Polyisobutylene production process with improved efficiencies and/or for forming products having improved characteristics and polyisobutylene products produced thereby

Information

  • Patent Grant
  • 9809665
  • Patent Number
    9,809,665
  • Date Filed
    Tuesday, March 8, 2011
    13 years ago
  • Date Issued
    Tuesday, November 7, 2017
    6 years ago
Abstract
A process for production of polyisobutylene includes subjecting a reaction admixture comprising isobutylene, a diluent for the isobutylene, which may be isobutane, and a catalyst composition, that may include a BF3/methanol catalyst complex, to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules. At least a fraction of the polyisobutylene molecules thus produced have alpha position double bonds and the polyisobutylene product has a number average molecular weight (MN) and a polydispersity index (PDI). The concentration of the diluent in the reaction admixture may be manipulated to control or change any one or more of (a) the relative size of the fraction, (b) the number average molecular weight of the product, (c) the polydispersity index of the product and (d) the relative size of the portion. The diluent concentration may be held constant to maintain any one or more of such characteristics constant.
Description
FIELD OF THE INVENTION

The invention described hereinafter relates to improvements in the polymerization of isobutylene. In particular, the invention relates to processes for preparing polyisobutylene (PIB) products having improved characteristics. More particularly, the invention relates to techniques for manipulation and control of liquid phase processes for producing polyisobutylene, polyisobutylene products having pre-selected characteristics, and methodology which enhances the operation and control of polyisobutylene reactors.


BACKGROUND OF THE INVENTION

U.S. Pat. No. 6,562,913 issued on May 13, 2003 and entitled “Process for Producing High Vinylidene Polyisobutylene” (hereinafter the '913 patent) relates, inter alia, to liquid phase polymerization processes for preparing low molecular weight (number average molecular weight (MN) less than about 10,000), highly reactive (terminal double bond content of at least about 70%) polyisobutylene products. In accordance with the disclosure of the '913 patent, a catalyst composition, which desirably may comprise a complex of BF3 and complexing agent such as methanol, and a feedstock containing isobutylene, are each introduced into a reaction zone where the same are intimately admixed with residual reaction mixture so as to present an intimately intermixed reaction admixture in the reaction zone. The intimately intermixed reaction admixture is maintained in its intimately intermixed condition and at a relatively constant temperature of at least about 0° C. while the same is in the reaction zone, whereby isobutylene therein is polymerized to form a polyisobutylene product having a high degree of terminal (vinylidene) unsaturation. A crude product stream comprising residual catalyst composition, unreacted isobutylene and polyisobutylene is then withdrawn from the reaction zone.


The introduction of feedstock into and the withdrawal of product stream from the reaction zone are each controlled such that the residence time of the isobutylene undergoing polymerization in the reaction zone is no greater than about 4 minutes, whereby the product stream contains a highly reactive polyisobutylene product. Preferably, the reaction zone may be the tube side of a shell-and-tube exchanger in which a coolant is circulated on the shell side. A recirculation loop may desirably be employed to circulate the reaction admixture through the tube side reaction zone at a linear velocity sufficient to establish and maintain an intimately intermixed condition in the admixture and remove heat generated by the exothermic polymerization reaction.


U.S. Pat. No. 7,037,999 issued on May 2, 2006 and entitled “Mid-Range Vinylidene Content Polyisobutylene Polymer Product and Process for Producing the Same” (hereinafter the '999 patent) describes, inter alia, mid-range vinylidene content PIB polymer products and processes for making the same. In accordance with the disclosure of the '999 patent, at least about 90% of the PIB molecules present in the product are polyisobutylene isomers having either alpha or beta position double bonds. The alpha (or terminal) position double bond (vinylidene) isomer content of the product may range from 20% to 70% thereof, and the content of tetra-substituted internal double bonds is very low, preferably less than about 5% and ideally less than about 1-2%. The mid-range vinylidene content PIB polymer products are desirably prepared by a liquid phase polymerization process conducted in a loop reactor similar to the reactors described in the '913 patent at a temperature which desirably may be about 60° F. or higher using a BF3/methanol catalyst complex and a contact time of no more than about 4 minutes.


U.S. Pat. No. 6,992,152 issued on Jan. 31, 2006 and entitled “Apparatus and Method for Controlling Olefin Polymerization process” (hereinafter the '152 patent) relates, inter alia, to methodology for controlling the operation of reactors such as those described in the '999 and '913 patents so as to achieve efficiencies in process operation and better uniformity of the product of the process. In particular, the '152 patent describes methodology for controlling the ratio of BF3 to catalyst composition to thereby control the reactivity (terminal double bond content) of the product. Specifically, such control is achieved by providing for introduction of a catalyst modifier separately from the introduction of the catalyst composition itself.


