Patent Grant
9266980
The present invention relates to the manufacture of polyisobutylene by way of cationic polymerization, characterized by high velocity as well as elevated circulation rates and turbulence in a loop reactor operated with relatively high pressure drop across a recirculating pump. Unexpected improvement is seen in heat transfer, monomer conversion, catalyst utilization and product characteristics as discussed hereinafter.
Processes for cationically polymerizing olefins are known in the art. U.S. Pat. No. 6,858,690 to Webb et al. discloses a method of making butyl rubber wherein processing efficiency including heat transfer is improved by utilizing a tertiary halogen initiator. See, also, U.S. Pat. No. 3,932,371 to Powers which discloses polymerization of copolymers of isoolefins and conjugated dienes in a two-phase system where propane is used as a diluent in order to improve heat transfer.
The polymerization of olefins using Friedel-Crafts type catalysts, such as boron trifluoride and aluminum trichloride is well known. The degree of polymerization of the products obtained varies according to which of the various known polymerization techniques is used and also varies with the parameters used to control the reaction. The molecular weight of the polymeric product is directly related to the degree of polymerization and that the degree of polymerization may be manipulated by manipulating process parameters so as to produce a variety of products having respective desired average molecular weights. Due to the nature and mechanics of the olefinic polymerization process, a polyolefin product has a single double bond remaining in each molecule at the end of the polymerization process. The position of this remaining double bond is often an important feature of the product. For example, polyisobutylene (PIB) molecules wherein the remaining double bond is in a terminal (vinylidene) position are known to be more reactive than PIB molecules wherein the remaining double bond is internal, that is, not in a terminal position. A PIB product wherein most of the double bonds are in a terminal position may often be referred to as high vinylidene or reactive PIB. The extent to which a polyolefin product has terminal double bonds may also be manipulated by manipulation of process parameters.
It is also known that alpha olefins, particularly PIB, may be manufactured in at least two different classes of material—regular and high vinylidene. Conventionally, these two product grades have been made by different processes, but both often and commonly use a diluted feedstock in which the isobutylene concentration may range from 40 to as high as 90% by weight. Non-reactive hydrocarbons, such as isobutane, n-butane and/or other lower alkanes commonly present in petroleum fractions, may also be included in the feedstock as diluents. The feedstock often may also contain small quantities of other unsaturated hydrocarbons such as 1-butene and 2-butene.
High vinylidene, or highly reactive PIB, a relatively new product in the marketplace, is characterized by a large percentage of terminal double bonds, typically greater than 70% and preferentially greater than 80%. This provides a more reactive product, compared to regular PIB, and hence this product is also referred to as highly reactive PIB. The terms highly reactive (HR-PIB) and high vinylidene (HV-PIB) are synonymous. The basic processes for producing HR-PIB all include a reactor system, employing BF3 and/or modified BF3 catalysts, such that the reaction time can be closely controlled and the catalyst can be immediately neutralized once the desired product has been formed. Since formation of the terminal double bond is kinetically favored, short reactions times favor high vinylidene levels. The reaction is quenched, usually with an aqueous base solution, such as, for example, NH4OH, before significant isomerization to internal double bonds can take place. Molecular weights are relatively low. HR-PIB having an average molecular weight of about 950-1050 is the most common product. Conversions, based on isobutylene, are kept at 75-85%, since attempting to drive the reaction to higher conversions reduces the vinylidene content through isomerization. Prior U.S. Pat. No. 4,152,499 dated May 1, 1979, prior U.S. Pat. No. 4,605,808 dated Aug. 12, 1986, prior U.S. Pat. No. 5,068,490 dated Nov. 26, 1991, prior U.S. Pat. No. 5,191,044 dated Mar. 2, 1993, prior U.S. Pat. No. 5,286,823 dated Jun. 22, 1992, prior U.S. Pat. No. 5,408,018 dated Apr. 18, 1995 and prior U.S. Pat. No. 5,962,604 dated Oct. 5, 1999 are all directed to related subject matter.
Other than the HR grades and the regular grades of PIB, a certain grade of PIB known as the enhanced grade has been more recently developed (EP 1381637 and related patents discussed below). The advantage of these series of products is that the overall reactivity is high without the need for high vinylidene content.
