Patent Grant
6911518
1. Field of the Invention
The present invention relates generally to methods of preparing hybrid “organic-inorganic” chemical compositions that are wholly useful by themselves or in combination with other comonomers for producing novel polymeric compositions with desirable physical properties such as adhesion to polymeric, composite and metal surfaces, water repellency, low dielectric constant, resistance to abrasion and fire, biological compatibility, and optical quality plastics. The new compositions reported herein contain two primary material combinations.
Part one of the combination is a silicon component which may be comprised of a silane, silicone, silsesquioxane, polyhedral oligomeric silsesquioxane, silicate, polyhedral oligomeric silicate or combinations thereof. The silicon-component provides chemical oxidation resistance, thermal stability, and structural reinforcement to the overall molecule. The second component of the composition is one or more ring strained olefinic groups. The ring strained olefinic groups provide the primary reactive functionality for polymerization and for solubilization. The ring strained olefin may be comprised in whole or part from primarily olefinic carbon-based rings (e.g. cyclo-propyl, butenyl, pentenyl, hexenyl, norbornenyl). In some cases one or more hetero atoms such as N, O, S, P, B may also be included in the strained olefinic ring (e.g. ring strained cyclic olefinic imides or ethers).
2. Brief Description of the Prior Art
Prior art has demonstrated that strained olefinic rings can be utilized in polymerizations using free radical and UV initiators and transition metal based catalysts. See Haddad et al., J. Amer. Chem. Soc. Polym. Preprints Vol 38, No 1. 1997, pp 127-128, and Mather et. al. Macromolecules Vol 32, (1999), pp 1194-1203 (utility of POSS-polynorbornenes); G. Odian, Principles of Polymerization, 3rd Ed. John Wiley & Sons, (1991) p 578 (polynorbornenes and their utility). Prior art by Tenney et al in U.S. Pat. No. 5,190,808 described the use of silane-substituted monomers containing only one strained ring olefin, per silicon, for the preparation of prepregs for the construction of printed circuit boards. This art was limited in scope and conception and did not fulfill the need for the development of other silicon based strained ring olefin systems that could serve as crosslinkers and zero volatile organic comonomers or as resin systems for use in the manufacture of electronic, medical, sporting goods, aerospace and automotive components, packaging and personal care products. Prior art by Leibfried in U.S. Pat. No. 4,900,779 reported the process of using the hydrosilation of hydridosilanes and strained ring olefins for the purposes of forming crosslinked network materials having tailorable physical properties. Leibfried does not teach methods that allow for the preparation and isolation of silicone, silane, polyhedral oligomeric silsesquioxane or polyhedral oligomeric silicates that bear olefinic strained rings. Nor did they teach the use of such isolable intermediate species for subsequent utility in ROMP polymerizations. Leibfried was also silent as to the usage of silation as method of preparing such materials rather only a hydrosilation method was taught for the attachment of the strained olefinic group to the silane silicon atoms. Literature by Hambley et al. report the preparation of silsesquioxane materials bearing a norbornyl functionality for the purposes of steric bulk and solubility. They did not utilize a strained ring olefinic type of norbornene group and they did not teach the use of such a derivative for polymerization purposes. See Hambley, et al., Applied Organometallic Chemistry (1992) Vol 6 No. 3, pp 253-260.
It is an objective of this invention to teach the preparation of silicon-based monomers, oligomers, polymers and nanostructures that bear one and more strained ring olefinic functionalities per molecule. When such compositions exist as solids, waxes or oily liquids, they are particularly desirable as low and zero volatility monomers and resins. The viscosity and melting point of such systems can be controlled through the molecular weight, composition and tertiary structure of the molecules. Solid versions of these molecules can exist with crystalline or amorphous solid-state structures. Both forms (solid and liquid) can be utilized as nanoreinforcements and as fillers in thermoplastics and thermoset systems, while all systems bearing more than one strained ring olefin can be used as high temperature crosslinkers and curatives in rubber, silicones, imides, and other olefin based polymers. It is desirable to incorporate strained ring olefins onto silicone, silsesquioxane, polyhedral oligomeric silsesquioxane, silicate and polyhedral oligomeric silicate for the purposes of improving biocompatability, hardness, fire resistance, oxidation resistance, and mechanical durability.