U.S. Pat. No. 6,844,401 issued on Jan. 18, 2005 and entitled “Apparatus for Preparing Polyolefin Products and Methodology for Using the Same” (hereinafter the '401 patent) relates, inter alia, to procedures, etc. for improving the processes described above. In particular, the '401 patent describes an olefin reactor system that includes at least two separate reactor zones operating in parallel. Such multiple reactor system provides process efficiencies and advantages particularly in connection with conversion rates and polymer polydispersity. In addition, the '401 patent describes downstream systems for quenching the residual catalyst leaving with the crude product to quickly prevent further reaction, for removal of catalyst residues by washing, and for separation of the product from unreacted monomer, dimers, oligomers and other undesirable contaminants such as diluents and the like.


In accordance with certain of the preferred embodiments of the '913, '999, '152 and '401 patents, polyisobutylene products may be manufactured by processes comprising liquid phase polymerization conducted in a loop reactor at a temperature ranging from 30 to 90° F. The preferred catalyst may be a BF3/methanol catalyst complex and the reactor residence time may usually be no more than about 4 minutes. One of the preferred products may be a relatively low molecular weight, mid-range (50-60%) alpha position (vinylidene) double bond content PIB polymer. At least about 90% of the PIB molecules present in the product are either alpha position (vinylidene) double bond or beta position double bond isomers. The other polyisobutylene isomers produced generally may comprise less than 10% and ideally less than 5% of the molecules.


Table 1 set forth below shows possible isomer structures that might be found in low molecular weight polyisobutylene products. Other isomers may possibly be included in minor amounts and should not affect the overall reactivity of the PIB molecule.


In general, the reactivity of an olefinic double bond is directly related to its degree of substitution. That is to say, the more highly substituted the olefinic double bond, the less reactive it is. Therefore, since Structure I (alpha position or vinylidene double bond) of Table 1 is only disubstituted, it is much more reactive than Structures II, III or IV where the double bond is in a beta position. Structures II and III are both 1,2,2 trisubstituted and are less reactive than Structure I, but because there is an available hydrogen on the terminal carbon, they are more reactive than Structure IV which is 1,1,2-trisubstituted with no terminal hydrogen. Structure V is tetra-substituted and is the least reactive of all the depicted isomers.


Generally speaking, PIB products produced in accordance with the processes described in the '913, '999, '152 and '401 patents discussed above contain mainly Structures I and IV with the other isomers being present in only minor concentrations. Highly reactive (HR) polyisobutylene products (see the '913 patent) may generally contain about 80-85 mole % of Structure I (alpha position double bond) and about 15-20 mole % of Structure IV (beta position double bond). Mid-range vinylidene content PIB polymer products (see the '999 patent), which may sometimes be referred to as “enhanced” products, also are generally predominantly comprised of only Structures I and IV, but generally in a ratio of about 55-60 mole % of Structure I and about 35-40 mole % of Structure IV, respectively, with minor concentrations of the other oligomers.









TABLE 1





Structures of PIB Isomers









embedded image









embedded image









embedded image









embedded image









embedded image











The '913, '999, '152 and '401 patents discussed above are each assigned to the assignee of the present application, and the entireties of the respective disclosures thereof are specifically incorporated herein by this reference thereto.


In conducting the processes described above, highly specialized equipment and procedures may often be utilized to enhance the operation and control of the polymerization reactions that are involved. Moreover, as in any industrial activity, methodology and/or equipment for enhancing capacity and throughput are sought continually. In particular, it is often very important in production of polyisobutylene to be able to carefully control (optimize) the rate at which the isobutylene is converted to polyisobutylene (conversion rate). It is also highly important in many cases to be able to carefully control (optimize) the polydispersity index (PDI) and/or the number average molecular weight (MN) of the polyisobutylene product. Even more importantly, it is extremely valuable in many commercial applications to be able to carefully control the concentration of reactive (terminal) double bonds in the polyisobutylene product.


SUMMARY OF THE INVENTION

In accordance with the concepts and principles of the invention described herein, a process for production of polyisobutylene is provided which addresses the issues presented in connection with prior art processes such as those described above. In particular, in one of its several important aspects, the invention described herein provides a polyisobutylene production process that includes subjecting a reaction admixture containing isobutylene, a diluent for the isobutylene and a catalyst composition to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules. The reaction conditions are preferably such that at least a fraction of the polyisobutylene molecules thus produced have alpha position (vinylidene) double bonds and the polyisobutylene product has a number average molecular weight and a polydispersity index. The process of the invention further includes the manipulation of the concentration of the diluent in the admixture to thereby control any one or more of (a) the relative size of the portion of the isobutylene that is converted to polyisobutylene, (b) the number average molecular weight of the product, (c) the polydispersity index of the product and (d) the relative size of the fraction of the polyisobutylene molecules thus produced that possess alpha position double bonds.


In further accordance with the concepts and principles of the invention, the diluent may preferably comprise isobutane and the catalyst composition may comprise a complex of BF3 and a primary alcohol complexing agent. Ideally, the complexing agent may be methanol.


In further accordance with the invention, the reaction admixture may preferably be subjected to suitable reaction conditions in a reaction zone where the reaction admixture is maintained in an intimately intermixed condition. Ideally, the zone may comprise a loop reactor reaction zone.


