Polyether polyols suitable for flexible polyurethane foam prepared by co-initiation of aqueous solutions of solid polyhydroxyl initiators

Abstract

Polyoxyalkylene polyether polyols suitable for preparation of flexible polyurethane foams are prepared by oxyalkylating an aqueous solution of one or more polyhydric, hydroxyl-functional solid initiators under conditions where both water as well as initiator are oxyalkylated. The polyols have calculated functionalities of between about 2.2 and 4.0 and hydroxyl numbers in the range of 10 to 180. The polyols may be used to prepare soft, high resiliency polyurethane flexible foams at low isocyanate indexes.

Description

Claims

1. A polyurethane flexible foam comprising the reaction product of:

a) an organic di- or polyisocyanate, at an isocyanate index of from about 70 to about 130; with

b) a polyether polyol component comprising at least one polyoxyalkylene polyether polyol comprising the oxyalkylation product of an aqueous solution of one or more polyhydric, hydroxyl-functional solid initiators comprising a saccharide, polysaccharide, or derivative thereof, wherein the water content of said aqueous solution is between 12 weight percent and 90 weight percent relative to the weight of said aqueous solution, and wherein said polyoxyalkylene polyether polyol has a calculated functionality of between about 2.2 and 4.0 and a hydroxyl number between about 10 and about 180 in the presence of

c) an effective amount of a urethane reaction-promoting catalyst;

d) water as a reactive blowing agent in an amount effective to prepare a flexible foam having a density of between about 0.5 lb/ft.sup.3, and 6 lb/ft.sup.3 ; and optionally

e) a cell-stabilizing amount of one or more surfactants.

2. The polyurethane flexible foam of claim 1 further comprising a non-reactive blowing agent such that the density of said polyurethane flexible foam is between about 0.5 lb/ft.sup.3 and 3.5 lb/ft.sup.3.

3. The polyurethane flexible foam of claim 1 wherein said isocyanate index is between about 85 and 125.

4. The polyurethane flexible foam of claim 1 wherein said at least one polyoxyalkylene polyether polyol comprises a polyol having a calculated functionality between about 2.2 and 3.7 and a hydroxyl number between about 20 and about 60, prepared by oxyalkylating an aqueous solution comprising sorbitol and from about 12 weight percent to about 50 weight percent water.