This invention teaches two processes that enable the preparation of strained olefin bearing silanes, siloxanes, silsesquioxanes, polyhedral oligomeric silsesquioxane, silicates and polyhedral oligomeric silicate from readily available feedstocks. The preferred manufacturing processes employ the silation of siloxides (Si—OA, where A=H, alkaline or alkaline earth metals) with silane reagents bearing at least one reactive ring-strained cyclic olefin functionality [e.g.,
where y=1-2 and X=OH, Cl, Br, I, alkoxide OR, acetate OOCR, peroxide OOR, amine NR2, isocyanate NCO, and R]. Alternatively, the same or closely related products can be prepared through the hydrosilation reaction between silanes bearing at least one silicon-hydrogen bond (Si—H) with ring-strained cyclic olefin reagents [e.g., 5-vinyl, 2 norbornene
The processes can be effectively practiced using polymeric silsesquioxanes [RSiO1.5]∞ where ∞=1-1,000,000 or higher and which contain unreacted silanol or silane groups at chain terminus or branch points, on POSS nanostructures of formulas [(RSiO1.5)n]Σ#, homoleptic, [(RXSiO1.5)n]Σ#, functionalized homoleptic, [(RSiO1.5)m(R′SiO1.5)n]Σ#, heteroleptic, and [(RSiO1.5)m(RXSiO1.0)n]93#, functionalized heteroleptic nanostructures, or on silanes RSiX3, or on linear, cyclic, oligomeric and polymeric siloxanes (polymeric formula RX2Si—(OSiRX)m—OSiRX2 where m=0-1000, X=OH, Cl, Br, I, alkoxide OR, acetate OOCR, peroxide OOR, amine NR2, isocyanate NCO, and R).
The advantages of the present invention will become apparent to those skilled in the art after having read the following detailed description of the preferred embodiment which is illustrated in the several figures of the drawing.
For the purposes of understanding this invention's chemical compositions the following definition for formula representations of Polyhedral Oligomeric Silsesquoxane (POSS) and Polyhedral Oligomeric Silicate (POS) nanostructures is made.
Polysilsesquioxanes are materials represented by the formula [RSiO1.5]∞ where ∞=molar degree of polymerization and R=organic substituent (H, siloxy, cyclic or linear aliphatic or aromatic groups that may additionally contain reactive functionalities such as alcohols, esters, amines, ketones, olefins, ethers or halides). Polysilsesquioxanes may be either homoleptic or heteroleptic. Homoleptic systems contain only one type of R group while heteroleptic systems contain more than one type of R group.
POSS and POS nanostructure compositions are represented by the formula:
In all of the above R is the same as defined above and X includes but is not limited to OH, Cl, Br, I, alkoxide (OR), acetate (OOCR), peroxide (OOR), amine (NR2) isocyanate (NCO), and R. The symbols m and n refer to the stoichiometry of the composition. The symbol Σ indicates that the composition forms a nanostructure and the symbol # refers to the number of silicon atoms contained within the nanostructure. The value for # is usually the sum of m+n. It should be noted that Σ# is not to be confused as a multiplier for determining stoichiometry, as it merely describes the overall nanostructural characteristics of the system (aka cage size).
This invention teaches the use of two different chemical processes for the preparation of hybrid (organic-inorganic) silicon-based molecular systems which contain strained organic groups. The process depicted in
In cases where the hydrosilation process does not produce satisfactory product compositions or where the method cannot be applied due to the chemical nature of the starting materials, an alternate method of synthesis has been developed. The process in
Structural representations of specific telechelic compositions that are claimed and which can be prepared using the above procedures are shown in FIG. 4. These compositions are in no way limiting and are shown to illustrate the diversity and utility of the described processes.