In still further accordance with the concepts and principles of the invention, it has been found that the relative size of the portion of the isobutylene that is converted to polyisobutylene is a direct function of the diluent concentration, the polydispersity index of the product is an indirect function of the diluent concentration, the average molecular weight of the product is an indirect function of the diluent concentration, and the relative size of the fraction of the produced polyisobutylene molecules having alpha position double bonds is a direct function of the diluent concentration. Thus, and again in accordance with the concepts and principles of the invention, the concentration of the diluent in the admixture may be increased to thereby increase the relative size of said fraction and/or said portion, the concentration of the diluent in the admixture may be increased to thereby decrease the polydispersity index of the product, and the concentration of the diluent in the admixture may be decreased to thereby increase the average molecular weight of the product.


Desirably, the concentration of the diluent in the admixture should be no more than about 50 weight % and preferably, the concentration of the diluent in the admixture should be no more than about 30 weight %, and ideally the concentration of the diluent in the admixture should be in the range of from about 8 to about 15 weight %.


In further accord with the concepts and principles of the invention, a process is provided which may include the step of selecting a diluent concentration for the admixture corresponding to a given relative size of said fraction, and the manipulating step may comprise maintaining the diluent content of the admixture at the selected concentration to thereby hold the relative size of said fraction essentially constant. In addition, the process may include the step of selecting a diluent concentration for the admixture corresponding to a given polydispersity index level, and the manipulating step may comprise maintaining the diluent content of the admixture at the selected concentration to thereby hold the polydispersity index of the product essentially constant. Also, the process may include the step of selecting a diluent concentration for the admixture corresponding to a given relative size of said portion, and the manipulating step may comprise maintaining the diluent content of the admixture at the selected concentration to thereby hold the relative size of the portion essentially constant. Of course, as would be readily understood by the routineer in the olefin polymerization art, the specific numerical correspondence between diluent concentration and any one or more of polydispersity index, molecular weight, size of fraction and/or size of portion will often need to be determined empirically in advance in order to have a set of values from which to select a predetermined diluent concentration. Conversely, the content and/or characteristics of the product stream may simply be monitored and the diluent concentration varied as needed in response.


In further accordance with the invention, the process may include the steps of treating the product to remove diluent and unreacted isobutylene therefrom and recycling at least one of the diluent and the unreacted isobutylene back to the reaction zone.


Furthermore, the invention provides a process for production of polyisobutylene that comprises subjecting a reaction admixture comprising isobutylene, a diluent for the isobutylene and a catalyst composition to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules and wherein at least a fraction of the polyisobutylene molecules have alpha position double bonds, said polyisobutylene product having a number average molecular weight and a polydispersity index, said polyisobutylene product having at least one parameter that is variable as a function of the concentration of the diluent in the admixture, said at least one parameter comprising (a) the relative size of said fraction, (b) the number average molecular weight of the product, (c) the polydispersity index of the product or (d) the relative size of the portion. In accordance with this aspect of the invention, the process may include the steps of choosing a diluent concentration corresponding to a pre-selected value of said at least one parameter and then maintaining the admixture at said chosen diluent concentration to thereby hold said parameter at the pre-selected value. In further accordance with this aspect of the invention, the parameter comprises the relative size of said portion, the average molecular weight of the product, the polydispersity index of the product and/or the relative size of said fraction.


The invention further provides an improved process for production of polyisobutylene wherein a reaction admixture including isobutylene, a diluent for the isobutylene and a catalyst composition is subjected to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules, wherein at least a fraction of the polyisobutylene molecules have alpha position double bonds and wherein the polyisobutylene product has a number average molecular weight and a polydispersity index, the improvement comprising increasing the concentration of the diluent in the admixture to thereby increase the relative size of said fraction, increase the relative size of said portion, decrease the number average molecular weight of the product, and/or decrease the polydispersity index of the product.


Conversely, the invention provides an improved process for production of polyisobutylene wherein a reaction admixture including isobutylene, a diluent for the isobutylene and a catalyst composition is subjected to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules, wherein at least a fraction of the polyisobutylene molecules have alpha position double bonds and wherein the polyisobutylene product has a number average molecular weight and a polydispersity index, the improvement comprising decreasing the concentration of the diluent in the admixture to thereby decrease the relative size of said fraction, decrease the relative size of said portion, increase the number average molecular weight of the product, and/or increase the polydispersity index of the product.


The invention further provides novel polyisobutylene products produced by the processes described above.





BRIEF DESCRIPTION OF THE DRAWINGS

The invention is described in detail below wherein like numerals and letters indicate like features and wherein:



FIG. 1 is a schematic diagram illustrating a laboratory reactor arrangement set-up for conducting isobutylene polymerization processes in accordance with the invention;



FIG. 2 is a graph showing the variation of polymer alpha (vinylidene) double bond content with changing diluent concentration (data at 40° F.);



FIG. 3 is a graph showing molecular weight (MN) and polydispersity index (PDI) trends with changing diluent concentration (data at 40° F.) (filled symbols show MN values—left axis; unfilled symbols show PDI—right axis);



FIG. 4 is a graph showing conversion trends with changing diluent content;



FIG. 5 is a schematic diagram depicting a PIB production process equipped for continuous recycling of isobutylene and/or diluent;



FIG. 6 is a graph showing variations in MN with changing diluent (isobutane) concentration;



FIG. 7 is a graph showing variations of viscosity (v) with changing diluent (isobutane) concentration;



FIG. 8 is a graph showing variations of PDI with changing diluent (isobutane) concentration; and



FIG. 9 is a graph showing variations of alpha (vinylidene) double bond content with changing diluent (isobutane) concentration.





DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Reference will now be made in detail to preferred embodiments of the present invention, examples of which are illustrated in the accompanying drawings.


The concepts and principles of the invention described herein are generally applicable in connection with each of the various PIB reactors and PIB production processes illustrated in the '913, '999, '152 and '401 patents discussed above, and should be applicable in connection with all reactors and reactor systems that are used for the production of highly reactive and/or mid-range vinylidene content PIB polymer products using liquid phase polymerization procedures. In this regard, it is to be noted that the feedstock for such reactors may comprise either isobutylene or an admixture of isobutylene and a suitable non-reactive diluent (solvent) therefor. Suitable feedstocks are described generally in the '913, '999, '152 and '401 patents discussed above. A particularly preferred feedstock comprises a high purity isobutylene monomer having a composition as set forth below in Table 2.









TABLE 2







Concentrations of individual components of Isobutylene stream










Component
Weight %







Methane
0.026



Ethane
 0.0006



Propane
 0.0024



Propylene
0.027



Isobutane
0.064



N-butane
0.010



Butene-1
0.016



Isobutylene
99.84 



T-butene-2
0.010



C-butene-2
0.063



1,3 butadiene
0.007



C5 +
0.007










In accordance with the concepts and principles of the invention, in the liquid phase production of polyisobutylene, an important and formerly unknown relationship between diluent concentration and the alpha vinylidene content of the product has been discovered. That is to say, in accordance with the concepts and principles of the invention, it has been discovered that an increase in diluent concentration in the reaction admixture generally results in higher alpha position (vinylidene) double bond concentration in the product. Moreover, in the same manner, an increase in diluent concentration leads generally to greatly improved (narrower) polydispersity indices. In these regards, and in further accordance with the invention, the diluent content in the reaction admixture may be 50 weight % or less, may desirably be 30 weight % or less, and may optimally be 10 weight % or less. Ideally, the desired diluent for isobutylene may be isobutane. However, in a more general sense, the desirable diluent should simply be capable of dissolving both isobutylene and polyisobutylene and should be inert to the polymer forming reactions taking place in the reactor. In this latter regard, a C3-C16 alkane or alkene, or a mixture of such substances, may be used as the diluent. Desirably, the diluent may be a C3-C16 1-alkene such as, for example, butene-1. In another sense, the diluent may advantageously comprise a mixture of hydrocarbons such as, for example, C4s and other light hydrocarbons.


As mentioned above, the processes of the present invention may generally and suitably be used in connection with the equipment and processes described in the '913, '999, '152 and '401 patents. However, for further clarity, the invention will be described here in connection with a simplified experimental reaction system 10 shown schematically in FIG. 1.


With reference to FIG. 1, the experimental reaction system 10 may desirably include a loop reactor 10, a recirculation pump 12, an isobutylene monomer inlet 14 which may include a pump 16, a diluent inlet 18 which also may include a diluent pump 20, an inlet 22 for the catalyst complex (initiator), and chilling system 24 to remove the heat of the exothermic polymerization reaction. As shown, the loop reactor 10 may include segments 10a, 10b and 10c as well as a pipe 26 which interconnects segments 10a and 10c as shown and provides a place for connection of pump 12. And as can be seen in FIG. 1, a chilling system 24 for the system may desirably include cooling jackets 24a, 24b and 24c respectively for the reactor segments 10a, 10b and 10c, a chilling fluid inlet 28 and a chilling fluid outlet 30. In addition, the system may also include a feedstock inlet 32, where the isobutylene monomer and a diluent are received and admixed for introduction into the reactor, and a product outlet 34 where the crude polymer product is withdrawn from the system.


In operation, a reaction mixture comprising isobutylene, a diluent for the isobutylene and a catalyst composition are recirculated by pump 12 through reactor segments 10a, 10b and 10c and pipe 26 while reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules are maintained in the reactor 10. In the meanwhile, isobutylene and a diluent therefor are introduced into the reactor 10 via inlet 32, catalyst composition (initiator) is introduced into the reactor via inlet 22 and crude product is withdrawn from the system via outlet 34.


Using the system 10, experiments were conducted maintaining the total flow rate of monomer to the reactor loop at 100 mL/min. Reactions were carried out at temperatures of 40° F. and 60° F. The pressure in the reactor loop was maintained at 200 psi. The internal diameter of the reactor tubes was 0.305″ and the total reactor volume was 228 cm3. Catalyst (initiator) flow was controlled at 0.02 mL/min such that the reaction set point was maintained. The recirculation rate in the reactor loop was 2 gpm. The catalyst composition comprised a complex of BF3 and methanol wherein the molar ratio of BF3 to methanol was 1:1. No modifier (methanol) was added to the reactor separately from the catalyst complex, although such a step might be desirable under some conditions. In this latter regard, the separate addition of modifier is described in detail in the '152 patent discussed above. A high purity isobutylene (purity >99.5 weight %) was used as the feedstock and a relatively high purity isobutane (purity 95 to 98 weight %) was used as the diluent.