The present invention is directed, in part, to controlling the reaction in a loop reactor by manipulating the tube velocity and recirculation rate of the process fluid. The invention is particularly concerned with polymerization of isobutylene and includes significant improvements to existing technology in terms of conversion, product attributes and so forth discussed in more detail below.
U.S. Pat. No. 6,844,400 shows an apparatus for polymerizing isobutylene wherein the recirculation rate is specified in the range of 20:1 to 50:1 and notes that higher recirculation ratios increase the degree of mixing, leading to narrower polymer distributions. Col. 9, lines 37-59. The '400 patent teaches to use two reactors in order to increase the conversion and to use lower flow rates to increase the residence time. Col. 11, line 57 to Col. 12, line 11. Related patents include U.S. Pat. Nos. 6,777,506 and 6,858,188. These patents all teach to increase residence time in order to increase conversion and lower polydispersity. See, also, U.S. Pat. No. 7,038,008 which discloses recirculation rates of 1000:1 to 1:1. See Col. 3, lines 55-64.
In U.S. Pat. No. 7,645,847 it is noted a Reynolds Number of at least 2000 is desirable in a tube and shell reactor for making isobutylene. Col. 8, lines 26-36, as well as a recirculation rate of from 20:1 to 50:1, Col. 5, lines 54-64. Single reactor conversion rates are disclosed at 51% in Table 6 for a residence time of 58 seconds. The '847 patent mentions:
The following patents describe mid-range vinylidene content polyisobutylene (PIB) polymers and processes for producing them: U.S. Pat. Nos. 7,037,099; 7,091,285; 7,056,990; and 7,498,396. The products are characterized in that at least about 90% of the PIB molecules present in the product comprise alpha or beta position isomers. The vinylidene (alpha) isomer content of the product may range from 20% to 70% thereof and the content of tetra-substituted internal double bonds is very low, preferably less than about 10% or 5% and ideally less than about 1-2%. The midrange vinylidene content PIB polymer products are prepared by a liquid phase polymerization process conducted in a loop reactor at a temperature of at least 60° F. using a BF3/methanol catalyst complex and a contact time of no more than 4 minutes. Otherwise, processing is similar to the other patents noted above.
Prior art systems are typically characterized by linear velocity in reactor tubes of less than 10 ft/sec as is seen in European Patent No. EP 1 242 464. Note particularly Table 4 where a linear velocity of 9.3 ft/sec is specified as well as Tables 6 and 8 where linear velocities of 6.59 ft/sec appear.
Despite numerous advances in the art, there is a need to provide more energy efficient and higher yield processes which provide superior material having lower polydispersity, even with higher molecular weight.
There is provided in one aspect of the invention a method of making a polyisobutylene polymer in a recirculating loop reactor with one or more reaction tubes in contact with a heat transfer medium comprising: (a) feeding isobutylene, catalyst and optionally other feed components to a residual reactor stream at a feed rate to form a reaction mixture; (b) recirculating the reaction mixture in the one or more reaction tubes of the loop reactor at a recirculation rate greater than the feed rate utilizing a recirculating pump operating at a pressure differential, delta P, corresponding to a recirculating flow; and (c) polymerizing the reaction mixture in the one or more tubes of the loop reactor to convert isobutylene to polyisobutylene polymer at a conversion rate expressed in %, w/w, while cooling the one or more tubes of the loop reactor with the heat transfer medium. During the process, a salient feature is (d) controlling the recirculation rate, the delta P and polymerization reaction of steps (b) and (c) to provide a linear velocity of the reaction mixture of at least 11 ft/sec in the one or more tubes of the loop reactor with the proviso that if the conversion of isobutylene is less than 55%, the recirculation rate, the delta P and the polymerization reaction of steps (b) and (c) are controlled to provide a linear velocity of the reaction mixture in the one or more reaction tubes of at least 13.5 ft/sec.
In another aspect, the pressure differential, delta P, of the recirculating pump is suitably from 35 psi to 70 psi and the process includes controlling the recirculation rate, pressure delta and polymerization reaction of steps (b) and (c) to provide a recirculation ratio of the recirculation rate to the feed rate of at least 30:1.