Structural representations of specific POSS and POS compositions that are claimed and which can be prepared using the above procedures are shown in FIG. 5. These compositions are in no way limiting and are shown to illustrate the diversity and utility of the described processes. It should further be noted that size of the POSS or POS nanostructure is not a limiting factor nor does the odd or even number of silicon or heteroatoms contained within a nanostructure limit the claimed compositions or processes.
Structural representations of specific POSS, POS, and silsesquioxane resin compositions that are claimed and which can be prepared using the above procedures are shown in FIG. 6. These compositions are in no way limiting and are shown to illustrate the diversity and utility of the described processes. It should again be noted that size of the POSS or POS nanostructure is not a limiting factor nor does the odd or even number of silicon or heteroatoms contained within a nanostructure nor the number of strained olefinic groups that can be placed on such a nanostructure limit the claimed compositions or processes.
Methods for Curing Compositions.
All of the compositions can be chemically cured using vulcanizing agents such as organoperoxides, persulfides and sulfur. Examples include AIBN (2,2′-azobisisobutyronitrile), Lupersol™ peroxides, benzoyl peroxide etc. and these are effective in 1-50 wt % loadings with loadings of 5-25 wt % being preferred. Such agents will utilize the strained olefinic carbon-carbon double bond as a polymerization point to form inter and intramolecular chemical bonds to adjacent olefinic groups.
The compositions can also be cured using a number of metal-based catalysts such as molybdenum, tungsten, and ruthenium carbenes, halides, phosphates, acetates, and salts. Examples include WCl6, MoCl5, (Grubb's catalyst) bis(tricyclohexylphosphine)benzylidine ruthenium (IV), (Schrock's catalyst) 2,6-disopropylphenylimido neophylidenemolybdenum (VI) bis(hexafluoro-t-butoxide), (Feher's catalyst, see Feher et al. J. Am. Chem. Soc. 1994, 116, pp 2145-2146) ([Mo(CHC(CH3)2C6H5)(N(CH(CH3)2)2C6H4)(c-C6H11SiO1.5)7(c-C6H11((CH3)3SiO)SiO0.5)1]Σ7, and cocatalysts such as organoaluminum and aluminum halides, such as methyl, ethyl propylaluminumchlorides, bromides and iodides. The catalyst-cocatalysts mixtures utilize ring opening polymerization and ring opening metathesis polymerization to form inter and intramolecular chemical bonds to adjacent olefinic groups. The elimination of ring-strain is a powerful driver of such polymerizations therefore these catalysts are effective at the 0.01 to 1000 millimole per mole of olefin level with preferably loadings of 0.1 to 20 millimole per mol of olefin.
Additionally, the compositions can be cured by reacting them with a number of di and polyfunctional silanes in the presence of a hydrosilation catalyst such as palladium, and platinum halides, olefin complexes or carbon supported versions. Silanes include but are not limited to telechelic hydride terminated oligomers such as tetramethyldisiloxane disilane, polydimethylsiloxane, and nontelechelic hydride bearing systems such as polycarbosilanes, POSS-polysilanes and polysiloxanes. Examples of effective hydrosilation catalysts include Karstedt's catalyst, Speier's catalyst, and 5% palladium supported on carbon. Such catalysts effectively promote the oxidative addition of the silicon-hydride bond of the silane to the olefinic carbon-carbon double bond of the strained-ring olefin bearing compositions claimed herein. The elimination of ring-strain during the hydrosilation process is also a driver of such polymerizations.
All of the compositions described in this disclosure can be effectively cured using the above methods. Compositions containing two or more strained olefins are particularly effective at increasing the rate of gelation and the extent of cure that can be achieve using the above mentioned procedures. The above mentioned cure techniques can be carried out using common solvents such as hexane, toluene, dichloromethane or they can be conducted with out solvents at temperatures sufficient to achieve a molten state. Through compositional formulation with mono, di, tri and polyfunctionalized combinations of the claimed strained olefin bearing compositions, the physical properties, viscocities, and cure times for neat resin mixtures can be selectively tailored to meet individual needs. Cure times ranging from seconds to hours have been achieved.
