Claims
- 1. A process for the production of a polyethylene microporous membrane having a thickness of at most 10 .mu.m, a breaking strength of at least 200 kg/cm.sup.2 and a porosity of at least 30%, which comprises heating and dissolving polyethylene having a weight average molecular weight of at least 5.times.10.sup.5 in a solvent, forming a gel sheet from the resulting solution, subjecting the gel sheet to a solvent removal treatment to adjust the amount of the solvent removal treatment to adjust the amount of the solvent in the gel sheet to 10 to 80% by weight, heating and stretching the sheet and then removing the residual solvent therefrom.
- 2. The process of claim 1, wherein the solvent is at least one member selected from the group consisting of aliphatic or cyclic hydrocarbons such as nonane, decane, undecane, dodecane, decalin and paraffin oils and mineral oil fractions having boiling points corresponding thereto.
- 3. The process of claim 2, wherein the solvent is a non-volatile solvent such as paraffin oils.
- 4. The process of claim 1, wherein the heating and dissolving is carried out at a temperature of 140.degree. to 250.degree. C.
- 5. The process of claim 1, wherein the solution has a polyethylene content of 1 to 10% by weight.
- 6. The process of claim 1, wherein the forming of a gel sheet is carried out by subjecting the polyethylene solution to extrusion through a die or to spreading over a support, cooling and gelling at a temperature below the gelling temperature and a cooling rate of at least 50.degree. C./min and then forming into a gel sheet with a thickness of 0.1 to 5 mm.
- 7. The process of claim 6, wherein the temperature is 15.degree. to 25.degree. C.
- 8. The process of claim 1, wherein the solvent removal treatment is carried out by immersing the gel sheet in a readily volatile solvent to extract the solvent.
- 9. The process of claim 7, wherein the readily volatile solvent is at least one member selected from the group consisting of hydrocarbons such as pentane, hexane and heptane, chlorinated hydrocarbons such as methylene chloride and carbon tetrachloride, fluorinated hydrocarbons such as trifluoroethane, ethers such as diethyl ether and dioxane and alcohols such as methanol, ethanol and propanol.
- 10. The process of claim 1, wherein the solvent removal treatment is carried out in such a manner that the gel sheet shrinks with a shrinkage of at least 50% in the thickness direction and at most 20% in the longitudinal and lateral directions.
- 11. The process of claim 1, wherein the heating and stretching is carried out biaxially simultaneously or in sequence at a temperature of from the crystal dispersion point to the crystal melting point of the polyethylene of the base stock sheet.
- 12. The process of claim 11, wherein the temperature is 90.degree. to 140.degree. C.
- 13. The process of claim 11, wherein the stretching is carried out with a surface magnification of at least 10 times.
Priority Claims (1)
Number |
Date |
Country |
Kind |
59-83872 |
Apr 1984 |
JPX |
|
Parent Case Info
This is a divisional application of application Ser. No. 728,806, filed Apr. 29, 1985.
US Referenced Citations (5)
Number |
Name |
Date |
Kind |
3468862 |
Schotland |
Sep 1969 |
|
3839516 |
Williams et al. |
Oct 1974 |
|
4472328 |
Sugimoto et al. |
Sep 1984 |
|
4486377 |
Lucchesi et al. |
Dec 1984 |
|
4490431 |
Vitzthum et al. |
Dec 1984 |
|
Divisions (1)
|
Number |
Date |
Country |
Parent |
728806 |
Apr 1985 |
|