It was unexpectedly found that conversion increases with increased recirculation rates at the same residence time, contrary to the teachings of the prior art. In this regard, note
In connection with the inventive process, products produced have unexpectedly lower polydispersities especially at higher molecular weight, also contrary to the teachings of the prior art. This feature is particularly desirable when the products are used for making derivatives such as alkyl phenols and/or fuel or lubricating oil additives. Moreover, relatively low polydispersities can be maintained, even when less diluent is used. Note, for example, Table 4, where molecular weight increases, while polydispersity and alpha vinylidene content remain relatively constant as the pressure drop and velocity increase and the isobutene diluent level is reduced from 10 wt. % to about 3.5 wt. %. A low diluent process uses less material and is very desirable from an economic perspective as well as an environmental perspective, since solvent does not need to be recycled or disposed of Reducing diluents levels while maintaining desired product attributes is enabled by employing high velocity in accordance with the invention.
A still further unexpected result is that alpha content does not decrease with increasing conversion. The prior art also teaches away in this regard.
Conventional boron trifluoride catalyst systems reported in the patent literature typically produce somewhat less than 900 lbs PIB/lb of BF3 and typically less than 450 lbs PIB/lb of BF3. Much higher production by catalyst is seen in accordance with the present invention; typically from 2 to 4 times more production per pound of BF3 as discussed hereinafter in connection with the following U.S. Pat. Nos. 7,485,764; 7,217,773; and 7,038,008. Catalyst usage decreases substantially as the linear velocity of the reaction mixture is increased as is seen in
Still further features and advantages of the invention will become apparent from the discussion which follows.
The invention is described in detail below with reference to the various Figures, wherein:
The invention is described in detail below with reference to several embodiments and numerous examples. Such discussion is for purposes of illustration only. Modifications to examples within the spirit and scope of the present invention, set forth in the appended claims, will be readily apparent to one of skill in the art. Terminology used throughout the specification and claims herein is given its ordinary meaning, for example, psi refers to pressure in lbs/inch and so forth. Terminology is further defined below.
The improved process of the present invention features the use of a Friedel-Crafts catalyst which is complexed with a complexing agent. Many useful Friedel-Crafts catalysts are known to those of ordinary skill in the related art field. In particular, many useful catalysts are described in the patents referenced above. Useful Friedel-Crafts catalysts include, for example, BF3, AlCl3, TiCl4, BCl3, SnCl4 and FeCl3 and the like. The complexing agent for the catalyst, and in particular for the BF3 catalyst, may be any compound containing a lone pair of electrons, such as, for example, an alcohol, an ester or an amine. For purposes of the present invention, however, the complexing agent may be an alcohol, desirably a primary alcohol, preferably a C1-C8 primary alcohol (such as, for example, methanol, ethanol, propanol, isopropanol, hexyl alcohol and the like) and ideally methanol. The molar ratio of BF3 to complexing agent in the catalyst composition is generally in the range of from approximately 0.5:1 to approximately 5:1 respectively, desirably within the range of from approximately 0.5:1 to approximately 2:1, and preferably within the range of from approximately 0.5:1 to approximately 1:1. Ideally, the catalyst composition may simply be a 1:1 complex of BF3 and methanol as is seen in the examples. For purposes of convenience, “catalyst” refers to a Friedel-Crafts catalyst of the class described above, while “catalyst complex” refers to the Friedel-Crafts catalyst and complexing agent up to a 1:1 molar ratio. When complexing agent is used in a molar excess with respect to the Friedel-Crafts catalyst it is referred to herein as modifier.
“Catalyst complex turnover number” and like terminology refers to the weight of polymer produced per unit weight of catalyst complex employed in the process.
“Consisting essentially of” and like terminology refers to the recited components and excludes other ingredients which would substantially change the basic and novel characteristics of the mixture or composition. Unless otherwise indicated or readily apparent, a composition or mixture consists essentially of the recited components when the composition or mixture includes 95% or more by weight of the recited components. That is, the terminology excludes more than 5% unrecited components.
Conversion of the reaction mixture to polymer is expressed in weight percent and calculated as the weight of polymer produced less the weight of isobutylene fed to the reaction system divided by the weight of isobutylene fed to the reaction system times 100%.