General Process Variables Applicable to All Processes
As is typical with chemical processes, there are a number of variables that can be used to control the purity, selectivity, rate and mechanism of any process. Variables influencing the process for the conversion of polysilsesquioxanes [RSiO1.5]∞] into POSS structures [(RSiO1.5)n]Σ#, [(RSiO1.5)m(RSiO1.5)n]Σ#,[(RSiO1.5)m(RXSiO1.0)n]93 #, [(RSiO1.5)m(RSiO1.5)n(RXSiO1.0)p]Σ# include but are not be limited to the following: silicon-oxygen ring size, chemical class and composition type [RSiO1.5]∞ (silsesquioxane), [(RSiO1.5)n(R2SiO)n]Σ# (silsesquioxane-siloxane), [(RSiO1.5)m(XSiO1.5)n]Σ# (silsesquioxane-silicate), effect of the organic substituents, process temperature, process solvent, process temperature, stoichiometry and the presence of a catalyst.
Listed below are a series of example processes and compositions which in no way limit the invention. Numerous related compositions and variations to the processes are easily conceived by us and others skilled in the art.
1,4-Bis(ethylnorbornenyldimethylsilyl)benzene. Chloroplatinic acid (0.023 g, 0.044 mmol) was added to a mixture of 1,4-bis(dimethylsilyl)benzene (80 g, 411 mmol) and 5-vinylnorbornene (130 mL, 910 mmol) in toluene (525 mL) at room temperature with magnetic stirring. After about 1.5 h, the solution had become yellow and very hot. A water-cooled condenser was attached and the solution cooled in liquid for 5 min. The cooling bath was removed and the solution allowed to stir at room temperature overnight. After stirring overnight, the solvent was removed in vacuo from the reaction mixture with heating to give a viscous yellow liquid (166.2 g, 93%). Product is a mixture of endo/exo isomers. Data for major isomer is given. 1H NMR (500 MHz, CDCl3): δ 7.46 (s, 4H), 6.07 (dd, 2H), 5.84 (dd, 2H), 2.77 (s, 2H), 2.71 (s, 2H), 1.93 (m, 2H), 1.80 (m, 2H), 1.36 (m, 2H), 1.26 (s, 2H), 1.18 (d, 2H), 1.07 (overlapping multiplets, 4H), 0.73 (overlapping multiplets, 4H), 0.44 (m, 2H), 0.21 (s, 6H), 0.20 (s, 6H).
1,5-Bis(ethylnorbornenyl)-1,1,3,3,5,5-hexamethyltrisiloxane. 1,1,3,3,5,5-Hexamethyltrisiloxane (65.7 g, 315 mmol) in toluene (80 mL) was added dropwise over 1.33 h to a mixture of 5-vinylnorbornene (100 mL, 700 mmol) and Karstedt's catalyst (0.050 mL) in toluene (120 mL) at room temperature with magnetic stirring. After the addition had proceeded for about 30 min, the solution had become very hot and so was placed in an ice bath for the remainder of the addition. The addition funnel was rinsed with toluene (25 mL) and this was added to the reaction mixture. After 3 d at room temperature, the solvent was removed in vacuo from the reaction mixture with heating to give a clear, colorless liquid (134.9 g, 95%). Product is a mixture of endo/exo isomers. Data for major isomer is given. 1H NMR (500 MHz, CDCl3): δ 6.10 (dd, 2H), 5.90 (dd, 2H), 2.80 (s, 2H), 2.74 (s, 2H), 1.94 (m, 2H), 1.83 (m, 2H), 1.40 (m, 2H), 1.31 (m, 2H), 1.22 (d, 2H), 1.09 (overlapping multiplets, 4H), 0.52 (overlapping multiplets, 4H), 0.04 (s, 12H), 0.01 (s, 6H).
