboxylate) and (2) a second poly(alkylene terephthalate) that is derived from terephthalic acid or its functional equivalent and a C2 to C12 aliphatic diol, and wherein the blend comprises 0.1 to about 99.9% by weight of poly(alkylene terephthalate) based on the total weight of the blend.
  • 8. The fiber of claim 1, wherein the polymer is a copolymer and the furan dicarboxylic acid is 2,5-furan dicarboxylic acid, and wherein the reaction mixture further comprises (i) at least one other acid selected from the group consisting of dicarboxylic acids, polyfunctional acids and hydroxy acids, or mixtures thereof, and (ii) optionally a polyol, wherein the diol and the optional polyol are present in a combined total molar ratio of at least 1.2:1 relative to the combined total moles of the 2,5-furan dicarboxylic acid and the at least one other acid, and wherein the 2,5-furan dicarboxylic acid is present in a molar ratio of from about 1:100 to about 100:1 relative to the at least one other acid.
  • 9. A yarn comprising the fiber of claim 1.
  • 10. A bicomponent fiber comprising the fiber of claim 1.
  • 11. A multifilament fiber comprising the fiber of claim 1.
  • 12. A fabric or a textile prepared from the fiber of claim 1.
  • 13. A fabric or textile according to claim 15 which is woven, knitted or non-woven.
  • 14. A method of making a fiber comprising: a. providing a polymer composition comprising poly(alkylene furandicarboxylate) obtained by polymerization of reaction mixture comprising furan dicarboxylic acid and a C2 to C12 aliphatic diol; andb. spinning the polymer composition to form fibers, such that the highest temperature applied to the polymer during spinning is in the range of from about 210 to about 265° C.
Parent Case Info

This application is a Continuation of U.S. application Ser. No. 16/394,545 filed on Apr. 25, 2019, which is a Continuation of U.S. application Ser. No. 14/385,903 filed on Sep. 17, 2014, which is a 371 of International Application No. PCT/US13/034735 filed Mar. 30, 2013, which claims benefit under 35 U.S.C. § 119(e) of U.S. Provisional Patent Application No. 61/618,449 filed on Mar. 30, 2012, which is incorporated herein by reference in its entirety

Provisional Applications (1)
Number Date Country
61618449 Mar 2012 US
Continuations (2)
Number Date Country
Parent 16394545 Apr 2019 US
Child 17738891 US
Parent 14385903 Sep 2014 US
Child 16394545 US