Polyisobutylene, “PIB” and like terminology refers to polymers made up of repeat units derived from isobutene, also referred to as isobutylene.
Such polymers are derived from feedstocks made up of purified isobutenes and hydrocarbon diluents, from isobutene concentrate, dehydro effluent, or from raffinate streams. The PIB polymer consists essentially of repeat units derived from isobutylene, but may contain minor amounts of material derived from 1-butenes, butadiene or other C4 olefins, 2-butenes (cis and/or trans) depending on the feedstock composition. Typically, the polymer is more than 99% by weight derived from isobutylene monomer. Particular compositions of interest in connection with the present invention have a number average molecular weight of from 500 to 4000 Daltons and in preferred embodiments significant amounts of alpha vinylidene terminated molecules:
Highly reactive (HR) PIB polymer compositions typically include more than 80 mole % alpha molecules, while mid-range vinylidene content PIB products contain less alpha and more beta olefin isomers (1,1,2-trisubstituted or 1,2,2-trisubstituted cis or trans isomer):
Other structures which may be present include tetrasubsituted structures, other trisubstituted structures with a double bond in the internal gamma position, structures with other internal double bonds and aliphatic structures, for example:
When calculating endgroup percentages, all PIB molecules found in the PIB compositions having a significant presence (more than half a percent or so) are included in endgroup calculations. The endgroup content is determined by nuclear magnetic resonance 13C NMR as is well known in the art.
Suitable feedstocks include purified isobutenes with or without hydrocarbon diluents such as isobutane, hexane and so forth. Purified isobutene is readily available in bulk with purity levels of more than 95% by weight, for example 98.5%+by weight or 99.5% by weight in some cases. The purified isobutene may be fed with diluents as seen in the examples herein. Other suitable feedstocks include isobutene concentrate, dehydro effluent, or raffinate having typical compositions noted in Tables 1-3 below.
One of skill in the art will appreciate that the feedstock may need to be purified to remove water and oxygenates such as alcohols, ethers and so forth to avoid adverse effects on the catalyst. Typical media for removal of impurities from hydrocarbon feed streams use molecular sieves, activated alumina and other hybrid adsorbents. A suitable absorbent to reduce water and oxygenate levels to desired limits is UOP AZ 300 (Des Plaines, Ill., USA). Post treatment, prior to feeding to the reactor, the feed stream preferably has less than 3 ppm of oxygenates and less than 1 ppm of water.
A mid-range vinylidene polymer composition refers to a PIB wherein a first portion of the PIB molecules have alpha position double bonds and a second portion of the molecules have beta position double bonds, wherein said first and second portions together include at least 80 mole % of the PIB molecules of the composition, wherein said first portion includes less than 75 mole % of the PIB molecules of the composition, and wherein no more than 10 mole % of the PIB molecules of the composition have tetra-substituted double bonds, the first and second portions together includes at least 85 mole % of the PIB molecules of the composition and preferably the said first and second portions together include at least 90 mole % of the PIB molecules of the compositions. Typically, the first portion includes less than 72.5 mole % of the PIB molecules of the composition and sometimes less than 70 mole % of the PIB molecules of the composition. In preferred cases, no more than 5 mole % of the PIB molecules of the composition have tetra-substituted double bonds.
“Highly reactive PIB” and like terminology means polyisobutylene polymers with more than 80 mole percent alpha vinylidene terminated molecules.
Kinematic viscosity of the PIB products of the invention is expressed in Cst @100° C. and is preferably measured in accordance with Test Method ASTM D 445.
Molecular weight herein is typically reported as number average molecular weight, in Daltons, and is measured by gel permeation chromatography (GPC). GPC measurements reported herein were carried out using a Viscotek GPCmax® instrument (Malvern instruments, Worcestershire, UK) employing a 3-column set-up (5 μm (particle size) 100 Angstrom (pore size), 5 μm 500 Angstrom, 5 μm 104 Angstrom) and a Refractive Index (RI) detector. Polyisobutylene standards were used to construct the calibration curve.
Polydispersity or PDI is defined as the ratio of the weight average molecular weight divided by the number average molecular weight of the polymer.