1,7-Bis(ethylnorbornenyl)-1,1,3,3,5,5,7,7-octamethyltetrasiloxane. 1,1,3,3,5,5,7,7-Octamethyltetrasiloxane (75.3 g, 267 mmol) in toluene (75 mL) was added dropwise over 1.87 h to a mixture of 5-vinylnorbornene (84 mL, 588 mmol) and Karstedt's catalyst (0.050 mL) in toluene (150 mL) at room temperature with magnetic stirring. The addition funnel was rinsed with toluene (25 mL) and this was added to the reaction mixture. After 2 d at room temperature, the solvent was removed in vacuo from the reaction mixture with heating to give a clear, colorless liquid (120.6 g, 87%). Product is a mixture of endo/exo isomers. Data for major isomer is given. 1H NMR (500 MHz, CDCl3): δ 6.10 (dd, 2H), 5.90 (dd, 2H), 2.80 (s, 2H), 2.74 (s, 2H), 1.94 (m, 2H), 1.83 (m, 2H), 1.40 (m, 2H), 1.31 (m, 2H), 1.22 (d, 2H), 1.08 (overlapping multiplets, 4H), 0.53 (overlapping multiplets, 4H), 0.05 (s, 12H), 0.04 (s, 12H).
1,3-Dicyclohexyl-1,1,3,3-tetrakis(ethylnorbornenyldimethylsilyl)disiloxane. Norbornenylethyldimethylchlorosilane (348 g, 1620 mmol) was added to 1,3-dicyclohexyltetrahydroxydisiloxane (100 g, 326 mmol) and triethylamine (250 mL) in chloroform (700 mL) at room temperature with magnetic stirring. After 4 d at room temperature, the reaction mixture was poured into water and the layers separated. The organic layer was washed with 1N HCl and water and stirred over MgSO4 and activated carbon. The mixture was filtered through Celite and the solvent was removed from the filtrate in vacuo with heating to give an orange, viscous liquid. Product is a mixture of endo/exo isomers. Data for major isomer is given. 1H NMR (500 MHz, CDCl3): δ 6.08 (dd, 4H), 5.87 (dd, 4H), 2.80 (s, 4H), 2.72 (s, 4H), 1.91 (m, 4H), 1.81 (m, 4H), 1.70 (br d, 10H), 1.37 (m, 4H), 1.25 (m, 4H), 1.20 (m, 10H), 1.06 (overlapping multiplets, 12H), 0.48 (overlapping multiplets, 10H), 0.04 (s, 24H). 13C NMR (CDCl)): δ 136.79, 132.15, 49.53, 44.98, 42.55, 42.33, 32.38, 27.81, 27.09, 26.93, 25.03, 17.31, 0.25, 0.18. 29Si NMR (CDCl)): δ 7.264, −69.730.