Experiments were conducted at various diluent concentration levels to study the effect of diluent concentration on alpha position double bond content, molecular weight (MN) and polydispersity index (PDI) of the product. In these experiments, the diluent level was varied between 0 and 27 weight %.


The chain end concentrations of the isomers were measured using 13C NMR spectroscopy. The molecular weight measurements were made using size exclusion chromatography (SEC).


The results of the experimentation are illustrated in FIGS. 2, 3 and 4. FIG. 2 shows variations in alpha position double bond isobutylene isomer content with changes in isobutane diluent concentration at 40° F. And as can be seen in FIG. 2, alpha isomer content increases with increased diluent concentration. Thus it is clear that the alpha isomer content of the product may be increased simply by increasing the concentration of the diluent in the reaction admixture. Also it is clear that if other conditions dictate, the alpha isomer content of the product may be decreased simply by decreasing the concentration of the diluent in the reaction admixture.


With reference to FIG. 3, the influence of diluent concentration on number average molecular weight (MN) and polydispersity index (PDI) can be seen. In FIG. 3, MN values are shown on the left axis and are represented by the filled symbols, while PDI values are shown on the right axis and are represented by the unfilled symbols. Of particular interest is the large drop in PDI at almost constant molecular weight between 0 and 10 wt % of diluent (isobutane) concentration. This may be of particular benefit in meeting the commercially valuable polydispersity specifications for PIB polymers. Thus it is clear that the PDI of the product may be decreased simply by increasing the concentration of the diluent in the reaction admixture. Also it is clear that if other conditions dictate, the PDI of the product may be increased simply by decreasing the concentration of the diluent in the reaction admixture. Furthermore, it is clear that the molecular weight of the product may be decreased simply by increasing the concentration of the diluent in the reaction admixture. Also it is clear that if other conditions dictate, the molecular weight of the product may be increased simply by decreasing the concentration of the diluent in the reaction admixture.


With reference to FIG. 4, it can also be seen that the rate of conversion of isobutylene into polyisobutylene increases with increasing diluent content. This perhaps can be attributed to the fact that higher diluent concentrations in the reactor may provide improved heat transfer characteristics.


As can be seen from the foregoing, alpha isomer content increases, polydispersity decreases, conversion increases and molecular weight decreases with increasing isobutane diluent concentration. Trends similar to those observed at 40° F. were also observed when the polymerization reactions were conducted at 60° F. Tabulated experimental data is reported below in Tables 3 and 4. As can be seen, these Tables also show the concentration of alpha and beta isomers in the polyisobutylene product obtained.









TABLE 3







Data showing the effect of diluent concentration on PIB properties at 40° F.














Number







Isobutane
Average

Concentration
Concentration


Diluent
Molecular

of Alpha
of Beta


Concentration
Weight
Polydispersity
Isomer
Isomer
Other
Conversion


(wt %)
(MN)
Index (PDI)
(Structure I)
(Structure IV)
Isomers
Rate
















0
3318
3.81
54.2
NA
NA
17.9


5
3288
3.31
56.5
33.6
9.9
22.1


10
3155
2.47
59.9
32.3
7.8
24.6


15
2909
2.25
65.4
32.5
2.1
27.2


20
2724
2.22
73.41
18.1
8.4
29.1


27
1785
2.19
75.3
20.3
4.4
33.4
















TABLE 4







Data showing the effect of diluent concentration on PIB properties at 60° F.