“Linear velocity” refers to the velocity of the recirculating reaction mixture in the tubes of the loop reactor and is calculated by dividing the volumetric flow rate of the reaction fluid by the cross-sectional area of the reaction tubes.
Recirculation ratio is calculated as the weight ratio of the reaction mixture recirculated to the feed added to the residual reactor stream.
Residence time is calculated as the volume of the reactor divided by the volumetric feed rate.
Any standard test method referred to herein is the version in effect as of Jan. 1, 2011.
With the process of the invention, there are seen dramatic increases in conversion and improved product quality. Without being bound by any particular theory, it is believed that improved heat transfer and mixing, in part, provide the benefits observed. The heat transfer coefficient of the process fluid was increased by increasing the pressure differential across a recirculating pump thereby increasing the velocity of the process fluid in the reactor tubes, likely decreasing the amount of relatively immobile material adjacent the reactor walls. In other words, by increasing the degree of turbulence of the tube side process fluid, the effect of undesirable boundary layer heat and mass transfer phenomena are reduced. The heat transfer is related to the Nusselt number of a fluid. Further, equations such as the Sieder Tate equations (for turbulent flow) provide a way to calculate the Nusselt number. These correlations relate the Nusselt number to the Reynolds number (ratio of inertial to viscous forces) and the Prandtl number (ratio of viscous diffusion to thermal diffusion). A potential problem faced in loop reactors is that there may be an increase in the viscosity of the tube side fluid at the heat transfer surface. This leads to a substantially lower internal heat transfer coefficient and a loss in conversion and productivity. It is seen in the examples which follow that the heat transfer coefficient increases dramatically and unexpectedly as the velocity in the tubes is increased above conventional levels.
Operation of the inventive process with a two-pass loop reactor is illustrated and described in connection in
Reactor 12 includes a feed chamber 24, a plurality of tubes indicated at 26 for upward flow, a plurality of tubes indicated at 28 for downward flow, as well as an upper plenum 30 and a receiving chamber 32 for circulated material. Reactor 12 is conventional in design and known in the art as a 1-2 shell and tube heat exchanger (1 shell, 2 pass). The reactor is suitably provided with 1164 tubes with tube outer diameter of 0.375″ and a wall thickness of 0.035″. The tubes are surrounded by a shell indicated at 34, 36 for circulating chilled coolant since the polymerization reaction is highly exothermic.
In operation, isobutylene feedstock is fed to a residual reactor stream 38 via a feed line 40 to form a reaction mixture which is optionally provided with catalyst modifier, typically methanol, at an injection point at 42 just upstream of pump 14. Pump 14 operates at a pressure differential, delta P, indicated in
Variable speed drive 18 contacts motor 16 which drives pump 14 at a pressure differential, delta P, across the pump which, in turn, corresponds to a recirculating flow rate in the reactor for a reaction mixture. The flow characteristics of the reaction mixture are also influenced by temperature in the reactor, molecular weight, monomer and diluent content and so forth as is readily appreciated by one of skill in the art. The flow characteristics of the reaction mixture are thus controlled by feed and catalyst rates, conversion of monomer, mixture composition and the temperatures in the reactor as is seen in the examples which follow. For a given mixture, feed rates and temperature, recirculation rates and hence velocity of the reaction mixture in the tubes of the reactor is most conveniently controlled by controlling the speed of pump 14 to provide a pressure differential, delta P (DP in the diagram), across the pump.
The pump circulates the reaction mixture to feed chamber 24 where the mixture is fed to a plurality of upwardly directed tubes indicated at 26 where it flows to plenum 30 before being transferred to a plurality of downwardly directed tubes indicated at 28 where it flows to receiving chamber 32. A polymerized product is withdrawn at 22 through a pressure relief valve indicated at 46. Residual reactor stream 38 remains in the system and feed line 40 provides fresh monomer to the residual stream as discussed above. Reactor 12 is operated under pressure sufficient to maintain the reaction mixture and its components in liquid form at reaction temperatures, suitably in the range of from about 40° F. to about 90° F. Further details relating to the operation of reactor 12 are provided in European Patent 1 242 464, the disclosure of which is incorporated by reference.