(2-Norbornenylethyldimethylsiloxy)-POSS: 2-Norbornenylethyldimethylchlorosilane (24.6 g, 0.114 mol, 1.05 eq) was added to a solution of Cp7T8(OH) (100 g, 0.109 mol) and triethylamine (33.1 g, 45.6 mL, 3 eq) in dry tetrahydrofuran (325 mL). The reaction was carried under an inert atmosphere in a three-necked, 2 L-roundbottom flask. Immediately upon addition of the chlorosilane, a precipitate of triethylamine hydrochloride formed. After stirring for 5 h an aliquot of the reaction mixture was removed and worked up as described below and analyzed by HPLC. After 5 h the reaction is essentially complete. The reaction mixture was transferred to a separatory funnel, the reaction flask rinsed with diethyl ether and the washings added to the contents of the separatory funnel. An additional 200 mL of diethyl ether was added to the flask and the organic phase washed with successive portions of 1N HCl and saturated NaCl solution. The organic THF/Ether phase was dried over MgSO4, filtered, and the concentrated by rotary evaporation. The resulting slurry was stirred with methanol and the solid collected by filtration to provide 105.9 g (89%) of Norbornenylethyldimethylsiloxy-POSS as a white powder. Because the starting 2-Norbornenylethyldimethylchlorosilane contains a mixture of exo and endo isomers, the Norbornenylethyldimethylsiloxy-POSS also contains a mixture of exo and endo isomers. Analysis by HPLC indicates product purity of greater that 99.3%. 1H NMR spectroscopy (major isomer 91%): 6.09 (1H dd, J=6 Hz, 3 Hz), 5.90 (1H dd, J=6 Hz, 3 Hz), 2.79 (br s, 1H), 2.73 (br s, 1H), 1.94 (m, 1H), 1.82 (m, 1H), 1.75 (m, 14H), 1.58-150 (m, 44H), 1.38 (m, 1H), 1.21 (d, 1H, J=8 Hz), 1.07 (m, 2H), 0.98 (m, 7H), 0.57 (m, 2H), 0.47 (m, 1H), 0.08 (s, 6H).
Tris(2-Norbornenylethyldimethylsiloxy)-POSS: 2-Norbornenylethyldimethylchlorosilane (73.6 g, 0.343 mol, 3.01 eq) was added to a heterogeneous solution of Cp7T7(OH)3 (100 g, 0.114 mol) and triethylamine (57.8 g, 79.6 mL, 0.571 mol 5 eq) in dry tetrahydrofuran (300 mL). The reaction was carried under an inert atmosphere in a three-necked, 2 L-roundbottom flask. Upon complete addition of the chlorosilane, the reaction mixture was stirred for 48 h. An aliquot of the reaction mixture was removed and worked up as described below. HPLC analysis of the aliquot indicated a single product. The reaction mixture was transferred to a separatory funnel, the reaction flask washed with diethyl ether and the washings added to the contents of the separatory funnel. An additional 200 mL of diethyl ether was added to the flask and the organic phase washed with successive portions of 1N HCl and saturated NaCl. The organic phase was dried over MgSO4, stirred with activated carbon, and the solvent removed by rotary evaporation. The resulting oil was stirred with MeOH, decanted and dried under vacuum at 70° C. to provide tris(2-Norbornenylethyldimethylsiloxy)-POSS as colorless viscous oil. Because the starting 2-Norbornenylethyldimethylchlorosilane contains a mixture of exo and endo isomers, the Tris(2-Norbornenylethyldimethylsiloxy)-POSS also contains a mixture of exo and endo isomers Analysis by HPLC indicates a single product. 1H NMR spectroscopy: 6.09 (3H dd, J=3 Hz, 6 Hz), 5.90 (3H dd, J=3 Hz, 6 Hz), 2.79 (br s, 3H), 2.73 (br s, 3H), 1.94 (m, 3H), 1.82-1.75 (overlapping multiplets, 17H), 1.58-1.38 (m, 46H), 1.21 (d, 3H), 1.06 (m, 6H), 0.86 (m, 7H), 0.62 (m, 6H), 0.47 (m, 3H), 0.08 (s, 18H).