Number







Isobutane
Average

Concentration


Diluent
Molecular

of Alpha
Concentration


Concentration
Weight
Polydispersity
Isomer
of Beta Isomer
Other
Conversion


(wt %)
(MN)
Index (PDI)
(Structure I)
(Structure IV)
Isomers
Rate
















0
2249
2.71
53.0
NA
NA
48.3


5
2373
2.23
54.4
34.8
10.8
52.3


10
2217
2.17
63.1
30.7
6.2
51.5


15
1637
1.91
69.5
25.3
5.2
57.5


20
1389
1.89
70.0
22.9
7.1
57.7


27
1109
1.85
73.3
17.6
9.1
62.3









In further accordance with the concepts and principles of the invention, the process also may provide for the continuous recycle of diluent and/or unreacted isobutylene. Such a process is depicted schematically in FIG. 5. With reference to FIG. 5, a reaction admixture comprising isobutylene, a diluent for isobutylene (advantageously isobutane) and a catalyst composition (preferably a complex of BF3 and a complexing agent such as methanol) is subjected in reactor 200 to reaction conditions suitable for causing at least a portion of the isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules. The conditions in reactor 200 are such that at least a fraction of the thus produced polyisobutylene molecules in the product have alpha position double bonds and the polyisobutylene product has a number average molecular weight and a polydispersity index. Upon leaving the reactor 200, the crude polyisobutylene product is washed in a scrubber 202 to remove catalyst residue and is subjected to flashing in a crude flash zone 204 to remove diluent and unreacted isobutylene. The product is then appropriately beneficiated further in a flash unit 212 and delivered downstream via outlet 214. At least a portion of the diluent and unreacted isobutylene flashed in zone 204 may then desirably be continuously recycled overhead back to the reactor 200 via lines 206 and 208. The diluent concentration in the reaction admixture in reactor 200 may desirably be manipulated and/or kept constant at any given time at such a level that it provides maximum benefit to the process in maintaining a desired alpha isomer content as well as in maintaining a low PDI. This, of course, may be done by adding diluent via line 216. The feed rate of fresh isobutylene delivered via line 210 may then be determined by the isobutylene conversion rate in the reactor, i.e., the higher the conversion rate, the higher the rate of fresh isobutylene feed. In addition, whenever desired, the diluent concentration may be varied to alter the alpha isomer content of the product, the PDI of the product, the molecular weight of the product and/or the conversion rate. In this latter connection, it is noteworthy that the alpha isomer content of the product and the conversion rate vary directly with diluent concentration while product molecular weight and PDI vary indirectly with diluent concentration.


Additional experimental data was gathered in connection with studies involving the synthesis of a highly reactive grade (alpha double bond content more than 80%) PIB using a scaled up version of a reactor which is set up essentially the same as the reactor 10. In connection with these studies, additional modifier is introduced essentially as described in the '152 patent. These studies reveal that it is greatly beneficial to operate the reactor using an isobutane diluent concentration of about 8-15 weight % and the following discussion is based on data derived therefrom.


In these studies, a reaction temperature of about 27° F. was maintained employing a chiller temperature of about 5° F. The input flow rate (isobutylene+diluent) was approximately 26 gpm and the volumetric flow rate of the recirculation pump was about 1260 gpm.


The catalyst flow rate was adjusted (ideally to between 0.03 and 0.05 weight % of the feed rate) such that a constant operating temperature was maintained. As per the '152 patent, the modifier was introduced separately into the reactor maintaining a methanol to catalyst ratio of 0.63:1 to synthesize a highly reactive (high vinylidene content) PIB product. In a highly reactive product, it is desirable for the molecular weight (MN), the PDI and the viscosity to be within certain limits, usually dictated by product specifications. One such product may have the following specifications: MN-2100 to 2500; PDI-1.6 to 2.2; Kinematic Viscosity (v)—1500 to 1750; and Alpha double bond content—Greater than 80 mole %. The usual aim of the manufacturing process is that all these specifications be met simultaneously.


In connection with the foregoing, the Kinematic viscosity (v) was measured using Cannon Fenske tubes immersed in a viscosity bath (Koehler KV3000). The MN and PDI measurements were obtained using SEC measurements as described earlier. The values obtained for the different parameters are as shown in FIGS. 6 thru 9. The dark heavy lines on the graphs show the desired specification parameters.


An essentially pure isobutane stream having a composition as set forth in Table 5 below was obtained from ISGAS for use in an effort to isolate the effects on PIB production of minor impurities in the isobutane diluent, although in a real practical sense it is generally not feasible to use such a material in a commercial operation. The total oxygenate content of the pure diluent stream was less than about 5 ppm (≈3.4 ppm methanol; ≈1.4 ppm MTBE).









TABLE 5







Purity of individual components of Isobutane diluent (99.8% purity)










Components
Weight %







Propane
 0.02



Isobutane
99.79



N-butane
 0.18










The experimental set-up and conditions for these efforts were essentially the same as those described above in connection with reaction system 10. The experimental data obtained as a result of these efforts are set forth below in Table 6.









TABLE 6







Product properties obtained using high purity Isobutane

















Alpha







position



Isobutane



double



diluent



bond



concentration


Kinematic
content



weight %
MN
PDI
Viscosity
mole %







 0
3292  
4  
3489
61.4



 8
3197.7
2.55
2693
58.5



13
2946.9
2.48
2637
59.9



18
2883  
2.43
2628
60.1



25
2751  
2.29
2213
60.3










It can be observed from Table 6 that the major advantage of being able to operate so as to produce a PIB having decreased polydispersity was achieved. That is to say, a substantial decrease in PDI and simultaneously in viscosity is achieved with increasing diluent concentration, while almost constant molecular weight is maintained. This is beneficial in a commercial sense for meeting both MN and PDI/viscosity specifications simultaneously. However, there is almost no change in the alpha double bond content with increasing isobutane diluent concentration as was observed in the case of lower purity isobutane.


In view of the foregoing it is clear that the present invention provides a mechanism for greatly reducing both PDI and viscosity by increasing diluent concentration with no substantial corresponding decrease in molecular weight. In addition, both viscosity and PDI can be maintained within specifications while achieving a target molecular weight. This is especially important in the production of HR (high vinylidene) grades of PIB where controlling the polydispersity and viscosity within specifications is of paramount importance. Moreover, the use of a lower purity isobutane diluent resulted in higher alpha double bond content as compared to high purity isobutane diluent. This could be the result of the presence of other hydrocarbon components in the feed or could be due to the presence of oxygenates other than methanol. With regard to the foregoing, it seems to be more likely that the other oxygenates play a role in the increased vinylidene content. In accordance with our studies, the primary suspect is dimethyl ether. These oxygenates play a role similar to additional methanol that is added as a modifier. As is known, methanol is also an oxygenate which may be added in a controlled manner to regulate vinylidene content.