Typically, the inventive process is operated wherein the recirculation rate is much higher than the feed rate as seen in the examples which follow. Coolant in the shell side of the reactor indicated at 34, 36, 48, 50 removes the heat of reaction. Any suitable coolant may be used, for example a 50:50 w/w mixture of water and methanol may be chilled and circulated in the shell section(s) to control reactor temperature.
Utilizing the procedure and materials described above, a 1-2 tube and shell reactor was operated to produce PIB using purified isobutylene diluted with isobutane and a BF3/methanol catalyst and modifier system. Details and results appear in Tables 4-9. In Tables 4-9, “catalyst complex” refers to a 1:1 w/w mixture of BF3/methanol. In these tables, the heat transfer coefficient, Q, is calculated from the log mean temperature difference as described immediately below and in connection with Equations (1)-(6) of
The heat transferred (Q) may be calculated either using shell-side (chilling fluid) or tube side (process fluid) data by Equation (1).
Q (BTU/hr) was calculated using tube reaction side data.
The terms in Equation (1) are as follows:
{dot over (m)}=mass flow rate of shell side fluid (methanol-water);
cp=specific heat of the shell side (cooling) fluid;
t1=chiller temperature inlet;
t2=chiller temperature outlet;
{dot over (M)}=mass flow rate of tube side fluid (process fluid)
Cp=specific heat of the tube side fluid (process fluid)
T1=inlet temp of (reactor) process fluid;
T2=outlet temperature of (reactor) process fluid;
The Fourier Equation for heat transfer relates the overall heat transfer co-efficient; ‘U’ to the amount of heat transfer (Q). For a 1-2 heat exchanger (1 shell and 2 tube passes), the equation can be written in the form of Equation (2) and Equation (3). (Process heat transfer, D. Q. Kern, McGraw Hill, 1950, pg 144).
Δt of Equation (3) is also known as the log mean temperature difference (LMTD);
A=Area available for heat exchange
In Equation (4), Ft=fractional ratio of the true temperature difference to the LMTD.
For satisfactory operation of 1-2 heat exchangers, the value of Ft is generally desired to be greater than 0.75 (Process heat transfer, D. Q. Kern, McGraw Hill, 1950, pg 145). Ft can be calculated by Equations (4) and (5) or through figures relating the values of the dimensionless parameters R and S to Ft (FIG. 18, pg 828, Kern, D. Q.).
R and S values for Equation 4 have been calculated in the Tables. Ft has been calculated from the R and S values.
The overall ‘U’ can be recalculated by rearranging equation (2) into the form shown in Equation (6).
The overall U as shown in equation (6) also appears in Tables 4-7.
The various features and advantages of the invention are readily apparent from Tables 4-7 and the appended Figures. Table 4 provides results for high vinylidene, HR PIB having a number average molecular weight of about 1000. It is seen in
Like results are seen with higher molecular weight HR PIB as linear velocity increases in the reaction system. At residence times of 3.5 minutes, conversion increases from 50 to nearly 60 weight percent (
Like results are also seen with mid-range vinylidene products produced as described in Tables 6, 7. Conversion rates increase dramatically as pressure differential and linear velocity increase (
Catalyst productivity (efficiency) is unexpectedly improved as compared to prior art systems. In Table 8, the process of the invention is compared with prior art reaction systems. Details as to calculation are summarized in Table 9. Catalyst productivity ranges from about 650 lbs polymer/lb catalyst complex up to about 2000 lbs polymer/lb catalyst complex with the process of the invention versus from about 150 lbs polymer/lb catalyst complex to about 300 lbs polymer/lb catalyst complex as reported in the prior art. When calculated based on BF3 only, similar increases in productivity are provided.
From the foregoing, it will be appreciated that conversion unexpectedly increases with increased recirculation rates at the same residence time, contrary to the teachings of the prior art. Higher yield is realized without significant additional capital or processing costs. It was also found that polydispersity decreases with substantially the same residence time as circulation rates increase all other things being equal. Also with the inventive process, products produced have unexpectedly lower polydispersities especially at higher molecular weight, also contrary to the teachings of the prior art. This feature is particularly desirable when the products are used for making derivatives such as alkyl phenols and/or fuel or lubricating oil additives.