(2-Norbornenylethyldimethylsiloxy)endodisilanol-POSS: A solution of 2-Norbornenylethyldimethylchlorosilane (24.5 g, 0.114 mol) in THF (40 mL) was added dropwise to a solution of Cp7T7(OH)3 (100 g, 0.114 mol) and triethylamine (57.8 g, 79.6 mL, 0.571 mol 5 eq) in dry tetrahydrofuran (700 mL). The Cp7T7(OH)3/triethylamine solution remained heterogeneous, as all of the Cp7T7(OH)3 would not dissolve. The addition of the 2-Norbornenylethyldimethylchlorosilane was carried out over a 12 h period. Afterwards an aliquot of the reaction mixture was withdrawn and worked up (as described below). HPLC analysis of the product indicated pure (2-Norbornenylethyldimethylsiloxy)endodisilanol-POSS. The reaction mixture was transferred to a seperatory funnel and Et2O (500 mL) added. The organic phase was washed with subsequent portions of 1N HCl (2×150 μL) and saturated brine (1×100 mL). The organic phase was dried over anhydrous MgSO4 and the solvent removed by rotary evaporation to provide (2-Norbornenylethyldimethylsiloxy)endodisilanol-POSS as a white solid. Analysis by HPLC indicates product purity of greater that 99%. 1H NMR spectroscopy (major isomer 91%): 6.09 (1H dd, J=6 Hz, 3 Hz), 5.90 (1H dd, J=6 Hz, 3 Hz), 4.18 and 4.17 (overlapping singlets, 2H), 2.79 (br s, 1H), 2.73 (br s, 1H), 1.97 (m, 1H), 1.82-1.75 (overlapping multiplets, 14H), 1.58-1.38 (m, 45H), 1.21 (d, 1H), 1.08-0.98 (overlapping multiplets, 10H), 0.62 (m, 2H), 0.47 (m, 1H), 0.120 and 0.116 (overlapping singlets, 6H).
1,3-(2-Norbornenylethyl)1,1,3,3-tetramethyldisiloxane: A solution of water (6.60 g, 0.367 mol, 1 eq) in tetrahydrofuran (60 mL) was added dropwise to a solution of 2-Norbornenylethyldimethylchlorosilane (150 g, 0.698 mol) and triethylamine (204 mL, 148 g 1.47 mol, 2.1 eq) in tetrahydrofuran (750 mL). A precipitate of triethylamine hydrochloride formed immediately upon addition of the aqueous tetrahydrofuran. The heterogeneous solution was stirred for 12 h, after which an aliquot of the reaction mixture was removed and worked up as described below. Thin layer chromatography (hexane elutant) indicated a single product. The triethylamine hydrochloride was removed by filtration, the filtrate transferred to a separatory funnel and diethyl ether (200 mL) added. The organic phase was washed with 1N HCl and saturated NaCl. The organic phase was dried over MgSO4, stirred with activated carbon and filtered. The organic solvent was removed by rotary evaporation to provide 1,3-(2-Norbornenylethyl)1,1,3,3-tetramehyldisiloxane as a pale yellow oil. The final product was purified by vacuum distillation to provide 92 g (70%) of 1,3-(2-Norbornenylethyl)1,1,3,3-tetramehyldisiloxane as a colorless oil. Analysis by 1H NMR spectroscopy (major isomer 91%): 6.11 (1H dd, J=6 Hz, 3 Hz), 5.90 (1H dd, J=6 Hz, 3 Hz), 2.80 (br s, 1H), 2.74 (br s, 1H), 1.94 (m, 1H), 1.84 (m, 1H), 1.39 (m, 1H) 1.22 (d, 1H J=8 Hz), 1.07 (m, 2H), 0.98 (m, 7H), 0.48 (m, 3H), 0.007 (s, 6H).