It appears that the invention provides the greatest benefit when the PIB production process is operated using a diluent concentration in the range of from about 8 to about 15 weight %, beyond which the gains are diminished as MN starts to decrease, especially when a lower purity (industrial grade) isobutane diluent is employed.


Although alpha position double bond content increases with increasing isobutane dilution (in the impure isobutane example), the more desired manner to control alpha content is by setting a suitable methanol to catalyst ratio. This is due to the fact that there usually is minimal control in an industrial setting over feedstock composition.

Claims
  • 1. A process for production of polyisobutylene comprising: subjecting a reaction admixture comprising isobutylene, a diluent for said isobutylene and a catalyst composition to reaction conditions in a reaction zone suitable for causing at least a portion of said isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules, at least a fraction of said polyisobutylene molecules having alpha position double bonds, said polyisobutylene product having a number average molecular weight and a polydispersity index;choosing a diluent concentration corresponding to a pre-selected value of at least one parameter selected from the size of the fraction or the molecular weight;maintaining the admixture at said chosen diluent concentration to thereby hold said parameter at said pre-selected value;treating said product to remove diluent and unreacted isobutylene therefrom; andrecycling at least one of the diluent and the unreacted isobutylene back to said zone, wherein said diluent consists essentially of isobutane and a C3-C16 1-alkene.
  • 2. The process as set forth in claim 1, wherein the diluent comprises a mixture of isobutane and 1-butene.
  • 3. A process for production of polyisobutylene comprising: subjecting a reaction admixture comprising isobutylene, a diluent for said isobutylene and a catalyst composition to reaction conditions suitable for causing at least a portion of said isobutylene to undergo polymerization to form a polyisobutylene product including polyisobutylene molecules, at least a fraction of said polyisobutylene molecules having alpha position double bonds, said polyisobutylene product having a number average molecular weight and a polydispersity index, said polyisobutylene product having at least one parameter that is variable as a function of the concentration of said diluent in said admixture, said at least one parameter comprising (a) the relative size of said fraction, (b) the number average molecular weight of said product, (c) the polydispersity index of said product or (d) the relative size of said portion;choosing a diluent concentration corresponding to a pre-selected value of at least one parameter; andmaintaining the admixture at said chosen diluent concentration to thereby hold said parameter at said pre-selected value,
  • 4. The process according to claim 3, wherein the independently provided diluent consists essentially of isobutane and a C3-C16 1-alkene.
CROSS REFERENCE TO RELATED APPLICATIONS

This application is a Divisional Application of U.S. patent application Ser. No. 12/468,195, entitled “Polyisobutylene Production Process with Improved Efficiencies and/or for Forming Products having Improved Characteristics and Polyisobutylene Products Produced Thereby”, filed May 19, 2009, currently pending and under prosecution. The priority of U.S. patent application Ser. No. 12/468,195 is hereby claimed and its disclosure incorporated herein by reference in its entirety.