A particularly useful unexpected result is that alpha content does not decrease with increasing conversion when a high velocity system is used to make the product.
The invention is further defined in the appended claims. Still further embodiments of the present invention include: a method of making a polyisobutylene polymer in a recirculating loop reactor with one or more reaction tubes in contact with a heat transfer medium comprising: (a) feeding isobutylene, catalyst and optionally other feed components to a residual reactor stream at a feed rate to form a reaction mixture; (b) recirculating the reaction mixture in the one or more reaction tubes of the loop reactor at a recirculation rate utilizing a recirculating pump operating at a pressure differential, delta P, of from 35 psi to 70 psi; (c) polymerizing the reaction mixture in the one or more tubes of the loop reactor to convert isobutylene to polyisobutylene polymer at a conversion rate expressed in %, w/w, while cooling the one or more tubes of the loop reactor with the heat transfer medium; (d) controlling the recirculation rate, the delta P and polymerization reaction of steps (b) and (c) to provide a recirculation ratio of the recirculation rate to the feed rate of at least 30:1; and (e) withdrawing polyisobutylene polymer from the loop reactor.
In any practice of the present invention, the conversion of isobutylene to polymer is from 50% to 80%, suitably wherein the conversion of isobutylene to polymer is at least 55%, least 60%, at least 65%, at least 70% or at least 75. Likewise in any embodiment, the delta P of the recirculating pump is typically at least 40 psi, suitably at least 45 psi, preferably in some cases the delta P of the recirculating pump is at least 50 psi or at least 55 psi.
The inventive process in any particular application may be operated at a recirculation ratio of from 30:1 to 50:1 such as at a recirculation ratio of at least 35:1, or at least 37.5:1, or at least 40:1 or operated at a recirculation ratio of at least 45:1.
A still further embodiment includes a method of making a polyisobutylene polymer in a recirculating loop reactor with one or more reaction tubes in contact with a heat transfer medium comprising: (a) feeding isobutylene, catalyst and optionally other feed components to a residual reactor stream at a feed rate to form a reaction mixture; (b) recirculating the reaction mixture in the one or more reaction tubes of the loop reactor at a recirculation rate greater than the feed rate utilizing a recirculating pump operating at a pressure differential, delta P, of from 35 psi to 70 psi; (c) polymerizing the reaction mixture in the one or more tubes of the loop reactor to convert isobutylene to polyisobutylene polymer at a conversion rate expressed in %, w/w, while cooling the one or more tubes of the loop reactor with the heat transfer medium; (d) controlling the recirculation rate, the delta P and polymerization reaction of steps (b) and (c) to provide a linear velocity of the reaction mixture of at least 11 ft/sec in the one or more tubes of the loop reactor with the proviso that if the conversion of isobutylene is less than 55%, the recirculation rate, the delta P and the polymerization reaction of steps (b) and (c) are controlled to provide a linear velocity of the reaction mixture in the one or more reaction tubes of at least 13.5 ft/sec; and (e) withdrawing polyisobutylene polymer from the loop reactor.
Still yet another embodiment of the present invention includes a method of making a polyisobutylene polymer in a recirculating loop reactor with one or more reaction tubes in contact with a heat transfer medium comprising: (a) feeding isobutylene, catalyst and optionally other feed components to a residual reactor stream at a feed rate to form a reaction mixture; (b) recirculating the reaction mixture in the one or more reaction tubes of the loop reactor at a recirculation rate greater than the feed rate utilizing a recirculating pump operating at a pressure differential, delta P, of from 35 psi to 70 psi; (c) polymerizing the reaction mixture in the one or more tubes of the loop reactor to convert isobutylene to polyisobutylene polymer at a conversion rate expressed in %, w/w, while cooling the one or more tubes of the loop reactor with the heat transfer medium; (d) controlling the recirculation rate, the delta P and polymerization reaction of steps (b) and (c) to provide a linear velocity of the reaction mixture of at least 11 ft/sec in the one or more tubes of the loop reactor with the proviso that if the conversion of isobutylene is less than 55%, the recirculation rate, the delta P and the polymerization reaction of steps (b) and (c) are controlled to provide a linear velocity of the reaction mixture in the one or more reaction tubes of at least 13.5 ft/sec and wherein further, there is provided a recirculation ratio of the recirculation rate to the feed rate of at least 30:1; and (e) withdrawing polyisobutylene polymer from the loop reactor.