Preparation of (5-norbornene-2-ethyl)Methylsiloxy Octaisobutyl-POSS: An Et2O (5 mL) solution of {(i-BuSiO1.5)6(i-Bu(OH)SiO1.5)2}Σ8 (890 mg, 1.00 mmol) was added a mixture of Dichloromethyl(5-norbornene-2-ethyl)silane (endo/exo=3/1, 282.3 mg, 1.20 mmol), Et3N (195 μL, 1.4 mmol), and Et2O (5 mL) at −35° C. After addition the resulting mixture was warmed to room temperature and stirred for 20 h. The mixture was hydrolyzed and extracted with diethyl ether. The organic layer was washed with brine, dried over Na2SO4. The residue was passed through a silica gel column using hexane as an eluent. Evaporation of the volatiles gave pure product (720 mg, 0.68 mmol) as a white powder in 68% yield. 1H NMR (CDCl3) δ 0.10 (s, 9H), 0.12 (s, 3H), 0.48-0.68 (m, 72H), 0.84-1.05 (m, 194H), 1.06-1.3 (m, 18H), 1.40-1.50 (m, 4H), 1.80-1.94 (m, 32H), 1.95-2.03 (m, 3H), 2.55 (br s, 1H), 2.77 (br s, 3H), 2.78-2.83 (m, 4H), 5.93 (q, 3J=5 Hz, 3J=10 Hz, 3H), 6.04(q, 3J=5 Hz, 3J=10 Hz, 1H), 6.09-6.14 (m, 4H). 13C NMR (CDCl3) δ −1.11, 15.86, 16.21, 22.58, 23.20, 23.83, 23.98, 24.06, 24.18, 25.76, 25.81, 25.89, 27.71, 29.50, 32.41, 33.10, 41.89, 41.97, 42.09, 42.65, 45.10, 45.20, 46.03, 49.61, 132.35, 136.29, 136.87, 136.96. 29Si NMR (CDCl3) δ −69.25, −69.23, −69.21, −69.15, −67.04, −21.73, −21.63. Calcd for C42H88O13Si9.
Octanorbornenyl-POSS
Norbornenyltriethoxysilane (115 mmoles) reacted with tetraethylammonium hydroxide (115 mmoles) in methyl isobutyl ketone (288 mL) for 72 hours to give norbornenyl-T8 cage as a white solid (10.65 g, 63.9%). 1H NMR (500.2 MHz, CDCl3, 300K) δ 6.11 (br), 5.95 (br), 3.00 (br), 2.91 (br), 1.83 (br), 1.77 (br), 1.36 (br), 1.29 (br), 1.17 (br), 1.09 (br), 0.44 (m). 13C NMR (125.8 MHz, CDCl3, 300 K) δ 21.30, 21.32, 21.43, 26.43, 26.79, 26.81, 42.28, 42.30, 42.31, 42.41, 44.23, 46.93, 50.72, 133.78, 133.97, 135.73, 137.63. 29Si NMR (99.4 MHz, CDCl3, 300 K) δ −68.1, −67.8, −67.5, −67.2, −66.9, −66.7.
Octanorbornenylethyl-POSS
Norbornenylethyltriethoxysilane (115 mmoles) reacted with tetraethylammonium hydroxide (115 mmoles) in methyl isobutyl ketone (288 mL) for 72 hours to give OctanorbornenylethylPOSS cages as a white solid (10.65 g, 63.9%).
Although the present invention has been described in terms of specific embodiments, it is anticipated that alterations and modifications thereof will become apparent to those skilled in the art. It is therefore intended that the following claims be interpreted as covering all such alterations and modifications as fall within the true spirit and scope of the invention.
This application claims the benefit of Provisional Application No. 60/171,888, filed Dec. 23, 1999.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3390168 | Brown | Jun 1968 | A |
| 4381396 | Ryang | Apr 1983 | A |
| 4657965 | Watanabe et al. | Apr 1987 | A |
| 4900779 | Leibfried | Feb 1990 | A |
| 5008360 | Bard et al. | Apr 1991 | A |
| 5034490 | Jacobine et al. | Jul 1991 | A |
| 5190808 | Tenney et al. | Mar 1993 | A |
| 5194489 | Frances et al. | Mar 1993 | A |
| 5412053 | Lichtenhan et al. | May 1995 | A |
| 5484867 | Lichtenhan et al. | Jan 1996 | A |
| 5589562 | Lichtenhan et al. | Dec 1996 | A |
| 5939576 | Lichtenhan et al. | Aug 1999 | A |
| 5942638 | Lichtenhan et al. | Aug 1999 | A |
| 6075068 | Bissinger | Jun 2000 | A |
| Number | Date | Country | |
|---|---|---|---|
| 20040068075 A1 | Apr 2004 | US |
| Number | Date | Country | |
|---|---|---|---|
| 60171888 | Dec 1999 | US |