US Referenced Citations (103)
Number Name Date Kind
132264 Eames et al. Oct 1872 A
2139038 Russell Dec 1938 A
2379656 Ruthruff Jul 1945 A
2407494 Hartvigsen Sep 1946 A
2411097 Kopp Nov 1946 A
2559062 Domte Jul 1951 A
2559984 Montgomery et al. Jul 1951 A
2727022 Linsk Dec 1955 A
2775577 Schmeider et al. Dec 1956 A
2815335 Welch Mar 1957 A
2833840 Longwell May 1958 A
2852500 Alexander et al. Sep 1958 A
2856395 Richard, Jr. et al. Oct 1958 A
2889370 Schechter Jun 1959 A
2918508 Coopersmith et al. Dec 1959 A
3024226 Nolan, Jr. et al. Mar 1962 A
3166546 Nolan, Jr. et al. Jan 1965 A
3284537 Webb, Jr. Nov 1966 A
3306907 McNinch et al. Feb 1967 A
3346354 Kautsky et al. Oct 1967 A
3382291 Brennan May 1968 A
3634383 Miller, Jr. Jan 1972 A
3726842 Treischmann et al. Apr 1973 A
3778487 Driscoll et al. Dec 1973 A
3780128 Shubkin Dec 1973 A
3849085 Kreuz et al. Nov 1974 A
3927041 Cengel et al. Dec 1975 A
3935249 Puskas et al. Jan 1976 A
3991129 Daniels Nov 1976 A
4110521 Barnett et al. Aug 1978 A
4152499 Boerzel et al. May 1979 A
4227027 Booth et al. Oct 1980 A
4231759 Udelhofen et al. Nov 1980 A
4238628 Cahill et al. Dec 1980 A
4242531 Carter Dec 1980 A
4311808 Su Jan 1982 A
4383093 Shiraki et al. May 1983 A
4391959 Fauth et al. Jul 1983 A
4400493 Abemanthy, Jr. et al. Aug 1983 A
4429099 Kennedy et al. Jan 1984 A
4433197 Vogel et al. Feb 1984 A
4465819 Kosanovich et al. Aug 1984 A
4558104 Bronstert et al. Dec 1985 A
4605808 Samson Aug 1986 A
4664406 Spitaler et al. May 1987 A
4691072 Schick et al. Sep 1987 A
4862702 O'Neal Sep 1989 A
4973733 Valkovich et al. Nov 1990 A
4982042 Akatsu et al. Jan 1991 A
5068490 Eaton Nov 1991 A
5175225 Ruhe, Jr. Dec 1992 A
5191044 Rath et al. Mar 1993 A
5192335 Cherpeck Mar 1993 A
5254649 Miln et al. Oct 1993 A
5254784 Nurminen et al. Oct 1993 A
5286823 Rath Feb 1994 A
5300701 Cherpeck Apr 1994 A
5408018 Rath Apr 1995 A
5439991 Colman et al. Aug 1995 A
5448001 Baird Sep 1995 A
5556932 Rath et al. Sep 1996 A
5563313 Chung et al. Oct 1996 A
5710225 Johnson et al. Jan 1998 A
5731379 Kennan et al. Mar 1998 A
5733993 Yu et al. Mar 1998 A
5767334 Nissfolk et al. Jun 1998 A
5779742 Baker Jul 1998 A
5792729 Harrison et al. Aug 1998 A
5811616 Holub et al. Sep 1998 A
5814706 Yu et al. Sep 1998 A
5910550 Rath Jun 1999 A
5945575 Sigwart et al. Aug 1999 A
5962604 Rath Oct 1999 A
5977251 Kao et al. Nov 1999 A
6132827 Miro Oct 2000 A
6300444 Tokumoto et al. Oct 2001 B1
6361856 Wakai et al. Mar 2002 B1
6384154 Sigwart et al. May 2002 B1
6407186 Rath et al. Jun 2002 B1
6441110 Sigwart et al. Aug 2002 B1
6479598 Lewtas et al. Nov 2002 B1
6517373 Rath et al. Feb 2003 B2
6525149 Baxter, Jr. et al. Feb 2003 B1
6562913 Baxter, Jr. et al. May 2003 B1
6642239 Rath Nov 2003 B2
6683138 Baxter, Jr. et al. Jan 2004 B2
6777506 Baxter, Jr. et al. Aug 2004 B1
6844400 Baxter, Jr. et al. Jan 2005 B2
6844401 Baxter, Jr. et al. Jan 2005 B2
6858188 Baxter, Jr. et al. Feb 2005 B2
6884858 Baxter, Jr. et al. Apr 2005 B2
6992152 Lobue et al. Jan 2006 B2
7037999 Baxter, Jr. et al. May 2006 B2
7049363 Auer et al. May 2006 B2
7056990 Baxter, Jr. et al. Jun 2006 B2
7091285 Baxter, Jr. et al. Aug 2006 B2
7105616 Auer Sep 2006 B2
7441104 Morris Oct 2008 B2
7498396 Baxter, Jr. et al. Mar 2009 B2
20030040587 Baxter, Jr. Feb 2003 A1
20030162918 Wettling et al. Aug 2003 A1
20030191257 Wettling et al. Oct 2003 A1
20050090612 Soane Apr 2005 A1
Foreign Referenced Citations (31)
Number Date Country
2195575 Feb 1996 CA
2217848 Dec 1996 CA
2334263 Dec 1999 CA
27 02 604 Jul 1978 DE
1 592 016 Jul 1981 DE
199 52 030 May 2001 DE
0 145 235 Jun 1985 EP
0 244 616 Mar 1987 EP
0 279 456 Aug 1988 EP
0 322 241 Jun 1989 EP
0 355 997 Feb 1990 EP
0 400 905 Dec 1990 EP
0 481 297 Apr 1992 EP
0 628 575 Dec 1994 EP
0 671 419 Sep 1995 EP
0 742 191 Nov 1996 EP
0 628 022 Mar 1998 EP
0 831 141 Mar 1998 EP
0 628 022 Nov 1998 EP
1 159 368 Jul 1969 GB
2 181 145 Apr 1987 GB
WO9310063 May 1993 WO
WO 9414739 Apr 1994 WO
WO 9931151 Jun 1999 WO
WO 9964482 Dec 1999 WO
WO 0077056 Dec 2000 WO
WO 0119873 Mar 2001 WO
WO 0127172 Apr 2001 WO
WO 0196426 Dec 2001 WO
WO 0206359 Jan 2002 WO
WO 0214385 Feb 2002 WO
Non-Patent Literature Citations (2)
Entry
Supplementary European Search Report.
1st examination report from Saudi Arabian application.
Related Publications (1)
Number Date Country
20110251359 A1 Oct 2011 US
Divisions (1)
Number Date Country
Parent 12468195 May 2009 US
Child 12932837 US