In any particular embodiment of the invention, the process may be operated continuously at a residence time of from 1 to 10 minutes, typically operated continuously at a residence time of from 2 to 8 minutes and in many cases preferably operated continuously at a residence time of from 3 to 6 minutes.
While the invention has been described in detail, modifications within the spirit and scope of the invention will be readily apparent to those of skill in the art. In view of the foregoing discussion, relevant knowledge in the art and references discussed above in connection with the Background and Detailed Description, the disclosures of which are all incorporated herein by reference, further description is deemed unnecessary. In addition, it should be understood that aspects of the invention and portions of various embodiments may be combined or interchanged either in whole or in part. Furthermore, those of ordinary skill in the art will appreciate that the foregoing description is by way of example only, and is not intended to limit the invention.
This application is a continuation application based on U.S. patent application Ser. No. 14/346,367 of the same title filed Mar. 21, 2014 now U.S. Pat. No. 8,946,361. Application Ser. No. 14/346,367 was based on Application No. PCT/US 2012/059464 filed Oct. 10, 2012 which was based upon U.S. Provisional Application Ser. No. 61/551,526, filed Oct. 26, 2011, also of the same title. The priorities of application Ser. No. 14/346,367, application No. PCT/US 2012/059464 and Provisional Application Ser. No. 61/551,526 are hereby claimed and their disclosures incorporated by reference into this application in their entirety.
| Number | Name | Date | Kind |
|---|---|---|---|
| 3932371 | Powers | Jan 1976 | A |
| 4152499 | Boerzel et al. | May 1979 | A |
| 4605808 | Samson | Aug 1986 | A |
| 5068490 | Eaton | Nov 1991 | A |
| 5191044 | Rath et al. | Mar 1993 | A |
| 5286823 | Rath | Feb 1994 | A |
| 5408018 | Rath | Apr 1995 | A |
| 5962604 | Rath | Oct 1999 | A |
| 6525149 | Baxter, Jr. et al. | Feb 2003 | B1 |
| 6562913 | Baxter, Jr. et al. | May 2003 | B1 |
| 6683138 | Baxter, Jr. et al. | Jan 2004 | B2 |
| 6777506 | Baxter, Jr. et al. | Aug 2004 | B1 |
| 6844400 | Baxter, Jr. et al. | Jan 2005 | B2 |
| 6858188 | Baxter, Jr. et al. | Feb 2005 | B2 |
| 6858690 | Webb et al. | Feb 2005 | B2 |
| 6884858 | Baxter, Jr. et al. | Apr 2005 | B2 |
| 6992152 | Lobue et al. | Jan 2006 | B2 |
| 7037099 | Linke et al. | May 2006 | B2 |
| 7038008 | Wettling et al. | May 2006 | B2 |
| 7056990 | Baxter, Jr. et al. | Jun 2006 | B2 |
| 7091285 | Baxter, Jr. et al. | Aug 2006 | B2 |
| 7217773 | Rath et al. | May 2007 | B2 |
| 7485764 | Rath et al. | Feb 2009 | B2 |
| 7498396 | Baxter, Jr. et al. | Mar 2009 | B2 |
| 7645847 | Baxter, Jr. et al. | Jan 2010 | B2 |
| 8946361 | Shaikh et al. | Feb 2015 | B2 |
| 20030096924 | Baxter et al. | May 2003 | A1 |
| 20140256891 | Shaikh | Sep 2014 | A1 |
| Number | Date | Country |
|---|---|---|
| 1242464 | Apr 2011 | EP |
| Number | Date | Country | |
|---|---|---|---|
| 20150197584 A1 | Jul 2015 | US |
| Number | Date | Country | |
|---|---|---|---|
| 61551526 | Oct 2011 | US |
| Number | Date | Country | |
|---|---|---|---|
| Parent | 14346367 | US | |
| Child | 14565577 | US |